Hybrid luminescent device for imaging of ionizing and penetrating radiation

Abstract

A hybrid luminescent device for converting ionizing and penetrating radiation energy such as x-rays, gamma rays, neutrons, ions, electrons, and the like into visible light for imaging applications. The hybrid luminescent device includes a phosphor screen disposed on an entrance face fiber optics scintillator which, in turn, may be removably coupled to a camera or like recording media. The hybrid luminescent device of the present invention is capable of providing enhanced radiation absorption efficiency, higher spatial resolution and enhanced brightness or luminescence output over that which is achievable by the phosphor screen and/or fiber optics scintillator when used separately as an intensifying screen for imaging of ionizing and/or penetrating radiation.

Description

FIELD OF THE INVENTION

The present invention relates to luminescent devices for use in imaging of ionizing and/or penetrating radiation such as x-rays, gamma-rays, neutrons, ions, electrons and the like. More particularly, the present invention relates to a hybrid luminescent device including a thin phosphor screen and a thick screen fiber optics scintillator and which hybrid device exhibits an improved luminescence output and enhanced radiation absorption efficiency over that which is individually achievable by either the thin phosphor screen or the fiber optics scintillator.

BACKGROUND OF THE INVENTION

In the field of radiation detection and imaging it is well known to use so called intensifying screens that contain luminescent material for converting the invisible penetrating radiation into visible light. The light produced by the luminescence of the penetrating radiation in the intensifying screen can then be made available for detection on film or by other electronic light-sensitive detector means such as a CCD (charged coupled device), photocathode or photodiode.

For example, in x-ray imaging applications, the intensifying screen will contain x-ray luminescent material, typically a thin layer of phosphor particles. The particular phosphor composition selected will be determined in accordance with the desired selected x-ray application in order to emit a relatively large number of light photons for each x-ray photon which strikes a phosphor particle in the phosphor layer.

It is desirable that the phosphor layer or intensifying screen exhibit good brightness or light output, good radiation absorption efficiency and good spatial resolution.

For medical x-ray applications in particular, the design of such intensifying screens has involved a trade-off between screens of large thickness, which result in increased luminescent radiation for a given x-ray level, but which also produce decreased image sharpness, and screens of less thickness, which result in improved image sharpness relative to the thicker screens, but which also require more x-ray radiation to produce acceptable film images, thereby increasing the x-ray dosage to which the patient must be exposed. In practice, the thicker or high speed screens are utilized in those applications which do not require maximum image sharpness, thereby reducing the patient exposure to x-rays, while thinner or medium speed and slow speed screens are utilized when increased image resolution is required. These latter screens employ thinner phosphor layers and may incorporate dyes to minimize transverse propagation of light by attenuating such rays more than a normal ray which travels a shorter path. In general, thinner or slow speed screens require approximately 8 times the x-ray dosage of thicker high speed screens.

There are many applications in medical x-ray imaging, industrial x-ray imaging and x-ray crystallography, among other disciplines, where spatial resolution must remain high. Heretofore, good resolution x-ray screens which have a radiation absorption efficiency upwards of 90%-100% simply did not exist, since 100% radiation absorption efficiency for thin phosphor screens have been generally thought impossible to achieve.

In accordance with the known practice, phosphors are coupled directly to radiographic film for use in medical x-ray imaging. It is also well known in the art to deposit a phosphor layer on a fiber optics face plate which, in turn, is directly coupled to a CCD camera. The fiber optics face plate functions as a light guide for channeling the light photons produced in the phosphor layer to the detector of the CCD.

Such electronic devices as CCDs are sensitive to direct penetrating radiation. Direct incidence of penetrating radiation onto CCDs will cause additional noise in the image and over time damage such devices by forming traps that result in reduced charge transfer efficiency and higher dark current.

The use of a phosphor deposited directly onto a CCD, i.e., without any fiber optics device, therefore has very limited applications. The phosphor frequently does not provide the shielding required to protect the CCD from radiation damage and keep the noise low from direct excitation of the radiation onto the CCD. This, as stated above, severely limits the lifetime of the CCD. Normally, this results in severe speckle noise which fogs the optical image that is deposited onto the CCD. In summary, direct imaging onto a CCD is possible, but it is not recommended with the combined use of a phosphor. A phosphor deposited onto a fiber optics device which is bonded to a CCD will provide shielding, but will have a relatively low conversion of radiation into light.

Accordingly, it would be desirable to be able to provide a luminescent device which combines the shielding capabilities of a fiber optics device and the brightness and good spatial resolution capabilities of a thin phosphor screen.

Various patents have proposed techniques for fabricating a phosphor layer which has both good resolution and enhanced brightness. The basic approach taken by the prior art has been directed to methods for depositing the active phosphor particles in an array of cells or pixels which are separated by wall members that are disposed generally parallel to the direction of x-ray travel. See for example, U.S. Pat. No. 5,302,423. The purpose of the wall members is to reflect light emitted by the pixelized phosphor particles and thereby prevent scattered light from reaching the detection means and contributing to a foggy image. Such pixelization techniques, however are complex and expensive and still require additional phosphor layer thickness to ensure a desired level of radiation absorption efficiency.

A radioluminescent or scintillating fiber optics is a special type of fiber optics material which has a core glass containing the rare earth element terbium. When activated by ultraviolet light, x-rays, or ionizing particles, terbium fluoresces in the green and peaks at a wavelength of 550 nm. Therefore, a face plate made of this type of fiber optics material can be used both as a scintillator as well as a light guide, and has been employed primarily in medical and nondestructive imaging as x-ray scintillators.

Scintillator fiber optic plates can be made thick in order to provide up to 100% radiation absorption efficiency without significant degradation in spatial resolution. This occurs because of the non-particle, low scatter, channeling nature of this type of luminescent device. While conventional scintillating fiber optics plates provide good radiation absorption efficiency and high spatial resolution, it would be desirable to be able to improve the brightness of such luminescent devices.

SUMMARY OF THE INVENTION

It is therefore a principle object of the present invention to provide a hybrid luminescent device for imaging penetrating radiation which combines the brightness or strong luminescence output under penetrating or ionizing radiation and good spatial resolution capabilities of a thin phosphor screen and the radiation absorption efficiency and high spatial resolution of a thick screen, fiber optics scintillator.

A hybrid luminescent device as disclosed here combines a thin phosphor layer disposed directly on an entrance face of a relatively thick screen, scintillating fiber optics (SFO) face plate.

