The following is directed to coated abrasive articles, and in particular coated abrasive articles including tooth-shaped abrasive particles.
Abrasive articles incorporating abrasive particles are useful for various material removal operations including grinding, finishing, polishing, and the like. Depending upon the type of abrasive material, such abrasive particles can be useful in shaping or grinding various materials in the manufacturing of goods. Certain types of abrasive particles have been formulated to date that have particular geometries, such as triangular abrasive particles and abrasive articles incorporating such objects. See, for example, U.S. Pat. Nos. 5,201,916; 5,366,523; and 5,984,988.
Previously, three basic technologies that have been employed to produce abrasive particles having a specified shape, which are fusion, sintering, and chemical ceramic. In the fusion process, abrasive particles can be shaped by a chill roll, the face of which may or may not be engraved, a mold into which molten material is poured, or a heat sink material immersed in an aluminum oxide melt. See, for example, U.S. Pat. No. 3,377,660. In sintering processes, abrasive particles can be formed from refractory powders having a particle size of up to 10 micrometers in diameter. Binders can be added to the powders along with a lubricant and a suitable solvent to form a mixture that can be shaped into platelets or rods of various lengths and diameters. See, for example, U.S. Pat. No. 3,079,243. Chemical ceramic technology involves converting a colloidal dispersion or hydrosol (sometimes called a sol) to a gel or any other physical state that restrains the mobility of the components, drying, and firing to obtain a ceramic material. See, for example, U.S. Pat. Nos. 4,744,802 and 4,848,041. Other relevant disclosures on abrasive particles and associated methods of forming and abrasive articles incorporating such particles are available at: http://www.abel-ip.com/publications/.
The industry continues to demand improved abrasive materials and abrasive articles.
According to one aspect, a coated abrasive article includes a substrate and a plurality of abrasive particles overlying the substrate, wherein at least 5% of the plurality of abrasive particles is tooth-shaped abrasive particles.
According to another aspect, a coated abrasive article includes a substrate and a plurality of abrasive particles including tooth-shaped abrasive particles, wherein at least 5% of the abrasive particles have a tilt angle greater than 44 degrees.
The present disclosure may be better understood, and its numerous features and advantages made apparent to those skilled in the art by referencing the accompanying drawings.
The following description in combination with the figures is provided to assist in understanding the teachings disclosed herein. The following discussion will focus on specific implementations and embodiments of the teachings. This focus is provided to assist in describing the teachings and should not be interpreted as a limitation on the scope or applicability of the teachings. However, other teachings can certainly be used in this application.
As used herein, the terms “comprises,” “comprising,” “includes,” “including,” “has,” “having” or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a method, article, or apparatus that comprises a list of features is not necessarily limited only to those features but may include other features not expressly listed or inherent to such method, article, or apparatus. Further, unless expressly stated to the contrary, “or” refers to an inclusive-or and not to an exclusive-or. For example, a condition A or B is satisfied by any one of the following: A is true (or present) and B is false (or not present), A is false (or not present) and B is true (or present), and both A and B are true (or present).
Also, the use of “a” or “an” is employed to describe elements and components described herein. This is done merely for convenience and to give a general sense of the scope of the invention. This description should be read to include one or at least one and the singular also includes the plural, or vice versa, unless it is clear that it is meant otherwise. For example, when a single embodiment is described herein, more than one embodiment may be used in place of a single embodiment. Similarly, where more than one embodiment is described herein, a single embodiment may be substituted for that more than one embodiment.
Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. The materials, methods, and examples are illustrative only and not intended to be limiting. To the extent that certain details regarding specific materials and processing acts are not described, such details may include conventional approaches, which may be found in reference books and other sources within the manufacturing arts. Moreover, unless stated otherwise, reference to any quantified value will be understood to be an average value based on a statistically-relevant sample size.
The following is directed to coated abrasive articles including tooth-shaped abrasive particles, methods of forming tooth-shaped abrasive articles, and methods of forming coated abrasive articles including tooth-shaped abrasive particles. The abrasive articles may be used in a variety of material removal operations for a variety of work pieces.
Referring again to
In one non-limiting embodiment, the mixture 113 may include at least a ceramic material and a liquid. In particular, the mixture 113 can be a gel formed of a ceramic powder material and a liquid, wherein the gel can be characterized as a shape-stable material having the ability to hold a given shape even in the green state (i.e., unfired or undried gel). In accordance with an embodiment, the gel can be formed of the ceramic powder material as an integrated network of discrete particles.
In certain aspects, control of certain processing conditions may be suitable for forming tooth-shaped abrasive particles. For example, the mixture 113 may be formed with a particular content of solid material to facilitate suitably forming the tooth-shaped abrasive particles. In one embodiment, the mixture 113 can have a high solids content, including for example, a solids content of at least about 25 wt %, such as at least about 35 wt %, at least about 42 wt %, at least about 44 wt %, at least about 46 wt %, at least about 48 wt %, at least about 50 wt %, or even at least about 51 wt % for the total weight of the mixture 113. Still, in at least one non-limiting embodiment, the solid content of the mixture 113 can be not greater than about 80 wt %, not greater than about 75 wt %, such as not greater than about 70 wt %, not greater than about 65 wt %, not greater than about 60 wt %, not greater than about 58 wt % or not greater than about 56 wt %. It will be appreciated that the content of the solids materials in the mixture 113 can be within a range between any of the minimum and maximum percentages noted above.
According to one embodiment, the ceramic powder material can include an oxide, a nitride, a carbide, a boride, an oxycarbide, an oxynitride, a superabrasive material or any combination thereof. It will be appreciated, that in certain alternative embodiments, in place of a ceramic powder material, one may choose to use a precursor of a ceramic powder material. A precursor can be a material, which may or may not be in a powder form, that is configured to change at least a portion of its composition or physical properties during processing to form a ceramic material. In particular instances, the ceramic material can include alumina. More specifically, the ceramic material may include a boehmite material, which may be a precursor of alpha alumina. The term “boehmite” is generally used to denote alumina hydrates including mineral boehmite, typically being Al2O3.H2O and having a water content on the order of 15%, as well as pseudoboehmite, having a water content higher than 15%, such as 20-38% by weight. It is noted that boehmite (including pseudoboehmite) has a particular and identifiable crystal structure, and accordingly unique X-ray diffraction pattern, and as such, is distinguished from other aluminous materials including other hydrated aluminas such as ATH (aluminum trihydroxide) a common precursor material used herein for the fabrication of boehmite particulate materials.
Furthermore, the mixture 113 can be formed to have a particular content of liquid material. Some suitable liquids may include inorganic materials, such as water or various organic materials such as alcohol and the like. In accordance with one embodiment, the mixture 113 can be formed to have a liquid content less than the solids content of the mixture 113. In more particular instances, the mixture 113 can have a liquid content of at least about 20 wt %, such as at least about 25 wt % for the total weight of the mixture 113. In other instances, the amount of liquid within the mixture 113 can be greater, such as at least about 35 wt %, at least about 40 wt %, at least about 42 wt % or at least about 44 wt % or at least 46 wt % or at least 48 wt % or at least 50 wt %. Still, in at least one non-limiting embodiment, the liquid content of the mixture can be not greater than about 80 wt %, such as not greater than about 65 wt %, not greater than about 60 wt % or not greater than about 55 wt %. It will be appreciated that the content of the liquid in the mixture 113 can be within a range between any of the minimum and maximum percentages noted above.
In some instances, the mixture 113 may have particular rheological characteristics to facilitate forming the tooth-shaped abrasive particles. For example, the mixture 113 may have a particular storage modulus. In one non-limiting embodiment, the mixture 113 can have a storage modulus of at least about 1×104 Pa, such as at least about 4×104 Pa, such as at least about 8×104 Pa, at least about 1×105 Pa, at least about 5×106 Pa, at least about 1×106 Pa, at least about 5×106 Pa or at least about 1×107 Pa. In at least one non-limiting embodiment, the mixture 113 may have a storage modulus of not greater than about 1×1010 Pa, not greater than about 1×109 Pa, not greater than about 1×108 Pa, or even not greater than about 1×107 Pa. It will be appreciated that the storage modulus of the mixture 113 can be within a range between any of the minimum and maximum values noted above.
The storage modulus can be measured via a parallel plate system using ARES or AR-G2 rotational rheometers, with Peltier plate temperature control systems. For testing, the mixture 113 can be extruded within a gap between two plates that are set to be approximately 8 mm apart from each other. After extruding the gel into the gap, the distance between the two plates defining the gap is reduced to 2 mm until the mixture 113 completely fills the gap between the plates. After wiping away excess mixture, the gap is decreased by 0.1 mm and the test is initiated. The test is an oscillation strain sweep test conducted with instrument settings of a strain range between 0.01% to 100%, at 6.28 rad/s (1 Hz), using 25-mm parallel plate and recording 10 points per decade. Within 1 hour after the test completes, lower the gap again by 0.1 mm and repeat the test. The test can be repeated at least 6 times. The first test may differ from the second and third tests. Only the results from the second and third tests for each specimen should be reported.
In another non-limiting embodiment, the mixture 113 may have a particular viscosity that facilitates formation of the tooth-shaped abrasive particles. For example, the mixture 113 can have a viscosity of at least about 1×105 Pa s, at least about 5×105 Pa s, at least about 1×106 Pa s, at least about 5×106 Pa s, at least about 1×107 Pa s, at least about 5×107 Pa s, at least about 1×108 Pa s, at least about 5×108 Pa s, at least about 1×109 Pa s, at least about 5×109 Pa s, at least about 1×1010 Pa s. In at least one non-limiting embodiment, the mixture 113 may have a viscosity of not greater than about 1×1015 Pa s, not greater than about 1×1013 Pa s, not greater than about 1×1012 Pa s, or even not greater than about 1×1010 Pa s. It will be appreciated that the viscosity of the mixture 113 can be within a range between any of the minimum and maximum values noted above. The viscosity can be measured in the same manner as the storage modulus as described above.
In still another non-limiting embodiment, the mixture 113 may have a particular yield stress. For example, the mixture 113 can have a yield stress of at least about 1×102 Pa, at least about 5×102 Pa at least about 1×104 Pa, at least about 5×104 Pa, at least about 1×105 Pa, at least about 5×105 Pa, at least about 1×106 Pa s, at least about 5×106 Pa s, at least about 1×107 Pa, at least about 5×107 Pa, or even at least about 1×108 Pa. In at least one non-limiting embodiment, the mixture 113 may have a yield stress of not greater than about 1×1010 Pa, not greater than about 1×109 Pa, not greater than about 1×108 Pa, or even not greater than about 1×107 Pa. It will be appreciated that the yield stress of the mixture 113 can be within a range between any of the minimum and maximum values noted above. The yield stress can be measured in the same manner as the storage modulus as described above.
The rheological characteristics of the mixture 113 can be distinct from conventional mixtures and gels, such as those described in certain references. Moreover, the mixture 113 can be formed to have a particular relationship between one or more rheological characteristics (e.g., viscosity, yield stress, storage modulus, etc.) to facilitate forming. Notably, the gel may be significantly more “stiff”, having a shear thinning characteristic, which may be entirely distinct from mixtures used in other forming methods.
In some optional embodiments, the mixture 113 can be formed to have a particular content of organic materials, including for example, organic additives that can be distinct from the liquid, to facilitate processing and formation of shaped abrasive particles according to the embodiments herein. Some suitable organic additives may include stabilizers, binders, such as fructose, sucrose, lactose, glucose, UV curable resins, and the like. It will be appreciated that the total content of all materials in the mixture (e.g., ceramic powder material, water, additives, etc.) add up to and do not exceed 100%.
