20210024798
The following is directed to abrasive particles, and more particularly, to abrasive particles having certain features and methods of forming such abrasive particles.
Abrasive articles incorporating abrasive particles are useful for various material removal operations including grinding, finishing, polishing, and the like. Depending upon the type of abrasive material, such abrasive particles can be useful in shaping or grinding various materials in the manufacturing of goods. Certain types of abrasive particles have been formulated to date that have particular geometries, such as triangular abrasive particles and abrasive articles incorporating such objects. See, for example, U.S. Pat. Nos. 5,201,916; 5,366,523; and 5,984,988.
Previously, three basic technologies that have been employed to produce abrasive particles having a specified shape, which are fusion, sintering, and chemical ceramic. In the fusion process, abrasive particles can be shaped by a chill roll, the face of which may or may not be engraved, a mold into which molten material is poured, or a heat sink material immersed in an aluminum oxide melt. See, for example, U.S. Pat. No. 3,377,660. In sintering processes, abrasive particles can be formed from refractory powders having a particle size of up to 10 micrometers in diameter. Binders can be added to the powders along with a lubricant and a suitable solvent to form a mixture that can be shaped into platelets or rods of various lengths and diameters. See, for example, U.S. Pat. No. 3,079,242. Chemical ceramic technology involves converting a colloidal dispersion or hydrosol (sometimes called a sol) to a gel or any other physical state that restrains the mobility of the components, drying, and firing to obtain a ceramic material. See, for example, U.S. Pat. Nos. 4,744,802 and 4,848,041. Other relevant disclosures on abrasive particles and associated methods of forming and abrasive articles incorporating such particles are available at: http://www.abel-ip.com/publications/.
The industry continues to demand improved abrasive materials and abrasive articles.
According to one aspect, an abrasive particle includes a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the side surface comprises a Mean Anisotropy Factor of at least 1.25.
According to another aspect, an abrasive particle includes a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the first major surface comprises a first protrusion disposed abutting the first side surface portion and extending along at least a portion of the first side surface portion, and further comprising an untextured region extending through a central region of the body, wherein the untextured region defines a majority of a total surface area of the first major surface.
In yet another aspect, an abrasive particle includes a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein a majority of the side surface comprises a plurality of microridges.
According to yet another aspect, a collection of abrasive particles includes a first abrasive particle comprising a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the body of the first abrasive particle comprises a first two-dimensional shape, and wherein the first major surface comprises a first protrusion abutting and extending along at least a portion of a first side surface portion of the side surface, and wherein the body further comprises an untextured region extending through a central region of the body, wherein the untextured region defines a majority of a total surface area of the first major surface, and further including a second abrasive particle comprising a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the body of the second abrasive particle comprises a two-dimensional shape that is different compared to the two-dimensional shape of the first abrasive particle.
In yet another aspect, a collection of abrasive particles comprises abrasive particles, wherein each particle of the collection of abrasive particles includes a body having a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface; and wherein a majority of the particles of the collection of abrasive particles comprises a plurality of microridges extending along at least a portion of the sides surface.
According to still another aspect, a collection of abrasive particles comprises abrasive particles, wherein a particle of the collection of abrasive particles includes a body having a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, and wherein the side surface includes a plurality of side surface portions extending between external corners of the body and wherein at least 45% of the side surface portions of the body include a plurality of microridges.
One aspect includes a collection of abrasive particles, wherein each abrasive particle of the collection of abrasive particles including a body having a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the first major surface and second major surface are substantially parallel with each other; and wherein the collection of abrasive particles comprises a Mean Non-Convexity Factor of at least 3.5 and a Non-Convexity Factor Standard Deviation of at least 2.4.
Another aspect includes a collection of abrasive particles, wherein each abrasive particle of the collection of abrasive particles comprises a body having a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, and wherein the collection of abrasive particles comprises a Mean Anisotropy Factor of at least 1.25.
And yet another aspect includes a collection of abrasive particles, wherein each abrasive particle of the collection of abrasive particles comprises a body having a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the body comprises a height as defined as the distance along the side surface between the first major surface and the second major surface wherein the collection of abrasive particles comprises a standard deviation of height of not greater than 100 microns, and wherein the collection of abrasive particles comprises a Mean Non-Convexity Factor of at least 3.5.
The present disclosure may be better understood, and its numerous features and advantages made apparent to those skilled in the art by referencing the accompanying drawings.
The following is directed to methods of forming abrasive particles and features of such abrasive particles. The abrasive particles may be used in various abrasive articles, including for example bonded abrasive articles, coated abrasive articles, and the like. Alternatively, the abrasive particles of the embodiments herein may be utilized in free abrasive technologies, including for example grinding and/or polishing slurries.
The mixture 101 can be formed to have a particular content of solid material, such as the ceramic powder material. For example, in one embodiment, the mixture 101 can have a solids content within a range of at least 25 wt % and not greater than 75 wt % for the total weight of the mixture 101.
According to one embodiment, the ceramic powder material can include an oxide, a nitride, a carbide, a boride, an oxycarbide, an oxynitride, and a combination thereof. In particular instances, the ceramic material can include alumina. More specifically, the ceramic material may include a boehmite material, which may be a precursor of alpha alumina. The term “boehmite” is generally used herein to denote alumina hydrates including mineral boehmite, typically being Al2O3•H2O and having a water content on the order of 15%, as well as pseudoboehmite, having a water content higher than 15%, such as 20-38% by weight. It is noted that boehmite (including pseudoboehmite) has a particular and identifiable crystal structure, and accordingly unique X-ray diffraction pattern, and as such, is distinguished from other aluminous materials including other hydrated aluminas such as ATH (aluminum trihydroxide) a common precursor material used herein for the fabrication of boehmite particulate materials.
Furthermore, the mixture 101 can be formed to have a particular content of liquid material. Some suitable liquids may include organic materials. Other suitable materials can include water. In accordance with one embodiment, the mixture 101 can be formed to have a liquid content less than the solids content of the mixture 101. In more particular instances, the mixture 101 can have a liquid content within a range of at least about 25 wt % and not greater than 75 wt % for the total weight of the mixture 101. The water content of the mixture 101 may be controlled to facilitate suitable drying upon shrinkage, which may assist with the formation of abrasive particles according to the embodiments herein.
Furthermore, to facilitate processing and forming abrasive particles according to embodiments herein, the mixture 101 can have a particular storage modulus. For example, the mixture 101 can have a storage modulus within a range of at least about 1×104 Pa and not greater than about 1×107 Pa. The storage modulus can be measured via a parallel plate system using ARES or AR-G2 rotational rheometers, with Peltier plate temperature control systems. For testing, the mixture 101 can be extruded within a gap between two plates that are set to be approximately 8 mm apart from each other. After extruding the gel into the gap, the distance between the two plates defining the gap is reduced to 2 mm until the mixture 101 completely fills the gap between the plates. After wiping away excess mixture, the gap is decreased by 0.1 mm and the test is initiated. The test is an oscillation strain sweep test conducted with instrument settings of a strain range between 0.1% to 100%, at 6.28 rad·s−1 (1 Hz), using 25-mm parallel plate and recording 10 points per decade. Within 1 hour after the test completes, the gap is lowered again by 0.1 mm and the test is repeated. The test can be repeated at least 6 times. The first test may differ from the second and third tests. Only the results from the second and third tests for each specimen should be reported. The viscosity can be calculated by dividing the storage modulus value by 6.28 s−1.
Furthermore, to facilitate processing and forming abrasive particles according to embodiments herein, the mixture 101 can have a particular viscosity, which may facilitate later processing (e.g., modification) and formation of the desired abrasive particles. For example, the mixture 101 can have a viscosity of at least about 4×103 Pa·s, at least about 5×103 Pa·s, at least about 6×103 Pa·s, at least about 8×103 Pa·s, at least about 10×103 Pa·s, at least about 20×103 Pa·s, at least about 30×103 Pa·s, at least about 40×103 Pa·s, at least about 50×103 Pa·s, at least about 60×103 Pa·s, or even at least about 65×103 Pa·s. In at least one non-limiting embodiment, the mixture 101 may have a viscosity of not greater than about 1×106 Pa·s, not greater than about 5×105 Pa·s, not greater than about 3×105 Pa·s, or even not greater than about 2×105 Pa·s. It will be appreciated that the viscosity of the mixture 101 can be within a range between any of the minimum and maximum values noted above.
Moreover, the mixture 101 can be formed to have a particular content of organic materials, including for example, organic additives that can be distinct from the liquid, to facilitate processing and formation of abrasive particles according to the embodiments herein. Some suitable organic additives can include stabilizers, plasticizers, surfactants, binders, such as fructose, sucrose, lactose, glucose, UV curable resins, and the like.
The embodiments herein may utilize a mixture 101 having a particular content of organic additives. For example, the content of organic materials within the mixture 101, particularly, any of the organic additives noted above may be a minor amount as compared to other components within the mixture 101. In at least one embodiment, the mixture 101 can have not greater than about 30 wt % organic material for the total weight of the mixture 101. In other instances, the amount of organic materials may be less, such as not greater than about 15 wt %, not greater than about 10 wt %, or even not greater than about 5 wt %. Still, in at least one non-limiting embodiment, the amount of organic materials within the mixture 101 can be at least about 0.1 wt %, such as at least about 0.5 wt % for the total weight of the mixture 101. It will be appreciated that the amount of organic materials in the mixture 101 can be within a range between any of the minimum and maximum values noted above.
Moreover, the mixture 101 can be formed to have a particular content of acid and/or base to facilitate processing and formation of abrasive particles according to the embodiments herein. Some suitable acids or bases can include nitric acid, sulfuric acid, citric acid, chloric acid, tartaric acid, phosphoric acid, ammonium nitrate, ammonium citrate. According to one particular embodiment, the mixture 101 can have a pH of less than about 5, and more particularly, within a range between about 2 and about 4, using a nitric acid additive.
The process of forming the abrasive particles can include forming the mixture 101 into a body. Referencing
In certain systems, the die 103 can include a die opening 105 having a particular shape. It will be appreciated that the die opening 105 may be shaped to impart a particular shape to the mixture 101 and the resulting body 111. Furthermore, the mixture 101 extruded through the die opening 105 and the resulting body 111 can have essentially the same cross-sectional shape as the die opening 105. In accordance with an embodiment, the die opening 105 can have a rectangular shape. In still other embodiments, the die opening 105 can be shaped to create certain features in one or more surfaces of the body 111 as the mixture exits the die 103. The features can include a controlled distribution of features. Thus in certain instances, extrusion of the mixture 101 from the die 103 and modification of the body 111 can happen simultaneously. That is, the mixture 101 can exit the die 103 and be formed into a body 111 having certain features in one or more surfaces, such that the during forming of the body 111, the body 111 is also modified to include one or more features in one or more surfaces of the body 111.
As further illustrated in
According to one particular embodiment, the belt 109 can be formed to have a film overlying a substrate, wherein the film can be a discrete and separate layer of material configured to facilitate processing and forming of abrasive particles. The process can include providing the mixture 101 directly onto the film of the belt to form the body 111. In certain instances, the film can include a polymer material, such as polyester. In at least one particular embodiment, the film can consist essentially of polyester.
In still another embodiment, the upper surface of the belt 109 can have a particular roughness, which may facilitate formation of the abrasive particles according to the embodiments herein. For example, the roughness of the surface of the belt 109 may impact the manner in which the body 111 is dried and may facilitate controlled cracking of the body 111. Various materials can be used for the belt 109 or as a coating on the surface of the belt 109. Some suitable materials can include inorganic materials, such as metal, metal alloys, ceramics, polycrystalline materials, amorphous phase materials, monocrystalline materials, or any combination thereof. In another embodiment, the belt 109 or upper surface of the belt 109 can include an organic material, such as a polymer, which may include materials such as epoxies, resins, thermosets, thermoplastics, polyimides, polyamides, and a combination thereof. It will be appreciated that the upper surface of the belt 109 may include one or more features, which are described in embodiments herein, which may be used to form a distribution of features in a portion of the body 111, such as the portion of the body 111 in contact with the upper surface of the belt 109 having such features. For example, aspects of the belt 109, such as surface roughness, material of the belt and the like, may be tailored to the specific aspects of the body 111 and the forming process to facilitate suitable formation of abrasive particles as described in embodiment herein.
In some embodiments, the belt 109 can be translated while moving the mixture 101 through the die opening 105. As illustrated in the system 100, the mixture 101 may be extruded in a direction 191. The direction of translation 110 of the belt 109 can be angled relative to the direction of extrusion 191 of the mixture. While the angle between the direction of translation 110 and the direction of extrusion 191 are illustrated as substantially orthogonal in the system 100, other angles are contemplated, including for example, an acute angle or an obtuse angle. Moreover, while the mixture 101 is illustrated as being extruded in a direction 191, which is angled relative to the direction of translation 110 of the belt 109, in an alternative embodiment, the belt 109 and mixture 101 may be extruded in substantially the same direction.
The belt 109 may be translated at a particular rate to facilitate processing. For certain processes according to embodiments herein, the rate of translation of the belt 109 as compared to the rate of extrusion of the mixture 101 in the direction 191 may be controlled to facilitate proper processing. For example, the rate of translation of the belt 109 can be essentially the same as the rate of extrusion to ensure formation of a suitable body 111.
For certain embodiments, the mixture 101 may be extruded to form a body 111 in the form of a body 111 having a generally rectangular cross-sectional shape as viewed in a plane defined by a height and width of the body 111. While the body 111 is illustrated as a sheet, it will be appreciated that the process is not so limited and the mixture can be formed into a body having any desired shape.
The process of forming the body 111 from the mixture 101 can include control of particular features and process parameters to facilitate suitable formation of abrasive particles having one or more features as provided in the embodiments herein. For example, in certain instances, the process of forming a body 111 from the mixture 101 can include forming a body 111 having a particular height. Moreover, it is noted that the height 181 of the body 111 can be controlled by varying a distance between the die 103 and the surface of the belt 109. Alternatively, the process may use a doctor blade or similar technique to control the height 181 of the body 111. Additionally, forming the mixture 101 into the body 111 can include controlling the dimensions of the body 111 based in part upon the viscosity of the mixture 101. In at least one embodiment, the body 111 is formed into a large layer of material having a first major surface having a major surface area of at least 10 cm2, such as at least 20 cm2 or at least 50 cm2 or at least 100 cm2 or at least 500 cm2 or at least 1 m2. Notably, the process of forming the body 111 may be conducted without the use of a mold or other production tool to form a plurality of individual and discrete portions of gel contained within openings of a production tool.
Furthermore, to facilitate processing and forming abrasive particles according to embodiments herein, the body 111, can have a particular viscosity, which can have any of the values noted above for the viscosity of the mixture 101.
The body 111 can have particular dimensions, including for example, a length (l), a width (w), and a height (h). In accordance with an embodiment, the body 111 may have a length that extends in the direction of the translating belt 109, which can be greater than the width, wherein the width of the body 111 is a dimension extending in a direction perpendicular to the length of the belt 109 and to the length of the sheet. The body 111 can have a height 181, wherein the length and width are greater than the height 181 of the body 111. As such, according to one embodiment, the length>width>height.
Notably, the height 181 of the body 111 can be the dimension extending vertically from the surface of the belt 109. In accordance with an embodiment, the body 111 can be formed to have a particular dimension of height 181, wherein the height may be an average height of the body 111 derived from multiple measurements. For example, the height 181 of the body 111 can be at least about 0.1 mm, such as at least about 0.5 mm. In other instances, the height 181 of the body 111 can be greater, such as at least about 0.8 mm, at least about 1 mm, at least about 1.2 mm, at least about 1.6 mm, or even at least about 2 mm. Still, in one non-limiting embodiment, the height 181 of the body 111 may be not greater than about 10 mm, not greater than about 5 mm, or even not greater than about 2 mm. It will be appreciated that the body 111 may have an average height within a range between any of the minimum and maximum values noted above.
After extruding the mixture 101 from the die 103, the body 111 may be translated in a direction 112 along the surface of the belt 109. Translation of the body 111 along the belt 109 may facilitate further processing. For example, after forming the body 111, the body 111 may be translated to a modification zone 120, wherein at least a portion of the body 111 is modified. The process of modifying the body 111 can include using one or more processes that can facilitate changing the stress generation within the body 111 during further processing. For example, the process of modifying the body 111 can include modifying portions of the body 111, such that upon further processing (e.g., drying), the portions of the body 111 associated with the modification can be regions of higher stress concentrations compared to those regions that are not modified, such that fracturing of the body may be more likely in the regions of higher stress concentrations, thus facilitating forming shaped precursor particles. For example, the process of modifying the body 111 may locally alter the stress generation in the body 111 during drying. In one embodiment, the process of modifying can include deforming at least a portion of the body 111. Modification of the body 111 may facilitate the formation of at least one crack initiation point in the body 111, such that during later processing (e.g., drying), the initial position of a crack or defect and the direction of crack propagation within the body 111 can be controlled. In one embodiment, the process of modifying the body 111 can include changing a physical feature of the body 111, such as an alteration of one or more surfaces and/or dimensions of the body 111.
