Patent Application
20200063593
The present disclosure relates to coating systems that include an abradable ceramic layer.
Components of high-temperature mechanical systems, such as, for example, gas turbine engines, operate in severe environments. For example, the high-pressure turbine blades and vanes exposed to hot gases in commercial aeronautical engines typically experience exterior surface temperatures of about 1000° C., with short-term peaks as high as 1100° C. Example components of high-temperature mechanical systems may include a Ni-based or Co-based super alloy substrate or a ceramic or ceramic matrix composite substrate.
Economic and environmental concerns, e.g., the desire for improved efficiency and reduced emissions, continue to drive the development of advanced gas turbine engines with higher inlet temperatures. Additionally, reducing over-tip leakage between a tip of a gas turbine engine blade and the surrounding blade track, or seal segment, can improve efficiency of a gas turbine engine. Many techniques have been used to reduce over-tip leakage, including labyrinth sealing and active tip clearance control. Static seal segments also may be used to seal between the blade track and rotating gas turbine engine blades using passive tip clearance control.
In some examples, the disclosure describes an article that includes a substrate including a metal or alloy; a bond coat directly on the substrate, wherein the bond coat includes an alloy including aluminum; an intermediate ceramic layer on the bond coat; and an abradable ceramic layer directly on the intermediate ceramic layer. The intermediate ceramic layer includes a stabilized tetragonal prime phase constitution and defines a first porosity. The intermediate layer includes between about 4 wt. % and about 20 wt. % yttria and a balance zirconia or hafnia; or a first mixture including between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia. The abradable ceramic layer includes zirconia or hafnia stabilized in the tetragonal prime phase by a second mixture including between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia. The abradable ceramic layer defines a second porosity, and the second porosity is higher than the first porosity.
In some examples, the disclosure describes a system that includes a system that includes an article and a gas turbine blade including a blade tip. The article includes a substrate including a metal or alloy; a bond coat directly on the substrate, wherein the bond coat includes an alloy including aluminum; an intermediate ceramic layer on the bond coat; and an abradable ceramic layer directly on the intermediate ceramic layer. The substrate is a part of a blade track. The intermediate ceramic layer includes a stabilized tetragonal prime phase constitution and defines a first porosity. The intermediate layer includes between about 4 wt. % and about 20 wt. % yttria and a balance zirconia or hafnia; or a first mixture including between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia. The abradable ceramic layer includes zirconia or hafnia stabilized in the tetragonal prime phase by a second mixture including between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia. The abradable ceramic layer defines a second porosity, and the second porosity is higher than the first porosity. The part of the blade track and the gas turbine blade are configured so the blade tip contacts a portion of the abradable ceramic layer during rotation of the gas turbine blade, and the abradable ceramic layer is configured to be abraded by the contact by the blade tip.
In some examples, the disclosure describes a method that includes forming a bond coat directly on a substrate. The bond coat includes an alloy including aluminum, and the substrate coating includes a metal or alloy. The method also includes thermally spraying an intermediate ceramic layer on the bond coat. The intermediate ceramic layer includes a stabilized tetragonal prime phase constitution and includes between about 4 wt. % and about 20 wt. % yttria and a balance zirconia or hafnia; or a first mixture including between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia. The method also includes thermally spraying an abradable ceramic layer directly on the intermediate ceramic layer. The abradable ceramic layer includes zirconia or hafnia stabilized in the tetragonal prime phase by a second mixture including between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, between about 2 wt. % and about 10 wt. % fugitive material, and a balance zirconia or hafnia.
The details of one or more examples are set forth in the accompanying drawings and the description below. Other features, objects, and advantages of the disclosure will be apparent from the description and drawings, and from the claims.
The disclosure describes articles that include a coating system including an intermediate ceramic layer and an abradable ceramic layer that each include a stabilized tetragonal prime phase constitution. At least the abradable ceramic layer includes between about 5 weight percent (wt. %) and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia. The abradable ceramic layer may have a sintering temperature greater than about 1375° C. (about 2507° F.), which may allow the coating system to be used to higher operating temperatures while maintaining the as-deposited thermal and mechanical properties. This may allow use of less cooling air, resulting in higher gas turbine engine operating efficiency and lower specific fuel consumption (SFC). The stabilized tetragonal prime phase constitution also may result in increased durability, erosion resistance, thermal shock resistance, or combinations thereof.
