The present invention relates to a method of producing a frame member for a window or a door, the method comprising the steps of:
providing a sheet of metal, rollforming the sheet of metal into a frame shell having a predetermined profile, and introducing a foaming material into the frame shell.
The invention further relates to a frame member and use of a frame member.
The frame member may furthermore be used to create a frame structure for at window or a door, such as a sash or a frame.
Traditional wooden frame or sash structures are considered aesthetically pleasing but are not very robust, particularly not when exposed to moisture, and they lack the insulating properties desired in modern buildings.
The robustness issues have previously been solved with window frames made from polyvinylchloride (PVC), which is very widely used, while other window makers, including the applicant, have chosen to make the frames from profiles with a wooden core, typically of ply-wood, and a polyurethane (PUR) shell. Other plastic materials have also been used for the shell, but PUR is by far the most widely used, since it has suitable properties with regard to weather resistance, insulation, mouldability etc.
These frames, however, still lack sufficient insulating properties to live up to the still stricter building regulations, which are being adopted in many countries, and it has therefore been attempted to include insulating materials in the frame member.
In U.S. Pat. No. 6,047,514, a process is described in which a window frame is produced by rolforming metal into a structural shape, extruding thermoplastic to both inside and outside. A urethane composition is then injected into the shape. This results in a complex production with much material and thus high costs.
It is the object of the invention to provide a method to manufacture a frame member having good thermal insulating properties, which are cheaper to produce and also provides an environmentally friendly alternative due to the less amount of material, having suitable rigidity and strength properties. It is also an object of the invention to provide a frame member that has a core made from a process that provides less internal tensions, and subsequently maintains its given shape.
This is achieved by the further steps of providing a sheet metal having a thickness of 0.25 mm or less and arranging the frame shell in a calibration tube until the foam material has set.
By using a method like this, a core of a foam material may be provided. The core may assume the shape of the profile, and therefore any additional machining of the core may be avoided. By allowing the foam to expand and fully set within the profile, internal tensions may be prevented within the core. The calibration tube may have an internal shape that corresponds to the desired shape of the frame shell. The injected foam material may therefore be allowed to expand within the profile and within the calibration tube, thereby maintaining the desired shape. the calibration tube helps to maintain the desired shape, which would not be reach if a calibration tube were not used, due to the small thickness of the metal. Hence, the foam material expands to assume the shape of the frame shell. This provides a frame member with sufficient structural strength and insulation properties approximately 4-5 times better than the insulation properties of wood. The strength imparting layer is preferably mostly made from a low thermal conductive metal, having a low thermal transfer value. The metal may be provided in a coil or roll of sheet metal, which is rollformed into a frame shell having a profile. The frame shell has an opening into which the foam material is injected. Once the foam material expands, the frame shell is held in a calibration tube or a similar device that helps to maintain the shape the metal has been roll formed into, in order to control the expansion. By allowing the foam to expand within the frame shell, under the influence of the calibration tube, internal tensions may be prevented within the core.
The foaming material may be provided by a composition that foams up to a rigid material, preferably having good insulation properties. The composition may comprise isocyanate and polyol, which upon reaction with each other creates a foam which expands within the profile. This is an advantage since the components are fluid until they react with each other. Once the components mix, they react with each other and with the humidity in the air to create a foam, which subsequently expand. The polyol may contain catalysts, surfactants, blowing agents etc. the isocyanate may contain additives such as chain extenders, cross linkers, surfactants, flame retardants, blowing agents, pigments, and fillers. A non-isocyanate may be used as well for creating the urethane foam.
In one embodiment, the method may comprise adding a reactant to the composition, wherein the reactant is CO2 or pentane gas. The reactant may allow the foaming reaction to increase.
In one embodiment, the setting of the foam may be accelerated by the addition of one or more accelerating agents to the composition. Accelerating agent(s) may be added to the composition as well, which will reduce the setting time and thereby the production costs.
In one embodiment, the method further comprises the step of pulling the frame shell through a calibration tube continuously during the setting time during which the foam material sets. By pulling the frame shell through the calibration tube, the frame shell may at the same time be conveyed to a subsequent production station. This will allow the core to assume the shape of the profile, and there is no risk that the expanding foam deforms the shape of the frame shell into which it has been rollformed. If the foaming has not concluded, the expansion may continue, and the frame shell may be deformed. The calibration tube may be an extrusion matrix or the like. The extrusion matrix may have a length of 1-40 meters, or even longer. The extrusion matrix/calibration tube may be a device which controls the shape of the profile during setting. The metal profile itself is made from thin metal foil, and may be easily deformable. Without the calibration tube/extrusion matrix the frame shell itself may not be able to withstand the pressure resulting from the foaming.
In one embodiment, the setting time may be less than 2 minutes, preferably less than 60 seconds, more preferably less than 30 seconds, even more preferably less than 20 seconds.
In one embodiment, the method steps are performed inline. The production rate may be 40 m/minute or faster, between 40 m/minute to 20 meter/minute or slower than 20 m/minute The production may occur in one continuous line, having successive stations. That may allow a continuous profile with a core to be produced. The individual frame members may subsequently be cut into suitable lengths.
