Patent Application
20240287658
The present invention relates generally to 3D-printed hydrogen storage systems using non-pyrophoric AB2 Laves phase hydrogen storage alloy.
Not applicable.
Hydrogen, generally considered to be the ultimate fuel, presents numerous potential benefits to be realized as well as numerous difficulties to be overcome. With capacity to serve as a fuel for combustion engines, other processes in which heat energy is derived from combustion and used; as well as a direct source of electrochemical energy in direct conversion processes such as, for example, those used in electrochemical fuel cells, hydrogen presents opportunities for production of energy without the creation of waste products bearing disposal difficulties.
The products of hydrogen combustion, whether thermal or electrochemical, are energy and water. Neither of these is toxic, neither presents difficulties of disposal of greenhouse gases, soot, or radioactive waste. From the standpoint of being a useful, high-energy content fuel, hydrogen is an excellent candidate for most of the uses in which fossil fuels are currently used. When used for direct conversion to electrical energy in a fuel cell, hydrogen does not yield oxides of carbon which often poison catalytic material used in such electrochemical cells, nor is radioactive waste generated as is the case with electricity-supplying nuclear-powered generators.
With these tremendous benefits accruing to its use as a fuel, some burdens in the use of hydrogen as a fuel may be expected. They are present and provide challenges to overcome. The greatest difficulties with hydrogen as a fuel lie in its containment and transportation. Hydrogen may be liquefied but there is tremendous cost involved in cooling and compressing; additionally, the containment vessel cannot be completely sealed; tremendous losses are incurred through evaporation. Compression of the gas itself is costly, although not nearly so much as liquefaction, and requires stout, durable, and heavy containers. Both are inefficient forms of storage in terms of energy storage per unit volume. Other storage means would be useful.
Various metals and metal alloy compositions are available for storage of hydrogen within the metallic crystal lattice, generally as a hydride. Metal hydride systems have the advantage of storing hydrogen at high density for long periods of time because they are formed by inserting hydrogen atoms into the crystal lattice of the metal. Storage of hydrogen as a solid is appealing as enhanced volumetric efficiency is available. Such materials will generally release heat upon charging, take-up of hydrogen, absorption of hydrogen, or hydriding. Conversely, heat is necessary to release stored hydrogen from the metallic structure.
Reversible metal hydrides are a broad class of materials that undergo a reversible reaction with hydrogen. Overall reversible reaction is written as:
where M is the hydridable alloy, MHx is the metal hydride and AH is the heat of formation of the metal hydride. The hydridable alloy surfaces serving to catalyze the breakup of hydrogen molecules into hydrogen atoms will be helpful prior to this reaction. The absorption reaction is exothermic, whereas the desorption reaction is endothermic. During this reaction, the metal lattice expands with the absorption of hydrogen, and the metal structure shrinks with the desorption of hydrogen, so the hydrogen storage alloy will usually have a larger effective surface area or smaller particles. When they are exposed to air, there is another possible reaction of these alloys:
The metal powder has a huge heat-generating reaction with oxygen, causing the surface temperature to rise significantly. High temperature causes the instability of the surface oxide layer, leading to a chain reaction between the metal powder and oxygen. This is known as pyrophoricity.
This spontaneous combustion means that the material must be specially handled by continuously providing a non-oxidative atmosphere/environment. From the perspective of distribution and improvement of hydrogen storage capacity, more importantly, the spontaneous combustion properties of these materials require special treatment during transportation. Their transportation methods are also severely restricted; usually, for example, due to their pyrophoric nature, such materials cannot usually be transported by air. Therefore, the pyrophoric nature of certain hydrogen storage alloys is one of the main safety issues related to the commercial use of hydrogen storage in the form of hydride alloys.
A series of non-pyrophoric metal hydrides are disclosed in U.S. Pat. Nos. 6,517,970 and 6,737,194 to Ovshinsky, et al., entitled “Non-pyrophoric hydrogen storage alloy”.
The patents state that the Ovshinsky alloys:
Unfortunately, compared with traditional metal hydrides, these prior art non-pyrophoric materials have a pressure composition temperature (PCT) curve with a relatively high slope and greater hydrogen trapping. This trapping reduces the reversible storage capacity of the alloys and creates various difficulties in practical application. New advanced materials with non-pyrophoricity, as well as high reversible capacity, low PCT curve slope (flattened plateau pressure), tailored plateau pressures and low material cost, are desired to meet the requirement of present-day hydrogen storage systems.
The ideal hydrogen storage material for large-scale commercial use must have:
If the material is missing any of these characteristics, it will be unfeasible for large-scale commercial use.
In many applications, especially when the hydride is used in mobile applications, the hydrogen storage capacity per unit weight of material is an important consideration. Relative to the weight of the material, the low hydrogen storage capacity can, for instance, reduce the mileage and therefore the driving range of hydrogen fuel vehicles using this material. To reduce the energy required to release hydrogen, a low desorption temperature/high plateau pressure is required. Also, to effectively utilize the available waste heat from vehicles, machinery, fuel cells or other similar equipment, a relatively low desorption temperature is required to release stored hydrogen.
