The present invention relates to a method of producing high performance lithium titanate Li4Ti5O12 (LTO) anode for lithium ion battery applications, more especially a process of producing LTO using precursors of TiO2 and Li2CO3 along with carbon by making use of Horizontal attrition milling technique which produces highly crystalline LTO with smaller particle size. The particle morphology was found to be non-uniform, well resolved particles with an average particle size of 342 nm. The smaller particles produced from Horizontal attrition mill may help in improving the lithium ion diffusion kinetics by shortening the lithium ion diffusion length. Carbon precursor used avoids stacking during milling which acts on a dual role as Process control agent (PCA) and carbon precursor. Annealing of milled precursors under inert atmosphere with PCA creating oxygen vacancies for which the charge compensation was done by converting Ti4+ ions into Ti3+ ions. The presence of Ti3+ in addition to Ti4+ in LTO greatly improves the electronic and ionic conductivity of the anode developed. The outcome of electrochemical characterization in half-cell configuration was around 156 mA h g−1 at 1 C and 97 mA h g at 10 C and in full cell configuration the capacity was around 0.47 mAh at 1 C rate with 98.5% retention after 650 charge-discharge cycles which is very promising. Because of the promising electrochemical properties in terms of charge discharge capacity, and rate capability material developed using the invented technique may be suitable for high energy density lithium ion battery application. The method developed by us has the advantage of being cost effective, high kinetic energy system compared to other milling techniques and is less time consuming.
Electric vehicle industry expects high energy density lithium ion batteries and therefore researchers are in search of new anode and cathode materials. Present study focuses on development of anode material, which becomes a suitable candidate for high energy density lithium ion battery applications and to design a scalable synthesis technique. Graphite is commonly used commercially available anode (Johnson et al, J. Power Sources 70 (1998), 48-54, Yoshio et al J. Electrochem. Soc. 147 (2000) 1245) and has specific capacity of 372 mA hg−1 (Peled et al, J Electrochem. Soc. 143 (1996) L4). It has voltage plateau of around 0.02 V making it prone to SEI and therefore affecting the electrochemical performance. Many anode materials involved intercalation (Nitta et al Part. Part. Syst. Charact. 31, 2014, 317-336) alloying and conversion mechanism (Obrovac et al Chem. Rev. 144 (2014), 11444-11502) are studied in-depth. Silica becomes one of the most hunted anodes, which becomes the material with highest theoretical capacity around 4200 mA hg−1. Since it accommodates more number of lithium ions it undergoes huge volume expansion, which numbers to be 400% and therefore is difficult to master it. TiO2 in both rutile and anatase form also becomes a promising anode with a capacity of around 350 mA hg−1 but has poor cycle life and rate capability owing to its semiconducting nature. In the present invention, we have chosen LTO as anode material owing to its high specific capacity of 175 mA hg−1 and stable voltage plateau of 1.55V. Since the voltage range is higher than the electrolyte decomposition voltage, it is free from solid electrolyte interface (SEI) formation. It accommodates three lithium ions and hence becomes a zero strain anode. Being a strain free anode, recently LTO has gained attention of many portable and electric vehicle battery industries. Further, long cycle life, high thermal stability (up to 280° C.), abundant and cost-effective Ti source and high rate capability properties of LTO making it more attractive. However, drawbacks such as poor electronic and ionic conductivity limit its electro-chemical performance. Doping with cations, carbon coating and surface coatings have been reported so far to overcome the above said limitations. Wet chemical methods such as hydrothermal (Qiu et al Chinese J of Chemistry, 28 (2010) 911), sol-gel (Shen et al, Materials chemistry and physics, 78 (2003) 437), spray drying (Wu et al, Electrocheima acta 78 (2012) 331), combustion (Prakash et al, Chem. Mater, 22 (2010) 2857) as well as solid state techniques were carried out to synthesize LTO anode. Since lithium titanate is lithiated form of titanium dioxide, there are several reports on synthesis of LTO from TiO2. Prior art reported the synthesis of LTO from either anatase or rutile phases of TiO2. Further, coating of LTO with anatase or rutile TiO2 was also reported to improve the electronic conductivity through the formation of Ti3+ ions. But when TiO2 as such was used as anode material for lithium ion batteries it resulted in poor electrochemical performance due to agglomeration and low packing density of TiO2 nanoparticles. In contrast when TiO2 (mixed phase) was used for the synthesis of LTO, it resulted in excellent electrochemical performance. Though many methods have reported to synthesize LTO, the factors such as (a) cost, (b) scalability and simplicity of material technology determine its commercial viability. Considering the above, in the present invention, we have adopted a sustainable and scalable low cost, energy efficient solid state method for the synthesis of LTO that can be suitable for electric vehicle lithium ion batteries. Since it is a single step large scale process devoid of solvents and large number of precursors, it may be considered as potential process for real application.