The embodiments herein may utilize a mixture 113 that can be distinct from certain types of slurries. For example, the content of organic materials within the mixture 113, particularly, any of the organic additives noted above may be a minor amount as compared to other components within the mixture 113. In at least one embodiment, the mixture 113 can be formed to have not greater than about 30 wt % organic material for the total weight of the mixture 113. In other instances, the amount of organic materials may be less, such as not greater than about 15 wt %, not greater than about 10 wt %, or even not greater than about 5 wt %. Still, in at least one non-limiting embodiment, the amount of organic materials within the mixture 113 can be at least about 0.5 wt % for the total weight of the mixture 113. It will be appreciated that the amount of organic materials in the mixture 113 can be within a range between any of the minimum and maximum values noted above. In at least one alternative aspect, the mixture 113 may be essentially free of organic material.
In some embodiments, the mixture 113 can be formed to have a particular content of acid or base, which may facilitate processing. Some suitable acids or bases can include nitric acid, sulfuric acid, citric acid, hydrochloric acid, tartaric acid, phosphoric acid, ammonium nitrate, and/or ammonium citrate. According to one particular embodiment, the mixture 113 can have a pH of less than about 5, and more particularly, within a range between at least about 2 and not greater than about 4, using a nitric acid additive. Alternatively, the rheology of the acidic gel can be further modified by converting the acidic gel to a basic gel through the use of bases such as ammonium hydroxide, sodium hydroxide, organics amines such as hexamethylenetetramine and the like.
In one embodiment, extrusion of the mixture 113 from the extruder 103 and through the cavities in the production tool 101 can include applying a force on the mixture 113 to facilitate extrusion. In accordance with an embodiment, a particular pressure may be utilized during extrusion. For example, the pressure can be at least about 10 kPa, such as at least about 50 kPa, at least about 100 kPa, at least about 200 kPa or at least about 300 kPa or at least 400 kPa or at least 500 kPa. Still, in at least one non-limiting embodiment, the pressure utilized during extrusion can be not greater than about 10,000 kPa, such as not greater than about 8,000 kPa not greater than about 6,000 kPa or not greater than 3,000 kPa or not greater than 1,000 kPa or not greater than 800 kPa. It will be appreciated that the pressure used to extrude the mixture 113 can be within a range between any of the minimum and maximum values noted above.
In accordance with one embodiment, the mixture 113 can have a coil value of at least about 100 N. The coil value can be measured on an instrument called a Shimpo compression tester manufactured by Shimpo Instruments, Itasca Illinois, using a sample of mixture ranging from 30-60 grams in mass, which is manually pressed into a plastic/stainless steel cylinder of 2″ in diameter. At the extrusion end of the cylinder, a plastic insert with a cylindrical hole establishes the compressed extrudate size of generally 0.25 inches in diameter. A plunger slides into the cylinder and when the test is started, the plunger will extrude the gel once the threshold coil force is reached. When the cylinder assembly is in position, the Shimpo compression tester moves a force probe down towards the plunger at a constant rate of 95-97 mm/min. When the threshold coil force is reached, the gel is extruded out of the insert hole and an output meter generates a peak force, which is the coil value. In another embodiment, the coil value of the mixture 113 can be at least about 200 N, such as at least about 300 N, at least about 400 N, at least about 500 N, at least about 600 N, at least about 700 N, at least about 800 N, at least about 900 N, at least about 1000 N. In one non-limiting embodiment, the coil value of the mixture 113 can be not greater than about 3000 N, such as not greater than about 2500 N, or even not greater than about 2000 N. Thus, certain mixtures according to the embodiments herein can be significantly more flow resistant compared to conventional mixtures.
In accordance with an embodiment, the production tool 101 can include cavities in the form of apertures that extend through the thickness of the production tool 101. The production tool 101 may be in the form of an endless belt for continuous operations. Additionally, the production tool may include a plurality of cavities for improving the production capabilities of the process. The cavities can have any two-dimensional shape and size depending upon the intended cross-sectional shape of the tooth-shaped abrasive particles. In one particular embodiment, the cavities can have a quadrilateral two-dimensional shape as viewed in the plane of the length and width of the production tool 101.
As further illustrated in
In one embodiment, the rate of translation of the production tool 101 may be controlled to facilitate the formation of precursor tooth-shaped abrasive particles and tooth-shaped abrasive particles having one or more features of the embodiments herein. In one particular embodiment, the rate of translation of the production tool 101 can be controlled relative to the rate of extrusion.
In one non-limiting embodiment, the mixture 113 may be extruded at an extrusion rate of at least 0.0015 cm/s, such as at least 0.005 cm/s, at least 0.008 cm/s, at least 0.01 cm/s, at least 0.015 cm/s, at least 0.02 cm/s, at least 0.05 cm/s, at least 0.08 cm/s, at least 0.10 cm/s, at least 0.20 cm/s, at least 0.30 cm/s, at least 0.40 cm/s, at least 0.50 cm/s. Still, in one non-limiting embodiment, the mixture 113 may be extruded at an extrusion rate of not greater than 5 m/s, such as not greater than 1 m/s, not greater than 0.5 m/s, not greater than 100 cm/s, not greater than 50 cm/s, not greater than 10 cm/s, not greater than 1 cm/s. It will be appreciated that the mixture 113 may be extruded at an extrusion rate within a range between any of the minimum and maximum values noted above.
In one non-limiting embodiment, the production tool may be translated at a translation rate of at least 0.10 cm/s, such as at least 0.50 cm/s, at least 0.80 cm/s, at least 1.0 cm/s, at least 1.5 cm/s, at least 2 cm/s, at least 3 cm/s, at least 4 cm/s, at least 5 cm/s, at least 6 cm/s, at least 7 cm/s, at least 8 cm/s, at least 9 cm/s. Still, in one non-limiting embodiment, the production tool 101 may be translated at a rate of not greater than 5 m/s, such as not greater than 1 m/s, not greater than 0.5 m/s, not greater than 100 cm/s, not greater than 50 cm/s, not greater than 25 cm/s, not greater than 15 cm/s. It will be appreciated that the production tool may be translated at a rate within a range between any of the minimum and maximum values noted above.
The formation of tooth-shaped abrasive particles having the features of the embodiments herein is based upon empirical knowledge of the interrelationships between multiple processing variables, including for example, but not limited to mixture rheology, extrusion rate, translation rate, grit size or die opening size, and environmental conditions (e.g., temperature, humidity, etc.). Moreover, the uncontrolled change of one process variable may require controlled change of two or more other processing variable parameters to accommodate for the uncontrolled change. Furthermore, because of the relative size of the shapes being formed, the process requires precision that can be impacted by an uncontrolled change of one or more process variables, thereby resulting in abrasive particles that are not tooth-shaped abrasive particles.
The production tool 101 may include an inorganic material, including for example, but not limited a ceramic, a metal, a metal alloy, or any combination thereof. In an alternative embodiment, the production tool 101 may include an organic material, such as a polymer, including for example, a fluoropolymer, such as polytetrafluoroethylene (PTFE).
In an alternative embodiment, the production tool 101 may include a specific composition that may be imparted to the mixture 113 contained on the surfaces of the cavities. For example, the surfaces of the cavities may be coated with an additive. The additive may be an inorganic material, organic material, or any combination thereof. In certain instances, the additive may be a dopant. In such embodiments, the mixture 113 may be doped while being extruded through the cavities of the production tool 101.
After extrusion of the mixture 113, the extruded mixture can be translated on the production tool 101 to undergo further optional post-shaping processing at stage 109. Some non-limiting examples of the post-shaping processing at stage 109 may include drying, cooling, spraying, doping, coating, or any combination thereof.
After conducting any optional post-shaping processing at stage 109, the extruded mixture can be translated to a release zone 110 where the extruded mixture portions are released from the cavities of the production tool 101 to form precursor tooth-shaped abrasive particles. The extruded mixture portions can be released from the production tool 101 using various techniques, including but not limited to, mechanical manipulation, vibration, impingement of a gas or liquid phase material, change in temperature (i.e., heating, cooling, freezing, etc.) and the like. In a preferred embodiment, the extruded mixture portions are engaged with a blade that facilitates separation from the production tool 101.
In accordance with an embodiment, the mixture 113 can experience a change in weight of less than about 5% for the total weight of the mixture 113 for the duration the mixture 113 is connected to the production tool 101. In other embodiments, the weight loss of the mixture 113 can be less, such as less than about 4%, less than about 3%, less than about 2%, less than about 1%, or even less than about 0.5%. Still, in one particular embodiment, the mixture 113 may have essentially no change in weight for the duration the mixture 113 is in the production tool 101.
Furthermore, during processing, the mixture 113 may experience a limited change in volume (e.g., shrinkage) for the duration the mixture 113 is connected to the production tool 101. For example, the change in volume of the mixture 113 can be less than about 5% for the total volume of the mixture 113, such as less than about 4%, less than about 3%, less than about 2%, less than about 1%, or even less than about 0.5%. In one particular embodiment, the mixture 113 may experience essentially no change in volume for the entire duration the mixture 113 is connected to the production tool 101.
In one non-limiting embodiment, the mixture 113 may undergo a controlled heating process, while the mixture 113 is connected to the production tool 101. For example, the heating process may include heating the mixture at a temperature greater than room temperature for a limited time. The temperature may be at least about 30° C., such as at least about 35° C., at least about 40° C., such as at least about 50° C., at least about 60° C., or even at least about 100° C. Still, the temperature may be not greater than about 300° C., such as not greater than about 200° C., or even not greater than about at least about 150° C., or even not greater than about 100° C. The duration of heating can be particularly short, such as not greater than about 10 minutes, not greater than about 5 minutes, not greater than about 3 minutes, not greater than about 2 minutes, or even not greater than about 1 minute.
The heating process may utilize a radiant heat source, such as infrared lamps to facilitate controlled heating of the mixture 113. Moreover, the heating process may be adapted to control the characteristics of the mixture and facilitate particular aspects of the shaped abrasive particles according to embodiments herein.
In certain instances, the precursor tooth-shaped abrasive particles can be gathered and undergo further processing. For example, further processing can include doping, calcining, impregnating, drying, sintering, and the like. In one embodiment, the precursor tooth-shaped abrasive particles may have a dopant material applied to one or more exterior surfaces. In accordance with an embodiment, applying a dopant material can include the application of a particular material, such as a salt, which can be a precursor salt material that includes a dopant material to be incorporated into the finally-formed shaped abrasive particles. For example, a metal salt can include an element or compound that is the dopant material. It will be appreciated that the salt material may be in liquid form, such as in a dispersion comprising the salt and liquid carrier. The salt may include nitrogen, and more particularly, can include a nitrate. In one embodiment, the salt can include a metal nitrate, and more particularly, consist essentially of a metal nitrate.
In one embodiment, the dopant material can include an element or compound such as an alkali element, alkaline earth element, rare earth element, hafnium, zirconium, niobium, tantalum, molybdenum, vanadium, or a combination thereof. In one particular embodiment, the dopant material includes an element or compound including an element such as lithium, sodium, potassium, magnesium, calcium, strontium, barium, scandium, yttrium, lanthanum, cesium, praseodymium, niobium, hafnium, zirconium, tantalum, molybdenum, vanadium, chromium, cobalt, iron, germanium, manganese, nickel, titanium, zinc, silicon, boron, carbon and a combination thereof.
In one embodiment, the precursor tooth-shaped abrasive particle may be dried. Drying may include removal of a particular content of material, including volatiles, such as water. In accordance with an embodiment, the drying process can be conducted at a drying temperature of not greater than about 300° C., such as not greater than about 280° C., or even not greater than about 250° C. Still, in one non-limiting embodiment, the drying process may be conducted at a drying temperature of at least about 10° C., such as at least 20° C. or at least 30° C. or at least 40° C. It will be appreciated that the drying temperature may be within a range between any of the minimum and maximum temperatures noted above.