Further, by using the abradable ceramic layer, the gas turbine engine may omit labyrinth sealing (including shrouded gas turbine engine blades), active tip clearance control, and other more complicated and/or heavy configurations, while still reducing fluid flow around the tip of the gas turbine blade.
In some examples, the intermediate ceramic layer may include a similar or substantially the same composition as the abradable ceramic layer. By including a similar or substantially the same composition, the intermediate ceramic layer and the abradable ceramic layer may have similar coefficients of thermal expansion, which may reduce stress at the interface between the intermediate ceramic layer and the abradable ceramic layer.
The abradable ceramic layer may define a higher porosity and/or larger average pore size than the intermediate ceramic layer. This may enable the intermediate ceramic layer to contribute environmental resistance to the coating system, while enabling the abradable ceramic layer to be abraded in response to contact with a gas turbine engine blade tip. The intermediate ceramic layer and the abradable ceramic layer may be applied using thermal spraying.
Substrate 14 may include a metal or alloy, such as, for example, a superalloy. Superalloys include alloys based on Ni, Co, Ni/Fe, and the like. Superalloys may include other additive elements to alter their mechanical properties, such as toughness, hardness, temperature stability, corrosion resistance, oxidation resistance, and the like, as is well known in the art. For example, a superalloy may include one or more additives or alloying elements such as titanium (Ti), cobalt (Co), aluminum (Al), a rare earth element, or the like. Substrate 14 may include any useful superalloy including, for example, those available from Martin-Marietta Corp., Bethesda, Md., under the trade designation MAR-M247; those available from Cannon-Muskegon Corp., Muskegon, Mich., under the trade designations CMSX-4 and CMSX-10; and the like.
Bond coat 16 is on substrate 14. Bond coat 16 may include an aluminum-containing alloy, such as a MCrAlY alloy (where M is Ni, Co, Fe, or NiCo), a β-NiAl nickel aluminide alloy (either unmodified or modified by Pt, Cr, Hf, Zr, Y, Si, or combinations thereof), a γ-Ni+γ′-Ni3Al nickel aluminide alloy (either unmodified or modified by Pt, Cr, Hf, Zr, Y, Si, or combinations thereof), or the like. In some examples, bond coat 16 may include Pt-modified aluminum-containing alloy.
As used herein, “formed on” and “on” mean a layer or coating that is formed on top of another layer or coating and encompass both a first layer or coating formed immediately adjacent a second layer or coating and a first layer or coating formed on top of a second layer or coating with one or more intermediate layers or coatings present between the first and second layers or coatings. In contrast, “formed directly on” and “directly on” denote a layer or coating that is formed immediately adjacent another layer or coating, i.e., there are no intermediate layers or coatings.
Bond coat 16 may define a thickness between about 76.2 micrometers (about 0.003 inches) and 508 micrometers (0.020 inches), such as between about 127 micrometers (about 0.005 inches) and about 203.2 micrometers (about 0.008 inches). Bond coat 16 provides an aluminum source for formation of an alumina scale on bond coat 16 by oxidation of bond coat 16.
Intermediate ceramic layer 18 is on bond coat 16. Intermediate ceramic layer 18 may include zirconia or hafnia stabilized in a tetragonal prime phase constitution. Intermediate ceramic layer 18 may include zirconia or hafnia and at least one rare earth oxide.
In some examples, intermediate ceramic layer 18 includes zirconia or hafnia stabilized in the tetragonal prime phase constitution by yttria. For example, intermediate ceramic layer 18 may include between about 4 wt. % and about 20 wt. % yttria. In some examples, intermediate ceramic layer 18 may include between about 4 wt. % and about 20 wt. % yttria and a balance zirconia or hafnia. In some examples, intermediate ceramic layer 18 may consist essentially of between about 4 wt. % and about 20 wt. % yttria and a balance zirconia or hafnia. As used herein, to “consist essentially of” means to consist of the listed element(s) or compound(s), while allowing the inclusion of impurities present in small amounts such that the impurities do not substantially affect the properties of the listed element or compound. For example, the purification of many rare earth elements may be difficult, and thus the nominal rare earth element may include small amounts of other rare earth elements. This mixture is intended to be covered by the language “consists essentially of.” In some examples, intermediate ceramic layer 18 may consist essentially of yttria-stabilized zirconia or yttria-stabilized hafnia, which includes about 92 weight percent (wt. %) to about 94 wt. % zirconia or hafnia stabilized by about 6 wt. % to about 8 wt. % yttria.
