Patent Application
20250050612
The present disclosure relates to a pressing module for forming cellulose products from an air-formed cellulose blank structure. The pressing module comprises a forming mould with a first mould part and a second mould part configured for interacting with each other for forming the cellulose products from the air-formed cellulose blank structure in the forming mould. The first mould part and/or the second mould part are movably arranged relative to each other in a pressing direction parallel to a longitudinal direction of the pressing module. The disclosure further relates to a method for forming cellulose products from an air-formed cellulose blank structure in a pressing module.
Cellulose fibres are commonly used as raw material for producing or manufacturing products. Products formed of cellulose fibres can be used in many different situations where there is a need for sustainable products. A wide range of products can be produced from cellulose fibres and a few examples are disposable plates and cups, cutlery, lids, bottle caps, coffee pods, blank structures, and packaging materials.
Forming mould systems are commonly used when manufacturing cellulose products from raw materials including cellulose fibres, and traditionally the cellulose products have been produced by wet-forming methods. A material commonly used for wet-forming cellulose fibre products is wet moulded pulp. Wet-formed products are generally formed by immersing a suction forming mould into a liquid or semi liquid pulp suspension or slurry comprising cellulose fibres, and when suction is applied, a body of pulp is formed with the shape of the desired product by fibre deposition onto the forming mould. With all wet-forming methods, there is a need for drying of the wet moulded product, where the drying process is a time and energy consuming part of the production. The demands on aesthetical, chemical and mechanical properties of cellulose products are increasing, and due to the properties of wet-formed cellulose products, the mechanical strength, flexibility, freedom in material thickness, and chemical properties are limited. It is also difficult in wet-forming processes to control the mechanical properties of the products with high precision.
One development in the field of producing cellulose products is dry-forming of cellulose products without using wet-forming methods. Instead of forming the cellulose products from a liquid or semi liquid pulp suspension or slurry, an air-formed cellulose blank structure is used. The air-formed cellulose blank structure is inserted into a forming mould and during the dry-forming of the cellulose products, the cellulose blank is subjected to a high forming pressure and a high forming temperature.
One difficulty with dry-forming methods is the problem with forming specific parts or sections of the cellulose products having complex shapes, such as shapes with negative draft angles or undercut sections. These types of complex product shapes are commonly wet-formed and thereafter pressed in several forming steps in order to establish the desired product shape. This is a time and energy consuming method, and there is thus a need for a more efficient and simple method and system for dry-forming cellulose products with complex shapes from an air-formed cellulose blank structure.
An object of the present disclosure is to provide a pressing module for forming cellulose products from an air-formed cellulose blank structure and a method for forming cellulose products from an air-formed cellulose blank structure in a pressing module, where the previously mentioned problems are avoided. This object is at least partly achieved by the features of the independent claims. The dependent claims contain further developments of the pressing module and the method.
The disclosure concerns a pressing module for forming cellulose products from an air-formed cellulose blank structure. The pressing module comprises a forming mould with a first mould part and a second mould part configured for interacting with each other for forming the cellulose products from the air-formed cellulose blank structure in the forming mould. The first mould part and/or the second mould part are movably arranged relative to each other in a pressing direction parallel to a longitudinal direction of the pressing module, and the first mould part and the second mould part are at least partly configured for being arranged in an overlapping relationship in the longitudinal direction during forming of the cellulose products. The first mould part comprises a first mould part section and a second mould part section arranged in connection to the first mould part section. The second mould part section is configured for being displaced relative to the first mould part section in a lateral direction of the pressing module during forming of the cellulose products in the forming mould. The first mould part section and the second mould part section are configured for applying a forming pressure onto the air-formed cellulose blank structure in the range of 1-100 MPa, preferably in the range of 4-20 MPa, during a single pressing operation upon forming of the cellulose products in the forming mould.
Advantages with these features are that the pressing module is providing an efficient way to produce cellulose products with complex shapes, such as shapes with negative draft angles or undercut sections. The single pressing operation is used for a time and energy saving production of the cellulose products. With a single pressing operation is meant that the cellulose products are formed from the cellulose blank structure in one single pressing step in the forming mould. In the single pressing operation, the first mould part and the second mould part are interacting with each other for establishing the forming pressure and a forming temperature during a single operational engagement step.
According to an embodiment, the first mould part section and the second mould part section are in the overlapping relationship at least partly configured for being positioned in a longitudinally overlapping section between the first mould part and the second mould part. The overlapping relationship with the longitudinally overlapping section is used for establishing a forming cavity between the mould parts for the forming of the cellulose products from the cellulose blank structure.
According to an embodiment, the second mould part section is configured for being displaced relative to the first mould part section in the lateral direction, towards the second mould part from an initial position to a pressing position during forming of the cellulose products. In the initial position, the forming mould can receive the cellulose blank structure between the mould parts and the cellulose blank structure can be displaced into the forming mould. In the pressing position, the cellulose blank structure is formed in the forming mould and the forming pressure can be applied onto the cellulose blank structure by the second mould part section.
According to an embodiment, the second mould part section is configured for being displaced relative to the first mould part section in the lateral direction, away from the second mould part from the pressing position back to the initial position after forming of the cellulose products. With this configuration, the forming mould could be used again for another product forming cycle.
