Patent Application
20160221893
The present disclosure related to a process for the preparation of isomers of xylene.
Xylene is monocyclic aromatic compound with two methyl groups attached to the benzene ring. It exists in three isomeric forms: ortho, meta and para-xylene. Mostly, the individual isomers of xylene are separated and consumed in specific end-uses. Ortho-xylene is used primarily in the synthesis of phthalic acid, unsaturated polyester resins, alkyd resins; meta-xylene is key component for the synthesis of isophthalic acid and para-xylene is an important precursor to terephthalic acid and dimethyl terephthalate.
Usually, xylene is synthesized by the Friedel-Crafts alkylation reaction. However, alkylation catalysts such as AlCl3, HF and H2SO4 employed in the Friedel-Crafts alkylation reaction have found to be environmentally hazardous. Therefore, in recent years, molecular sieve catalyst such as zeolites and silico aluminophosphate have attracted attention as alkylation catalysts, typically, due to their higher acidic properties, potential for regeneration and easy of separation from the reaction mixture.
However, use of such acidic alkylation catalysts in alkylation of toluene produces mix-xylenes, containing predominantly meta-xylene and para-xylene with very minor amount of ortho-xylene. While, the alkylation of toluene in the presence of basic alkylation catalyst such as Na—X-zeolite, Na—Y-zeolite, Na-beta-zeolite Na-ZSM-5 zeolite, Cs—X zeolite, Ba zeolite, and Rb—X zeolite predominantly, produces ethyl benzene and styrene due to side chain alkylation reaction.
Therefore, there is need to develop a simple and economic process for the preparation of isomers of xylene, particularly ortho-xylene using the basic alkylation catalyst.
Some of the objects of the present disclosure, which at least one embodiment is able to achieve, are discussed herein below.
It is an object of the present disclosure to provide safe and economic process for the preparation of alkyl aromatic compounds using the basic alkylation catalyst composite.
It is another object of the present disclosure to provide safe and economic process for the preparation of isomers of xylene using the basic alkylation catalyst composite.
It is a further object of the present disclosure to provide a selective process for the preparation of ortho-xylene using the basic alkylation catalyst composite.
Other objects and advantages of the present disclosure will be more apparent from the following description when read in conjunction with the accompanying drawing, which are not intended to limit the scope of the present disclosure.
As used in the present specification, the term ‘molecular sieve’ is used to define class of materials that exhibits selected sorption properties.
A represents XRD for the Sr—X zeolite catalyst composite obtained after refluxing Na X-zeolite with strontium nitrate;
B represents XRD for the Sr—X zeolite catalyst composite obtained after repeating the method step of refluxing Na X-zeolite with strontium nitrate two times; and
C represents XRD for the Sr—X zeolite catalyst composite obtained after repeating the method step of refluxing Na X-zeolite with strontium nitrate three times.
In accordance with one aspect of the present disclosure there is provided a process for the preparation of isomers of xylene; said process comprising the following steps:
Typically, the molecular sieve is at least one zeolite selected from the group consisting of X-zeolite, Y-zeolite, beta-zeolite, ZSM-5 zeolite mordenite, ZSM-48, ZSM-22, ZSM-23, ZSM-57 and MCM-22.
Typically, the molecular sieve is at least one silico aluminophosphate (SAPO) selected from the group consisting of SAPO-5, SAPO-11, SAPO-17, SAPO-18, SAPO-44, SAPO-34 and SAPO-48.
Typically, the metal is at least one selected from the group consisting of group I elements, group II elements, group III elements, lanthanides and transition metals.
Typically, the metal is at least one selected from the group consisting of barium, strontium, magnesium and calcium.
Typically, the ratio of toluene to methanol ranges between 1:1 and 4:1.
Typically, the flow rate of toluene is maintained at a weight hourly space velocity of 1 to 5 per hr. of the activated alkylation catalyst composite.
Typically, the inert gas is at least one selected from the group consisting of nitrogen, argon and helium.
Typically, the flow rate of the inert gas ranges between 5 and 15 per min.
Alkylation of toluene using the acidic alkylation catalyst predominantly produces meta and para isomers of xylene, while the basic alkylation catalyst produces ethyl benzene and styrene. Therefore, with the view of increasing the yield of ortho-xylene, the inventors of the present disclosure have conducted several experiments and trials using number of alkylation catalysts. The inventors surprisingly found that the basic alkylation catalyst composite comprising molecular sieve loaded with at least one metal ion can selectively be used for the preparation of the isomers of xylene typically, ortho-xylene. Accordingly, the inventors of the present disclosure have developed a novel process for alkylation of toluene using the basic alkylation catalyst composite.
In accordance with one aspect of the present disclosure there is provided a process for the preparation of isomers of xylene.