The present invention thus reduces the interdependency of spatial resolution and absorption efficiency of the phosphor screen. In this invention, the high spatial resolution of a thin phosphor screen can be combined with a highly absorbing luminescent material to provide a combination which exhibits superior spatial resolution and brightness over the phosphor material alone. The result is a high spatial resolution, highly absorbing, high light output scintillating device.

As a consequence, the hybrid luminescent device of the present invention can provide higher radiation absorption efficiency, thereby providing improved signal statistics over the prior art. This increased absorption efficiency is also important in providing shielding to an electronic light detection device on the opposite side of the screen away from the radiation. Therefore, in applications where it is appropriate to couple phosphor screens or deposit phosphor particles onto a non-scintillating fiber optics imaging conduit like those now used in digital x-ray imaging systems, improvements in luminescence yield and radiation absorption efficiency will be obtained when a similar layer thickness of phosphor is used on the radiation entry surface of scintillating fiber optics.

The hybrid luminescent device disclosed herein can be coupled directly onto a front-illuminated CCD or a back-illuminated CCD, and can be configured to provide the appropriate radiation shielding well into the million volt energy range of the penetrating or ionizing radiations to provide a device that will provide very high sensitivity. Alternatively, the hybrid luminescent device of the present invention can be coupled to a camera or light recording device directly, i.e., directly onto a CCD, or it can be coupled through a lens to a camera.

Further still, another alternative is to place the hybrid luminescent device onto a fiber optics image conduit or image taper (demagnification device) that is already attached to a CCD, other electronic sensor or as input into an image intensifier tube. This device configuration advantageously offers the benefit of greater flexibility for interchanging phosphor screens of different compositions, densities and/or thickness for different applications without the risk of damaging the CCD or other electronic sensor.

The hybrid luminescent device of the present invention also captures a larger percentage of photons from penetrating radiations. Therefore, for a given exposure of radiation, use of this invention will provide improvements in image quality over the prior art. Conversely, for a similar image quality, lower levels of radiation can be used to provide safer exposure levels. The invention will advantageously provide improved medical diagnosis through the combination of improved image quality and lower patient dose. The lower patient dose will allow more frequent intervals of testing to monitor possible onset of cancers in risk cases.

The present invention will also provide improved nondestructive inspections and enhanced crystal structure determinations, basically for the same reasons of enhanced image quality and reduced exposures (higher throughput) as described above. Higher x-ray inspection throughput is also an important consideration for efficient on-line process monitoring.

Another advantage of the present invention is that the combination of the two luminescent devices provides enhanced signal capability, which is especially advantageous for use in the field of transmission electron microscopy. The enhanced signal results in improved signal to noise ratios which will allow investigators the opportunity to improve discrimination among features during an examination. In general, all of these benefits can result in social gains in terms of improved health care, enhanced efficiency and improved product development (fewer rejects, less waste).

Methods and apparatus which incorporate the features described above and which function as described above constitute specific objects of this invention.

Other and further objects of the present invention will be apparent from the following description and claims and are illustrated in the accompanying drawings, which by way of illustration, show preferred embodiments of the present invention and the principles thereof and what are now considered to be the best modes contemplated for applying these principles. Other embodiments of the invention embodying the same or equivalent principles may be used and structural changes may be made as desired by those skilled in the art without departing from the present invention and the purview of the appended claims.

BRIEF DESCRIPTION OF THE DRAWING VIEWS

FIG. 1 is an isometric view of the hybrid luminescent device of the present invention which includes a thin phosphor screen and a thick fiber optic scintillator.

FIG. 2 is a sectional view taken along the line and in the direction of arrows 2--2 of FIG. 1.

FIG. 3 is a schematic illustration showing a measurement set up for testing the hybrid luminescent device of the present invention for use as an x-ray scintillator.

FIG. 4 is a graph which plots luminescence output or brightness for several embodiments of the invention (samples 9, 11, and 13) as a function of x-ray energy. Brightness values for prior art luminescent devices (samples 8, 10, and 12) are shown for comparison.

FIG. 5 is a graph which plots normalized luminescence output (brightness) of the invention (sample 15) as a function of x-ray energy. Luminescence output curves for other prior art luminescent devices (samples 14, 16 and 17) are shown for comparison.

FIG. 6 is a schematic illustration showing a measurement set up for testing the hybrid luminescent device of the present invention for use as an electron scintillator.

FIG. 7 is a graph showing the relative brightness of a scintillating fiber optics (SFO) face plate with a 17 .mu.m P20 ((ZnCd)S:Ag) phosphor coating (curve 1); a 20 .mu.m P20 ((ZnCd)S:Ag) phosphor coating on glass (curve 2); and a SFO without a phosphor coating (curve 3).

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

A hybrid luminescent device in accordance with one embodiment of the present invention is generally designated by reference numeral 10 in FIG. 1. The hybrid luminescent device 10 is specially constructed to capture and convert penetrating or ionizing radiation into light that is detectable by a sensing or recording medium.

The hybrid luminescent device 10 consists of a phosphor layer attached to a scintillating fiber optics face plate (herein referred to as "SFO"). The SFO is composed of a non crystalline amorphous substance such as inorganic glass or plastic luminescent material, with inorganic glass material preferred.

Especially suitable scintillating fiber optics glass material for use in the present invention include; terbium-activated silicate luminescent glasses as disclosed in U.S. Pat. No. 5,122,671; terbium activated borate luminescent glasses as disclosed in U.S. Pat. No. 5,108,959; and the cerium-activated, lithium enriched luminescent glass composition as disclosed in U.S. Pat. No. 4,415,810. Such luminescent glass compositions as noted above are preferred over crystalline fiber optics scintillator or scintillant such as that disclosed in U.S. Pat. No. 4,101,781 since glass fibers can be formed much longer and with more compact spacing as compared to grown crystal scintillating fiberoptic material disclosed in U.S. Pat. No. 4,101,781. The luminescent glass material also provides over a twofold increase in spatial resolution.

