Wavelength-converting casting composition and white light-emitting semiconductor component

Information

  • Patent Grant
  • 7276736
  • Patent Number
    7,276,736
  • Date Filed
    Thursday, July 10, 2003
    21 years ago
  • Date Issued
    Tuesday, October 2, 2007
    17 years ago
Abstract
The wavelength-converting casting composition is based on a transparent epoxy casting resin with a luminous substance admixed. The composition is used in an electroluminescent component having a body that emits ultraviolet, blue or green light. An inorganic luminous substance pigment powder with luminous substance pigments is dispersed in the transparent epoxy casting resin. The luminous substance is a powder of Ce-doped phosphors and the luminous substance pigments have particle sizes ≦20 μm and a mean grain diameter d50≦5 μm.
Description
BACKGROUND OF THE INVENTION

1. Field of the Invention


The invention relates to a wavelength-converting casting composition based on a transparent epoxy casting resin which is mixed with a luminous substance, for an electroluminescent component having a body that emits ultraviolet, blue or green light.


2. Description of the Related Art


A component of that type has become known, for instance, from German published, non-prosecuted patent application DE 38 04 293. The reference describes an arrangement with an electroluminescent diode or laser diode, in which the emissions spectrum emitted by the diode is shifted toward longer wavelengths, by means of a plastic element mixed with a fluorescing, light-converting, organic colorant. The light emitted by the arrangement as a result has a different color from what the light emitting diode emitted. Depending on the type of colorant added to the plastic, it is possible to produce LED arrays that light up in different colors with one and the same type of light-emitting diode (LED).


In many potential applications for LEDs, such as in display elements in motor vehicle dashboards, illumination in aircraft and automobiles, and in LED displays capable of showing full color, there is an increasing demand for LED arrays with which mixed color light and in particular white light can be generated.


However, the prior art casting compositions of the type referred to at the outset with organic luminous substances exhibit a shift in the color location, that is, the color of the light emitted by the electroluminescent component, under temperature and temperature/humidity stresses Japanese patent disclosure JP-07 176 794-A describes a white-light-emitting planar light source, in which two diodes that emit blue light are disposed on one face end of a transparent plate and emit light into the transparent plate. The transparent plate is coated on one of the two opposed main sides with a fluorescing substance that emits light when it is excited with the blue light of the diodes. The light emitted by the fluorescing substance has a different wavelength from the blue light emitted by the diodes. In this known component, it is especially difficult to apply the fluorescing substance in such a way that the light source emits homogeneous white light. Moreover, replicability and mass production presents major problems, because even slight fluctuations in the layer thickness of the fluorescing layer, for instance from irregularities of the surface of the transparent plate, cause a change in the white of the light emitted.


SUMMARY OF THE INVENTION

It is accordingly an object of the invention to provide a wavelength-converting casting mass, which overcomes the above-mentioned disadvantages of the prior art devices and methods of this general type and with which electroluminescent components can be produced that emit homogeneous mixed-colored light, and which enables mass production at reasonable engineering effort and expense and with maximally replicable component characteristics. The emitted Light should be color-stable even under temperature and temperature/humidity stresses. It is a further object to specify a use for the casting mass and a method for producing the composition.


With the foregoing and other objects in view there is provided, in accordance with the invention, a wavelength-converting casting composition, or converting a wavelength of ultraviolet, blue or green light emitted by an electro-luminescent component, comprising:

  • a transparent epoxy casting resin;
  • an inorganic luminous substance pigment powder dispersed in the transparent epoxy resin, the pigment powder comprising luminous substance pigments from a phosphorus group having the general formula A2B5X12:M;
  • the luminous substance pigments having grain sizes ≦20 μm and a mean grain diameter d50≦5 μm.


In accordance with an added feature of the invention, the mean grain diameter d50 of the luminous substance pigments is between one and two micrometers.


Inorganic/mineral luminous substances are extremely stable with regard to temperature and temperature/humidity stresses.


In accordance with an additional feature of the invention, the composition includes the following parts:

  • a) epoxy casting resin ≧60% by weight;
  • b) luminous substance pigments >0 and ≦25% by weight;
  • c) thixotropic agent >0 and ≦10% by weight;
  • d) mineral diffusor >0 and ≦10% by weight;
  • e) processing adjuvant >0 and ≦3% by weight;
  • f) hydrophobic agent >0 and ≦3% by weight; and
  • g) adhesion promoters >0 and ≦2% by weight.


Suitable epoxy casting resins are described for instance in German published, non-prosecuted patent application 25 42 465 (pp. 4–9, in particular examples 1–4), and in European patent disclosure EP 0 039 017 (pp. 2–5, in particular examples 1–8). The disclosures of those documents are hereby expressly incorporated by reference.


Pyrogenic silicic acid is for instance used as the thixotropic agent. The thixotropic agent is used to thicken the epoxy casting resin, so as to reduce the sedimentation of the luminous substance pigment powder. The flow and wetting properties are also adjusted or processing the casting resin.


CaF2 is preferably used as a mineral diffusor for optimizing the luminous pattern of the component.


Glycol ether is for instance suitable as a processing adjuvant. It improves the compatibility between the epoxy casting resin and the luminous substance pigment powder and is thus used to stabilize the dispersion of luminous substance pigment powder and epoxy casting resin. To that end, surface modifiers based on silicone can also be employed.