Therefore, there is a need in the art for hydrogen storage materials that are non-pyrophoric, have a high reversible hydrogen storage capacity, a low hydrogen desorption temperature/high plateau pressure, a relatively flat PCT isotherm curve plateau pressure, a low hysteresis, low trapping, and low materials cost.
The present invention comprises a hydrogen storage system. The hydrogen storage system may include a hydrogen storage alloy containment vessel. The hydrogen storage alloy containment vessel may include an external pressure containment vessel. The hydrogen storage alloy containment vessel may also include a thermally conductive compartmentalization network disposed within the external pressure containment vessel. The thermally conductive compartmentalization network may create compartments within the external pressure containment vessel within which a hydrogen storage alloy may be disposed.
The hydrogen storage alloy containment vessel may further include a hydrogen storage alloy disposed therein. The hydrogen storage alloy may be a non-pyrophoric AB2 Laves phase hydrogen storage alloy. The alloy may have an A-site to B-site elemental ratio of not more than about 0.5. The alloy may have an alloy composition including about (in at %): Zr: 2.0-5.5, Ti: 27-31.3, V: 8.3-9.9, Cr: 20.6-30.5, Mn: 25.4-33.0, Fe: 1.0-5.9, and Al: 0.1-0.4. More preferably, the alloy may have an alloy composition including about (in at %): Zr: 2.9-5.5, Ti: 27-30.3, V: 8.3-9.3, Cr: 20.6-26.5, Mn: 29.4-32.1, Fe: 1.5-5.9, and Al: 0.1-0.4.
The non-pyrophoric AB2 Laves phase hydrogen storage alloy may further include up to about 4 at % nickel as an equal substitute for up to about 2 at % chromium or up to about 2 at % manganese or both. The alloy may have a total hydrogen storage capacity of at least about 1.7 wt % or 1.8 wt % at about 500 psi and about 20° C. The alloy may further have a trapped hydrogen capacity of not more than about 0.25 wt % (preferably not more than about 0.2 wt % and more preferably not more than about 0.15 wt % or 0.10 wt %) at about 14.5 psi and about 20° C.
The hydrogen storage alloy may have a PCT isotherm slope of no more than about 0.8 (preferably not more than about 0.7 or 0.6). The non-pyrophoric AB2 Laves phase hydrogen storage alloy may have a hysteresis of not more than about 0.5 or 0.4 (preferably not more than about 0.3 and more preferably not more than about 0.2 or 0.1).
The alloy may also contain about 1-10 at % total of at least one element selected from the group consisting of Ba, Co, Cu, Cs, K, Li, Mm, Mo, Na, Nb, Ni, Rb, Ta, Tl, and W (where Mm is mischmetal).
One or both of the external pressure containment vessel and the thermally conductive compartmentalization network may be fabricated by 3D printing processes. Both of the external pressure containment vessel and the thermally conductive compartmentalization network may be fabricated simultaneously as a single unit by a 3D printing process.
The thermally conductive compartmentalization network may be fabricated by a 3D metal printing process, in which the highly thermally conductive printed metal is selected from the group consisting of aluminum, aluminum alloys, copper, copper alloys, magnesium and magnesium alloys. The 3D metal printing process may comprise deposition by Selective Laser Melting (SLM) and/or Direct Metal Laser Sintering (DMLS).
In addition, the present invention comprises a method of fabricating the hydrogen storage system by fabricating the thermally conductive compartmentalization network disposed within said external pressure containment vessel via a 3D printing process, and depositing the hydrogen storage alloy within said hydrogen storage alloy containment vessel.
Both the external pressure containment vessel and the thermally conductive compartmentalization network may be fabricated by the 3D printing process. Both the external pressure containment vessel and the thermally conductive compartmentalization network may be fabricated simultaneously as a single unit by the 3D printing process. The 3D printing process may comprise deposition by Selective Laser Melting (SLM) and/or Direct Metal Laser Sintering (DMLS).
The thermally conductive compartmentalization network may be fabricated by the 3D printing process, in which a highly thermally conductive printed metal is selected from the group consisting of: aluminum, aluminum alloys, copper, copper alloys, magnesium and magnesium alloys. The 3D printing process may comprise deposition by Selective Laser Melting (SLM) and/or Direct Metal Laser Sintering (DMLS).
For a more complete understanding of the features and advantages of the present invention, reference is now made to the detailed description of the invention along with the accompanying figures and in which:
The present invention is a non-pyrophoric, AB2 Laves phase hydrogen storage alloy and hydrogen storage systems using the alloys. The alloy may preferably have an A-site to B-site elemental ratio of about <=0.5. The alloy may preferably have a total hydrogen storage capacity of at least about 1.7 wt % or 1.8% wt % at about 500 psi and about 20° C. The alloy may further have a trapped hydrogen capacity of not more than about 0.25 wt % (preferably not more than about 0.2 wt % and more preferably not more than about 0.15 wt % or 0.1 wt %) at about 14.5 psi and about 20° C.
The hydrogen storage alloy may have a pressure composition temperature (PCT) isotherm slope of no more than about 0.8 (preferably not more than about 0.7 or 0.6). The non-pyrophoric AB2 Laves phase hydrogen storage alloy may have a hysteresis of not more than about 0.5 or 0.4 (preferably not more than about 0.3 and more preferably not more than about 0.2 or 0.1).