As is best seen in FIG. 2, the SFO is fashioned into an array of many parallel fibers. Fibers may range in diameter from about 3 .mu.m to about 3 mm with 10 .mu.m fibers being preferred in a single plate. The fibers have a first given refractive index and are surrounded by a cladding material of a second, lower refractive index such that the fibers will trap light that is produced in the fiber from radiation-induced scintillations in the glass or plastic material. The fibers also trap light which is produced by the radiation-induced scintillations in the overlying phosphor layer. In the fiber bundle, the light which is produced within each fiber and/or which is produced in the adjacent phosphor layer and is captured within each fiber, is guided or channeled to the exit face of the SFO to produce a very sharp image plane corresponding to the various intensities of light produced by the absorbed penetrating radiation. For example, there is a linear relationship between the radiation absorbed and the light produced in both the phosphor layer or the SFO. The sharp image plane allows direct contact of the hybrid device 10 to a film or electronic sensor such as a CCD, photodiode or photocathode. The light will emit in each layer with a wavelength ranging from the ultraviolet to the near infrared based on the material host matrix and the luminescent activation employed or selected.

Preferable emission is from a glass fiber that emits green light as in U.S. Pat. No. 5,120,970.

The phosphor layer may be selected to match a preferred camera receptor such as a CCD. In the CCD case, green to red light is channeled through the SFO, at the same time green light is simultaneously produced in the SFO to provide optimal sensitivity. In the case of a photomultiplier or photocathode receptor, the preferred phosphor emission is from the near UV through the blue and the appropriate phosphor materials can be selected accordingly. In this case, the predominantly green emitting SFO can be used as in the CCD case since there are also emission bands that extend into the blue region. For a more indepth discussion of useful green and blue emitting luminescent glass compositions see C. Bueno, et. al. SPIE Vol 1327, "Properties and Characteristics of Optimal Glass II" (1990), pages 79-91.

Further examples of phosphor configurations that are useful with this invention are as follows. Phosphor particles ranging in size from submicron--50 .mu.m in diameter, preferably 2-10 .mu.m in diameter, may be deposited directly onto the SFO through a solvent and adhered with either an inorganic or organic binder, or conversely can be deposited by some other means such as a sputtering technique or through a vapor deposition process. There are several techniques known to those skilled in the art for depositing phosphors onto glass and fiber optic glass plates. This technology has been perfected for the military night vision image intensifier cameras and other image intensification devices.

The invention can also be achieved by a simple combination of commercially available phosphor screens onto the SFO plates. Commercial phosphor screens are typically composed of luminescent particles which are bonded to a flexible mylar material and are held in place either by a spring compression, via an optical epoxy or grease or by a host of other techniques known to those skilled in the art. The phosphor screen that is to be deposited onto the scintillating fiber optic need not be limited to a single phosphor material, but may consist of a mixture of phosphor materials to achieve the desired characteristics such as emission in the desired wavelengths or with the appropriate luminescent output.

Interspersed throughout the fiber bundle in a generally hexagonal pattern are individual fibers of extramural absorber (EMA) material. This is common art in the field of manufacture of face plates of fiberoptics. The EMA material preferably comprises opaque black or other dark color glass fibers. The EMA material reduces fiber to fiber light cross talk by absorbing light photons which exit a glass fiber from which they originate or which have entered a glass fiber at an angle greater than a predetermined critical angle as a result of scintillation activity in the adjacent phosphor layer. The light photons which are absorbed within the EMA material are designated by phantom arrows (see FIG. 2). By reducing cross-talk, the EMA material improves the spatial resolution of the image at the exit face of the SFO. However, the brightness is also reduced as fewer light photons will reach the image plane at the exit face of the SFO.

Several examples are given to illustrate the preparation and characteristics of the hybrid luminescent device of the invention. The following examples are to be construed as illustrative only and not limiting in any manner the scope and spirit of the invention as defined by the appended claims.

EXAMPLE 1

In this example, various combinations of commercial phosphor screens and scintillating fiber optics face plates were combined and tested for their suitability for use as x-ray screens. The various x-ray screen pair combinations were coupled to a CCD camera via a 1:3.31 non scintillating fiber optics taper. The measurement setup for the data contained in the following Tables 1, 2, and 3 is shown schematically in FIG. 3. The absorption efficiency is defined as the percent of incident radiation absorbed in the luminescent devices.

The brightness is defined as the level of light emitted after radiation is presented to the device.

The relative brightness is a value that is compared to a normal reference value of 1.

The spatial resolution is defined as the spatial response of the converted object pattern in the image domain. This is normally tested with alternating lines of high density and low density with a spacing (frequency) close to that expected for the response of the imaging system.

The highest frequency of these alternating lines represents the maximum spatial resolution of the system.

The brightness levels are measured directly by a wide linearity CCD device.

The absorption efficiency, A%, is calculated by the formula: A%=(1-exp (.sup.- ux)).times.100 at various energies of the penetrating radiation.

Table 1 compares the CCD response, the corresponding relative brightness levels and the spatial resolution of the invention (sample 4) in relation to prior art luminescence devices, samples 1-3 and 5. Sample 1 shows a high resolution phosphor attached to a high speed (i.e., numerical aperture (N.A.)=1), non-scintillating fiber optics image transfer device. The CCD response for this device is shown and a relative brightness of 1.0 is set as the reference value. The spatial resolution of 9-10 line pairs per millimeter (lp/mm) observed is close to that of the Nyquist frequency of the camera system employed. The absorption efficiency is only 27% with this beam.

TABLE 1__________________________________________________________________________Absorption Efficiency relative brightness and spatial resolution ofinvention in relation toprior art Thickness Absorption SpatialSmpl (mm) of fiber Numerical Efficiency Relative Resolution.sup.3# Fiber Optic optic Aperture.sup.1 (%).sup.2 Brightness (lp/mm)__________________________________________________________________________1. Non-scintillating 5 1.0 27 1.0 9-10 fiber optic with Gd2O2S:Tb (50 mg/cm.sup.2)2. Scintillating fiber 7 0.6 .sup. 85.sup.5 0.66 10-11 optic.sup.4, no mirror, no phosphor over- coat3. Scintillating fiber 6.4 0.6 .sup. 85.sup.5 1.24 10-11 optic with mirror coating (Al)4. Scintillating fiber 7 0.6 92 1.78 10-11 optic with Gd2O2S:Tb (50 mg/cm.sup.2)5. Non-scintillating 5 0.6 27 0.85 9-10 fiber optic with Gd2O2S:Tb (50 mg/cm.sup.2)6. Non-scintillating 5 1.0 18 8.09 3-3.5 fiber optic with (ZnCd)S:Ag, Cu (100 mg/cm.sup.2)7. Scintillating fiber 7 0.6 90 9.02 5-6 optic with (ZnCd)S:Ag, Cu (100 mg/cm.sup.2)__________________________________________________________________________ .All data at 70 kV with an Aluminum HVL of 2 mm for an exposure of 100 mR .X ray sensors coupled via DowCorning Optical grease # Q23067 .Low noise CCD with onchip integration used. .All Xray exposures taken with Kevex 160 Microfocus Xray source .sup.1 NA = (N.sub.2.sup.2 -N.sub.1.sup.2).sup.1/2 where: N.sub.1 = Refractive index of the cladding material N.sub.2 = Refractive index of the core material .sup.2 Absorption efficiency computed for monochromatic 70 kV xrays. A (% = 1- exp (-.mu.x). Attenuation coefficent computed using Harmonex Xray, 1992. .sup.3 Spatial resolution maximum for this camera system is 10-11 lp/mm based on the demagnificaztion of the 15 .mu.m pixels by the 1:3.31 taper resulting in an effective pixel size of .about.50 .mu.m at the input to the taper, or .about.10 lp/mm. .sup.4 Based on U.S. Pat. No. 5,122,671 .sup.5 The scintillating glass in this thickness absorbs 100% of the xray energy, however the thin cladding is inactive and reduces the effective absorption efficiency

