Patent Application
20070112243
1. Field of the Invention
The present invention is directed to a treatment system for the remediation of polychlorinated biphenyls (PCBs), chlorinated pesticides, and other halogenated compounds. Specifically, the treatment system comprises a plurality of catalyzed zero-valent metal particles and a hydrogen donating solvent.
2. Description of Related Art
PCBs are a group of synthetic aromatic compounds with the general formula C12H10-xClx. PCBs are among the most persistent, bioaccumulative, and toxic compounds and are responsible for the primary risk at numerous sediment sites. PCBs are a group of synthetic aromatic compounds that were historically used in industrial paints, caulking material, and adhesives, as their properties enhanced structural integrity, reduced flammability, and boosted antifungal properties. PCBs have been used in many industrial applications because of their robust physical and chemical properties such as their resistance to acids, bases, and oxidation, their excellent dielectric characteristics, and their thermal stability at high temperatures (up to 350° C.). When PCBs were released into the environment, they were sorbed to particulate matter that was then dispersed over large areas. PCBs can be introduced into the food chain by the uptake of contaminated soils by biota and humans can directly inhale or absorb PCBs by dermal contact.
Although the United States Environmental Protection Agency (USEPA) has banned the manufacture of PCBs since 1979, PCBs are still present in the environment posing possible adverse health affects to both humans and animals. Prior to the USEPA's ban on PCB production, PCBs were commonly used as additives in paints and asphalt-based adhesives that were subsequently applied to a variety of structures. Governmental facilities constructed as early as 1930 utilize PCB-containing binders or PCB-containing paints, which are now leaching into the environment and posing ecological and worker health concerns. PCBs have been found in at least 500 of the 1,598 National Priorities List (Superfund) sites identified by USEPA. Many of the most costly cleanups are at sediment sites dominated by PCB contamination. Additionally, PCBs can still be found in the paints located on NASA property at a number of NASA Centers. The PCB and metal levels in painted structures on Kennedy Space Center have been documented to be as high as 31,000 ppm. PCBs have been introduced into the NASA work environment via improper disposal and accidental leaks from transformers, heat exchanges, and hydraulic systems. Numerous NASA Centers have older metal structures upon which paints containing PCBs were applied. These painted structures are posing worker and ecological health hazards and, in several instances, are now considered a TSCA-level (Toxic Substance Control Act) waste. Some of the impacted structures could be refurbished and utilized for new programs, but because the paint currently on the structures is heavily laden with PCBs, the programs are unable to reuse or even discard these structures without significant cost.
The removal of contaminants from natural resources and structures is an ongoing, significant problem. Because of the serious health problems associated with the bioaccumulation of PCBs in animals, including humans, and the desire for NASA programs to have a quick non-destructive means of removing PCBs from existing structures, numerous tactics have been considered with various degrees of success. To date, no definite in-situ, non-destructive method is available for the remediation of PCBs found in natural media. Current technologies as listed below require costly dredging or excavating and are environmentally unfriendly. This costly alternative required heavy machinery to physically remove the contaminated soil. The soil removed is considered a TSCA regulated waste and must be disposed of via:
In the invention disclosed in U.S. Pat. No. 6,664,298 filed on Oct. 2, 2001, and incorporated into the present application by express reference thereto, a method was disclosed for delivering a reactive material to a contaminant in situ. The method incorporated the concept of either emulsification of the reactant or encapsulation of the reactant prior to its delivery to the contaminant in situ. The method disclosed and claimed in U.S. Pat. No. 6,664,298 has particular success in using a zero-valent metal emulsion containing metal particles, surfactant, oil and water in a method of enhancing dehalogenation of dense non-aqueous phase liquid (DNAPL) sources. While it is known that zero-valent iron is very effective in the treatment of chlorinated hydrocarbons, such as dissolved trichloroethylene (TCE), zero-valent iron, by itself, is unable to completely dechlorinate PCBs or more robust halogenated compounds such as chlorinated pesticides dissolved in aqueous solutions.