Prior-art patents as well as non-patent literature related to the field of present invention available in public domains are discussed below.
Singhal et al. [U.S. Pat. No. 6,827,921 B1/2004] invented a method of synthesizing nano sized lithium titanate from titanium and lithium precursors by refluxing them with an organic solvent followed by heat treatment in inert gas atmosphere. Here anatase TiO2 was used and concluded that the presence of vacant interstitial sites allows diffusion of lithium into TiO2 resulting in the formation of lithium titanate. The wet chemical method involved the use of expensive organic solvents, tedious reflux process and intermediate heating step. Zaghib et al. (US patent No. 0243467 A1/2007) claimed a method of producing Li4Ti5O12 with metal ion dopants along with carbon coating. The process was found to be multi-step process involving carbon coating of TiO2 followed by milling with lithium precursor. Further, milling period was found to be long (24 h) and involved two step annealing process. Hence the process is tedious and less attractive for commercial applications. Fujimoto et al. (U.S. Pat. No. 6,372,384 B1/2002) reported a method of producing doped lithium titanate for improved load characteristics of lithium ion batteries. It disclosed that the possible phase formation temperature for lithium titanate was around 800-900° C. When the temperature is below 800° C., it resulted in failure of phase formation and when 900° C. exceeds then leads to the formation of impurities phases which degrade the electrochemical performance. Spliter et al. (U.S. Pat. No. 6,890,510 B2/2005) claimed a method of producing pure lithium titanate nano-powders. The technique reported here adapts a combination of wet chemical as well as solid-state technique. The method involved two step calcination and two-step synthesis process was found to be more tedious among the above-mentioned prior art patented works. Amatucci et al. (U.S. Pat. No. 7,211,350 B2/2007) claimed a milling method for producing lithium titanate nano-powders by shorter annealing time. The resulting nano sized lithium titanate anode produced a capacity of 100 mA hg−1 at 10 C rate and was found to be stable over 500 cycles. Though the synthesized material shows promising electrochemical performance, the scalability of the process is concern. Yu et al (US patent No. US 0244439 A1/2012) invented lithium titanate anode containing some of the dopants like potassium or phosphorous and reported to use the technique of ball milling with TiO2 and lithium carbonate as the precursors. The Chinese patent No. CN101587948 B) discloses the synthesis of carbon coated lithium titanate by a two step ball milling and two step annealing process. Initially various inorganic salts of titanium dioxide in single phase were milled followed by annealing at lower temperature. Further the annealed intermediate product was milled with carbon source and calcined under inert atmospheres to form the carbon coated lithium titanate powders.
According to CN102364729 A Lithium titanate was synthesized using a wet milling process followed by two step calcination for carbon coating on lithium titanate powders using activated carbon material. Various solvents for milling and various carbon precursors were used for optimization. The synthesis technique required two step annealing process under oxidizing atmosphere to form activated carbon coated lithium titanate material.
In another Patent application No. CN102664252 A, carbon coated lithium titanate was synthesized using a single step ball milling process. But a mixture of acetylene black and CNT was used as carbon precursor. It is seen that usage of CNT may improve the electrochemical performance, however the difference in the density between LTO and CNT as well as the tedious method and expensive process cost for synthesizing CNTs making the process inefficient.
