Patent Application
20190225491
The present invention relates broadly to a method of purifying metal oxide particles produced from a synthesis process, and uses thereof. More particularly, the present invention relates to a method of purifying a plurality of iron oxide particles produced from a thermal decomposition synthesis process so that the purified iron oxide particles may be used for biomedical and/or other consumer-based applications.
The following discussion of the background to the invention is intended to facilitate an understanding of the invention. However, it should be appreciated that the discussion is not an acknowledgement or admission that any of the material referred to was published, known or part of the common general knowledge in Australia or any other country as at the priority date of any one of the claims of this specification.
Over the last decade there has been much attention directed towards producing magnetic (nano) particles for a range of biomedical applications such as therapeutics, bio-sensing, cell separation and staining, and magnetic resonance imaging (MRI).
Iron oxide particles with different magnetic properties can be produced according to known literature methods. However, the purity of the iron oxide particles produced according to these methods leaves much to be desired, which renders them unsuitable for many of the biomedical applications highlighted above.
The cleaning or purification procedures outlined in these known literature methods are not well described. In many cases, regardless of the synthesis method used to produce the iron oxide particles, the cleaning or purification procedure typically involves washing the as-produced particles with copious amounts of a low order alcohol to remove the excess reagents and/or undesirable by-products associated with the synthesis method employed.
For example, one of the most commonly used methods for the production of iron oxide particles is the thermal decomposition technique because of the advantages associated with this technique such as monodispersity and high crystallinity of the obtained particles post-synthesis. In the last part of this particular technique, the obtained iron oxide particles are precipitated out of solution using ethanol. Here, however, the iron oxide particles are still impure on account of the particles being embedded within a range of unreacted organic compounds (oleic acid) and reaction solvents (1-octadecene) employed during the thermal decomposition reaction, as well as a number of by-products emerging from the reaction. Park et al[1] outlines a method in the literature to remove the excess oleic acid and 1-octadecene impurities by washing the impure iron oxide particles with copious amounts of ethanol. Yet, in practice, there is little evidence to suggest that the sole use of ethanol can remove all the impurities associated with this thermal decomposition reaction.
For biomedical and other consumer-based applications, the purification of the metal oxide particles is critical as impurities can influence a range of factors such a magnetic particle performance, size and subsequent phase transfer of these particles to aqueous or other polar solvents. For instance, if the surface of a particle is not sufficiently clean, a solution containing such impure particles will not behave like a colloidal suspension, causing the particles to aggregate, which may in turn affect their magnetic properties, and subsequently their application. Moreover, the large size due to particle aggregation will also affect their biological applicability, for instance their uptake mechanism by different organs, organelles and the lymphatic system.
Thus, there is an important need to remove excess reaction by-products from the surface of such metal oxide particles in a controllable and reproducible manner.
The present invention seeks to provide a method of purifying metal oxide particles post chemical synthesis, and uses thereof, which will overcome or substantially ameliorate at least some of the deficiencies of the prior art, or to at least provide an alternative.
According to a first aspect of the present invention, there is provided a method of purifying a plurality of metal oxide particles produced from a synthesis process, the method comprising the step of:
Preferably, the at least one aliphatic ether is at least partially miscible with the at least one flocculant.
Preferably, the at least one aliphatic ether and the at least one flocculant are in a 1:1 (vol/vol) ratio.
Preferably, the at least one aliphatic ether is selected from the group consisting of a primary aliphatic ether, a secondary aliphatic ether and a tertiary aliphatic ether.
Preferably, the at least one aliphatic ether is selected from the group consisting of diethyl ether, di-n-propyl ether, tert-butyl methyl ether and di-n-octyl ether.
Preferably, the at least one flocculant is selected from the group consisting of an alcohol, an aldehyde and a ketone.
Preferably, the at least one flocculant is an alcohol selected from the group consisting of a primary alcohol, a secondary alcohol and a tertiary alcohol.
Preferably, the alcohol is a primary alcohol selected from the group consisting of methanol, ethanol and n-propanol.
Preferably, the at least one aliphatic ether is diethyl ether and the at least one flocculant is methanol.
Preferably, the first solvent composition further comprises at least one non-polar solvent.
Preferably, the at least one aliphatic ether and the at least one non-polar solvent are at least partially miscible with the at least one flocculant.
Preferably, the at least one aliphatic ether, the at least one non-polar solvent and the at least one flocculant are in a 1:1:2 (vol/vol) ratio.