In the invention disclosed in U.S. Pat. No. 7,008,964, filed on May 28, 2003, and incorporated into the present application by express reference thereto, another emulsion system for remediating contaminated media is disclosed. A zero-valent metal emulsion containing zero-valent metal particles doped with a catalytic metal is disclosed to remediate halogenated aromatic compounds, such as PCBs, from natural resources, i.e., in the ground. However, this option for the removal of PCBs found in natural media using an emulsion has several limitations. This emulsion includes emulsion particles comprised of an aqueous interior with bimetal particles encapsulated in a surfactant stabilized hydrophobic solvent membrane. The use of a water-only solvent interior continuum has several disadvantages. Most importantly, making the aqueous-based emulsion requires the potentially hazardous step of adding pure water to the catalytic metal coated zero-valent metal particle. This step is particularly hazardous because:
The present invention is directed to a treatment system comprising a plurality of catalyzed zero-valent metal particles and an organic hydrogen donating solvent. This treatment system provides a major benefit of eliminating PCBs in situ. Destruction of the PCB offers one of the greatest benefits, as only PCB destruction can eliminate future liabilities. The treatment system provides a “paste”-like system that is preferably applied to natural media and ex-situ structures. As will become clear, the present invention expands on the concept described in the previously cited applications to effectively remove and remediate PCBs and other halogenated compounds such as chlorinated pesticides found in natural media, painted structures, and other ex-situ facilities.
In a first preferred embodiment, the treatment system is used for the in-situ remediation of PCBs, chlorinated pesticides, and other halogenated compounds found in natural media including groundwater, surface water, sediment, and soil. The present treatment system has the advantage that it does not negatively alter the natural media, allowing the contaminant to be treated in situ without costly dredging, therefore decreasing the impact of cleanup. Additionally, the treatment system provides no hazardous by-products, which eliminates long-term environmental liabilities, minimizes the potential of leaching or spreading hazardous waste into the environment, and eliminates costly hazardous waste disposal costs.
In a second preferred embodiment, the treatment system is used for the removal and destruction of PCBs found in ex-situ structures, such as painted structures, or within the binding or caulking material on ex-situ structures. The treatment system could be very beneficial to entities responsible for PCB-laden structures and other PCB contamination problems. Not only are these structures a demolition hazard, they are allowing constant leaching of PCBs into surrounding soils and other natural media. Sites containing PCBs in their structures include the U.S. Navy, Army, utility companies, etc. The present invention provides an in-situ PCB remediation process that is applicable for the treatment of ex-situ structures containing metal and PCB compounds within externally applied coatings such as paint. The treatment system extracts and degrades only the PCBs found in the structure, leaving in most cases the structure virtually unaltered. The present treatment system as applied to ex-situ structures functions to disassociate the PCBs from the coating, i.e. paint, and degrades the chlorinated aromatics into biphenyl, a benign by-product. The treatment system may be applied using a “paint-on and wipe-off” process, that in the end leaves the structure PCB-free and virtually unaltered in physical form. The treatment system may also be applied utilizing dip tanks where pieces of caulking or adhesives are treated in batches prior to non-TSCA regulated disposal. The present treatment system has far reaching implications to older facilities across the world; allowing them to be remediated and reused by implementing a PCB cleanup technology that removes and degrades the PCBs while on the structure.