According to an embodiment, the second mould part section comprises a pressing surface configured for pressing the air-formed cellulose blank structure in the lateral direction towards the second mould part during forming of the cellulose products. The pressing surface is used for pressing one or more sections of the cellulose blank structure towards the second mould part in the lateral direction during forming of the cellulose products from the cellulose blank structure in the forming mould. The pressing surface could further be used for pressing one or more sections of the cellulose blank structure towards the second mould part in other suitable directions depending on the configuration of the pressing surface and the second mould part.
According to an embodiment, the second mould part comprises a forming structure configured for interacting with the pressing surface. The pressing surface is configured for pressing the air-formed cellulose blank structure in the lateral direction towards the forming structure during forming of the cellulose products. The forming structure is configured for interacting with the pressing surface, and the pressing surface is pressing the air-formed cellulose blank structure in the lateral direction towards the forming structure in the second mould part during forming of the cellulose products. The forming structure is arranged with a shape that is corresponding to a desired shape of a part or section of the cellulose products.
According to an embodiment, the forming structure is arranged as a recess in the second mould part and the pressing surface is configured for pressing the air-formed cellulose blank structure into the recess during forming of the cellulose products. The pressing surface and the recess are used for an efficient forming of the complex shape of the cellulose product. The pressing surface is pressing the air-formed cellulose blank structure into the recess during forming of the cellulose products. The recess could for example form an undercut section of the second mould part with a negative draft angle. The forming structure may extend along the second mould part as a single continuous recess, or a plurality of recesses may be arranged along the second mould part. In a further alternative, the forming structure may be arranged as a recess having a spiral shape that is forming a threaded structure in the cellulose product.
According to an embodiment, the first mould part further comprises a base structure arranged in connection to the first mould part section and the second mould part section. The first mould part section and the base structure are movably arranged in the longitudinal direction relative to each other, and upon movement of the first mould part section and the base structure relative to each other, the second mould part section is configured for being displaced in the lateral direction. The relative movement between the first mould part section and the base structure could thus be used for displacing the second mould part section in the lateral direction, for an efficient forming process.
According to an embodiment, the second mould part section is arranged as a deformation element. During the forming of the cellulose products, the deformation element is deformed to exert the forming pressure on the cellulose blank structure in the forming mould. Through the deformation of the deformation element, an even pressure distribution is achieved even if the cellulose products are having complex three-dimensional shapes, such as shapes with a recessed undercut section having a negative draft angle, or if the cellulose blank structure is having a varied thickness. To exert a required forming pressure on the cellulose blank structure, the deformation element is made of a material that can be deformed when a force or pressure is applied, and the deformation element is suitably made of an elastic material capable of recovering size and shape after deformation.
The second mould part section may thus be arranged as a deformable deformation element, i.e. a deformation element that is configured to elastically deform upon exertion of a compression force on the second mould part.
The compression force acting on the second mould part section may for example be generated by moving the base structure towards the first mould part section and thereby squeezing the second mould part section, which is located between the base structure and the first mould part section. The squeezing of the second mould part section results in that the second mould part section elastically deforms and becomes partly displaced in the lateral direction towards the second mould part, and thereby enabling compression forming of the air-formed cellulose blank structure.
According to an embodiment, the second mould part section is arranged as one or more displaceable stiff mould elements. The stiff mould elements are providing an alternative solution to the deformation elements.
The disclosure further concerns a method for forming cellulose products from an air-formed cellulose blank structure in a pressing module. The pressing module comprises a forming mould with a first mould part and a second mould part configured for interacting with each other for forming the cellulose products from the air-formed cellulose blank structure in the forming mould. The first mould part and/or the second mould part are movably arranged relative to each other in a pressing direction parallel to a longitudinal direction of the pressing module. The first mould part comprises a first mould part section and a second mould part section arranged in connection to the first mould part section. In a single pressing operation, the method comprises the steps: providing the air-formed cellulose blank structure and arranging the air-formed cellulose blank structure between the first mould part and the second mould part; displacing the first mould part and/or the second mould part into an at least partly overlapping relationship in the longitudinal direction, where in the overlapping relationship the first mould part section and the second mould part section are at least partly positioned in a longitudinally overlapping section between the first mould part and the second mould part; displacing the second mould part section relative to the first mould part section in a lateral direction of the pressing module; and applying a forming pressure by the first mould part section and the second mould part section onto the air-formed cellulose blank structure in the range of 1-100 MPa, preferably in the range of 4-20 MPa, for forming the cellulose products in the forming mould.
Advantages with these features are that the method is providing an efficient way to produce cellulose products with complex shapes or where specific parts or sections of the cellulose products are having complex shapes, such as shapes with negative draft angles or undercut sections. The single pressing operation is used for a time and energy saving production of the cellulose products. With a single pressing operation is meant that the cellulose products are formed from the cellulose blank structure in one single pressing step in the forming mould. In the single pressing operation, the first mould part and the second mould part are interacting with each other for establishing the forming pressure and a forming temperature during a single operational engagement step. The overlapping relationship is used for establishing a forming cavity between the mould parts for the forming of the cellulose products from the cellulose blank structure.