Broadly, the inventive hydrogen storage alloy contains about (in at %): Zr: 2.0-5.5, Ti: 27-31.3, V: 8.3-9.9, Cr: 20.6-30.5, Mn: 25.4-33.0, Fe: 1.0-5.9, and Al: 0.1-0.4.
More narrowly, the inventive hydrogen storage may contain about (in at %): Zr: 2.9-5.5, Ti: 27-30.3, V: 8.3-9.3, Cr: 20.6-26.5, Mn: 26.4-32.1, Fe: 1.5-5.9, and Al: 0.1-0.4.
The alloy may also contain about 1-10 at % total of at least one element selected from the group consisting of Ba, Co, Cu, Cs, K, Li, Mm, Mo, Na, Nb, Ni, Rb, Ta, Tl, and W (where Mm is mischmetal). Low electronegativity elements (such Ba, Cs, K, Li, Na, Rb, Mm) can purify the alloy by reacting with impurity oxides, while relatively high electronegativity elements (such as Co, Cu, Mo, Nb, Ta, Tl and W) can be dissolved in AB2 Laves phase to improve hydriding properties.
The non-pyrophoric AB2 Laves phase hydrogen storage alloy may further include up to about 4 at % nickel as an equal substitute for up to about 2 at % chromium or up to about 2 at % manganese or both. Addition of nickel to the alloys can help to reduce hysteresis due to its highly catalytic nature and ductility. Nickel can also prevent the formation of body-centered cubic (BCC) secondary phase in alloys since its alloys have a higher averaging number of outer electrons.
To achieve non-pyrophoricity on exposure to ambient atmosphere, the at % of ductility-enhancing elements have been increased and the at % of brittle-enhancing elements have been decreased to reduce the inventive alloy material's decrepitation. Hydrogen embrittles metals by entering the grain boundaries and creating pressure at the weakest point. This causes micro-cracks that begin to propagate through the grain structure. This process is known as decrepitation. Decrepitation is the main reason for the loss of capacity during long cycling. Usually, high content manganese alloys are prone to decrepitation because manganese is a highly brittle element. Alternatively, vanadium, chromium or nickel containing alloys have less decrepitation issues.
Table 1 lists the compositions and properties of non-pyrophoric alloys of the present invention, two typical pyrophoric alloys and the prior art alloy of the Ovshinsky patents.
Another advantage of the higher content of ductility enhancing elements, such as vanadium and chromium, of the inventive hydrogen storage alloys can increase the ductility of the metal hydride alloy, which in turn, reduces hysteresis.
To understand hysteresis, it should be noted that one of the most important features of a metal hydride storage system is its plateau pressure, which indicates the pressure at which metal hydrides reversibly absorb/desorb large quantities of hydrogen. Generally, there is a difference between equivalent pressures for absorption and desorption in the pressure-composition isotherms. This differential in absorption and desorption pressure is known as hysteresis.
For example, compared with the low hysteresis (0.143) HA1036, the low vanadium and chromium HA697 and HA703 alloys have high hysteresis values of 0.827 and 0.616, respectively, as shown in
The vanadium and manganese contents strongly affect the hysteresis of AB2 Laves phase hydrogen storage alloys, while the effect of the chromium is relatively weak. High vanadium content can significantly reduce the hysteresis, while high manganese content does the opposite.
Another reason why the inventive, high vanadium and chromium, hydrogen storage alloys tend not to catch fire is that V and Cr tend to form dense oxide layers that can protect the alloy from further oxidation (i.e. pyrophoric burning). Alternatively, manganese and iron form porous oxide layers that cannot protect the alloy from further contacting and reacting with oxygen.
Unfortunately, a high content of vanadium and chromium in AB2 Laves phase alloys tends to form a secondary body-centered cubic (BCC) phase. The BCC phase is a disordered structure of solid solution atoms and requires elements with similar atomic sizes and low external electrons. Generally speaking, there is a body-centered cubic phase in which the average number of external electrons is less than 5.4. Therefore, the high content of titanium, vanadium and chromium in such alloys promote the formation of the BCC phase due to their similar atomic size and lower number of external electrons.
The existence of this secondary BCC phase distorts the flatness of the plateau pressure of the PCT isotherms because the BCC phase has two hydride structures. These include a BCC phase where hydrogen atoms occupy octahedral sites and a face-centered cubic (FCC) phase where hydrogen atoms are located in tetrahedral sites. Usually, the hydrogen in large octahedral sites of the BCC hydride phase is irreversible, thereby trapping a huge amount of hydrogen, while the hydrogen in the small tetrahedral sites of the FCC phase is reversible, but plateau pressures of the FCC phase may not be the range of AB2 Laves phase alloys.
Since manganese has a larger atomic radius and a high number of external electrons, a high content of manganese can prevent the formation of a second BCC phase in the AB2 Laves phase. Therefore, the high-content manganese AB2 alloy has a relatively flat plateau pressure but has a high degree of self-ignitability and high hysteresis. In order to achieve non-ignition and low hysteresis, the manganese content in AB2 alloy should not exceed about 33 at %. More preferably the manganese does not exceed about 32 at %.