A two step synthesis process was disclosed in CN103022462 A, where a combination of solid state reaction followed by spray drying was carried out for the synthesis of carbon coated lithium titanate. Multi-step process including slurry preparation, drying, spray drying and annealing seems to be time consuming making the method less attractive and less economical.
As per CN103730649 A, Carbon coated lithium titanate was prepared using ball milling process in which inorganic salts of titanium and lithium are milled together to form the mixture. Further carbon coating was carried out by polymerization process using polymer as carbon precursor under inert atmosphere. This was then followed by spray drying and two step annealing process to produce single phase crystalline, carbon coated lithium titanate anode, which is not attractive for commercial application.
Li et al [Li. et al Int. J. Electrochem. Sci., 6 (2011) 3210-3223] synthesized carbon coated LTO by ball milling technique using amorphous TiO2 nano-clusters as raw material. Unlike in the present invention, where commercial cost-effective TiO2 is used as precursor, here TiO2 synthesized by micro-emulsion process using CTAB as structure directing agent was used for milling. Since the milling technique followed was wet milling in this study, it requires additional heating step to remove the moisture. Further, carbon coating was carried out to improve the electronic conductivity, whereas in the present invention stearic acid used in the milling process plays a dual role, i.e. it acts as carbon source as well as process control agent to improve electronic conductivity and to avoid powder stacking respectively. Spinel Li4Ti5O12 performance highly depends on both the electronic and ionic conductivity, however, developing a low-cost strategy to improve its electronic and ionic conductivity still remains challenging. In study carried out by Yan et al [Yan et al. J. Mater. Chem. A, (2015), 3,11773], a facile cost-saving carbothermal reduction method was followed to synthesize micro scaled surface modified Ti(III) spinel Li4Ti5O12 particles using anatase—TiO2, Li2CO3, and acetylene black (AB) as Ti, Li and carbon precursor respectively. Remarkably, this indigenous design can easily eliminate the influence of the residual carbon, and thus makes it possible to individually study the effect of the Ti (III) on the bulk Li4Ti5O12. The presence of Ti (III) on the surface of Li4Ti5O12 not only improves the electronic conductivity, but also enhances the Li+ diffusion coefficient, therefore decreasing electrochemical polarization and improving the rate performance of LTO. In another study, Li4Ti5O12@CNT composites were prepared by a controlled in situ growth of CNTs on Li4Ti5O12. Since CNTs improve electronbridge between LTO particles, the electronic conductivity of Li4Ti5O12@CNT composites is better than that of pristine LTO and hence Li4Ti5O12@CNT composites show superior lithium storage properties comparable to the pristine Li4Ti5O12. Further, lithium titanate was also prepared by ball milling using micron sized TiO2 particles and lithium hydroxide as Ti and Li precursor respectively. However, the whole process involved a two-step milling, intermediate drying and then annealing again to produce lithium titanate.
It is known that smaller particle size and well crystallinity are both crucial for Li4Ti5O12 to achieve higher capacity and higher rate capability. Considering this, Zhu et al has developed [Zhu, et al. Energy Environ. Sci., 4 (2011) 4016] a facile method to synthesize a carbon-coated nano-sized Li4Ti5O12 by a combination of pre-carbon coating and spray drying. Though micron-size spherical particles used in this study induces large tap density and consequently enhance the volumetric energy density, the commercial TiO2 used for milling was initially carbon coated using sucrose by ball milling followed by carbonization to produce carbon coated TiO2, which was later milled with lithium carbonate to produce LTO. The process is found to be tedious involving multistep milling and annealing and hence it may be less attractive for commercial application. Matsui et al [J. Am. Ceram. Soc., 91 (2008) 1522-1527] synthesized lithium titanate using anatase TiO2 of particle size around 50 nm and lithium acetate as Ti and Li precursors respectively. Unlike in the present invention in which milled powders annealed at once to achieve the desire properties, two step annealing process and carbon coating was carried out in the reported study to produce single phase lithium titanate with improved electronic conductivity. Wang et al [J. Appl. Electrochem 40 (2010) 821-831] developed a modified ball-milling-assisted green solid reaction method followed by two step annealing process to prepare Li4Ti5O12/C composite materials using lithium carbonate, anatase TiO2, and activated carbon as Li, Ti and carbon precursors respectively. Further, hexane was also used as solvent for milling. Though the process employs tedious milling and annealing process to obtain phase pure lithium titanate with 10.6 wt % of carbon content, it still lacks in electrochemical performance compared to the lithium titanate according to the present invention.
