Cushion and method of manufacturing the same

Abstract

A cushion has a main body formed of fibers including organic synthetic fibers which are stereoscopically intertwined. A cured polyurethane resion covers surfaces of the fibers and binds the fibers at their intersections. The cured polyurethane resin is obtained by curing a polyurethane prepolymer with water or steam.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a cushion used for seats in vehicles such as automobiles or aircraft and to a method of manufacturing such a cushion.

2. Description of the Prior Art

Various materials are used for conventional cushions for seats used in vehicles such as automobiles or aircraft. Examples of such materials include palmrock, using palm fibers, a synthetic resin foam such as a polyurethane foam, or a cotton-like material of organic synthetic fibers.

Palmrock, however, has a large specific gravity and easily collapses.

Polyurethane foam has poor air permeability and cannot provide a comfortable cushion. High-resiliency polyurethane foams considered to provide more comfort have larger specific gravities than flexible polyurethane foams.

A cotton-like material consisting of organic synthetic fibers easily collapses, so it is not suitable for use in a cushion either.

SUMMARY OF THE INVENTION

It is, therefore, an object of the present invention to provide a cushion which can maintain an excellent cushioning effect over a relatively long period of time and which has a small specific gravity and excellent air permeability, and to provide a method of manufacturing such a cushion.

In order to achieve the above object of the present invention, there is provided a cushion comprising a cushion main body comprising organic synthetic fibers having a denier of 1 to 20 which are stereoscopically intertwined, and a cured polyurethane resin which binds the fibers at their intersections.

The cushion according to the present invention can be manufactured in the following manner. A cushion main body comprising organic synthetic fibers having a denier of 1 to 20 which are stereoscopically intertwined is impregnated with a polyurethane prepolymer solution so as to allow the prepolymer to attach itself to the surfaces of the fibers. The cushion body is then subjected to centrifugation to remove excess solution from the cushion body. The prepolymer is then brought into contact with a curing agent comprising water and is cured, thereby bonding the fibers at their intersections.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an illustration for explaining the structure of a cushion according to the present invention;

FIG. 2 is a perspective view showing an example of an organic synthetic fiber used in the cushion according to the present invention;

FIG. 3 is a perspective view showing another example of an organic synthetic fiber used in the cushion according to the present invention;

FIG. 4 is a graph showing the relationship between hardness and density in cushions in the Examples together with cushions in the Comparative Examples; and

FIGS. 5 and 6 are illustrations for explaining the structures of the cushions in the Comparative Examples.

FIGS. 7 to 12 are graphs showing the properties of the cushion of the invention together with those of a comparative cushion.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

A cushion according to the present invention will be described with reference to the accompanying drawings.

Referring to FIG. 1, a cushion according to the present invention comprises main body 10, comprising organic synthetic fibers 11 which are stereoscopically intertwined. Main body 10 has a cotton-like structure, and fibers 11 have a relatively large number of intersections 12. The organic synthetic fibers can consist of, for example, polyester fiber, nylon fiber, acrylic fiber or polypropylene fiber. The cross-sectional shape of the fiber to be used is not critical. Thus, a fiber having circular or profile cross-sections can be used. The fibers can be hollow or solid. Hollow fibers are preferred because they reduce the weight of the cushion product. Furthermore, each fiber can be made of a single material or a plurality of materials. The organic synthetic fiber illustrated in FIG. 2 is a hollow fiber of the so-called conjugated type and is obtained by combining two fiber materials 21 and 22 having different thermal shrinkage coefficients. The fiber illustrated in FIG. 3 is a solid fiber of the conjugated type, and is obtained by combining two fiber materials 31 and 32 having different thermal shrinkage coefficients. The fibers must have a denier of 1 to 20, and preferably have a length of 25 to 150 mm. If the denier is over 20, the degree of intertwining of the fibers are poor, and the intertwined fibers tend to loosen or come untied.

Main body 10 can also contain inorganic fibers such as metal or glass fibers in addition to organic synthetic fibers. When inorganic fibers are used, they must be included in an amount of 5 to 90% by weight based on the total weight of main body 10.

Main body 10 normally has a density of 0.01 to 0.1 g/cm.sup.3 and preferably has a density of 0.015 to 0.060 g/cm.sup.3. Such a main body is obtained by intertwining fibers at a crimping density of 5 to 20 fibers per inch.