According to an embodiment, the method further comprises the step: applying a forming temperature onto the air-formed cellulose blank structure when the first mould part and the second mould part are displaced into the at least partly overlapping relationship in the longitudinal direction, wherein the forming temperature is in the range of 100-300° C., preferably in the range of 100-200° C. The forming temperature is used together with the forming pressure for an efficient forming of the cellulose blank structure in the single pressing operation.
According to an embodiment, the method further comprises the step: establishing the forming pressure onto the air-formed cellulose blank structure between the first mould part section and the second mould part and between the second mould part section and the second mould part. With this step, at least the first mould part section and the second mould part section are used for exerting the forming pressure onto the cellulose blank structure during the forming of the cellulose products, for an efficient forming of products having complex shapes.
According to an embodiment, the method further comprises the step: displacing the second mould part section relative to the first mould part section in the lateral direction, towards the second mould part from an initial position to a pressing position during forming of the cellulose products.
According to an embodiment, the method further comprises the step: displacing the second mould part section relative to the first mould part section in the lateral direction, away from the second mould part from the pressing position back to the initial position after forming of the cellulose products.
According to an embodiment, the second mould part section comprises a pressing surface. The method further comprises the step: pressing the air-formed cellulose blank structure by the pressing surface in the lateral direction towards the second mould part during forming of the cellulose products. The pressing surface is pressing one or more sections of the cellulose blank structure towards the second mould part in the lateral direction during forming of the cellulose products from the cellulose blank structure in the forming mould. The pressing surface could further be pressing one or more sections of the cellulose blank structure towards the second mould part in other suitable directions depending on the configuration of the pressing surface and the second mould part.
According to an embodiment, the second mould part comprises a forming structure configured for interacting with the pressing surface. The method further comprises the step: pressing the air-formed cellulose blank structure by the pressing surface in the lateral direction towards the forming structure during forming of the cellulose products.
The forming structure is interacting with the pressing surface during forming of the cellulose products, and the pressing surface is pressing the air-formed cellulose blank structure in the lateral direction towards the forming structure in the second mould part. The forming structure is arranged with a shape that is corresponding to a desired shape of a part or section of the cellulose products.
According to an embodiment, the forming structure is arranged as a recess in the second mould part. The method further comprises the step: pressing the air-formed cellulose blank structure by the pressing surface into the recess during forming of the cellulose products. The pressing surface and the recess are used for an efficient forming of the complex shape of the cellulose product. The recess could for example form an undercut section of the second mould part with a negative draft angle. The forming structure may extend along the second mould part as a single continuous recess, or a plurality of recesses may be arranged along the second mould part. In a further alternative, the forming structure may be arranged as a recess having a spiral shape that is forming a threaded structure in the cellulose product.
According to an embodiment, the first mould part further comprises a base structure arranged in connection to the first mould part section and the second mould part section. The first mould part section and the base structure are movably arranged in the longitudinal direction relative to each other. The method further comprises the steps: displacing the first mould part section and the base structure relative to each other in the longitudinal direction, and displacing the second mould part section in the lateral direction upon movement of the first mould part section and the base structure relative to each other. The relative movement between the first mould part section and the base structure could thus be used for displacing the second mould part section in the lateral direction, for an efficient forming process.
According to an embodiment, the second mould part section is arranged as a deformation element. The method further comprises the step: displacing the second mould part section relative to the first mould part section in the lateral direction through deformation of the deformation element. During the forming of the cellulose products, the deformation element is deformed to efficiently exert the forming pressure on the cellulose blank structure in the forming mould. Through the deformation of the deformation element, an even pressure distribution is achieved even if the cellulose products are having complex three-dimensional shapes, such as shapes with recessed undercut section having a negative draft angle, or if the cellulose blank structure is having a varied thickness.
According to an embodiment, the second mould part section is arranged as one or more stiff mould elements. The method further comprises the step: displacing the one or more stiff mould elements relative to the first mould part section in the lateral direction. The stiff mould elements are providing an alternative solution to the deformation elements.
The stiff mould elements may be displaced with a suitable actuator, such as a mechanical, hydraulic, pneumatic, or electric actuator. A combination of different actuators may also be used.
The first mould part section and the base structure are in an embodiment movably arranged in the longitudinal direction relative to each other. Upon movement of the first mould part section and the base structure relative to each other, the one or more displaceable stiff mould elements constituting the second mould part section are configured for being displaced in the lateral direction. The first mould part may for example be arranged with one or more actuators for movement of the one or more displaceable stiff mould elements, where the relative movement between the first mould part section and the base structure in the longitudinal direction is used by the actuators for the lateral displacement of the one or more displaceable stiff mould elements. Alternatively, the actuators comprise actuating means that is displacing the one or more displaceable stiff mould elements without impact from the relative movement between the first mould part section and the base structure.
The one or more actuators displacing the stiff mould elements are in an embodiment connected to the first mould part section and/or second mould part section and configured to at least partly displace the stiff mould elements in the lateral direction by a linear movement and/or a rotating movement upon the relative motion between the first mould part section and the base structure in the longitudinal direction. The linear movement of the stiff mould elements refers to a movement induced by the relative motion between the first mould part section and the base structure, where the stiff mould elements are extended laterally along a line at an angle to the pressing direction and in a direction towards the cellulose blank structure in the forming mould.
