This application claims priority from Japanese Patent Application No. JP2004-016126, filed Jan. 23, 2004, the entire disclosure of which is incorporated herein by reference.
This invention relates to a magnetic head mounted in a magnetic recording system, more specifically to a magnetoresistive head and a fabricating method thereof to read information recorded on a magnetic recording medium.
Recently, a GMR (Giant Magnetoresistive) head using a so-called “spin valve”, which has a basic configuration consisting of magnetic layer/nonmagnetic conductive layer/magnetic layer/antiferromagnetic layer as written in JP-A 358310/1992, has been widely adopted for a magnetoresistive head mounted in a magnetic recording system as a read sensor. In the spin valve, a magnetic film in which the magnetization direction is pinned in one direction by magnetic exchange coupling with an antiferromagnetic film is called a pinned layer. On the other hand, another magnetic layer is called a free layer because the magnetization direction can be changed in response to an external field.
A GMR head using a spin valve transduces a magnetic signal to a voltage change or a current change by using the phenomenon in which the electrical resistivity changes according to the angle of magnetization between the pinned layer and the free layer. Therefore, it is most important that the magnetization direction of the pinned layer be fixed unidirectionally (concretely, the direction perpendicular to the magnetic recording medium) when making the spin valve function as a magnetic sensor. That is, it is necessary that the magnetic field required to reverse the magnetization of the pinned layer (which corresponds to a magnetic exchange coupling field given by the antiferromagnetic layer) be controlled to be sufficiently larger than the signal field from the magnetic recording medium, the leakage field from the write head, and so on. Moreover, considering the annealing process during magnetic head fabrication and the operating environmental temperature of the head, the thermal stability of the magnetic exchange coupling field, which is imparted to the pinned layer from the antiferromagnetic layer, also becomes an important factor.
Currently, a large magnetic exchange coupling field can be obtained, and, because of their excellent thermal stability, alloys designated by Mn-M1 containing about 50 at % Mn (where M1 is a noble metal such as Pt etc.) have come into mainstream use for the antiferromagnetic film. These materials do not impart a magnetic exchange coupling field to the pinned layer on the as-deposited spin valve. This is because a Mn-M1 alloy is a disordered alloy having an FCC structure as-deposited and does not exhibit antiferromagnetism. In the case where a magnetic exchange coupling field is imparted to the pinned layer, it is generally necessary to apply annealing under magnetic field. It is known that a Mn-M1 alloy phase-transforms to an ordered alloy having a Cu—Au I type structure by annealing at a temperature around 230° C.˜270° C., and becomes antiferromagnetic. Additionally, while the annealing is carried out in a magnetic field, the pinned layer exchange-couples with the antiferromagnetic layer unidirectionally and can pin the magnetization direction. That is, in the case where a Mn-M1 alloy is used for the antiferromagnetic film to control the magnetization direction of the pinned layer, an annealing step in a magnetic field is necessary to obtain a large magnetic exchange coupling field and an excellent thermal stability.
In general, it is preferable that the upper and lower shields which are placed sandwiching the spin valve in the direction of the film thickness, the free layer being one component of the spin valve, and the magnetic pole at the write head have magnetization directions controlled to be the in direction of the track width which is perpendicular to the magnetization of the pinned layer (the direction perpendicular to the magnetic recording medium). Therefore, there is a concern that annealing in a magnetic field to control the magnetization direction of the pinned layer affects the above-mentioned other magnetic layers, specifically the magnetization direction of the free layer. If the magnetization direction of the free layer is shifted from the desired the track width direction, problems arise such as destroying the symmetrical nature of the response characteristics relative to an external field and not being able to obtain excellent reading characteristics. Therefore, it is necessary to pay close attention to control the magnetization direction between the pinned layer and the free layer to be orthogonal.
Moreover, because a Mn-M1 alloy (where M1 is a noble metal such as Pt, etc.) needs a film thickness of at least about 10˜20 nm, one expects there to be a disadvantage in terms of making the distance between the upper and lower shields narrower with increasing recording density.
As another means to pin the magnetization direction of the pinned layer, a configuration of a pinned layer is disclosed in the patent document JP-A 7235/1996, in which a pinned layer configuration not using an antiferromagnetic layer is described consisting of a magnetic layer/antiferromagnetic coupling layer/magnetic layer which is so-called “self-pinned”. Moreover, in the patent documents JP-A 57538/2000 and JP-A 251224/2000, a configuration is disclosed in which a hard magnetic material is used as one of the above-mentioned magnetic layers in order to pin the magnetization of the “self-pinned” pinned layer more strongly. In this configuration, the annealing process in field is not necessary to obtain magnetic exchange coupling with the antiferromagnetic layer. Additionally, because there is no antiferromagnetic layer, the total film thickness of the spin valve can be made thinner, with the resultant advantage that the gap between the upper and lower shields can be made narrower. However, there is no detailed description concerning the direction control of the magnetization of the pinned layer and free layer presented above, and there is no guarantee of normal operation after the thermal and magnetic histories during fabrication of a magnetic head.