As shown in FIG. 1, fibers 11 of main body 10 are uniformly and thinly coated with cured polyurethane resin 13, which firmly binds fibers 11 at their intersections 12.

Cured polyurethane resin 13 is obtained by curing a polyurethane prepolymer with water including steam. Any polyurethane prepolymer having isocyanate groups can be used. Preferably, a polyurethane prepolymer prepared from a polyol having a functionality (the number of hydroxyl groups) of 2.0 to 8 and a molecular weight per hydroxyl group of 300 to 2,000, and having an isocyanato group (--NCO) content of 2 to 30% by weight is used. Ethylene oxide can be added to the polyol in an amount of up to 20% by weight. Many such polyurethane prepolymers are commercially available.

In order to bind fibers 11 substantially only at intersections 12 with resin 13, main body 10 is impregnated with a solution of a polyurethane prepolymer in an organic solvent. The organic solvent to be used herein can be a halogenated hydrocarbon such as trichloroethylene (trichlene), dichloroethylene, trichloroethane, carbon tetrachloride, or ethylene chloride. The polyurethane prepolymer is dissolved in a solvent at a concentration of 1 to 100% by weight and preferably at a concentration of 10 to 70% by weight.

The polyurethane prepolymer solution can also contain a flame-retardant to give the cushion flame-retardant qualities. Liquid flame-retardants that are miscible with the polyurethane prepolymer solution are preferred. Examples of such flame-retardants include phosphoric acid esters (organic phosphates), halogenated phosphoric acid esters (organic phosphates), condensed phosphoric acid esters (organic phosphates), and nitrogen-containing phosphoric acid esters (organic phosphates). They are commercially available. The flame-retardant is added in an amount of 5 to 15 parts by weight and preferably in an amount of about 8 parts by weight based on 100 parts by weight of the polyurethane prepolymer.

In order to impregnate main body 10 with the polyurethane prepolymer solution, it can be dipped in the solution. The prepolymer is preferably contained in an amount of 10 to 70%, preferably 20 to 50%, most preferably 30 to 40% by weight based on the total weight of main body 10. Thereafter, main body 10 must be centrifuged (at a centripetal acceleration rate of, e.g., 50 to 1,000 m/sec.sup.2) to remove any excess solution. The centrifugation allows the solution on the exposed surfaces of the fibers to be removed and substantially only the solution at the intersections of the fibers to remain. Thereafter, body 10 is placed in a mold consisting of upper and lower molds of metal nets or punched metals. Body 10 is packed in the mold to a density of, e.g., 0.01 to 0.1 g/cm.sup.3, which is the final density of the cushion.

Finally, the polyurethane prepolymer attached to body 10 is brought into contact with water or steam introduced from outside the mold. The water or steam preferably has a temperature of 80.degree. to 130.degree. C. Water or steam is used in an amount not less than the NCO equivalent weight of the polyurethane prepolymer. The reaction between water or steam and the isocyanato groups is fast, and the polyurethane prepolymer can cure within 30 seconds or more. The curing time can be further shortened by adding 10 to 1,000 ppm of an amine such as a tertiary amine (e.g., triethylenediamine or morpholine) to the water or steam.

Cured main body 10 is removed from the mold. Then, as shown in FIG. 1, a cushion is obtained in which the surfaces of fibers 11 are coated with cured polyurethane resin 13 and intersections 12 of fibers 11 are bound by cured polyurethane resin 13. Cured resin 13 is preferably contained in main body 10 in an amount of 20 to 40% by weight based on the total weight of main body 10.

The cured polyurethane resin has a strong adhesive force and excellent heat resistance. According to the present invention, since mainly water is used as a curing agent (cross-linking agent), curing can be performed safely.

EXAMPLE 1

Polyester cotton (hollow conjugated type "Esup 6d" available from TOYOBO CO., LTD.) was impregnated with an excessive amount of a solution (prepolymer concentration: 1 to 70% by weight) of a polyurethane prepolymer (having an NCO% of 5%.+-.0.2% and prepared from polyol "MN3050" and toluene diisocyanate "T-80" available from Mitsui Toatsu Chemicals, Inc.) in trichlene. The cotton was centrifuged to remove any excess solution and was placed in a mold at a predetermined density. In this case, the weight ratio of cotton to polyurethane prepolymer was about 7:3. The centripetal acceleration rate was about 50 to 1,000 m/sec.sup.2. If it is desirable to change the hardness of any portion of the cushion, the cotton density or prepolymer content of that portion can be changed.