In yet another embodiment, modifying at least portion of the body 111 can include changing a chemical composition of at least a portion of the body 111. In certain instances, modifying the body 111 can include changing a rheological property of the body 111. In certain instances, the process of modifying the body 111 can include applying or providing at least one additive to at least a portion of the body 111, such that the additive may chemically and/or physically alter the body 111. The additive may facilitate a change in the body that leads to regions of higher stress concentrations during further processing, which can facilitate controlled fracturing of the body 111. Such modifications may facilitate changing the stress within the body 111, such that of the body 111 includes regions of higher stress relative to other regions within the body 111 having a lower stress. The distribution of the regions of higher stress and lower stress may be controlled by controlling one or more parameters associated with the modification process, including but not limited to, the control of the distribution of features formed in the body, control of the distribution of one or more additives within the body, and the like. Notably, when the process of modifying the body 111 is combined with other processes (e.g., certain drying conditions) it may facilitate formation of abrasive particles having the features described herein.
The process of modification and drying may have one or more parameters that can be controlled and facilitate the formation of various types of abrasive particles. For example, certain parameters that may influence the characteristics of the finally-formed abrasive particles can include, but are not limited to, composition of the upper surface of the belt 109, the surface roughness of the upper surface of the belt 109, the distribution of features formed in the body 111 during modification, the shape, size and/or cross-sectional shape of the distribution of features formed in the body 111 during modification, the distribution and type of one or more additives used during modification, the rheological properties (e.g., viscosity, etc.) of the body 111, the size, shape, and composition of raw materials within the body 111, the height of the body 111, the depth of the features, drying temperature, relative humidity, drying rate, drying time, rate of translation through the drying environment, or any combination thereof.
In one particular embodiment, the process of modifying can include forming a controlled distribution of features in at least a portion of the body. For example, as illustrated in
According to one embodiment, the controlled distribution of features can be defined as a pattern or array of features, having at least one repeating unit. In another embodiment, the controlled distribution of features can be a random distribution of features, such that there is no discernable short-range or long-range order to the arrangement of the features. Other examples of controlled distributions may include a radial pattern, a spiral pattern, a phyllotactic pattern, an asymmetric pattern, a self-avoiding random distribution, or any combination thereof.
The features of the controlled distribution may include a variety of shapes and/or structures. For example, the features may include at least one of a protrusion, a depression, an interconnected structure, a discrete and isolated structure, or any combination thereof. In at least one embodiment, the features can have various cross-sectional shapes, including for example, but not limited to, a U-shape, a V-shape, and the like. In certain instances, at least a portion of the body 111 can be formed to have a controlled distribution of features including an interconnected network of depressions, such as illustrated in
The size, shape and spacing of the features may be controlled and facilitate formation of precursor abrasive particles, and thus the finally-formed abrasive particles of a desired size. In one particular embodiment, the size, shape, and spacing between the features may facilitate formation of abrasive particles according to embodiments herein. The desired spacing between the features may influence the target average particle size of the abrasive particles to be formed. In at least one embodiment, the features may be formed to have sharp corners or a small radius of curvature, which may effectively concentrate the stress at the desired locations within the body 111 and further facilitate controlled cracking to generate the desired shape and size of abrasive particles, which can include those abrasive particles having the features of the embodiments herein.
For at least one aspect, the size of the features in the body 111 can be controlled to facilitate formation of abrasive particles according to embodiments herein. For example, the features can include at least one feature having a length (Lf), a width (Wf) and a depth (Df). In at least one embodiment, the length can be the longest dimension, the width can be the second longest dimension in the same plane as the length, and the depth can be the shortest dimension of the feature, which may be in direction perpendicular to the plane defined by the length and the width. Notably, in one embodiment Lf≥Wf≥Df. Still, in another embodiment, the body may have dimensions based on Lf≥Df≥Wf.
According to at least one embodiment, a feature may be in the form of a depression formed within the body 111.
In yet another embodiment, the protrusions 232 can define regions of the body 111 extending above the upper surface 112 of the body 111. The protrusions 232 can have an average height 234 relative to the average height 181 of the body. For example, the protrusions 232 may have an average height that is at least 5% of the average height 181 of the body 111. In other instances, the average height 234 of the protrusions 232 can be greater, such as at least 10% of the average height 181 of the body 111 or at least 15% or at least 20% or at least 25% or at least 30% or at least 35% or at least 40% or at least 45% or at least 50% or at least 55% or at least 60% or at least 65% or at least 70% or at least 75% or at least 80% or at least 85% or at least 90% or at least 95%. Still, in one non-limiting embodiment, the average height 234 can be not greater than 99% of the average height 181 of the body 111, such as not greater than 95% or not greater than 90% or not greater than 85% or not greater than 80% or not greater than 75% or not greater than 70% or not greater than 65% or not greater than 60% or not greater than 55% or not greater than 50% or not greater than 45% or not greater than 40% or not greater than 35% or not greater than 30% or not greater than 25% or not greater than 20% or not greater than 15% or not greater than 10% or not greater than 5%. It will be appreciated that the average height 234 can be within a range including any of the minimum and maximum percentages noted above. Control of the average height 234 of the protrusions 232 may facilitate suitable processing and improved formation of abrasive particles having the feature of the embodiments herein. One or more of such features may be present within the finally-formed abrasive particles.
The protrusions 232 may result from the modification process. In certain instances, when one or more depressions are formed the mixture of the body 111 is moved, and the protrusions 232 may result in areas around the depression 231. In other instances, the material of the body 111 may adhere to the form used to modify the surface of the body 111, and when the form is being pulled away from the body 111 some material of the body 111 may adhere to the form. Such adhesion between the form and the body 111 may cause the formation of protrusions. In certain instances, it may be desirable to limit the formation of protrusions due to adhesion between the form and the body during the modification process.
According to one embodiment, the process of modifying the body 111 can include modifying at least one surface of the body 111. As illustrated in
In at least one embodiment, the features formed in at least a portion of the surface (e.g., the upper surface 112) of the body 111 can be created by contacting a form to the surface of the body 111 to be modified. The form can have one or more features (e.g., protrusions, walls, openings, etc.) that can be used to create corresponding features in the body 111. Referring briefly to
It will be appreciated that various other forms may be used with the process. The forms can generally have any combination of features. The shape, size, and arrangement of the features of the form may impact the size and shape of the abrasive particles formed. Moreover, the features of the form may influence the shape features present in the abrasive particles. Such shape features are described in embodiments herein. Certain forms may utilize a particular arrangement of projections or walls that are interconnected and define openings.
While the forms of the embodiments herein have been illustrated as having generally planar shapes, it will be appreciated that the form can have various other shapes. For example, the forms can be in the shape of a roller that is configured to roll over the body 111 and impart features into the body 111. A form having such a shape may be suitable for continuous processing operations.
Moreover, as illustrated in
Any of the forms of the embodiments herein can be made of a particular material. For example, some suitable materials can include inorganic materials, organic materials, synthetic materials, natural materials, or any combination thereof. Some examples of inorganic materials can include metal, metal alloys, glass, ceramic, polycrystalline, monocrystalline, or any combination thereof. Some suitable organic materials can include polymers, such as epoxies, resins, thermosets, thermoplastics, polyimides, polyamides, or any combination thereof. The form may be a composite material including any combination of materials noted herein. The material of the form, particularly of the protrusions that will be in contact with the body, may be made of a particular material to limit the ability of the mixture to stick to the form. In certain instances, the material of the form is selected to ensure that the material of the body (i.e., the mixture) will not adhere to the material of the form, such that the features formed in the surface of the body can be made efficiently, with the proper shape and resolution. A form that limits the adhesion between the body and the form may limit unintended distortions in the body during modification, and may facilitate improved control of the shape and size of the abrasive particles formed from the controlled cracking processes.
In at least one embodiment, the surface of the form may be coated with a material prior to contacting the form to the body. Such coating materials may be permanent or temporary. The coating material can be an inorganic material, organic material, natural material, synthetic material or any combination thereof. For example, in one particular embodiment, the coating material can be an oil, such as a lubricant.
In yet another embodiment, the surface of the form, and particularly the protrusions to be contacting the portions of the body to cause the modification, may be coated with a chemical agent that will facilitate proper formation of the features in the body. The chemical agent may be a chemical element or chemical composition. The chemical agent may be an additive that can assist with modification of the body as described in embodiments herein, including for example a dopant. The chemical agent may be a permanent or temporary material added to the surface of the form. The chemical agent may be an inorganic material, organic material, natural material, synthetic material, or any combination thereof.
It will be appreciated that the features may be formed in other surfaces. For example, in an alternative embodiment, a surface of the belt 109 configured to contact the mixture 101 can be formed to have features. Accordingly, during deposition of the mixture 101 onto the belt 109, the body 111 can be formed and the features on the belt 109 can impart features into the surface of the body 111 in contact with the feature on the belt 109. As such, the process of forming the body and modifying the body are conducted substantially simultaneously. Such an alternative process may or may not be used with a separate modification zone 120 wherein other surfaces of the body 111 may be modified as described in the embodiments herein. For example, in one embodiment, the upper surface 112 of the body 111 and the lower surface of the body 111 in contact with the belt 109 may be modified according to any of the techniques described herein.
In at least one embodiment, the belt 109 can have an upper surface having a particular surface roughness. The upper surface of the belt is configured to contact the mixture 101 and the body 111. The belt 109 may not necessarily have any features, but may have a particular surface roughness that may facilitate later processing to form the abrasive particles. Notably, it has been observed that certain materials having a certain roughness may assist with drying and controlled cracking of the body 111 to facilitate formation of the abrasive particles according to embodiments herein. In at least one embodiment, forming the mixture 101 into the body 111 includes forming the mixture 101 on the belt, wherein the belt has a controlled surface roughness and surface energy relative to the mixture 101 to facilitate controlled cracking and formation of a plurality of precursor abrasive particles from the controlled cracking process.
As noted herein, in another embodiment, the processes of modifying the body 111 can include providing one or more additives to at least a portion of the body 111. Such additives may be used to physically or chemically alter the body 111, such that during later processing (e.g., drying) the additives may facilitate controlled cracking of the body to form precursor abrasive particles. The one or more additives can be applied to one or more surfaces of the body 111, including for example, any of the exterior surfaces of body 111. Some suitable processes for applying the one or more additives can include depositing, spraying, printing, blasting, scanning, ejecting, heating, and the like. The one or more additives may be added as solid particles, a liquid, a gas or a combination thereof. The one or more additives may be added as part of an additive composition, which may include the additives and other materials, such as a carrier fluid configured to contain the one or more additives for ease of processing and delivery of the additive to the body 111.
Some suitable additives can include rheology modifiers, dopants, pore formers, volatilization agents, and the like. Examples of dopants can include, but is not limited to, alkali elements, alkaline earth elements, rare-earth elements, hafnium (Hf), zirconium (Zr), niobium (Nb), tantalum (Ta), molybdenum (Mo), and a combination thereof. In particular instances, the dopant can include an element such as lithium (Li), sodium (Na), potassium (K), magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), scandium (Sc), yttrium (Y), lanthanum (La), cesium (Ce), praseodymium (Pr), niobium (Nb), hafnium (Hf), zirconium (Zr), tantalum (Ta), molybdenum (Mo), vanadium (V), chromium (Cr), cobalt (Co), iron (Fe), germanium (Ge), manganese (Mn), nickel (Ni), titanium (Ti), zinc (Zn), or any combination thereof. Some suitable examples of rheology modifiers can include organic materials, acids, bases, or any combination thereof. Certain additives, such as the dopants, may be added during various phases of processing. For example, the dopants may be added during the formation of the mixture. Alternatively, the dopant may be added to the precursor abrasive particles after some drying and/or some calcination of the precursor abrasive particles.
It will also be appreciated that the mixture may include seed material, such as alpha alumina seeds or iron oxide seeds, which may assist with the formation of a high temperature phase of material in the finally-formed and sintered abrasive particles.
Some suitable examples of pore formers can include hollow particles made of organic or inorganic materials, beads, spheres, glass, ceramics, glass-ceramics, natural materials, and the like. Some suitable inorganic materials can include oxides or carbon-containing materials, such as graphite, salts such as such as sodium chloride, potassium chloride, magnesium chloride, calcium chloride, sodium silicate, sodium carbonate, sodium sulfate, potassium sulfate, magnesium sulfate, or any combination thereof. In certain instances, the pore formers can include materials having low volatilization temperatures, such that upon further processing at suitable temperatures the pore formers volatilize forming a gas thereby leaving pores behind in the body 111. Some exemplary oxide-containing materials may include glasses, glass-ceramics, ceramics, and a combination thereof. Other exemplary organic pore formers can include wax, seeds, and shells, sulfosuccinates, naphthalenes, polyvinyls, ketones, polystyrenes, polyethylenes, polypropylenes, acrylics, benzene-containing polymers, alkyds, polyalkydes, epoxies, phenolics, acetals, and a combination thereof. Suitable inorganic pore formers can include hollow particles, such as beads, spheres, or the like made of materials such as glass, ceramics, glass-ceramics, or a combination thereof.
Some suitable volatilization agents can include organic materials, naturally occurring materials, or any combination thereof. Volatilization agents can be configured to volatilize at certain temperatures to form a gas phase. Such volatilization agents may be suitable for the creation of porosity within the body 111 during later processing, which can facilitate controlled cracking of the body and formation of abrasive particles having one or more features of the embodiments herein.
The one or more additives may also include the use of one or more precursor additives. A precursor additive is one or more elements or compounds that may undergo further processing to form an additive. The one or more precursor additives may be mixed to form one or more additives prior to providing the precursor to the body 111. In other instances, the one or more precursor additives may be provided to the body 111, and later processing may facilitate the formation of the additive within the body 111 (i.e., in-situ additive formation). For example, one or more precursor additives can be applied to at least a portion of the body 111, the body can undergo further processing (e.g., heating), which may facilitate the formation of one or more additives within the body from the one or more precursor additives.
In one embodiment, the additives can be selectively deposited on at least a portion of the body 111. For example, various techniques may be utilized to selectively deposit the one or more additives (or one or more precursor additives) to a portion of the body 111, such that affected portion of the body 111 can have treated areas and untreated areas. The treated areas are defined as areas where the one or more additives have been applied and the untreated areas are defined as areas of the body 111 where the one or more additives have not been applied. The creation of treated and untreated areas on the body may facilitate controlled cracking through later processing and the formation of abrasive particles having one or more features of the embodiments herein. It will be appreciated that the portions of the body 111 that may be affected can be any of the portions described in embodiments herein as being suitable for modification, including for example, any of the exterior surfaces of the body 111. The additives may be applied to the body such that the treated portions define a controlled distribution as described in the embodiments herein.
After modifying the at least one portion of the body 111, the body 111 may undergo further treatment to facilitate formation of the abrasive particles. As illustrated in
The drying process may result in the formation of any one or more features of the abrasive particles according to embodiments herein, including such features, but not limited to, microridges, protrusions, depressions, and any combination thereof. According to one embodiment, drying the body can include forming microridges on at least a portion of a side surface of at least one of the abrasive particles. In another embodiment, drying the body can include forming microridges on at least a portion of a side surface of a majority of the abrasive particles. In still another embodiment, drying the body can include forming microridges on a majority of the side surface of a majority of the abrasive particles. For another embodiment, drying the body can include forming microridges on at least a portion of a side surface of each of the abrasive particles.
As noted herein, the process of modification may define at least one crack initiation point within the body 111, and the drying process may be conducted under certain process parameters to control the initiation of the crack and the direction of crack propagation within the body. The at least one crack initiation point may correspond to one or more features formed within the body 111, including for example, but not limited to, a protrusion, a depression, an interconnected structure, a discrete and isolated structure, or any combination thereof. In certain instances, the at least one crack initiation point can be abutting the one or more features. Moreover, drying may be conducted such that the crack propagation extends along the length of the one or more features, such that the one or more features substantially guides the direction of the crack for at least a portion of the length of the crack. As such, in certain instances, the cracking process results in the formation of precursor abrasive particles having a portion of the controlled distribution of features within the body, such as a major surface of the body on which the features were formed. It will be appreciated, that the process of modifying the body 111 may also include forming a plurality of crack initiation points, wherein each of the crack initiation points is associated with a feature formed in the body 111 or the provision of an additive within a particular region of the body 111.