Adding zirconium to the alloys can help to reduce the formation of the secondary BCC phase. This is because zirconium atoms are large and do not like to form disordered solid solution phases with titanium, vanadium and chromium. The addition of Zr to AB2 alloys can result in hydrogen storage alloys having high thermal stability and low plateau pressures. This is because of zirconium's large radius and low electronegativity.
For AB2 Laves phase alloys, the Zr/Ti ratio controls the tetrahedral interstitial sites and average electronegativity, as well as determining plateau pressures. Lower Zr/Ti values facilitate the formation of alloys with high plateau pressures while higher values result in lower plateau pressures. Thus, the plateau pressure can be, at least somewhat, tailored to the needs of the end use of the hydrogen storage alloys.
In AB2 Laves phase, the A/B ratio can affect plateau flatness. The A/B ratio has been slightly reduced to less than or equal to 0.5 to limit formation of any secondary BCC phase. This is because A-site elements, which have low outer electron numbers, favor the formation of the BCC disordered solid solution phase. Therefore, alloys that are lean in A-site elements limit the secondary phase. The existence of the secondary BCC phase can destroy the flatness of the plateau because the BCC phase has two hydride structures, that is, the BCC phase where hydrogen atoms occupy octahedral sites and the FCC phase where hydrogen atoms are located at tetrahedral sites. The hydrogen stored at the octahedral sites of the BCC hydride phase is irreversible at reasonable pressures and temperatures, thus forming hydrogen traps in the metal lattice. Although the hydrogen at tetrahedral sites of the FCC phase is reversible, the plateau pressures are not as useful as those in the AB2 Laves phase.
While decrepitation is the main reason for the loss of capacity during long cycling and pyrophoric burning, another reason is partly related to the stresses and strains of charging/discharging cycling. High hysteresis usually exhibits high stresses and strains, thereby resulting in high decrepitation. Some elements, such as vanadium, chromium and nickel, could reduce this disadvantage in such materials.
The price of pure vanadium is several times higher than ferrovanadium. Replacement of pure vanadium with low-cost ferrovanadium will significantly reduce cost of materials to produce the alloys. Typically, ferrovanadium alloy contains 15%-17% Fe and 1%-2% Al. Iron negatively affects the flammability and high hysteresis of AB2 Laves phase alloys, while aluminum negatively affects capacity and platform flatness, resulting in lower levels of both elements and better performance. Table 3 lists the compositions and properties of non-pyrophoric alloys with low Fe contents of the present invention.
The Zr can be about 2.0 at %, 2.1 at %, 2.2 at %, 2.3 at %, 2.4 at %, 2.5 at %, 2.6 at %, 2.7 at %, 2.8 at %, 2.9 at %, 3.0 at %, 3.1 at %, 3.2 at %, 3.3 at %, 3.4 at %, 3.5 at %, 3.6 at %, 3.7 at %, 3.8 at %, 3.9 at %, 4.0 at %, 4.1 at %, 4.2 at %, 4.3 at %, 4.4 at %, 4.5 at %, 4.6 at %, 4.7 at %, 4.8 at %, 4.9 at %, 5.0 at %, 5.1 at %, 5.2 at %, 5.3 at %, 5.4 at %, 5.5 at % or other incremental at % between.
The Ti can be about 27.0 at %, 27.1 at %, 27.2 at %, 27.3 at %, 27.4 at %, 27.5 at %, 27.6 at %, 27.7 at %, 27.8 at %, 27.9 at %, 28.0 at %, 28.1 at %, 28.2 at %, 28.3 at %, 28.4 at %, 28.5 at %, 28.6 at %, 28.7 at %, 28.8 at %, 28.9 at %, 29.0 at %, 29.1 at %, 29.2 at %, 29.3 at %, 29.4 at %, 29.5 at %, 29.6 at %, 29.7 at %, 29.8 at %, 29.9 at %, 30.0 at %, 30.1 at %, 30.2 at %, 30.3 at %, 30.4 at %, 30.5 at %, 30.6 at %, 30.7 at %, 30.8 at %, 30.9 at %, 31.0 at %, 31.1 at %, 31.2 at %, 3.3 at % or other incremental at % between.
The V can be about 8.3 at %, 8.4 at %, 8.5 at %, 8.6 at %, 8.7 at %, 8.8 at %, 8.9 at %, 9.0 at %, 9.1 at %, 9.2 at %, 9.3 at %, 9.4 at %, 9.5 at %, 9.6 at %, 9.7 at %, 9.8 at %, 9.9 at % or other incremental at % between.