The stiff mould elements are connected to the one or more actuators such that they follow the movement of the one or more actuators. According to an embodiment, one or more stiff mould elements are connected to one or more actuators such that one or more stiff mould elements apply the forming pressure onto the cellulose blank structure. The rotating movement of the stiff mould elements refers to a movement induced by the relative motion between the first mould part section and the base structure, where the stiff mould elements are extended laterally by the one or more actuators with a spiral-like movement in a direction at an angle to the pressing direction and towards the cellulose blank structure. The rotating movement allows, for example, that a plurality of stiff mould elements connected to the one or more actuators can be displaced in the spiral-like movement, such that the stiff mould elements form an extended continuous shape when pressing against the cellulose blank structure, and where the stiff mould elements form a discontinuous and overlapping shape with less extent in the lateral direction compared to the extended continuous shape when the first mould part section and the base structure are in relative motion.
The disclosure will be described in detail in the following, with reference to the attached drawings, in which
Various aspects of the disclosure will hereinafter be described in conjunction with the appended drawings to illustrate and not to limit the disclosure, wherein like designations denote like elements, and variations of the described aspects are not restricted to the specifically shown embodiments, but are applicable on other variations of the disclosure.
The cellulose products 1 are dry-formed from the air-formed cellulose blank structure 2 in the pressing module PM. With an air-formed cellulose blank structure 2 is meant an essentially air-formed fibrous web structure produced from cellulose fibres. The cellulose fibres may originate from a suitable cellulose raw material, such as a pulp material. Suitable pulp materials are for example fluff pulp, paper structures, or other cellulose fibre containing structures. The cellulose fibres may also be extracted from agricultural waste materials, for example wheat straws, fruit and vegetable peels, bagasse, etc. With air-forming of the cellulose blank structure 2 is meant the formation of a cellulose blank structure in a dry forming process in which the cellulose fibres are air-formed to produce the cellulose blank structure 2. When forming the cellulose blank structure 2 in the air-forming process, the cellulose fibres are carried and formed to the fibre blank structure 2 by air as carrying medium. This is different from a normal papermaking process or a traditional wet-forming process, where water is used as carrying medium for the cellulose fibres when forming the paper or fibre structure. In the air-forming process, small amounts of water or other substances may if desired be added to the cellulose fibres in order to change the properties of the cellulose products, but air is still used as carrying medium in the forming process. The cellulose blank structure 2 may, if suitable have a dryness that is mainly corresponding to the ambient humidity in the atmosphere surrounding the air-formed cellulose blank structure 2. As an alternative, the dryness of the cellulose blank structure 2 can be controlled in order to have a suitable dryness level when forming the cellulose products 1.
The air-formed cellulose blank structure 2 may be formed of cellulose fibres in a conventional air-forming process or in a cellulose blank air-forming module. For example, the cellulose blank structure 2 may have a composition where the fibres are of the same origin or alternatively contain a mix of two or more types of cellulose fibres, depending on the desired properties of the cellulose products 1. The cellulose fibres used in the cellulose blank structure 2 are during the forming process of the cellulose products 1 strongly bonded to each other with hydrogen bonds, due to applied forming pressure and forming temperature together with adequate moist content in the cellulose blank structure 2. The cellulose fibres may be mixed with other substances or compounds to a certain amount as will be further described below. With cellulose fibres is meant any type of cellulose fibres, such as natural cellulose fibres or manufactured cellulose fibres. The cellulose blank structure 2 may specifically comprise at least 95% cellulose fibres, or more specifically at least 99% cellulose fibres.
The air-formed cellulose blank structure 2 may have a single-layer or a multi-layer configuration. A cellulose blank structure 2 having a single-layer configuration is referring to a structure that is formed of one layer containing cellulose fibres. A cellulose blank structure 2 having a multi-layer configuration is referring to a structure that is formed of two or more layers comprising cellulose fibres, where the layers may have the same or different compositions or configurations.
The cellulose blank structure 2 may comprise one or more additional cellulose layers comprising cellulose fibres, where an additional cellulose layer for example is arranged as a carrying layer for one or more other layers of the cellulose blank structure 2. The one or more additional cellulose layers may act as reinforcement layers having a higher tensile strength than other layers of the cellulose blank structure 2. This is useful when one or more air-formed layers of the cellulose blank structure 2 have compositions with low tensile strength in order to avoid that the cellulose blank structure 2 will break during the forming of the cellulose products 1. The one or more additional cellulose layers with higher tensile strength act in this way as a supporting structure for other layers of the cellulose blank structure 2. The one or more additional cellulose layers may be of a different composition than the rest of the cellulose blank structure 2, such as for example a tissue layer containing cellulose fibres, an airlaid structure comprising cellulose fibres, or other suitable layer structures. It is thus not necessary that the one or more additional cellulose layers are air-formed. Other suitable additional layers may also be used such as for example silicone coated structures or bio-based films.