Preferably, the least one non-polar solvent is hexane.
Preferably, the method further comprises, after step a), the step of:
Preferably, the at least one non-polar solvent is at least partially miscible with the at least one flocculant.
Preferably, the at least one non-polar solvent and the at least one flocculant are in a 1:1 (vol/vol) ratio.
Preferably, the at least one non-polar solvent is hexane and the at least one flocculant is ethanol.
Preferably, the method further comprises, after step a) but before step b), the step of:
Preferably, the physical separation procedure is selected from the group consisting of magnetic separation, centrifugation, filtration and decantation.
Preferably, the method further comprises, after step b), the step of:
Preferably, the least one non-polar solvent is hexane.
Preferably, the method further comprises, after step b) but before step c), the step of:
Preferably, the physical separation procedure is selected from the group consisting of magnetic separation, centrifugation, filtration and decantation.
According to a second aspect of the present invention, there is provided a method of purifying a plurality of iron oxide particles produced from a thermal decomposition synthesis process between an iron-oleate complex and oleic acid in 1-octadecene, the method comprising the steps of:
Preferably, the method further comprises, after step a) but before step b), the step of:
Preferably, the method further comprises, after step b) but before step c), the step of:
Preferably, the method further comprises, the step of:
According to a third aspect of the present invention, there is provided a use of iron oxide particles purified according to the method of the second aspect as a contrast agent for magnetic resonance imaging (MRI).
According to a fourth aspect of the present invention, there is provided a use of iron oxide particles purified according to the method of the second aspect as magnetic particles in a magnetism-assisted process selected from the group of processes consisting of magnetic separation, magnetism-directed targeting and magnetism-induced heating.
Other aspects of the invention are also disclosed.
Notwithstanding any other forms which may fall within the scope of the present invention, preferred embodiments of the invention will now be described, by way of example only, with reference to the accompanying drawings in which:
The present invention is predicated on the finding of a method for purifying metal oxide particles produced according to any one of a number of metal oxide particle synthesis processes including but not limited to thermal decomposition methods, hydrothermal synthesis methods, co-precipitation methods and micro-emulsion techniques. Regardless of the synthesis process, all metal oxide particle synthesis processes require a level of rigorous purification to remove the excess reactants and the associated by-products.
One of the most commonly used and preferred synthesis processes to produce iron oxide particles is the thermal decomposition method employed by Park et al[1], because of the desirable properties achieved using this method such as monodispersity and high crystallinity, as well as the propensity for large-scale manufacturing. In the last phase of the thermal decomposition method, iron oxide particles are precipitated out of the reaction solution using ethanol. The iron oxide particles obtained in this manner are typically embedded within a range of unreacted organic compounds and reaction solvents used during the synthesis, such as excess oleic acid and 1-octadecene. To address this, Park et al[1] relies on a purification step in which the precipitated iron oxide particles are washed in copious amounts of ethanol to remove the unwanted organic contaminants. However, in practice, there is little evidence that the sole use of ethanol is sufficient to remove these unwanted organic contaminants.
Embodiments of the present invention will be described in terms of purifying a plurality of iron oxide particles produced according to the thermal decomposition method employed by Park et al[1]. However, it will be appreciated by those skilled in the relevant art that the rigorous cleaning protocol outlined below could equally be employed in the purification of iron oxide particles, and indeed other metal oxide particles, produced according to one of the other highlighted syntheses processes
A method of purifying a plurality of iron oxide particles produced from a thermal decomposition synthesis process between an iron-oleate complex and oleic acid in 1-octadecene according to a preferred embodiment of the present invention will now be described.
The method comprises, as a first step, step a), the step of washing the plurality of as-produced iron oxide particles in a first solvent composition comprising of an aliphatic ether and a flocculant in the form of a solvent.
The inventors have found that the choice of aliphatic ether and flocculant is dependent on the basis that these solvents should be at least partially miscible with each other.
The aliphatic ether may be a primary, secondary or tertiary aliphatic ether.
As will be described in the examples below, good results have been obtained when the aliphatic ether is selected from the group consisting of diethyl ether, di-n-propyl ether, tert-butyl methyl ether (TBME) and di-n-octyl ether.
In a preferred embodiment, the aliphatic ether is diethyl ether.
The flocculant may be selected from the group consisting of an alcohol, an aldehyde and a ketone.
Suitably, the flocculant is a low order alcohol selected from the group consisting of a primary alcohol, a secondary alcohol and a tertiary alcohol.