Han et al [Han, et al. Appl Phys A 114 (2014) 925-930] reported the synthesis of Li4Ti5O12 by milling method using Li2CO3 and anatase TiO2 as Ti and Li precursor and studied different degree of milling to test the hypothesis that finer starting materials can result in a smaller Li4Ti5O12 particle size and better high-rate discharging capacities. The degree of milling was controlled by using three different ZrO2 ball sizes for high-energy milling (3 h) and 5 mm balls for planetary ball milling (24 h). The results indicated that high-energy milling produced significantly finer starting materials and Li4Ti5Ou particles compared to those produced by ball milling. Here again usage of solvent, intermediate drying step and slow annealing procedure makes the process tedious and time consuming. [Jhan, et al reported [Journal of Power Sources 198 (2012) 294-297] the synthesis of LTO/multi-walled carbon nanotube (MWCNT) composite is prepared by a ball-milling-assisted solid-state reaction and concluded that LTO nanoparticles were confined in the inter space of the MWCNT matrix and MWCNT prevent the aggregation of LTO particles during the calcination process of the solid-state reaction. Further, the entanglement of the MWCNTs and LTO creates an effective conductive network, which improves the conductivity of LTO. Therefore, the entanglement structure improves the electrochemical properties of LTO, such as the rate capability and cyclic stability. In addition, Sol-gel assisted ball milling technique [Yan, et al Journal of Alloys and Compounds 470 (2009) 544-547] was reported to produce lithium titanate where in it was synthesized by adopting sol-gel process, ball milling and then calcination process. The overall process including wet chemical method, intermediate heating, milling and a two step annealing process seems to be complicated, time consuming and expensive process though it exhibit reasonable electrochemical performance. Mechanical alloying is a basic technique used for milling of homogenous mixture of blended precursors and was used for synthesis of various alloying materials. Particularly, high kinetic horizontal rotary or horizontal attrition milling unit is the one that used for the solid state milling of composites with realistic of scalability and used for the production of alloys like Fe—Cr, Ni—Cr or milling of high-speed steel for particle size reduction. Since horizontal attrition milling forms a kinetic energy of 2-3 times higher than that of conventional planetary ball milling, milling time less than one order of magnitude can be reflected in former system in comparison with the later system. The main processing principle of milling is to transfer energy from kinetic collision of balls (Zoz et al Simo36-Paper) to powder. The continuous collection of milled powders without any wastage and environmental friendly condition added further advantages to horizontal attrition milling.
It can be inferred that none of the patents as well as literature matches with the present invention. Most of the patents were dealt with the synthesis of LTO by wet milling in the presence of a dispersing agent and the use of additional carbon coating and external doping for improving the electrical conductivity. Further, reduced atmosphere (H2+Ar) was used for creating oxygen vacancies to produce Ti3+ ions, which increase electrical conductivity in LTO. In contrast, in the present invention, we have adopted horizontal attrition milling, in which milling of Li and Ti (mixed phase) precursors with stearic acid which act as process control agent (PCA) as well as carbon precursor was carried out without external dopant ions, carbon precursor, and reducing atmosphere.