In some examples, having intermediate ceramic layer 18 consist essentially of zirconia and yttria or hafnia and yttria may improve the thermal cycling resistance (e.g., a long thermal cycling life), and/or adhesion of intermediate ceramic layer 18 to bond coat 14 or an optional scale layer (see
In some examples, rather than including zirconia or hafnia and yttria, intermediate ceramic layer 18 may include or consist essentially of zirconia or hafnia and a mixture of rare earth oxides. For example, intermediate ceramic layer 18 may include a base oxide including zirconia and/or hafnia; a first rare earth oxide including ytterbia; a second rare earth oxide including samaria; and a third rare earth oxide including at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia. In some examples, the third rare earth oxide may include gadolinia such that the intermediate ceramic layer 18 may include zirconia, ytterbia, samaria, and gadolinia on bond coat 16. Intermediate ceramic layer 18 may include predominately (e.g., the main component or a majority) the base oxide zirconia mixed with a minority amounts of ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia.
In some examples, the composition including zirconia, ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia may provide improved thermal insulation and protection to substrate 14 from high temperatures, e.g., high-temperature of the turbine gas compared to other coating compositions or microstructures. For example, during operation of article 10 in a high temperature environment, heat is transferred through coating system 12 through conduction and radiation. The inclusion of one or more rare earth oxides, such as ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia within a layer of predominately zirconia or hafnia may help decrease the thermal conductivity of intermediate ceramic layer 18, e.g., compared to a layer including zirconia or hafnia and yttria. While not wishing to be bound by any specific theory, the inclusion of ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia in intermediate ceramic layer 18 may reduce thermal conductivity through one or more mechanisms, including phonon scattering due to point defects and grain boundaries in the zirconia crystal lattice due to the rare earth oxides, reduction of sintering, and porosity.
The composition of intermediate ceramic layer 18 may be selected to provide a stabilized tetragonal prime (t′) phase constitution. To achieve a stabilized tetragonal prime phase constitution, intermediate ceramic layer 18 may include between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia, and a balance zirconia or hafnia and any impurities present. In some examples, intermediate ceramic layer 18 may consist essentially of between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia. In some examples, intermediate ceramic layer 18 may include or consist essentially of between about 7.0 wt. % and about 8.0 wt. % ytterbia, between about 1.0 wt. % and about 2.0 wt. % samaria, and between about 2.0 wt. % and about 3.0 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia. In some examples, intermediate ceramic layer 18 may include about 7.5 wt. % ytterbia, about 1.5 wt. % samaria, about 2.5 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia and any impurities present. In any of the above example, the at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia may include or consist essentially of gadolinia.
In some examples, the inclusion of ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia in intermediate ceramic layer 18 may also provide intermediate ceramic layer 18 with increased resistance to calcia-magnesia-alumina-silicate (CMAS) degradation compared to yttria-stabilized zirconia, reduced thermal conductivity compared to yttria-stabilized zirconia, reduced sintering at a given temperature compared to yttria-stabilized zirconia, or combinations thereof. In some examples, inermediate ceramic coating 18 including yttria or hafnia, ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia may have a sintering temperature greater than 1375° C. (about 2507° F.), or even greater than 1425° C. (about 2597° F.), which may allow use at higher operating temperatures, reduced use of cooling air, or both. This may increase efficiency and reduce specific fuel consumption (SFC) of a gas turbine engine in which coating system 12 is used.