The features and advantages of the present invention will become apparent from the following detailed description of a preferred embodiment thereof, taken in conjunction with the accompanying drawings, in which:
The present invention is directed to a treatment system comprising a plurality of catalyzed zero-valent metal particles and an organic hydrogen donating solvent. The reference to “an organic hydrogen donating solvent” should be construed to include solvents that only include organic compounds as well as solvents that include organic compounds and non-organic compounds, such as water. The preferred organic hydrogen donating solvents include, but are not limited to, alcohols. Most preferably, the alcohols are diols, triols, ethanol, methanol, glycerin, and mixtures thereof. As indicate above, any of these organic compounds may also be preferably mixed with water to form the organic hydrogen donating solvent. The preferred catalyzed zero-valent metal particles are bimetallic particles wherein a zero-valent metal particle is coated with a catalytic metal. Most preferably, the bimetallic particle is formed from a zero-valent iron (Fe) or zero-valent magnesium (Mg) particle coated with a noble metal. Most preferably, the noble metal is palladium (Pd), nickel (Ni), zinc (Zn) or a mixture thereof. In a preferred embodiment, the zero-valent metal particles are microscale or nanoscale zero-valent magnesium or zero-valent iron particles. Preferably, the microscale particles would have a diameter in the range of 1-3 microns. Whereas, the preferred nanoscale particles would have a diameter in the range of 20-300 nm. It should be understood that other zero-valent metal particles and combinations may be used. The catalytic metal is preferably selected from the group consisting of noble metals and transition metals. The preferred mass percent palladium by weight ranges from approximately 0.08-8%, but higher and lower ranges could still yield positive results.
In one preferred embodiment, the bimetallic particles may be formed using a mechanical alloying technique. Mechanical alloying is a high-energy milling process for producing composite materials with an even distribution (though not homogeneous in the rigorous sense) of one material into another. By definition, at least one of the materials must be metallic to be considered an alloy. The mechanical alloying techniques most commonly used involve ball milling, vibratory milling, attrition, or roller milling. Ball milling is a process in which a material is loaded into a canister partially filled with milling balls. The canister is then rotated at high speed on its major axis so that the balls are held by centripetal force to the inside wall until they reach the highest point inside the canister. Gravitational force then exceeds the upward force of the balls and they fall to the bottom of the canister where they impact other balls and the canister wall. The approximate critical speed of any ball mill is given below and is usually on the order of about 250 RPMs,
Nc=7.05/(D1/2)
where Nc=critical speed and D=milling canister diameter
Vibrator milling is a process similar to ball milling except that the milling vessel is vigorously shaken in a back and forth motion or in a back in forth motion in conjunction with a lateral motion that produces a “figure 8” path. This type of milling relies solely on the extremely high-energy collisions between rapidly moving milling balls rather than the collisions between the balls and the canister wall, as described for ball milling. Since vibrator mills can often shake canisters at a rate of approximately 1200 RPMs, often producing ball speeds of upwards of 5 m/s, vibrator milling commonly yields the desired reduction in particle size at a rate one order of magnitude faster than that of ball milling. Two other less common types of milling are attrition milling and roller milling. These processes are not commonly seen in laboratory settings but are often seen in industrial work. Attrition milling relies on rapidly spinning paddles to stir the milling balls present in the milling vessel. The rate of size reduction observed is often similar to the rate of reduction observed for vibrator mills of similar size; however, due to the necessity of a cooling system this type of milling is often limited in its capabilities to systems that can be milled in liquid media. Roller Milling is a process that relies on fracturing caused by stress induced in the system from the compression of materials between two rolling bars or cylinders. It is most often used for reduction of very coarse materials into less coarse materials that can later be reduced in size by other means. For all milling types, the reduction of particle size relies on stresses induced in individual particles caused by collisions within the milling vessel. This process reduces the average particle size until equilibrium is reached, at which point no further size reduction is observed.
In a preferred embodiment of the present invention, Mg/Pd bimetallic particles may be produced using relatively short milling times, with the high-energy vibrational mill previously described, to avoid complete dissolution of the small quantity of brittle palladium into the large quantity of malleable magnesium. For the scale up, a paint shaker fitted with custom plates to hold the milling canisters may be chosen as the mill engine. Tungsten Carbide is preferably used as the milling vessel material in most high-energy, small-scale mills because it is extremely durable and does not break down over time or cause the introduction of contaminates into the milling material. The use of an extremely durable milling vessel is not necessary for producing the Mg/Pd bimetallic particles because the introduction of some contaminates would not appreciably affect the reactivity of the metal, thus galvanized steel pipes (purchased from Ace Hardware with internal diameter—5.03 cm, length—17.8cm) with steel end caps were used. Steel ball bearings (mass—22.3grams each, volume—1.6 cm3 each) were chosen as the preferred grinding matrix. Since the paint shaker chosen operates at approximately 600 RPMs (as opposed to 1250 RPMs observed for the Spex Centi-prep) longer milling times were necessary. It has already been shown that most often, the optimum rate of comminution is observed when milling canisters are filled 40-60% with grinding materials and 10-20% with particulate material, by volume. It was determined that longer milling times actually reduced the rate of dechlorination. Longer milling times cause the palladium to be completely embedded into the magnesium thereby producing less active surface. Therefore, the optimum milling time is in the range of 20-40 min.