The objectives of the invention are:
Though large numbers of techniques are available for synthesis of lithium titanate, they all involve highly complicated synthesis procedures, huge amount of solvents, toxic chemicals and expensive techniques. The measures followed to overcome the disadvantages of LTO like poor electronic and ionic conductivity require the addition of one more step to the synthesis process making it more complicated and unsuitable for commercial applications. In the present invention we intent to develop a simple, economical and energy efficient scalable technique for production of LTO anode by a single step synthesis process-solid state method using TiO2 and Li2CO3 as precursor for Ti and Li respectively. Though synthesis of LTO from TiO2 and Li2CO3 reported previously by planetary ball milling, horizontal attrition milling process the most reliable technique for up-scaling without affecting the cost has been adopted by us for the first time to synthesize LTO. According to prior patent art and published literatures, many method of synthesis involves a two-step procedure wherein initially synthesis of LTO is carried out and later ex-situ carbon coating is done. Whereas in the instant invention, we have developed a single step process in which, the synthesis of LTO and carbon coating carried out simultaneously. The stearic acid used in the present invention plays a dual role, one as process controlling agent (PCA) to avoid stacking powders during milling and other as carbon precursor which is an added advantage compared to other technique. Further, it also helps to produce oxygen vacancies which can improve the electronic conductivity. The method followed here provides the ease of up scaling. This method ensures high cost effectiveness as the precursors used and the equipment handled is highly cost effective. Accordingly, a method of producing high performance lithium titanate anode using horizontal attrition milling process is disclosed here comprising the following features:
TiO2 (anatase or rutile or anatase and rutile) and Li2CO3 are used as titanium and lithium precursors respectively.
Different crystal phases of TiO2's such as anatase (100%), rutile (100%), mixed phases (anatase 60-80% & rutile 20-40%) were used to optimize the suitable titanium precursors required for the synthesis of lithium titanate. The resulting lithium titanate from 100% anatase, 100% rutile, 60% anatase & 40% rutile, and 80% anatase & 20% rutile TiO2 is referred as A-LTO, R-LTO, M1-LTO and M2-LTO respectively.
Lithium carbonate and titanium precursors were milled in horizontal attrition milling unit for a period of 0.5-2 hrs to blend them properly and to reduce the particle size.
Ball to powder ratio was maintained as 1:12 employing stainless steel vials as milling medium with 0.5-1 mm dia. stainless steel balls. A PCA is used to prevent the stacking of powders. Here 2-5 wt. % of stearic acid is used as PCA which then acts as carbon source also.
Blending of above mixture was carried out at a speed of 250 rpm and milling was done at 250-500 rpm for 0.5-2 hrs.
Milled powders are discharged and stored for annealing and characterization.
Annealing temperature and annealing time were optimized. Powders were pelletized using a 30-35 mm die with a pressure of 0.5-1 ton using a hydraulic press. When in pellet form, it ensures proper inter-particle contact and more heat transfer making annealing uniform throughout.
Annealing was carried out in argon or nitrogen or air atmosphere in tubular furnace.
Annealed powders were collected and grinded to fine powder and stored. On characterization of the resultant powders as anode material for Li-ion battery application, it was found to give excellent electrochemical performance in terms of high specific capacity, high rate capability and good cyclic stability.
A method of producing high performance nano sized lithium titanate powders for making the anode for lithium ion battery, using horizontal attrition milling according to our invention comprising the steps of: a) mixing of mixed phase having 60-80% anatase and 20-40% rutile of TiO2 as titanium precursor with Li2CO3 as lithium precursor in a stoichiometric ratio of 5:4 with 5 wt % of extra Lithium carbonate to compensate the lithium loss during heat treatment; b) adding 2 to 5% stearic acid which plays as process control agent as well as carbon precursor to the above mixture; c) milling in a horizontal attrition milling unit maintained with the ball to powder ratio of 10:1-12:1 at a speed of 250-500 rpm for 0.5-2 hrs; d) repeating the process of milling with the parameters mentioned in step c) for a period ranging from 40 to 48 times in a pattern by increase and decreasing the speed for a period of 0.5 to 2 hrs; e) discharging the milled powders from horizontal attrition milling unit on completion of milling and storing them for annealing in dry form; f) pelletizing the milled powder using a 30-35 mm die at a pressure of 0.5-1 ton using a hydraulic press to ensure proper inter-particle contact, more heat transfer, and thus making the process of annealing uniform throughout; g) annealing of the composite milled and pelletized powder under inert atmosphere of argon in a tubular furnace maintained at a temperature ranging from 700-900° C. with a heating rate of 10° C./min for a period of 2-12 hrs; and h) grinding the annealed pellets to a fine powder and validate its efficiency as anode material in half/full cell configuration for lithium ion battery application.