Moreover, it is necessary to apply a longitudinal biasing field to a GMR head using a spin valve to give a multi-domain structure to the free layer to keep out Barkhausen noise created when a free layer becomes a multi-magnetic domain structure. A longitudinal biasing method is disclosed in the patent document JP-A 57223/1995, in which a hard magnetic material or a laminated layer of a magnetic layer and an antiferromagnetic layer is placed at both sides of the spin valve and a longitudinal biasing field is applied to the free layer to make it a single domain structure. In particular, the former is called a hard-bias structure, and it has become the mainstream of present GMR head structures.
The hard-bias structure is effective in keeping out Barkhausen noise. On the other hand, it is well known that the structure pins the magnetization of the free layer at the edges of the sensor and forms a so-called insensitive area. Because the magnetization direction of the free layer is hard to change in response to a signal field in the insensitive area, formation of the insensitive area substantially lowers reading sensitivity. Especially, this problem is expected to become more conspicuous with progressive narrowing of the track width and increasing occupation ratio of the insensitive area as the longitudinal recording density of magnetic recording systems increase in the future. Moreover, since the magnetization direction of the pinned layer is shifted due to a longitudinal biasing field caused by the hard magnetic material, there is concern that it will decrease reading output and affect the symmetry of the reading waveform.
If the longitudinal biasing field applied to the free layer is reduced by, for instance, thinning the film thickness of the hard magnetic material to solve these problems, the effectiveness of keeping out Barkhausen noise becomes inadequate. This means that keeping out Barkhausen noise and insuring reading sensitivity have a trade-off relationship, and it is difficult to satisfy both at the same time.
Another means to apply a longitudinal biasing field to the free layer is disclosed in the patent document JP-A 250205/2001, in which a laminated bias film consisting of laminated films of a bias nonmagnetic film/bias magnetic film/bias antiferromagnetic film is fabricated connected to the free layer after forming the spin valve consisting of an antiferromagnetic layer/pinned layer/nonmagnetic conductive film/free layer. In this configuration, the magnetization direction of the longitudinal biasing magnetic film is pinned by magnetic exchange coupling with the longitudinal biasing antiferromagnetic film. Moreover, a longitudinal biasing field can substantially be applied to the free layer by coupling the free layer with the longitudinal biasing magnetic layer magnetically or antiferromagnetically through the longitudinal biasing nonmagnetic film. In this case, one expects that there is an advantage that the longitudinal biasing field can be easily adjusted by controlling the film thickness of the longitudinal biasing nonmagnetic film. However, in this configuration, it is very difficult to produce an orthogonal array of the magnetization of the pinned layer and longitudinal biasing magnetic layer. That is, because two annealing steps in a magnetic field are necessary in which magnetization of the pinned layer is pinned in a direction perpendicular to the magnetic recording medium in the first step and magnetization of the longitudinal biasing magnetic film is pinned in the track width direction in the second step, a problem arises in which the magnetization direction of the pinned layer is shifted to the track width direction from a direction perpendicular to the magnetic recording medium after the second annealing step. In order to pin the magnetization of the pinned layer and longitudinal biasing magnetic film in orthogonal directions, it is necessary to trade-off the magnitude of the magnetic exchange coupling applied to either of the aforementioned magnetic films and their thermal stability. In this case, it may be very difficult to obtain reading characteristics with high reliability.
In the future, because of the reasons described above, one expects that reconciling guaranteed reading sensitivity and suppressed Barkhausen noise may become difficult to achieve in a hard-bias structure by progressive narrowing of the track width with increasing longitudinal recording density of magnetic recording systems. That is, in a hard-bias structure, it is virtually impossible to obtain reading characteristics which can be used for future magnetic recording devices with high recording density; therefore it is necessary to establish a new longitudinal biasing method. On the other hand, in an alternate longitudinal biasing method which is currently being proposed, controlling the magnetization direction of the layer applying a longitudinal biasing field to the pinned layer and free layer is difficult, thereby problems may arise such as decreased reading sensitivity and affected symmetry of the reading waveform. It is a common problem not only for next generation magnetoresistive heads such as a current CIP (Current in the plane)-GMR head, but also for a TMR (Tunneling Magnetoresistive) head and a CPP (Current perpendicular to the plane)-GMR head which are expected to be used in practice.
It is a feature of the present invention to provide a method for easily controlling the magnetization direction of a layer applying a longitudinal biasing field to the pinned layer and the free layer in a magnetoresistive head having a longitudinal biasing method in lieu of a hard-bias.
Representative features of the present invention disclosed in the patent application are summarized as follows. A “self-pinned” structure is used which can firmly pin the magnetization direction of the pinned layer without placing an antiferromagnetic film on the pinned layer, an annealing process in a magnetic field perpendicular to the magnetic recording medium is not necessary to control the magnetization direction, and an annealing process in a magnetic field in the track width direction and applying a magnetic field at room temperature are needed.