The Cr can be about 20.6 at %, 20.7 at %, 20.8 at %, 20.9 at %, 21.0 at %, 21.1 at %, 21.2 at %, 21.3 at %, 21.4 at %, 21.5 at %, 21.6 at %, 21.7 at %, 21.8 at %, 21.9 at %, 22.0 at %, 22.1 at %, 22.2 at %, 22.3 at %, 22.4 at %, 22.5 at %, 22.6 at %, 22.7 at %, 22.8 at %, 22.9 at %, 23.0 at %, 23.1 at %, 23.2 at %, 23.3 at %, 23.4 at %, 23.5 at %, 23.6 at %, 23.7 at %, 23.8 at %, 23.9 at %, 24.0 at %, 24.1 at %, 24.2 at %, 24.3 at %, 24.4 at %, 24.5 at %, 24.6 at %, 24.7 at %, 24.8 at %, 24.9 at %, 25.0 at %, 25.1 at %, 25.2 at %, 25.3 at %, 25.4 at %, 25.5 at %, 25.6 at %, 25.7 at %, 25.8 at %, 25.9 at %, 26.0 at %, 26.1 at %, 26.2 at %, 26.3 at %, 26.4 at %, 26.5 at %, 26.6 at %, 26.7 at %, 26.8 at %, 26.9 at %, 27.0 at %, 27.1 at %, 27.2 at %, 27.3 at %, 27.4 at %, 27.5 at %, 27.6 at %, 27.7 at %, 27.8 at %, 27.9 at %, 28.0 at %, 28.1 at %, 28.2 at %, 28.3 at %, 28.4 at %, 28.5 at %, 28.6 at %, 28.7 at %, 28.8 at %, 28.9 at %, 29.0 at %, 29.1 at %, 29.2 at %, 29.3 at %, 29.4 at %, 29.5 at %, 29.6 at %, 29.7 at %, 29.8 at %, 29.9 at %, 30.0 at %, 30.1 at %, 30.2 at %, 30.3 at %, 30.4 at %, 30.5 at % or other incremental at % between.
The Mn can be about 25.4 at %, 25.5 at %, 25.6 at %, 25.7 at %, 25.8 at %, 25.9 at %, 26.0 at %, 26.1 at %, 26.2 at %, 26.3 at %, 26.4 at %, 26.5 at %, 26.6 at %, 26.7 at %, 26.8 at %, 26.9 at %, 27.0 at %, 27.1 at %, 27.2 at %, 27.3 at %, 27.4 at %, 27.5 at %, 27.6 at %, 27.7 at %, 27.8 at %, 27.9 at %, 28.0 at %, 28.1 at %, 28.2 at %, 28.3 at %, 28.4 at %, 28.5 at %, 28.6 at %, 28.7 at %, 28.8 at %, 28.9 at %, 29.0 at %, 29.1 at %, 29.2 at %, 29.3 at %, 29.4 at %, 29.5 at %, 29.6 at %, 29.7 at %, 29.8 at %, 29.9 at %, 30.0 at %, 30.1 at %, 30.2 at %, 30.3 at %, 30.4 at %, 30.5 at %, 30.6 at %, 30.7 at %, 30.8 at %, 30.9 at %, 31.0 at %, 31.1 at %, 31.2 at %, 31.3 at %, 31.4 at %, 31.5 at %, 31.6 at %, 31.7 at %, 31.8 at %, 31.9 at %, 32.0 at %, 32.1 at %, 32.2 at %, 32.3 at %, 32.4 at %, 32.5 at %, 32.6 at %, 32.7 at %, 32.8 at %, 32.9 at %, 33.0 at % or other incremental at % between.
The Fe can be about 1.0 at %, 1.1 at %, 1.2 at %, 1.3 at %, 1.4 at %, 1.5 at %, 1.6 at %, 1.7 at %, 1.8 at %, 1.9 at %, 2.0 at %, 2.1 at %, 2.2 at %, 2.3 at %, 2.4 at %, 2.5 at %, 2.6 at %, 2.7 at %, 2.8 at %, 2.9 at %, 3.0 at %, 3.1 at %, 3.2 at %, 3.3 at %, 3.4 at %, 3.5 at %, 3.6 at %, 3.7 at %, 3.8 at %, 3.9 at %, 4.0 at %, 4.1 at %, 4.2 at %, 4.3 at %, 4.4 at %, 4.5 at %, 4.6 at %, 4.7 at %, 4.8 at %, 4.9 at %, 5.0 at %, 5.1 at %, 5.2 at %, 5.3 at %, 5.4 at %, 5.5 at %, 5.6 at %, 5.7 at %, 5.8 at %, 5.9 at % or other incremental at % between.
The Al can be about 0.1 at %, 0.2 at %, 0.3 at %, 0.4 at % or other incremental percentage between.
The Ni can be about 0.0 at %, 0.1 at %, 0.2 at %, 0.3 at %, 0.4 at %, 0.5 at %, 0.6 at %, 0.7 at %, 0.8 at %, 0.9 at %, 1.0 at %, 1.1 at %, 1.2 at %, 1.3 at %, 1.4 at %, 1.5 at %, 1.6 at %, 1.7 at %, 1.8 at %, 1.9 at %, 2.0 at %, 2.1 at %, 2.2 at %, 2.3 at %, 2.4 at %, 2.5 at %, 2.6 at %, 2.7 at %, 2.8 at %, 2.9 at %, 3.0 at %, 3.1 at %, 3.2 at %, 3.3 at %, 3.4 at %, 3.5 at %, 3.6 at %, 3.7 at %, 3.8 at %, 3.9 at %, 4.0 at % or other incremental at % between.