In a preferred embodiment under the invention, Li4Ti5O12 is produced by Horizontal attrition milling using TiO2 and Li2CO3 as precursor for Ti and Li respectively. TiO2 used here is very much cost effective which reduces the production cost. Cost effectiveness of TiO2 precursor, no intermediate drying process, high loading of powder per batch and less milling time make our invention more attractive for commercial application. The carbon present in LTO produces a reductive atmosphere in the presence of argon and creates oxygen vacancies. One oxygen vacancies resulting two electrons and for charge compensation transfer of one electron to adjacent Ti4+ in the lattice of LTO leads to the formation of Ti3+. This role of oxygen vacancies are expected to improve the electronic conductivity. Presence of Ti3+ ions are interpreted from XPS analysis and also from physical color change of samples from white to blue. FE-SEM was done to find out the particle size and was seen that M2-LTO with higher atomic concentration of Ti3+ ions produces smaller particles size of around 250-900 nm. Smaller the particle size, smaller is the lithium ion diffusion path length, therefore increasing the electrochemical performance. HR-TEM analysis showed the presence of thin layer of carbon and highly crystalline LTO particles which showed well defined fringes with morphology similar to that of FESEM analysis.
Other features and advantages of the present invention should become apparent from the following description of the preferred process and read in conjunction with the accompanying drawings, which illustrate, by way of example, the principles of the invention.
In accordance with the invention, high performance lithium titanate anode having excellent electrochemical characteristics are developed using TiO2 and Li2CO3 precursors by a simple, economical and scalable Horizontal attrition milling technique to achieve highly conducting lithium titanate. The preferred embodiments of the process under the invention with particular reference to the drawings are as follows.
Lithium titanate as an efficient anode for high energy density lithium ion battery application, according to the invention is synthesized by a simple, facile, fast, and economical and energy efficient Horizontal attrition milling technique. According to the invention, suitable Ti precursor is used without further purification or treatment. For synthesis of LTO, TiO2 and Li2CO3 in the stoichiometry ratio of 5:4 with 5 wt % of extra Lithium carbonate to compensate the lithium loss during heat treatment are transferred to the stainless steel horizontal vial of attrition milling unit. Stainless steel ball used as grinding media and with the ball to powder ratio of 10:1-12:1 was used for milling. Milling was carried out for a period of 0.5-2 hrs with appropriate acceleration and deceleration. Speed of milling was controlled between 250-500 rpm, which will avoid raise in temperature and thereby damage of the instrument. The capacity of milling vials is about 500-2500 g per run, which makes it attractive for large-scale production. Stearic acid was added as the process control agent to avoid stacking and the powders after milling were collected in the form of dry powders and stored properly.
The milled powders were then annealed to produce single-phase lithium titanate anode. Prior literatures have reported that temperatures above 750° C. results in the formation of crystalline lithium titanate. In the prior works argon atmosphere with mixed phases of hydrogen, nitrogen and air was used for annealing of lithium titanate. Mixed gas atmosphere is reported to create oxygen vacancies in the lithium titanate anode producing Ti3+ concentration. Ti3+ vacancies due to its more electron concentration improve the intrinsic electronic conductivity of lithium titanate.
According to the instant invention, LTO was synthesized using non-toxic, eco-friendly, cheap TiO2 precursors which were available commercially and was used without further purification. Horizontal attrition milling technique used in this embodiment of the invention enables proper blending and uniform particle size reduction of TiO2. Due to its high energy produced, it ensures less milling time compared to conventional planetary ball milling technique. The process control agent, which becomes a default additive for milling process here acts as a carbon source and helps to create oxygen vacancies and therefore improves the electronic conductivity of the material. This technique thus enables us to produce an efficient anode material lithium titanate, which can be very much suitable for high energy density lithium ion battery application.