Intermediate ceramic layer 18 may define relatively low porosity. For example, intermediate ceramic layer 18 may define a porosity of between about 5 vol. % and about 15 vol. %, such as between about 8 vol. % and about 12 vol. %. The size of the pores may be between about 0.5 micrometers and about 5 micrometers, and the pores may be present within or between splats formed by the coating process. The porosity of intermediate ceramic layer 18 may be measured using electron microscopy, optical microscopy, mercury porosimetry, or the like. The porosity in intermediate ceramic layer 18 may be a result of the deposition process used to form intermediate ceramic layer 18. For example, intermediate ceramic layer 18 may be deposited using a thermal spray process, such as air plasma spraying, suspension plasma spraying, high velocity oxy-fuel (HVOF) spraying, or the like. Thermal spray processes may deposit intermediate ceramic layer 18 as a set of softened or melted splats, including internal porosity and pores between adjacent splats. By controlling the deposition process, porosity of intermediate ceramic layer 18 may be controlled to be relatively low, such that intermediate ceramic layer 18 functions as a barrier layer against infiltration of environmental species through intermediate ceramic layer 18 to bond coat 16 and/or substrate 14.
In some examples, intermediate ceramic layer 18 may be a relatively thin layer. For example, first layer 42 may be between about 76.2 micrometers (about 0.003 inches) and about 381 micrometers (about 0.015 inches), such as between about 127 micrometers (about 0.005 inches) and about 203.2 micrometers (about 0.008 inches).
Abradable ceramic layer 20 is directly on intermediate ceramic layer 18. Abradable ceramic layer 20 has higher porosity than intermediate ceramic layer 18, such that abradable ceramic layer 20 abrades upon contact with a rotating component adjacent to coating system 12, such as a gas turbine engine blade.
Abradable ceramic layer 20 may include or consist essentially of zirconia or hafnia and a mixture of rare earth oxides. For example, abradable ceramic layer 20 may include a base oxide including zirconia and/or hafnia; a first rare earth oxide including ytterbia; a second rare earth oxide including samaria; and a third rare earth oxide including at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia. In some examples, the third rare earth oxide may include or consist essentially of gadolinia such that the abradable ceramic layer 20 may include or consist essentially of zirconia, ytterbia, samaria, and gadolinia on intermediate ceramic layer 18. Abradable ceramic layer 20 may include predominately (e.g., the main component or a majority) zirconia or hafnia mixed with a minority amounts of ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia.
In some examples, the composition including zirconia or hafnia, ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia may provide improved thermal insulation and protection to substrate 14 from high temperatures, e.g., high-temperature of the turbine gas compared to other coating compositions or microstructures, as described above with reference to intermediate ceramic layer 18. Additionally, the higher porosity of abradable ceramic layer 20 may reduce thermal conductivity of abradable ceramic layer 20 relative to intermediate ceramic layer 18.
The composition of abradable ceramic layer 20 may be selected to provide a stabilized tetragonal prime (t′) phase constitution. To achieve a stabilized tetragonal prime phase constitution, abradable ceramic layer 20 may include between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia, and a balance zirconia or hafnia and any impurities present. In some examples, abradable ceramic layer 20 may consist essentially of between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia. In some examples, abradable ceramic layer 20 may include or consist essentially of between about 7.0 wt. % and about 8.0 wt. % ytterbia, between about 1.0 wt. % and about 2.0 wt. % samaria, and between about 2.0 wt. % and about 3.0 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia. In some examples, abradable ceramic layer 20 may include about 7.5 wt. % ytterbia, about 1.5 wt. % samaria, about 2.5 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia and any impurities present. In any of the above example, the at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia may include or consist essentially of gadolinia. In some examples, abradable ceramic layer 20 may include a similar or substantially the same composition (including oxides, compositional amounts, or both) as intermediate ceramic layer 18.
In some examples, the inclusion of ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia in abradable ceramic layer 20 may also provide abradable ceramic layer 20 with increased resistance to calcia-magnesia-alumina-silicate (CMAS) degradation compared to yttria-stabilized zirconia, reduced thermal conductivity compared to yttria-stabilized zirconia, reduced sintering at a given temperature compared to yttria-stabilized zirconia, or combinations thereof. In some examples, abradable ceramic layer 20 including yttria or hafnia, ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia may have lower bulk hardness than yttria-stabilized zirconia, which may facilitate abradability of abradable ceramic layer 20. In some examples, abradable ceramic layer 20 including yttria or hafnia, ytterbia, samaria, and at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia may have a sintering temperature greater than 1375° C. (about 2507° F.), or even greater than 1425° C. (about 2597° F.), which may allow use at higher operating temperatures, reduced use of cooling air, or both. This may increase efficiency and reduce specific fuel consumption (SFC) of a gas turbine engine in which coating system 12 is used.