The hydrophobic agent, such as liquid silicone wax, is also used to modify the pigment surface; in particular, the compatibility and wettability of the inorganic pigment surface is improved with the organic resin.


The adhesion promoter, such as functional alkoxysiloxane, improves the adhesion between the pigments and the epoxy resin in the cured state of the casting composition. As a result it is attained that the boundary face between the epoxy resin and the pigments will not rupture, for instance in response to temperature fluctuations. Caps between the epoxy resin and the pigments would cause light losses in the component.


The epoxy casting resin, preferably with a reactive triple oxiran ring, preferably includes a monofunctional and/or multifunctional epoxy casting resin system (≧80% by weight, such as bisphenol-A-diglycidyl ether) a reactive diluent (≦10% by weight, such as aromatic monoglycidyl ether), a multifunctional alcohol (≦5% by weight), a degassing agent based on silicone (≦1% by weight), and a decolorizing component to adjust the color number (≦1% by weight).


In accordance with another feature of the invention, the luminous substance pigments are substantially spherical particles or flakelike particles. The tendency to clumping of such pigments is advantageously very slight. The H2O content is below 2%.


In the production and processing of epoxy casting resin components with inorganic luminous substance pigment powders, in general not only wetting but also sedimentation problems occur. Especially luminous substance pigment powders with d50≦5 μm have a strong tendency to clumping. In the last-named composition of the casting composition, the luminous substance pigments, with the above-indicated particle size, can advantageously be substantially free of clumps and can be dispersed homogeneously in the epoxy casting resin. This dispersion is stable even under long-term storage of the casting composition. Essentially no problems of wetting and/or sedimentation occur.


In accordance with a further feature of the invention, the luminous substance pigments are particles of Ce-doped garnets, such as, particularly, YAG:Ce particles. An advantageous dopant concentration is 1%, for example, and an advantageous luminous substance concentration is 12%, for example. The preferred high-purity luminous substance pigment powder also advantageously has an iron content of ≦5 ppm. A high iron content leads to high light losses in the component. The luminous substance pigment powder is highly abrasive. The iron content in the casting composition can therefore rise considerably during production. Iron contents in the casting composition <20 ppm are advantageous.


The inorganic luminous substance YAG:Ce has the particular advantage, among others, that this involves insoluble color pigments with an index of refraction of approximately 1.84. As a result, along with the wavelength conversion, dispersion and scattering effects occur that lead to good mixing of blue diode emissions with yellow converter radiation.


It is also especially advantageous that the luminous substance concentration in the epoxy resin when inorganic luminous substance pigments are used is not limited by the solubility, as is the case for organic colorants.


For further reduction of clumping, the luminous substance pigments may advantageously be provided with a silicone coating.


With the above and other objects in view there is also provided, in accordance with the invention, a method of producing a wavelength-converting casting composition, for converting a wavelength of ultraviolet, blue or green light emitted by an electroluminescent component, the method which comprises:

  • providing a base of transparent epoxy casting resin;
  • providing a luminous substance pigment powder or luminous substance pigments from a phosphorus group having the general formula A3B5X12:M;
  • tempering the luminous substance pigment powder at a temperature of ≧200° C. and subsequently mixing the tempered pigment powder with the epoxy casting resin.


Tempering is preferably effected for approximately ten hours. As a result, again the tendency to clumping can be reduced.


As an alternative or in addition for this purpose, the luminous substance pigment powder, before being mixed with the epoxy casting resin, can be slurried in a higher-boiling alcohol and subsequently dried. A further possibility for reducing clumping is to add a hydrophobic silicone wax to the luminous substance pigment powder before the powder is mixed with the epoxy casting resin. Surface stabilization of the phosphors by heating the pigments in the presence of glycol ethers, for instance for 16 hours at T>60° C., is especially advantageous.


To avoid problematic contamination upon dispersal of the luminous substance pigments, caused by abrasion, reaction vessels, agitators and dispersing devices as well as rolling mechanisms of glass, corundum, carbide and nitride materials as well as especially hardened types of steel are used. Clump-free luminous substance dispersions are also obtained by ultrasonic methods or by the use of screens and glass ceramic frits.


An especially preferred inorganic luminous substance for producing optoelectronic components that light up white is the phosphorous YAG:Ce (Y3Al5O12:Ce3−). This phosphorous can be especially simply mixed zenith transparent epoxy casting resins conventionally used in LED technology. Also conceivable as luminous substances are other garnets, doped with rare earths, such as Y3Ga5O12:Ce3−, Y(Al,Ga)5O12:Ce3+, and Y(Al,Ga)5O12:Tb3+.


To generate mixed-colored light, the thiogallates doped with rare earths are moreover especially suitable, examples being CaGa2S4:Ce3+ and SrGa2S5:Ce3+. Once again, the use of aluminates doped with rare earths, such as YAlO3:Ce3+, YGaO3:Ce3+, Y(Al,Ga)O3:Ce3+, and orthosilicates doped with rare earths, M2SiO5:Ce3− (M:Sc,Y,Sc), such as Y2SiO5:Ce3+ is conceivable. In all the yttrium compounds, the yttrium can in principle also be replaced with scandium or lanthanum.


Therefore, in the phosphorous group A3B5X12:M, the variables may stand for the following exemplary elements: A=Y, Ca, Sr; B =Al, Ga, Si; X=O, S; and M=Ce3−, Tb3−.