The use of a scintillating fiber optic (SFO) without any overcoatings (sample 2) provides improved spatial resolution, improved x-ray absorption efficiency, but a lower light level than the more efficient crystalline phosphor screen. However, light escaping out the back of the device can be harnessed with the use of a mirror (sample 3) in order to effectively channel the light back towards the CCD. This results in no detectable change in the spatial resolution but provides an improvement over the uncoated configuration by nearly a factor of 2.

The SFO sensor (sample 3) is nearly 25% brighter than the phosphor screen, sample 1.

Sample 4, an example of the use of the present invention, provides further gains over the phosphor/non-scintillating configuration (sample 1), the SFO configurations with no coatings (sample 2), and with the mirror coating (sample 3). In this case the spatial resolution remains high, but the relative brightness jumps to 1.78 with a combined absorption efficiency of 92%. In this case the brightness improvement of the popular phosphor alone configuration is 78%. The brightness enhancement over the mirror backed SFO configuration is 43%. This indicates that the use of the hybrid luminescent device of the present invention will provide at least another 43% improvement in dose efficiency or dose reduction over prior technology under these x-ray conditions.

It should be noted that the SFO has a numerical aperture (N.A.) of 0.6. The impact of using a smaller N.A. is that the acceptance angle of light into and out of the plate is smaller than that of a fiber optic with a numerical aperture of 1.0. This means that light from a more remote location in the deposited phosphor will enter a fiber with the 1.0 N.A. fiber optics plate than with the 0.6 N.A. fiber optics plate. The higher resolution of the SFO further biases the combined spatial resolution of the hybrid luminescent device toward higher values.

In this invention, comparable or higher light levels can be obtained from a smaller N.A. fiber optics component (as shown in sample 4, Table 1) and also provide higher spatial resolution and improved modulation through the resolution pattern used over that of the faster non-scintillating fiber optic/phosphor configuration.

Sample 5 shows what the relative brightness levels would be if the phosphor were deposited onto a non-scintillating fiber optics plate that has an equivalent N.A. to the SFO of sample 4. Note that there is a reduction in the relative brightness in relation to the higher speed fiber optics plate in sample 1 and the resolution does not improve as it does in the present invention, sample 4.

It should be noted that the spatial resolution of this configuration can be increased by using smaller CCD pixels, or by using a nonscintillating fiber optics taper with a smaller demagnification or by using a nonscintillating fiber optics taper with no magnification at all (concerning the latter, see Table 4). Using a configuration where there is only a N.A.=1.0 straight (non-tapered, no demagnification) fiber optics conduit attached to a CCD containing 25 .mu.m.times.25 .mu.m pixels, the inventors detected, very high modulation at 14.3 lp/mm through a 14.3 lp/mm lead filled alternating density pattern at 70 kV with the new invention using sample 4 (Table 1). There was virtually no modulation through this same pattern using sample 1 of Table 1. Therefore, if sample 1 and sample 4 were each placed onto a similar CCD directly, i.e. with no interfering fiber optic, sample 4 would provide a higher spatial resolution and higher image contrast due to a smaller light spread onto the CCD and the contribution of the high resolution light produced from the SFO. So in the direct coupling of phosphor coated fiber optics, the present invention will provide not only increased light levels (in most cases and especially at higher energies), but also more directivity into single pixels due to its lower N.A., and the contribution to high resolution from the SFO part of the device.

As stated above, the higher numerical aperture of sample 1 results in a higher exit angle which results in light diffusion into remote pixels. Since there is more stray light from the higher N.A. sample, sample 1, in relation to the invention, sample 4, the average CCD intensity from sample 1 increases in relation to sample 4 when the respective samples are attached directly to a CCD or through a straight fiber optics component with a N.A.=1. In these cases, these devices accept the higher angle of light, substantially prevalent in sample 1 (in relation to sample 4) that increases the corresponding CCD pixel value in relation to sample 4. This light is transferred into adjacent fibers or pixels. Even though there is increased light in relation to the invention when moving to a faster optical system, the present invention (sample 4) still has a higher modulation transfer function and a higher spatial resolution. As stated, this is visibly and quantitatively apparent in practice. The fiber optics taper, which has a smaller acceptance angle than a straight fiber optics conduit or CCD rejects some of the stray light from the higher N.A. material, sample 1. As a result, the difference in light levels increases and sample 4 now becomes much brighter than the sample 1 approach.

In general, the light level increase for the invention will be much greater than other phosphor configurations on higher N.A. fiber optics as the acceptance angle of the optics decreases. For example, lens optics typically have more restricted acceptance angles than fiber optics for a given field of view. Therefore, for a given field of view, a lens will collect, by as much as a factor of 10, less light than a fiber optic component.

Further gains in spatial resolution can be obtained as the x-ray energy is decreased for any configuration with the use of this invention. This can be realized since the phosphor layer can be made thinner to absorb an equivalent amount of radiation. For applications such as mammography, it may be required to go to smaller CCD pixels in order to fully exploit the spatial resolution that can be obtained from this system. With a thin deposition of phosphor onto the SFO, i.e., on the order of 10 .mu.m, the inventors have measured better the 20 lp/mm spatial resolution. An estimate of 10% modulation through the line pattern was observed with this configuration at 40 kV.