U.S. patent application Ser. No. 10/977,622 discloses a preferred ball milling process for making the bimetallic particles. U.S. patent application Ser. No. 10/977,622 is incorporated in the present application by express reference thereto. The preferred ball milling process includes milling the zero-valent metal particle with the catalytic metal to form the bimetallic particle. In the ball milling process, the zero-valent metal particle has a particle size of less than about 10 microns, preferably 0.1-10 microns or smaller, prior to milling. In the preferred ball milling process, the catalytic metal is supported on a carbon support structure prior to milling. The zero-valent metal particle (e.g. microscale magnesium) is preferably ball milled with 1-10% palladium supported on carbon. The preferred mass percent palladium by weight ranges from approximately 0.01-15%, and more preferably 0.08-8%.
U.S. Pat. No. 7,008,964 discloses a preferred process for making the bimetallic particles by coating a zero-valent particle with a catalytic metal. U.S. Pat. No. 7,008,964 is incorporated in the present application by express reference thereto. In this preferred embodiment, microscale zero-valent iron is coated with palladium (Pd) using a solution of K2PdCl6 as follows. Approximately 100 g of microscale zero-valent iron particles, such as provided by Alfa Aesar, Inc. or BASF, Inc., is weighed and placed in a Buchner Funnel. The microscale zero-valent iron particles are then washed with 100 ml of a 5% hydrochloric (HCI) or sulfuric (H2SO4) solution (5 mL HCL or H2SO4 and 95 mL of Deoxygenated DI water). The microscale zero-valent iron particles are then filtered. Then 0.19 g of K2PdCl6 is weighed out and dissolved in 100 mL of deoxygenated DI water. All of the filtered microscale zero-valent iron particles are placed in an Erlenmeyer flask and the K2PdCl6 solution was added. The resulting mixture is stirred in the flask using a magnetic stirrer for 5 minutes. The solution is then allowed to settle and filtered until dry. The resulting bimetallic microscale particles have a palladium coating of approximately 0.06% Pd/Fe. In a second preferred embodiment, microscale zero-valent iron is coated with palladium (Pd) using a 40 g/L Pallamerse solution. The Pallamerse solution is made up of 10.0% potassium dinitrosulfate palladate (II), K2(Pd(NO2)2SO4. The following procedure indicates a preferred method for coating 2.5 g of microscale zero-valent iron particles. The microscale zero-valent iron particles are washed in a Buchner Funnel with 10 mL of 10% H2SO4 solution. The microscale zero-valent iron particles are then rinsed with 10 mL of deoxygenated DI water. Then, 5 mL of the Pallamerse solution is then added and the mixture is allowed to sit for 2 minutes before filtering. After the mixture is filtered, the microscale zero-valent iron particles are washed with 10 mL of deoxygenated DI water. The material is then filtered until dry. The resulting bimetallic microscale particles had a palladium coating of approximately 7% Pd/Fe.
The treatment system is preferably formulated as a “paste-like” system that contains the catalyzed zero-valent metal particles and the organic hydrogen donating solvent within a thickener and a stabilizing agent. In a preferred embodiment, a “paste-like” system is formed by coating the catalyzed zero-valent metal particles with glycerin in an ethanol solution with calcium stearate added as a thickener. Other thickeners may be added including, but not limited to, PEG, glycerin, paraffin, stearate, and mixtures thereof. In this preferred embodiment, glycerin is used as a stabilizing agent. However, other stabilizing agents include, but are not limited to, mineral oil, vegetable oil, or mixtures thereof. In this preferred embodiment, calcium stearate is used as the thickener. However, the thickener may also be a starch.