Preferably, the casting composition according to the invention is used in a radiation-emitting semiconductor body, In particular with an active semiconductor layer or semiconductor layer sequence of GaxIn1−xN or GaxAl1−xN, which in operation emits an electromagnetic radiation of the ultraviolet, blue and/or green spectral range. The luminous substance particles n the casting composition convert some of the radiation originating in this spectral range into radiation with a longer wavelength, in such a way that the semiconductor component emits mixed radiation, and in particular mixed-colored light is comprising this radiation as well as radiation from the ultraviolet, blue and/or green spectral range. This means for instance that the luminous substance particles spectrally selectively absorb some of the radiation emitted by the semiconductor body and emit in the longer-wave range. Preferably, the radiation emitted by the semiconductor body has a relative maximum intensity at a wavelength lambda λ≦520 nm, and the wavelength range spectrally selectively absorbed by the luminous substance particles is outside this maximum intensity.


It is also advantageous t possible for a plurality of different kinds of luminous substance particles, which emit at different wavelengths, to be dispersed in the casting composition. This is preferably achieved by means of different doping in different host lattices. This advantageously makes it possible to generate manifold color mixtures and color temperatures of the light emitted by the component This is especially of interest for LEDs capable of emitting full color.


In a preferred use of the casting composition of the invention, a radiation-emitting semiconductor body (such as an LED chip) is at least partly enclosed by the casting composition. The casting composition is preferably simultaneously used as a component envelope (housing). The advantage of a semiconductor component in accordance with this embodiment is essentially that conventional production lines used to make conventional LEDs (such as radial LEDs) can be used to produce it. For the component envelope, instead of the transparent plastic used for this purpose in conventional LEDs, the casting composition can simply be employed.


With the casting composition of the invention, it is possible in a simple way, with a single colored light source, particularly an LED with a single semiconductor body that emits blue light, to create mixed-colored and in particular white light. For instance to generate white light with a semiconductor body that emits blue light, some of the radiation emitted by the semiconductor body is converted out of the blue spectral range into the yellow spectral range, which is complementary in color to blue, by means or inorganic luminous substance particles.


The color temperature or color location of the white light can be varied by a suitable choice of the luminous substance, its particle size, and its concentration. In addition, luminous substance mixtures can also be employed, and as a result advantageously the desired tonality of the color of the emitted light can be adjusted very precisely.


Especially preferably, the casting composition is used in a radiation-emitting semiconductor body in which the emitted radiation spectrum has a maximum intensity at a wavelength between 420 nm and 460 nm, and in particular at 430 nm (examples being semiconductor bodies based on GaxAl1−xN) or 450 nm (such as semiconductor bodies based on GaxIn1−xN). With such a semiconductor component, nearly all the colors and mixed colors in the CIE chromaticity diagram can advantageously be generated.


Instead of the radiation-emitting semiconductor body of electroluminescing semiconductor material, however, some other electroluminescing material may be used, such as polymer material.


With the objects of the invention is view there is further provided, in accordance with the invention, a light-emitting semiconductor component, comprising:

  • a semiconductor body formed of a semiconductor layer sequence and being capable, during an operation of the semiconductor component, of emitting electromagnetic radiation in at least one of an ultraviolet, blue, and green spectral range;
  • a wavelength-converting casting composition disposed in a vicinity of the semiconductor body, the casting composition being formed of a transparent epoxy casting resin and an inorganic luminous substance pigment powder dispersed in the transparent epoxy resin, the pigment powder comprising luminous substance-pigments from a phosphorus group having the general formula A3B5X12:M and having grain sizes ≦20 μm and a mean grain diameter d50≦5 μm;
  • the luminous substance pigments converting a portion of the radiation originating from the ultraviolet, blue and green spectral range into radiation of a higher wavelength, such that the semiconductor component emits mixed radiation including the higher-wavelength radiation and radiation from at least one of the ultraviolet, blue and green spectral range.


In other words, the casting composition is especially suitable for a light-emitting semiconductor component (for instance an LED), in which the electroluminescing semiconductor body is disposed in a recess of a prefabricated housing, optionally already provided with a leadframe, and the recess is provided with the casting composition. This kind of semiconductor component can be produced in great numbers on conventional production lines. All that is needed, after mounting of the semiconductor body in the housing, is to fill the recess with the casting composition.


A semiconductor component that emits white light can be produced with the casting composition according to the invention advantageously by choosing the luminous substance in such a way that a blue radiation emitted by the semiconductor body is converted into complementary wavelength ranges, in particular blue and yellow, or additive color triads, such as blue, green and red. The yellow or green and red light is generated via the luminous substances. The color tonality (color location in the CIE chromaticity diagram) of the white light thus produced can then be varied by means of a suitable choice of the luminous substance or luminous substances in terms of their mixture and concentration.


To improve the mixing of the radiation emitted by an electroluminescing semiconductor body with the radiation converted by the luminous substance and thus to improve the homogeneity of color of the light emitted by the component, in an advantageous feature of the casting composition according to the invention a blue-luminescing colorant, which attenuates a so-called directional characteristic of the radiation emitted by the semiconductor body. The term “directional characteristic” is understood to mean that the radiation emitted by the semiconductor body has a preferential emission direction.