Abradable ceramic layer 20 may define relatively higher porosity that intermediate ceramic layer 18. For example, abradable ceramic layer 20 may define a porosity of between about 10 vol. % and about 40 vol. %, such as between about 15 vol. % and about 35 vol. %, or between about 20 vol. % and about 30 vol. %. The porosity of abradable ceramic layer 20 may be measured using electron microscopy, optical microscopy, mercury porosimetry, or the like. The porosity in abradable ceramic layer 20 may be a result of the deposition process used to form abradable ceramic layer 20. For example, abradable ceramic layer 20 may be deposited using a thermal spray process, such as air plasma spraying, suspension plasma spraying, high velocity oxy-fuel (HVOF) spraying, or the like. Thermal spray processes may deposit intermediate ceramic layer 18 as a set of softened or melted splats, including internal porosity and pores between adjacent splats. By controlling the deposition process, porosity of abradable ceramic layer 20 may be controlled to be relatively higher, such that abradable ceramic layer 20 abrades in response to contact by a rotating component.
In some examples, abradable ceramic layer 20 may be deposited in combination with a fugitive material. The fugitive material may include any material that may be removed, e.g., by heating, after deposition of abradable ceramic layer 20. In some examples, the fugitive material may include graphite, hexagonal boron nitride, or a polymer such as a polyester. The fugitive material then is melted or burned off in a post-deposition heat treatment, or during operation of the gas turbine engine, to form pores in abradable ceramic layer 20. In some examples, the porosity of abradable ceramic layer 20 can additionally or alternatively be created and/or controlled by plasma spraying the coating material using a co-spray process technique in which the coating material and coating material additive are fed into the plasma stream with two radial powder feed injection ports.
Abradable ceramic layer 20 may define a thickness between about 254 micrometers (about 0.01 inches) and about 2032 micrometers (about 0.08 inches). For example, abradable ceramic layer 20 may define a thickness between about 508 micrometers (about 0.02 inches) and about 1016 micrometers (about 0.04 inches).
In some examples, a coating system may include an oxide scale layer between the bond coat and the intermediate ceramic layer.
Oxide scale 34 may be formed by thermal oxidation of bond coat 16, and facilitates adhesion between bond coat 14 and intermediate ceramic layer 18. Oxide scale 34 may include one or more oxides formed by oxidation of bond coat 14. For example, oxide scale 34 may include alumina, chromia, silica, or combinations thereof. In some examples, oxide scale 34 include a majority alumina.
Articles 10 and 30 of
The contact between blade tip 44 and a portion of the abradable ceramic layer coating system 52 of may be intentional for at least some of the temperatures experienced by article 50 and turbine blade 42. For example, turbine blade 42 may experience thermal expansion when heated to its operating temperature from the temperature when the gas turbine engine is not in use. At the same time, article 50 may also undergo thermal expansion when heated to the operating temperature. The thermal expansion experienced by turbine blade 42 and article 50 may result in a change in distance between substrate 54 of article 50 and blade tip 44. In some embodiments, the thickness of the abradable ceramic layer of coating system 52 may be selected such that blade tip 44 approximately contacts surface 48 of the abradable ceramic layer at a low temperature, such as a minimum operating temperature or a temperature of the surrounding environment when the gas turbine engine is not operating. The thickness of the abradable ceramic layer may also be selected such that when turbine blade 42 and article 50 are at an operating temperature, blade tip 44 contacts and abrades at least a portion of the abradable ceramic layer but does not contact or abrade underlying layers of coating system 52 and/or substrate 54.
As
Of course, in actual gas turbine engines, more than one blade is used. The turbine blades may follow substantially the same path along article 50 as the blades rotate during operation. However, the turbine blades may vary slightly in length or alignment, and thus may abrade different portions of the abradable ceramic layer. Accordingly, groove 56 may be essentially a superposition of the grooves formed by each turbine blade 42. Because of this, the seal between a turbine blade 42 and coating system 52 may not be perfect but may be improved compared to a seal between a turbine blade 42 and article 50 that does not include coating system 52 including the abradable ceramic layer.