In one embodiment, the low order alcohol is a primary alcohol selected from the group consisting of methanol, ethanol and n-propanol.
In a preferred embodiment, the flocculant is methanol.
The inventors have found that the ratio of aliphatic ether to flocculant in the first solvent composition may be varied by up to 20% (for example, approximately a 5 ml variation of either solvent) and still achieve an effective cleaning protocol.
In a preferred embodiment, the aliphatic ether and the flocculant are in a 1:1 (vol/vol) ratio. Good results detailing the effectiveness of this 1:1 (vol/vol) ratio can be found in the Examples and Table provided below.
The inventors have also found that the ratio of solvent used in the first solvent composition to the amount of iron oxide particles is critical to achieving a good cleaning protocol. For instance, as shown in Table 1, the study as exemplified in Examples 5A to 5E described below, demonstrates that as the ratio of solvent to iron oxides particles transitions from 49.0:1.0 to 47.0:3.0, the effectiveness of the cleaning protocol steadily worsens.
Whilst not wishing to be bound by any one particular theory, the inventors believe that this reduced cleaning efficiency is due, at least in part, to finite miscibility of contaminant species bound onto as-prepared iron oxide particles with the solvent mixture used for cleaning, along with an equilibrium state responsible for co-existence of contaminant species bound onto particles surface and those in the solvent mixture.
As will be described in Example 1 below, excellent results have been obtained when the first solvent composition comprises diethyl ether and methanol in a 1:1 (vol/vol) ratio, where the ratio of solvent to iron oxide particles is 49:1.
The inventors have also found that the first solvent composition may further comprise a non-polar solvent, in addition to the aliphatic ether and the flocculant. It will be appreciated by those skilled in the relevant art that the choice of non-polar solvent, aliphatic ether and flocculant is dependent on the basis that these solvents should be at least partially miscible with each other.
In a preferred embodiment, the non-polar solvent is hexane.
As will be described in Example 19 below, good results have been obtained when the first solvent composition comprises hexane, diethyl ether and methanol in a 1:1:2 (vol/vol) ratio, where the ratio of solvent to iron oxide particles is 49:1.
Once washed, the plurality of washed iron oxide particles are then isolated from the first solvent composition using a physical separation procedure. It will be appreciated by those skilled in the relevant art that any one of a number of standard procedures may be used to isolate the washed iron oxide particles, including but not limited to, magnetic separation, centrifugation, filtration and decantation.
As will be described in the examples below, good results have been obtained when the plurality of washed iron oxide particles are separated from the first solvent composition using magnetic separation.
The method comprises, as a second step, step b), the step of further washing the plurality of iron oxide particles washed according to step a) in a second solvent composition comprising of a non-polar solvent and a flocculant.
Again, the inventors have found that the choice of non-polar solvent and flocculant is dependent on the basis that these solvents should be at least partially miscible with each other.
In a preferred embodiment, the non-polar solvent is hexane and the flocculant is ethanol used in a 1:1 (vol/vol) ratio.
Again, once washed, the plurality of further washed iron oxide particles are then isolated from the second solvent composition using a physical separation procedure such as magnetic separation.
The method comprises, as a third step, step c), the step of dispersing the plurality of further washed iron oxide particles in a third solvent composition which is comprised of a non-polar solvent.
In a preferred embodiment, the non-polar solvent is hexane.
It will be appreciated by those skilled in the relevant art that any one of steps a) to c) of the cleaning protocol described above may be repeated, according to step d), to achieve the desired purity.
In essence, the inventors have found that by conducting each of steps a) to c) of the cleaning protocol described above, it is possible to obtain iron oxide particles of sufficient purity to render them viable for a range of biomedical applications such as therapeutics, bio-sensing, cell separation and staining, magnetic separation techniques for separating a desired entity in solution from, for example, chemical reactants and/or by-products, magnetism-directed targeting, magnetism-induced heating, and as a contrast agent for magnetic resonance imaging (MRI).
The following examples and figures are provided for illustrative purposes. It is thus understood that the examples and figures are not to be construed as limiting. The skilled person in the art will clearly be able to envisage further modifications of the principles laid out herein.
Impure iron oxide particles were obtained according to the thermal decomposition method as outlined in Park et al[1], albeit with some slight differences in that, an anhydrous iron (III) chloride precursor was used for the synthesis instead of iron (III) chloride hexahydrate, and the post-synthesis step of precipitating the obtained iron oxide particles from solution using copious amounts of ethanol was not employed.