A semiconductor component according to the invention that emits white light, with an electroluminescing semiconductor body emitting blue light, can be especially preferably achieved by admixing the inorganic luminous substance YAG:Ce (Y3Al5O12:Ce3−) with the epoxy resin used for the casting composition. Some of the blue radiation emitted by the semiconductor body is shifted by the inorganic luminous substance (Y3Al5O12:Ce3−) into the yellow spectral range and thus into a wavelength range that is complementary in color to the color blue. The color tonality (color location in the CIE chromaticity diagram) of the white light can then be varied by means of a suitable choice of the colorant concentration.


In addition, light-scattering particles, so-called diffusers, can be added to the casting composition. As a result, the color impression and the emission characteristics of the semiconductor component can advantageously be still further optimized.


With the casting composition of the invention, advantageously an ultraviolet radiation emitted by an electroluminescing semiconductor body along with the visible radiation can advantageously be converted into visible light. This markedly increases the brightness of the light emitted by the semiconductor body.


A particular advantage of semiconductor components according to the invention that emit white light, and in which YAG:Ce is used in particular as the luminescence-converting colorant, s that this luminous substance on excitation with blue light causes a spectral shift of approximately 100 nm between absorption and emission. This leads to a substantial reduction and reabsorption of the light emitted by the luminous substance and thus to a higher light yield. Moreover, YAG:Ce advantageously has high thermal and photochemical (such as UV) stability (substantially higher than organic luminous substances) so that even white-emitting diodes for outdoor use and/or high temperature ranges can be produced.


YAG:Ce has by now proved itself to be the best-suitable luminous substance in terms of reabsorption, light yield, thermal and photochemical stability, and processability. However, the use of other Ce-doped phosphors, in particular Ce-doped types of garnet, is also conceivable.


The wavelength conversion of the primary radiation is determined by the crystal field cleavage of the active transition metal centers in the host lattice. By substituting Gd and/or Lu for Y, or Ga for Al in the Y3Al5O12 garnet lattice, the emission wavelengths can be shifted in various ways, and this can also be done by the type of doping. By substituting Eu3− and/or Cr3− for Ce3− centers, corresponding shifts can be brought about. Corresponding dopings with Nd3− and Er3− even make it possible, because of the greater ion radii and thus reduced crystal field cleavage, to make components that emit infrared (IR) light.


Other features which are considered as characteristic for the invention are set forth in the appended claims.


Although the invention is illustrated and described herein as embodied in a wavelength-converting casting composition, its use, and method for its production, it is nevertheless not intended to be limited to the details shown, since various modifications and structural changes may be made therein without departing from the spirit of the invention and within the scope and range of equivalents of the claims.





The construction and method of operation of the invention, however, together with additional objects and advantages thereof will be best understood from the following description of specific embodiments when read in connection with the accompanying drawings.


BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a schematic sectional view of a first semiconductor component with a casting composition according to the invention;



FIG. 2 is a schematic sectional view of a second semiconductor component with a casting composition according to the invention;



FIG. 3 is a schematic sectional view of a third semiconductor component with a casting composition according to the invention;



FIG. 4 is a schematic sectional view of a fourth semiconductor component with a casting composition according to the invention;



FIG. 5 is a schematic sectional view of a fifth semiconductor component with a casting composition according to the invention;



FIG. 6 is a graph of an emission spectrum of a semiconductor body that emits blue light, with a layer sequence on the basis of GaN;



FIG. 7 is a graph of the emissions spectra of two semiconductor components with a casting composition according to the invention, which emit white light; and



FIG. 8 is a graph of the emissions spectra of further semiconductor components that emit white light.





DESCRIPTION OF THE PREFERRED EMBODIMENTS

Reference is now had to the figures of the drawing in which elements that are identical or that function identically are identified by the same reference numerals throughout.


In the light-emitting semiconductor component of FIG. 1, the semiconductor body 1 is secured by its back-side contact 11 to a first electrical terminal by means of an electrically conductive joining means such as a metal solder or an adhesive. The front-side contact 12 is joined to a second electrical terminal 3 by means of a bond wire 14.


The free surfaces of the semiconductor body 1 and portions of the electrical terminals 2 and 3 are enclosed directly by a hardened, wavelength-converting casting or potting composition 5. The casting composition preferably has the following: epoxy casting resin 80 to 90% by weight, luminous substance pigments (YAG:Ce) ≦15% by weight, diethylene glycol monomethyl ether ≦2% by weight, Tegopren 6875−45≦2% by weight, Aerosil 200 ≦5% by weight.


The exemplary embodiment of a semiccnductocr component according to the invention shown in FIG. 2 differs from that of FIG. 1 in that the semiconductor body 1 in portions of the electrical terminals 2 and 3 are enclosed not by a wavelength-converting potting mass but by a transparent envelope 15. The transparent envelope 15 does not cause any change in the wavelength of the radiation emitted by the semiconductor body 1 and for instance comprises an epoxy, silicone or acrylate resin conventionally used in LED technology, or some other suitable radiation-permeable material, such as inorganic glass.


A layer 4 is applied to the transparent envelope 15. The layer 4 comprises a wavelength-converting casting composition and, as shown in FIG. 2, covers the entire surface of the envelope 15. It Is equally conceivable for the layer 4 to cover only a portion of the surface. The layer 4 for instance comprises a transparent epoxy resin which is mixed with luminous substance particles 6. Once again, for a semiconductor component that emits white light, YAG:Ce is preferred as the luminous substance.