The Ba, Co, Cu, Cs, K, Li, Mm, Mo, Na, Nb, Ni, Rb, Ta, Tl, and W (where Mm is mischmetal) can be about 1.0 at %, 1.1 at %, 1.2 at %, 1.3 at %, 1.4 at %, 1.5 at %, 1.6 at %, 1.7 at %, 1.8 at %, 1.9 at %, 2.0 at %, 2.1 at %, 2.2 at %, 2.3 at %, 2.4 at %, 2.5 at %, 2.6 at %, 2.7 at %, 2.8 at %, 2.9 at %, 3.0 at %, 3.1 at %, 3.2 at %, 3.3 at %, 3.4 at %, 3.5 at %, 3.6 at %, 3.7 at %, 3.8 at %, 3.9 at %, 4.0 at %, 4.1 at %, 4.2 at %, 4.3 at %, 4.4 at %, 4.5 at %, 4.6 at %, 4.7 at %, 4.8 at %, 4.9 at %, 5.0 at %, 5.1 at %, 5.2 at %, 5.3 at %, 5.4 at %, 5.5 at %, 5.6 at %, 5.7 at %, 5.8 at %, 5.9 at %, 6.0 at %, 6.1 at %, 6.2 at %, 6.3 at %, 6.4 at %, 6.5 at %, 6.6 at %, 6.7 at %, 6.8 at %, 6.9 at %, 7.0 at %, 7.1 at %, 7.2 at %, 7.3 at %, 7.4 at %, 7.5 at %, 7.6 at %, 7.7 at %, 7.8 at %, 7.9 at %, 8.0 at %, 8.1 at %, 8.2 at %, 8.3 at %, 8.4 at %, 8.5 at %, 8.6 at %, 8.7 at %, 8.8 at %, 8.9 at %, 9.0 at %, 9.1 at %, 9.2 at %, 9.3 at %, 9.4 at %, 9.5 at %, 9.6 at %, 9.7 at %, 9.8 at %, 9.9 at %, 10.0 at % or other incremental at % between.
The alloy can have a trapped hydrogen capacity (at about 14.5 psi and about 20° C.) of no more than about 0.08 wt %, 0.09 wt %, 0.10 wt %, 0.11 wt %, 0.12 wt %, 0.13 wt %, 0.14 wt %, 0.15 wt %, 0.16 wt %, 0.17 wt %, 0.18 wt %, 0.19 wt %, 0.20 wt %, 0.21 wt %, 0.22 wt %, 0.23 wt %, 0.24 wt %, 0.25 wt % other incremental wt % between. The alloy can have a trapped hydrogen capacity (at about 14.5 psi and about 20° C.) of less than 0.08 wt %.
The alloy can have a PCT isotherm slope of no more than about 0.50, 0.51, 0.52, 0.53, 0.54, 0.55, 0.56, 0.57, 0.58, 0.59, 0.60, 0.61, 0.62, 0.63, 0.64, 0.65, 0.66, 0.67, 0.68, 0.69, 0.70, 0.71, 0.72, 0.73, 0.74, 0.75, 0.76, 0.77, 0.78, 0.79, 0.80 or other incremental value between. The alloy can have a PCT isotherm slope of less than 0.50.
The alloy can have a hysteresis of not more than about 0.04, 0.05, 0.06, 0.07, 0.08, 0.09, 0.10, 0.11, 0.12, 0.13, 0.14, 0.15, 0.16, 0.17, 0.18, 0.19, 0.20, 0.21, 0.22, 0.23, 0.24, 0.25, 0.26, 0.27, 0.28, 0.29, 0.30, 0.31, 0.32, 0.33, 0.34, 0.35, 0.36, 0.37, 0.38, 0.39, 0.40, 0.41, 0.42, 0.43, 0.44, 0.45, 0.46, 0.47, 0.48, 0.49, 0.50 or other incremental value between.
The alloy can have a total hydrogen storage capacity (at about 500 psi and about 20° C.) of at least about 1.70 wt %, 1.71 wt %, 1.72 wt %, 1.73 wt %, 1.74 wt %, 1.75 wt %, 1.76 wt %, 1.77 wt %, 1.78 wt %, 1.79 wt %, 1.80 wt % other incremental wt % between. The alloy can have a total hydrogen storage capacity (at about 500 psi and about 20° C.) of greater than 1.80 wt %.
The hydrogen storage system 1 of the present invention can be seen in
It is preferable that at least the thermally conductive compartmentalization network 3 is produced by a 3D printing process. Alternatively, both the thermally conductive compartmentalization network 3 and the external pressure containment vessel 2 are produced simultaneously by a 3D printing process.
The elongate tubes 2 are packed firmly into a bundle within the external pressure containment vessel 2 so that each elongate tube 5 in the bundle is in firm contact along its longitudinal surface with the longitudinal surfaces of other elongate tubes 5. In addition, the outer elongate tubes 5 in the bundle make firm contact along their longitudinal surfaces with the longitudinal inside surface of the external pressure containment vessel 2.