Briefly, to 1 mL of the obtained iron oxide particles was added 49 mL of a first solvent composition comprising a (1:1 vol/vol) mixture of the non-polar solvent, diethyl ether, and the flocculent, methanol. The highly waxy iron oxide particles dispersed readily in the first solvent composition, and the majority of the particles immediately precipitated out of solution.
The mixture was then sonicated for 5 minutes to facilitate efficient cleaning of the iron oxide particles. The iron oxide particles were then magnetically separated from the solution by applying a magnet immediately to the outside of the reaction vessel for approximately 2 to 3 minutes. Magnetic separation of the iron oxide particles indicated purification, as prior to cleaning; the impure iron oxide particles obtained from the thermal decomposition process could not be magnetically separated from the surrounding organic solvents and impurities. The supernatant was decanted off while the now separated iron oxide particles remained at the bottom of the vessel on account of the external magnetic field. The magnet was then removed and then the semi-purified iron oxide particles were subjected to a second solvent composition comprising a non-polar solvent in the form of hexane and a flocculent in the form of ethanol. Here, the hexane (10 mL) was added first to cause the semi-purified iron oxide particles to redisperse into solution, turning the solution black. The ethanol (10 mL) was then added to the solution and the resulting mixture was sonicated for 5 minutes. The iron oxide particles were again magnetically separated according to the same procedure as described above. The cleaned iron oxide particles appeared black, wet and without an oily sheen or residue. Finally, the cleaned iron oxide particles were dispersed in hexane to form a colloidal suspension.
The efficiency of the cleaning protocol of Example 1 was assessed via transmission electron microscopy (TEM) and Fourier transform infrared spectroscopy (FTIR) of the obtained iron oxide particles dried under ambient conditions.
This example shows a rapid (5-15 minutes), low cost (˜0.2 L versus tens of litres of organic solvents for purification), environmentally friendly (by minimising organic solvent wastes), high yield and more effective (i.e. better cleaning) method for the purification of iron oxide particles from residual solvents and organic impurities. Furthermore, the ability to magnetically separate the cleaned iron oxide particles throughout the purification process is further evidence of the excellent cleaning efficacy of this protocol.
As shown in
FTIR is a useful technique for assessing the nature and relative abundance of any organic impurity that might be present on the surface of the iron oxide particles obtained from the thermal decomposition synthesis, pre- and post-purification. This, in turn, will reflect upon the level of purification achieved through a particular cleaning protocol.
The FTIR spectrum shown in
In contrast, when the impure iron oxide particles are cleaned by employing the above-described protocol, the cleaned iron oxide particles show only limited features, thereby suggesting in the first instance of most of the impurities have been removed during the cleaning process. Specifically, as is apparent from the FTIR spectrum in
Careful analysis of the FTIR vibrations observed in the spectrum (
Another important peak observed in the FTIR spectrum (
Additional peaks at 2850 cm−1 and 2918 cm−1 in the FTIR spectrum (
In summary, therefore, the inventors have surprisingly found that the cleaning protocol of Example 1 removes most of the unreacted chemical precursors and by-products associated with the thermal decomposition synthesis in a simple washing step.
It will be appreciated that the flocculant, methanol, may be exchanged for ethanol, propanol or acetone.
This present example follows a similar cleaning protocol to that described in Example 1, with the exception that the cleaning protocol described here comprises an additional step of washing the cleaned iron oxide particles a second time with the second solvent composition (1:1 ratio of hexane and ethanol).
As shown in
The FTIR spectrum shown in
Whilst not wishing to be bound by any one particular theory, the inventors are of the view that this change in value strongly suggests that the nature of coordination of the COO− group to the metal ion changes from bidentate chelating to a predominantly bridging ligand configuration. As such, this indicates a change in the nature of the bonding between the iron oxide particles and the oleate species from covalent towards ionic and hydrogen bonding. Considering that the strength of covalent bonds is significantly higher than those of other bonds, the additional cleaning step involving the second solvent composition (1:1 ratio of hexane to ethanol) appears to loosen the layer of organic molecules bound to the surface of the iron oxide particles.
This present example follows a similar particle cleaning protocol as described in Example 1, with the exception that in the cleaning protocol described here, the step of washing the cleaned iron oxide particles using the second solvent composition (1:1 ratio of hexane and ethanol) is repeated a further three (3) times.