In one embodiment, the method may further comprise the step of wrapping the profile with a second strength imparting layer. The second strength imparting layer may be a decorative layer. The second strength imparting layer may also be a layer contributing to the strength of the frame member.
In one embodiment, the foam material may be introduced through an opening extending along the length of the profile. The opening may be a pre bend fold included in the frame shell produced when the forming is performed. The opening may therefore extend along the entire length of the frame shell.
After introducing the foam material, the opening may be closed. It may be closed either by overlapping the metal ends, by adding a second material to close the opening, or by providing locking function. There may be other ways to close the opening, and it may be possible that the closure is temporary while the foam sets.
In one embodiment, the frame shell is composed of two or more frame shell parts. The frame parts may be jointed together before injection of the foam. The joining may be performed by welding or use of adhesives.
In another aspect the invention relates to a frame member such as a side, a top or a bottom piece for a sash or frame structure for a window or door, said frame member comprising a core substantially made from a foamed material having a thermal conductivity below 0.037 W/m K and at least one strength imparting layer, covering at least a part of the core. The strength imparting layer comprises a rollformed sheet of metal formed into a frame shell having a predetermined profile. The foamed material is adapted to be injected into the metal profile and the at least one strength imparting layer has a thickness of 0.25 mm or less, preferably 0.15 mm or less, more preferably between 0.04-0.15 mm.
This provides a frame member formed from a metal sheet and pre formed to its profile shape. The injected foam material may therefore be allowed to expand within the profile. Hence, the foam material expands to assume the shape of the metal profile. This provides a frame member with sufficient structural strength and insulation properties approximately 4-5 times better than the insulation properties of wood. Further, since the core is allowed to expand and cool within the profile, the core maintains its given shape and internal tensions may be prevented. The strength imparting layer is preferably mostly made from a low thermal conductive metal, having a low thermal transfer value. The metal may be provided in a roll or coil of sheet metal, which is rollformed into frame shell having a profile. The frame shell may have an opening into which the foam material may be injected. Once the foam material expands, the frame shell may be held in a calibration tube in order to control the expansion. When the expansion is completed, the core may have assumed the same shape as the frame shell. By allowing the foam to expand within the frame shell, under the influence of the calibration tube, there is no risk that the finished frame member will be deformed during the influence of the expanding foam.
The core may have a density above 80 kg/m3 and/or between 80-200 kg/m3.
In one embodiment, the core may be made of polyurethane. Polyurethane has many desired properties such as good insulating properties and a suitable rigidity. Alternatively, some other materials with good insulting properties may be used, such as EPS. The polyurethane may be a non-isocyanate based polyurethane or isocyanate based polyurethane. A stiffening element may be incorporated into the core before or after setting of the foam.
In one embodiment, the foamed material is provided by a composition comprising materials setting quickly such as isocyanate and polyol. This is an advantage since the components are fluid until they react with each other. Once the materials are mixed, they may react with each other and with the humidity in the air to create a foam, and subsequently expand. The frame shell may comprise an opening. An injection nozzle may be inserted through the opening. The composition of Isocyanate and polyol may be poured or injected into the frame shell inline through the opening or through an injection nozzle. When isocyanate and polyol reacts with each other and the humidity in the air it may foam. The foaming procedure may be accelerated by applying CO2 or pentane gases into the frame shell. Generally, the normal setting time will be around 60 sec. However, the setting time until the foam has expanded in full may vary between around 20 seconds to 180 seconds. The setting time may also be accelerated by adding accelerators to the composition. Preferably the ingredients for the foam is injected while the frame shell is moved along a production line.
After the injection of the foam material, the frame shell may be closed, and the foam may expand therein. The closing may be any suitable closing arrangement, such as a snap lock or the like. The closing arrangement may also be a pre bend fold which is folded into its position after the injection nozzle has been removed. Preferably all the operations are done inline at successive stations. closing of the frame shell may also be performed while the frame shell is moving down the production line.
Without wishing to be bound by theory, the invention is based on the recognition that the contribution of strength of the individual components of the frame member renders it possible to provide a frame member with properties corresponding to the local load and hence demand for bending, compressive and torsional strength.
The cross-sectional configuration of the frame member is bound by certain requirements. In the top section of the frame member, adapted to face the exterior, the local load will primarily be compressive stress, whereas at the bottom section, adapted to face the interior of the building, the tensile stress is predominant. The further into the core element towards the center, the tensile and the compressive stress equalizes and consequently the stress diminishes. According to the laws of statics, the moment of inertia and hence the bending stiffness increases by the power of three of the height of the element in question. Therefore, by strengthening a frame member at its periphery, by partly or completely providing a frame member with a strength imparting layer, a proportionally greater contribution of the strengthening material is provided to the member, than if the same material were provided in the center of the frame member.
The strength imparting layer may be formed by two or more parts, for instance a top part and a bottom part, or a first side part and a second side part. Preferably, the core is preferably eventually covered in full regardless of whether it has one or more parts in order to give the frame shell the desired strength capabilities and to protect the core from the surrounding environment.