According to one embodiment, the drying conditions may be coupled with certain parameters of the modification process to enable controlled cracking of the body 111 and formation of the desired abrasive particles. The process of drying may facilitate controlled cracking of the body 111, such that a crack is initiated and grows in the body, extending through the body 111, and separating the body into smaller pieces that form the precursor abrasive particles. The controlled cracking is a distinct process from conventional processes (e.g., molding, printing, crushing, mechanical sectioning and agitation or vibration), because during controlled cracking the body 111 is torn and fractured under conditions to yield precursor (i.e., green) abrasive particles of a targeted shape. In at least one embodiment, the process relies only on the processes of modifying and drying to alter the body 111 into the precursor abrasive particles. The process does not necessarily require the use of any production tools (e.g., screens or molds) to achieve the formation of the abrasive particles, and notably abrasive particles of a targeted size and shape. Such a process represents an efficient mechanism for creating abrasive particles with a high yield of targeted grains sizes and shapes. Moreover, the resulting abrasive particles are characterized by certain unique features (e.g., microridges on the side surface and/or protrusions and/or depressions, etc.) due to the forming process.
According to one embodiment, drying can include drying in an environment having a drying temperature of at least 20° C., such as at least 25° C. or at least 30° C. or at least 40° C. or at least 50° C. or at least 60° C. or at least 70° C. or at least 80° C. or at least 90° C. or at least 100° C. or at least 110° C. or at least 120° C. or at least 130° C. or at least 140° C. or at least 150° C. or at least 160° C. or at least 170° C. or at least 180° C. or at least 190° C. or at least 200° C. or at least 210° C. or at least 220° C. or at least 230° C. or at least 240° C. Still, in another non-limiting embodiment, drying can be conducted in an environment at a drying temperature of not greater than 250° C., such as not greater than 240° C. or not greater than 230° C. or not greater than 220° C. or not greater than 210° C. or not greater than 200° C. or not greater than 190° C. or not greater than 180° C. or not greater than 170° C. or not greater than 160° C. or not greater than 150° C. or not greater than 140° C. or not greater than 130° C. or not greater than 120° C. or not greater than 110° C. or not greater than 100° C. or not greater than 90° C. or not greater than 80° C. or not greater than 70° C. or not greater than 60° C. or not greater than 50° C. or not greater than 40° C. or not greater than 30° C. It will be appreciated that drying can be conducted in an environment at a drying temperature of within a range including any of the minimum and maximum temperatures noted above, including but not limited to, within a range of at least 20° C. and not greater than 250° C., such as within a range including at least 50° C. and not greater than 150° C. The temperatures noted above can be an average temperature calculated from a statistically relevant number of random positions within a drying environment.
In yet another embodiment, drying can include drying the body in an environment having a relative humidity of at least 10%, such as at least 20% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% Still, the relative humidity within the environment can be not greater than 90%, such as not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20%. In at least one embodiment, the relative humidity within the environment can be within a range including any of the minimum and maximum percentages noted above, including for example, at least 10% and not greater than 70% or within a range of at least 10% and not greater than 70%. The relative humidity noted above can be an average relative humidity calculated from a statistically relevant number of random positions within a drying environment.
In yet another embodiment, drying can include controlling the flow rate of gases (e.g., air) within the drying environment. For example, according to one embodiment, the flow rate of the gas through the drying environment can be at least 0.1 m/s, such as at least 0.2 m/s or at least 0.5 m/s or at least 0.7 m/s or at least 1 m/s or at least 1.2 m/s or at least 1.5 m/s or at least 1.7 m/s or at least 2 m/s or at least 2.2 m/s or at least 2.5 m/s or at least 2.7 m/s or at least 3 m/s or at least 3.2 m/s or at least 3.5 m/s or at least 3.7 m/s or at least 4 m/s or at least 4.2 m/s or at least 4.5 m/s. Still, in at least one non-limiting embodiment, the flow rate of the gas (e.g., air, inert gas, oxidizing gas, reducing gas, or any combination thereof) can be not greater than 5 m/s or not greater than 4.7 m/s or not greater than 4.5 m/s or not greater than 4.2 m/s or not greater than 4 m/s or not greater than 3.7 m/s or not greater than 3.5 m/s or not greater than 3.2 m/s or not greater than 3 m/s or not greater than 2.7 m/s or not greater than 2.5 m/s or not greater than 2.2 m/s or not greater than 2 m/s or not greater than 1.7 m/s or not greater than 1.5 m/s or not greater than 1.2 m/s or not greater than 1 m/s or not greater than 0.7 m/s or not greater than 0.5 m/s. It will be appreciated that the flow rate of the gas or gases can be within a range including any of the minimum and maximum values noted above, including for example, within a range including at least 0.1 m/s and not greater than 5 m/s.
In yet another embodiment, the process of drying can include applying radiation to the body 111. The radiation may have a wavelength at least 0.1 microns or at least 0.5 microns or at least 1 micron or at least 2 microns or at least 3 microns or at least 5 microns or at least 10 microns or at least 20 microns or at least 50 microns or at least 100 microns or at least 200 microns or at least 500 microns or at least 700 microns or at least 1 mm. Still, in at least one non-limiting embodiment, the radiation can have a wavelength of not greater than 1 m, such as not greater than 0.8 m or not greater than 0.5 m or not greater than 0.1 m, or not greater than 1 cm or not greater than 1 mm or not greater than 500 microns or not greater than 100 microns or not greater than 10 microns. It will be appreciated that the radiation can have a wavelength within a range including any of the minimum and maximum values noted above. For example, in one embodiment the radiation can have a wavelength within a range of at least 0.1 microns to not greater than 1 mm. Still, in other embodiments, the radiation may have a wavelength within a range of at least 1 mm to not greater than 1 m.
In one embodiment, the process of drying to conduct controlled cracking of the body 111 and the formation of precursor abrasive particles may be conducted without the use of other processes, including but not limited to, mechanical devices (e.g., sectioning devices) intended to contact the body and separate the body into smaller pieces, ablation processes, vibratory processes, acoustic processes, and the like. In at least one embodiment, the process of forming the precursor abrasive particles from the body 111 is completed using only a drying process and controlling one or more drying conditions including the drying temperature, the relative humidity, drying rate, application of radiation, or any combination thereof. In at least one embodiment, the process of drying can include fracturing of the mixture to create a collection of abrasive particles. A collection of abrasive particles is described in more detail in the embodiments herein.
After forming the precursor abrasive particles 141, the precursor abrasive particles 141 may be translated through additional zones for further processing. Alternatively, the precursor abrasive particles 141 may be collected in a bin at the end of the belt 109 for further processing.
In accordance with an embodiment, the process of forming the abrasive particles may further comprise a calcining process, wherein the precursor abrasive particles are subject to a particular heating process to remove water and form calcined abrasive particles. In at least one embodiment, the calcining temperature used to calcine the precursor abrasive particles can be at least 600° C., such as at least 650° C. or at least 700° C. or at least 750° C. or at least 800° C. or at least 850° C. or at least 900° C. or at least 950° C. or at least 1000° C. or at least 1050° C. In still another non-limiting embodiment, the calcining temperature can be not greater than 1100° C. or not greater than 1050° C. or not greater than 1000° C. or not greater than 950° C. or not greater than 900° C. or not greater than 850° C. or not greater than 800° C. or not greater than 750° C. or not greater than 700° C. or not greater than 650° C. It will be appreciated that the calcining temperature can be within a range including any of the minimum and maximum values noted above, including for example, within a range including at least 600° C. and not greater than 1100° C.
After calcination, certain optional processes may be applied to the calcined abrasive particles. For example, an impregnation process may be used wherein one or more additives may be applied to the calcined abrasive particles. The additives can include any of the additives described in embodiments herein, including but not limited to, one or more dopants.
After conducting calcination, the calcined abrasive particles may be sintered to form abrasive particles. Sintering of the precursor abrasive particles 141 may be utilized to densify the particles. In a particular instance, the sintering process can facilitate the formation of a high-temperature phase of the ceramic material. For example, in one embodiment, the calcined abrasive particles may include alumina and sintering is conducted to form a high-temperature phase of alumina, such as alpha alumina. In at least one embodiment, sintering may be conducted at a sintering temperature within a range including at least 1100° C. to not greater than 2000° C. The duration of sintering at the sintering temperature may be within a range including at least 5 minutes to not greater than 10 hours.
Non-shaped abrasive particles are generally formed through different processes as disclosed herein and generally have different shape attributes. For example, non-shaped abrasive particles are typically formed by a comminution process, wherein a mass of material is formed and then crushed and sieved to obtain abrasive particles of a certain size. However, a non-shaped abrasive particle will have a generally random arrangement of the surfaces and edges, and generally will lack any recognizable two-dimensional or three dimensional shape in the arrangement of the surfaces and edges around the body. Moreover, non-shaped abrasive particles of the same group or batch generally lack a consistent shape with respect to each other, such that the surfaces and edges are randomly arranged when compared to each other. Therefore, non-shaped grains or crushed grains have a significantly lower shape fidelity compared to shaped abrasive particles.
The abrasive particles formed through embodiments herein can be controlled-height abrasive particles having controlled two-dimensional shapes as viewed top down in a plane of the length and width of the particle. Generally, the abrasive particles of the embodiments herein can have two or more surfaces, such as the first and second major surfaces that can be substantially parallel to each other and which may include features as disclosed in the embodiments herein. Notably, the arrangement of the first and second major surfaces extending parallel to each other and defining the length and width of the body generally give the particles a planar shape and a controlled height. The body of the abrasive particles may further include a side surface extending between the first and second major surfaces. The side surface can have various contours depending upon the processing conditions used to form the particles. Notably, as described herein, the process can be used to form a batch of abrasive particles, wherein the batch can include two or more different shapes of abrasive particles.
As will be appreciated, the elongated abrasive particle can have a length defined by the longitudinal axis 652, a width defined by the lateral axis 653, and a vertical axis 654 defining a height. As will be appreciated, the body 651 can have a primary aspect ratio of length:width such that the length is greater than the width. Furthermore, the length of the body 651 can be greater than or equal to the height. Moreover, the width of the body 651 can be greater than or equal to the height 654.
As further illustrated in
It will be appreciated that the CHAP are not so limited and can include other two-dimensional shapes. For example, the abrasive particles of the embodiments herein can include particles having a body with a two-dimensional shape as defined by a major surface of the body from the group of shapes including polygons, irregular polygons, irregular polygons including arcuate or curved sides or portions of sides, complex shapes having a combination of polygons shapes, star shapes, shapes with arms extending from a central region (e.g., cross-shaped bodies) and a combination thereof. The processes disclosed herein can be used to form shaped abrasive particles having the features described herein.
As further illustrated, the body 751 of the abrasive particle 750 can have a side surface 754 having an irregular two-dimensional shape as viewed in the plane of the first or second major surfaces 752 or 753. An irregular two-dimensional shape is one in which the shape does not have a recognizable shape, such as a polygonal shape. The irregular two-dimensional shape is characterized by a side surface 754 that can have a random or unpredictable contour. Such an abrasive particle can be formed according to the processes of the embodiments herein. The body 751 can have seven external corners 771, 772, 773, 774, 775, 776, and 777 (771-777). The external corners 771-777 are portions that would cause significant deflection of an imaginary rubber band around the side surface 754 of the body 751 by at least 10 degrees or greater.
According to any of the abrasive particles of the embodiments herein, the body of the abrasive particle can have a primary aspect ratio of length:width that can be at least 1.1:1, such as at least 1.2:1 or at least 1.5:1 or at least 1.8:1 or at least 2:1 or at least 3:1 or at least 4:1 or at least 5:1 or at least 6:1 or even at least 10:1. In another non-limiting embodiment, the body can have a primary aspect ratio of length:width of not greater than 100:1, such as not greater than 50:1 or not greater than 10:1 or not greater than 6:1 or not greater than 5:1 or not greater than 4:1 or not greater than 3:1 or even not greater than 2:1. It will be appreciated that the primary aspect ratio of the body can be with a range including any of the minimum and maximum ratios noted above.
Furthermore, the body of any of the shaped abrasive particles of the embodiments herein can have a secondary aspect ratio of width:height that can be at least 1.1:1, such as at least 1.2:1 or at least 1.5:1 or at least 1.8:1 or at least 2:1 or at least 3:1 or at least 4:1 or at least 5:1 or at least 8:1 or even at least 10:1. Still, in another non-limiting embodiment, the secondary aspect ratio width:height can be not greater than 100:1, such as not greater than 50:1 or not greater than 10:1 or not greater than 8:1 or not greater than 6:1 or not greater than 5:1 or not greater than 4:1 or not greater than 3:1 or even not greater than 2:1. It will be appreciated the secondary aspect ratio of width:height can be with a range including any of the minimum and maximum ratios of above.
In another embodiment, the body of any of the abrasive particles can have a tertiary aspect ratio of length:height that can be at least 1.1:1, such as at least 1.2:1 or at least 1.5:1 or at least 1.8:1 or at least 2:1 or at least 3:1 or at least 4:1 or at least 5:1 or at least 8:1 or even at least 10:1. Still, in another non-limiting embodiment, the tertiary aspect ratio length:height can be not greater than 100:1, such as not greater than 50:1 or not greater than 10:1 or not greater than 8:1 or not greater than 6:1 or not greater than 5:1 or not greater than 4:1 or not greater than 3:1. It will be appreciated that the tertiary aspect ratio can be with a range including any of the minimum and maximum ratios and above.
The abrasive particles of the embodiments herein can have a body including a crystalline material, and more particularly, a polycrystalline material. Notably, the polycrystalline material can include abrasive grains. In one embodiment, the body of the abrasive particle can be essentially free of an organic material, including for example, a binder. In at least one embodiment, the abrasive particles can consist essentially of a polycrystalline material.
The abrasive grains (i.e., crystallites) contained within the body of the abrasive particles may have an average grain size that is generally not greater than 20 microns, such as not greater than 18 microns or not greater than 16 microns or not greater than 14 microns or not greater than 12 microns or not greater than 10 microns or not greater than 8 micron or not greater than 5 microns or not greater than 2 microns or not greater than 1 micron or not greater than 0.9 microns or not greater than 0.8 microns or not greater than 0.7 microns or even not greater than 0.6 microns. Still, the average grain size of the abrasive grains contained within the body of the abrasive particles can be at least 0.01 microns, such as at least 0.05 microns or at least 0.06 microns or at least 0.07 microns or at least 0.08 microns or at least 0.09 microns or at least 0.1 microns or at least 0.12 microns or at least 0.15 microns or at least 0.17 microns or at least 0.2 microns or even at least 0.5 microns. It will be appreciated that the abrasive grains can have an average grain size within a range including any of the minimum and maximum values noted above.
In accordance with an embodiment, the body of the abrasive particle can have an average particle size, as measured by the largest dimension measurable on the body (i.e., the length), of at least 100 microns. In fact, the body of the abrasive particle can have an average particle size of at least 150 microns, such as at least 200 microns or at least 300 microns or at least 400 microns or at least 500 microns or at least 500 microns or at least 600 microns or at least 800 microns or even at least 900 microns. Still, the body of the abrasive particle can have an average particle size that is not greater than 5 mm, such as not greater than 3 mm or not greater than 2 mm or even not greater than 1.5 mm. It will be appreciated that the body of the abrasive particle can have an average particle size within a range including any of the minimum and maximum values noted above.
In yet another embodiment, the particulate material can have a body having an average particle size, which may be selected from a group of predetermined sieve sizes. For example, the body can have an average particle size of not greater than about 5 mm, such as not greater than about 3 mm, not greater than about 2 mm, not greater than about 1 mm, or even not greater than about 0.8 mm. Still, in another embodiment, the body may have an average particle size of at least about 0.1 microns or at least 1 micron or at least 0.1 mm or at least 0.5 mm. It will be appreciated that the body may have an average particle size within a range between any of the minimum and maximum values noted above.