The one or more air-formed layers of the cellulose blank structure 2 are fluffy and airy structures, where the cellulose fibres forming the structures are arranged relatively loosely in relation to each other. The fluffy cellulose blank structures 2 are used for an efficient dry-forming of the cellulose products 1, allowing the cellulose fibres to form the cellulose products 1 in an efficient way during the dry-forming process in the pressing module PM.
The pressing module PM comprises one or more forming moulds 3, and the one or more forming moulds 3 are configured for dry-forming the cellulose products 1 from the cellulose blank structure 2. The pressing module PM may be arranged with only one forming mould 3 in a single-cavity configuration, or alternatively with two or more forming moulds in a multi-cavity configuration. A single-cavity configuration pressing module thus comprises only one forming mould 3 with a first mould part 3a and a cooperating second mould part 3b. A multi-cavity configuration pressing module comprises two or more forming moulds 3, each having cooperating first mould parts 3a and second mould parts 3b.
In the embodiment illustrated in
The pressing module PM can for example be constructed so that the first mould part 3a or the second mould part 3b is movable and arranged to move towards the other mould part during the dry-forming process, where the other mould part is stationary or non-movably arranged. In the embodiment illustrated in
As indicated in
The cellulose products 1 are dry-formed from the cellulose blank structure 2 in the forming mould 3 by applying the forming pressure PF and a forming temperature TF onto the air-formed cellulose blank structure 2. The cellulose blank structure 2 is heated to a forming temperature TF in the range of 100-300° C., preferably in the range of 100-200° C., and pressed with a forming pressure PF in the range of 1-100 MPa, preferably in the range of 4-20 MPa. The first mould part 3a is arranged for forming the cellulose products 1 through interaction with the corresponding second mould part 3b. During dry-forming of the cellulose products 1, the cellulose blank structure 2 is arranged in the forming mould 3, between the first mould part 3a and the second mould part 3b, and exerted to the forming pressure PF in the range of 1-100 MPa, preferably in the range of 4-20 MPa, and the forming temperature TF in the range of 100-300° C., preferably in the range of 100-200° C. When dry-forming the cellulose products 1, hydrogen bonds are formed between the cellulose fibres in the cellulose blank structure 2 arranged between the first mould part 3a and the second mould part 3b, due to the applied forming pressure PF and forming temperature TF together with adequate moist content in the cellulose blank structure 2. The temperature and pressure levels are for example measured in the cellulose blank structure 2 during the dry-forming process with suitable sensors arranged in or in connection to the cellulose fibres in the cellulose blank structure 2. The cellulose blank structure 2 is typically containing less than 45 weight percent water when formed in the forming mould 3.
A cellulose product forming cycle is schematically illustrated in
The cellulose blank structure 2 may be arranged into the forming mould 3 in any suitable way, and as an example, the cellulose blank structure 2 may be fed with a suitable feeding device, which is transporting the cellulose blank structure 2 to the forming mould 3 in the feeding direction DF. The feeding device could for example be a conveyor belt, a forming wire unit, an industrial robot, or any other suitable manufacturing equipment. The transportation speed may differ depending on the types of cellulose products 1 produced, and is chosen to match the forming speed in the forming mould 3.
An embodiment of the forming mould 3 is illustrated more in detail in
The first mould part 3a further comprises a base structure 5 arranged in connection to the first mould part section 4a and the second mould part section 4b. The first mould part section 4a and the base structure 5 are movably arranged relative to each other in the pressing direction DP. Upon movement of the first mould part section 4a relative to the base structure 5, the second mould part section 4b is displaced in the lateral direction DLA, as understood from
The second mould part section 4b is in this embodiment arranged as a deformation element. The second mould part section 4b formed by the deformation element comprises a pressing surface 6 configured for pressing the air-formed cellulose blank structure 2 in the lateral direction DLA towards the second mould part 3b during forming of the cellulose products 1, as illustrated in
The second mould part section 4b is typically arranged as a deformable deformation element. In other words, the second mould part section 4b is configured to deform, in particular elastically deform, upon applying a compression force on the second mould part 4b in the longitudinal direction DLO by means of movement of the first mould part section 4a relative to the base structure 5 in the longitudinal direction DLO.
The deformation element forming the second mould part section 4b in the embodiment illustrated in
The deformation element forming the second mould part section 4b is arranged between a base structure surface 8 of the base structure 5 and a first mould part section surface 9 of the first mould part section 4a. The base structure surface 8 and first mould part section surface 9 have an essentially horizontal extension, i.e. the surfaces 8, 9 are extending essentially perpendicular to the longitudinal direction DLO. Having the deformation element arranged between essentially horizontal surfaces 8, 9 enables a compact shape of the deformation element, and thus a larger ratio of metal surface of the first mould part 3a being available for press forming of the cellulose blank structure 2. As a result, a greater part of the cellulose blank structure 2 may be press formed between two metal surfaces of the first and second mould parts 3a, 3b. This is generally desirable because press forming of a cellulose blank structure 2 between two metal surfaces typically results in a better surface quality of the finished product, compared with press forming between an elastic element and a metal surface. Consequently, the technical effect of the deformation element arranged between essentially horizontal surfaces 8, 9 is a cellulose product 1 with a greater degree of high quality surface finish, while at the same time using an elastic deformation element to form complex shapes.