In accordance with an embodiment, the process of forming the tooth-shaped abrasive particles may include calcining, which includes removal of volatiles and a phase change in the material, including for example, a high-temperature phase material (e.g., alpha alumina). In yet another embodiment, the process for forming tooth-shaped abrasive particles may include impregnation of calcined precursor tooth-shaped abrasive particles with a dopant. In another embodiment, formation of the tooth-shaped abrasive particles from the precursor tooth-shaped abrasive particles can include sintering. Sintering may be conducted to densify the particles. In a particular instance, the sintering process can facilitate the formation of a high-temperature phase ceramic material. For example, in one embodiment, the precursor shaped abrasive particle may be sintered such that a high-temperature phase of alumina, such as alpha alumina is formed. It will be appreciated that certain additional processes, such as cleaning, may be completed on the production tool 101, to facilitate regular and repetitive processing.
After forming the tooth-shaped abrasive particles, such particles may be disposed onto a substrate to form a fixed abrasive article, such as a coated abrasive article. Further details on the coated abrasive articles and methods for forming such articles are described herein.
Referring now to
According to one non-limiting embodiment, the plurality of abrasive particles can include a blend of different types of abrasive particles. A blend can include a first portion of abrasive particles and a second portion of abrasive particles. In one embodiment, the tooth-shaped abrasive particles can be present in the first portion, the second portion, or both the first portion and second portion. In one instance, the first portion or the second portion may include only tooth-shaped abrasive particles. According to one embodiment, the blend can include a first portion of abrasive particles of a first type and a second portion of abrasive particles of a second type, wherein the first type and second type are different from each other based on at least one abrasive characteristic selected from the group of average grain size, average particle size, friability, toughness, hardness, two-dimensional shape, three-dimensional shape, any of the features described in the embodiments herein, or any combination thereof.
In one non-limiting aspect, the plurality of abrasive particles can include at least 10 grams of abrasive particles, such as at least 100 grams abrasive particles, at least 500 grams of abrasive particles, at least 1 kg of abrasive particles or at least 10 kg of abrasive particles.
In another aspect, the plurality of abrasive particles may include at least 10 abrasive particles, such as at least 20 abrasive particles or at least 30 abrasive particles or at least 50 abrasive particles or at least 100 abrasive particles or at least 500 abrasive particles. It will be appreciated that the number of abrasive particles of the in the plurality of abrasive particles may be within a range of at least 10 abrasive particles to not greater than a hundred thousand abrasive particles, such as within a range of at least 10 abrasive particles to not greater than a thousand abrasive particles or within range of at least 20 abrasive particles are not greater than 100 abrasive particles.
In still another aspect, the plurality of abrasive particles may include at least a portion, and in some cases, all of the abrasive particles included in a fixed abrasive article, such as, a coated abrasive article. In another embodiment, the plurality of abrasive particles may include all of the abrasive particles in a plurality of fixed abrasive articles.
As illustrated in the non-limiting embodiments of
In one non-limiting embodiment, a tooth-shaped abrasive particle can include a body 201 having a tip region 210 including a tip 211 and a base region 212 including a base 214. The base region 212 may be at the opposite end of the body from the tip region 210 along a length of the body 201. In another aspect, the body 201 may be substantially linear for a majority of the total length of the body 201. In another aspect, the body 201 may be substantially linear for a majority of the total length of the body 201. As used herein, the term substantially linear refers to a body that does not deviate from a linear axis more than 20%, such as not greater than 10% or not greater than 5%.
In one non-limiting aspect, the tip 211 may be defined by a convergence of at least two surfaces of the body 201. For example, the body 201 may include surfaces 221, 222, 223, and 224 (221-224) extending between the tip region 210 and the base region 212. In one embodiment, at least two of the surfaces (221-224) 221 may converge to form at least a portion of the tip 211. In some non-limiting examples, the tip 211 may be defined by a convergence of the surface 223 and surface 224, which generally define the thickness of the body 201. In another embodiment, the surfaces 221 and 222 may converge and be separated from each other at the tip 211 by a tip edge 213. In such embodiments, the tip 211 may be in the form of a wedge, wherein the body 201 in the dimension of the thickness converges to a tip edge 213 and the surfaces 221 and 222 defining the width of the body 201 may stay separated at the tip 211 by the tip edge 213. As best shown in
In other aspects, the tip 211 may be defined by convergence of more than two surfaces, such as at least three surfaces or at least four surfaces of the body 201. In such embodiments, the tip 211 may come have a tip edge defined by the convergence of at least three or more surfaces of the body.
According to one non-limiting embodiment, the tip edge 213 can have a tip edge length 233 as defined by the shortest distance between exterior corners 231 to 232 that is less than the average thickness (t) of the body 201, such as not greater than 95% or not greater than 90% or not greater than 85% or not greater than 80% or not greater than 75% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% of the average thickness of the body 201. Still, in another non-limiting embodiment, the tip edge length 233 may be at least 20% of the average thickness of the body 201, such as at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90% or at least 95% of the average thickness of the body 201. It will be appreciated that the tip edge length 233 can be within range including any of the minimum and maximum percentages noted above, including for example within a range of at least 20% and not greater than 95% of the average thickness, or within range including at least 50% not greater than 95% of the average thickness of the body 201.
In still another non-limiting embodiment, the tip edge length 233 may have a particular relationship to the width of the body 201. In one instance, the tip edge length 233 may be less than an average width of the body 201. According to one non-limiting example, the tip edge length 233 can be not greater than 99% of the average width of the body 201, such as not greater than 95% or not greater than 90% or not greater than 85% or not greater than 80% or not greater than 75% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% of the average width of the body 201. Still, in another embodiment non-limiting embodiment, the tip edge length 233 may be at least 0.1% of the average width of the body 201, such as at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90% or at least 95% of the average width of the body 201. It will be appreciated that the tip edge length 233 can be within range including any of the minimum and maximum percentages noted above, including for example within a range of at least 20% and not greater than 95% of the average width, or within range including at least 50% not greater than 95% of the average width of the body 201. Still, in another non-limiting embodiment, the tip edge length 233 may be substantially similar to the width average width of the body 201.
In accordance with one aspect, the tip region 210 may be defined by a taper including a reduction in the width and/or thickness of the body 201 in the tip region 210. In accordance with one embodiment, the tip region 210 can include a reduction in the width of the body 201 in the tip region 210. In another non-limiting embodiment, the tip region 210 can include a reduction in the thickness of the body 201 in the tip region 210. In another alternative embodiment, the tip region 210 may be defined by a taper including a reduction in the width and thickness of the body 201 in the tip region 210. Still, in another embodiment, the tip region 210 can be defined by taper including a change in the width of the body that is greater than a change in the thickness of the body 201 in the tip region 210. For another embodiment, the tip region 210 can be defined by taper including a change in the thickness of the body that is greater than a change in the width of the body 201 in the tip region 210. According to one non-limiting embodiment, the tip region 210 can be defined by a taper including a change in the thickness of the body 201 and where the average width is substantially the same throughout the tip region 210. For at least one other non-limiting embodiment, the tip region 210 can be defined by a taper including a change in the width of the body 201 and where the average thickness may be substantially the same throughout the tip region 210.
In certain non-limiting embodiments, the tip region 210 may have a tip region length that is not greater than 90% of the length of the body 201, such as not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20% or not greater than 10% or not greater than 5% of the total average length of the body. In still another non-limiting embodiment, the tip region can have a tip region length of at least 5% of the length of the body 201, such as at least 10% or at least 15% or at least 20% or at least 25% or at least 30% or at least 40%. It will be appreciated that the tip region length can be within a range including any of the minimum and maximum percentages noted above, including for example, but not limited to, within a range of at least 5% and not greater than 90% of the length of the body, or within range including at least 15% and not greater than 50% of the length of the body.
In accordance with another embodiment, the tip region 210 may include an asymmetric taper. An asymmetric taper is defined by one surface having a greater angling or curvature as compared to another surface. In particular instances an asymmetric taper may be characterized by a first surface (e.g., surface 224) of the body having a different contour as compared to another surface (e.g., surface 221, 222, and/or surface 223) of the body. For example, the first surface may have a greater curvature as compared to the second surface. In certain non-limiting embodiments, the second surface may be substantially linear and the first surface may be angled or curved non-parallel relationship relative to the second surface. The first and second surfaces may converge at the tip 211. The first surface may be longer than the second surface in the tip region 210.
In another non-limiting embodiment, the tooth-shaped abrasive particles may have a particular taper angle. For example, the surface (e.g., surface 224) with the greatest curvature in the tip region 210 can define a taper angle 252 as the angle between a line a tangent line to point 255 on the surface 224 and a point 251 at the tip 211 furthest from point 255. The point 255 defines the start of the taper region 210 on the surface 224. In accordance with an embodiment, the taper angle 252 can be at least 1 degree, such as at least 5 degrees or at least 8 degrees or at least 10 degrees or at least 15 degrees or at least 20 degrees or at least 25 degrees or at least 30 degrees or at least 40 degrees or at least 45 degrees. In another non-limiting embodiment, the taper angle 252 can be not greater than 90 degrees, such as not greater than 85 degrees or not greater than 80 degrees or not greater than 70 degrees or not greater than 60 degrees or not greater than 50 degrees or not greater than 40 degrees or not greater than 30 degrees. It will be appreciated that the taper angle 252 may be within a range including any of the minimum and maximum values noted above, including for example, but not limited to, within a range including at least 5 degrees and not greater than 90 degrees or at least 5 degrees and not greater than 70 degrees or at least 10 degrees and not greater than 50 degrees. In certain instances, but not all, the taper angle may only be evident in the plane defined by the length and width of the body 201.
As noted herein, each of the tooth-shaped abrasive particles may include a base region 212 at an opposite end of the body 201 from the tip region 210. The base region 212 may include a base 214. In accordance with an embodiment, the base 214 can include a projection 215 extending from the body 201. More particularly, the projection 215 may extend from the body 201 in a direction away from the longitudinal axis 280. In particular instances, the projection 215 may extend away from the tip 211. In some embodiments, but not all, the projection 215 may only be evident in a view of the particle from a plane defined by the length and width of the body 201.
In one aspect, the body 201 of the tooth-shaped abrasive particle may have a base angle 261 that can define the angle at which the protrusion extends from the body 201. The base angle 261 can be the angle between the surface 224 of the body 201 and a surface 262 extending from exterior corner 217 of a base surface 216. In one non-limiting embodiment, the base angle 261 may be an obtuse angle. For example, the base angle 261 can be at least 91 degrees, such as at least 92 degrees or at least 93 degrees or at least 94 degrees or at least 95 degrees or at least 97 degrees or at least 99 degrees or at least 105 degrees or at least 110 degrees or at least 120 degrees or at least 130 degrees or at least 140 degrees. In another non-limiting embodiment, the base angle 261 may be not greater than 180 degrees, such as not greater than 178 degrees or not greater than 170 degrees or not greater than 160 degrees or not greater than 150 degrees. It will be appreciated that the base angle 261 can be within a range including the minimum and maximum values noted above.
In another non-limiting embodiment, the base 214 can include a projection 215 having a projection length (Lp). The projection length may be the length of the longest side of the projection 215 in the base region 212 excluding the base surface 216. For example, as illustrated in
Another non-limiting embodiment, the base 214 can include a base surface 216. The base surface 216 may extend between exterior corners 217 and 218. The exterior corner 217 may be a corner between the base surface 216 and surface 224, wherein surface 224 in some instances can be the most curved surface in the tip region 210. The exterior corner 217 may be an upper corner 217 and the exterior corner 218 may be a lower corner 218 spaced apart from the upper corner across the length of the base surface 216. In one embodiment, the exterior corner 218 may be a corner on the base 214 furthest from the tip 211. In another embodiment, the exterior corner 218 may be a corner on the base 214 closer to the longitudinal axis 280 as compared to the exterior corner 217.
In one non-limiting embodiment, the exterior corner 217 can have a corner radius less than a corner radius of the tip 211. Still, in another embodiment, the exterior corner 218 can have a corner radius less than a corner radius of the tip 211.