The treatment system is used to treat PCB or other halogenated compounds to degrade the PCB into a benign end-product. It should be understood that any reference to PCBs in the present application also expressly includes a reference to other suitable halogenated compounds, including, but not limited to Chlordane and DDT. Once in contact with contaminated media, the PCBs diffuse into the treatment system and undergo degradation. The PCBs continue to enter, diffuse, and degrade into non-halogenated end-products. The present treatment system has found particular use in remediating PCB-containing natural media and ex-situ structures.
In a first embodiment, the treatment system is applied to natural media. The treatment system causes the PCB to be extracted or removed from the media (e.g. soil or sediment), and degrades the chlorinated aromatics into biphenyl or other non-chlorinated benign by-products.
In a preferred embodiment of the present invention used in treating natural media, the treatment system comprises zero-valent magnesium (Mg) particles coated with a small amount of palladium (Pd) utilized in conjunction with an organic hydrogen donating solvent, preferably alcohols and water. The treatment system has two functions in remediating sediments: first, to adsorb the PCBs from the soil matrix; second, to degrade the extracted PCBs. The process for sorbing the PCB molecules from the inorganic or organic external soil or humic particles to the treatment system is aided by the incorporation of a lipophilic earth-friendly solvent, preferably ethanol, corn oil, or limonene, within the treatment system. This lipophilic compound will draw the hydrophobic PCB molecules into the treatment system via salvation. The second process is the degradation or dehalogenation of the PCBs. The solvent selection for this process is limited to organic solvents that are capable of donating a hydrogen atom to the PCB structure. Solvents with this ability include, but are not limited to, solvents containing one or more hydroxyl groups (e.g. alcohols) such as methanol, ethanol, and glycerin. This hydrogen atom, as will be described in more detail below, replaces the chlorine atom on the biphenyl ring. Solvents with hydroxyl groups, preferably methanol, ethanol, and glycerin, in the absence of water have been shown to be as effective in the dehalogenation process as pure water. Additionally, the use of this non-water solvent allows the treatment system to be effective over extended periods of time. The previous water-only containing emulsion lost its efficacy within 24 hours after being manufactured. This, as stated earlier, is due to the competing reaction of water and magnesium that leaves oxidized magnesium that is incapable of providing the necessary electrons for the dehalogenation process. The catalyzed zero-valent metal particles are preferably manufactured using a mechanical alloying method. The catalyzed zero-valent metal particles have been optimized for use in the treatment system and preferably comprise 0.1% palladium (Pd) on zero-valent magnesium (Mg), referred to herein as a Mg/Pd bimetal. Although other magnesium bimetals have also been shown to be effective, for example nickel (Ni) coated magnesium (Mg). The Mg/Pd bimetal is a potent hydrodechlorination reagent capable of removing the chlorine from high concentration solutions of chlorocarbons in minutes. The degradation end-product for the dehalogenation of all Arochlor mixtures is the biphenyl ring, which is a benign end-product. Magnesium metal, a powerful reducing agent, reacts with water to form hydrogen gas (H2) and magnesium hydroxide. Palladium is a well-documented hydrogenation catalyst that chemisorbs molecular hydrogen, weakening the bond between the hydrogen atoms, forming atomic hydrogen bound to the palladium surface. It is hypothesized that the interaction of the bimetallic magnesium/palladium system with a solvent containing available hydrogen moieties (i.e. alcohols or water) results in the generation of atomic hydrogen at particular sites on the metal surface. The bound, atomic hydrogen is available for reaction with PCB molecules in solution yielding a reductive dehalogenation reaction. The proposed reaction mechanism is shown below:
Mg+2H2O→Mg(OH)2+H2
H2(Pd catalyst)+RCl→RH+HCl
Rapid and almost complete dechlorination of PCBs in aqueous/solvent systems in the presence of the catalyst system described above was demonstrated.