Particles for use in the abrasives industry are generally graded to a given particle size distribution before use. Such distributions typically have a range of particle sizes, from coarse particles to fine particles. In the abrasive art, this range is sometimes referred to as a “coarse”, “control”, and “fine” fractions. Abrasive particles graded according to abrasive industry accepted grading standards specify the particle size distribution for each nominal grade within numerical limits. Such industry accepted grading standards (i.e., abrasive industry specified nominal grade) include those known as the American National Standards Institute, Inc. (ANSI) standards, Federation of European Producers of Abrasive Products (FEPA) standards, and Japanese Industrial Standard (JIS) standards. ANSI grade designations (i.e., specified nominal grades) include: ANSI 4, ANSI 6, ANSI 8, ANSI 16, ANSI 24, ANSI 36, ANSI 40, ANSI 50, ANSI 60, ANSI 80, ANSI 100, ANSI 120, ANSI 150, ANSI 180, ANSI 220, ANSI 240, ANSI 280, ANSI 320, ANSI 360, ANSI 400, and ANSI 600. FEPA grade designations include P8, P12, P16, P24, P36, P40, P50, P60, P80, P100, P120, P150, PI 80, P220, P320, P400, P500, P600, P800, P1000, and P1000. JIS grade designations include JIS8, JIS12, JIS 16, JIS24, JIS36, JIS46, JIS54, JIS60, JIS80, JIS 100, JIS150, JIS180, JIS220, JIS240, JIS280, JIS320, JIS360, JIS400, JIS600, JIS800, JIS 1000, JIS 1500, JIS2500, JIS4000, JIS6000, JIS8000, and JIS10,000. Alternatively, the abrasive particles can graded to a nominal screened grade using U.S.A. Standard Test Sieves conforming to ASTM E-1 1 “Standard Specification for Wire Cloth and Sieves for Testing Purposes.” ASTM E-1 1 prescribes the requirements for the design and construction of testing sieves using a medium of woven wire cloth mounted in a frame for the classification of materials according to a designated particle size. A typical designation may be represented as −18+20 meaning that the particles pass through a test sieve meeting ASTM E-1 1 specifications for the number 18 sieve and are retained on a test sieve meeting ASTM E-1 1 specifications for the number 20 sieve. In various embodiments, the particulate material can have a nominal screened grade comprising: −18+20, −20/+25, −25+30, −30+35, −35+40, −40+45, −45+50, −50+60, −60+70, −70/+80, −80+100, −100+120, −120+140, −140+170, −170+200, −200+230, −230+270, −270+325, −325+400, −400+450, −450+500, or −500+635. Alternatively, a custom mesh size could be used such as −90+100. The body of the particulate material may be in the form of a shaped abrasive particle, as described in more detail herein.
Some suitable materials for use in the body of the abrasive particle can include of nitrides, oxides, carbides, borides, oxynitrides, oxyborides, oxycarbides, carbon-based materials, diamond, naturally occurring minerals, rare-earth-containing materials, natural minerals, synthetic materials, or any combination thereof. In particular instances, the abrasive particles can include an oxide compound or complex, such as aluminum oxide, zirconium oxide, titanium oxide, yttrium oxide, chromium oxide, strontium oxide, silicon oxide, magnesium oxide, rare-earth oxides, or any combination thereof. In one particular embodiment, the body can include at least 95 wt % alumina for the total weight of the body. In at least one embodiment, the body can consist essentially of alumina. Still, in certain instances, the body can include not greater than 99.5 wt % alumina for the total weight of the body. In accordance with an embodiment, the body may consist essentially of alpha alumina. In certain instances, the body may be formed such that it includes not greater than about 1 wt % of any low-temperature alumina phases. As used herein, low temperature alumina phases can include transition phase aluminas, bauxites or hydrated alumina, including for example gibbsite, boehmite, diaspore, and mixtures containing such compounds and minerals. Certain low temperature alumina materials may also include some content of iron oxide. Moreover, low temperature alumina phases may include other minerals, such as goethite, hematite, kaolinite, and anastase.
Moreover, in particular instances, the body of the abrasive particles can be formed from a seeded sol-gel. In at least one embodiment, the body of any of the abrasive particles of the embodiments herein may be essentially free of iron, rare-earth oxides, and a combination thereof. Reference herein to a body having a certain features (e.g., composition) will also be understood to refer to a batch of abrasive particles that can have the same feature (e.g., composition).
In accordance with certain embodiments, certain abrasive particles can be compositional composites, such that at least two different types of grains are contained within the body of the abrasive particle. It will be appreciated that different types of grains are grains having different compositions with regard to each other. For example, the body of the abrasive particle can be formed such that it includes at least two different types of grains, wherein the types of grains are selected from the group of nitrides, oxides, carbides, borides, oxynitrides, oxyborides, oxycarbides, carbon-based materials, diamond, naturally occurring minerals, rare-earth-containing materials, natural minerals, synthetic materials, and a combination thereof.
The body of the abrasive particles may include additives, such as dopants, which may be in the form of elements or compounds (e.g., oxides). Certain suitable additives can include any of the materials described herein. The body of an abrasive article may include a specific content of one or more additives (e.g., dopant). For example, the body may include not greater than about 30 wt % additives for the total weight of the body. In still other embodiments, the amount of additives may be less, such as not greater than about 25 wt % or not greater than about 20 wt % or not greater than about 18 wt % or not greater than about 15 wt % or not greater than about 12 wt % or not greater than about 10 wt % or not greater than about 8 wt % or not greater than 5 wt % or not greater than 2 wt %. Still, the amount of additives can be at least about 0.5 wt % for a total weight of the body, such as at least about 1 wt %, at least about 2 wt % or at least about 3 wt % or at least about 4 wt % or at least about 5 wt % or at least about 8 wt % or even at least about 10 wt %. It will be appreciated that the amount of additive within the body may be within a range including any of the minimum and maximum percentages noted above.
The body of the abrasive particle may be particularly dense. For example, the body may have a density of at least about 95% theoretical density, such as at least about 96% or even at least about 97% theoretical density.
The body 801 can have a side surface 804 that can include multiple side surface portions that are separated from each other by exterior corners of the body. The first side surface portion 813 can define a fraction of the side surface 804 that can be disposed between a first external corner 815 and a second external corner 816. As illustrated and according to an embodiment, the first side surface portion 813 can be a fraction of the total length of the side surface 804 defining the perimeter of the body 801.
According to one embodiment, the body 801 can include a plurality of side surface portions, wherein each of the side surface portions extend for a length of at least 5% of a total length of the body, such as at least 10% or at least 15% or at least 20% or at least 25%. In another non-limiting embodiment, each of the side surface portions can extend for a length of not greater than 80% of a length of the body, such as not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30%. It will be appreciated that the length of the side surface portions can be within a range including any of the minimum and maximum percentages noted above.
As further illustrated in
In at least one embodiment, the first protrusion 811 can extend for a fraction of the total length of the side surface 804 defining the perimeter of the body 801. In one particular embodiment, the first protrusion 811 can extend for at least 30% of the total length of the first side surface portion 813, which is measured as the distance between the first external corner 815 and the second external corner 816. In another embodiment, the first protrusion 811 can extend for at least 40% of the total length of the first side surface portion 813 or at least 50% or at least 60% or at least 70% or at least 80% or even at least 90% of the total length of the first side surface portion 813. In one particular embodiment, the first protrusion 811 can extend parallel to each other for the entire length of the first side surface portion 813. Still, in another non-limiting embodiment, the first protrusion 811 can extend for not greater than 99% of the total length of the first side surface portion 813, such as not greater than 95% or not greater than 90% or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% of the total length of the first side surface portion 813. It will be appreciated that the first protrusion 811 can extend for length within a range including any of the minimum and maximum percentages noted above.
According to one embodiment, the first major surface 802 surface can include the untextured region 850 that extends through the central region 851 of the body. The untextured region 850 can include the midpoint 852 of the first major surface 802 of the body 801. Notably, the first protrusion 811 can be abutting a portion the untextured region 850.
Notably, in certain instances, the features (e.g., depressions and protrusions) on the first major surface 802 can be positioned near the perimeter of the body 801, such that the body 801 includes at least one untextured region 850 within the central region 851 of the body. Still, in at least one embodiment, at least a portion of the untextured region 850 can be abutting a portion of the side surface (e.g., the fourth side surface portion 843), such that there are no features intervening between the untextured region 850 and at least one portion of the side surface. In another embodiment, the first protrusion 811 can be spaced apart from the untextured region 850 of the first major surface 802.
In yet another embodiment, the untextured region 850 may have a two-dimensional shape that is substantially the same as the two-dimensional shape of the body 801. For example, as illustrated in
In at least one embodiment, the untextured region 850 can define a significant portion of the first major surface 802, including for example, at least a majority of the surface area of the first major surface 802. In at least one embodiment, the untextured region 850 can occupy at least 10%, such as at least 20% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or even at least 80% of the total surface area of the first major surface. Such an evaluation may be made by viewing the particle using an optical microscope at a suitable magnification (e.g., as shown in
The untextured region 850 may have a notably distinct waviness and/or surface roughness. For example, the untextured region 850 can have a waviness (Rw) that is distinct from the waviness within the region of the first major surface 802 associated with the first depression 811 and the first protrusion 812. Moreover, in at least one embodiment, the untextured region 850 can have a surface roughness (Ra) that is distinct from the surface roughness of the first major surface 802 associated with the first protrusion 811.
In certain instances, any of the features in the first major surface 802 can abut the untextured region 850. For example, the first protrusion 811 can abut the untextured region 850. The untextured region is a region that is absent the features (e.g., protrusions and/or depressions) formed during the process of modifying the body. The untextured region 850 can have some surface contours, such as a curvature (e.g., concave curvature), but is generally absent the features formed in the body near the side surface portions. Moreover, in certain embodiments, the untextured region 850 may have a substantially planar contour.
According to another embodiment, the first side surface portion 813 and the first protrusion 811 can have substantially the same contour as viewed in the plane of the first major surface 802. For example, as illustrated in
As further illustrated in
In at least one embodiment, any protrusions or depressions can intersect one or more side surface portions. For example, the first protrusion 811 can be formed such that it intersects the second side surface portion 823. Moreover, as illustrated in
The first major surface 802 can include a second protrusion 821 extending in a direction parallel to the second side surface portion 823. As illustrated and according to an embodiment, the second side surface portion 823 can be a fraction of the total length of the side surface 804 defining the perimeter of the body 801. As further illustrated and according to one embodiment, the first major surface 802 can further include a second side surface region 822 disposed between the second side surface portion 823 and the second protrusion 821. The second side surface region 822 can be abutting and extending along the second side surface portion 823.
The second protrusion 821 can be abutting the second side surface region 822. As illustrated and according to one embodiment, the second protrusion 821 and the second side surface region 822 can extend parallel to each other and parallel to the second side surface portion 823. In at least one embodiment, the second protrusion 821 and the second side surface region 822 can extend parallel to each other for at least a portion of the second side surface portion 823. The second protrusion 821 and the second side surface region 822 can extend for a fraction of the total length of the side surface 804 defining the perimeter of the body 801. In one particular embodiment, the second protrusion 821 can extend for at least 30% of the total length of the second side surface portion 823, which is measured as the distance between the second external corner 816 and the third external corner 817. In another embodiment, the second protrusion 821 can extend for at least 40% of the total length of the second side surface portion 823 or at least 50% or at least 60% or at least 70% or at least 80% or even at least 90% of the total length of the second side surface portion 813. In one particular embodiment, the second protrusion 821 can extend for the entire length of the second side surface portion 823. Still, in another non-limiting embodiment, the second protrusion 821 can extend for not greater than 99% of the total length of the second side surface portion 823, such as not greater than 95% or not greater than 90% or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% of the total length of the second side surface portion 823. It will be appreciated that the second protrusion 821 can extend for length within a range including any of the minimum and maximum percentages noted above.
According to another embodiment, the second side surface portion 823 and the second protrusion 821 can have substantially the same contour compared to each other as viewed in the plane of the first major surface 802. For example, as illustrated in
According to one embodiment, any of the features on the major surfaces of the body can intersect each other. For example, as illustrated in
In at least one embodiment, the first major surface 802 may include a third portion of a side surface 833. The third side surface portion 833 can be distinct from the first side surface portion 813 and the second side surface portion 823. In particular, the third side surface portion 833 can be separated from the first side surface portion 813 and the second side surface portion 823 by at least one external corner. According to the illustrated embodiment of
In at least one embodiment, the second protrusion 821 and the second side surface region 822 can intersect the third side surface portion 833 proximate the third external corner 817. In particular, the third side surface portion 833 may be distinct from the first and second portions of the side surface 813 and 823 in that there is no third protrusion extending along the third side surface portion 833. The first major surface 802 does include a third side surface region 832 extending along and abutting the third side surface portion 833. The third side surface region 832 can have any of the features of the other side surface regions described herein. The third side surface region 832 may be in the form of a ridge extending vertically above the surface of the untextured region 850 and may have any feature of the protrusions described in embodiments herein. Moreover, as illustrated, the third side surface region 832 can be abutting the untextured region 850 extending through the central region 851 of the body 801. Additionally, the third side surface region 832 can intersect the second protrusion 821 proximate the third external corner 817.
In at least one embodiment, the first major surface 802 may include a fourth portion of a side surface 843. The fourth side surface portion 843 can be distinct from the first side surface portion 813, the second side surface portion 823, and the third side surface portion 833. In particular, the fourth side surface portion 843 can be separated from the first side surface portion 813, the second side surface portion 823, and the third side surface portion 833 by at least one external corner. According to the illustrated embodiment of
In at least one embodiment, the fourth side surface portion 843 can be distinct from the other portions of the side surface 813, 823, and 833, in that it defines an unfeatured edge 844. The unfeatured edge 844 defines a joint between the first major surface 802 and the fourth side surface portion 843 and does not include any features, such as protrusions and/or depressions, which are generally formed during the forming process. More particularly, in one embodiment, the unfeatured edge 844 can abut the untextured region 850 extending through the central region 851 of the first major surface 802 of the body 801. Accordingly, there are no intervening features (e.g., protrusions or depressions) between the untextured region 850 of the central region 851 and the fourth side surface portion 843. It will be appreciated that the abrasive particles of the embodiments herein may include one or more unfeatured edges that can intersect one or more featured edges, wherein a featured edge comprises at least one feature (e.g., a protrusion or depression) extending along a portion of the side surface as described in embodiments herein.
As further illustrated, certain features from the abutting side surface portions can intersect the fourth side surface portion 843. For example, the first protrusion 811 can intersect the fourth side surface portion 843 proximate the first external corner 815.
As illustrated, the abrasive particle 850 includes a body 851 including a first major surface 852, a second major surface (not illustrated), and a side surface (not illustrated in the view of
As further illustrated in
Notably,
As illustrated in the plot, the first protrusion 853 extends above the first major surface 852. As illustrated, the first protrusion 853 can be in direct contact with the untextured region 890. The first protrusion 853 can extend along the entire length of the first side surface portion 854 between the first external corner 855 and the second external corner 856. Moreover, the first protrusion 853 can have substantially the same contour as viewed top-down (as provided in
As further illustrated in
Notably,
According to the illustrated embodiment of
The first major surface 852 of the body 851 can further include a first depression 867, which can be adjacent to the second protrusion 863 and extend along a majority of the length of the second protrusion 863. The first depression 867 can be positioned between the second protrusion 863 and the untextured region 890. The first depression 867 can further extend along the direction of the second protrusion 863 and the second side surface portion 864. Moreover, in the embodiment, of
The second protrusion 863 can further be abutting the first depression 867. As illustrated and according to one embodiment, the second protrusion 863 and the first depression 867 can extend for a fraction of the total length of the side surface defining the perimeter of the body 801. In one particular embodiment, the second protrusion 863 and/or the first depression 867 can extend for not greater than 30% of the total length of the second side surface portion 864, which is measured as the distance between the external corners 856 and 857. In another embodiment, the second protrusion 863 and/or the first depression 867 can extend parallel to each other for at least 40% of the total length of second side surface portion 864 or at least 50% or at least 60% or at least 70% or at least 80% or even at least 90% of the total length of the second side surface portion 864. In one particular embodiment, the second protrusion 863 and/or the first depression 867 can extend parallel to each other for the entire length of the second side surface portion 864. Still, in another non-limiting embodiment, the second protrusion 863 and/or the first depression 867 can extend parallel to each other for not greater than 99% of the total length of the second side surface portion 864, such as not greater than 95% or not greater than 90% or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% of the total length of the second side surface portion 864. It will be appreciated that the second protrusion 863 and/or the first depression 867 can extend parallel to each other for length within a range including any of the minimum and maximum percentages noted above.
It will be appreciated that other abrasive particles can include more than one depression. For example, particles of the embodiments herein may have one or more depressions on the surface, and such depressions can be associated with and abutting more than one other portions of the upper surface of the body, including for example, one or more protrusions, the untextured region, and the like. One or more protrusions can be disposed between a depression and a side surface portion. Likewise, one or more depressions can be disposed between a protrusion and the untextured region.