In yet another embodiment, the base surface 216 can extend at an angle relative to the longitudinal axis 280 of the body 201. For example, the base surface 216 may be angled relative to a longitudinal axis 280 to define a base surface angle 237. In one embodiment, the base surface angle 237 may be an acute angle. According to a non-limiting embodiment, the base surface angle 237 can be not greater than 90 degrees, such as not greater than 88 degrees or not greater than 86 degrees or not greater than 84 degrees or not greater than 82 degrees or not greater than 80 degrees or not greater than 75 degrees or not greater than 70 degrees or not greater than 65 degrees or not greater than 60 degrees or not greater than 55 degrees or not greater than 50 degrees or not greater than 45 degrees or not greater than 40 degrees. In another non-limiting embodiment, the base surface angle 237 may be at least 5 degrees, such as at least 10 degrees or at least 15 degrees or at least 20 degrees or at least 25 degrees or at least 30 degrees or at least 35 degrees or at least 40 degrees or at least 45 degrees or at least 50 degrees or at least 55 degrees. It will be appreciated that the base surface angle 237 can be within a range including any of the minimum and maximum values noted above.
In another embodiment, the base region 212 can have a primary peak angle 238 at the exterior corner 218 between the base surface 216 and the surface 264. In one aspect, the primary peak angle 238 can be at least 45 degrees and not greater than 150 degrees as viewed in the plane define by the length and the width of the body 201. According to one embodiment, the primary peak angle 238 can be at least 50 degrees, such as at least 55 or at least 60 degrees or at least 65 degrees or at least 70 degrees or at least 75 degrees or at least 80 degrees or at least 85 degrees or at least 90 degrees or at least 95 degrees or at least 100 degrees. In another non-limiting embodiment, the primary peak angle 238 can be not greater than 145 degrees or not greater than 140 degrees or not greater than 135 degrees or not greater than 130 degrees or not greater than 125 degrees or not greater than 120 degrees or not greater than 115 degrees or not greater than 110 degrees or not greater than 100 degrees or not greater than 95 degrees. It will be appreciated that the primary peak angle 238 can be within a range including any of the minimum and maximum values noted above.
According to another embodiment, the exterior corner 218 can define a primary peak as viewed in a plane defined by the length and width of the body 201. According to one embodiment, the primary peak can have a tip sharpness, which can be measured by the primary peak angle 238, that is less than a tip sharpness of the tip 211 of the body 201, which may also be measured by a tip angle 277 at the point 251 on the tip 211 of the body 201. According to one particular embodiment, the primary peak angle 238 can be at least 5% less than the tip angle 277, such as at least 8% less or at least 10% less or at least 12% less or at least 15% less or at least 20% less or at least 25% less or at least 30% less or at least 40% less or at least 50% less or at least 60% less or at least 70% less or at least 80% less or at least 90% less. In one non-limiting embodiment, the primary peak angle 238 can be at not greater than 99% less than the tip angle 277, such as not greater than 95% less or not greater than 90% less or not greater than 80% less or not greater than 60% less or not greater than 40% less. It will be appreciated that the primary peak angle 238 can be less than the tip angle 277 within a range of any of the minimum and maximum percentages noted above.
In another aspect, it was unexpected that the base region 212 would have at least one or more sharper tips as compared to the tip region 210. This is particular notable because the base region 212 can generally include a greater volume of material than the tip region 210 based on the cross-sectional area of the base region 212 as compared to the tip region 210.
In one non-limiting aspect, the base surface 218 may have a particular surface morphology, which may facilitate unexpected and improved performance. In accordance with one embodiment, the base surface 218 can include at least one peak 233, such as a plurality of peaks 233 extending from the base surface 218. In another embodiment, the base surface 218 may include at least one valley 234, such as a plurality of valleys 234 extending between the plurality of peaks 233 across at least a portion of the base surface 218. In accordance with another non-limiting embodiment, the plurality of peaks 233 and valleys 234 may be randomly disposed on the base surface 218.
In some instances, but not all, the base surface 218 may have a surface roughness that is different than a surface roughness of at least one of the surfaces (221-224) of the body 201. In one embodiment, the base surface 218 may have a surface roughness that is greater than a surface roughness of a side surface of the body (221-224) in the tip region 210 or the elongated region 240 of the body 201.
In accordance with another embodiment, the base surface 218 may include at least one peak of the plurality of peaks 233 having a tip radius less than a tip radius of the tip 211 of the body 201. Still, in another non-limiting embodiment, the base surface 218 may include at least two peaks of the plurality of peaks 233 having a tip radius less than a tip radius of the tip 211 of the body 201.
In certain tooth-shaped abrasive particles of the embodiments herein, the base region 212 may include a first peak 235 and a second peak 236 as viewed in two dimensions defined by a plane of the length and thickness of the body 201, as provided in
According to another non-limiting aspect, the base surface 216 can include one or more facets 241. The facets 241 define regions on the base surface that are substantially planar. In particular instances, the facets 241 may extend between the plurality of peaks 233 and values 234 of the base surface 215. In some instances, the base surface 218 may include at least two facets that are abutting each other and define a common edge extending between the two facets.
As noted herein, the tooth-shaped abrasive particles of certain embodiments may include a tip region 210, a base region 212 and elongated region 240 disposed between the tip region 210 and the base region 212. More specifically, the elongated region 240 can extend between the tip region 210 and the base region 212. In one non-limiting embodiment, the elongated region 240 between the tip region 210 and the base region 212 having a substantially constant width. For example, in one embodiment the elongated region 240 may have a change in width of not greater than 10% over the length of the elongated region 240, such as not greater than 8% or not greater than 5% or not greater than 3%. In at least one embodiment, the elongated region 240 may have a change in width of at least 0.5%, such as least 1% or at least 2% over the length of the elongated region 240. It will be appreciated that the change in the width of the body 201 in the elongated region 240 may be within a range including any of the minimum and maximum percentages noted above.
In another embodiment, the elongated region 240 may have a change in thickness of not greater than 10% over the length of the elongated region 240, such as not greater than 8% or not greater than 5% or not greater than 3%. In at least one embodiment, the elongated region 240 may have a change in thickness of at least 0.5%, such as least 1% or at least 2% over the length of the elongated region 240. It will be appreciated that the change in the thickness of the body 201 in the elongated region 240 may be within a range including any of the minimum and maximum percentages noted above.
In other instances, the tooth-shaped abrasive particles may have other features. For example, in some instances, the body may include striations 271. Such striations may be present on at least one of the surfaces, such as surfaces 221-224. More particularly, the striations 271 may be present on at least a portion of all of the side surfaces 222-224. In another non-limiting embodiment, the striations 271 may extend in a direction of the length of the body 201. In still another embodiment, the striations 271 may extend over a majority of the surface area of at least one or more surfaces 221-224. According to one particular embodiment, the striations 271 extend over a majority of the surface area of all of the surfaces 221-224.
According to one embodiment, the body 201 of the tooth-shaped abrasive particles may have a particular primary aspect ratio (length/width) that may result from the disclosed forming process and may also facilitate certain features and/or improved performance. In one aspect, the tooth-shaped abrasive particles may have a primary aspect ratio of (length/width) of at least 1.1 or at least 1.2 or at least 1.5 or at least 2 or at least 2.5 or at least 3 or at least 3.5 or at least 4 or at least 4.5 or at least 5 or at least 5.5 or at least 6 or at least 8 or at least 10. In another non-limiting embodiment, the body 201 can have a primary aspect ratio of length:width of not greater than 1000 or not greater than 100 or not greater than 50 or not greater than 20 or not greater than 10 or not greater than 5 or not greater than 3 or not greater than 2.8. It will be appreciated that the primary aspect ratio of the body 201 can be with a range including any of the minimum and maximum ratios noted above. Furthermore, it will be appreciated that the primary aspect ratio may represent a primary aspect ratio of a single tooth-shaped abrasive particle or an average of a plurality of tooth-shaped abrasive particles.
All aspect ratios of the embodiments herein are measured by image processing. A plurality of tooth-shaped abrasive particles are mounted and set on a stage for imaging. Imaging may be completed via an optical microscope such as a DSX 700 Olympus at a suitable magnification, such as 2×-8×. After taking a suitable image of a suitable statistically relevant sample size of the particles (e.g., at least 200 particles), the image (RGB color or grayscale) is saved as a representative image of the particle's length and width dimensions. See, for example,
According to one embodiment, the body 201 of the tooth-shaped abrasive particles may have a particular secondary aspect ratio (length/thickness) that may result from the disclosed forming process and may also facilitate certain features and/or improved performance. In one non-limiting embodiment, the body 201 can have a secondary aspect ratio of length/thickness that can be at least 1.1 or at least 1.2 or at least 1.5 or at least 2 or at least 2.5 or at least 3 or at least 3.5 or at least 4 or at least 4.5 or at least 5 or at least 5.5 or at least 6 or at least 8 or at least 10. Still, in another non-limiting embodiment, the secondary aspect ratio (length/thickness) may be not greater than 1000 or not greater than 100 or not greater than 50 or not greater than 20 or not greater than 10 or not greater than 5 or not greater than 3 or not greater than 2.8. It will be appreciated the secondary aspect ratio of length/thickness can be with a range including any of the minimum and maximum ratios of above. Furthermore, it will be appreciated that the secondary aspect ratio may represent a secondary aspect ratio of a single tooth-shaped abrasive particle or an average of a plurality of tooth-shaped abrasive particles.
According to one embodiment, the body 201 of the tooth-shaped abrasive particles may have a particular tertiary aspect ratio (length/thickness) that may result from the disclosed forming process and may also facilitate certain features and/or improved performance. In another embodiment, the body 201 can have a tertiary aspect ratio (width/thickness) of at least 0.5, such as at least 0.6 or at least 0.7 or at least 0.8 or at least 0.9 or at least 1.0 or at least 1.1 or at least 1.2 or at least 1.3 or at least 1.4 or at least 1.5 or at least 2 or at least 2.5 or at least 3 or at least 4. In another non-limiting embodiment, the tertiary aspect ratio (width/thickness) can be not greater than 10, such as not greater than 8 or not greater than 5 or not greater than 3 or not greater than 2 or not greater than 1.5 or not greater than 1.3 or not greater than 1.1. It will be appreciated that the tertiary aspect ratio can be with a range including any of the minimum and maximum ratios noted above. It will be appreciated that the tertiary aspect ratio of the body 201 can be within a range including any of the minimum and maximum ratios noted above. Furthermore, it will be appreciated that the tertiary aspect ratio may represent a tertiary aspect ratio of a single tooth-shaped abrasive particle or an average of a plurality of tooth-shaped abrasive particles.
The tooth-shaped abrasive particles of the embodiments herein can have a body including a crystalline material, and more particularly, a polycrystalline material. Notably, the polycrystalline material can include abrasive grains (i.e., crystallites). In one embodiment, the body of the tooth-shaped abrasive particle can be essentially free of an organic material, including for example, a binder. In at least one embodiment, the tooth-shaped abrasive particles can consist essentially of a polycrystalline material.
The abrasive grains (i.e., crystallites) contained within the body 201 of the tooth-shaped abrasive particles may have an average grain size that is generally not greater than 20 microns, such as not greater than 18 microns or not greater than 16 microns or not greater than 14 microns or not greater than 12 microns or not greater than 10 microns or not greater than 8 micron or not greater than 5 microns or not greater than 2 microns or not greater than 1 micron or not greater than 0.9 microns or not greater than 0.8 microns or not greater than 0.7 microns or even not greater than 0.6 microns or even not greater than 0.2 microns. Still, the average grain size of the abrasive grains contained within the body of the tooth-shaped abrasive particles can be at least 0.01 microns, such as at least 0.05 microns or at least 0.06 microns or at least 0.07 microns or at least 0.08 microns or at least 0.09 microns or at least 0.1 microns or at least 0.12 microns or at least 0.15 microns or at least 0.17 microns or at least 0.2 microns or even at least 0.5 microns. It will be appreciated that the abrasive grains can have an average grain size within a range including any of the minimum and maximum values noted above. The average grain size can be calculated using the uncorrected intercept method as known to those of skill in the art.