In one embodiment, the strength imparting layer may be interrupted by at least one thermal bridge preventing gap. The gap may be positioned so that a thermal bridge is prevented. Since the frame shell is preferably made from a metal, the risk of cold/heat transfer from the outside to the inside of the window may be reduced if a gap is provided.
In one embodiment, the thermal bridge preventing gap is covered with a material different from the strength imparting layer. This material should preferably be a material with very low heat transfer value, such as a polymer tape, a vinyl foil or the like.
The frame member may have a maximum extension of 5 mm at a load of 300 Newton, preferably a maximum extension of 5 mm at a load of 800 Newton.
Preferably the strength imparting layer may be selected from a group consisting of aluminium, copper, stainless steel alloy, such as austenitic stainless steel, AISI Type 316 Stainless Steel and/or AISI Type 304 Stainless Steel. Aluminium is generally easy to work with and is available in a number of different thicknesses. Austenitic stainless steel and/or AISI Type 304 Stainless Steel has/have a considerable lower thermal conductivity than aluminium. Where the thermal conductivity for aluminium is approximately 240 W/m K it is only 16.2 W/m K for AISI Type 304 stainless steel and thereby considerably lower. This is particularly important when it is being used for window or door frame members, where hot and cold air meet at the frame, and thereby water vapour may accumulate on the warm side of the window or door frame, which is undesirable. In comparison, the thermal conductivity for wood is approximately 1.2 W/m K.
The strength imparting layer may constitute, one layer, more than one layer and/or the different strength imparting layers may be made of the same and/or different materials. The strength imparting layer is preferably a film or a foil with weatherproof qualities. The strength imparting layer may also be made of other types of steel or alloys.
The frame member may further comprise at least a second strength imparting cover layer. The second strength imparting layer may be in a different material than the strength imparting layer. The second strength imparting layer may be a decorative layer, provided by a foil or a veneer or the like. The second strength imparting layer may be adapted to contribute to the strength of the frame member.
The second strength imparting cover layer may be selected from a group consisting of: a biobased veneer, such as bamboo veneer, hemp veneer, basically any kind of wood veneer, or a plastic layer such as vinyl. Other materials such as fiberglass, polypropylene, polyvinylchloride or carbon fiber may also be used. The second strength imparting cover layer may both act as a strengthening layer and a decorative layer, as this will be the outer most layer of the window or door frame. The second strength imparting layer preferably has a thickness between 0.1 and 1 mm, more preferably between 0.4 and 0.7 mm.
The frame member may be provided with an additional receiving element, preferably embedded in the core. The receiving elements may be individual receiving elements for receiving attachment means in the form of screws or dovels placed directly where the attachment are meant to be positioned. Alternatively or additionally, a plate like element, for example a laminated plate, may be sandwiched post production of the core or embedded in the core during moulding thereof.
The strength imparting layer and the second strength imparting cover layer is preferably made of different materials.
The frame members may be wrapped in a wrapping device for wrapping profiles in laminates and foils, preferably provided with rolls for the different layers and divided into wrapping zones. Ideally the zones and/or rolls are easily exchangeable for an adaptable production line. This production process allows for a differentiated rollforming/wrapping, because the rollers with the different layers are easily exchangeable, for example if different kinds of rollforming materials or wrapping materials are required or if first a batch of small frame members requiring one strength imparting layer are run succeeded by larger frames requiring for example two strength imparting layers or a strength imparting layer of a different material or thickness.
It may also be possible to semi wrap the frame member. For example, a first layer may be provided on the side of the frame adapted to face the interior side of a building, while the side of the frame adapted to face the exterior side of the building may be provided with a different layer.
After the frame member has been wrapped, it is cut of in suitable lengths.
The frame members may be joined with a dove tail connection in the corners or glued together, to create a frame structure.
The foamed material may preferably be a rigid material in order to contribute to the rigidity and strength of the frame member.
The frame member may be a profiled and/or prism shaped frame member.
Substantially made from a foamed material, should be construed as meaning that separate elements of other materials may be incorporated into the core material, for receiving screws, dowels or other attachment means.
The frame member would as such replace the traditional wooden frame members and would thus constitute the supporting structure of the window or door. The frame member may thus be forming part of or constitute a frame or sash structure for a door or a window.
In yet another aspect the invention relates to use of a frame member according to the invention, for the production of a window or a door.
In the following, the invention will be described in further detail with reference to the drawings in which:
When the expansion is completed, the frame member 1 is constituted by a core 3 of polyurethane and an at least partly surrounding metal frame shell 2, as seen in
The frame member 1 may be provided with one or more receiving elements for receiving attachment means.
The same reference numbers apply to the same features throughout the application. The scope of the present invention is set out by the accompanying claim set. In the context of the claims, the terms “comprising” or “comprises” do not exclude other possible elements or steps. Also, the mentioning of references such as “a” or “an” etc. should not be construed as excluding a plurality. When referring to a frame member, it is to be construed as a sash member and/or a frame member. In general, the features of the embodiments shown and described may be combined freely and no feature should be seen as essential unless stated in the independent claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| PA 2017 70329 | May 2017 | DK | national |