As illustrated in
As further illustrated in
The first major surface 852 can further include a third protrusion 883 located proximate to the fourth external corner 858. The third protrusion 883 can extend for a fraction of the length of the fourth side surface portion 884. As further illustrated in
Moreover, in one embodiment, the first major surface 922 can have a first surface area (A1) and the second major surface 923 can have a second surface area (A2). According to one embodiment, the first surface area can be different than the second surface area. Notably, in at least one instance, A1 can be less than A2. In more particular instances, the difference between the first surface area (A1) and the second surface area (A2) can be defined by a ratio (A1/A2), wherein A1/A2 can be not greater than 1, such as not greater than 0.9 or not greater than 0.8 or not greater than 0.7 or not greater than 0.6 or not greater than 0.5 or not greater than 0.4 or not greater than 0.3 or not greater than 0.3 or not greater than 0.2 or not greater than 0.1. Still, in another non-limiting embodiment, the ratio (A1/A2) can be at least 0.01, such as at least 0.05 or at least 0.1 or at least 0.2 or at least 0.3 or at least 0.4 or at least 0.5 or at least 0.6 or at least 0.7 or at least 0.8 or even at least 0.9. It will be appreciated that the ratio (A1/A2) can be within a range including any of the minimum and maximum values noted above.
While all of the images of the abrasive particles of
Moreover, reference herein to any dimensional characteristic (e.g., length, width, height, etc.) can be reference to a dimension of a single particle, a median value, or an average value derived from analysis of a suitable sampling of particles. Unless stated explicitly, reference herein to a dimensional characteristic can be considered reference to a median value that is based on a statistically significant value derived from a random sampling of suitable number of particles. Notably, for certain embodiments herein, the sample size can include at least 10, and more typically, at least 40 randomly selected particles from a batch of particles. A batch of particles may include, but need not necessarily be limited to, a group of particles that are collected from a single process run. In yet another instance, a batch of abrasive particles can be a group of abrasive particles of an abrasive article, such as a fixed abrasive article. For example, a batch of particles may include an amount of abrasive particles suitable for forming a commercial grade abrasive product, such as at least about 20 lbs. of particles.
According to one embodiment, a majority of the side surface can include a plurality of microridges. For example as illustrated in the image of
The plurality of microridges 1505 appear to have multiple, distinct morphologies or types. A first type of microridge can include isolated microridges 1506, which can be defined by microridges extending out the side surface and along the side surface. The isolated microridges 1506 can be separated by generally smooth planar regions. The second type of microridge can include scaled microridges 1507, which may have a scaled or layered appearance. Another type of includes expanding microridges, which includes a plurality microridges extending outward from a focal region. Such microridges are described in accordance with
In one embodiment, an abrasive particle can have a side surface, wherein at least 51% of the total surface area of the side surface includes the plurality of microridges 1505. In another embodiment, a greater percentage of the side surface 1504 can include the plurality of microridges 1505, including for example, but not limited to, at least 52% or at least 54% or at least 56% or at least 58% or at least 60% or at least 62% or at least 64% or at least 66% or at least 68% or at least 70% or at least 72% or at least 74% or at least 76% or at least 78% or at least 80% or at least 82% or at least 84% or at least 86% or at least 88% or at least 90% or at least 92% or at least 94% or at least 96% or at least 98% or even at least 99% of the total surface area of the side surface. In another non-limiting embodiment, not greater than 99% of the total surface area of the sides surface 1504 can include the plurality of microridges 1505, such as not greater than 98% or not greater than 96% or not greater than 94% or not greater than 92% or not greater than 90% or not greater than 88% or not greater than 86% or not greater than 84% or not greater than 82% or not greater than 80% or not greater than 78% or not greater than 76% or not greater than 74% or not greater than 72% or not greater than 70% or not greater than 68% or not greater than 66% or not greater than 64% or not greater than 62% or not greater than 60% or not greater than 58% or not greater than 56% or not greater than 54% or not greater than 52%. It will be appreciated that the total surface area of the side surface covered by the plurality of microridges 1505 can be within a range including any of the minimum and maximum percentages noted above.
As noted in other embodiments, the side surface may include a plurality of side surface portions, wherein each side surface portion is defined as a portion of the side surface extending between the external corners of the body. According to one embodiment, at least 45% of the side surface portions for a given abrasive particle can include the plurality of microridges. In still other embodiments, the percentage can be greater, including for example, at least 52% of the side surface portions of the body include the plurality of microridges, or at least 54% or at least 56% or at least 58% or at least 60% or at least 62% or at least 64% or at least 66% or at least 68% or at least 70% or at least 72% or at least 74% or at least 76% or at least 78% or at least 80% or at least 82% or at least 84% or at least 86% or at least 88% or at least 90% or at least 92% or at least 94% or at least 96% or at least 98% or at least 99%. In at least one embodiment, all of the side surface portions of the side surface for a given abrasive particle can include the plurality of microridges.
While it will be understood that the two-dimensional shape of the body as viewed top-down will determine the number of side surface portions for an abrasive particle, in at least one embodiment, the body can include at least three side surface portions including the plurality of microridges. In other embodiments, the number of side surface portions including the plurality of microridges can be greater, such as at least four or at least five or at least six or at least seven or at least eight. Still, it will be appreciated that in at least one embodiment, an abrasive particle may be formed such that at least one side surface portion does not include the plurality of microridges.
In another embodiment, at least one of the isolated microridges of the plurality of isolated microridges 1506 can be made up of different regions having different shapes. For example, at least one of the isolated microridges can include a head region 1513 and a tail region 1514 connected to and extending from the head region 1513. As depicted and according to one embodiment, the head region 1503 can have a rounded shape. The tail region 1514 can have an elongated shape. In at least one embodiment, an isolated microridge can include a series of these regions linked together and separated by one or more gaps 1516. The gaps 1516 can define an interruption in the isolated microridges 1506. The gaps 1516 can define smooth regions positioned along the irregular path of the one or more isolated microridges 1506. In at least one embodiment, the irregular path of an isolated microridge 1506 can include a plurality of gaps 1516, and thus the isolated microridge may be characterized as a series of isolated microridge portions 1517 extending along an irregular path. Any of the isolated microridge portions can include a head region and tail region.
The plurality of isolated microridges 1506 may extend along the side surface for a significant distance. For example, at least one of the isolated microridges 1506 can extend for at least 10% of the average height of the side surface 1504. In other embodiments, the length of one or more isolated microridges 1506 on the side surface 1504 can be at least 20% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90% or at least 95% of the average height of the side surface 1504. In still another non-limiting embodiment, the length of one or more isolated microridges 1506 on the side surface 1504 can be not greater than 99% or not greater than 90% or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% of the average height of the side surface. It will be appreciated that the length of one or more of the isolated microridges 1506 along the side surface 1504 can be within a range including any of the minimum and maximum percentages noted above.
In certain instances, one or more of the plurality of isolated microridges 1506 can have a total length of at least 100 microns, such as at least 150 microns or at least 200 microns or at least 300 microns or at least 400 microns. Still, depending upon the height of the abrasive particle, the total length of at least one of the isolated microridges 1506 may be not greater than 2 mm, such as not greater than 1 mm or even not greater than 500 mm.
The plurality of isolated microridges 1506 may have a very small thickness, particularly in the tail region 1514, wherein the thickness is measured in a direction transverse to the microridge and the direction defining the length of the microridge. As depicted in
The plurality of isolated microridges 1506 may have a thickness in the head region 1513 that is greater than the thickness in the tail region 1514. As depicted in
As further depicted in
According to one embodiment, and as depicted in
In one aspect, the primary ridges 1521 can have any of the features with respect to size and direction as described in accordance with the isolated microridges. For example, the primary ridges 1521 may extend along the side surface 1504 for a significant distance. For example, at least one of the primary ridges 1521 can extend for at least 10% of the average height of the side surface 1504. In other embodiments, the length of one or more primary ridges 1521 on the side surface 1504 can be at least 20% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90% or at least 95% of the average height of the side surface. In still another non-limiting embodiment, the length of one or more primary ridges 1521 on the side surface 1504 can be not greater than 99% or not greater than 90% or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% of the average height of the side surface 1504. It will be appreciated that the length of one or more primary ridges 1521 along the side surface 1504 can be within a range including any of the minimum and maximum percentages noted above.
In certain instances, one or more of the primary ridges 1521 can have a total length of at least 100 microns, such as at least 150 microns or at least 200 microns or at least 300 microns or at least 400 microns. Still, depending upon the height of the abrasive particle, the total length of at least one of the primary ridges 1521 may be not greater than 2 mm, such as not greater than 1 mm or even not greater than 500 mm. It will be appreciated that the total length of at least one of the primary ridges 1521 can be within a range including any of the minimum and maximum values noted above.
As further depicted in
As further depicted in
In certain embodiments, the plurality of wrinkles 1522 may define cuts through the primary ridges 1521, which may form gaps 1523 or regions of reduced height in the primary ridges 1521. According to one embodiment, one of more of the primary ridges 1521 can include at least one gap 1523 between elongated portions defining the primary ridge 1521. The gap 1523 may be associated with and/or connected to one or more wrinkles 1522 extending from the gap 1523.
As noted herein, the scaled microridges 1507 can have a scaled or scaly appearance. Unlike the isolated microridges 1506, the scaled microridges 1507 appear to have a greater waviness and/or roughness. Moreover, the region of the side surface having the scaled microridges 1507 can define a region of the side surface having a greater roughness compared to the region of the side surface including the isolated microridges 1506. The scaled microridges 1506 and isolated microridges 1507 may also be distinguished from each other based on one or more other surface features, including for example, but not limited to, waviness, maximum surface roughness, and the like.
As further depicted in
According to another embodiment, and as illustrated in
In addition to or as an alternative to any of the features described herein, the abrasive particles formed through the methods described herein can have particular features, which may be associated with the side surface or portions of the side surface.
The definition of the Fourier Transform (FT) is given below:
It is implied that “f” is the original image and (x,y) its horizontal and vertical axes, and “F” is the Fourier Transform of the original image, and (u,v) its axis in the frequency space.
And where j=√−1 and “N” is the size of the original image in pixel.
By definition, we have FTi(FT(f))=f. The Fourier Transform F of the original image “f” can be written as follows:
F=A×e
−jφ
We call “A” the magnitude of the Fourier Transform, and φ its phase. To calculate MAF we focus on the variable “A”, as it is the magnitude that contains the information of interest.
A Principle Component Analysis (PCA) technique is then used to evaluate the image that is analyzed by the Fourier Transform. The Fourier Transform “F” may be considered as a probability distribution. Hence, “F” is normalized as follows:
Now, let
We compute me covariance COV of U:
COV=E[(U−E(U))×(U−E(U))T]
Where E is defined as:
As F is symmetric, it follows that E(U)=0. Hence, we have:
COV=E(U×UT)
COV is symmetric and positive-definite matrix. Hence, it can be written as:
σ1 and σ2 are the principal components of F. We define the anisotropy factor γ as:
A suitable programming language, such as Python (version 2.7), can be used to generate the Fourier Transform image from the original image. The computer program can also be used to calculate the Anistropy Factor (AF).
An abrasive particle of an embodiment herein may have a particular MAF, such as at least 1.25 or at least 1.30 or at least 1.40 or at least 1.50 or at least 1.60 or at least 1.70 or at least 1.80 or at least 1.90 or at least 2.00 or at least 2.10 or at least 2.20 or at least 2.30 or at least 2.40 or at least 2.50 or at least 2.60 or at least 2.70 or at least 2.80 or at least 2.90 or at least 3.00 or at least 3.10 or at least 3.20 or at least 3.30 or at least 3.40 or at least 3.50 or at least 3.60 or at least 3.70. Still, according to one non-limiting embodiment, an abrasive particle may have a MAF of not greater than 20, such as not greater than 15 or not greater than 12 or not greater than 10 or not greater than 8 or not greater than 7 or not greater than 6 or not greater than 5 or not greater than 4. It will be appreciated that the MAF can be within a range including any of the minimum and maximum values noted above. Such values and ranges of values are relevant to a collection of abrasive particles formed according to an embodiment.
In another embodiment, the Anisotropy Factor (AF) described in the equations above can be plotted for one or more grains to create a histogram of AF value versus frequency. From the histogram, one can calculate an Anisotropy Factor Standard Deviation (i.e., first standard deviation of the AF histogram). According to one embodiment, the Anisotropy Factor Standard Deviation can be at least 0.75, such as at least 0.8 or at least 0.85 or at least 0.90 or at least 1.00 or at least 1.05 or at least 1.10 or at least 1.20. Still, in another non-limiting embodiment, the Anisotropy Factor Standard Deviation can be not greater than 10, such as not greater than 9 or not greater than 8 or not greater than 7 or not greater than 6 or not greater than 5 or not greater than 4 or not greater than 3 or not greater than 2. It will be appreciated that the Anisotropy Factor Standard Deviation can be within a range including any of the minimum and maximum values noted above. Such values and ranges of values are relevant to a collection of abrasive particles formed according to an embodiment.
As noted herein, the MAF and Anisotropy Factor Standard Deviation can be generated for a single abrasive particle or a collection of abrasive particles. To quantify MAF and Anisotropy Factor Standard Deviation for a single abrasive particle, a suitable number of regions of the side surface should be sampled (e.g., at least 3 distinct regions) to generate a statistically relevant sample set. The MAF and Anisotropy Factor Standard Deviation should be measured at those regions that appear to have the greatest texture (e.g., microridges) to the extent that such regions are large enough for sampling. In some instances, such regions may be associated with controlled cracking during processing. As will be described in embodiments herein the MAF and Anisotropy Factor Standard Deviation can also be used to analyze a collection of abrasive particles. To calculate these values based on a collection of abrasive particles, at least 8 abrasive particles are randomly selected from the collection and three randomly selected regions of the side surface are analyzed. To the extent that certain regions of the side surface demonstrate greater texture, such as illustrated in
According to another aspect, certain abrasive particles of the embodiments herein can have distinct regions, which may have a significantly different MAF and Anisotropy Factor Standard Deviation with respect to each other. For example as illustrated in
According to one embodiment, the first region 1805 of an abrasive particle can have a particular MAF. For example, the MAF can be not greater than 1.20, such as not greater than 1.10 or not greater than 1.00 or not greater than 0.90 or not greater than 0.80 or not greater than 0.70 or not greater than 0.60 or not greater than 0.50 or not greater than 0.40 or not greater than 0.30. Still, in one non-limiting embodiment, the MAF of the first region 1805 of an abrasive particle can be at least 0.30 or at least 0.40 or at least 0.50 or at least 0.60 or at least 0.70 or at least 0.80 or at least 0.90 or at least 1.00 or at least 1.10. It will be appreciated that the MAF of the first region 1805 can be within a range including any of the minimum and maximum values noted above. Such values and ranges of values are relevant to a collection of abrasive particles formed according to an embodiment.
In yet another aspect, the second region 1806 of an abrasive particle can have a particular MAF, such as at least 1.30 or at least 1.40 or at least 1.50 or at least 1.60 or at least 1.70 or at least 1.80 or at least 1.90 or at least 2.00 or at least 2.10 or at least 2.20 or at least 2.30 or at least 2.40 or at least 2.50 or at least 2.60 or at least 2.70 or at least 2.80 or at least 2.90 or at least 3.00 or at least 3.10 or at least 3.20 or at least 3.30 or at least 3.40 or at least 3.50 or at least 3.60 or at least 3.70. In another non-limiting embodiment, the MAF of the second region 1806 of an abrasive particle can be not greater than 20 or not greater than 15 or not greater than 12 or not greater than 10 or not greater than 8 or not greater than 7 or not greater than 6 or not greater than 5 or not greater than 4. It will be appreciated that the MAF of the second region 1806 of an abrasive particle can be within a range including any of the minimum and maximum values noted above. Such values and ranges of values are relevant to a collection of abrasive particles formed according to an embodiment.
As noted above,
As illustrated in
According to one embodiment, the first region 1805 can have an average height of not greater than 90% of the height of the body 1801, such as not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20% or not greater than 10% or not greater than 5%. Still, in another embodiment, the first region 1805 can have an average height of at least 1% of the height of the body or at least 2% or at least 5% or at least 8% or at least 10% or at least 15% or at least 20% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80%. It will be appreciated that the first region 1805 can have an average height within a range including any of the minimum and maximum percentages noted above. In instances where the side surface clearly has only a first and second region (e.g.,
In another embodiment, the second region 1806 can have an average height of not greater than 90% of the height of the body 1801 or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20% or not greater than 10% or not greater than 5%. In still another non-limiting embodiment, the second region 1806 can have an average height of at least 5% of the height of the body or at least 8% or at least 9% or at least 10% or at least 12% or at least 15% or at least 20% or at least 25% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90%. It will be appreciated that the second region 1806 can have an average height within a range including any of the minimum and maximum percentages noted above. Such values and range of values are relevant to a collection of abrasive particles according to embodiments herein.