In accordance with an embodiment, the body 201 of the tooth-shaped abrasive particle can have an average particle size, as measured by the largest dimension measurable on the body (i.e., the length), of at least 100 microns. In fact, the body 201 of the tooth-shaped abrasive particle can have an average particle size of at least 150 microns, such as at least 200 microns or at least 300 microns or at least 400 microns or at least 500 microns or at least 500 microns or at least 600 microns or at least 800 microns or even at least 900 microns. Still, the body 201 of the tooth-shaped abrasive particle can have an average particle size that is not greater than 5 mm, such as not greater than 3 mm or not greater than 2 mm or even not greater than 1.5 mm. It will be appreciated that the body of the tooth-shaped abrasive particle can have an average particle size within a range including any of the minimum and maximum values noted above.
Particles for use in the abrasives industry are generally graded to a given particle size distribution before use. Such distributions typically have a range of particle sizes, from coarse particles to fine particles. In the abrasive art, this range is sometimes referred to as a “coarse”, “control”, and “fine” fractions. Abrasive particles graded according to abrasive industry accepted grading standards specify the particle size distribution for each nominal grade within numerical limits. Such industry accepted grading standards (i.e., abrasive industry specified nominal grade) include those known as the American National Standards Institute, Inc. (ANSI) standards, Federation of European Producers of Abrasive Products (FEPA) standards, and Japanese Industrial Standard (JIS) standards. ANSI grade designations (i.e., specified nominal grades) include: ANSI 4, ANSI 6, ANSI 8, ANSI 16, ANSI 24, ANSI 36, ANSI 40, ANSI 50, ANSI 60, ANSI 80, ANSI 100, ANSI 120, ANSI 150, ANSI 180, ANSI 220, ANSI 240, ANSI 280, ANSI 320, ANSI 360, ANSI 400, and ANSI 600. FEPA grade designations include P8, P12, P16, P24, P36, P40, P50, P60, P80, P100, P120, P150, PI 80, P220, P320, P400, P500, P600, P800, P1000, and P1000. JIS grade designations include JIS8, JIS12, JIS 16, JIS24, JIS36, JIS46, JIS54, JIS60, JIS80, JIS 100, JIS150, JIS180, JIS220, JIS240, JIS280, JIS320, JIS360, JIS400, JIS600, JIS800, JIS 1000, JIS 1500, JIS2500, JIS4000, JIS6000, JIS8000, and JIS10,000. Alternatively, the abrasive particles can be graded to a nominal screened grade using U.S.A. Standard Test Sieves conforming to ASTM E-1 1 “Standard Specification for Wire Cloth and Sieves for Testing Purposes.” ASTM E-1 1 prescribes the requirements for the design and construction of testing sieves using a medium of woven wire cloth mounted in a frame for the classification of materials according to a designated particle size. A typical designation may be represented as −18+20 meaning that the particles pass through a test sieve meeting ASTM E-1 1 specifications for the number 18 sieve and are retained on a test sieve meeting ASTM E-1 1 specifications for the number 20 sieve. In various embodiments, the particulate material can have a nominal screened grade comprising: −18+20, −20/+25, −25+30, −30+35, −35+40, −40+45, −45+50, −50+60, −60+70, −70/+80, −80+100, −100+120, −120+140, −140+170, −170+200, −200+230, −230+270, −270+325, −325+400, −400+450, −450+500, or −500+635. Alternatively, a custom mesh size could be used such as −90+100. The body of the particulate material may be in the form of a shaped abrasive particle, as described in more detail herein.
Some suitable materials for use in the body 201 of the tooth-shaped abrasive particles can include a ceramic material, including but not limited to, nitrides, oxides, carbides, borides, oxynitrides, oxyborides, oxycarbides, carbon-based materials, diamond, naturally occurring minerals, rare-earth-containing materials, natural minerals, synthetic materials, or any combination thereof. In particular instances, the tooth-shaped abrasive particles can include an oxide compound, such as aluminum oxide, zirconium oxide, titanium oxide, yttrium oxide, chromium oxide, strontium oxide, silicon oxide, magnesium oxide, rare-earth oxides, or any combination thereof.
In one particular embodiment, the body 201 can include at least 95 wt % alumina for the total weight of the body 201. Still, in certain instances, the body can include not greater than 99.5 wt % alumina for the total weight of the body. In at least one embodiment, the body 201 can consist essentially of alumina, and more particularly, consist essentially of alpha alumina. In certain instances, the body 201 may be formed such that it includes not greater than about 1 wt % of any low-temperature alumina phases. As used herein, low temperature alumina phases can include transition phase aluminas, bauxites or hydrated alumina, including for example gibbsite, boehmite, diaspore, and mixtures containing such compounds and minerals. Certain low temperature alumina materials may also include some content of iron oxide. Moreover, low temperature alumina phases may include other minerals, such as goethite, hematite, kaolinite, and anastase.
Moreover, in particular instances, the body 201 of the tooth-shaped abrasive particles can be formed from a seeded sol-gel. In at least one embodiment, the body of any of the tooth-shaped abrasive particles of the embodiments herein may be essentially free of iron, rare-earth oxides, and a combination thereof. Reference herein to a body having a certain features (e.g., composition) will also be understood to refer to a batch of a tooth-shaped abrasive particles that can have the same feature (e.g., composition).
In accordance with certain embodiments, certain tooth-shaped abrasive particles can be compositional composites, such that at least two different types of grains are contained within the body of the tooth-shaped abrasive particle. It will be appreciated that different types of grains are crystallite grains having different compositions with regard to each other. For example, the body of the tooth-shaped abrasive particle can be formed such that it includes at least two different types of grains, wherein the types of grains are selected from the group of nitrides, oxides, carbides, borides, oxynitrides, oxyborides, oxycarbides, carbon-based materials, diamond, naturally occurring minerals, rare-earth-containing materials, natural minerals, synthetic materials, and a combination thereof.
The body 201 of the tooth-shaped abrasive particles may include additives, such as dopants, which may be in the form of elements or compounds (e.g., oxides). Certain suitable additives can include any of the materials described herein. The body of a tooth-shaped abrasive particle may include a specific content of one or more additives (e.g., dopant). For example, the body may include not greater than about 30 wt % additives for the total weight of the body. In still other embodiments, the amount of additives may be less, such as not greater than about 25 wt % or not greater than about 20 wt % or not greater than about 18 wt % or not greater than about 15 wt % or not greater than about 12 wt % or not greater than about 10 wt % or not greater than about 8 wt % or not greater than 5 wt % or not greater than 2 wt %. Still, the amount of additives can be at least about 0.5 wt % for a total weight of the body, such as at least about 1 wt %, at least about 2 wt % or at least about 3 wt % or at least about 4 wt % or at least about 5 wt % or at least about 8 wt % or even at least about 10 wt %. It will be appreciated that the amount of additive within the body may be within a range including any of the minimum and maximum percentages noted above.
The body of the tooth-shaped abrasive particle may be particularly dense. For example, the body may have a density of at least about 95% theoretical density, such as at least about 96% or at least 97% or at least 98% or at least 99% theoretical density.
The tooth-shaped abrasive particles of the embodiments herein are a particular type of shaped abrasive particle. Shaped abrasive particles may be formed through particular processes, including molding, printing, casting, extrusion, and the like. Shaped abrasive particles can be formed such that each particle has substantially the same arrangement of surfaces and edges relative to each other. For example, a group of shaped abrasive particles generally have the same arrangement and orientation and or two-dimensional shape of the surfaces and edges relative to each other. As such, the shaped abrasive particles have a relatively high shape fidelity and consistency in the arrangement of the surfaces and edges relative to each other. Moreover, constant height abrasive particles (CHAPs) can also be formed through particular processes that facilitate formation of thin-shaped bodies that can have irregular two-dimensional shapes when viewing the major surface top-down. CHAPs can have less shape fidelity than shaped abrasive particles, but can have substantially planar and parallel major surfaces separated by a side surface.
By contrast, non-shaped particles can be formed through different processes and have different shape attributes compared to shaped abrasive particles and CHAPs. For example, non-shaped particles are typically formed by a comminution process wherein a mass of material is formed and then crushed and sieved to obtain abrasive particles of a certain size. However, a non-shaped particle will have a generally random arrangement of surfaces and edges, and generally will lack any recognizable two-dimensional or three dimensional shape in the arrangement of the surfaces and edges. Moreover, non-shaped particles do not necessarily have a consistent shape with respect to each other, and therefore have a significantly lower shape fidelity compared to shaped abrasive particles or CHAPs. The non-shaped particles generally are defined by a random arrangement of surfaces and edges for each particle and with respect to other non-shaped particles.
According to one embodiment, the substrate 301 can include an organic material, inorganic material, and a combination thereof. In certain instances, the substrate 301 can include a woven material. However, the substrate 301 may be made of a non-woven material. Particularly suitable substrate materials can include organic materials, including polymers, and particularly, polyester, polyurethane, polypropylene, polyimides such as KAPTON from DuPont, paper. Some suitable inorganic materials can include metals, metal alloys, and particularly, foils of copper, aluminum, steel, and a combination thereof.
The make coat 303 can be applied to the surface of the substrate 301 in a single process, or alternatively, the plurality of abrasive particles 305 can be combined with a make coat 303 material and applied as a mixture to the surface of the substrate 301. Suitable materials of the make coat 303 can include organic materials, particularly polymeric materials, including for example, polyesters, epoxy resins, polyurethanes, polyamides, polyacrylates, polymethacrylates, poly vinyl chlorides, polyethylene, polysiloxane, silicones, cellulose acetates, nitrocellulose, natural rubber, starch, shellac, and mixtures thereof. In one embodiment, the make coat 303 can include a polyester resin. The coated substrate can then be heated in order to cure the resin and the abrasive particulate material to the substrate. In general, the coated substrate 301 can be heated to a temperature of between about 100° C. to less than about 250° C. during this curing process.
Moreover, it will be appreciated that the coated abrasive article 300 can include one or more types of abrasive particles in the plurality of abrasive particles 305. The different types of abrasive particles can differ from each other in composition, two-dimensional shape, three-dimensional shape, grain size, particle size, hardness, friability, agglomeration, or any combination thereof. In one embodiment, the coated abrasive article 300 can include different amounts of the different types of abrasive particles depending upon the application. It will be appreciated that in some embodiments the coated abrasive may not necessarily include different types of shaped abrasive particles and can consist essentially of a single type of shaped abrasive particle.
According to one particular embodiment, the plurality of abrasive particles 305 may include a limited content of agglomerated particles, and more particularly, a limited content of agglomerated tooth-shaped particles. Some agglomerates of tooth-shaped abrasive particles may be joined or sinter-bonded to each other. In one aspect, the plurality of abrasive particles 305 may include not greater than 50% of agglomerated particles for a total count of particles in the plurality of abrasive particles 305, such as not greater than 48% or not greater than 46% or not greater than 44% or not greater than 42% or not greater than 40% or not greater than 38% or not greater than 36% or not greater than 34% or not greater than 32% or not greater than 30% or not greater than 28% or not greater than 26% or not greater than 24% or not greater than 22% or not greater than 20% or not greater than 18% or not greater than 16% or not greater than 14% or not greater than 12% or not greater than 10% or not greater than 8% or not greater than 6% or not greater than 4% or not greater than 2%. In one particular embodiment, the plurality of abrasive particles 305 can be free of agglomerated particles, and more particularly, tooth-shaped abrasive particles that are joined or sinter-bonded to each other. Notably, in certain conventional fixed abrasive articles including shaped abrasive particles, the fixed abrasive particles may agglomerate in the form of “twins” or “triplets” which are particles that are sintered to each other. The processes herein may facilitate formation of batches of abrasive particles and fixed abrasives including a plurality of abrasive particles having a limited content of agglomerated particles.