With an elastic deformation element, there is thus no need for a base structure surface 8 and a first mould part section surface 9 that are inclined, curved or having other complex shapes to provide lateral movement of the deformation element. Instead, the material characteristics of the deformation element itself ensures that the deformation element deforms in a desired way during pressing.
In some example embodiments, a certain degree of inclination of one or both of the base structure surface 8 and a first mould part section surface 9 can be implemented depending on the circumstances.
For example, in one example embodiment, a first inclination angle (not shown) of the base structure surface 8 and a second inclination angle (not shown) of the first mould part section surface 9 is between +10° and −10° relative a plane extending perpendicular to the longitudinal direction DLO.
During the forming of the cellulose products 1, the deformation element is deformed to exert the forming pressure PF on the cellulose blank structure 2 in the forming mould 3, and through deformation of the deformation element, an even pressure distribution is achieved even if the cellulose products are having complex three-dimensional shapes, such as the shape established by the forming structure 7 with a recessed undercut section having a negative draft angle αNEG, or if the cellulose blank structure 2 is having a varied thickness. To exert a required forming pressure PF on the cellulose blank structure 2, the deformation element is made of a material that can be deformed when a force or pressure is applied, and the deformation element is suitably made of an elastic material capable of recovering size and shape after deformation. The deformation element may further be made of a material with suitable properties that is withstanding the high forming pressure PF and forming temperature TF levels used in the forming mould 3 when forming the cellulose products 1. Certain elastic or deformable materials have fluid-like properties when being exposed to high pressure levels. If the deformation element is made of such a material, an even pressure distribution can be achieved in the forming process, where the pressure exerted onto the cellulose blank structure 2 from the deformation element is equal or essentially equal in all directions. When the deformation element under pressure is in its fluid-like state, a uniform fluid-like pressure distribution is achieved. The forming pressure PF is with such a material thus applied to the cellulose blank structure 2 from all directions, and the deformation element may exert an isostatic forming pressure on the cellulose blank structure 2 during the dry-forming of the cellulose products 1.
The deformation element may be made of a suitable structure of elastomeric material or materials, and as an example, the deformation element may be made of a massive structure or an essentially massive structure of silicone rubber, polyurethane, polychloroprene, or rubber with a hardness in the range 20-90 Shore A, e.g. be a massive deformation element. Other materials for the deformation element E may for example be suitable gel materials, liquid crystal elastomers, and MR fluids. Instead of using a single deformation element structure, a plurality of deformation element structures may be used.
In some example embodiments, the deformation element essentially retains its volume during pressing and only its shape is changed to ensure that the forming pressure PF is applied to the cellulose blank structure.
With massive deformation element is meant a flexible structure, which has a similar ability to exert the forming pressure PF on the cellulose blank structure 2, in the same way as the deformation element described in the embodiments above, but with a greater elastic deformation zone compared to thinner membrane structures. The massive deformation element may be constructed with a thick membrane structure or even be made of a homogenous body of a flexible material. The flexible material may have properties that will make the material float out between the forming mould parts 3a and 3b when the forming pressure PF is applied.
In a further alternative non-illustrated embodiment, the massive deformation element may have a varied thickness, where the massive deformation element is for example shaped or casted into a structure with a varied thickness. The thinner and thicker areas of the massive deformation element with varied thickness may compensate for areas in the forming mould parts 3a, 3b which need smaller or bigger deformation of the membrane in order to equalize or even out the pressure exerted on the cellulose blank structure 2. By using a massive deformation element structure, the forming mould 3 can be made cheaper and simpler in construction.
The massive deformation element is constructed so that when the pressure is applied from the forming mould parts 3a and 3b, the massive deformation element deforms in order to exert the forming pressure PF on the cellulose blank structure. The massive deformation element may be made of a material with suitable properties as mentioned above. Other suitable materials or combinations of materials with elastomeric properties may also be used. Due to the flexible properties of the massive deformation element, the massive deformation element exerts an even pressure on the cellulose blank structure 2.
A further advantage with an elastic deformation element is that it will return to its original position or shape after a compression event automatically due to the inherent characteristic of the elastic deformation element.
As shown in
Depending on the design of the forming mould 3, the base structure 5 may also apply the forming pressure PF onto a part or section of the air-formed cellulose blank structure 2 in the range of 1-100 MPa, preferably in the range of 4-20 MPa, during the single pressing operation OSP. In the illustrated embodiment, the upper part of the cellulose blank 2 is formed between the base structure 5 and the second mould part, as shown in
With a single pressing operation OSP is meant that the cellulose product 1 is formed from the cellulose blank structure 2 in one single pressing step in the forming mould 3 of the pressing module PM. In the single pressing operation OSP, the first mould part 3a and the second mould part 3b are interacting with each other for establishing the forming pressure PF and the forming temperature TF during a single operational engagement step. Thus, in the single pressing operation OSP, the forming pressure PF and the forming temperature TF are not applied to the cellulose blank structure in two or more repeated pressing operations.