In further detail, the above-described features can be achieved by improving the following three points; (1) a mechanism to pin the magnetization direction of the pinned layer, (2) a device to apply a longitudinal biasing field to the free layer, (3) an apparatus to control the magnetization direction of the magnetic layer applying a longitudinal biasing field to the pinned layer and the free layer.
(1) As a way of pinning the magnetization direction of the pinned layer, the configuration of the pinned layer includes at least two magnetic layers, which are laminated though an antiferromagnetic coupling layer, and the adjoining magnetic layers form a laminated body coupling antiferromagnetically to each other.
At least one of the magnetic layers constituting the pinned layer may be composed of a hard magnetic material. Additionally, the saturation magnetic flux density and the film thickness of each magnetic layer constituting the pinned layer are controlled to make the substantial magnetic moment almost zero when the magnetization of each magnetic layer constituting the pinned layer is aligned in an antiparallel manner. As a result, the magnetization of the pinned layer does not easily reverse or rotate in response to the external field, and the magnetization direction can be substantially pinned. Forming a pinned layer while applying a magnetic field in a desired direction (that is, a direction perpendicular to the magnetic recording medium) and inducing uniaxial magnetic anisotropy makes it possible to control the magnetization direction of the pinned layer.
Additionally, in a magnetic head fabrication process, there are cases where the magnetization direction of the pinned layer is changed or the direction dispersed on a microscopic scale caused by various thermal and magnetic histories. However, the solution to the problems will be described in detail below (3).
(2) A way of applying a longitudinal biasing field to a free layer works by laminating a nonmagnetic separate layer/longitudinal biasing layer/antiferromagnetic layer on the opposite side of the nonmagnetic conductive layer or nonmagnetic tunneling barrier layer connected to the free layer.
It is preferable to induce uniaxial magnetic anisotropy applying a field in track width direction in the case of forming the free layer and the longitudinal biasing layer. The longitudinal biasing layer pins the magnetization direction in the track width direction by magnetic exchange coupling with the antiferromagnetic layer. At the edge of the track width direction of the magnetoresistive sensor, a longitudinal biasing field is applied in the track width direction by return of magnetic flux essentially from the longitudinal biasing layer to the free layer. Additionally, the effect can be enhanced by antiferromagnetically coupling the free layer and longitudinal biasing layer through the nonmagnetic separate layer. Since the magnitude of the longitudinal biasing field can be arbitrarily changed by selecting the magnetic moment of the longitudinal biasing layer and the material and film thickness of the nonmagnetic layer, it is possible to easily reconcile high reading sensitivity and suppressed Barkhausen noise. Moreover, materials and film thicknesses, which have a large magnetic exchange coupling with excellent thermal stability, are preferably adopted for the antiferromagnetic layer.
(3) A magnetization direction controlling method of the pinned layer and the magnetic film applying a longitudinal biasing field to the free layer is described as follows. Magnetization of the longitudinal biasing layer is set to be in the track width direction by annealing while applying a magnetic field in the track width direction after depositing of a magnetoresistive film comprising the pinned layer including a laminated body in which the adjoining magnetic layers are antiferromagnetically coupled to each other, a nonmagnetic conductive layer or nonmagnetic tunneling barrier layer, a free layer, a nonmagnetic separate layer, a longitudinal biasing layer, and an antiferromagnetic layer.
During the annealing process in a magnetic field, there is a possibility that the magnetization of the pinned layer is shifted from a desired direction, but the magnetization direction of the pinned layer can be aligned in the direction perpendicular to the magnetic recording medium by applying a magnetic field at room temperature after completing the annealing process. Even if the magnetization direction of the pinned layer is shifted from the direction perpendicular to the magnetic recording medium, it can be restored to the direction perpendicular to the magnetic recording medium by applying a static field at room temperature. The important thing herein is that it is possible to control the magnetization direction of the pinned layer to be in a desired direction even if a special treatment such as an annealing process in a magnetic field is not applied. That is, a step determining the magnetization direction of the pinned layer does not affect the magnetization direction of the free layer and the longitudinal biasing layer which applies a longitudinal biasing field to the free layer. Therefore, the magnetization directions of the pinned layer and the longitudinal biasing layer which applies a longitudinal biasing field to the free layer can be easily aligned in an orthogonal direction without interfering with each other.
Embodiments of the present invention achieve control of the magnetization direction of the pinned layer and a layer which applies a longitudinal biasing field to the free layer, and provide a magnetoresistive head and a manufacturing method thereof which can accomplish high reading sensitivity, suppression of Barkhausen noise, and excellent symmetry of a reading waveform even if there is progress in narrowing the track width.
The specific embodiments of the present invention will be described with reference to the accompanying drawings as follows. For the simplicity of understanding, the same symbols are allocated to the same parts in the following figures.