Furthermore, in one embodiment, the plurality of abrasive particles 305 may include a limited content of hook-shaped abrasive particles. Hook shaped abrasive particles may include extruded, hook-shaped abrasive particles. Hook-shaped abrasive particles are characterized by at least one end of the body that curls significantly back toward the particle to be characterized as a hook-shape.
Various methods may be used to place the abrasive particles on the backing (i.e., substrate), including for example, but not limited to, projection (e.g., mechanical or electrostatic), gravity feeding, production tools with suitably sized openings to temporarily hold the abrasive particles in a desired orientation until they are transferred to the backing or an adhesive layer, vibration, pick-and-place systems, and the like. Certain methodologies may be more suitable for controlling one or more aspects of the position and/or orientation of the abrasive particles relative to each other and the backing.
According to one particular embodiment, the tooth-shaped abrasive particles may have a particular orientation, such as a vertical orientation relative to the substrate 301. As described in other embodiments herein, the tooth-shaped abrasive particles 306 can have a tip region 210 and a base region 212 opposite the tip region 210 across the length of the body. In one aspect, a certain content of tooth-shaped abrasive particles 306 can be oriented with the tip region 210 closer to the substrate 301 than the base region 212. In at least one embodiment, a greater content of tooth-shaped abrasive particles can have their tip regions 210 closer to the substrate 301 than their base regions 212 as compared to the content of tooth-shaped abrasive particles with their base regions 212 closer to the substrate 301 than their tip regions 210. According to one particular embodiment, at least 60%, such as at least 70% or at least 80% or at least 90% of the tooth-shaped abrasive particles their tip regions 210 closer to the substrate 301 than their base regions 212.
After sufficiently forming the make coat 303 with the plurality of abrasive particles 305 contained therein, the size coat 304 can be formed to overlie and bond the plurality of abrasive particles 305 to the substrate 301. The size coat 304 can include an organic material, may be made essentially of a polymeric material, and notably, can use polyesters, epoxy resins, polyurethanes, polyamides, polyacrylates, polymethacrylates, poly vinyl chlorides, polyethylene, polysiloxane, silicones, cellulose acetates, nitrocellulose, natural rubber, starch, shellac, and mixtures thereof.
According to a particular embodiment, each of the tooth-shaped abrasive particles 504-508 may be disposed in a predetermined position on the backing 501. For example, each of the tooth-shaped abrasive particles 504-508 may have at least one of a predetermined lateral position, a predetermined longitudinal position, a predetermined radial position, and/or a predetermined rotational orientation relative to the backing 501 and relative to each other. In a more particular embodiment, each of the tooth-shaped abrasive particles 504-508 may have a combination of two or more of a predetermined lateral position, a predetermined longitudinal position, a predetermined radial position, and/or a predetermined rotational orientation relative to the backing 501 and relative to each other.
According to one aspect, the tooth-shaped abrasive particles 504-508 are disposed on predetermined lateral and longitudinal positions on the backing 501. As illustrated in the non-limiting embodiment of
In accordance with another embodiment, the plurality of abrasive particles 503 on a coated abrasive article can be arranged in a predetermined distribution relative to each other as viewed top-down. A predetermined distribution can be defined by a combination of predetermined positions on a backing that are purposefully selected. In one embodiment, a predetermined distribution can include a pattern, such that the predetermined positions can define a two-dimensional array. In another embodiment, an array may include have short range order defined by a unit of abrasive particles. In yet another aspect, an array may also be a pattern, having long range order including regular and repetitive units linked together, such that the arrangement may be symmetrical and/or predictable. In some instances, an array may have an order that can be predicted by a mathematical formula. It will be appreciated that two-dimensional arrays can be formed in the shape of polygons, ellipsis, ornamental indicia, product indicia, or other designs.
In another aspect, a predetermined distribution can also include a non-shadowing arrangement. For example, a non-shadowing arrangement may include a controlled, non-uniform distribution, a controlled uniform distribution, and a combination thereof. In some non-limiting instances, a non-shadowing arrangement may include a radial pattern, a spiral pattern, a phyllotactic pattern, an asymmetric pattern, a self-avoiding random distribution, a self-avoiding random distribution and a combination thereof. In one embodiment, a non-shadowing arrangement may include a particular arrangement of abrasive particles (i.e., shaped abrasive particles and/or diluent particles) relative to each other, wherein the degree of overlap of the abrasive particles during an initial phase of a material removal operation is not greater than about 25%, such as not greater than about 20%, not greater than about 15%, not greater than about 10%, or even not greater than about 5%. In particular instances, a non-shadowing arrangement may include a distribution of abrasive particles, wherein upon engagement with a workpiece during an initial stage of a material removal operation, a portion (e.g., a minority of all shaped abrasive particles on the backing, a majority of all shaped abrasive particles on the backing, or even essentially all) of the abrasive particles engage a different region of the surface of the workpiece. A non-shadowing arrangement may utilize a particular distribution of shaped abrasive particles relative to each other and relative to a grinding direction and/or one or more axes of the backing.
In one embodiment, the predetermined distribution can be partially, substantially, or fully asymmetric. For example, according to one embodiment, the predetermined distribution can overlie the entire abrasive article, can cover substantially the entire abrasive article (i.e., greater than 50% but less than 100%), overlie multiple portions of the abrasive article, or overlie a fraction of the abrasive article (i.e., less than 50% of the surface area of the article). As used herein, “a phyllotactic pattern” means a pattern related to phyllotaxis. Phyllotaxis is the arrangement of lateral organs such as leaves, flowers, scales, florets, and seeds in many kinds of plants. Many phyllotactic patterns are marked by the naturally occurring phenomenon of conspicuous patterns having arcs, spirals, and whorls. The pattern of seeds in the head of a sunflower is an example of this phenomenon.
According to one embodiment, the first region 710 can include a group of abrasive particles 711 having a generally random rotational orientation with respect to each other. The group of abrasive particles 711 can be arranged in a random distribution relative to each other, such that there is no discernable short-range order or long-range order with regard to the placement of the group of abrasive particles 711. In one embodiment, the group of abrasive particles 711 may be substantially homogenously distributed within the first region 710, such that the formation of clumps (two or more particles in contact with each other) is limited.
In another aspect, the second region 720 can include a group of abrasive particles 721 arranged in a controlled distribution relative to each other. For one embodiment, the group of abrasive particles 721 can have a regular and controlled rotational orientation relative to each other. In another embodiment, the group of shaped abrasive particles 721 can have generally the same rotational orientation as defined by the same rotational angle on the backing of the coated abrasive 701. In one aspect, the group of shaped abrasive particles 721 can be substantially homogenously distributed within the second region 720, such that the formation of clumps (two or more particles in contact with each other) is limited.
According to another aspect, the third region 730 can include a group of abrasive particles 731 and secondary particles 732. In one embodiment, the group of abrasive particles 731 and secondary particles 732 can be arranged in a controlled distribution relative to each other. For example, the group of shaped abrasive particles 731 can have a regular and controlled rotational orientation relative to each other. According to another non-limiting embodiment, the group of shaped abrasive particles 731 can have generally one of two types of rotational orientations on the backing of the coated abrasive 701. In one instance, the group of shaped abrasive particles 731 and secondary particles 732 can be substantially homogenously distributed within the third region 730, such that the formation of clumps (two or more particles in contact with each other) is limited.
For another aspect, a fourth region 740 can include a group of abrasive particles 741 and secondary particles 742 having a generally random distribution with respect to each other. For example, the group of abrasive particles 741 can have a random rotational orientation with respect to each other. In one embodiment, group of abrasive particles 741 and secondary particles 742 can be arranged in a random distribution relative to each other, such that there is no discernable short-range or long-range order. In another embodiment, the group of shaped abrasive particles 741 and the secondary particles 742 can be substantially homogenously distributed within the fourth region 740, such that the formation of clumps (two or more particles in contact with each other) is limited.
The coated abrasive article 700 can include different regions 710, 720, 730, and 740, each of which can include different groups of particles, such as shaped particles and secondary particles. The coated abrasive article 700 is intended to illustrate the different types of groupings, arrangements, and distributions of particles that may be created using the systems and processes of the embodiments herein. The illustration is not intended to be limited to only those groupings of particles and it will be appreciated that coated abrasive articles can be made including only one region as illustrated in
According to one aspect, the plurality of abrasive particles on the coated abrasive may have a particular tilt angle, such as at least 2 degrees, such as at least 5 degrees, at least 10 degrees, at least 15 degrees, at least 20 degrees, at least 25 degrees, at least 30 degrees, at least 35 degrees, at least 40 degrees, at least 45 degrees, at least 50 degrees, at least 55 degrees, at least 60 degrees, at least 70 degrees, at least 80 degrees, or even at least 85 degrees. Still, the tilt angle 136 may be not greater than about 90 degrees, such as not greater than about 85 degrees, not greater than about 80 degrees, not greater than about 75 degrees, not greater than about 70 degrees, not greater than about 65 degrees, not greater than about 60 degrees, such as not greater than about 55 degrees, not greater than about 50 degrees, not greater than about 45 degrees, not greater than about 40 degrees, not greater than about 35 degrees, not greater than about 30 degrees, not greater than about 25 degrees, not greater than about 20 degrees, such as not greater than about 15 degrees, not greater than about 10 degrees, or even not greater than about 5 degrees. It will be appreciated that the tilt angle can be within a range between any of the above minimum and maximum degrees. The tilt angle may be measured using techniques disclosed in US 2019/0160630 incorporated by reference herein in its entirety.
According to one particular aspect, the content of abrasive particles overlying the backing can be controlled based on the intended application. For example, the plurality abrasive particles can be overlying at least 5% of the total surface area of the backing, such as at least 10% or at least 20% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90%. In still another embodiment, the coated abrasive article may be essentially free of silane.
Furthermore, the abrasive articles of the embodiments herein can have a particular content of particles overlying the substrate. In one embodiment, the particles can define an open coat abrasive product having a coating density of particles (i.e., abrasive particles, secondary particles, or both abrasive particles and secondary particles) of not greater than about 70 particles/cm2. In other instances, the density of particles per square centimeter of the abrasive article may be not greater than about 65 particles/cm2, such as not greater than about 60 particles/cm2, not greater than about 55 particles/cm2, or even not greater than about 50 particles/cm2. Still, in one non-limiting embodiment, the density of the open coat coated abrasive can be at least about 5 particles/cm2, or even at least about 10 particles/cm2. It will be appreciated that the density of particles per square centimeter of abrasive article can be within a range between any of the above minimum and maximum values.
In certain instances, the abrasive article can have an open coat density of not greater than about 50% of particles (i.e., abrasive particles or secondary particles or the total of abrasive particles and secondary particles) covering the exterior abrasive surface of the article. In other embodiments, the area of the particles relative to the total area of the surface on which the particles are placed can be not greater than about 40%, such as not greater than about 30%, not greater than about 25%, or even not greater than about 20%. Still, in one non-limiting embodiment, the percentage coating of the particles relative to the total area of the surface can be at least about 5%, such as at least about 10%, at least about 15%, at least about 20%, at least about 25%, at least about 30%, at least about 35%, or even at least about 40%. It will be appreciated that the percent coverage of the particles can be within a range between any of the above minimum and maximum values.