The first mould part section 4a and the second mould part section 4b are in the overlapping relationship at least partly configured for being positioned in the longitudinally overlapping section SOL between the first mould part 3a and the second mould part 3b. During the single pressing operation OSP, the second mould part section 4b is displaced relative to the first mould part section 4a in the lateral direction DLA towards the second mould part 3b from an initial position PI to a pressing position PP during forming of the cellulose products 1. After the forming of the cellulose products 1 in the single pressing operation OSP, the second mould part section 4b is displaced relative to the first mould part section 4a in the lateral direction DLA away from the second mould part 3b from the pressing position PP back to the initial position PI.
To form the cellulose products 1 from the air-formed cellulose blank structure 2 in a single pressing operation OSP, the air-formed cellulose blank structure 2 is provided from a suitable source and thereafter arranged between the first mould part 3a and the second mould part 3b, as shown in
Upon further movement of the first mould part 3a towards the second mould part 3b, the base structure 5 is moved in the pressing direction DP into the position shown in
In the embodiment illustrated in
An alternative embodiment of the forming mould 3 is illustrated more in detail in
The first mould part 3a further comprises a base structure 5 arranged in connection to the first mould part section 4a and the second mould part section 4b. The first mould part section 4a and the base structure 5 are movably arranged relative to each other in the pressing direction DP. Upon movement of the first mould part section 4a and the base structure 5 relative to each other, the second mould part section 4b is displaced in the lateral direction DLA, as understood from
The second mould part section 4b is in this embodiment arranged as a deformation element. The second mould part section 4b formed by the deformation element comprises a pressing surface 6 configured for pressing the air-formed cellulose blank structure 2 in the lateral direction DLA towards the second mould part 3b during forming of the cellulose products 1, as illustrated in
The deformation element forming the second mould part section 4b in the embodiment illustrated in
The deformation element is configured for exerting the forming pressure PF on the cellulose blank structure 2 during forming of the cellulose products 1. The deformation element may be attached with suitable attachment means to the first mould part section 4a and the base structure 5, such as for example glue or mechanical fastening members. Alternatively, the deformation element is positioned between the first mould part section 4a and the base structure 5 without any attachment means and instead held in position through the configuration of the first mould part section 4a and the base structure 5, as understood from the figures.
During the forming of the cellulose products 1, the deformation element is deformed to exert the forming pressure PF on the cellulose blank structure 2 in the forming mould 3, and through deformation of the deformation element, an even pressure distribution is achieved even if the cellulose products are having complex three-dimensional shapes, such as the shape established by the forming structure 7 with a recessed undercut section having a negative draft angle αNEG, or if the cellulose blank structure 2 is having a varied thickness. The deformation element may be made of the materials and have the configurations and properties described above in connection to the embodiment illustrated in
As shown in
Depending on the design of the forming mould 3, the base structure 5 may also apply the forming pressure PF onto a part or section of the air-formed cellulose blank structure 2 in the range of 1-100 MPa, preferably in the range of 4-20 MPa, during the single pressing operation OSP. In the illustrated embodiment, the upper part of the cellulose blank 2 is formed between the base structure 5 and the second mould part 3b, as shown in
With a single pressing operation OSP is meant that the cellulose product 1 is formed from the cellulose blank structure 2 in one single pressing step in the forming mould 3 of the pressing module PM. In the single pressing operation OSP the first mould part 3a and the second mould part 3b are interacting with each other for establishing the forming pressure PF and the forming temperature TF during a single operational engagement step. Thus, in the single pressing operation OSP, the forming pressure PF and the forming temperature TF are not applied to the cellulose blank structure in two or more repeated pressing operations.
The first mould part section 4a and the second mould part section 4b are in the overlapping relationship at least partly configured for being positioned in the longitudinally overlapping section SOL between the first mould part 3a and the second mould part 3b. During the single pressing operation OSP, the second mould part section 4b is displaced relative to the first mould part section 4a in the lateral direction DLA towards the second mould part 3b from an initial position PI to a pressing position PP during forming of the cellulose products 1. After the forming of the cellulose products 1 in the single pressing operation OSP, the second mould part section 4b is displaced relative to the first mould part section 4a in the lateral direction DLA away from the second mould part 3b from the pressing position PP back to the initial position PI.
To form the cellulose products 1 from the air-formed cellulose blank structure 2 in a single pressing operation OSP, the air-formed cellulose blank structure 2 is provided from a suitable source and thereafter arranged between the first mould part 3a and the second mould part 3b, as shown in
Upon further movement of the second mould part 3b in the pressing direction DP towards the first mould part 3a, the base structure 5 is moved in the pressing direction DP into the position shown in
In the embodiment illustrated in
A further embodiment of the forming mould 3 is illustrated more in detail in
The second mould part section 4b is also in this embodiment arranged as a deformation element, as described above, and the second mould part section 4b formed by the deformation element comprises a pressing surface 6 configured for pressing the air-formed cellulose blank structure 2 in the lateral direction DLA towards the second mould part 3b during forming of the cellulose products 1, as illustrated in
During the forming of the cellulose products 1, the deformation element is deformed to exert the forming pressure PF on the cellulose blank structure 2 in the forming mould 3, and through deformation of the deformation element, an even pressure distribution is achieved even if the cellulose products are having complex three-dimensional shapes, such as the shape established by the forming structure 7, or if the cellulose blank structure 2 is having a varied thickness. The deformation element may be made of the materials and have the configurations and properties described above in connection to the embodiment illustrated in
As shown in
With a single pressing operation OSP is meant that the cellulose product 1 is formed from the cellulose blank structure 2 in one single pressing step in the forming mould 3 of the pressing module PM. In the single pressing operation OSP, the first mould part 3a and the second mould part 3b are interacting with each other for establishing the forming pressure PF and the forming temperature TF during a single operational engagement step. Thus, in the single pressing operation OSP, the forming pressure PF and the forming temperature TF are not applied to the cellulose blank structure in two or more repeated pressing operations.