A magnetoresistive film 120 is formed on a substrate 100 after forming a lower shield 110, and the track width direction is patterned into a desired shape by photolithography, ion milling, or reactive ion etching. Next, an insulator layer 140 is formed at both sides of the magnetoresistive film 120 using a lift-off method. Similarly, in the sensor height direction, the magnetoresistive film 120 is patterned into a desired shape by photolithography, ion milling, or reactive ion etching, and an insulator layer 141 is formed using a lift-off method. The order of patterning the magnetoresistive film 120 may also be exchanged between the track width direction and sensor height direction.
Then, an upper shield 150 is formed. The lower shield 110 and upper shield 150 are also working as a pair of electrodes supplying current in the film-thickness direction of the magnetoresistive film 120, and they detect the electrical resistivity change of the magnetoresistive film 120. Therefore, it is preferable that interfaces between the lower shield 110 and the magnetoresistive film 120 and between the magnetoresistive film 120 and the upper shield 150 are free of electrical contact resistance. In order to mitigate this effect, just prior to forming the magnetoresistive film 120 and the upper shield 150, surface oxide layers and adherents/absorbents are removed effectively using plasma etching or ion beam etching. Furthermore, the lower shield and the lower electrode can be formed individually as substrate/lower shield/lower gap/lower electrode/magnetoresistive film (similar to the upper shield and upper electrode).
One example of a detailed film configuration of the magnetoresistive film 120 is a primary layer 121/first magnetic layer 122/antiferromagnetic coupling layer 123/second magnetic layer 124/nonmagnetic conductive layer or nonmagnetic tunneling barrier layer 125/magnetic free layer 126/antiferromagnetic separate layer 127/longitudinal biasing layer 128/antiferromagnetic layer 129/protection layer 130. The first magnetic layer 122/antiferromagnetic coupling layer 123/second magnetic layer 124 correspond to the pinned layer and pins the magnetization direction without using the antiferromagnetic layer. On the other hand, the magnetization direction of the magnetic free layer 126 easily rotates in response to an external field. Therefore, the relative angle between the second magnetic layer 124 comprising the pinned layer and the magnetic free layer 126 changes in response to a signal field from the magnetic recording medium; correspondingly, the electrical resistivity of the magnetoresistive film 120 changes and an electromagnetically transformed reading output is obtained.
In the figures, the magnetization direction of each magnetic layer is indicated by symbols such as arrows. An overview of the situation where a longitudinal biasing field is applied to the free layer will be described using this. The first magnetic layer 122 and the second magnetic layer 124 constituting the free layer are antiferromagnetically coupled through the antiferromagnetic coupling layer 123, and the magnetizations are aligned perpendicular to the medium (sensor height direction). Symbols 151 and 152 show the magnetization directions of the first magnetic layer 122 and the second magnetic layer 124, respectively. The magnetization of the longitudinal biasing layer 128 applying a longitudinal biasing field to the free layer 126 is pinned to the track width direction and is exchange-coupling with the antiferromagnetic layer 129 as shown in an arrow 154. Accordingly, since magnetic flux returns at the edge of track between the longitudinal biasing layer 128 and magnetic free layer 126 as shown by an arrow 155, the magnetization directions of the magnetic free layer 126 and longitudinal biasing layer 128 become stable. That is, a bias field is applied substantially to the magnetic free layer 126 in the track width direction, and it creates the effect of making the magnetic free layer 126 a single domain. Additionally, in the case where the magnetic free layer 126 and the longitudinal biasing layer 128 are antiferromagnetically coupled to each other through the nonmagnetic separate layer 127, the effect is further enhanced.
As mentioned above, by controlling the magnetization direction of each magnetic layer a magnetoresistive head can be obtained which realizes high reading sensitivity, suppression of Barkhausen noise, and excellent symmetry of reading waveforms. In the figure, the magnetization direction 154 of the longitudinal biasing layer 128 is shown toward the left when viewed from the air bearing surface, but it may be toward right (in this case, the magnetization direction 153 of the magnetic free layer 126 is aligned toward the left). It is similar for the magnetization directions 151 and 152 of the first magnetic layer 122 and the second magnetic layer 124 constituting the pinned layer.
In the first embodiment, a configuration was shown as an example in which the pinned layer is formed on a side close to the substrate 100 in the magnetoresistive layer 120. On the other hand, in the second embodiment, the order of lamination is reversed as the primary layer 121/antiferromagnetic layer 129/longitudinal biasing layer 128/nonmagnetic layer 127/magnetic free layer 126/nonmagnetic conductive layer or nonmagnetic tunneling barrier layer 125/second magnetic layer 124/antiferromagnetic coupling layer 123/first magnetic layer 122/protection layer 130. Additionally, the primary layer 121/antiferromagnetic layer 129 are not etched in the track width dimension, and they are patterned wider than the part of longitudinal biasing layer 128/nonmagnetic separate layer 127/magnetic free layer 126/nonmagnetic conductive layer or nonmagnetic tunneling barrier layer 125/second magnetic layer 124/antiferromagnetic coupling layer 123/first magnetic layer 122/protection layer 130. When etching the magnetoresistive layer 120, fabrication in the above-described shape is possible by controlling the etching time while monitoring etched particles using a mass spectrometer, etc.