Some abrasive articles may have a particular content of particles (i.e., abrasive particles or secondary particles or the total of abrasive particles and secondary particles) for a given area (e.g., ream, wherein 1 ream=30.66 m2) of the backing. For example, in one embodiment, the abrasive article may utilize a normalized weight of particles of at least about 1 lbs/ream (14.8 grams/m2), such as at least 5 lbs/ream or at least 10 lbs/ream or at least about 15 lbs/ream or at least about 20 lbs/ream or at least about 25 lbs/ream or even at least about 30 lbs/ream. Still, in one non-limiting embodiment, the abrasive article can include a normalized weight of particles of not greater than about 90 lbs/ream (1333.8 grams/m2), such as not greater than 80 lbs/ream or not greater than 70 lbs/ream or not greater than 60 lbs/ream or not greater than about 50 lbs/ream or even not greater than about 45 lbs/ream. It will be appreciated that the abrasive articles of the embodiments herein can utilize a normalized weight of particles within a range between any of the above minimum and maximum values.
In certain instances, the abrasive articles can be used on particular workpieces. A suitable exemplary workpiece can include an inorganic material, an organic material, a natural material, and a combination thereof. According to a particular embodiment, the workpiece can include a metal or metal alloy, such as an iron-based material, a nickel-based material, and the like. In one embodiment, the workpiece can be steel, and more particularly, can consist essentially of stainless steel (e.g., 304 stainless steel).
Many different aspects and embodiments are possible. Some of those aspects and embodiments are described herein. After reading this specification, skilled artisans will appreciate that those aspects and embodiments are only illustrative and do not limit the scope of the present invention. Embodiments may be in accordance with any one or more of the embodiments as listed below.
Embodiment 1. A coated abrasive article comprising:
a substrate; and
a plurality of abrasive particles overlying the substrate, wherein at least 5% of the plurality of abrasive particles are tooth-shaped abrasive particles.
Embodiment 2. A coated abrasive article comprising:
a substrate; and
a plurality of abrasive particles including tooth-shaped abrasive particles, wherein at least 5% of the abrasive particles have a tilt angle greater than 44 degrees.
Embodiment 3. The coated abrasive article of embodiment 2, wherein at least 5% of the plurality of abrasive particles are tooth-shaped abrasive particles.
Embodiment 4. The coated abrasive article of any one of embodiments 1 and 3, wherein at least 6% of the abrasive particles are tooth-shaped abrasive particles or at least 8% or at least 10% or at least 12% or at least 15% or at least 18% or at least 20% or at least 22% or at least 25% or at least 28% or at least 30% or at least 32% or at least 35% or at least 38% or at least 40% or at least 42% or at least 45% or at least 48% or at least 50% or at least 52% or at least 55% or at least 58% or at least 60% or at least 62% or at least 65% or at least 68% or at least 70% or at least 72% or at least 75% or at least 78% or at least 80% or at least 82% or at least 85% or at least 88% or at least 90% or at least 92% or at least 95% or at least 98% or at least 99%.
Embodiment 5. The coated abrasive article of any one of embodiments 1 and 3, wherein the plurality of abrasive particles consists of only tooth-shaped abrasive particles.
Embodiment 6. The coated abrasive article of any one of embodiments 1 and 3, wherein the plurality of abrasive particles comprises a blend including a first portion of abrasive particles and a second portion of abrasive particles, and wherein the tooth-shaped abrasive particles are included in the first portion, the second portion, or both the first portion and second portion.
Embodiment 7. The coated abrasive article of embodiment 1, wherein at least 5% of the abrasive particles have a tilt angle greater than 44 degrees.
Embodiment 8. The coated abrasive article of any one of embodiments 2 and 7, wherein at least 6% of the abrasive particles have a tilt angle greater than 44 degrees or at least 10% or at least 15% or at or at least 20% or at least 25% or at least 30% or at least 35% or at least 40% or at least 45% or at least 50% or at least 55% or at least 60% or at least 65% or at least 70% or at least 75% or at least 80% or at least 85% or at least 90% or at least 95% or at least 99%.
Embodiment 9. The coated abrasive article of any one of embodiments 2 and 7, wherein not greater than 99% of the plurality of abrasive particles have a tilt angle greater than 44 degrees or not greater than 95% or not greater than 90% or not greater than 85%.
Embodiment 10. The coated abrasive article of any one of embodiments 2 and 7, wherein at least 5% of the tooth-shaped abrasive particles have a tilt angle greater than 44 degrees or at least 10% or at least 15% or at or at least 20% or at least 25% or at least 30% or at least 35% or at least 40% or at least 45% or at least 50% or at least 55% or at least 60% or at least 65% or at least 70% or at least 75% or at least 80% or at least 85% or at least 90% or at least 95% or at least 99%.
Embodiment 11. The coated abrasive article of any one of embodiments 2 and 7, wherein not greater than 99% of the tooth-shaped abrasive particles have a title angle greater than 44 degrees or not greater than 95% or not greater than 90% or not greater than 85%.
Embodiment 12. The coated abrasive article of any one of embodiments 1 and 2, wherein the plurality of abrasive particles includes at least 10 grams of abrasive particles or at least 100 grams of abrasive particles or at least 500 grams of abrasive particles or at least 1 kg of abrasive particles or at least 10 kg of abrasive particles.
Embodiment 13. The coated abrasive article of any one of embodiments 1 and 2, wherein the plurality of abrasive particles includes at least 10 abrasive particles or at least 20 abrasive particles or at least 30 abrasive particles or at least 50 abrasive particles or at least 100 abrasive particles or at least 500 abrasive particles.
Embodiment 14. The coated abrasive article of any one of embodiments 1 and 2, wherein each of the tooth-shaped abrasive particles comprises a body having a length, a width, and a thickness, wherein length>width≥thickness.
Embodiment 15. The coated abrasive article of any one of embodiments 1 and 2, wherein the tooth-shaped abrasive particles comprises a body including a tip region including a tip of the body, a base region including a base of the body, wherein the base region is at an opposite end of the body from the tip region along a length of the body.
Embodiment 16. The coated abrasive article of embodiment 15, wherein the tip is defined by a convergence of at least 2 surfaces of the body or a convergence of at least 3 surfaces of the body or a convergence of at least 4 surfaces of the body.
Embodiment 17. The coated abrasive article of embodiment 15, wherein the tip comprises a tip edge defined by a convergence of at least 3 surfaces of the body or by a convergence of at least 4 surfaces of the body.
Embodiment 18. The coated abrasive article of embodiment 15, wherein the tip edge defines a wedge shape defined by a convergence of side surfaces in the dimension of the width of the particle, wherein a tip edge length is substantially similar to a thickness of the body.
Embodiment 19. The coated abrasive article of embodiment 18, wherein the tip edge length is not greater than 99% of the average thickness of the body or not greater than 95% or not greater than 90% or not greater than 85% or not greater than 80% or not greater than 75% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% of the average thickness of the body.
Embodiment 20. The coated abrasive article of embodiment 18, wherein the tip edge length is at least 20% of the average thickness of the body or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90% or at least 95%.
Embodiment 21. The coated abrasive article of embodiment 15, wherein the tip includes a tip edge having a tip edge length that is less than an average width of the body.
Embodiment 22. The plurality of abrasive particles of embodiment 21, wherein the tip edge length is not greater than 99% of the average width of the body or not greater than 95% or not greater than 90% or not greater than 85% or not greater than 80% or not greater than 75% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% of the average width.
Embodiment 23. The plurality of abrasive particles of embodiment 22, wherein the tip edge length is at least 20% of the average width of the body or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90% or at least 95%.
Embodiment 24. The coated abrasive article of embodiment 15, wherein the tip includes a tip edge having a length substantially similar to the average width of the body.
Embodiment 25. The coated abrasive article of embodiment 15, wherein the tip region is defined by a taper including a reduction in the width of the body over a tip region length.
Embodiment 26. The coated abrasive article of embodiment 15, wherein the tip region is defined by a taper including a reduction in the width and thickness of the body over a tip region length.
Embodiment 27. The coated abrasive article of embodiment 15, wherein the tip region is defined by a taper including a change in the width of the body that is greater than a change in the thickness of the body in the tip region.
Embodiment 28. The coated abrasive article of embodiment 15, wherein the tip region is defined by a taper including a change in the width of the body and wherein the thickness is substantially the same throughout the length of the tip region.
Embodiment 29. The coated abrasive article of embodiment 15, wherein the tip region has a tip region length (Ltr) that is not greater than 90% of a total length of the body or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20% or not greater than 10% or not greater than 5% of the total average length of the body.
Embodiment 30. The coated abrasive article of embodiment 15, wherein the tip region has a tip region length (Ltr) of at least 5% of a total length of the body or at least 10% or at least 15% or at least 20% or at least 25% or at least 30% or at least 40%.
Embodiment 31. The coated abrasive article of embodiment 15, wherein the tip region comprises an asymmetric taper including a first surface and a second surface, wherein the first surface has a different contour as compared to the second surface.
Embodiment 32. The coated abrasive article of embodiment 31, wherein the first surface has a greater curvature compared to the second surface.
Embodiment 33. The coated abrasive article of embodiment 31, wherein the second surface is substantially linear and the first surface is angled in a non-parallel relationship relative to the second surface.
Embodiment 34. The coated abrasive article of embodiment 31, wherein the first surface and second surface converge at the tip.
Embodiment 35. The coated abrasive article of embodiment 31, wherein the first surface is longer than the second surface.
Embodiment 36. The coated abrasive article of embodiment 15, wherein the base comprises a projection extending from the body, wherein the projection extends at a base angle relative to a longitudinal axis of the body, wherein the base region includes a base angle of at least 91 degrees and not greater than 180 degrees.
Embodiment 37. The coated abrasive article of embodiment 33, wherein the projection has a length (Lp) that is not greater than 90% of a total average length (L) of the body or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20% or not greater than 10% or not greater than 5% of the total average length (L) of the body.
Embodiment 38. The coated abrasive article of embodiment 37, wherein the projection has a length (Lp) that is at least 1% of a total average length (L) of the body or at least 3% or at least 5% or at least 8% or at least 10% or at least 15% of the total average length (L) of the body.
Embodiment 39. The coated abrasive article of embodiment 33, wherein the projection has a base surface including upper corner and a lower corner spaced apart from the upper corner across the length of the base surface.
Embodiment 40. The coated abrasive article of embodiment 39, wherein the upper corner or the lower corner comprises a corner radius less than a corner radius of the tip.
Embodiment 41. The coated abrasive article of embodiment 37, wherein the projection extends at an obtuse base angle.
Embodiment 42. The coated abrasive article of embodiment 41, wherein the projection extends at a base angle of at least 91 degrees or at least 92 degrees or at least 93 degrees or at least 94 degrees or at least 95 degrees or at least 97 degrees or at least 99 degrees or at least 105 degrees or at least 110 degrees or at least 120 degrees or at least 130 degrees or at least 140 degrees.
Embodiment 43. The coated abrasive article of embodiment 42, wherein the projection extends at a base angle of not greater than 178 degrees or not greater than 170 degrees or not greater than 160 degrees or not greater than 150 degrees.
Embodiment 44. The coated abrasive article of embodiment 15, wherein the base region comprises a base including a base surface, wherein the base surface is angled relative to the longitudinal axis of the body.
Embodiment 45. The coated abrasive article of embodiment 44, wherein the base surface is angled at an acute angle relative to the longitudinal axis of the body.
Embodiment 46. The coated abrasive article of embodiment 44, wherein the base surface is angled at not greater than 90 degrees relative to the longitudinal axis of the body or not greater than 88 degrees or not greater than 86 degrees or not greater than 84 degrees or not greater than 82 degrees or not greater than 80 degrees or not greater than 75 degrees or not greater than 70 degrees or not greater than 65 degrees or not greater than 60 degrees or not greater than 55 degrees or not greater than 50 degrees or not greater than 45 degrees or not greater than 40 degrees.
Embodiment 47. The coated abrasive article of embodiment 46, wherein the base surface is angled at an angle of at least 5 degrees relative to the longitudinal axis of the body or at least 10 degrees or at least 15 degrees or at least 20 degrees or at least 25 degrees or at least 30 degrees or at least 35 degrees or at least 40 degrees or at least 45 degrees or at least 50 degrees or at least 55 degrees.