In the initial step, the alkylation catalyst composite comprising a molecular sieve loaded with at least one metal ion is activated at a temperature of 450 to 650° C. for a time period of 30 min to 2 hrs. in a reactor to obtain an activated alkylation catalyst composite. The temperature for activating the alkylation catalyst composite is attained by heating the reactor at a rate of 4 to 10° C. per minute.
In accordance with one embodiment of the present disclosure the molecular sieve may be zeolite selected from the group consisting of X-zeolite, Y-zeolite, beta-zeolite, ZSM-5 zeolite mordenite, ZSM-48, ZSM-22, ZSM-23, ZSM-57, MCM-22 and mixtures thereof.
In accordance with another embodiment of the present disclosure the molecular sieve may be silico aluminophosphate (SAPO) selected from the group consisting of SAPO-5, SAPO-11, SAPO-17, SAPO-18, SAPO-44, SAPO-34, SAPO-48 and combinations thereof.
Typically, the metal loaded on molecular sieve is at least one selected from the group consisting of group I elements, group II elements, group III elements, lanthanides and transition metals. Typically, the metal loaded on molecular sieve is at least one selected from the group consisting of barium, strontium, magnesium and calcium.
In the next step, the activated alkylation catalyst composite is contacted with toluene and methanol at a temperature of 300 to 500° C. to obtain a reaction mixture comprising isomers of xylene as ortho-xylene, meta-xylene and para-xylene.
The mass of ortho-xylene present in the reaction mixture is greater the individual mass of para-xylene and meta-xylene.
The ratio of toluene to methanol is maintained in the range of 1:1 to 4:1 and the flow rate of toluene is maintained at a weight hourly space velocity of 1 to 5 per hr. of the activated catalyst. The method step of contacting the activated alkylation catalyst composite with toluene and methanol is carried out in the presence of inert gas selected from the group consisting of nitrogen, argon, helium and combinations thereof. The flow rate of inert gas is maintained in the range of 5 to 15 ml/min.
The present disclosure is further described in light of the following examples which are set forth for illustration purpose only and not to be construed for limiting the scope of the disclosure.
Step 1: Preparation of Na—X Zeolite:
5 gm of zeolite was treated with 20 liter of 0.5 M aqueous solution of sodium nitrate (NaNO3) under reflux for 8 hrs, followed by filtration, washing with water until the filtrate became free from sodium ions, drying at 120° C. for 8 h and calcination at 550° C. for 4 h in air. The ratio of aqueous solution of sodium nitrate to zeolite was maintained as 10:1. The procedure was repeated twice to obtain Na—X zeolites.
Step II—Preparation of an Alkylation Catalyst Composite (Ba—X Zeolite Catalyst Composite) Using Na—X Zeolite:
The Na—X zeolite was treated with 0.5 M of barium acetate solution using the method described in step I to obtain a Ba—X zeolite. In this process the sodium nitrate is replaced with barium acetate.
Step III—Preparation of Isomers of Xylene Using Ba—X Zeolite Catalyst Composite:
2 g of Ba—X zeolites catalyst composite of 0.8 to 1.7 mm mesh size was taken in a quartz micro reactor. Temperature in the reactor was ramped with 8° C./min to 500° C. Catalyst was activated in presence of air for a time period of 1 hr. Then the temperature of the activated catalyst was brought down to 420° C. Feed of Toluene and methanol (4:1) with a weight hourly space velocity (WHSV) (toluene)=2.5 h−1 was fed into pre-heater with a syringe pump and nitrogen was fed with calibrated Rota meter with the flow of 10 ml/min. Products were cooled in condenser maintained at 2° C. and products are collected in gas liquid separator maintained at 5° C. Products were analyzed through gas chromatograph equipped with FID using a carbowax (polar) column of 60 m×0.25 um×0.25 mm.
The Na—X zeolite was treated with 0.5 M of calcium nitrate (CaNO3) solution using the step-I of Example 1 to obtain a Ca—X zeolite. In this process sodium nitrate is replaced with calcium nitrate.
Preparation of Isomers of Xylene Using Ca—X Zeolite Catalyst Composite:
The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process Ba—X zeolites catalyst composite is replaced with Ca—X zeolite catalyst composite
The Na—X zeolite was treated with 0.5 M of Magnesium nitrate (MgNO3) solution using the step-I of Example 1 to obtain a Mg—X zeolite. In this process sodium nitrate is replaced with Magnesium nitrate.
Preparation of Isomers of Xylene Using Mg—X Zeolite Catalyst Composite:
The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process Ba—X zeolite catalyst composite is replaced with Mg—X zeolites catalyst composite.
The Na—X zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO3)2) solution using Step-I of Example 1 to obtain a Sr—X zeolite. In this process sodium nitrate is replaced with Strontium nitrate.
Preparation of Isomers of Xylene Using Sr—X Zeolite Catalyst Composite:
The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process Ba—X zeolite catalyst composite is replaced with Sr—X zeolites catalyst composite.