As shown in
However, as in the case of Example 2, the FTIR spectrum (
A number of other changes in the FTIR spectrum (
For instance, new peaks at 1066 cm−1 and 3675 cm−1 observed in the FTIR spectrum (
In summary, the FTIR analyses clearly reveal that after multiple cleaning steps according to the protocol of Example 3, a layer of oleate molecules becomes the predominant capping agent on the surface of the iron oxide particles.
This present example follows a similar particle cleaning protocol as described in Example 1, with the exception that in the cleaning protocol described here, the step of washing the cleaned iron oxide particles using the second solvent composition (1:1 ratio of hexane and ethanol) is repeated a further five (5) times.
As shown in
Similarly, the FTIR spectrum (
Whilst not wishing to be bound by any one particular theory, the inventors are of the view that only a very fine layer of oleate caps the surface of the iron oxide particles cleaned according to the protocol of Example 4. This impact upon the applicability of these particles, such that once these iron oxide particles are precipitated out of solution, it becomes extremely difficult to redisperse these particles in either a non-polar or polar solvent.
In summary, therefore, the inventors have found that the iron oxide particles purified according to the protocols described in Examples 1 and 2 are more readily redispersed in non-polar or polar solvents.
This present example follows a similar particle cleaning protocol as described in Example 1, with the exception that the ratio of first solvent composition (1:1 diethyl ether to methanol) to the iron oxide particles to be purified was gradually decreased from the 49:1 ratio employed in the protocol of Example 1 to: 48.75:1.25 (Example 5A), 48.5:1.5 (Example 5B), 48.25:1.75 (Example 5C), 48.0:2.0 (Example 5D), and 47.0:3.0 (Example 5E). This was done to assess the impact of increasing the amount of impure iron oxide particles relative to the volume of the first solvent composition used in the cleaning protocol.
It is evident from the TEM images (
Also, while the iron oxide particles cleaned according to the protocol of each of Examples 5A to 5E could be separated using an external magnet applied to the wall of the reaction vessel (suggesting some degree of cleaning), the process was not particularly efficient as it took longer to separate the iron oxide particles (suggesting inefficient cleaning) than it did for the iron oxide particles cleaned according to the protocol of Example 1. The iron oxide particles thus obtained using magnetic separation displayed a mild to strong oily sheen suggestive of a less than efficient cleaning protocol, in contrast to that seen for Example 1 above.
The FTIR spectra (
In summary, therefore, the inventors have found that an appropriate solvent to particle ratio is critical for an efficient cleaning methodology.
This present example follows a similar cleaning protocol as described in Example 1, with the exception that the non-polar solvent (diethyl ether) used in the first solvent composition was substituted for di-n-propyl ether. This was done to assess the impact of the increasing carbon chain length of ethers on the cleaning efficiency in respect of the first solvent composition.
The inventors have found that while the iron oxide particles could not be purified to the same degree as when diethyl ether was used in the first solvent composition (Example 1), the iron oxide particles were still capable of being magnetically separated after the first washing step, thus indicating some degree of cleaning.
Indeed, it is evident from the TEM image (
As shown in
In summary, the inventors have found that the choice of solvent for use in at least the first solvent composition is important for realising an efficient cleaning methodology.
This present example employs a cleaning protocol similar to that described in Example 1, with the exception that the first solvent composition comprised the non-polar solvent, dioctyl ether as opposed to diethyl ether. This increase in the carbon chain length from C2 (ethyl) to C8 (octyl) corresponds to an increase in non-polarity of the solvent. In this respect, the similarity in the symmetric structures of diethyl ether and dioctyl ether could potentially allow the impact of non-polarity of the ether side groups on the cleaning efficiency of the iron oxide particles to be assessed.
However, the inventors found that the degree of non-polarity of the dioctyl ether rendered it immiscible with the other component of the first solvent composition, that being the methanol flocculant. As a result, the impure iron oxide particles added to this immiscible solvent mixture dispersed only in the dioctyl ether phase without interaction with the methanol phase. This proved problematic during the iron oxide particle cleaning procedure of Example 7 as without the direct availability of a suitable flocculant (i.e. methanol), the iron oxide particles could not be precipitated. Hence, further purification steps could not be performed and the iron oxide particles could not be purified using this first solvent composition.
This present example follows a similar cleaning protocol as described in Example 1, with the exception that the first solvent composition comprised the non-polar solvent, diphenyl ether as opposed to diethyl ether. While diethyl ether has two aliphatic ethyl groups on either side of the oxygen molecule, the side groups of diphenyl ether are aromatic groups. In this respect, the similarity in the symmetric structures of diethyl ether and diphenyl ether could potentially allow the impact of non-polarity of either side chains on the particle cleaning protocol to be assessed.