EXAMPLE 2

As is the conventional approach in prior art x-ray screens, thicker phosphor screens are used to more effectively absorb the penetrating radiation as the radiation energy is increased. However, with the present invention, the phosphor layer need not be made thicker since the SFO will provide all the x-ray absorption efficiency required. However, the use of thicker phosphor screens in combination with an SFO can provide further and substantial increases in brightness and improvements in spatial resolution over the use of the phosphor alone or even with most practical non-scintillating fiber optics.

An example of the use of a thick phosphor screen in combination with a SFO is shown in samples 6 and 7 (Table 1) and samples 11 and 13 (Table 2). In these cases, large increases in brightness can be obtained from the low resolution screen. This brightness can be augmented by the use of the SFO in combination with the low resolution screen. In this case the brightness increases by 5-10% at 70 kV (see Tables 1 and 2), but this % increase goes up by approximately 40% under 160 kV x-rays using a beam of the kind typically employed in nondestructive inspections (see Table 2). It is also interesting to note that the spatial resolution goes up for the (ZnCd) S:Ag,Cu screen with the use of the present invention (see Table 1, sample 7 and Table 2, sample 13). Incrementally thinner depositions of this very bright screen may make the combination of the SFO and this phosphor a very attractive approach for the medical imaging industry. A thin screen of this material is now not typically used because it will have an unacceptably low absorption efficiency as compared to the commonly used Gd.sub.2 O.sub.2 S:Tb or gadolinium oxysulfide (GOS) screens of comparable thickness.

Sample 8 is a reference material similar to that of sample 1. Table 2 provides data as the x-ray energy is increased. Sample 9 is an example of the present invention, similar to that tested in sample 4. Note that the repeat measurement of this sample results in a value similar to that shown for sample 4 in Table 1. Importantly, the improvement in brightness at 70 kV increases to 2.57 at 160 kV.

Sample 10 shows an example of the prior art. Note that this phosphor is composed of a thicker deposition of the same phosphor material as samples 8 and 9 and subsequently produces a much higher signal. The invention, sample 11, shows an improvement from 1.22 at 70 kV to 1.44 at 160 kV. The spread in light levels is not as high as in the first case since this phosphor material is thicker and more absorbing of these x-ray beams than the thinner phosphor screen. More importantly is the improvement in spatial resolution of sample 11, the invention, in relation to the prior art.

As already discussed, the improvement in light output for the (ZnCd) S:Cu,Ag material, samples 12 vs 13, is not as pronounced because of the high phosphor layer thickness of this material. It should be noted with regard to sample 12 that as the x-ray energies are increased, the relative brightness levels decrease in relation to the GOS material. This is consistent with the lower absorption characteristics of the lower effective atomic number phosphor. However, the present invention as illustrated in sample 13 buffers this decrease with improved absorption efficiency and corresponding conversion through the SFO. For example, sample 13 remains at least 6.5 fold brighter than the reference material at all energies.

TABLE 2__________________________________________________________________________Brightness of Fiber Optic/Phosphor Combinations as a Function of X-RayEnergy..sup.1 Spatial Resolution X-Ray EnergySampl Fiber Optic Phosphor at 70 kV (lp/mm) 70 kV 120 kV 160 kV__________________________________________________________________________ 8 1.0 NA non- Gd.sub.2 O.sub.2 S:Tb 9-10 1.00 1.00 1.00 scintillating FO 50 mg/cm.sup.2 9 0.6 NA Gd.sub.2 O.sub.2 S:Tb 10-11 1.87 2.29 2.57 Scintillating FO 50 mg/cm.sup.210 1.0 NA non- Gd.sub.2 O.sub.2 S:Tb 6-6.5 3.46 3.50 3.67 scintillating FO 100 mg/cm.sup.211 0.6 NA Gd.sub.2 O.sub.2 S:Tb 6.5-7 4.23 4.83 5.30 Scintillating FO 100 mg/cm.sup.212 1.0 NA non- (Zn Cd)S:Ag, Cu 3-3.5 6.68 5.35 4.81 scintillating FO 100 mg/cm.sup.213 0.6 NA (Zn Cd)S:Ag, Cu 5.8-6.3 7.03 6.75 6.59 Scintillating FO 100 mg/cm.sup.2__________________________________________________________________________ .All xray exposures taken with Kevex 160 Microfocus xray unit at energies listed .Coupling grease, CCD camera, N.A. and Spatial Resolution Information as in Table 1. .Scintillatinq Fiber Optic Based on U.S. Pat. No. 5,122,671 .sup.1 Beam Filtration: 70 kV: 2 mm pure aluminum 120 kV: 4 mm pure aluminum 160 kV: 8 mm pure aluminum

FIG. 4 graphically shows the trends of the invention and the prior art for the examples in Table 2. In the various embodiments of the invention (samples 9, 11, and 13), there is an increasing gap in brightness as the energy is increased in relation to the prior art devices of Samples 8, 10 and 12, respectively. This graph shows that this gap would continue to decrease at energies below 70 kV.

Regarding the generally adverse effect of increasing radiation energies on spatial resolution of connected luminescent devices, a scintillating fiber optics will also experience lower spatial resolution as the energy is increased if the fibers are not aligned with the cone beam of x-rays arriving at the hybrid structure. A focused scintillating fiber optics (i.e. where the glass fibers are directed back toward the focal spot) can reduce the spatial resolution loss from the SFO.

It should be noted that the use of a thinner phosphor layer with the SFO may produce a comparable or acceptable signal level and enhanced spatial resolution in relation to a faster, phosphor screen on a non-scintillating fiber optic. Conversely, a combination of the SFO with a thicker phosphor screen can offer substantial improvements in light output with very acceptable values of spatial resolution and as such can enable the use of the thicker (brighter) screen in applications previously believed to require thinner higher resolution phosphor screens.

During this investigation, we also discovered that the use of an optical coupling fluid between the phosphor layer and the fiber optics increases the spatial resolution by around 10-20% with a concomitant loss in brightness of about 25%. The use of an optical coupling fluid to further enhance spatial resolution should therefore be weighed against the required speed and exposure of the application. It should be noted that the brightness and the spatial resolution both increase with the use of the appropriate optical coupling fluid between fiber optic components, i.e., the SFO and a non-scintillating fiber optic or between the SFO and a CCD.