In a CPP-GMR head using a nonmagnetic conductive layer for the layer 125, a parasitic resistance of the primary layer 121/antiferromagnetic layer 129, etc. causes a decrease in reading output. Therefore, like the structure shown in the figure, the primary layer 121/antiferromagnetic layer 129 can be used as a part of the lower electrode when the primary layer 121/antiferromagnetic layer 129 are patterned wider than the track width, and it is effective in deterring the decrease in the reading output.
In this embodiment, the primary layer 121/antiferromagnetic layer 129 are shown as a shape not etched, but a part of the primary layer 121/antiferromagnetic layer 129 may be etched in the film-thickness direction. Conversely, in addition to the primary layer 121/antiferromagnetic layer 129, a part of the longitudinal biasing layer 128 may be etched in the film-thickness direction.
Since the resistance of the nonmagnetic tunneling barrier layer is large enough in a TMR head using a nonmagnetic tunneling barrier layer as the layer 125, the decrease in reading output caused by parasitic resistance is hardly observed. Thus, like the first embodiment shown in
Next, each component of the magnetoresistive head shown in
Commonly used materials for the substrate 100, the lower shield 110, the upper shield 150, and the insulator films 140 and 141 are shown as one example, because they are not necessary limited in the present invention. AlTiC, SiC, or those coated with Al2O3 are used for the substrate 100. Single or multi-layer films selected from Ni—Fe alloys and their nitrates, Co—Zr, Co—Hf, or Co—Ta system amorphous alloys, etc. are used for the lower shield 110 and the upper shield 150. It is simple that they can be formed by a sputtering method and a plating method. Short circuits between the lower shield 110 and the upper shield 150 can be prevented by using Al2O3, SiO2, AlN, SiN, or mixtures thereof and multi-layer films as the insulator films 140 and 141. These are preferably formed by a sputtering method.
The magnetoresistive film 120 is preferably fabricated by a sputtering method from the viewpoint of film-thickness, controllability of alloy composition, and mass-production efficiency. An example of the film configuration of the magnetoresistive film 120 is as follows. For instance, Ta (2.5)/Ni47Cr40Fe13 (3.5)/Ni85Fe15 (1)/Ru (0.5)/Co50Fe50 (2.15)/Ru (0.35)/Co90Fe10 (2.5)/Al (0.45)-oxide/Co90Fe10 (0.5)/Ni85Fe15 (3)/Ru (0.8)/Cu (0.6)/ Co90Fe10 (2.5)/Mn52Pt48 (14)/Ta (5), etc. Herein, the number shown in ( ) is the film-thickness, and the unit is nm. The unit of each alloy component showing the subscript of each element is at %. Ta (2.5)/Ni47Cr40Fe13 (3.5)/Ni85Fe15 (1)/Ru (0.5), Co50Fe50 (2.15), Ru (0.35), Co90Fe10 (2.5), Al (0.45)-oxide, Co90Fe10 (0.5)/Ni85Fe15 (3), Ru (0.8)/Cu (0.6), Co90Fe10 (2.5), Mn52Pt48 (14), and Ta (5) correspond to the primary layer 121, the first magnetic layer 122, the antiferromagnetic coupling layer 123, the second magnetic layer 124, nonmagnetic tunneling barrier layer 125, the magnetic free layer 126, the nonmagnetic separate layer 127, the longitudinal biasing layer 128, the antiferromagnetic layer 129, and the protection layer 130, respectively.
Besides a single layer film, for instance Ni—Fe or Co—Fe, etc., a magnetic multilayer film such as Co—Fe/Ni—Fe or Co—Fe/Ni—Fe/Co—Fe etc. may be used for the first magnetic layer 122, the second magnetic layer 124, the magnetic free layer 126, and the longitudinal biasing layer 128, which are components of the magnetoresistive film 120. Moreover, a so-called synthetic ferrimagnetic structure such as Co—Fe/Ni—Fe/Ru/Ni—Fe may be used for the magnetic free layer 126.
A material containing Fe, Co, and Ni as the main component which has a high spin polarization ratio at the Fermi energy is used for the second magnetic layer 124 and the magnetic free layer 126 to make the MR ratio larger which strongly affects the reading output. Moreover, it is more useful to use Heusler alloys such as Co50Mn25Ge25 and Co50Mn25Si25, etc., or half metals such as Fe3O4 which have a larger spin polarization ratio. Furthermore, it is desirable that the composition and film thickness of the magnetic free layer 126 be properly adjusted to exhibit low magnetostriction and low coercivity besides the MR ratio, and that attention be paid to make small the interlayer coupling field with the second magnetic layer 124.
The expression “Al (0.45)-oxide” for the nonmagnetic tunnel barrier layer 125 means that it uses a so-called natural oxidation method, in which oxygen is introduced in the chamber after the deposition of an Al film. If control is possible to prevent excess oxidation, methods such as radical oxidation and plasma oxidation may be used, and an oxide film may be formed by reactive sputtering, and Al2O3 directly deposited. Additionally, besides Al oxide, an oxide or nitride including Mg, Al, Si, Ti, V, Mn, Zr, Nb, Hf, and Ta may be used.
