Claims
- 1. An abrasion resistant decorative laminate meeting NEMA abrasion resistance standards and also capable of withstanding 175-200 cycles of initial wear in the same test comprising:
- a backing layer and laminated thereto a thermoset laminating resin impregnated decorative facing sheet, said decorative facing sheet having a print design thereon and an ultra-thin abrasion resistant coating over said print design, said ultra-thin abrasion resistant coating having a thickness of up to about 0.3 mils comprising a mixture of (1) an abrasion resistant hard mineral particle size 20-50 microns in high concentration sufficient to provide for abrasion resistance without interfering with visibility and (2) stabilizing binder material for said mineral, said thermoset resin being impregnated throughout said print sheet and said coating, said binder material not interfering with visibility, and with said ultra-thin abrasion resistant coating forming the uppermost layer of said laminate.
- 2. A decorative laminate in accordance with claim 1 wherein said thermoset resin is melamineformaldehyde resin.
- 3. A laminate in accordance with claim 2 wherein said binder comprises predominantly microcrystalline cellulose.
- 4. A laminate in accordance with claim 3 wherein said abrasion resistant mineral particles constitute alumina, silica or mixtures thereof.
- 5. A laminate in accordance with claim 2 wherein said abrasion resistant mineral is alumina, and wherein said alumina is chemically bound to said melamine resin with a silane.
- 6. A laminate in accordance with claim 1 wherein said ultra-thin abrasion resistant coating is directly over said print design and has a thickness of 0.02-0.2 mils.
- 7. A decorative, high-pressure laminate in accordance with claim 1 wherein said backing comprises a plurality of phenolic impregnated paper sheets and said facing sheet comprises a paper sheet impregnated with melamine resin, said abrasion resistant particles comprising alumina particles, said binder material comprising microcrystalline cellulose, said abrasion resistant coating comprising about 5-10 parts by weight of said microcrystalline cellulose for about 20-120 parts by weight of said alumina, the thickness of said coating being about 0.02-0.2 mils.
- 8. A laminate in accordance with claim 7 wherein said alumina is bonded to said melamine resin with a silane.
- 9. A laminate in accordance with claim 1, wherein said ultra-thin abrasion resistant coating has a thickness no greater than 0.3 mils.
- 10. A laminate in accordance with claim 1 wherein the quantity by weight of said binder material in said abrasion resistant coating is no greater than the quantity by weight of said mineral therein, and said binder material constitutes a mixture.
Parent Case Info
This is a division of application Ser. No. 879,848, now U.S. Pat. No. 4,255,480, which is a continuation-in-part of application Ser. No. 758,265 filed Jan. 10, 1977, now abandoned.
US Referenced Citations (20)
Foreign Referenced Citations (1)
Number |
Date |
Country |
47-30635 |
Aug 1972 |
JPX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
879848 |
Feb 1978 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
758265 |
Jan 1977 |
|