Water or steam (at 80.degree. to 130.degree. C.) in an amount not less than the NCO equivalent amount of the polyurethane prepolymer was blown into the polyester cotton in the mold for 3 minutes. The polyurethane prepolymer was thus cured and the body was removed from the mold to provide the cushion of Example 1.

EXAMPLE 2

5 to 15 parts (preferably about 8 parts) of a liquid flame-retardant ("Thermolin 101", available from Asahi Glass Co., Ltd.) were added to 100 parts of a trichlene solution of the same polyurethane prepolymer as in Example 1. As in Example 1, polyester cotton was impregnated with an excessive amount of the resultant solution. The cotton was centrifuged to remove any excess solution and was placed in a mold at a predetermined density.

Water or steam at 80.degree. to 130.degree. C. in an amount not less than the NCO equivalent amount was blown into the polyester cotton in the mold for 3 minutes to cure the polyurethane prepolymer. The body was removed from the mold to provide the cushion of Example 2.

COMPARATIVE EXAMPLE 1

A polyurethane raw material (formulation in Table 1) was prepared which consisted of a polyether polyol having a molcular weight of 3,000 and a functionality of 3, toluene diisocyanate (T-80), water as a foaming agent, and other additives. After mixing the material with a mixing head, it was injected into a warm mold in a predetermined amount, and the mold was closed. The mold was heated at 170.degree. C. for 10 minutes (5 minutes for the HR foam) to cure the foam. The foam was then removed from the mold. If a flame-retardant is added, it is to be added in an amount of 10 to 20 parts.

TABLE 1______________________________________(Polyurethane Foam Formulation) Mold Foam (parts by weight)______________________________________Polyol EP551 100 (Mitsui Toatsu Chemicals, Inc.)Foaming agent Water 3.6 Dubco 33LV 0.25 (Sankyo Air Products K. K.)Catalyst Stannous octate 0.15 (Yoshitomi Pharmaceutical Industries, Ltd.)Foam Stabilizer L-520 1.5 (Nihon Unikah K. K.)Isocyanate T-80 45.7 (Mitsui Toatsu Chemicals, Inc.) INDEX 105Foaming agent Freon 11 5 to 15 (Asahi Glass Co., Ltd.)Flame-retardant Thermolin 101 15 (Asahi Glass Co., Ltd.)______________________________________

Referring to Table 1, "EP 551" has a functionality of 3, and a molecular weight of 3,000.

COMPARATIVE EXAMPLE 2

Latex was sprayed onto unbound palm fibers which were then compressed to a predetermined thickness and dried with hot air at 120.degree. C. The compressed body was cut to a predetermined size. The cut body was placed in a mold and was again sprayed with latex. After the mold was closed, the body was dried with heated air at 120.degree. C. The dried body was removed from the mold to provide palmrock.

In the obtained palmrock, fibers 50 were bound with latex 51, as shown in FIG. 5.

COMPARATIVE EXAMPLE 3

Low-melting point binder fibers (4d; melting point: 110.degree. C.) were mixed and unbound with polyester cotton (6d; hollow conjugated type) in a weight ratio of 7:3. The mixture was formed into a sheet having a thickness of 20 mm. The sheet was placed in a mold at a specific density. After closing the mold, the binder resin was melted by heated air at a temperature higher than the melting point of the resin. After the resin was solidified upon cooling, the body was removed from the mold to obtain a cotton cushion.

In the cushion of Comparative Example 3, as shown in FIG. 6, only low-melting point binder resin 60 is bound, and polyester cotton 61 is mixed with this matrix.

Various properties of the cushions in Examples 1 and 2 and Comparative Examples 1 to 3 are shown in Table 2 below. Table 3 shows properties and pad performance (experimental values) of the prepolymers which can be used in the present invention. FIG. 4 shows the relationship between density and hardness in the cushions of Examples 1 and 2 and Comparative Examples 1 to 3.