In certain instances, the abrasive particles of the embodiments herein can have a particular shape on the side surface. As illustrated in
As is evidence from the images provided in
As described in more detail herein, any one of the features described in the embodiments herein can be associated with a collection of abrasive particles. Moreover, it will be appreciated that various combinations of the other features described in embodiments herein can be present in a collection of abrasive particles. A collection of abrasive particles can be a plurality, and more particularly, a portion of abrasive particles present in a fixed abrasive article. The collection can be, but need not necessarily be, formed according to an embodiment. The collection of abrasive particles may in some circumstances include all particles that are part of a fixed abrasive. Alternatively, a collection of abrasive particles may be a portion of free abrasive particles that are not part of a fixed abrasive article.
In one aspect, a collection of abrasive particles can include abrasive particles having a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface. The collection of abrasive particles may have a particular Mean Non-Convexity Factor (MNCF). The MNCF is used to describe the two-dimensional shape of the abrasive particles and is a mean value generated from evaluating the non-convexity factor, which is calculated from a two-dimensional, top-down image of the abrasive particles. It should be noted that a randomly selected abrasive particles are placed on a surface and vibrated. The abrasive particles are presumed to have aligned with their longest axis parallel to the surface and the particles are imaged in such a position or transferred carefully to a suitable surface, being careful to maintain the orientation obtained after vibration, to be mounted for imaging.
As an example,
According to one aspect, a collection of abrasive particles according to an embodiment can have a MNCF of at least 3.5, such as at least 3.75 or at least 4.0 or at least 4.5 or at least 5.0 or at least 5.5 or at least 6.0 or at least 6.5 or at least 7.0 or at least 7.5 or at least 8.0 or at least 8.5 or at least 9.0. Still, in another non-limiting embodiment, the MNCF can be not greater than 30 or not greater than 25 or not greater than 20 or not greater than 18 or not greater than 15 or not greater than 14 or not greater than 13 or not greater than 12 or not greater than 11 or not greater than 10.5. The MNCF can be within a range including any of the minimum and maximum values noted above. It should be noted that the MNCF of the abrasive particles of the embodiments herein may differ significantly from those of shaped abrasive particles, which are formed through different processes and typically have a higher degree of shape fidelity and lower MNCF compared to each other.
Using the histogram of NCF versus frequency one may also evaluate the Non-Convexity Factor Standard Deviation (NCFSD) of the sampling of abrasive particles from the collection of abrasive particles. The NCFSD is a first standard deviation measurement presuming a Gaussian distribution of the data and may indicate the variation in the non-convexity values. According to one embodiment, the abrasive particles of the collection can have a NCFSD of at least 2.4, such as at least 2.5 or at least 2.6 or at least 2.7 or at least 2.8 or at least 2.9 or at least 3.0 or at least 3.1 or at least 3.2 or at least 3.3 or at least 3.4 or at least 3.5. Still, in one non-limiting embodiment, the abrasive particles of the collection can have a NCFSD that is not greater than 30, such as not greater than 25 or not greater than 20 or not greater than 15 or not greater than 10 or not greater than 8 or not greater than 6 or not greater than 4. The NCFSD can be within a range including any of the minimum and maximum values noted above.
The collection of abrasive particles can have any of the features noted in other embodiments, including for example, but not limited to MAF, Anisotropy Factor Standard Deviation, difference in MAF between a first and second region of the side surface, average height of a first region, average height of a second region, difference in relative average heights of the first and second regions to each other, the average height of the first region relative to the average height of the body, the average height of the second region relative to the average height of the body or any combination thereof. The values of any of the features of embodiments herein can be equally applicable to a collection of abrasive particles, with the difference being that any features are measured from a suitable sampling of randomly selected abrasive particles as opposed to a single abrasive particle.
According to one embodiment, the collection of abrasive particles may have a particular standard deviation of height. The height is measured as noted herein along the side surface in a direction substantially perpendicular to at least one of the first or second major surfaces. The forming processes of the embodiments herein may facilitate formation of abrasive particles having a controlled height and particular standard deviation of height, such as not greater than 100 microns or not greater than 90 microns or not greater than 85 microns or not greater than 80 microns or not greater than 75 microns or not greater than 70 microns or not greater than 65 microns or not greater than 60 microns or not greater than 55 microns or not greater than 50 microns or not greater than 45 microns or not greater than 40 microns or not greater than 35 microns. Still, in one non-limiting embodiment, the abrasive particles of the collection can have a standard deviation of height of at least 1 micron, such as at least 5 microns or at least 10 microns or at least 15 microns or at least 20 microns or at least 25 microns or at least 30 microns or at least 35 microns. It will be appreciated that the standard deviation of height for the collection of abrasive particles can be within a range including any of the minimum and maximum values noted above.
According to one embodiment, the substrate 1001 can include an organic material, inorganic material, and a combination thereof. In certain instances, the substrate 1001 can include a woven material. However, the substrate 1001 may be made of a non-woven material. Particularly suitable substrate materials can include organic materials, including polymers, and particularly, polyester, polyurethane, polypropylene, polyimides such as KAPTON from DuPont, paper. Some suitable inorganic materials can include metals, metal alloys, and particularly, foils of copper, aluminum, steel, and a combination thereof.
The make coat 1003 can be applied to the surface of the substrate 1001 in a single process, or alternatively, the abrasive particulate materials 1005, 1006, 1007 can be combined with a make coat 1003 material and applied as a mixture to the surface of the substrate 1001. Suitable materials of the make coat 1003 can include organic materials, particularly polymeric materials, including for example, polyesters, epoxy resins, polyurethanes, polyamides, polyacrylates, polymethacrylates, poly vinyl chlorides, polyethylene, polysiloxane, silicones, cellulose acetates, nitrocellulose, natural rubber, starch, shellac, and mixtures thereof. In one embodiment, the make coat 1003 can include a polyester resin. The coated substrate can then be heated in order to cure the resin and the abrasive particulate material to the substrate. In general, the coated substrate 1001 can be heated to a temperature of between about 100° C. to less than about 250° C. during this curing process.
Moreover, it will be appreciated that the coated abrasive article can include one or more collections of various types of abrasive particles, including the abrasive particulate materials 1005, 1006, and 1007, which may represent the abrasive particles of the embodiments herein. The embodiments herein can include a fixed abrasive article (e.g., a coated abrasive article) having a first collection of abrasive particles (e.g., abrasive particulate materials 1005) representative of the abrasive particles of the embodiments herein. Any fixed abrasive may further employ a second collection of abrasive particles therein, which may be representative of another type of abrasive particle according to the embodiments herein, which may be distinct in one or more manners from the abrasive particles of the first collection, including but not limited to, one or more abrasive characteristics as described herein. The same features may be utilized in a bonded abrasive article.
The abrasive particulate materials 1005, 1006, and 1007 can include different types of abrasive particles according to embodiments herein. The different types of abrasive particles can differ from each other in composition, two-dimensional shape, three-dimensional shape, size, and a combination thereof as described in the embodiments herein. As illustrated, the coated abrasive 1000 can include a first type of abrasive particle 1005 and a second type of shaped abrasive particle 1006. The coated abrasive 1000 can include different amounts of the first type and second type of abrasive particles 1005 and 1006. It will be appreciated that the coated abrasive may not necessarily include different types of abrasive particles, and can consist essentially of a single type of abrasive particle. As will be appreciated, the abrasive particles of the embodiments herein can be incorporated into various fixed abrasives (e.g., bonded abrasives, coated abrasive, non-woven abrasives, thin wheels, cut-off wheels, reinforced abrasive articles, and the like), including in the form of blends, which may include different types of shaped abrasive particles, shaped abrasive particles with diluent particles, and the like. Moreover, according to certain embodiments, a batch of particulate material may be incorporated into the fixed abrasive article in a predetermined orientation, wherein each of the abrasive particles can have a predetermined orientation relative to each other and relative to a portion of the abrasive article (e.g., the backing of a coated abrasive).
The abrasive particles 1007 can be diluent particles different than the first and second types of abrasive particles 1005 and 1006. For example, the diluent particles can differ from the first and second types of abrasive particles 1005 and 1006 in composition, two-dimensional shape, three-dimensional shape, size, and a combination thereof. For example, the abrasive particles 1007 can represent conventional, crushed abrasive grit having random shapes. The abrasive particles 1007 may have a median particle size less than the median particle size of the first and second types of abrasive particles 1005 and 1006.
After sufficiently forming the make coat 503 with the abrasive particulate materials 1005, 1006, 1007 contained therein, the size coat 1004 can be formed to overlie and bond the abrasive particulate materials 1005, 1006, 1007 in place. The size coat 1004 can include an organic material, may be made essentially of a polymeric material, and notably, can use polyesters, epoxy resins, polyurethanes, polyamides, polyacrylates, polymethacrylates, poly vinyl chlorides, polyethylene, polysiloxane, silicones, cellulose acetates, nitrocellulose, natural rubber, starch, shellac, and mixtures thereof.
The abrasive particulate material 1102 of the bonded abrasive 1100 can include different types of abrasive particles 1103, 1104, 1105, and 1106, which can have any of the features of different types of abrasive particles as described in the embodiments herein (e.g., shaped, CHAP, etc.). Notably, the different types of abrasive particles 1103, 1104, 1105, and 1106 can differ from each other in composition, two-dimensional shape, three-dimensional shape, size, and a combination thereof as described in the embodiments herein.
The bonded abrasive 1100 can include a type of abrasive particulate material 1107 representing diluent abrasive particles, which can differ from the different types of abrasive particles 1103, 1104, 1105, and 1106 in composition, two-dimensional shape, three-dimensional shape, size, and a combination thereof.
The porosity 1108 of the bonded abrasive 1100 can be open porosity, closed porosity, and a combination thereof. The porosity 1108 may be present in a majority amount (vol %) based on the total volume of the body of the bonded abrasive 1100. Alternatively, the porosity 1108 can be present in a minor amount (vol %) based on the total volume of the body of the bonded abrasive 1100. The bond material 1101 may be present in a majority amount (vol %) based on the total volume of the body of the bonded abrasive 1100. Alternatively, the bond material 1101 can be present in a minor amount (vol %) based on the total volume of the body of the bonded abrasive 1100. Additionally, abrasive particulate material 1102 can be present in a majority amount (vol %) based on the total volume of the body of the bonded abrasive 1100. Alternatively, the abrasive particulate material 1102 can be present in a minor amount (vol %) based on the total volume of the body of the bonded abrasive 1100.
According to one embodiment, a collection of abrasive particles can include at least a first abrasive particle and a second abrasive particle, wherein the first abrasive particle has a different two-dimensional shape compared to the two-dimensional shape of the second abrasive particle. The two-dimensional shape is the shape of the particle as viewed top-down in the plane defined by the length and width of the particle body. For example, the particle of
Moreover, as illustrated in
The collection of abrasive particles can be incorporated into fixed abrasive, such as a coated abrasive, bonded abrasive, and the like. Within a collection there may be groups of particles. Groups of particles are particles that have the same two-dimensional shape with respect to each other. For example, a collection of abrasive particles can include a first group of abrasive particles, wherein each of the particles of the first group has substantially the same two-dimensional shape. Referring again to
It will be appreciated that the embodiments herein also include a collection of abrasive particles including at least one abrasive particle having a plurality of microridges along the side surface of the body. Reference herein to the microridges will be understood to be reference to any type of the microridges or a combination of types of microridges. More particularly, in one embodiment, a majority of the abrasive particles of the collection of abrasive particles can include a plurality of microridges on at least a portion of the side surfaces. For example, in at least one aspect, at least 51% of the abrasive particles of the collection of abrasive particles include the plurality of microridges on at least a portion of their side surface, such as at least 52% or at least 54% or at least 56% or at least 58% or at least 60% or at least 62% or at least 64% or at least 66% or at least 68% or at least 70% or at least 72% or at least 74% or at least 76% or at least 78% or at least 80% or at least 82% or at least 84% or at least 86% or at least 88% or at least 90% or at least 92% or at least 94% or at least 96% or at least 98% or at least 99% of the abrasive particles of the collection of abrasive particles. Still, in at least one non-limiting embodiment, not greater than 99% of the abrasive particles of the collection of abrasive particles may include the plurality of microridges on at least a portion of the side surface, such as, not greater than 98% or not greater than 96% or not greater than 94% or not greater than 92% or not greater than 90% or not greater than 88% or not greater than 86% or not greater than 84% or not greater than 82% or not greater than 80% or not greater than 78% or not greater than 76% or not greater than 74% or not greater than 72% or not greater than 70% or not greater than 68% or not greater than 66% or not greater than 64% or not greater than 62% or not greater than 60% or not greater than 58% or not greater than 56% or not greater than 54% or not greater than 52% of the abrasive particles of the collection of abrasive particles. It will be appreciated that the percentage of abrasive particles in the collection of abrasive particles including the plurality of microridges on at least a portion of the side surfaces can be within a range including any of the minimum and maximum percentages noted above.
In yet another embodiment, a majority of the total surface area of the side surfaces of the abrasive particles in the collection can include a plurality of microridges. For example, at least 51% of the total surface area of the side surfaces of the abrasive particles of the collection can include the plurality of microridges or at least 52% or at least 54% or at least 56% or at least 58% or at least 60% or at least 62% or at least 64% or at least 66% or at least 68% or at least 70% or at least 72% or at least 74% or at least 76% or at least 78% or at least 80% or at least 82% or at least 84% or at least 86% or at least 88% or at least 90% or at least 92% or at least 94% or at least 96% or at least 98% or at least 99%. In one non-limiting embodiment, not greater than 99% of the total surface area of the sides surfaces of the abrasive particles of the collection can include the plurality of microridges, such as, not greater than 98% or not greater than 96% or not greater than 94% or not greater than 92% or not greater than 90% or not greater than 88% or not greater than 86% or not greater than 84% or not greater than 82% or not greater than 80% or not greater than 78% or not greater than 76% or not greater than 74% or not greater than 72% or not greater than 70% or not greater than 68% or not greater than 66% or not greater than 64% or not greater than 62% or not greater than 60% or not greater than 58% or not greater than 56% or not greater than 54% or not greater than 52%. It will be appreciated that the total surface area of the side surface of the abrasive particles in the collection including the plurality of microridges can be within a range including any of the minimum and maximum percentages noted above.
In yet another aspect, the side surfaces of the bodies of the abrasive particles having side surface portions, where each side surface portion is that portion of the side surface extending between external corners of the body. Generally, each abrasive particle has at least three side surface portions extending around the peripheral surface of the body between the first and second major surfaces. For at least one embodiment, the collection of abrasive particles can be formed such that at least one abrasive particle in the collection has at least 45% of the side surface portions of the body including the plurality of microridges. In another embodiment, at least 10% of the abrasive particles of the collection have at least 45% of the side surface portion of the body including the plurality of microridges. In other instances, the percentage of abrasive particles in the collection having at least 45% of the side surface portions of the body including the plurality of microridges can be greater, such as at least 20% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90% or at least 95% It will be appreciated that in one embodiment, each of the abrasive particles of the collection can include at least 45% of the side surface portions of the body including the plurality of microridges. Still, in one non-limiting embodiment, the percentage of abrasive particles of the collection including at least 45% of the side surface portions of the body including the plurality of microridges can be not greater than 98% or not greater than 90% or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20% or not greater than 10%. It will be appreciated that the percentage of abrasive particles of the collection having at least 45% of the side surface portions of the body including the plurality of microridges can be within a range including any of the minimum and maximum values noted above.
In still another embodiment, the collection of abrasive particles can include abrasive particles having a greater percentage of the side surface portions including the plurality of microridges. For example, at least 52% of the side surface portions of the body include the plurality of microridges, or at least 54% or at least 56% or at least 58% or at least 60% or at least 62% or at least 64% or at least 66% or at least 68% or at least 70% or at least 72% or at least 74% or at least 76% or at least 78% or at least 80% or at least 82% or at least 84% or at least 86% or at least 88% or at least 90% or at least 92% or at least 94% or at least 96% or at least 98% or at least 99% of the side surface portions of the body include the plurality of microridges. It will be appreciated that the percentage of side surface portions including the plurality of microridges can be combined with any of the foregoing percentages of particle in the collection identified as having the plurality of microridges. For example, it is contemplated that in certain embodiments, at least 10% of the abrasive particles of the collection can have at least 50% of their side surface portions having the plurality of microridges. In another example, at least 50% of the abrasive particles of the collection may have at least 50% of their side surface portions having the plurality of microridges. And as a further example, in another embodiment, it may be noted that at least 70% of the abrasive particles of the collection may have at least 60% of their side surface portions having the plurality of microridges. And yet in another embodiment, each of the abrasive particles of the collection can have all side surface portions including the plurality of microridges.
The formation of a collection of abrasive particles, which may or may not have discrete groups of abrasive particles in the collection may be controlled by one or more process parameters, including but not limited to, the shape of the form used to modify the mixture, the modification process, the drying process, and the like. It will be appreciated that a collection of abrasive particle can include a plurality of groups of abrasive particles, and particularly, more than two distinct groups of abrasive particles.