FIG. 3 illustrates a particularly advantageous and preferred embodiment of the invention. The first and second electrical terminals 2, 3 are embedded in an opaque, and optionally prefabricated, basic housing 8 that has a recess 9. The term “prefabricated” is understood to mean that the basic housing 8 is already finished at the terminals 2, 3, for instance by means of injection molding, before the semiconductor body is mounted on the terminal 2. The basic housing 8, by way of example, is formed of opaque plastic, and in terms of its form the recess 9 is embodied as a reflector 17 for the radiation emitted by the semiconductor body in operation (the reflection optionally being achieved by means of suitable coating of the inside walls of the recess 9). Such basic housings 8 are used in particular for LEDs that are surface-mounted on printed circuit boards. They are applied, before mounting of the semiconductor body, to a conductor strip (lead frame) that has the electrical terminals, 2, 3, the application for instance being done by injection molding.


The recess 9 is filled with a casting composition 5, whose composition is equivalent to that given above in conjunction with the description of FIG. 1.



FIG. 4 shows a so-called radial diode. Here, the electroluminescing semiconductor body 1 is secured, for instance by soldering or adhesive bonding, in a part 16, embodied as a reflector, of the first electrical terminal 2. Such housing constructions are known in LED technology and therefore require no further description here. The free surfaces of the semiconductor body 1 are covered directly by a casting composition 5 containing luminous substance particles 6, and the casting composition in turn is surrounded by a further transparent housing envelope 10.


It will be appreciated by those skilled in the art that, in the construction of FIG. 4 as well, analogously to the component of FIG. 1, an integral envelope comprising hardened casting composition 5 with luminous substance particles 6, may also be used.


In the exemplary embodiment of FIG. 5, a layer 4 (see the List of materials given above) is coated directs on the semiconductor body 1. The semiconductor body 1 and portions of the electrical terminals 2, 3 are enclosed by a further transparent housing envelope 10. The latter causes no change in wavelength of the radiation that has passed through the layer 4, and it is made for instance from a transparent epoxy resin that as usable in LED technology, or from glass.


Such semiconductor bodies 1 provided with a layer 4 and without an envelope can naturally advantageously be used in all the housing constructions known from LED technology (such as SMD housings, and radial housings; see FIG. 4).


In all the components described above, in order to optimize the color impression of the light emitted and to adapt the emission characteristics, the casting composition 5, optionally the transparent envelope 15, and/or optionally the further transparent envelope 10 may have light-scattering particles, advantageously so-called diffusers. Examples of such diffusers are mineral fillers, in particular CaF2, TiO2, SiO2, CaCO3, or BaSO4, or organic pigments. These materials can easily be added to epoxy resins.



FIGS. 6–8 illustrate emissions spectra. FIG. 6 refers to a semiconductor body that emits blue light (luminescence maximum at λ˜430 nm) and FIGS. 7 and 8 refer to semiconductor components that emit white light. In each case, the wavelength λ is plotted in nm on the abscissa, and a relative electroluminescence (EL) intensity is plotted on the ordinate.


Of the radiation emitted by the semiconductor body in FIG. 6, only some is converted into a longer-wavelength range, so that white light is created as the mixed color. The dashed line 30 in FIG. 7 represents an emissions spectrum of a semiconductor component which emits radiation comprising two complementary wavelength ranges (blue and yellow) and thus emits combined white light. The emissions spectrum here has one maximum each at wavelengths between approximately 400 and approximately 430 nm (blue) and between approximately 550 and 580 nm (yellow). The solid line 31 represents the emissions spectrum of a semiconductor component that mixes the color white from three wavelength ranges (additive color triad comprising blue, green and red). The emissions spectrum here has one maximum each for the wavelengths of approximately 430 nm (blue), approximately 500 nm (green) and approximately 615 nm (red).



FIG. 8 shows an emissions spectrum of a white-emitting semiconductor component, which is provided with a semiconductor body that transmits an emissions spectrum as shown in FIG. 6 and in which TAG:Ce is used as the luminous substance. Of the radiation shown in FIG. 6 emitted by the semiconductor body, only some is converted into a longer-wavelength range, so that white light is created as a mixed color. The variously dashed lines 3233 of FIG. 8 represent emissions spectra of semiconductor components according to the invention, in which the epoxy resin of the casting composition 5 has different YAG:Ce concentrations. Each emissions spectrum has one maximum intensity between lambda=420 nm and lambda=430 nm (i.e., in the blue spectrum), and between lambda=520 nm and lambda=545 nm (i.e., in the green spectrum). The emission bands having the longer-wavelength maximum intensity are predominantly located in the yellow spectral range. The graph of FIG. 8 shows that in the semiconductor component of the invention, the CIE color location of the white light can be varied in a simple way by varying the luminous substance concentration in the epoxy resin.


While the foregoing specification refers specifically to a semiconductor body, for example LED chips or laser diode chips, the invention is not in the least restricted to these embodiments. The term may also be understood to mean a polymer LED, or instance, that emits an equivalent radiation spectrum.

