Patent Application
20160222136
The present invention discloses a method for fractionating dextrin, relating to the application of the technology of stepwise precipitation with polyethylene glycol in fractionating dextrin, belonging to the technical field of food processing.
At present, as a method for fractionating dextrin, there are mainly a fractionating method by exclusion chromatography and a fractionating method by precipitation with alcohol. The former is costly due to expensive fillers and expensive chromatographic power systems (i.e., pumps). Additionally, by the fractionating method by exclusion chromatography, it is difficult to realize industrial production due to small capacity. The fractionating method by precipitation with alcohol has the following disadvantages: it is likely to have local co-precipitation during the addition of alcohol thus to cause poor fractionation effect; the decrease in concentration of the dextrin due to the increase in total volume of the dextrin solution during the addition of alcohol results in low yield of dextrin; and the fractionating process highly depends upon the ambient temperature and the repeatability is thus low.
In view of this, the present invention is to provide a novel method for fractionating dextrin and thus to provide a novel method for preparing low-dispersity dextrin. It has been found in the present invention that dextrin is incompatible with polyethylene glycol in aqueous solution and a larger molecular weight of the dextrin results in more significant incompatibility with polyethylene glycol. Accordingly, the stepwise precipitation of dextrin components having a molecular weight from large to small may be realized by gradually increasing the concentration of polyethylene glycol by gradually adding polyethylene glycol to dextrin in aqueous solution. On this basis, the present invention establishes a novel method for fractionating dextrin, which is named “stepwise precipitation method for fractionating dextrin by polyethylene glycol”.
An objective of the present invention is to provide a method for fractionating dextrin.
The present invention employs the following technical solution: a method for fractionating dextrin is provided, for the purpose of fractionating dextrin by the stepwise precipitation technology by polyethylene glycol, specifically:
1. preparation of dextrin solution: dispersing 15-25 g of tapioca starch in 100 mL of n-butyl alcohol, adding 1 mL of concentrated hydrochloric acid, hydrolyzing for 3 days at 40° C., adding 14 mL of 1M NaHCO3 to terminate the reaction, centrifuging for 15 min at 4000 g, precipitating, washing with 50% ethanol solution for several times until there is no chloride ion, drying in an oven at 40° C., crushing, and sieving to obtain the dextrin; and the dextrin is dissolved in the distilled water to prepare a dextrin solution at a concentration of 0.9%-3.6%;
2. stepwise precipitation by polyethylene glycol for fractionating: adding 5 g of polyethylene glycol to 100 mL of dextrin solution at a mass concentration of 0.9%-3.6%, stirring while heating until the polyethylene glycol is dissolved, that is, the solution becomes clear, naturally cooling in air to 25° C., remaining at 25° C. in a water bath for 24 h, centrifuging for 15 min at 4000 g if any precipitation occurs, washing the obtained precipitate with trichloromethane to remove the residual polyethylene glycol, drying for 24 h at 40° C., crushing and sieving to obtain a dextrin component Fraction 1; continuously adding 5 of polyethylene glycol to the supernatant, and repeating the above processes to obtain a dextrin component Fraction 2; if no precipitation occurs, continuously adding 5 g of polyethylene glycol until the precipitation occurs; and repeating the above processes until the amount of polyethylene glycol added reaches 60 g, thus to obtain 9 to 12 graded dextrin components; and
3. Identification about dispersity of dextrin: the dextrin components are analyzed by high-efficiency exclusion chromatography by a multi-angle laser detector and a differential detector, to calculate the molecular weight and coefficient of dispersion of dextrin.
The polyethylene glycol is polyethylene glycol having a number-average molecular weight of 4000 Da, 6000 Da or 8000 Da.
The present invention has the beneficial effects of simple production process, low cost, high yield, large capacity and good grading effect compared with the prior art.