Another embodiment of the invention is the presence of Ti3+ ions and oxygen vacancies created during annealing process under argon atmosphere. Milled lithium titanate precursors are pelletized using 30-35 mm die at a pressure of 0.5-1 ton and this ensures proper inter-particle contact. This makes proper crystallization of the bulk powders. The PCA present along with argon gas creates oxygen vacancies and therefore for charge compensation, Ti4+ ions are converted to Ti3+ ions.
The above embodiment of the present investigation facilitates formation of Ti3+ ion rich lithium titanate by a simple and economical Horizontal attrition milling technique. Lithium titanate synthesized under optimized condition of Ti precursors and annealing condition exhibit excellent electrochemical performance in terms of rate capability and cyclic stability showing its better role as a promising material in lithium ion batteries.
Having described the process of the invention in a general way, now we will further illustrate the mode of execution and demonstrate the characteristics/properties of LTO according to the process under the invention and also its electrochemical properties with the help of the following examples. The present invention is, however, not limited to these examples and various embodiments are possible within the scope thereof.
Li4Ti5O12 was synthesised using horizontal attrition milling process. The invention produces LTO using four different phases of TiO2. It uses pure anatase phase, rutile phase, Mixed phase 1 (60% Anatase and 40% Rutile) and Mixed phase two (80% Anatase and 20% Rutile) accordingly the respective LTO phases are labelled as A-LTO, R-LTO, M1-LTO and M2-LTO. The technique makes use of milling the raw TiO2 powders with Li2CO3 in a stochiometric ratio of 5:4 with 5 wt % of extra Lithium carbonate to compensate the lithium loss during heat treatment. For horizontal attrition milling powder ratio was maintained to be 10:1-12:1 with stainless steel as milling medium and stainless steel balls of 0.5 mm diameter. Process control agent (PCA) was used to prevent stacking of the powders to the walls of the vials. Here stearic acid was used as PCA. It was used to 2-5 wt % as it may contribute to the carbon content as well. The powders were initially blended at 250 rpm followed by milling at a speed between 250-500 rpm. This process was continued for 48 repetitions after which the powders were discharge and then stored for annealing and characterization. The schematic illustration for the synthesis of lithium titanate in the present invention is shown in
The product of example 1 is calcined to produce highly crystalline single phase LTO. Annealing was carried out under argon, nitrogen and air atmosphere. The powders were pelletized using a 30-35 mm die under 0.5-1 ton pressure using a hydraulic press. When in pellet form it is expected to exert uniform heat distribution by improved inter-particle contact. In inert gas atmosphere, purging was carried out using the respective gas to ensure oxygen is completely expelled. Heat treatment was carried out at 700-900° C. with a heating rate of 10° C./min. In the presence of inert atmosphere, carbon from PCA creates a reductive atmosphere to produce oxygen vacancies. When these oxygen-vacancies are created, the charge compensation is done by titanium ion in oxidation state of four. To find the influence of annealing time, annealing was carried out for different time lapses like 2-12 h. All the anatase TiO2 will be converted to rutile above 650° C. and then lithium diffusion into the lattice takes place. Lithium titanate formation takes place above 750° C. In the presence of inert atmosphere, carbon from stearic acid aids as carbon source creating uniform carbon layer to improve the electronic conductivity and also restricts the grain growth. X-ray diffraction studies were carried out to find the phase formation and crystallinity of the material developed using the invented method and is shown in =18.39, 35.57, 43.24, 57.21, 62.83, 66.07 which can be indexed to phase of pure lithium titanate respectively, (in agreement with ICDD #00-049-0207). The sharp peaks indicate that the LTO formed is crystalline. Such a pure phase with high order crystallinity may help to improve the battery properties of the developed anode material. The size and morphology of the materials were evaluated by field emission scanning electron microscopy and the results are depicted in