Claims
  • 1. Light emitting semiconductor body for use in an LED housing, said semiconductor body being provided with a layer comprising a wavelength-converting casting composition; andsaid casting composition comprising luminous substance particles;said luminous substance particles comprising luminous substance pigments selected from the group consisting of garnets doped with rare earths; thiogallates doped with rare earths; aluminates doped with rare earths; and orthohsilicates doped with rare earths; andsaid luminous substance pigments having grain sizes ≦20 μm and a median diameter ≦5 μm, wherein 50% of the pigments have a grain diameter greater than said median diameter and 50% of the pigments have a grain diameter less than said median diameter.
  • 2. Semiconductor body according to claim 1, wherein the median diameter of said luminous substance pigments is between 1 and 2 micrometers.
  • 3. Semiconductor body according to claim 1, wherein said luminous substance pigments contain Ce-doped garnet material.
  • 4. Semiconductor body according to claim 1, wherein said luminous substance pigments contain YAG:Ce material.
  • 5. Semiconductor body according to claim 1, wherein the iron content in the casting composition is ≦20 ppm.
  • 6. Semiconductor body according to claim 1, wherein the luminous substance pigments are provided with a silicone coating.
  • 7. Semiconductor body according to claim 1, wherein said luminous substance pigments convert radiation from the ultraviolet, blue or green spectral range into light with a relatively longer wavelength.
  • 8. Semiconductor body according to claim 1, wherein said layer containing light-scattering particles.
  • 9. Semiconductor body according to claim 1, wherein said semiconductor body is adapted to emit radiation in a blue spectral range having a maximum luminescence intensity at a wavelength between 420 nm and 460 nm.
  • 10. Semiconductor body according to claim 1, wherein the casting composition further comprises a transparent resin.
  • 11. Semiconductor body according to claim 10, wherein the transparent resin is an epoxy resin.
  • 12. Light emitting semiconductor body for use in an LED housing, said semiconductor body being provided with a layer comprising a wavelength-converting casting composition; andsaid casting composition comprising luminous substance particles;said luminous substance particles comprising luminous substance pigments from Ce-doped phosphors; andsaid luminous substance pigments having grain sizes ≦20 μm, and a median diameter ≦5 μm, wherein 50% of the pigments have a grain diameter greater than said median diameter and 50% of the pigments have a grain diameter less than said median diameter.
  • 13. Semiconductor body according to claim 12, wherein the median diameter of said luminous substance pigments is between 1 and 2 micrometers.
  • 14. Semiconductor body according to claim 12, wherein the iron content in the casting composition is ≦20 ppm.
  • 15. Semiconductor body according to claim 12, wherein the luminous substance pigments are provided with a silicone coating.
  • 16. Semiconductor body according to claim 12, wherein said luminous substance pigments convert radiation from the ultraviolet, blue or green spectral range into light with a relatively longer wavelength.
  • 17. Semiconductor body according to claim 12, wherein said layer containing light-scattering particles.
  • 18. Semiconductor body according to claim 12, wherein said semiconductor body is adapted to emit radiation in a blue spectral range having a maximum luminescence intensity at a wavelength between 420 nm and 460 nm.
  • 19. Semiconductor body according to claim 12, wherein the casting composition further comprises a transparent resin.
  • 20. Semiconductor body according to claim 19, wherein the transparent resin is an epoxy resin.
Priority Claims (1)
Number Date Country Kind
196 38 667 Sep 1996 DE national
CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation (and claims the benefit of priority under 35 USC 120) of U.S. application Ser. No. 09/843,080, filed Apr. 25, 2001, now U.S. Pat No. 6.592,780, which is a continuation of U.S. application Ser. No. 09/650,932, filed Aug. 29, 2000, now U.S. Pat. No. 6,245,259, which is a division of application Ser. No. 09/536,564, filed Mar. 28, 2000, now U.S. Pat. No. 6,277,301, which is a division of application Ser. No. 09/082,205, filed May 20, 1998, now U.S. Pat. No. 6,066,861, which was a continuation of international application PCT/DE97/02 139, filed Sep. 22, 1997, which designated the United States.