The first mould part section 4a and the second mould part section 4b are in the overlapping relationship at least partly configured for being positioned in the longitudinally overlapping section SOL between the first mould part 3a and the second mould part 3b. During the single pressing operation OSP, the second mould part section 4b is displaced relative to the first mould part section 4a in the lateral direction DLA towards the second mould part 3b from an initial position PI to a pressing position PP during forming of the cellulose products 1. After the forming of the cellulose products 1 in the single pressing operation OSP, the second mould part section 4b is displaced relative to the first mould part section 4a in the lateral direction DLA away from the second mould part 3b from the pressing position PP back to the initial position PI.
To form the cellulose products 1 from the air-formed cellulose blank structure 2 in a single pressing operation OSP, the air-formed cellulose blank structure 2 is provided from a suitable source and thereafter arranged between the first mould part 3a and the second mould part 3b, as shown in
Upon further movement of the first mould part 3a towards the second mould part 3b, the base structure 5 is moved in the pressing direction DP into the position shown in
The air-formed cellulose blank structure 2 is pressed by the pressing surface 6 of the second mould part section 4b in the lateral direction DLA towards the second mould part 3b during forming of the cellulose products 1, and the air-formed cellulose blank structure 2 is thus pressed by the pressing surface 6 in the lateral direction DLA towards the forming structure 7 and into the recess during forming of the cellulose products, as shown in
In the embodiment illustrated in
A further embodiment of the forming mould 3 is illustrated more in detail in
In a further alternative non-illustrated embodiment, the second mould part section is arranged as one or more displaceable stiff mould elements instead of one or more deformation elements. The configuration of the forming mould may be similar to the ones described above, but instead the stiff mould elements are displaced relative to the first mould part section in a lateral direction of the pressing module during forming of the cellulose products in the forming mould. With such a configuration, the first mould part comprises a first mould part section and the second mould part section arranged in connection to the first mould part section. The second mould part section is configured for being displaced relative to the first mould part section in the lateral direction of the pressing module during forming of the cellulose products in the forming mould. The first mould part section and the second mould part section are configured for applying a forming pressure onto the air-formed cellulose blank structure in the range of 1-100 MPa, preferably in the range of 4-20 MPa, during a single pressing operation upon forming of the cellulose products in the forming mould. The first mould part may further comprise a base structure arranged in connection to the first mould part section and the second mould part section. The first mould part section and the base structure are movably arranged in the longitudinal direction relative to each other. Upon movement of the first mould part section and the base structure relative to each other, the one or more displaceable stiff mould elements constituting the second mould part section are configured for being displaced in the lateral direction. The first mould part may for example be arranged with one or more actuators for movement of the one or more displaceable stiff mould elements, where the relative movement between the first mould part section and the base structure in the longitudinal direction is used by the actuators for the lateral displacement of the one or more displaceable stiff mould elements. Alternatively, the actuators comprises actuating means that is displacing the one or more displaceable stiff mould elements without impact from the relative movement between the first mould part section and the base structure.
For the different embodiments, the first mould part section 4a, the base structure 5, and the second mould part 3b, may be made of a stiff mould material, such as for example steel, aluminium or other suitable metals or metallic materials, or alternatively a combination of different suitable materials that also may include combinations of metals, metallic materials, and composite materials.
It should be understood that the pressing module PM with the forming mould 3 may have other designs and constructions compared to the one described in the embodiments above. The forming mould 3 may also for the different embodiments be arranged with a cutting device, where the cellulose products 1 are cut in the forming mould into a desired shape during the forming process. When the cellulose products 1 have been cut from the cellulose material in the forming process, a remaining residual cellulose fibre structure is formed. The residual cellulose fibre structure could be recycled and used again when air-forming new cellulose blank structures 2.
It will be appreciated that the above description is merely exemplary in nature and is not intended to limit the present disclosure, its application or uses. While specific examples have been described in the specification and illustrated in the drawings, it will be understood by those of ordinary skill in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the present disclosure as defined in the claims. Furthermore, modifications may be made to adapt a particular situation or material to the teachings of the present disclosure without departing from the essential scope thereof. Therefore, it is intended that the present disclosure not be limited to the particular examples illustrated by the drawings and described in the specification as the best mode presently contemplated for carrying out the teachings of the present disclosure, but that the scope of the present disclosure will include any embodiments falling within the foregoing description and the appended claims. Reference signs mentioned in the claims should not be seen as limiting the extent of the matter protected by the claims, and their sole function is to make claims easier to understand.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2151541-6 | Dec 2021 | SE | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2022/082345 | 11/17/2022 | WO |