In the aforementioned example of a TMR head configuration, if the nonmagnetic tunneling barrier layer is substituted for a nonmagnetic conductive layer, an embodiment of the present invention could be used as a CPP-GMR head as it is. As the nonmagnetic conductive layer, Cu, Ag, and Au, etc. may be deposited from about 1 to 5 nm.
A preferable example of the film configuration magnetic free layer 126/nonmagnetic separate layer 127/longitudinal biasing layer 128/antiferromagnetic layer 129/protection layer 130 is Co90Fe10 (0.5)/Ni85Fe15 (3)/Ru (0.8)/Cu (0.6)/Co90Fe10 (2.5)/Mn52Pt48 (14)/Ta (5), etc. If, after being formed, the magnetoresistive film is annealed while applying a magnetic field in the track width direction, a large unidirectional magnetic anisotropy is given to the longitudinal biasing layer Co90Fe10 (2.5) by a magnetic exchange coupling with Mn52Pt48 (14), thus the magnetization direction can be pinned in the track width direction. Additionally, because the unidirectional magnetic anisotropy has excellent thermal stability, it has high reliability.
Here, an example is shown using an ordered alloy Mn52Pt48 as the antiferromagnetic layer 129 which pins the magnetization direction of the longitudinal biasing layer 128 in one direction.
As another candidate of a material for the antiferromagnetic layer 129, it may be possible to use a disordered alloy antiferromagnetic film which is expressed by Mn-M2 (where M2 is a material including at least one element selected from Cr, Fe, Ru, Pd, Ir, or Pt) such as, for example, Fe50Mn50 and Mn80Ir20.
Additionally, Ru (0.8)/Cu (0.6) is used as the nonmagnetic separate layer in this embodiment to couple antiferromagnetically the magnetic free layer 126 with the longitudinal biasing layer 128. Cr, Cu, Ru, Rh, Pd, Re and Ir and their alloys and multi-layer films may be used as the nonmagnetic separate layer 127 which generates antiferromagnetic coupling. However, if the antiferromagnetic coupling between the magnetic layer 126 and the longitudinal biasing layer 128 is made too strong, the problem of decreasing output arises because the magnetization of the magnetic free layer 126 becomes difficult to rotate by the signal field from the medium. Like the aforementioned example, the strength of the antiferromagnetic coupling can be set arbitrarily by making the nonmagnetic separate layer 127 multilayer and by making the film-thickness thicker.
Next, a detailed explanation will be given of the film configuration of the pinned layer in the magnetoresistive layer.
In order to strongly pin the magnetization direction of the pinned layer even if an external field is applied, at least one of a plurality of magnetic layers constituting the pinned layer may include a hard magnetic material.
Next is shown the magnetoresistive transfer curve of the CIP-GMR including glass substrate/Ni47Cr40Fe13 (4.2)/Ru (0.45)/Ni85Fe15 (0.5)/Co90Fe10 (1.5)/Cu (1.9)/Co90Fe10 (2.5)/Ru (0.35)/Co50Fe50 (t)/Ru (1)/Ta (2). Depositions of the free layer Ni85Fe15 (0.5)/Co90Fe10 (1.5) and the pinned layer Co90Fe10 (2.5)/Ru (0.35)/Co50Fe50 (t) were carried out in a magnetic field of 8 kA/m perpendicular to the track width direction and medium, respectively. As representative examples, the magnetoresistive transfer curves of the Co50Fe50 film thicknesses of 1.9 nm, 2.15 nm, and 2.4 nm are shown in
In this embodiment, the configuration of the pinned layer is fourth magnetic layer 134/third antiferromagnetic coupling layer 133/third magnetic layer 132/second antiferromagnetic coupling layer 131/first magnetic layer 122/first antiferromagnetic coupling layer 123/second magnetic layer 124. Symbols 156 and 157 in the figure indicate the magnetization direction of the third magnetic layer and the magnetization direction of the fourth magnetic layer, respectively. In the first and second embodiments, the configuration of the pinned layer included two magnetic layers. But, when the configuration contains more than three magnetic layers as, for instance, in Co—Fe/Ru/Co—Fe and the third embodiment, the magnetization direction is pinned more strongly.
As mentioned above, the magnetization direction of the pinned layer can be pinned strongly against an external magnetic field by the following conditions: at least two magnetic layers are included in the pinned layer, the magnetic layers are laminated through the antiferromagnetic coupling layer, the adjacent aforementioned magnetic layers include a laminated body antiferromagnetically coupling with each other, at least one magnetic layer includes a hard magnetic material with a large coercivity, and the film-thickness of each magnetic layer is controlled to make the magnetic moment almost substantially zero when the magnetization of each magnetic layer is aligned antiparallel. The material and film-thickness of each layer may be properly controlled within a range meeting these conditions.