Many different aspects and embodiments are possible. Some of those aspects and embodiments are described herein. After reading this specification, skilled artisans will appreciate that those aspects and embodiments are only illustrative and do not limit the scope of the present invention. Embodiments may be in accordance with any one or more of the embodiments as listed below.
Embodiment 1. An abrasive particle comprising:
a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the side surface comprises a Mean Anisotropy Factor of at least 1.25.
Embodiment 2. An abrasive particle comprising:
a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the first major surface comprises a first protrusion disposed abutting a first side surface portion and extending along at least a portion of the first side surface portion, and further comprising an untextured region extending through a central region of the body, wherein the untextured region defines a majority of a total surface area of the first major surface.
Embodiment 3. An abrasive particle comprising:
a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein a majority of the side surface comprises a plurality of microridges.
Embodiment 4. The abrasive particle of any one of embodiments 2 and 3, wherein the side surface comprises a Mean Anisotropy Factor of at least 1.25.
Embodiment 5. The abrasive particle of any one of embodiments 1 and 4, wherein the Mean Anisotropy Factor is at least 1.30 or at least 1.40 or at least 1.50 or at least 1.60 or at least 1.70 or at least 1.80 or at least 1.90 or at least 2.00 or at least 2.10 or at least 2.20 or at least 2.30 or at least 2.40 or at least 2.50 or at least 2.60 or at least 2.70 or at least 2.80 or at least 2.90 or at least 3.00 or at least 3.10 or at least 3.20 or at least 3.30 or at least 3.40 or at least 3.50 or at least 3.60 or at least 3.70.
Embodiment 6. The abrasive particle of any one of embodiments 1 and 4, wherein the Mean Anisotropy Factor is not greater than 20 or not greater than 15 or not greater than 12 or not greater than 10 or not greater than 8 or not greater than 7 or not greater than 6 or not greater than 5 or not greater than 4.
Embodiment 7. The abrasive particle of any one of embodiments 1, 2, and 3, wherein the side surface comprises an Anisotropy Factor Standard Deviation of at least 0.75 or at least 0.8 or at least 0.85 or at least 0.90 or at least 1.00 or at least 1.05 or at least 1.10 or at least 1.20.
Embodiment 8. The abrasive particle of any one of embodiments 1, 2, and 3, wherein the side surface comprises an Anisotropy Factor Standard Deviation of not greater than 10 or not greater than 9 or not greater than 8 or not greater than 7 or not greater than 6 or not greater than 5 or not greater than 4 or not greater than 3 or not greater than 2.
Embodiment 9. The abrasive particle of any one of embodiments 1, 2, and 3, wherein the side surface comprises a first region extending from the first major surface and a second region extending from the second major surface, and wherein the first region and second region abut on the side surface, and wherein the second region comprises a Mean Anisotropy Factor that is greater than the first region.
Embodiment 10. The abrasive particle of embodiment 9, wherein the second region extends for a greater percentage of the height as compared to the first region.
Embodiment 11. The abrasive particle of embodiment 9, wherein the first region has an average height of not greater than 90% of the height of the body or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20% or not greater than 10% or not greater than 5%.
Embodiment 12. The abrasive particle of embodiment 9, wherein the first region has an average height of at least 1% of the height of the body or at least 2% or at least 5% or at least 8% or at least 10% or at least 15% or at least 20% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80%.
Embodiment 13. The abrasive particle of embodiment 9, wherein the second region comprises an average height of not greater than 90% of the height of the body or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20% or not greater than 10% or not greater than 5%.
Embodiment 14. The abrasive particle of embodiment 9, wherein the second region has an average height of at least 5% of the height of the body or at least 8% or at least 9% or at least 10% or at least 12% or at least 15% or at least 20% or at least 25% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90%.
Embodiment 15. The abrasive particle of embodiment 9, wherein the first region comprises a Mean Anisotropy Factor of not greater than 1.20 or not greater than 1.10 or not greater than 1.00 or not greater than 0.90 or not greater than 0.80 or not greater than 0.70 or not greater than 0.60 or not greater than 0.50 or not greater than 0.40 or not greater than 0.30.
Embodiment 16. The abrasive particle of embodiment 9, wherein the Mean Anisotropy Factor of the first region is at least 0.30 or at least 0.40 or at least 0.50 or at least 0.60 or at least 0.70 or at least 0.80 or at least 0.90 or at least 1.00 or at least 1.10.
Embodiment 17. The abrasive particle of embodiment 9, wherein the Mean Anisotropy Factor of the second region at least 1.30 or at least 1.40 or at least 1.50 or at least 1.60 or at least 1.70 or at least 1.80 or at least 1.90 or at least 2.00 or at least 2.10 or at least 2.20 or at least 2.30 or at least 2.40 or at least 2.50 or at least 2.60 or at least 2.70 or at least 2.80 or at least 2.90 or at least 3.00 or at least 3.10 or at least 3.20 or at least 3.30 or at least 3.40 or at least 3.50 or at least 3.60 or at least 3.70.
Embodiment 18. The abrasive particle of embodiment 9, wherein the Mean Anisotropy Factor of the second region is not greater than 20 or not greater than 15 or not greater than 12 or not greater than 10 or not greater than 8 or not greater than 7 or not greater than 6 or not greater than 5 or not greater than 4.
Embodiment 19. The abrasive particle of embodiment 9, wherein the first region and second region define a stepped region on the side surface of the body.
Embodiment 20. The abrasive particle of embodiment 9, wherein the second region comprises a plurality of microridges.
Embodiment 21. The abrasive particle of embodiment 20, wherein the plurality of microridges extend in substantially the same direction relative to each other.
Embodiment 22. The abrasive particle of any one of embodiments 1, 2, and 3, wherein the first major surface and second major surface are substantially parallel to each other.
Embodiment 23. The abrasive particle of any one of embodiments 1 and 2, wherein a majority of the side surface comprises a plurality of microridges.
Embodiment 24. The abrasive particle of any one of embodiments 3 and 23, wherein at least a portion of the plurality of microridges comprises a plurality of isolated microridges defined by microridges extending from the side surface and separated by generally smooth planar regions.
Embodiment 25. The abrasive particle of embodiment 24, wherein the plurality of isolated microridges extend along the side surface in an irregular path.
Embodiment 26. The abrasive particle of embodiment 24, wherein at least one of the isolated microridges of the plurality of isolated microridges comprises a head region and a tail region connected to and extending from the head region, wherein the head region has a rounded shape and the tail region has an elongated shape.
Embodiment 27. The abrasive particle of any one of embodiments 3 and 23, wherein at least a portion of the plurality of microridges comprises a plurality of scaled microridges.
Embodiment 28. The abrasive particle of embodiment 27, wherein at least a portion of the scaled microridges of the plurality of scaled microridges comprise a primary ridge and a plurality of wrinkles extending from the primary ridge.
Embodiment 29. The abrasive particle of embodiment 28, wherein the primary ridge extends along the side surface in an irregular path.
Embodiment 30. The abrasive particle of embodiment 28, wherein at least a portion of the plurality of wrinkles extend along the side surface in an irregular path away from the primary ridge.
Embodiment 31. The abrasive particle of embodiment 28, wherein the wrinkles are defined grooves extending along the side surface along an irregular path.
Embodiment 32. The abrasive particle of embodiment 28, wherein the wrinkles extend along a curved path.
Embodiment 33. The abrasive particle of embodiment 28, wherein the plurality of scaled microridges includes a greater number of wrinkles compared to the number of primary ridges.
Embodiment 34. The abrasive particle of embodiment 28, wherein the wrinkles extend in a different direction compared to one or more primary ridges, and the wrinkles extend between two or more primary ridges.
Embodiment 35. The abrasive particle of embodiment 28, wherein the primary ridge includes at least one gap between elongated portions.
Embodiment 36. The abrasive particle of embodiment 27, wherein at least a portion of the scaled microridges have a scaled appearance.
Embodiment 37. The abrasive particle of embodiment 27, wherein at least a portion of the scaled microridges have a layered appearance.
Embodiment 38. The abrasive particle of embodiment 27, wherein at least a portion of the scaled microridges include a plurality of raised portions with irregular shapes and wrinkles extending between the plurality of raised portions.
Embodiment 39. The abrasive particle of any one of embodiments 3 and 23, wherein the plurality of microridges is a conchoidal fracturing feature.
Embodiment 40. The abrasive particle of any one of embodiments 3 and 23, wherein the plurality of microridges is formed during controlled cracking of the side surface.
Embodiment 41. The abrasive particle of any one of embodiments 3 and 23, wherein the plurality of microridges includes a precipice region.
Embodiment 42. The abrasive particle of any one of embodiments 3 and 23, wherein at least 51% of the total surface area of the side surface includes the plurality of microridges or at least 52% or at least 54% or at least 56% or at least 58% or at least 60% or at least 62% or at least 64% or at least 66% or at least 68% or at least 70% or at least 72% or at least 74% or at least 76% or at least 78% or at least 80% or at least 82% or at least 84% or at least 86% or at least 88% or at least 90% or at least 92% or at least 94% or at least 96% or at least 98% or at least 99%.
Embodiment 43. The abrasive particle of embodiment 42, wherein not greater than 99% of the total surface area of the sides surface includes the plurality of microridges or not greater than 98% or not greater than 96% or not greater than 94% or not greater than 92% or not greater than 90% or not greater than 88% or not greater than 86% or not greater than 84% or not greater than 82% or not greater than 80% or not greater than 78% or not greater than 76% or not greater than 74% or not greater than 72% or not greater than 70% or not greater than 68% or not greater than 66% or not greater than 64% or not greater than 62% or not greater than 60% or not greater than 58% or not greater than 56% or not greater than 54% or not greater than 52%.
Embodiment 44. The abrasive particle of any one of embodiments 3 and 23, wherein the side surface of the body includes side surface portions, and wherein each side surface portion extends between external corners of the body, and wherein at least 45% of the side surface portions include the plurality of microridges.
Embodiment 45. The abrasive particle of embodiment 44, wherein the body includes at least three side surface portions including the plurality of microridges.
Embodiment 46. The abrasive particle of embodiment 44, wherein all of the side surface portions include the plurality of microridges.
Embodiment 47. The abrasive particle of embodiment 44, wherein at least 52% of the side surface portions of the body include the plurality of microridges, or at least 54% or at least 56% or at least 58% or at least 60% or at least 62% or at least 64% or at least 66% or at least 68% or at least 70% or at least 72% or at least 74% or at least 76% or at least 78% or at least 80% or at least 82% or at least 84% or at least 86% or at least 88% or at least 90% or at least 92% or at least 94% or at least 96% or at least 98% or at least 99%.
Embodiment 48. The abrasive particle of embodiment 44, wherein the body includes at least one side surface portion that does not include the plurality of microridges.
Embodiment 49. The abrasive particle of any one of embodiments 1 and 3, further comprising a first protrusion abutting the first side surface portion and extending along at least a portion of the first side surface portion.
Embodiment 50. The abrasive particle of any one of embodiments 2 and 49, wherein the first major surface comprises a first depression extending in a direction parallel to a first side surface portion, and wherein the first protrusion is disposed between the first side surface portion and the first depression, the first protrusion abutting the first side surface portion and extending along at least a portion of the first side surface portion.
Embodiment 51. The abrasive particle of any one of embodiments 2 and 50, wherein the first protrusion extends for at least 30% of the total length of the first side surface portion or at least 40% of the total length of the first side surface portion or at least 50% of the total length of the first side surface portion or at least 60% of the total length of the first side surface portion or at least 70% of the total length of the first side surface portion or at least 80% of the total length of the first side surface portion or at least 90% of the total length of the first side surface portion.
Embodiment 52. The abrasive particle of any one of embodiments 2 and 50, wherein the first depression extends for at least 30% of the total length of the first side surface portion or at least 40% of the total length of the first side surface portion or at least 50% of the total length of the first side surface portion or at least 60% of the total length of the first side surface portion or at least 70% of the total length of the first side surface portion or at least 80% of the total length of the first side surface portion or at least 90% of the total length of the first side surface portion.
Embodiment 53. The abrasive particle of any one of embodiments 2 and 50, wherein the first side surface portion is defined as a portion of the side surface extending between two external corners of the body.
Embodiment 54. The abrasive particle of any one of embodiments 2 and 50, wherein the first side surface portion is a fraction of the total length of the side surface defining the perimeter of the body.
Embodiment 55. The abrasive particle of any one of embodiments 2 and 50, wherein the first protrusion extends for a fraction of the total length of the side surface defining the perimeter of the body.
Embodiment 56. The abrasive particle of any one of embodiments 2 and 50, wherein the first depression extends for a fraction of the total length of the side surface defining the perimeter of the body.
Embodiment 57. The abrasive particle of any one of embodiments 2 and 50, wherein the first side surface portion and first protrusion have substantially the same contour as viewed in the plane of the first major surface.
Embodiment 58. The abrasive particle of any one of embodiments 2 and 50, wherein the first protrusion intersects a second side surface portion that is distinct from the first side surface portion.
Embodiment 59. The abrasive particle of any one of embodiments 1 and 3, further comprising an untextured region extending through a central region of the body, wherein the untextured region defines a majority of a total surface area of the first major surface.
Embodiment 60. The abrasive particle of any one of embodiments 2 and 59, wherein the untextured region defines at least 55% of the total surface area of the first major surface or at least 60% or at least 65% or at least 70% or at least 75% or at least 80% or at least 85% or at least 90%.
Embodiment 61. The abrasive particle of any one of embodiments 2 and 59, wherein the untextured region defines not greater than 99% of the total surface area of the first major surface or not greater than 95% or not greater than 90% or not greater than 85% or not greater than 80% or not greater than 75% or not greater than 70% or not greater than 65% or not greater than 60% or not greater than 55%.
Embodiment 62. The abrasive particle of any one of embodiments 2 and 59, wherein the first protrusion abuts a portion of the untextured region, and wherein the first protrusion is spaced apart from the central region of the body.
Embodiment 63. The abrasive particle of any one of embodiments 2 and 59, wherein the first protrusion extends above the surface of the untextured region.
Embodiment 64. The abrasive particle of any one of embodiments 2 and 59, wherein the untextured region abuts a portion of the side surface of the body.
Embodiment 65. The abrasive particle of any one of embodiments 2 and 59, wherein the untextured region comprises a two-dimensional shape substantially the same as the two-dimensional shape of the body.
Embodiment 66. The abrasive particle of any one of embodiments 2 and 50, wherein the first depression has an average depth that is at least 5% and not greater than 99% of an average height of the body.
Embodiment 67. The abrasive particle of any one of embodiments 2 and 50, wherein the first protrusion has an average height that is at least 5% and not greater than 99% of an average height of the body.
Embodiment 68. The abrasive particle of any one of embodiments 2 and 50, further comprising a second protrusion abutting a second side surface portion and extending along the second side surface portion.
Embodiment 69. The abrasive particle of embodiment 68, wherein the first major surface comprises a second depression extending in a direction parallel to the second side surface portion.
Embodiment 70. The abrasive particle of embodiment 69, wherein the first depression intersects the second depression.
Embodiment 71. The abrasive particle of embodiment 69, wherein the first depression and second depression intersect proximate to an external corner separating the first side surface portion and second side surface portion.
Embodiment 72. The abrasive particle of embodiment 69, wherein the second protrusion abuts the first depression.
Embodiment 73. The abrasive particle of embodiment 69, wherein the first protrusion abuts the second depression.
Embodiment 74. The abrasive particle of embodiment 69, wherein the first protrusion abuts the second protrusion.
Embodiment 75. The abrasive particle of any one of embodiments 2 and 50, further comprising an unfeatured edge extending between the first major surface and a third portion of a side surface, wherein the third side surface portion is distinct from the first side surface portion.
Embodiment 76. The abrasive particle of embodiment 75, wherein the third side surface portion and first side surface portion are separated from each other by at least one external corner on the side surface.
Embodiment 77. The abrasive particle of any one of embodiments 2 and 50, wherein the body includes a bottom edge joining the second major surface and the side surface, wherein at least a portion of the bottom edge has an irregular contour.
Embodiment 78. The abrasive particle of any one of embodiments 1, 2 and 3, wherein the body comprises a two-dimensional shape as viewed in a plane defined by a length and a width of the body selected from the first group consisting of regular polygons, irregular polygons, ellipsoids, numerals, Greek alphabet characters, Latin alphabet characters, Russian alphabet characters, complex shapes having a combination of polygonal shapes, a shape with linear and curved portions, and a combination thereof.
Embodiment 79. The abrasive particle of any one of embodiments 1, 2 and 3, wherein the body comprises an irregular two-dimensional shape as viewed in a plane defined by a length and a width of the body.