TABLE 2__________________________________________________________________________ Comparative Example 1 Comparative (Polyurethane Foam) Comparative Example 3 Flexible HR Example 2 (Cotton Example 1 Example 2 Foam Foam (Palmrock) Cushion)__________________________________________________________________________Density (g/cm.sup.3) 0.015 to 0.015 to 0.026 to 0.040 to 0.060 to 0.020 to 0.060 0.060 0.050 0.060 0.200 0.060Compressionstrength 4 to 60 3.5 to 55 6 to 30 10 to 30 8 to 40 8 to 40(kg/314 cm.sup.2)Ball 60 60 40 60 55 55rebound (%)Repeated 50%deflection,80000 cycle 4 4 3 3 10 10compressionset (%)70.degree. C., 50% com- 15 15 8 6 20 40pression set (%)Air permeability 200 200 20 to 5 to 300 200(cc/cm.sup.2 /sec) or more or more 100 20 or more or moreLocal hardness Possible Possible Impossible Possible PossiblechangeHardening time 4 min. 3 min. 10 min. 5 min. 7 min. 7 min.Combustion TestFor auto- Flame- Flame- Flame- Semi Semi flame- Flame-mobiles retardant retardant retardant flame- retardant to retardantMVSS 302 retard- fire retard-Para. ant antFor air- Combus- Self-ex- Self-extinguish- Combustible Self-extin-craft (1) tible tinguish- ing guishing ingFor rail- Flame- Flame- Flame-retardant* Combustible Flame-road ve- retardant retardant retardanthicles (2)__________________________________________________________________________ (1) Test according to Appendix F, Section II of Procedures for Testing Aircraft (2) Combustion Test by Senpaku Gijutsu Kenkyusho Note* Each polyurethane foam tested contains a different content (parts) of flameretardant. Polyurethane foams containing no flameretardant are combustible. TABLE 3__________________________________________________________________________Prepolymer(polyol) MN1000 MN1500 MN1500 MN1500 MN3050 EP550N CP560__________________________________________________________________________polyol Functionality 3 3 3 3 3 3 6struc- Molecular 1000 1500 1500 1500 3000 3000 6000ture weight Remarks Terminal E.O. added (increased reactivity)Prop- NCO % 5.0 7.4 5.0 2.8 4.9 4.9 5.1erties Viscocity Gelled 34500 151000 Gelled 5840 6310 13500of pre- CP (atpolymer 23.degree. C.)preparedfromT-80Pad Hardness 18.8 21.1 18.2 15.2 18.5 17.8 18.0properties (kg/314 cm.sup.2) at 0.025 g/cm.sup.3 den- sitiy Ball 51 60 57 53 60 58 61 rebound (%) 70.degree. C., 50% 18 18 16 15 15 15 15 compres- sion set (%) Repeated 5 5 4 4 4 4 4 50% de- flection, 80000 cycle compres- sion set (%)__________________________________________________________________________

EXAMPLE 3

Using fibers of 6 denier and 38 denier, cushions were prepared under the same conditions as in Example 1. The properties of the cushions are shown in Table 4 below.

TABLE 4______________________________________Denier of Fiber 6 38Sample No. 1 2 3 4______________________________________Density Kg/m.sup.3 20.3 24.3 20.5 25.3Harness 2.5 4.6 2.0 3.0Hardness/Density 125 189 98 118Change rate inHardness (%) 13 20 21 22Change rate inDistortion (%) 12 14 29 19Appearance Good Fibers tend to be untied______________________________________

EXAMPLE 4

Various properties of a cushion of the invention (size: 500 mm.times.500 mm.times.100 mm) prepared according to the procedures in Example 1 were measured. As a comparison, a cushion having the same size was prepared by crimping fibers of 300 denier, dipping the crimped fiber in a polyurethane prepolymer solution, removing solution only by the gravity without centrifugation, and steam-curing the fiber. The results are shown in FIGS. 7 to 12, in which curve a denotes the invention and curve b denotes the comparison.

FIG. 7 shows the relationship between the density (kg/m.sup.3) and the deflection at 50 kgf (mm). It is seen that the cushion of the invention is smaller in density than the comparison at the same level of deflection.