In the so-called CPP type magnetoresistive head, in which a sense current flows in the film-thickness direction of the magnetoresistive film, a short-circuit occurs on the air bearing surface between the pinned layer and free layer because of the influence of smearing in the lapping process of air bearing surface, thereby the yield may be reduced. In order to avoid this, it is preferable that a so-called flux guide type head structure be adopted. That is, it is a structure in which the pinned layer or the free layer is not exposed and short circuit of the sensor is prevented. In this structure, the configuration of the present invention can be flexibly applied as it is.
The magnetoresistive film 120 is patterned in a desired pattern in the sensor height direction using photolithography, ion milling or reactive ion etching. Moreover, it is patterned to a smaller dimension and in a desired pattern in the sensor height direction using photolithography, ion milling or reactive ion etching. Ion milling and reactive ion etching are carried out using equipment having an end-point detect function such as a mass spectrometer, etc., thereby layers from the top protection layer 130 to the nonmagnetic conductive layer or the nonmagnetic tunneling barrier layer 125 are etched while the layers below the magnetic free layer 126 are left unetched. If it is in the range where the magnetic moment of the magnetic free layer 126 is not reduced to an extreme, the surface of the magnetic free layer 126 might be slightly over-etched. Moreover, in addition to the layers below the magnetic free layer 126, a part of the nonmagnetic conductive layer or the nonmagnetic tunneling barrier layer 125 may not be milled. Next, the insulator layer 142 is formed using a lift-off method at both edges of the sensor height direction of the magnetoresistive layer 120. Finally, the upper shield 150 is formed, and the electrical resistivity change of the magnetoresistive film 120 is then detected by the lower shield 110 and the upper shield 150. As described in the first embodiment, the order of patterning the magnetoresistive film 120 may be exchanged between the track width direction and the sensor height direction.
As shown in
As track narrowing makes progress, the problem that the magnetic effective track width does not become narrow is obvious even if the patterning dimension is made smaller. In the current hard bias structure, the shield gap has to be greater around both edges of the track width direction compared with around the center part of track width. The reason is that it is not possible that the total layer thickness of the laminated film placed at both edges of the track width direction of the magnetoresistive film (mainly, hard magnetic film/electrode film in the case of a CIP type, and insulator film/hard magnetic film (/insulator film) in the case of a CPP type) is controlled to be thinner than the layer film thickness of the magnetoresistive film. In this case, around both edges of the track width direction, reading sensitivity is low but a problem of so-called “side reading” arises because it is easy for flux to flow into the free layer caused by the wider shield gap, thus the magnetic effective track width cannot be made narrower. It is clear that this problem becomes serious with narrowing track width. A structure of a magnetic head of the present embodiment effectively works to solve this problem.
It can be said a more preferable structure is when the aforementioned fifth embodiment is combined with the other embodiments, because it becomes possible to fabricate with high yield a read head exhibiting excellent reading characteristics.
In order to obtain excellent reading characteristics in magnetoresistive heads of the embodiments mentioned above, controlling the magnetization direction of each magnetic layer is very important. First, problems of the prior art are shown based on the experimental results. In this case, a prior art means a configuration, in which nonmagnetic separate layer/longitudinal biasing layer/second antiferromagnetic layer are deposited on a standard spin valve type GMR film or TMR film including first antiferromagnetic layer/pinned layer magnetic film/nonmagnetic conductive layer or nonmagnetic tunneling barrier layer/free magnetic film. Magnetoresistive transfer curves of the GMR films are shown in
After depositing the aforementioned GMR film, annealing in a magnetic field is carried out twice in vacuum. The annealing conditions are, in order, (1) 250° C.×9 hours while applying a magnetic field of 1.1 MA/m in the sensor height direction and (2) 250° C.×3 hours while applying a magnetic field of 24 kA/m in the track width direction. The purpose of these conditions is to pin the magnetization of the pinned layer in the sensor height direction and to pin the magnetization of the longitudinal biasing layer in the track width direction, respectively. In the figure, measurement results are shown comparing after annealing (1) and after annealing (1)+(2).
As clearly shown in
On the other hand, the magnetization directions of the pinned layer and longitudinal biasing layer can be easily controlled in the GMR film in which an ordered system MnPt alloy is used for the first antiferromagnetic layer and a disordered system MnIr alloy is used for the second antiferromagnetic layer: Ta (2.5)/Ni47Cr40Fe13 (3.5)/Ni85Fe15 (1)/Mn52Pt48 (18)/Co75Fe25 (1.5)/Ru (0.8)/Co75Fe25 (2)/Cu (1.95)/Co90Fe10 (0.5)/Ni85Fe15 (3)/Ru (0.8)/Cu (0.7)/Co90Fe10 (2.5)/Mn80Ir20 (9)/Ta (5). In this case, it is because the direction of magnetic exchange coupling field applied to the longitudinal biasing layer by the Mn80Ir20 (9) can be changed by annealing at a relatively low temperature and for a short time. The condition of annealing (2) used in this embodiment is 250° C.×10 minutes, and the magnetization direction of the pinned layer is hardly affected by this annealing.