EXAMPLE 3

The results of Table 1 and Table 2 as described above involve coupling various combinations to a CCD with a preinstalled non-scintillating fiber optics taper placed as a light input to the CCD. Table 3 provides a configuration where the phosphor is directly attached to the taper.

TABLE 3__________________________________________________________________________Brightness and Spatial Resolution of Fiber Optic/Phosphor Combinations asFunction of X-Ray Energy..sup.1 Spatial Resolution Brightness (DN/mR) (lp/mm)Sampl Fiber Optic Coating or screen 70 kV 120 kV 160 kV 70 kV 120 kV 160 kV__________________________________________________________________________14 Bare Taper Gd.sub.2 O.sub.2 S:Tb 17.1 24.6 16.2 9 7.5 7.5 50 mg/cm.sup.215 0.6 NA Gd.sub.2 O.sub.2 S:Tb 23.3 53.4 45.6 9 8 6 Scintillating 50 mg/cm.sup.2 FO16 0.6 NA none 8.5 28.4 27.5 9 7.5 6 Scintillating FO17 0.6 NA mirror 15.3 50.4 48.3 10.5 9.5 9 Scintillating FO__________________________________________________________________________ Data collected in accordance with footnote 2. .sup.1 Beam Filtration: 70 kV: 2 mm pure Aluminum 120 kV: 19 mm pure Aluminum, 1.3 mm Copper 160 kV: 19 mm pure Aluminum, 2.9 mm Copper

This coupling configuration simulates an actual phosphor CCD coupling configuration in that a number of commercial systems, some currently in the field of mammography, are based on attaching a high resolution phosphor directly to such a taper.

FIG. 5 shows in graphical form the response of those values in Table 3 and further illustrates the improvement in light output that can be obtained by using the hybrid luminescent device of the present invention. From inspection of the curves in FIG. 5, it becomes readily apparent to those skilled in the art that the thicker SFO plates as used in both the present invention and in prior art will capture an increasingly greater number of x-ray photons and subsequently convert more of these captured photons into light than is achieved by the prior art phosphor screens alone. It is also apparent that the hybrid luminescent device of the present invention is brighter than all combinations at the critical lower energy range frequently used in medical imaging. Table 4 also shows that the resolution remains high for this hybrid device across the energy range studied.

EXAMPLE 4

When coupling removable luminescent devices (i.e., such as a screen fiber optics face plate or a phosphor screen) directly onto a CCD for testing purposes, there is always a risk when applying or removing the luminescent device that the CCD will suffer damage by either abrasion or by some other mechanical defect such as a broken wire bond. The experiments of this example and which are described in Table 4 below provide data where some other fiber optics component is already attached to the CCD in order to avoid damage to the CCD and to maintain consistency of performance of the device for various tests.

TABLE 4__________________________________________________________________________Brightness and Spatial Resolution Results of Fiber Optic/PhosphorCombinationsas a Function of X-Ray Energy.sup.1 Spatial Resolution BrightnessSampl Fiber Optic Coating or screen at 70 kV (lp/mm) 70 kV 120 kV 160 kV__________________________________________________________________________A. High Resolution Phosphor Configurations18 1.0 NA non- Gd.sub.2 O.sub.2 S:Tb 9.5 1.00 1.00 1.00 scintillating FO 50 mg/cm.sup.219 0.6 NA non- Gd.sub.2 O.sub.2 S:Tb 13 0.48 0.52 0.59 scintillating FO 50 mg/cm.sup.220 0.6 NA Gd.sub.2 O.sub.2 S:Tb 16 0.79 1.51 2.21 Scintillating FO 50 mg/cm.sup.221 0.6 NA none 21 0.29 0.88 1.43 Scintillating FO22 0.6 NA mirror 18 0.53 1.44 2.25 Scintillating FOB. High Output Phosphor Configurations23 1.0 NA non- Gd.sub.2 O.sub.2 S:Tb 5 4.54 3.94 3.96 scintillating FO 100 mg/cm.sup.224 0.6 NA non- Gd.sub.2 O.sub.2 S:Tb 8 1.87 2.13 2.40 Scintillating FO 100 mg/cm.sup.225 0.6 NA Gd.sub.2 O.sub.2 S:Tb 10 1.88 2.86 3.64 Scintillating FO 100 mg/cm.sup.2__________________________________________________________________________ .sup.1 Philips 160 kV xray source. A 2048 .times. 2048 CCD chip that is used. A permanently bonded N.A. = 1.0 image conduit fiber optic plate is attached to the CCD. DowCorning # Q23067 for coupling. 70 kV: 2 mm pure Aluminum; 120 kV: 19 mm pure Aluminum, 1.3 mm Copper 160 kV: 19 mm pure Aluminum, 2.9 mm Copper

Table 4 shows the response of the hybrid luminescent device input into the CCD via a straight 1.0 N.A. fiber optics conduit (6 .mu.m fiber diameter) attached to a CCD. In some cases this is more of a direct analogy to coupling these devices directly to the CCD. Again, if the input to the conduit is viewed by a CCD, then the phosphor would have to be coupled through a shielding fiber optics as shown in Table 4. Two types of non-scintillating fiber optics coupling units are presented in Table 4 as are two types of phosphor screen systems. There is a coupling unit with N.A.=1.0 and a second with N.A.=0.6. Data for a high resolution and a high output set of phosphor configurations is provided and compared to the hybrid analogs. Mirror backed scintillating fiber optics data is provided for comparison.

The results in Table 4 show that dramatic improvements are possible in spatial resolution when a 0.6 N.A. fiber optics face plate is placed between a phosphor and the CCD. As stated earlier, a non scintillating fiber optics face plate is required to assure that the CCD and other detection devices is properly shielded from direct radiation. Table 4 shows that an SFO can improve both the resolution over the non-scintillating 0.6 N.A. fiber optic and the 1.0 N.A. non-scintillating fiber optic. Furthermore, Table 4 shows that the present invention will enhance the light output or brightness at all energies listed over the 0.6 N.A. non-scintillating fiber optic and above and is competitive with the 1.0 N.A. non-scintillating fiber optic which captures a larger portion of stray light than the 0.6 N.A. fiber optics. In this case, the 1.0 N.A. non-scintillating fiber optic is showing higher levels than in the previous taper experiments since the CCD captures more of this light through the high speed conduit (which simulates coupling to the bare CCD).