The electrochemical properties are the final target of the invented technique. The property of anode developed was tested in half-cell configuration using lithium metal as counter electrode. The crystalline anode material prepared was used for electrode fabrication to test the efficiency for electrochemical properties. For electrode fabrication, the electrode active material synthesized using horizontal attrition milling is taken along with conductive carbon and binder in a ratio of 80:10:10. They are grinded together and dissolved in NMP solvent to form homogenous slurry, which can be used for electrode fabrication. This slurry was coated over a current collector (in the present case copper foil acts as current collector) using doctor blade in a thickness of 15 micrometer. The resulting electrode is then dried at 60° C. for 12 h to evaporate the moisture and ensure the proper adherence of active material to the current collector. Then to ensure proper drying this is then dried at 120° C. for another 6 h. The efficiency of the horizontal attrition mill synthesized lithium titanate anode is tested using coin-cell to find the electrochemical performance using the electrodes fabricated using the above-mentioned process. An electrode was punched around 12 mm diameter and was weighed to find the active material weight. Lithium metal was used as the counter electrode and LiPF6 as electrolyte (EC:DEC:EMC in 1:1:1 vol %). The cells were assembled in argon-filled glove box to avoid the oxidation of electrolyte and to ensure the safety of lithium metal. The cells were then kept aside for a period of 6 h for wettability and stabilization of the open circuit voltage. The as fabricated cells were then tested using MTS pro 2000 Arbin instruments to find the electrochemical properties.
As M2-LTO developed in the present invention is found to be efficient in terms of electrochemical performance, benchmark studies were carried out to find the efficiency of the material for practical applications. Commercial lithium titanate powders were fabricated as thin film electrodes on copper foil using same procedure mentioned in example 3. Then it was cut to 12 mm discs to fabricate half-cell for electrochemical studies. Bench mark studies (
The LTO material synthesized by solid state milling method as mentioned in Example 1 was tested for electrochemical efficiency in full cell configuration with combination of LiFePO4 as cathode. The composite cathode consists of 88:8:4 (LFP:CB:PVDF) in the weight ratio. The cathode laminate thickness was 60 μm and the active materials loading was 3 mg/cm2. The anode consists of 80:10:10 (LTO:CB:PVDF) in the weight ratio. The anode laminate thickness was 50 μm and the active materials loading was 2.6 mg/cm2. The capacities were matched based on the half cell performance of LTO and LFP vs. Li metal. The anode to cathode active material weight ratio was maintained to be 0.88:1. The electrochemical performance of LFP-LTO full cell was tested using borosilicate glass fibre separator in 2032 type coin cell with 1M LiPF6 in EC:DEC:DMC (Geylon, PR China) as electrolyte. The initial charge process was carried out at C/10 rate, which is known as the formation step. The full cell delivered a capacity of 0.65 mAh during the formation step as shown in
Present embodiment explained the method of producing the lithium titanate anode with in-situ carbon coating, smaller particle size with Ti3+ ions and oxygen vacancies. The invention highlights a reliable method for up-scaling of nano materials using a simple, cost effective technique. It used titanium dioxide and lithium carbonate as titanium and lithium precursors along with process control agent to improve the efficiency of milling process. The parameters like ratios of different phases of titanium dioxide precursor suitable for producing single phase, crystalline lithium titanate powders with oxygen vacancies, annealing atmosphere, annealing time are optimized and corresponding physico-chemical and electrochemical studies were carried out as explained in above mentioned examples. It is identified that mixed phases of titanium dioxide milled with lithium carbonate in horizontal attrition mill was efficient in creating highly performing anode material with desirable characteristics for lithium ion battery applications.
We have bought out the novel features of the invention by explaining some of its preferred embodiments thereby enabling any person skilled in the art to understand and visualize our invention. It is also to be understood that the above invention is not limited in its application to the details set forth in the above description or illustrated in the drawings. The phraseology and terminology employed herein are for the purpose of description only and should not be regarded as limiting. Although the invention has been preferred embodiments thereof, variations and modifications can be affected within the spirit and scope of the invention as described herein above and as defined in the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201711006147 | Feb 2017 | IN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IN2018/050080 | 2/17/2018 | WO | 00 |