In a preferred embodiment, a mixing device can be used to mix the treatment system into the sediment or it may be pumped into a matrix of concern. The preferred treatment system includes zero-valent magnesium particles coated with palladium (hereinafter referred to as Mg/Pd) that reacts with PCBs during and after mixing over a period of minutes to days, and may either remain in the sediment or be recovered. Introduction of Mg/Pd may be as a bare metal or in a biodegradable solvent reagent paste, which has the dual benefit of stripping strongly bound PCBs into the solvent phase and controlling the rapid oxidation of Mg in water. Alternatively, the catalyzed zero-valent metal particle, preferably Mg/Pd, may be coated with a small amount of a stabilizing agent, such as oil or glycerin, and inserted into the sediment. The oil is preferably a vegetable or mineral oil. However, this method of remediating PCBs may have some disadvantages. The Mg/Pd may become ineffective shortly after the oil is removed from the surface of the Mg/Pd particle through natural degradation of the oil in the sediment. Recovery of Mg/Pd may be possible by introducing the treatment system on a magnetic support like iron particles. This treatment system may be used in combination with others, such as placement of a thin layer cap to minimize subsequent resuspension, or amendment of the benthic layer with a sequestration agent such as activated carbon to treat residuals. Preliminary results have demonstrated up to 99% removal of PCBs in river sediment over a period of 5 days. This treatment system may be used to dechlorinate PCBs in riverine and estuarine sediment in situ or ex situ. A small particle size (e.g. micrometer to mesh-size) zero-valent magnesium particle is coated with a small amount of palladium (˜0.1% by weight), then added to the sediments and mixed. The reaction is allowed to proceed over a period of minutes to days.
In a second embodiment, the treatment system is applied to ex-situ structures and causes the PCBs to disassociate from the coating, i.e., paint, and the chlorinated aromatics are degraded to biphenyl, the benign by-product. Once the treatment system is in contact with a contaminated structure, the paint softens allowing the PCBs to diffuse into the treatment system and undergo degradation. The PCBs continue to enter, diffuse, and degrade into non-halogenated end-products.
It should be understood that the application of a thickened solvent solution without any catalyzed material (e.g. ethanol or limonene with corn starch or other thickener) can be applied to a structure for removing PCBs. This thickened solvent solution would include a hydrogen donating solvent, such as methanol, ethanol or glycerin, and a thickener, such as calcium stearate or a starch. This technique is a subset of the technique described above. Simply using a thickened solvent to remove PCBs from weathered surfaces without degrading the PCBs is an option. Experiments were conducted using this extraction only process and the results are provided in the Experimental Results Section. After the PCBs are removed from the structure, the catalyzed system may be used to degrade the PCBs or the PCBs may be disposed of using other known conventional disposal methods.
In a preferred embodiment, PCBs may be removed from painted structures using the present treatment system. The treatment system has two primary functions: 1) to extract the PCBs from 40 year old material; and 2) to degrade the extracted PCBs. The process for removing PCBs from structures is accomplished as an independent step to the degradation process. The goal is to extract the PCBs out of the paint without destroying the paint and partition the PCBs into an environmentally friendly solvent. Research has indicated that this step can usually be accomplished within the first 24 hours of the treatment system contacting the paint. PCBs are extremely hydrophobic and prefer to be in the treatment system over hardened paint or binder material. The solvent selected for the treatment system must be used to open, but not destroy, the paint's polymeric lattice structure, allowing pathways for PCB movement out of the paint and into the solvent. A number of solvents are available for use within the treatment system. The second process is the degradation or dehalogenation of the PCBs. The solvent selection for this process is limited to solvents that are capable of donating a hydrogen atom to the PCB structure. Solvents with this ability include, but are not limited to, solvents containing one or more hydroxyl groups (alcohols) such as methanol, ethanol, and glycerin.
The following Experiment Results are used to illustrate the beneficial results that are obtained using the present treatment system. However, it should be understood by one of ordinary skill in the art that the treatment system may be modified from these preferred embodiments without departing from the scope of the present invention.