US Referenced Citations (144)
Number Name Date Kind
2096693 Cox Oct 1937 A
2192869 Pearce Mar 1940 A
3312851 Flowers et al. Apr 1967 A
3316109 Rimbach Apr 1967 A
3440471 Baczewski et al. Apr 1969 A
3453604 Geusic et al. Jul 1969 A
3483416 Vermeulen Dec 1969 A
3510732 Amans May 1970 A
3529200 Potter Sep 1970 A
3565815 Christy Feb 1971 A
3573568 Siegel Apr 1971 A
3593055 Geusic Jul 1971 A
3602758 Thorton Aug 1971 A
3621340 Singh Nov 1971 A
3654463 Geusic et al. Apr 1972 A
3659136 Grodkiewicz Apr 1972 A
3691482 Pinnow et al. Sep 1972 A
3699478 Pinnow et al. Oct 1972 A
3700479 Arents Oct 1972 A
3715611 De Mesquita et al. Feb 1973 A
3740616 Suzuki et al. Jun 1973 A
3742277 Peters Jun 1973 A
3742833 Sewell et al. Jul 1973 A
3743833 Mantic et al. Jul 1973 A
3774086 Vincent, Jr. Nov 1973 A
3787684 Isenberg Jan 1974 A
3819974 Stevenson et al. Jun 1974 A
3822215 Grodkiewicz Jul 1974 A
3875456 Kano et al. Apr 1975 A
3932881 Mita Jan 1976 A
3942185 Lebailly Mar 1976 A
3976877 Thillays Aug 1976 A
4093890 Verriet et al. Jun 1978 A
4139657 Watanabe Feb 1979 A
4146790 Goetzberger et al. Mar 1979 A
4173495 Rapp et al. Nov 1979 A
4178274 Denk et al. Dec 1979 A
4203792 Thompson May 1980 A
4262206 Viehmann Apr 1981 A
4298820 Bongers et al. Nov 1981 A
4307297 Groff et al. Dec 1981 A
4365052 Reeh et al. Dec 1982 A
4431941 Roy et al. Feb 1984 A
4479886 Kasenga Oct 1984 A
4495514 Lawrence et al. Jan 1985 A
4550256 Berkstresser et al. Oct 1985 A
4599537 Yamashita Jul 1986 A
4684592 Matsuda et al. Aug 1987 A
4707635 Tateyama et al. Nov 1987 A
4710674 Sigai Dec 1987 A
4716337 Huiskes et al. Dec 1987 A
4727283 Van Kemenade et al. Feb 1988 A
4734619 Havel Mar 1988 A
4758449 Kimura et al. Jul 1988 A
4780752 Angerstein et al. Oct 1988 A
4816369 Matsuda et al. Mar 1989 A
4818434 Lindmayer Apr 1989 A
4818983 Hara et al. Apr 1989 A
4825124 Sigai Apr 1989 A
4843280 Lumbard et al. Jun 1989 A
4851695 Stein Jul 1989 A
4875750 Spaeth et al. Oct 1989 A
4894583 Berkstresser et al. Jan 1990 A
4935856 Dragoon Jun 1990 A
5003181 Morlotti Mar 1991 A
5019746 Merg May 1991 A
5035483 Waitl et al. Jul 1991 A
5035513 Fehrenbach et al. Jul 1991 A
5107317 Takasaki Apr 1992 A
5126214 Tokailin et al. Jun 1992 A
5166456 Yoshino Nov 1992 A
5184114 Brown Feb 1993 A
5196763 Yang et al. Mar 1993 A
5202777 Sluzky et al. Apr 1993 A
RE34254 Dragoon May 1993 E
5208462 O'Conner et al. May 1993 A
5256725 Takada et al. Oct 1993 A
5294897 Notani et al. Mar 1994 A
5369289 Tamaki et al. Nov 1994 A
5379186 Gold et al. Jan 1995 A
5382452 Bruno et al. Jan 1995 A
5387836 Adachi et al. Feb 1995 A
5417886 Tateiwa et al. May 1995 A
5424573 Kato et al. Jun 1995 A
5432358 Nelson et al. Jul 1995 A
5471113 DeBacker et al. Nov 1995 A
5479050 Pritchard et al. Dec 1995 A
5535230 Abe Jul 1996 A
5543657 Diffenderfer et al. Aug 1996 A
5545386 Kaneyoshi et al. Aug 1996 A
5578839 Nakamura et al. Nov 1996 A
5600202 Yamada et al. Feb 1997 A
5602418 Imai et al. Feb 1997 A
5607621 Ishihara et al. Mar 1997 A
5624602 Lenox et al. Apr 1997 A
5635110 Chadha et al. Jun 1997 A
5643674 Bruno et al. Jul 1997 A
5652438 Sassa et al. Jul 1997 A
5656832 Ohba et al. Aug 1997 A
5665793 Anders Sep 1997 A
5670798 Schetzina Sep 1997 A
5685071 Gates, Jr. et al. Nov 1997 A
5707549 Matsukiyo et al. Jan 1998 A
5744233 Opitz et al. Apr 1998 A
5747832 Nakamura et al. May 1998 A
5772916 Jamil et al. Jun 1998 A
5788881 Chadha et al. Aug 1998 A
5798537 Nitta Aug 1998 A
5813752 Singer et al. Sep 1998 A
5813753 Vriens et al. Sep 1998 A
5847507 Butterworth et al. Dec 1998 A
5863810 Kaldenberg Jan 1999 A
5879647 Wataya et al. Mar 1999 A
5906771 Watkins et al. May 1999 A
5952036 Tadaki et al. Sep 1999 A
5959316 Lowery Sep 1999 A
5994722 Averbeck et al. Nov 1999 A
5998925 Shimizu et al. Dec 1999 A
6066861 Hohn et al. May 2000 A
6069440 Shimizu et al. May 2000 A
6078063 Nakamura et al. Jun 2000 A
6085971 Tews et al. Jul 2000 A
6140040 Palm et al. Oct 2000 A
6180029 Hampden-Smith et al. Jan 2001 B1
6245259 Hohn et al. Jun 2001 B1
6277301 Hohn et al. Aug 2001 B1