Here, however, like in Example 7, the inventors found that the diphenyl ether and methanol components of the first solvent composition were immiscible. Thus, when the impure iron oxide particles were added to this immiscible solvent mixture, the iron oxide particles dispersed only in the diphenyl ether phase without interaction with the methanol phase. This again proved problematic during the particle cleaning protocol of Example 8 as without the direct availability of a suitable flocculant (i.e. methanol), the iron oxide particles could not be precipitated. Hence, further purification steps could not be performed and the iron oxide particles could not be purified using this first solvent composition.
This present example follows a similar cleaning protocol to that described in Example 1, with the exception that the first solvent composition comprised the non-polar solvent, tert-butyl ethyl ether (TBME) as opposed to diethyl ether. This was done to assess the impact of the position of the ether group and the symmetric nature of the ethers on cleaning efficiency. TBME was selected as it is an asymmetrical ether with the chemical structure, (CH3)3COCH3. This significant change in structure was used to determine any impact on the purification process using R≠R′, whilst maintaining its characteristic functional group.
It is evident from the TEM image (
In summary, therefore, the inventors have found that the choice of an appropriate solvent is important for realising an efficient cleaning methodology.
The cleaning protocol of the present example is similar to that of Example 1, with the exception that the low order alcohol (such as methanol ethanol or propanol) used as a flocculant in the first solvent composition was replaced by a higher order alcohol (such as butanol) in the present example. This was done to assess if the use of a low order alcohol was critical for the purification process.
The inventors found, however, that butanol was not miscible with diethyl ether, which meant that the impure iron oxide particles remained in the top diethyl ether phase whilst the lower butanol layer remained clear. Followed by vigorous sonication, these particles were independently subjected to centrifugation and magnetic separation. However, the iron oxide particles obtained could not be separated by either of these techniques.
In summary, the inventors have found that at least partial miscibility of the non-polar solvent and flocculent in the first solvent composition is paramount to achieving a high cleaning efficiency of iron oxide particles, as demonstrated in Example 1.
According to this example, the flocculant, methanol, was removed from the first solvent composition to determine if the use of methanol or another low-order alcohol as flocculant was critical for the purification process.
According to this protocol, diethyl ether (49 mL) was combined with 1 mL of the impure iron oxide particles and the resulting mixture was sonicated for 10 minutes. The iron oxide particles were then subjected to centrifugation and magnetic separation. However, the iron oxide particles could not be separated by either of these techniques.
In summary, the inventors have found that the inclusion of a lower order alcohol and/or a flocculant in the first solvent composition is critical for achieving purification of the iron oxide particles to the same level of purity as demonstrated in the cleaning protocol of Example 1.
This comparative example follows the iron oxide particle cleaning protocol described in Park et al.[1] in which the iron oxide particles were cleaned via repeated washing steps using an excess amount of a low order alcohol, which in the case of Park et al.[1] was ethanol.
To achieve this, 100 μL of impure iron oxide particles was added to 50 mL of ethanol in a 50 mL centrifuge tube and then mixed via sonication for two hours. The particle solution appeared to be immiscible with the ethanol even after extended periods of sonication. The particles were then collected by centrifugation and the supernatant was discarded. After centrifugation, the iron oxide particles were stuck to the inside wall of the centrifuge tube. 50 mL of additional ethanol was then added and the solution was sonicated for a further two hours in an attempt to dislodge the iron oxide particles from the inside wall of the centrifuge tube, and thus suspend them in the ethanol. This process was repeated 10 times over a number of days.
Here, however, the inventors found that despite extended sonication of the solution at each stage of the washing process, a number of the iron oxide particles could not be recovered after each washing step. Notably, it was not possible to magnetically separate the iron oxide particles until after the 4th ethanol wash, at which point less than half the sample could be magnetically separated, suggesting only a minor degree of cleaning at this stage.
The inventors observed that the amount of iron oxide particles capable of being magnetically separated increased gradually as the number of ethanol washes increased. However, it is widely apparent that a significant proportion of the iron oxide particles (over 50%) were lost during the cleaning steps.