25 g of tapioca starch was dispersed in 100 mL of n-butyl alcohol (analytically pure), added with 1 mL of concentrated hydrochloric acid (analytically pure), hydrolyzed for 72 h at 40° C., added with 14 mL of 1M NaHCO3 to terminate the reaction, centrifuged for 15 min at 4000 g, precipitated, washed with 50% ethanol solution for several times until there was no chloride ion, and dried for 24 h in an oven at 40° C. to obtain the dextrin. The dextrin was dissolved in the distilled water to prepare a dextrin solution at a concentration of 3.6%. 5 g of polyethylene glycol (analytically pure) having a number-average molecular weight of 8000 Da was added to 100 mL of dextrin solution, stirred while heating until the polyethylene glycol was dissolved, that is, the solution became clear, naturally cooled in air to 25° C., remained at 25° C. in a water bath for 24 h, and centrifuged for 15 min at 4000 g; the resulting concentrated phase was washed with trichloromethane to remove the residual polyethylene glycol, dried for 24 h at 40° C., crushed and sieved to obtain a dextrin component Grade 1; 5 g of polyethylene glycol was continuously added to the supernatant, and the above processes were repeated until the amount of polyethylene glycol added reached 60 g, thus to obtain 11 graded dextrin components. The dextrin products were analyzed by high-efficiency exclusion chromatography by a multi-angle laser detector and a differential detector. The respective molecular weight of the 11 dextrin components is shown as follows:
Dextrin 1 (when added with 5 g of polyethylene glycol): weight-average molecular weight: 2.380×104 Da; and coefficient of dispersion: 1.38;
Dextrin 2 (when added with 10 g of polyethylene glycol): weight-average molecular weight: 2.1660×104 Da; and coefficient of dispersion: 1.13;
dextrin 3 (when added with 15 g of polyethylene glycol): weight-average molecular weight: 2.011×104 Da; and coefficient of dispersion: 1.16;
dextrin 4 (when added with 20 g of polyethylene glycol): weight-average molecular weight: 1.879×104 Da; and coefficient of dispersion: 1.21;
dextrin 5 (when added with 25 g of polyethylene glycol): weight-average molecular weight: 1.329×104 Da; and coefficient of dispersion: 1.13;
dextrin 6 (when added with 30 g of polyethylene glycol): weight-average molecular weight: 1.281×104 Da; and coefficient of dispersion: 1.18;
dextrin 7 (when added with 35 g of polyethylene glycol): weight-average molecular weight: 8.029×103 Da; and coefficient of dispersion: 1.19;
dextrin 8 (when added with 40 g of polyethylene glycol): weight-average molecular weight: 6.081×103 Da; and coefficient of dispersion: 1.17;
dextrin 9 (when added with 45 g of polyethylene glycol): weight-average molecular weight: 5.584×103 Da; and coefficient of dispersion: 1.17;
dextrin 10 (when added with 50 g of polyethylene glycol): weight-average molecular weight: 5.561×103 Da; and coefficient of dispersion: 1.21; and
dextrin 11 (when added with 60 g of polyethylene glycol): weight-average molecular weight: 5.443×103 Da; and coefficient of dispersion: 1.38.
15 g of tapioca starch was dispersed in 100 mL of n-butyl alcohol (analytically pure), added with 1 mL of concentrated hydrochloric acid (analytically pure), hydrolyzed for 72 h at 40° C., added with 14 mL of 1M NaHCO3 to terminate the reaction, centrifuged for 15 min at 4000 g, precipitated, washed with 50% ethanol solution for several times until there was no chloride ion, and dried for 24 h in an oven at 40° C. to obtain the dextrin. The dextrin was heated and dissolved in the distilled water to prepare a dextrin solution at a concentration of 0.9%. 5 g of polyethylene glycol (analytically pure) having a number-average molecular weight of 4000 Da was added to 100 mL of dextrin solution, stirred while heating until the polyethylene glycol was dissolved, that is, the solution became clear, naturally cooled in air to 25° C., remained at 25° C. in a water bath for 24 h, and centrifuged for 15 min at 4000 g; the obtained precipitate was washed with trichloromethane to remove the residual polyethylene glycol, dried for 24 h at 40° C., crushed and sieved to obtain a dextrin component Grade 1; 5 g of polyethylene glycol was continuously added to the supernatant, and the above processes were repeated until the amount of polyethylene glycol added reached 60 g, thus to obtain 9 graded dextrin components. The dextrin products were analyzed by high-efficiency exclusion chromatography by a multi-angle laser detector and a differential detector. The respective molecular weight of the 9 dextrin components is shown as follows:
Dextrin 1 (when added with 15 g of polyethylene glycol): weight-average molecular weight: 3.297×104 Da; and coefficient of dispersion: 1.34;
Dextrin 2 (when added with 20 g of polyethylene glycol): weight-average molecular weight: 1.141×104 Da; and coefficient of dispersion:
1.17;
Dextrin 3 (when added with 25 g of polyethylene glycol): weight-average molecular weight: 9.235×103 Da; and coefficient of dispersion: 1.24;
Dextrin 4 (when added with 30 g of polyethylene glycol): weight-average molecular weight: 1.066×104 Da; and coefficient of dispersion: 1.09;
dextrin 5 (when added with 40 g of polyethylene glycol): weight-average molecular weight: 9.386×103 Da; and coefficient of dispersion: 1.17;
Dextrin 6 (when added with 45 g of polyethylene glycol): weight-average molecular weight: 8.992×103 Da; and coefficient of dispersion: 1.18;
weight-average molecular weight: 7.987×10×3 Da; and coefficient of dispersion: 1.28;
Dextrin 8 (when added with 55 g of polyethylene glycol): weight-average molecular weight: 7.786×103 Da; and coefficient of dispersion: 1.15;
Dextrin 9 (when added with 60 g of polyethylene glycol): weight-average molecular weight: 6.381×103 Da; and coefficient of dispersion: 1.47.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201410473784.X | Sep 2014 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2014/087501 | 9/26/2014 | WO | 00 |