The hydrogen storage system can include non-storage components 4 within the system. These non-storage components 4 may include heat transport and/or generation means, as well as gaseous transport means. Further, the non-storage components 4 may be sensors, such as, for instance thermal probes to monitor internal temperature. The non-storage components 4 may be inserted within the hydrogen storage alloy 7 as desired (see
As depicted in
Another technique for forming the hydrogen storage system 1 of the present invention is to insert an externally created thermally conductive compartmentalization network 3 into a proto-pressure vessel. Once the thermally conductive compartmentalization network 3 is inserted, the proto-pressure vessel is mechanically worked to form the final external pressure containment vessel 2, which encases the thermally conductive compartmentalization network 3.
Alternatively, the entire hydrogen storage system 1, including the external pressure containment vessel 2 and the thermally conductive compartmentalization network 3, can be formed simultaneously via 3D printing technology. This usually includes methods of 3D printing of metal.
Metal 3D printing is a catchall term for several technology families. Simply put, metal 3D printing refers to any technology that creates metal objects layer by layer through sintering, melting, and welding with metal.
Metal 3D printing is one of the most heavily invested in and fastest-growing manufacturing technologies. It can be used in conjunction with other manufacturing technologies, but it is also capable of producing prototypes and finished products on its own. In some cases, 3D-printed metal objects perform just as well as machined parts. It can be in prototyping, aerospace, mechanical engineering, specific tools, and other applications.
Aluminum is a lightweight alloy with high flexibility, good strength, and superior thermal properties and it has become the primary metal used in 3D printing. Aluminum 3D printers have been used in biomedical, automotive, and aerospace applications. Aluminum's core strength is its ability to be molded and used for functional objects as well as prototypes. The material is suitable for both prototyping and manufacturing. The quality of 3D-printed aluminum parts is comparable to that of synthetic parts. Aluminum's material properties make it an excellent choice for high-performance functional parts that are subjected to high loads.
Available 3D printing technologies include, but are not limited to:
Of these, DMSL/SLM can be considered a useful technique for forming the entire hydrogen storage system 1.
Selective Laser Melting (SLM) and Direct Metal Laser Sintering (DMLS) are two metal additive manufacturing processes that use metal powder bed fusion, the process where a heat source is utilized to fuse metal particles one layer at a time. Both make objects in a way similar to SLS, the main difference being these technologies are used in the production of metal parts instead of plastic. Typical materials used are metal powder, aluminum, stainless steel, and titanium.
DMLS is used for producing parts from metal alloys. Instead of melting it, DMLS heats the metal powder with a laser to the point where it fuses together on a molecular level. SLM uses the laser to fully melt the metal powder to form a homogeneous part, in other words, it makes parts from single element materials, such as titanium.
DMLS and SLM processes do need structural support in order to limit the possibility of distortion, which can result from the high temperatures used during printing. The two technologies have a lot of similarities: both use a laser to scan and selectively fuse (or melt) metal powder particles, bonding them together and building a part layer-by-layer. Also, the materials used in both processes are metals that come in a granular/powder form.
The differences between SLM and DMLS come down to the fundamentals of the particle bonding process. SLM uses metal powders with a single melting temperature and fully melts the particles, while in DMLS the powder is composed of materials with variable melting points that fuse on a molecular level at elevated temperatures. Essentially, SLM produces parts from a single metal, while DMLS produces parts from metal alloys.
Both SLM and DMLS are used in industrial applications to create end-use engineering products. Using such technologies, the entire hydrogen storage system 1, including the external pressure containment vessel 2 and the thermally conductive compartmentalization network 3 can be formed simultaneously.
Using SLM and/or DMLS, the hydrogen storage system 1 of the present invention can be formed layer by layer such that both the external pressure containment vessel 2 and the thermally conductive compartmentalization network 3 are simultaneously formed bit by bit. This can involve use of a single material for the entire hydrogen storage system 1. However, the external pressure containment vessel 2 and the thermally conductive compartmentalization network 3 may also be formed of different materials using the same techniques. Metal alloys that are useful for the thermally conductive compartmentalization network 3 are highly thermally conductive alloys. These include metals such as: aluminum and aluminum alloys; copper and copper alloys; magnesium and magnesium alloys. The external pressure containment vessel 2 may be formed of those materials from which conventional pressure containers are made. These include aluminum, aluminum alloys, and steels (i.e. carbon and stainless).
In addition, the present invention comprises a method of fabricating the hydrogen storage system by fabricating the thermally conductive compartmentalization network disposed within said external pressure containment vessel via a 3D printing process, and depositing the hydrogen storage alloy within said hydrogen storage alloy containment vessel.
Both the external pressure containment vessel and the thermally conductive compartmentalization network may be fabricated by the 3D printing process. Both the external pressure containment vessel and the thermally conductive compartmentalization network may be fabricated simultaneously as a single unit by the 3D printing process. The 3D printing process may comprise deposition by Selective Laser Melting (SLM) and/or Direct Metal Laser Sintering (DMLS).
The thermally conductive compartmentalization network may be fabricated by the 3D printing process, in which a highly thermally conductive printed metal is selected from the group consisting of: aluminum, aluminum alloys, copper, copper alloys, magnesium and magnesium alloys. The 3D printing process may comprise deposition by Selective Laser Melting (SLM) and/or Direct Metal Laser Sintering (DMLS).