6295750 Harwell et al. Oct 2001 B1
6455213 Lee Sep 2002 B1
6576930 Reeh et al. Jun 2003 B2
6592780 Hohn et al. Jul 2003 B2
6596141 Rasmussen Jul 2003 B2
6600175 Baretz et al. Jul 2003 B1
6613247 Hohn et al. Sep 2003 B1
6666993 Milewski Dec 2003 B2
6692659 Brown et al. Feb 2004 B2
6803719 Miller et al. Oct 2004 B1
6812500 Reeh et al. Nov 2004 B2
20010030326 Reeh et al. Oct 2001 A1
20010045647 Höhn et al. Nov 2001 A1
20040016908 Hohn et al. Jan 2004 A1
20040016938 Baretz et al. Jan 2004 A1
20040094757 Braune et al. May 2004 A1
20050127385 Reeh et al. Jun 2005 A1
20050161694 Reeh et al. Jul 2005 A1
Foreign Referenced Citations (142)
Number Date Country
1 007 825 Oct 1995 BE
1915290 Oct 1969 DE
2018353 Oct 1970 DE
2018354 Oct 1970 DE
2059909 Jun 1971 DE
7128442 Dec 1971 DE
2347289 Apr 1974 DE
26 42 465 Mar 1978 DE
3315675 Nov 1983 DE
2835184 Sep 1986 DE
3804293 Aug 1989 DE
3804293 Aug 1989 DE
90 13 615 Jan 1991 DE
9013615.2 Jan 1991 DE
44 32 035 Mar 1996 DE
4432035 Mar 1996 DE
196 38 667 Apr 1998 DE
196 38 667 Apr 1998 DE
29724458 May 2001 DE
297 24 381 Dec 2001 DE
0 039 017 Nov 1981 EP
0333162 Sep 1989 EP
0 387 715 Sep 1990 EP
0486052 May 1992 EP
0 862 794 Sep 1998 EP
0936682 Aug 1999 EP
2004989 Dec 1969 FR
2043403 Feb 1971 FR
2044727 Feb 1971 FR
2073134 Sep 1971 FR
1263185 Feb 1972 GB
1317731 May 1973 GB
1317732 May 1973 GB
1332462 Oct 1973 GB
2000173 Jan 1979 GB
2053953 Feb 1981 GB
1589964 May 1981 GB
2149416 Jun 1985 GB
46-7462 Dec 1971 JP
47-17684 Sep 1972 JP
48-6962 Mar 1973 JP
46-39866 Jun 1973 JP
49-1221 Jan 1974 JP
49-24355 Mar 1974 JP
49-112577 Oct 1974 JP
49-122292 Nov 1974 JP
50-43913 Apr 1975 JP
50-74875 Jun 1975 JP
51145288 Dec 1976 JP
52-009334 Jan 1977 JP
52009334 Jan 1977 JP
52-40959 Mar 1977 JP
52-45181 Oct 1977 JP
53001180 Jan 1978 JP
53-100787 Sep 1978 JP
54-41660 May 1979 JP
54-066093 May 1979 JP
55-5533 Jan 1980 JP
55004898 Jan 1980 JP
56-1224 Jan 1981 JP
56-058884 May 1981 JP
58-043584 Mar 1983 JP
59-50455 Apr 1984 JP
60-185457 Sep 1985 JP
61-240680 Oct 1986 JP
61-248839 Nov 1986 JP
60090680 Nov 1986 JP
62020237 Jan 1987 JP
62-94659 Jun 1987 JP
62201989 Sep 1987 JP
62-232827 Oct 1987 JP
63-280467 Nov 1988 JP
64-071053 Mar 1989 JP
1-189695 Jul 1989 JP
1175103 Jul 1989 JP
01179471 Jul 1989 JP
1260707 Oct 1989 JP
02011694 Jan 1990 JP
2-91980 Mar 1990 JP
2080970 Mar 1990 JP
2-138361 May 1990 JP
2138361 May 1990 JP
03220286 Sep 1991 JP
03287690 Dec 1991 JP
4110236 Apr 1992 JP
4-63162 May 1992 JP
4-63163 May 1992 JP
04137570 May 1992 JP
4142070 May 1992 JP
4-175265 Jun 1992 JP
4-38538 Sep 1992 JP
5-38926 May 1993 JP
5-152609 Jun 1993 JP
5-63068 Aug 1993 JP
05315652 Nov 1993 JP
05315653 Nov 1993 JP
05315624 Dec 1993 JP
5335624 Dec 1993 JP
05347432 Dec 1993 JP
6013075 Jan 1994 JP
6017130 Jan 1994 JP
06053554 Feb 1994 JP
6-69546 Mar 1994 JP
06-077540 Mar 1994 JP
06076754 Mar 1994 JP
6085314 Mar 1994 JP
06 104491 Apr 1994 JP
06163988 Jun 1994 JP
6-208845 Jul 1994 JP
06204570 Jul 1994 JP
6-268257 Sep 1994 JP
6279568 Oct 1994 JP
06306356 Nov 1994 JP
7-99345 Apr 1995 JP
00799345 Apr 1995 JP
7-42152 Jul 1995 JP
7-176794 Jul 1995 JP
07-176794 Jul 1995 JP
7-193281 Jul 1995 JP
07-292354 Nov 1995 JP
8-7614 Jan 1996 JP
08007614 Jan 1996 JP
08-032120 Feb 1996 JP
00864860 Mar 1996 JP
08-096958 Apr 1996 JP
09 027642 Jan 1997 JP
9028642 Feb 1997 JP
9-73807 Mar 1997 JP
0810101997 Mar 1997 JP
1985851996 May 1997 JP
2443391996 May 1997 JP
2453811996 May 1997 JP
3590041996 May 1997 JP
10 012925 Jan 1998 JP
8-92549 Apr 1998 JP
10-242513 Sep 1998 JP
2927229 May 1999 JP
11-220174 Aug 1999 JP
9623030 Aug 1996 WO
9748138 Dec 1997 WO
WO9812757 Mar 1998 WO
WO9805078 May 1998 WO
Related Publications (1)
Number Date Country
20040084687 A1 May 2004 US
Divisions (2)
Number Date Country
Parent 09536564 Mar 2000 US
Child 09650932 US
Parent 09082205 May 1998 US
Child 09536564 US
Continuations (3)
Number Date Country
Parent 09843080 Apr 2001 US
Child 10616783 US
Parent 09650932 Aug 2000 US
Child 09843080 US
Parent PCT/DE97/02139 Sep 1997 US
Child 09082205 US