Step I Preparation Na-Beta Zeolites Catalyst:
5 gm of H-Beta zeolite was treated with 20 ml of 0.5 M aqueous solution of sodium nitrate under reflux for 8 hrs., followed by filtration, washing with water until the filtrate became free from sodium ions, drying at 120° C. for 8 h and calcination at 550° C. for 4 h in air. The ratio of sodium nitrate to zeolite was maintained as 10:1. The procedure was repeated twice to obtain Na-Beta zeolite.
Step II Preparation of an Alkylation Catalyst Composite (Sr-Beta Zeolite Catalyst Composite) Using Na-Beta Zeolites:
The Sr-beta zeolite catalyst was prepared by using the procedure described for the preparation of Na-beta zeolites (Step I). In this process sodium nitrate is replaced with Strontium nitrate (Sr(NO3)2).
Preparation of Isomers of Xylene Using Sr-Beta Zeolite Catalyst Composite:
The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process Ba—X zeolite catalyst composite is replaced with Sr—X beta zeolites catalyst composite.
The Sr-ZSM-5 zeolite was prepared by using the Step-I of the Example 6, in this process H-Beta zeolite is replaced with H-ZSM-5 zeolite.
Preparation of Isomers of Xylene Using Sr-ZSM-5 Zeolite Catalyst Composite:
The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process Ba—X zeolite catalyst composite is replaced with Sr-ZSM-5 zeolites catalyst composite.
The Sr-ZSM-5 zeolite was prepared by using Step I of Example 6, in this process H-Beta zeolite is replaced with H—Y zeolite.
Preparation of Isomers of Xylene Using Sr—Y Zeolite Catalyst Composite:
The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process Ba—X zeolite catalyst composite is replaced with Sr—Y zeolites catalyst composite
The catalytic activity of Sr—X zeolite catalyst composite was compared with the catalytic activity of Mg—X zeolite catalyst composite, Ca—X zeolite catalyst composite and Ba—X zeolite. (shown in
Characterization
XRD Analysis:
Atomic Absorption Spectrometry (AAS):
The percent sodium (Na) exchanged with the metal ions selected from the group consisting of magnesium(Mg), calcium(Ca), strontium(Sr) and barium(Ba) was determined by Atomic Absorption Spectrometry.
The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process Ba—X zeolite catalyst composite is replaced with commercially available Na—X zeolite catalyst.
The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process Ba—X zeolite catalyst composite is replaced with commercially available H-Beta and H-ZSM-5. The amount of the xylene produced by the Sr—X zeolite composite was then compared with amount of the xylene produced using H-Beta and HZSM-5
The embodiments herein and the various features and advantageous details thereof are explained with reference to the non-limiting embodiments in the description. Descriptions of well-known components and processing techniques are omitted so as to not unnecessarily obscure the embodiments herein. The examples used herein are intended merely to facilitate an understanding of ways in which the embodiments herein may be practiced and to further enable those of skill in the art to practice the embodiments herein. Accordingly, the examples should not be construed as limiting the scope of the embodiments herein.
The foregoing description of the specific embodiments will so fully reveal the general nature of the embodiments herein that others can, by applying current knowledge, readily modify and/or adapt for various applications such specific embodiments without departing from the generic concept, and, therefore, such adaptations and modifications should and are intended to be comprehended within the meaning and range of equivalents of the disclosed embodiments. It is to be understood that the phraseology or terminology employed herein is for the purpose of description and not of limitation. Therefore, while the embodiments herein have been described in terms of preferred embodiments, those skilled in the art will recognize that the embodiments herein can be practiced with modification within the spirit and scope of the embodiments as described herein.
Throughout this specification the word “comprise”, or variations such as “comprises” or “comprising”, will be understood to imply the inclusion of a stated element, integer or step, or group of elements, integers or steps, but not the exclusion of any other element, integer or step, or group of elements, integers or steps.
The use of the expression “at least” or “at least one” suggests the use of one or more elements or ingredients or quantities, as the use may be in the embodiment of the invention to achieve one or more of the desired objects or results.
The numerical values given for various physical parameters, dimensions and quantities are only approximate values and it is envisaged that the values higher than the numerical value assigned to the physical parameters, dimensions and quantities fall within the scope of the invention and the claims unless there is a statement in the specification to the contrary.
While certain embodiments of the inventions have been described, these embodiments have been presented by way of example only, and are not intended to limit the scope of the inventions. Variations or modifications in the process or compound or formulation or combination of this invention, within the scope of the invention, may occur to those skilled in the art upon reviewing the disclosure herein. Such variations or modifications are well within the spirit of this invention. The accompanying claims and their equivalents are intended to cover such forms or modifications as would fall within the scope and spirit of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2754/MUM/2013 | Aug 2013 | IN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IN13/00651 | 10/25/2013 | WO | 00 |