Furthermore, Table 4 shows that if the spatial resolution of about 10 lp/mm is adequate, than this can be achieved by use of a much thicker phosphor screen (100 mg/cm.sup.2) coupled to the SFO but with nearly a factor of 2 improvement in brightness. These values improve to nearly a factor of 4 at 160 kV without degradation in the spatial resolution of the image.

Table 4 also demonstrates that there are gains to coupling the heavier loaded (100 mg/cm.sup.2) phosphor to the SFO in terms of brightness or resolution over coupling this same phosphor to the 0.6 N.A. non-scintillating fiber optics shown.

EXAMPLE 5

The performance characteristics for the hybrid luminescent device was also studied for use as an electron scintillator for transmission electron microscopy (TEM) in terms of brightness in the electron energy range of 100-400 keV.

The SFO face plate tested contains 6-.mu.m fibers. The piece tested for this study was made without EMA. A piece measuring 57 mm.times.39 mm.times.7.5 mm was used for the measurements of brightness. To test the effect of phosphor coating on the brightness, the plate surface facing the incident electrons was coated with a 17-.mu.m layer of a Zinc-Cadmium Sulfide, silver doped phosphor ((ZnCd)S:Ag), referred to herein as a green "P20 phosphor". The entire surface was then coated with a thin layer of aluminum for charge conduction and light reflection.

The measurement setup is schematically shown in FIG. 6. The above prepared SFO plate is placed on a leaded glass window which seals the microscope vacuum and provides x-ray shielding. To avoid Newton rings, which have been observed due to the small, irregular gap between the SFO and the glass window, a piece of aluminum foil, 18.+-.2 .mu.m thick, with a cut-out window was used to support the SFO. The gap thus created was much greater than the light wavelength (550 nm) involved, thereby Newton rings are completely eliminated. Two Nikon lenses, one with a focal length of 24 mm and an f-number of 2.8, the other 85 mm and f2,0, were used face-to-face to relay the image to a CCD chip. Focusing rings on both lenses are set to infinity, and apertures were set all the way open. The theoretical magnification of such a lens configuration is the focal length ratio of the two lenses, i.e. 85/24=3.54.times.. Actual measurement using a USAF 1951 test pattern gives a magnification of .times.3.46.+-.1%. A Photometrics CCD camera and a Macintosh computer were used to acquire and analyze images. The camera head was type CH250 and the CCD chip was a Kodak KAF-4200 with 2k.times.2k pixels and a pixel size of 9 .mu.m.times.9 .mu.m.

FIG. 7 shows the relative brightness of the SFO with the 17 .mu.m P20 phosphor coating (curve 1) at electron energies ranging form 100 to 400 keV at 25 keV increments, on a JEOL-4000EX microscope. The vertical axis is the image mean intensity, obtained by maintaining uniform illumination of constant beam current of 100 pA/cm.sup.2 for all voltages at the microscope small focusing screen. The exposure time was 60 seconds for all images. For comparison, curve 2 and curve 3 show the brightness of a 20 .mu.m-P20 phosphor on glass (i.e. without the SFO) and an uncoated SFO (without the phosphor), respectively, measured under identical conditions as for curve 1.

The relative brightness data for the above three combinations is summarized below in Table 5 with the P20 phosphor on glass normalized to 1 at 4 select electron beam energies.

TABLE 5__________________________________________________________________________Brightness of Fiber Optic/Phosphor Combinationsas a Function of Electron Beam Energy Relative Brightness Levels at the given electron beam energiesSampl Substrate Phosphor 100 kV 200 kV 300 kV 400 kV__________________________________________________________________________26 Clear Glass Disc P-20* phosphor, 1.00 1.00 1.00 1.00 20 .mu.m thickness 0.6 NA P-20 phosphor, 1.1 1.7 2.5 3.127 Scintillating FO 17 .mu.m thickness__________________________________________________________________________ *P-20 is (ZnCd)S:Ag

The photon output of the SFO, without phosphor coating (i.e. curve 3, FIG. 7), increased linearly with the energy of the incident electrons, but was about 20-40% that of the combined phosphor and SFO screen (curve 1) for the entire energy range tested. With a 17-.mu.m layer of P20 phosphor coating, the SFO is brighter than the 20-.mu.m layer of phosphor coating on glass for the entire energy range tested. The invention shows a decrease in brightness from 100 to 300 keV, but becomes less so in the range 300 to 400 keV, and is expected to flatten-out and increase after that, as the brightness of the SFO becomes dominant.

Table 5 demonstrates that this invention has value in improving the detection of electron beams. Note that the thinner phosphor material on the SFO provides nearly a factor of 3 improvement in light output at 400 keV electron energy than the same phosphor on a piece of glass. (Note: this data was collected via lens coupling to a CCD camera. The transmission of the glass plate used as sample 26 is expected to provide at least the same, if not better transmission of light produced in the phosphor than the use of a 1.0 N.A. fiber optics plate). The drawback of the clear glass plate in systems design is that there is severe spatial resolution degradation if this plate is coupled directly to a CCD or through a fiber optics window. These examples show the importance of the absorption powers of the SFO even for an electron beam which has a smaller penetration range than an x-ray beam for an equivalent energy.

While we have illustrated and described the preferred embodiments of our invention, it is to be understood that these are capable of variation and modification, and we therefore do not wish to be limited to the precise details set forth, but desire to avail ourselves of such changes and alterations as fall within the purview of the following claims.

Claims

1. A hybrid luminescent device for converting penetrating or ionizing radiation into light that can be detected by an electronic or film recording medium and which provides high luminescence output, high radiation absorption efficiency and high spatial resolution irrespective of radiation energy levels, the hybrid luminescent device comprising:

a) a fiber optics scintillator including an entrance face and an exit face, said exit face is adapted for coupling to a light detection device for image recordation, said fiber optics scintillator formed from a non-crystalline amorphous substance and characterized as having:

i) a first radiation absorption efficiency;

ii) a first brightness value;

iii) a first spatial resolution value;

b) a phosphor layer disposed on said entrance face of said fiber optics scintillator, said phosphor layer characterized as having:

i) a second radiation absorption efficiency lower than the first radiation absorption efficiency of said fiber optics scintillator;

ii) a second brightness value higher than the first brightness value of said fiber optics scintillator;

iii) a second spatial resolution value lower than the first spatial resolution value of said fiber optics scintillator; and wherein

c) the hybrid luminescent device exhibits:

i) a third radiation absorption efficiency higher than the first radiation absorption efficiency of said fiber optics scintillator;

ii) a third brightness value higher than a combined total of the first and second brightness values of said fiber optics scintillator and phosphor layer, respectively; and

iii) a third spatial resolution value about that of the first spatial resolution value of said fiber optics scintillator.