FIG. 8 shows the relationship between the density (kg/m.sup.3) and the deflection at 50-90 kgf (mm). The larger the deflection difference, better the sitting comfortability. It is seen that the deflection difference is larger in the cushion of the invention than in the comparison, indicating that the cushion of the invention is better in the sitting comfortability than the comparison.

FIG. 9 shows the relationship between the density (kg/m.sup.3) and the hysteresis loss rate. The smaller the rate, the better the sitting comfortability.

FIG. 10 shows the relationship between the density and the logarithmic decrement.

FIG. 11 shows the relationship between the density and the resonance frequency. It is desired that the frequency is low, and is 4.0 Hz or less for a motorcar for riding or passenger car.

FIG. 12 shows the relationship between the density and the transmissibility at 6 Hz. It is desired that the transmissibility is lower for the sitting comfortability to suppress unpleasantness and improve the sitting comfortability since the resonance point in human body is at about 5 to 6 Hz.

As described above, according to the present invention, cushions are obtained which are lighter than conventional cushions, have excellent air permeability, do not easily collapse, and provide excellent seating comfort. These advantages are obtained in the invention because a fine fiber of 1 to 20 denier is used and the centrifugation is applied to remove excess polyurethane as a binder, thereby binding the fiber substantially only at the intersections. Both the manufacturing equipment and molds and the manufacturing procedures are simple, there is no fear of pollution, and manufacturing costs are low.

Claims

1. A cushion comprising:

a main body comprising organic synthetic fibers having a denier of 1 to 20 which are stereoscopically intertwined; and

a cured polyurethane resin which binds the fibers at intersectiosn thereof.

2. A cushion according to claim 1, wherein the organic synthetic fibers are fibers selected from the group consisting of polyester, nylon, acrylic, and polypropylene fibers.

3. A cushion according to claim 1, wherein the organic synthetic fibers have a length of 25 to 150 mm, and are crimped at a density of 5 to 20 fibers per inch.

4. A cushion according to claim 1, having a density of 0.01 to 0.1 g/cm.sup.3.

5. A cushion according to claim 1, wherein the polyurethane resin is contained in an amount of 10 to 70% by weight based on a total weight of said cushion.

6. A cushion comprising:

a main body comprising organic synthetic fibers which are stereoscopically intertwined, said fibers having a denier of 1 to 20; and

a binder comprising steam-cured polyurethane resin binding said fibers at intersections thereof;

said cushion being obtained by dipping said main body in a polyurethane prepolymer solution to attach said prepolymer to said main body, centrifuging said main body to remove excess solution therefrom, and bringing said prepolymer remaining in said main body into contact with a curing agent comprising steam to cure said prepolymer.

7. A cushion according to claim 7, wherein the organic synthetic fibers are fibers selected from the group consisting of polyester, nylon, acrylic, and polypropylene fibers.

8. A cushion according to claim 7, wherein the organic synthetic fibers have a length of 25 to 150 mm, and are crimped at a density of 5 to 20 fibers per inch.

9. A cushion according to claim 7, having a density of 0.01 to 0.1 g/cm.sup.3.

10. A cushion according to claim 7, wherein the polyurethane resin is contained in an amount of 10 to 70% by weight based on the total weight of said cushion.

11. A cushion according to claim 1, wherein the cured polyurethane resin contains a flame-retardant.

12. A cushion according to claim 6, wherein the cured polyurethane resin contains a flame-retardant.

13. A cushion according to claim 7, wherein the polyurethane resin is contained in an amount of 20 to 50% by weight based on the total weight of said cushion.

14. A cushion according to claim 8, wherein the polyurethane resin is contained in an amount of 30 and 40% by weight based on the total weight of said cushion.

15. A cushion according to claim 14, wherein the organic synthetic fibers have a length of 25 to 150 mm, are crimped at a density of 5 to 20 fibers per inch, and having a density of 0.01 to 0.1 g/cm.sup.3.

16. A cushion according to claim 3, wherein the polyurethane resin is contained in an amount of 20 to 50% by weight based on the total weight of said cushion.

17. A cushion according to claim 16, wherein the polyurethane resin is contained in an amount of 30 and 40% by weight based on the total weight of said cushion.

18. A cushion according to claim 17, wherein the cured polyurethane resin contains a flame-retardant.