It is evident from the TEM image (
However, from a comparison of the FTIR spectrum (
In summary, the inventors have found that even though the use of ethanol as a solvent may result in a reasonable cleaning efficacy, there are not only significant drawbacks associated with this approach including time, labour, cost, and solvent-intensiveness, but also a significant loss of product during the cleaning process.
This comparative example follows an iron oxide cleaning protocol frequently cited in the prior art (Burdinski, 2013)[2] in which the first solvent composition comprises the non-polar solvent, hexane, in combination with a semi miscible or fully miscible polar solvent, most commonly ethanol, propanol, or acetone.
This cleaning protocol was investigated to compare the efficacy and effectiveness of this approach with the methodology employed in Example 1.
As a representative flocculant, acetone was combined with hexane at a (1:1 vol/vol) ratio. Impure iron oxide particles were then added to this solvent mixture at a (1:49 vol/vol) ratio and the mixture was sonicated for 5 minutes.
The inventors found that the iron oxide particles cleaned according to this approach could not be magnetically separated from the solution, and hence, they were instead collected by centrifugation at 10,000 RPM for 10 minutes. The obtained iron oxide particles were then suspended in 10 mL of hexane and 10 mL of ethanol was added. The resulting solution was then mixed for 10 minutes, sonicated for 5 minutes, and then the iron oxide particles were magnetically separated.
As shown in the TEM image (
Indeed, a comparison of the FTIR spectrum (
In summary, therefore, the inventors have found that while a first solvent composition comprising hexane and acetone provides a modest degree of cleaning, the iron oxide particles thus obtained are not as clean as those obtained according to the cleaning protocol of Example 1.
Increasing the amount of flocculant(s) in the solvent composition has been reported to improve the precipitation and purification of particles (Burdinski, 2013)[2].
The present example is similar to the cleaning protocol of Example 13, albeit with the difference that the amount of flocculent (acetone or ethanol) used in the first solvent composition is twice that of hexane used in Example 13. Here, 1 mL of the impure iron oxide particles was heated at 50° C. and 10 mL of hexane, also heated to 50° C., was added to the heated iron oxide particles to obtain a homogenous solution. To this was added 20 mL of acetone to precipitate the iron oxide particles. The precipitated particles were subsequently collected by centrifugation at 5000 rpm for 30 minutes and resuspended in 5 mL of hexane, followed by addition of 10 mL of acetone. The particles were collected again by centrifugation and the washing process was repeated two more times.
As shown in
The FTIR spectrum (
According to this example, the first solvent composition comprised a combination of the non-polar solvent, hexane, and a low order alcohol in the form of either methanol or butanol as a flocculant, both of which remain immiscible with hexane.
When impure iron oxide particles were added to the first solvent composition, the inventors found that even after forced mixing through sonication, the impure iron oxide particles remained in the upper solvent layer of hexane whilst the bottom methanol or butanol layer remained completely clear. Moreover, all attempts to collect the iron oxide particles via centrifugation at 10,000 rpm for 30 minutes failed, where all of the iron oxide particles remained in solution and could not be precipitated.
According to this example, the first solvent composition comprised a (1:1) combination of hexane and diethyl ether. The cleaning protocol was carried out by adding 49 mL of the first solvent composition to 1 mL of impure iron oxide particles. The mixture was sonicated for 10 minutes and the particles were then subjected to centrifugation at 10,000 rpm for 30 minutes. However, the particles could not be precipitated by centrifugation. Moreover, these particles could not be separated by magnetic separation. In a further step, 49 mL of ethanol was then added to this mixture as a flocculant to promote precipitation of the iron oxide particles. However, it was still not possible to collect the particles by centrifugation.
The suitability of petrol as a particle cleaning agent was assessed based on its non-polar nature and complex composition. According to this example, unleaded petrol containing n-hexane to n-nonane (12%), isomeric alkanes and n-butane (11%), cyclohexane and derivatives (5%), butene to hexene (25%), 1-nonene (12%), toluene (1%), xylenes (22%) and higher aromatics (11%) in approximate concentrations was used. This example is similar to Example 1, with the exception that the first cleaning step involved petrol instead of a solvent composition containing diethyl ether and methanol. Here, 49 mL of petrol was combined with 1 mL of impure iron oxide particles. This solution was mixed by sonication for 10 minutes. Following this primary washing step, a portion of the particles were capable of being magnetically separated, suggesting that petrol has some efficacy when cleaning iron oxide particles. However, to collect the total amount of iron oxide particles, centrifugation was performed at 5000 rpm for 30 minutes. The obtained iron oxide particles were resuspended in 20 mL of a second solvent composition comprising a (1:1 vol/vol) ratio of hexane and ethanol. This mixture was then sonicated for 10 minutes, followed by collection of the iron oxide particles via magnetic separation.