Sediments
Experiments were also conducted using sediments from two different rivers, River A and River B, to assess the efficacy of the neat (bare) Mg/Pd material in actual, aged, PCB-contaminated sediments. Mg/Pd was added to flasks containing a sediment slurry (approximately 25% water addition to in-situ water content conditions), and were gently mixed 4 days on an oscillatory shaker table. A typical chromatogram from the River A sediment showing control sample and a treated sample are shown in
Painted Structures
Due to the wide variety of structural properties associated with each specific PCB-laden paint, the choice of solvent(s) incorporated into the treatment system is specific to the paint being treated. Experiments have shown that solvent systems that work very well at softening and removing the PCBs found in one variety of paint can be ineffective when applied to another. Therefore, the final formulation of the treatment system must be determined in the laboratory, using paint samples from the proposed area prior to determining the final formulation of the treatment system to apply. The data provided below illustrates the ability of the treatment system to remove PCBs and degrade them from painted structures.
Additional treatment system formulation properties that must be addressed for each site-specific application include viscosity and stability. The treatment system must be viscous or thick enough to remain where it is applied on the structure. Several thickening agents have been tested. Adding a stabilizing agent ensures that the treatment system will not evaporate and leave the unprotected catalyzed zero-valent metal particle exposed. Due to the extreme reactivity of the treatment system, the choice of thickening agents and stabilizing agents is complex. During the testing of the treatment system, a number of reagents were evaluated to ensure the rate of dehalogenation was not inhibited by its addition to the system. The following tables include examples of the data obtained with the addition of glycerin as a stabilizing agent and thickener, showing no interference of this additive on the PCB reduction potential.
The following Tables demonstrate the efficacy of the treatment system with various solvent systems. Table 1 illustrates the typical results achieved in an aqueous treatment system comprised of water and 10% methanol. Methanol was then added to the water to make the solution more organic in nature increasing the solubility levels of PCBs in the stock solution. Due to safety concerns associated with the large production of hydrogen atoms when the Mg/Pd was added to the water, pure methanol and ethanol solutions were substituted and tested, resulting in similar rates of reduction as shown in Table 2 and 3.
As is evident from the data found in Table 1-3, the degradation of PCBs can be achieved rapidly and completely in the presence of the present treatment system.
Table 4 shows the experimental results obtained using a Aroclor 1260 standard. This testing was performed in order to determine whether the addition of glycerin would hinder the PCB degradation. As can be seen from this Table, the addition of glycerin to the treatment system does not inhibit the degradation of PCBs.
Table 5 provides the results of experiments conducted using the treatment system to dehalogenate PCBs. The results were analyzed using GC/MS. This testing was performed to determine whether the addition of starch inhibited PCB degradation.
Table 6 shows the results of tests conducted in order to determine the ability of solvents, in this case limonene, to remove PCBs from Galbestos, a construction material used formerly with Roberston Metal Buildings. The Table shows the application of multiple dips of the Galbestos structure from hanger 1 at Moffett Field in solvents.
Table 7 shows the results of tests conducted to evaluate the various solvents for the extraction efficiency to remove PCBs from Galbestos material in hanger 1 at Moffett Field.
Although the present invention has been disclosed in terms of a number of preferred embodiments, it will be understood that numerous modifications and variations could be made thereto without departing from the scope of the invention as defined by the following claims:
This application claims the benefit under 35 U.S.C. 119(e) of U.S. Provisional Application Ser. No. 60/708,126 filed Aug. 11, 2005, and U.S. Provisional Application Ser. No. 60/708,127 filed on Aug. 11, 2005, the contents of which are incorporated herein by reference.
The invention described herein was made in the performance of work under a NASA contract and by an employee of the United States Government and is subject to the provisions of Public Law 96-517 (35 U.S.C. §202) and may be manufactured and used by or for the Government for governmental purposes without the payment of any royalties thereon or therefore.
| Number | Date | Country | |
|---|---|---|---|
| 60708126 | Aug 2005 | US | |
| 60708127 | Aug 2005 | US |