Additionally,
Thus, in the case where the two, first and second, antiferromagnetic layers are used for pinning the magnetization directions of the pinned layer and the longitudinal biasing layer as in the prior art, controlling the magnetization direction becomes difficult, so that a magnetoresistive head with excellent reading characteristics cannot be obtained.
A magnetization direction controlling method of each magnetic layer according to an embodiment of the present invention will be described below.
Afterwards, an element is formed by using photolithography or ion milling/reactive ion etching/plating etc. (A fabrication process of a write head is included though the details are omitted). Depending on the thermal and magnetic field histories received in the various processes during this step, the magnetization direction of the pinned layer may be shifted from a desired direction. For this problem, it is possible to reset the magnetization direction of the pinned layer in the direction perpendicular to the magnetic recording medium by applying a static field at room temperature (that is, special temperature control is not required) at the final step. That is, an annealing step in a magnetic field, which is carried out by applying a magnetic field in the direction perpendicular to the medium (sensor height direction), is not contained in this series of process flow. Therefore, the magnetization directions of the pinned layer and longitudinal biasing layer 128 can be stabilized in the desired directions, respectively, maintaining orthogonality easily without causing the problem that the magnetization of the longitudinal biasing layer 128 shifts from the track width direction.
The experimental results carried out using the aforementioned magnetization direction controlling method are shown below.
As shown in
On the other hand, as shown in
The tunneling magnetoresistive sensor fabricated by the aforementioned process flow displayed a curve profile of a normal magnetoresistive transfer curve as substantiated by the fact that the magnetization of Co50Fe50 (2.5)/Ru (0.35)/Co90Fe10 (2.5) corresponding to the pinned layer is pinned in a desired direction, and a maximum large MR ratio of 18% was obtained. Herein, a result of the tunneling magnetoresistive sensor is shown as an example, but it is clear that a similar result is obtained in a CPP-GMR in which a nonmagnetic layer such as Cu etc. is used in lieu of the tunneling barrier layer having an Al oxide film.
Effects of a magnetoresistive head according to an embodiment of the present invention are shown below compared to the prior art.
As shown in
In the aforementioned magnetic head according to embodiments of the present invention and a magnetic recording system wherein mounted, reading characteristics with high sensitivity and reliability can be obtained.
It is to be understood that the above description is intended to be illustrative and not restrictive. Many embodiments will be apparent to those of skill in the art upon reviewing the above description. The scope of the invention should, therefore, be determined not with reference to the above description, but instead should be determined with reference to the appended claims along with their full scope of equivalents.
Number | Date | Country | Kind |
---|---|---|---|
2004-016126 | Jan 2004 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
5583725 | Coffey et al. | Dec 1996 | A |
6344954 | Redon et al. | Feb 2002 | B1 |
6381107 | Redon et al. | Apr 2002 | B1 |
6504689 | Gill et al. | Jan 2003 | B1 |
6545848 | Terunuma | Apr 2003 | B1 |
6560077 | Fujiwara et al. | May 2003 | B2 |
6600638 | Gill | Jul 2003 | B2 |
6721139 | Gill | Apr 2004 | B2 |
6724587 | Gill | Apr 2004 | B2 |
20010012188 | Hasegawa et al. | Aug 2001 | A1 |
20020097537 | Shimazawa | Jul 2002 | A1 |
20020181165 | Gill | Dec 2002 | A1 |
20020181166 | Gill | Dec 2002 | A1 |
20020186514 | Childress et al. | Dec 2002 | A1 |
20020186515 | Gill | Dec 2002 | A1 |
20030002230 | Dee et al. | Jan 2003 | A1 |
20030042903 | Hasegawa et al. | Mar 2003 | A1 |
20030103299 | Saito | Jun 2003 | A1 |
20030137781 | Carey et al. | Jul 2003 | A1 |
20030174446 | Hasegawa | Sep 2003 | A1 |
20030179514 | Pinarbasi | Sep 2003 | A1 |
20030206383 | Meguro et al. | Nov 2003 | A1 |
20040008455 | Hasegawa et al. | Jan 2004 | A1 |
20040042130 | Lin et al. | Mar 2004 | A1 |
20040047088 | Hasegawa | Mar 2004 | A1 |
20040061983 | Childress et al. | Apr 2004 | A1 |
20040246632 | Nishioka et al. | Dec 2004 | A1 |
20050105222 | Sbiaa et al. | May 2005 | A1 |
20050174704 | Lin et al. | Aug 2005 | A1 |
20060067016 | Childress et al. | Mar 2006 | A1 |
Number | Date | Country |
---|---|---|
04-358310 | Dec 1992 | JP |
07-057223 | Mar 1995 | JP |
08-007235 | Jan 1996 | JP |
2000-057538 | Feb 2000 | JP |
2000-251224 | Sep 2000 | JP |
2001-250205 | Sep 2001 | JP |
2001-250205 | Sep 2001 | JP |
Number | Date | Country | |
---|---|---|---|
20050162786 A1 | Jul 2005 | US |