Embodiment 48. The coated abrasive article of embodiment 15, wherein the base comprises a base surface including peaks and valleys.
Embodiment 49. The coated abrasive article of embodiment 48, wherein the arrangement of peaks and valleys is a random arrangement of peaks and valleys.
Embodiment 50. The coated abrasive article of embodiment 15, wherein the base comprises a base surface having a surface roughness greater than a surface roughness of a side surface of the body in an elongated region or the tip region.
Embodiment 51. The coated abrasive article of embodiment 15, wherein the base comprises a base surface having a plurality of peaks, wherein at least one peak of the plurality of peaks has a tip radius less than a tip radius of the tip of the body.
Embodiment 52. The coated abrasive article of embodiment 51, wherein at least 2 different peaks of the plurality of peaks each have a tip radius less than a tip radius of the tip of the body.
Embodiment 53. The coated abrasive article of embodiment 15, wherein the base comprises a primary peak as viewed in two dimensions define by the length and the width, wherein the primary peak comprises a primary peak angle of at least 45 degrees and not greater than 150 degrees.
Embodiment 54. The coated abrasive article of embodiment 53, wherein the primary peak angle is at least 50 degrees or at least 55 or at least 60 degrees or at least 65 degrees or at least 70 degrees or at least 75 degrees or at least 80 degrees or at least 85 degrees or at least 90 degrees or at least 95 degrees or at least 100 degrees.
Embodiment 55. The coated abrasive article of embodiment 54, wherein the primary peak angle is not greater than 145 degrees or not greater than 140 degrees or not greater than 135 degrees or not greater than 130 degrees or not greater than 125 degrees or not greater than 120 degrees or not greater than 115 degrees or not greater than 110 degrees or not greater than 100 degrees or not greater than 95 degrees.
Embodiment 56. The coated abrasive article of embodiment 15, wherein the base surface is defined by one or more facets having a substantially planar surface extending toward a primary peak of the base surface.
Embodiment 57. The coated abrasive article of embodiment 15, wherein the base surface comprises at least two facets that are abutting each other and define a common edge extending between the two facets.
Embodiment 58. The coated abrasive article of embodiment 15, wherein the base includes a first peak and a second peak separated from each other by a first valley as viewed in two-dimensions by a plane defined by the length and thickness of the body or in two-dimensions by a plane defined by the length and width of the body.
Embodiment 59. The coated abrasive article of embodiment 15, wherein the base comprises a primary peak as viewed in two dimensions define by the length and the width, wherein the primary peak comprises a tip sharpness that is greater than a tip sharpness of the tip of the body.
Embodiment 60. The coated abrasive article of embodiment 59, wherein a primary peak angle, as measured in two-dimensions defined by a plane of the length and width of the body, is at least 5% less than a tip angle of the tip of the body, as measured by a tip angle in two-dimensions defined by the plane of the length and width of the body or at least 8% or at least 10% or at least 12% or at least 15% or at least 20% or at least 25% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90%.
Embodiment 61. The coated abrasive article of embodiment 15, further comprising an elongated region extending between the tip region and the base region.
Embodiment 62. The coated abrasive article of embodiment 61, wherein the elongated region defines a region between the tip region and the base region having a substantially constant width.
Embodiment 63. The coated abrasive article of embodiment 61, wherein the elongated region defines a region between the tip region and the base region having a substantially constant thickness.
Embodiment 64. The coated abrasive article of embodiment 61, wherein the elongated region defines a region having a change in width or thickness of not greater than 10% over the length of the elongated region or not greater than 8% or not greater than 5% or not greater than 3%.
Embodiment 65. The coated abrasive article of embodiment 15, wherein the body is linear for at least a majority of a total length of the body.
Embodiment 66. The coated abrasive article of embodiment 15, wherein the body comprises striations on at least one surface.
Embodiment 67. The coated abrasive article of embodiment 66, wherein the striations extend in a direction of the length of the body.
Embodiment 68. The coated abrasive article of any one of embodiments 1 and 2, further comprising not greater than 50% of agglomerated particles for a total count of particles in the plurality of abrasive particles or not greater than 48% or not greater than 46% or not greater than 44% or not greater than 42% or not greater than 40% or not greater than 38% or not greater than 36% or not greater than 34% or not greater than 32% or not greater than 30% or not greater than 28% or not greater than 26% or not greater than 24% or not greater than 22% or not greater than 20% or not greater than 18% or not greater than 16% or not greater than 14% or not greater than 12% or not greater than 10% or not greater than 8% or not greater than 6% or not greater than 4% or not greater than 2%, wherein the plurality of abrasive particles is free of agglomerated particles.
Embodiment 69. The coated abrasive article of any one of embodiments 1 and 2, wherein each of the tooth-shaped abrasive particles comprise a ceramic material.
Embodiment 70. The coated abrasive article of embodiment 69, wherein the ceramic material is selected from the group consisting of oxides, carbides, nitrides, borides, diamond, or any combination thereof.
Embodiment 71. The coated abrasive article of embodiment 69, wherein the ceramic material includes a majority content of alpha alumina.
Embodiment 72. The coated abrasive article of embodiment 69, wherein the ceramic material includes at least 90 vol % alpha alumina for a total volume of each body of the tooth-shaped abrasive particles.
Embodiment 73. The coated abrasive article of embodiment 69, wherein each of the tooth-shaped abrasive particles are free of a binder material or organic material.
Embodiment 74. The coated abrasive article of any one of embodiments 1 and 2, wherein the plurality of abrasive particles have a predetermined position relative to each other.
Embodiment 75. The coated abrasive article of embodiment 74, wherein the plurality of abrasive particles have a predetermined lateral position, a predetermined longitudinal position, a predetermined radial position, a predetermined rotational orientation, or any combination thereof.
Embodiment 76. The coated abrasive article of any one of embodiments 1 and 2, wherein the plurality of abrasive particles comprises not greater than 60% hook-shaped particles for a total number of abrasive particles in the plurality of abrasive particles or not greater than 58% or not greater than 56% or not greater than 54% or not greater than 52% or not greater than 50% or not greater than 48% or not greater than 46% or not greater than 44% or not greater than 42% or not greater than 40% or not greater than 38% or not greater than 36% or not greater than 34% or not greater than 32% or not greater than 30% or not greater than 28% or not greater than 26% or not greater than 24% or not greater than 22% or not greater than 20% or not greater than 18% or not greater than 16% or not greater than 14% or not greater than 12% or not greater than 10% or not greater than 8% or not greater than 6% or not greater than 4% or not greater than 2%, wherein the plurality of abrasive particles is free of hook shaped particles.
Embodiment 77. The coated abrasive article of any one of embodiments 1 and 2, wherein the plurality of abrasive particles is distributed over the substrate in a predetermined distribution.
Embodiment 78. The coated abrasive article of any one of embodiments 1 and 2, wherein the plurality of abrasive particles has a random rotational orientation.
Embodiment 79. The coated abrasive article of any one of embodiments 1 and 2, wherein the plurality of abrasive particles is arranged in a two-dimensional array.
Embodiment 80. The coated abrasive article of any of the preceding embodiments, wherein each body of each shaped abrasive particle of the plurality of shaped abrasive particles comprises a cross-sectional shape selected from the group consisting of a regular polygon, an irregular polygon, an ellipse, a circle or any combination thereof.
Tooth-shaped abrasive particles were made according to the following conditions. A mixture was created including approximately 48-55 wt % boehmite, which was obtained from Sasol Corporation. One suitable type of commercially available boehmite is Disperal. The boehmite was mixed and seeded with 1% alpha alumina seeds relative to the total alumina content of the mixture. The alpha alumina seeds were made by milling of corundum using conventional techniques, described for example in U.S. Pat. No. 4,623,364. The mixture also included 45-52 wt % water and 2.5-7 wt % additional nitric acid. The ingredients were mixed in a planetary mixer of conventional design and mixed under reduced pressure to remove gaseous elements from the mixture (e.g., bubbles). The coil value was approximately 1000-1500 N.
After gelling, the mixture was extruded into and through cavities of a production tool. The extrusion rate and translation rate of the production tool were finely controlled to facilitate formation of a batch of abrasive particles having a high content of tooth-shaped abrasive particles (e.g., above 65% of all total particles). Sieving and sorting techniques were further used to increase the percentage of tooth-shaped abrasive particles in the batch. The cavities of the production tool had a quadrilateral shape having a side length of 0.5 mm. The gel mixture was extruded through the cavities of the production tool and dried for approximately 8-30 minutes before being removed from the cavities by contact by a brush on the back-side of the production tool. The precursor shaped abrasive particles were sintered between 1300-1350° C. for approximately 10 minutes.
Exemplary tooth-shaped abrasive particles formed according to Example 1 and are provided in the image of
The particles from Example 1 (Sample S1) were tested according to a single grit grinding test (SGGT) in two different orientations: 1) a tip region up orientation wherein the tip was initiating the grinding of the workpiece; and 2) a base region up orientation wherein the base was initiating the grinding of the workpiece. In conducting the SGGT, one single abrasive particle is held in a grit holder by a bonding material of epoxy. The abrasive particle is secured in the desired orientation (i.e., tip region up orientation or base region up orientation) and moved across a workpiece of 304 stainless steel for a scratch length of 8 inches using a wheel speed of 22 m/s and an initial scratch depth of 30 microns. The abrasive particle produces a groove in the workpiece having a cross-sectional area. For each sample set, each shaped abrasive particle completes 15 passes across the 8 inch length, 10 individual particles are tested for each of the orientation and the results are analyzed. The test measures the forces exerted by the grit on the workpiece. The tangential force (Ft) is in the direction that is parallel to the surface of the workpiece and the direction of the groove. The normal force (Fn) perpendicular to the surface of the workpiece is also measured. The combination of manual touch-off by infeeding a spinning grain slowly at micron intervals and net change in the measured cross-sectional area of the groove from beginning to the end of the scratch length is used to determine the shaped abrasive particle wear. The net change in the cross-sectional area of the groove for each pass can be measured. For the SGGT, the net cross-sectional area of the groove (A) defined as the difference between the cross-sectional area of the groove below the surface and the cross-sectional area of the material displaced above the surface. Performance (Ft/A or Fn/A) is defined as the ratio of the tangential or normal force to the net cross-sectional area of the groove.
The SGGT is conducted using two different orientations of the abrasive particles relative to the workpiece as described above. The SGGT is conducted with a first sample set of abrasive particles in a first orientation (e.g., tip region up orientation for tooth-shaped abrasive particles). The SGGT is also conducted with a second sample set of abrasive particles in a second orientation ((e.g., tip region up orientation for tooth-shaped abrasive particles).
The above-disclosed subject matter is to be considered illustrative, and not restrictive, and the appended claims are intended to cover all such modifications, enhancements, and other embodiments, which fall within the true scope of the present invention. Thus, to the maximum extent allowed by law, the scope of the present invention is to be determined by the broadest permissible interpretation of the following claims and their equivalents, and shall not be restricted or limited by the foregoing detailed description.
The Abstract of the Disclosure is provided to comply with Patent Law and is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims. In addition, in the foregoing Detailed Description, various features may be grouped together or described in a single embodiment for the purpose of streamlining the disclosure. This disclosure is not to be interpreted as reflecting an intention that the claimed embodiments require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive subject matter may be directed to less than all features of any of the disclosed embodiments. Thus, the following claims are incorporated into the Detailed Description, with each claim standing on its own as defining separately claimed subject matter.
This application claims priority under 35 U.S.C. § 119(e) to U.S. Provisional Patent Application No. 62/954,270, filed Dec. 27, 2019, by Samuel S. MARLIN, et al., entitled “ABRASIVE ARTICLES AND METHODS OF FORMING SAME,” which is assigned to the current assignee hereof and incorporated herein by reference in its entirety for all purposes.