As shown in
The FTIR spectrum (
This present example is similar to the cleaning protocol described in Example 1, with the exception that petrol and methanol (1:1) were employed in the first solvent composition. After cleaning, it was found that the iron oxide particles could be magnetically separated suggesting that petrol may be a suitable replacement for diethyl ether in the first solvent composition. It is notable that the iron oxide particles cleaned according to the present example could be magnetically separated more easily than in Example 17, where only petrol was used in the first solvent composition. This goes some way to highlight the importance of combining a non-polar solvent with an appropriate flocculent and/or a low order alcohol to obtain the highest possible particle cleaning efficiency.
The quality of the iron oxide particles cleaned according to the protocol of the present example would appear to be largely the same as that in Example 17, as confirmed by the TEM image (
This present example is similar to the cleaning protocol described in Example 1, with the exception that the first solvent composition is comprised of two non-polar solvents (diethyl ether and hexane) and a flocculant (methanol) in a 1:1:2 (vol/vol) ratio.
The addition of hexane to the first solvent composition associated with the primary cleaning step appears to clean the particles to a high level comparable to that observed in the cleaning protocol of Example 1. Evidence for this observed improvement is apparent in the TEM image in
Hexane (95% purity) was obtained from RCI Labscan Ltd (Australian distributor) and used without further purification. Methanol (99.8% purity), ethanol (99.5% purity), propan-2-ol (99% purity) and diethyl ether (99.5% purity) were obtained from Chem-Supply Pty Ltd (South Australia) and used without further purification. Butanol (99.8% purity), di-n-propyl ether (99% purity), tert-butyl methyl ether (TBME) (98% purity) and di-n-octyl ether (99% purity) were obtained from Sigma Aldrich and used without further purification. Unleaded petrol grades (“petrol”); product codes 010066-85, 22004-85, 929141-85) were obtained from Mobil Oil Australia Pty Ltd and used without further purification.
Whenever a range is given in the specification, for example, a temperature range, a time range, or concentration range, all intermediate ranges and subranges, as well as all individual values included in the ranges given are intended to be included in the disclosure. It will be understood that any subranges or individual values in a range or subrange that are included in the description herein can be excluded from the claims herein.
All definitions, as defined and used herein, should be understood to control over dictionary definitions, definitions in documents incorporated by reference, and/or ordinary meanings of the defined terms.
Flocculants, or flocculating agents (also known as flocking agents), are chemicals that promote flocculation by causing colloids and other suspended particles in liquids to aggregate, forming a floc.
The indefinite articles “a” and “an,” as used herein in the specification, unless clearly indicated to the contrary, should be understood to mean “at least one.”
The phrase “and/or,” as used herein in the specification, should be understood to mean “either or both” of the elements so conjoined, i.e., elements that are conjunctively present in some cases and disjunctively present in other cases. Multiple elements listed with “and/or” should be construed in the same fashion, i.e., “one or more” of the elements so conjoined. Other elements may optionally be present other than the elements specifically identified by the “and/or” clause, whether related or unrelated to those elements specifically identified. Thus, as a non-limiting example, a reference to “A and/or B”, when used in conjunction with open-ended language such as “comprising” can refer, in one embodiment, to A only (optionally including elements other than B); in another embodiment, to B only (optionally including elements other than A); in yet another embodiment, to both A and B (optionally including other elements); etc.
While the invention has been described in conjunction with a limited number of embodiments, it will be appreciated by those skilled in the art that many alternatives, modifications and variations in light of the foregoing description are possible. Accordingly, the present invention is intended to embrace all such alternatives, modifications and variations as may fall within the spirit and scope of the invention as disclosed.
Where the terms “comprise”, “comprises”, “comprised” or “comprising” are used in this specification (including the claims) they are to be interpreted as specifying the presence of the stated features, integers, steps or components, but not precluding the presence of one or more other features, integers, steps or components, or group thereof.
The present application may be used as a basis or priority in respect of one or more future applications and the claims of any such future application may be directed to any one feature or combination of features that are described in the present application. Any such future application may include one or more of the following claims, which are given by way of example and are non-limiting in regard to what may be claimed in any future application.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2016903721 | Sep 2016 | AU | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/AU2017/050981 | 9/8/2017 | WO | 00 |