The technique of
In some examples, although not shown in
The technique of
The technique of
Abradable ceramic layer 20 may be sprayed from a coating material that includes the materials in abradable ceramic layer 20 and a fugitive material. The fugitive material may include any material that may be removed, e.g., by heating, after deposition of abradable ceramic layer 20. In some examples, the fugitive material may include graphite, hexagonal boron nitride, or a polymer such as a polyester.
The technique of
Clause 1: An article comprising: a substrate comprising a metal or alloy; a bond coat directly on the substrate, wherein the bond coat comprises an alloy including aluminum; an intermediate ceramic layer on the bond coat, wherein the intermediate ceramic layer comprises a stabilized tetragonal prime phase constitution, wherein the intermediate ceramic layer defines a first porosity, and wherein the intermediate ceramic layer comprises: between about 4 wt. % and about 20 wt. % yttria and a balance zirconia or hafnia; or a first mixture comprising between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia; and an abradable ceramic layer directly on the intermediate ceramic layer, wherein the abradable ceramic layer comprises zirconia or hafnia stabilized in the tetragonal prime phase by a second mixture comprising between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia, wherein the abradable ceramic layer defines a second porosity, and wherein the second porosity is higher than the first porosity.
Clause 2: The article of clause 1, wherein the intermediate ceramic layer comprises more ytterbia than a combination of all other rare earth oxides present in the intermediate ceramic layer.
Clause 3: The article of clause 1 or 2, wherein the intermediate ceramic layer comprises zirconia stabilized in the tetragonal prime phase by about 7.5 wt. % ytterbia, about 1.5 wt. % samaria, and about 2.5 wt. % gadolinia, and a balance zirconia or hafnia.
Clause 4: The article of any one of clauses 1 to 3, wherein the abradable ceramic layer comprises more ytterbia than a combination of all other rare earth oxides present in the intermediate ceramic layer.
Clause 5: The article of any one of clauses 1 to 4, wherein the intermediate ceramic layer comprises zirconia stabilized in the tetragonal prime phase by about 7.5 wt. % ytterbia, about 1.5 wt. % samaria, and about 2.5 wt. % gadolinia, and a balance zirconia or hafnia.
Clause 6: The article of any one of clauses 1 to 5, wherein the intermediate ceramic layer defines a porosity of between about 5 vol. % and about 15 vol. %.
Clause 7: The article of any one of clauses 1 to 6, wherein the intermediate ceramic layer defines an average pore size of between about 0.5 micrometers and about 5 micrometers.
Clause 8: The article of any one of clauses 1 to 7, wherein the abradable ceramic layer defines a porosity of between about 10 vol. % and about 40 vol. %.
Clause 9: The article of any one of clauses 1 to 8, wherein the bond coat comprises at least one of MCrAlY, wherein M is selected from Co, Fe, Ni, or combinations thereof; β-NiAl; or γ-Ni+γ′-NiAl.
Clause 10: The article of any one of clauses 1 to 9, further comprising an alumina scale layer between the bond coat and the intermediate ceramic layer.
Clause 11: A system comprising: the article of any one of clauses 1 to 10, wherein the substrate comprises a part of a blade track; and a gas turbine engine blade comprising a blade tip, wherein the part of the blade track and the gas turbine blade are configured so the blade tip contacts a portion of the abradable ceramic layer during rotation of the gas turbine blade, and wherein the abradable ceramic layer is configured to be abraded by the contact by the blade tip.
Clause 12: The system of clause 11, wherein the gas turbine engine blade further comprises an abrasive coating on the blade tip.
Clause 13: A method comprising: forming a bond coat directly on a substrate, wherein the bond coat comprises an alloy including aluminum, and wherein the substrate coating comprises a metal or alloy; thermally spraying an intermediate ceramic layer on the bond coat, wherein the intermediate ceramic layer comprises a stabilized tetragonal prime phase constitution, and wherein the intermediate ceramic layer comprises: between about 4 wt. % and about 20 wt. % yttria and a balance zirconia or hafnia; or a first mixture comprising between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, and between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, and a balance zirconia or hafnia; and thermally spraying an abradable ceramic layer directly on the intermediate ceramic layer, wherein the abradable ceramic layer comprises zirconia or hafnia stabilized in the tetragonal prime phase by a second mixture comprising between about 5 wt. % and about 10 wt. % ytterbia, between about 0.5 wt. % and about 2.5 wt. % samaria, between about 1 wt. % and about 4 wt. % of at least one of lutetia, scandia, ceria, neodymia, europia, or gadolinia, between about 2 wt. % and about 10 wt. % fugitive material, and a balance zirconia or hafnia.