2. The invention as defined in claim 1 wherein said phosphor layer comprises a gadolinium oxysulfide rare earth material.

3. The invention as defined in claim 2 wherein said fiber optics scintillator comprises luminescent terbium-activated borate glass material.

4. The invention as defined in claim 3 wherein the radiation to be converted is x-ray radiation and wherein the hybrid luminescent device provides a radiation absorption efficiency in a range from about 90% to about 100% and a spatial resolution of at least 5 lp/mm.

5. The invention as defined in claim 2 wherein said fiber optics scintillator comprises luminescent terbium-activated silicate glass material.

6. The invention as defined in claim 5 wherein the radiation to be converted is x-ray radiation and wherein the hybrid luminescent device provides a radiation absorption efficiency in a range from about 90% to about 100% and a spatial resolution of at least 5 lp/mm.

7. The invention as defined in claim 2 wherein said fiber optics scintillator comprises cerium-activated, lithium enriched luminescent glass material.

8. The invention as defined in claim 7 wherein the radiation to be converted is x-ray radiation and wherein the hybrid luminescent device provides a radiation absorption efficiency in a range from about 90% to about 100% and a spatial resolution of at least 5 lp/mm.

9. The invention as defined in claim 1 wherein said phosphor layer comprises a zinc-cadmium sulfide, silver- and copper-doped ((ZnCd)S:Ag,Cu) phosphor material.

10. The invention as defined in claim 9 wherein said fiber optics scintillator comprises luminescent terbium-activated borate glass material.

11. The invention as defined in claim 10 wherein the radiation to be converted is x-ray radiation and wherein the hybrid luminescent device provides a radiation absorption efficiency in a range from about 90% to about 100% and a spatial resolution of at least 5 lp/mm.

12. The invention as defined in claim 9 wherein said fiber optics scintillator comprises luminescent terbium-activated silicate glass material.

13. The invention as defined in claim 12 wherein the radiation to be converted is x-ray radiation and wherein the hybrid luminescent device provides a radiation absorption efficiency in a range from about 90% to about 100% and a spatial resolution of at least 5 lp/mm.

14. The invention as defined in claim 9 wherein said fiber optics scintillator comprises cerium-activated, lithium enriched luminescent glass material.

15. The invention as defined in claim 14 wherein the radiation to be converted is x-ray radiation and wherein the hybrid luminescent device provides a radiation absorption efficiency in a range from about 90% to about 100% and a spatial resolution of at least 10 lp/mm.

16. The invention as defined in claim 1 wherein said phosphor layer comprises a zinc-cadmium sulfide, silver-doped ((ZnCd)S:Ag) phosphor material.

17. The invention as defined in claim 16 wherein said fiber optics scintillator comprises luminescent terbium-activated borate glass material.

18. The invention as defined in claim 17 wherein the radiation to be converted is electron radiation in a range of about 100-400 keV.

19. The invention as defined in claim 16 wherein said fiber optics scintillator comprises luminescent terbium-activated silicate glass material.

20. The invention as defined in claim 19 wherein the radiation to be converted is electron radiation in a range of about 100-400 keV.

21. The invention as defined in claim 16 wherein said fiber optics scintillator comprises cerium-activated, lithium enriched luminescent glass material.

22. The invention as defined in claim 21 wherein the radiation to be converted is electron radiation in a range of about 100-400 keV.

23. A hybrid luminescent device for converting penetrating or ionizing radiation into light that can be detected by an electronic or film recording medium and which provides high luminescence output, high radiation absorption efficiency and high spatial resolution irrespective of radiation energy levels, the hybrid luminescent device comprising:

a) a fiber optics scintillator including an entrance face and an exit face, said exit face is adapted for coupling to a light detection device for image recordation, said fiber optics scintillator formed from a non-crystalline amorphous substance and characterized as having:

i) a first radiation absorption efficiency;

ii) a first brightness value;

iii) a first spatial resolution value;

b) a phosphor layer disposed on said entrance face of said fiber optics scintillator, said phosphor layer characterized as having:

i) a second radiation absorption efficiency lower than the first radiation absorption efficiency of said fiber optics scintillator;

ii) a second brightness value;

iii) a second spatial resolution value lower than the first spatial resolution value of said fiber optics scintillator; and wherein:

c) the hybrid luminescent device exhibits:

i) a third radiation absorption efficiency higher than the first radiation absorption efficiency of said fiber optics scintillator;

ii) a third brightness value higher than a highest one of the first and second brightness values of said fiber optics scintillator and phosphor layer, respectively; and

iii) a third spatial resolution value about that of the first spatial resolution value of said fiber optics scintillator.

24. The invention as defined in claim 23 wherein said phosphor layer comprises a gadolinium oxysulfide rare earth material.

25. The invention as defined in claim 24 wherein said fiber optics scintillator comprises luminescent terbium-activated borate glass material.

26. The invention as defined in claim 24 wherein said fiber optics scintillator comprises luminescent terbium-activated silicate glass material.

27. The invention as defined in claim 24 wherein said fiber optics scintillator comprises cerium-activated, lithium enriched luminescent glass material.

28. The invention as defined in claim 23 wherein said phosphor layer comprises a zinc-cadmium sulfide, silver- and copper-doped ((ZnCd)S:Ag,Cu) phosphor material.

29. The invention as defined in claim 28 wherein said fiber optics scintillator comprises luminescent terbium-activated borate glass material.

30. The invention as defined in claim 28 wherein said fiber optics scintillator comprises luminescent terbium-activated silicate glass material.

31. The invention as defined in claim 28 wherein said fiber optics scintillator comprises cerium-activated, lithium enriched luminescent glass material.

32. The invention as defined in claim 23 wherein said phosphor layer comprises a zinc-cadmium sulfide, silver-doped ((ZnCd)S:Ag) phosphor material.

33. The invention as defined in claim 32 wherein said fiber optics scintillator comprises luminescent terbium-activated borate glass material.

34. The invention as defined in claim 32 wherein said fiber optics scintillator comprises luminescent terbium-activated silicate glass material.

35. The invention as defined in claim 32 wherein said fiber optics scintillator comprises cerium-activated, lithium enriched luminescent glass material.