It will be understood that particular embodiments described herein are shown by way of illustration and not as limitations of the invention. The principal features of this invention can be employed in various embodiments without departing from the scope of the invention. Those skilled in the art will recognize, or be able to ascertain using no more than routine experimentation, numerous equivalents to the specific procedures described herein. Such equivalents are considered to be within the scope of this invention and are covered by the claims.
All publications, patent applications and patents mentioned in the specification are indicative of the level of skill of those skilled in the art to which this invention pertains. All publications and patent applications are herein incorporated by reference to the same extent as if each individual publication or patent application was specifically and individually indicated to be incorporated by reference.
The use of the word “a” or “an” when used in conjunction with the term “comprising” in the claims and/or the specification may mean “one,” but it is also consistent with the meaning of “one or more,” “at least one,” and “one or more than one.” The use of the term “or” in the claims is used to mean “and/or” unless explicitly indicated to refer to alternatives only or the alternatives are mutually exclusive, although the disclosure supports a definition that refers to only alternatives and “and/or.” Throughout this application, the term “about” is used to indicate that a value includes the inherent variation of error for the device, the method being employed to determine the value, or the variation that exists among the study subjects.
As used in this specification and claim(s), the words “comprising” (and any form of comprising, such as “comprise” and “comprises”), “having” (and any form of having, such as “have” and “has”), “including” (and any form of including, such as “includes” and “include”) or “containing” (and any form of containing, such as “contains” and “contain”) are inclusive or open-ended and do not exclude additional, unrecited elements or method steps. In embodiments of any of the compositions and methods provided herein, “comprising” may be replaced with “consisting essentially of” or “consisting of”. As used herein, the phrase “consisting essentially of” requires the specified integer(s) or steps as well as those that do not materially affect the character or function of the claimed invention. As used herein, the term “consisting” is used to indicate the presence of the recited integer (e.g., a feature, an element, a characteristic, a property, a method/process step or a limitation) or group of integers (e.g., feature(s), element(s), characteristic(s), propertic(s), method/process steps or limitation(s)) only.
The term “or combinations thereof” as used herein refers to all permutations and combinations of the listed items preceding the term. For example, “A, B, C, or combinations thereof” is intended to include at least one of: A, B, C, AB, AC, BC, or ABC, and if order is important in a particular context, also BA, CA, CB, CBA, BCA, ACB, BAC, or CAB. Continuing with this example, expressly included are combinations that contain repeats of one or more item or term, such as BB, AAA, AB, BBC, AAABCCCC, CBBAAA, CABABB, and so forth. The skilled artisan will understand that typically there is no limit on the number of items or terms in any combination, unless otherwise apparent from the context.
As used herein, words of approximation such as, without limitation, “about”, “substantial” or “substantially” refers to a condition that when so modified is understood to not necessarily be absolute or perfect but would be considered close enough to those of ordinary skill in the art to warrant designating the condition as being present. The extent to which the description may vary will depend on how great a change can be instituted and still have one of ordinary skilled in the art recognize the modified feature as still having the required characteristics and capabilities of the unmodified feature. In general, but subject to the preceding discussion, a numerical value herein that is modified by a word of approximation such as “about” may vary from the stated value by at least ±1, 2, 3, 4, 5, 6, 7, 10, 12 or 15%.
All of the devices and/or methods disclosed and claimed herein can be made and executed without undue experimentation in light of the present disclosure. While the devices and/or methods of this invention have been described in terms of preferred embodiments, it will be apparent to those of skill in the art that variations may be applied to the compositions and/or methods and in the steps or in the sequence of steps of the method described herein without departing from the concept, spirit and scope of the invention. All such similar substitutes and modifications apparent to those skilled in the art are deemed to be within the spirit, scope and concept of the invention as defined by the appended claims.
Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. It is therefore evident that the particular embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit of the disclosure. Accordingly, the protection sought herein is as set forth in the claims below.
To aid the Patent Office, and any readers of any patent issued on this application in interpreting the claims appended hereto, applicants wish to note that they do not intend any of the appended claims to invoke paragraph 6 of 35 U.S.C. § 112 as it exists on the date of filing hereof unless the words “means for” or “step for” are explicitly used in the particular claim.
This application is a continuation of U.S. application Ser. No. 17/870,124 filed Jul. 21, 2022, which claims priority to: U.S. Provisional Application Ser. No. 63/225,366 filed Jul. 23, 2021 entitled “Non-Pyrophoric Hydrogen Storage Alloys and Hydrogen Storage Systems Using the Alloys”; U.S. Provisional Application Ser. No. 63/225,389 filed Jul. 23, 2021 entitled “Hydrogen Storage Systems Using Non-Pyrophoric Hydrogen Storage Alloys”; and U.S. Provisional Application Ser. No. 63/225,399 filed Jul. 23, 2021 entitled “3D Printed Hydrogen Storage Systems Using Non-Pyrophoric Hydrogen Storage Alloys”. The entire contents of the foregoing applications are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 63225366 | Jul 2021 | US | |
| 63225389 | Jul 2021 | US | |
| 63225399 | Jul 2021 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 17870124 | Jul 2022 | US |
| Child | 18654838 | US |