Clause 14: The method of clause 13, further comprising heating at least the abradable ceramic layer to substantially remove the fugitive material, wherein the intermediate ceramic layer defines a first porosity, and wherein, after the substantial removal of the fugitive material, the abradable ceramic layer defines a second porosity that is greater than the first porosity.
Clause 15: The method of clause 13 or 14, further comprising heating the bond coat to form an alumina scale on a surface of the bond coat, wherein thermally spraying the intermediate ceramic layer on the bond coat comprises thermally spraying the intermediate ceramic layer directly on the alumina scale.
Clause 16: The method of any one of clauses 13 to 15, wherein the intermediate ceramic layer comprises zirconia or hafnia stabilized in the tetragonal prime phase by about 7.5 wt. % ytterbia, about 1.5 wt. % samaria, and about 2.5 wt. % gadolinia, and a balance zirconia or hafnia.
Clause 17: The method of any one of causes 13 to 16, wherein the intermediate ceramic layer comprises zirconia or hafnia stabilized in the tetragonal prime phase by about 7.5 wt. % ytterbia, about 1.5 wt. % samaria, and about 2.5 wt. % gadolinia, and a balance zirconia or hafnia.
Clause 18: The method of any one of clauses 13 to 17, wherein the intermediate ceramic layer defines a porosity of between about 5 vol. % and about 15 vol. % and an average pore size of between about 0.5 micrometers and about 5 micrometers.
Clause 19: The method of any one of clauses 13 to 18, wherein the abradable ceramic layer defines a porosity of between about 10 vol. % and about 40 vol. %.
Clause 20: The method of any one of clauses 13 to 19, wherein the bond coat comprises at least one of MCrAlY, wherein M is selected from Co, Fe, Ni, or combinations thereof; β-NiAl; or γ-Ni+γ′-NiAl.
A substrate including between about 66.16 and about 68.24 wt. % Ni, between about 9.30 and about 9.70 wt. % W, between about 9 and about 9.50 wt. % Co, between 8 and about 8.5 wt. % Cr, between about 5.4 and about 5.7 wt. % Al, about 0.25 wt. % Si, about 0.1 wt. % Mn, and between about 0.06 and 0.09 C, available under the trade designation Mar-M 247™ from Cannon-Muskegon Corp, Muskegon, Mich. was coated with an MCrAlY bond coat formed from a powder including between 19.0 and 26.0 wt. % Co, between 14.0 and 21.0 wt. % Cr, between 11.0 and 14.0 wt. % Al, between 0.2 and 0.8 wt Y, between 0.1 and 0.5 wt. % Hf, between 0.1 and 0.7 wt. % Si, and a balance Ni available under the trade designation Amdry™ 386-4 from Oerlikon Metco, Pfaffikon, Switzerland. An yttria-stabilized zirconia intermediate coating including 7 wt. % yttria was deposited on the MCrAlY bond coat, and an abradable coating was deposited on the intermediate coating from a powder including about 7.75 wt. % Yb2O3, about 2.78 wt. % Gd2O3, about 1.9 wt. % Sm2O3, about 1.58 wt. % Hf, about 0.01 wt. % Fe2O3, less than 0.01 wt. % MgO, about 0.48 wt. % Na2O, about 0.01 wt. % SiO2, about 0.5 wt. % other oxides, about 3.97 wt. % organic solids, and about 3.65 wt. % polyester, and a balance ZrO2. The yttria-stabilized zirconia intermediate coating and the abradable coating were deposited using air plasma spraying.
Sintering was investigated by exposing a first sample to a temperature of 1371° C. for 100 hours and a second sample to a temperature of 1427° C. for 100 hours.
Various examples have been described. These and other examples are within the scope of the following claims.