Embodiment 80. The abrasive particle of any one of embodiments 1, 2 and 3, wherein the body includes at least one material from the group of oxides, carbides, nitrides, borides, oxycarbides, oxynitrides, oxyborides, natural minerals, synthetic materials, carbon-based materials, and a combination thereof.
Embodiment 81. The abrasive particle of any one of embodiments 1, 2 and 3, wherein the body comprises alumina.
Embodiment 82. The abrasive particle of any one of embodiments 1, 2 and 3, wherein the body consists essentially of alumina.
Embodiment 83. The abrasive particle of any one of embodiments 1, 2 and 3, wherein the body includes at least one oxide from the group of aluminum oxide, zirconium oxide, titanium oxide, yttrium oxide, chromium oxide, strontium oxide, silicon oxide, magnesium oxide, rare-earth oxides, or any combination thereof.
Embodiment 84. The abrasive particle of any one of embodiments 1, 2 and 3, further comprising a fixed abrasive including the abrasive particle.
Embodiment 85. The abrasive particle of embodiment 69, wherein the fixed abrasive is a coated abrasive.
Embodiment 86. The abrasive particle of embodiment 69, wherein the fixed abrasive is a bonded abrasive.
Embodiment 87. A collection of abrasive particles comprising:
a first abrasive particle comprising:
a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the body of the first abrasive particle comprises a first two-dimensional shape, and wherein the first major surface comprises a first protrusion abutting and extending along at least a portion of a first side surface portion of the side surface, and wherein the body further comprises an untextured region extending through a central region of the body, wherein the untextured region defines a majority of a total surface area of the first major surface; and a second abrasive particle comprising:
a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the body of the second abrasive particle comprises a two-dimensional shape that is different compared to the two-dimensional shape of the first abrasive particle.
Embodiment 88. A collection of abrasive particles, wherein each abrasive particle of the collection of abrasive particles includes a body having a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, and wherein a majority of the particles of the collection of abrasive particles comprises a plurality of microridges extending along at least a portion of the sides surface.
Embodiment 89. A collection of abrasive particles, wherein an abrasive particle of the collection of abrasive particles includes:
a body having a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, and wherein the side surface includes a plurality of side surface portions extending between external corners of the body; and wherein at least 45% of the side surface portions of the body include a plurality of microridges.
Embodiment 90. A collection of abrasive particles, wherein each abrasive particle of the collection of abrasive particles comprises:
a body having a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the first major surface and second major surface are substantially parallel with each other; and wherein the collection of abrasive particles comprises a Mean Non-Convexity Factor of at least 3.5 and a Non-Convexity Factor Standard Deviation of at least 2.4.
Embodiment 91. A collection of abrasive particles, wherein each abrasive particle of the collection of abrasive particles comprises:
a body having a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface; and wherein the collection of abrasive particles comprises a Mean Anisotropy Factor of at least 1.25.
Embodiment 92. A collection of abrasive particles, wherein each abrasive particle of the collection of abrasive particles comprises:
a body having a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the body comprises a height as defined as the distance along the side surface between the first major surface and the second major surface;
wherein the collection of abrasive particles comprises a standard deviation of height of not greater than 100; and wherein the collection of abrasive particles comprises a Mean Non-Convexity Factor of at least 3.5.
Embodiment 93. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, and 92, further comprising a Mean Anisotropy Factor of at least 1.25.
Embodiment 94. The collection of abrasive particles of any one of embodiments 91 and 93, wherein the Mean Anisotropy Factor is at least 1.30 or at least 1.40 or at least 1.50 or at least 1.60 or at least 1.70 or at least 1.80 or at least 1.90 or at least 2.00 or at least 2.10 or at least 2.20 or at least 2.30 or at least 2.40 or at least 2.50 or at least 2.60 or at least 2.70 or at least 2.80 or at least 2.90 or at least 3.00 or at least 3.10 or at least 3.20 or at least 3.30 or at least 3.40 or at least 3.50 or at least 3.60 or at least 3.70.
Embodiment 95. The collection of abrasive particles of any one of embodiments 91 and 93, wherein the Mean Anisotropy Factor is not greater than 20 or not greater than 15 or not greater than 12 or not greater than 10 or not greater than 8 or not greater than 7 or not greater than 6 or not greater than 5 or not greater than 4.
Embodiment 96. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, further comprising an Anisotropy Factor Standard Deviation of at least 0.75 or at least 0.8 or at least 0.85 or at least 0.90 or at least 1.00 or at least 1.05 or at least 1.10 or at least 1.20.
Embodiment 97. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, further an Anisotropy Factor Standard Deviation of not greater than 10 or not greater than 9 or not greater than 8 or not greater than 7 or not greater than 6 or not greater than 5 or not greater than 4 or not greater than 3 or not greater than 2.
Embodiment 98. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, wherein the side surface comprises a first region extending from the first major surface and a second region extending from the second major surface, and wherein the first region and second region abut on the side surface, and wherein the second region comprises a Mean Anisotropy Factor that is greater than the first region.
Embodiment 99. The collection of abrasive particles of embodiment 98, wherein the second region extends for a greater percentage of the height as compared to the first region.
Embodiment 100. The collection of abrasive particles of embodiment 98, wherein the first region has an average height of not greater than 90% of the height of the body or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20% or not greater than 10% or not greater than 5%.
Embodiment 101. The collection of abrasive particles of embodiment 98, wherein the first region has an average height of at least 1% of the height of the body or at least 2% or at least 5% or at least 8% or at least 10% or at least 15% or at least 20% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80%.
Embodiment 102. The collection of abrasive particles of embodiment 98, wherein the second region comprises an average height of not greater than 90% of the height of the body or not greater than 80% or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30% or not greater than 20% or not greater than 10% or not greater than 5%.
Embodiment 103. The collection of abrasive particles of embodiment 98, wherein the first region has an average height of at least 5% of the height of the body or at least 8% or at least 9% or at least 10% or at least 12% or at least 15% or at least 20% or at least 25% or at least 30% or at least 40% or at least 50% or at least 60% or at least 70% or at least 80% or at least 90%.
Embodiment 104. The collection of abrasive particles of embodiment 98, wherein the first region comprises a Mean Anisotropy Factor of not greater than 1.20 or not greater than 1.10 or not greater than 1.00 or not greater than 0.90 or not greater than 0.80 or not greater than 0.70 or not greater than 0.60 or not greater than 0.50 or not greater than 0.40 or not greater than 0.30.
Embodiment 105. The collection of abrasive particles of embodiment 98, wherein the Mean Anisotropy Factor of the first region is at least 0.30 or at least 0.40 or at least 0.50 or at least 0.60 or at least 0.70 or at least 0.80 or at least 0.90 or at least 1.00 or at least 1.10.
Embodiment 106. The collection of abrasive particles of embodiment 98, wherein the Mean Anisotropy Factor of the second region at least 1.30 or at least 1.40 or at least 1.50 or at least 1.60 or at least 1.70 or at least 1.80 or at least 1.90 or at least 2.00 or at least 2.10 or at least 2.20 or at least 2.30 or at least 2.40 or at least 2.50 or at least 2.60 or at least 2.70 or at least 2.80 or at least 2.90 or at least 3.00 or at least 3.10 or at least 3.20 or at least 3.30 or at least 3.40 or at least 3.50 or at least 3.60 or at least 3.70.
Embodiment 107. The collection of abrasive particles of embodiment 98, wherein the Mean Anisotropy Factor of the second region is not greater than 20 or not greater than 15 or not greater than 12 or not greater than 10 or not greater than 8 or not greater than 7 or not greater than 6 or not greater than 5 or not greater than 4.
Embodiment 108. The collection of abrasive particles of embodiment 98, wherein the first region and second region define a stepped region on the side surface of the body.
Embodiment 109. The collection of abrasive particles of embodiment 98, wherein the second region comprises a plurality of microridges.
Embodiment 110. The collection of abrasive particles of embodiment 98, wherein the plurality of microridges extend in substantially the same direction relative to each other.
Embodiment 111. The collection of abrasive particles of any one of embodiments 87, 88, 89, 91, and 92, further comprising a Mean Non-Convexity Factor of at least 3.5.
Embodiment 112. The collection of abrasive particles of any one of embodiments 90 and 111, wherein the Mean Non-Convexity Factor is at least 3.75 or at least 4.0 or at least 4.5 or at least 5.0 or at least 5.5 or at least 6.0 or at least 6.5 or at least 7.0 or at least 7.5 or at least 8.0 or at least 8.5 or at least 9.0.
Embodiment 113. The collection of abrasive particles of any one of embodiments 90 and 111, wherein the Mean Non-Convexity Factor is not greater than 30 or not greater than 25 or not greater than 20 or not greater than 18 or not greater than 15 or not greater than 14 or not greater than 13 or not greater than 12 or not greater than 11 or not greater than 10.5.
Embodiment 114. The collection of abrasive particles of any one of embodiments 87, 88, 89, 91, and 92, further comprising a Non-Convexity Factor Standard Deviation of at least 2.4.
Embodiment 115. The collection of abrasive particles of any one of embodiments 90 and 114, wherein the Non-Convexity Factor Standard Deviation is at least 2.5 or at least 2.6 or at least 2.7 or at least 2.8 or at least 2.9 or at least 3.0 or at least 3.1 or at least 3.2 or at least 3.3 or at least 3.4 or at least 3.5.
Embodiment 116. The collection of abrasive particles of any one of embodiments 90 and 114, wherein the Non-Convexity Factor Standard Deviation is not greater than 30 or not greater than 25 or not greater than 20 or not greater than 15 or not greater than 10 or not greater than 8 or not greater than 6 or not greater than 4.
Embodiment 117. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, and 91, further comprising a standard deviation of height of not greater than 100 microns and a Mean Non-Convexity Factor of at least 3.5.
Embodiment 118. The collection of abrasive particles of any one of embodiments 91 and 117, wherein the standard deviation of height is not greater than 90 microns or not greater than 85 microns or not greater than 80 microns or not greater than 75 microns or not greater than 70 microns or not greater than 65 microns or not greater than 60 microns or not greater than 55 microns or not greater than 50 microns or not greater than 45 microns or not greater than 40 microns or not greater than 35 microns.
Embodiment 119. The collection of abrasive particles of any one of embodiments 91 and 117, wherein the standard deviation of height is at least 1 micron or at least 5 microns or at least 10 microns or at least 15 microns or at least 20 microns or at least 25 microns or at least 30 microns or at least 35 microns.
Embodiment 120. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, further comprising at least one feature of the group consisting of:
a Mean Non-Convexity Factor of at least 3.5;
a Non-Convexity Factor Standard Deviation of at least 2.4;
a Mean Anisotropy Factor of at least 1.25;
a standard deviation of height of not greater than 100 microns;
or any combination thereof.
Embodiment 121. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, wherein the first major surface and second major surface are substantially parallel to each other.
Embodiment 122. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, further comprising a fixed abrasive including the collection of abrasive particles.
Embodiment 123. The collection of abrasive particles of embodiment 122, the fixed abrasive is a coated abrasive.
Embodiment 124. The collection of abrasive particles of embodiment 122, wherein the fixed abrasive is a bonded abrasive.
Embodiment 125. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, further comprising a first group of abrasive particles, each of the abrasive particles in the first group being a first abrasive particle.
Embodiment 126. The collection of abrasive particles of embodiment 125, further comprising a second group of abrasive particles, each of the abrasive particles in the second group being a second abrasive particle.
Embodiment 127. The collection of abrasive particles of embodiment 126, wherein the two-dimensional shape of the body of the first abrasive particle, as viewed in a plane defined by a length and a width of the body, is selected from the first group consisting of regular polygons, irregular polygons, numerals, Greek alphabet characters, Latin alphabet characters, Russian alphabet characters, complex shapes having a combination of polygonal shapes, a shape with linear and curved portions, and a combination thereof.
Embodiment 128. The collection of abrasive particles of embodiment 126, wherein the body of the first abrasive particle comprises a two-dimensional shape as viewed in a plane defined by a length and a width of the body that is an irregular polygonal shape.
Embodiment 129. The collection of abrasive particles of embodiment 126, wherein the two-dimensional shape of the body of the second abrasive particle, as viewed in a plane defined by a length and a width of the body, is selected from the first group consisting of regular polygons, irregular polygons, numerals, Greek alphabet characters, Latin alphabet characters, Russian alphabet characters, complex shapes having a combination of polygonal shapes, a shape with linear and curved portions, and a combination thereof.
Embodiment 130. The collection of abrasive particles of embodiment 126, wherein the body of the first abrasive particle comprises a two-dimensional shape as viewed in a plane defined by a length and a width of the body that is an irregular polygonal shape, and wherein the body of the second abrasive particle comprises a two-dimensional shape as viewed in a plane defined by a length and a width of the body that is an irregular polygonal shape different than the irregular polygonal shape of the body of the first abrasive particle.
Embodiment 131. The collection of abrasive particles of embodiment 126, wherein the body of the first abrasive particle includes a plurality of side surface portions and a majority of the side surface portions are substantially planar.
Embodiment 132. The collection of abrasive particles of embodiment 131, wherein all of the side surface portions of the body of the first abrasive particle are substantially planar.
Embodiment 133. The collection of abrasive particles of embodiment 131, wherein the first side surface portion has a curved contour.
Embodiment 134. The collection of abrasive particles of embodiment 131, wherein the first side surface portion has an irregular contour.
Embodiment 135. The collection of abrasive particles of embodiment 131, wherein the body of the first abrasive particle includes a plurality of side surface portions, and each of the side surface portions extend for a length of at least 5% of a length of the body or at least 10% or at least 15% or at least 20% or at least 25%.
Embodiment 136. The collection of abrasive particles of embodiment 131, wherein each of the side surface portions of the body of the first abrasive particle extend for a length of not greater than 50% of a length of the body or not greater than 40% or not greater than 30%.
Embodiment 137. The collection of abrasive particles of embodiment 126, wherein further comprising a third abrasive particle comprising a body including a first major surface, a second major surface opposite the first major surface, and a side surface extending between the first major surface and the second major surface, wherein the body of the second abrasive particle comprises a two-dimensional shape that is different compared to the two-dimensional shape of the body of the first abrasive particle and the two-dimensional shape of the body of the second abrasive particle.
Embodiment 138. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, wherein the body comprises a first side surface portion extending for at least a portion of a distance between two external corners of the body and further comprising a first protrusion extending for at least 30% of a total length of the first side surface portion of the side surface or at least 40% of the total length of the first side surface portion or at least 50% of the total length of the first side surface portion or at least 60% of the total length of the first side surface portion or at least 70% of the total length of the first side surface portion or at least 80% of the total length of the first side surface portion or at least 90% of the total length of the first side surface portion.
Embodiment 139. The collection of abrasive particles of embodiment 138, wherein the first side surface portion is defined as a portion of the side surface extending between two external corners of the body.
Embodiment 140. The collection of abrasive particles of embodiment 138, wherein the first side surface portion is a fraction of the total length of the side surface defining the perimeter of the body.
Embodiment 141. The collection of abrasive particles of embodiment 138, wherein the first protrusion extends for a fraction of the total length of the side surface defining the perimeter of the body.
Embodiment 142. The collection of abrasive particles of embodiment 138, wherein the first side surface portion and first protrusion have substantially the same contour as viewed in the plane of the first major surface.
Embodiment 143. The collection of abrasive particles of embodiment 138, wherein the first protrusion intersects a second side surface portion that is distinct from the first side surface portion.
Embodiment 144. The collection of abrasive particles of embodiment 138, further comprising a first depression extending in a direction parallel to the first side surface portion of the side surface.
Embodiment 145. The collection of abrasive particles of embodiment 144, further comprising a second depression extending in a direction parallel to a second side surface portion, and further comprising a second protrusion disposed between the second side surface and the second depression, the second protrusion abutting the second side surface portion and extending along the second side surface portion.
Embodiment 146. The collection of abrasive particles of embodiment 138, wherein further comprising an unfeatured edge extending between the first major surface and a third side surface portion, wherein the third side surface portion is distinct from the first side surface portion.
Embodiment 147. The collection of abrasive particles of embodiment 146, wherein the third side surface portion and first side surface portion are separated from each other by at least one external corner on the side surface.
Embodiment 148. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, wherein the body includes a bottom edge joining the second major surface and the side surface, wherein at least a portion of the bottom edge has an irregular contour.
Embodiment 149. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, wherein the body comprises at least one material from the group of oxides, carbides, nitrides, borides, oxycarbides, oxynitrides, oxyborides, natural minerals, synthetic materials, carbon-based materials, and a combination thereof.
Embodiment 150. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, wherein further comprising:
a first group of abrasive particles, each of the abrasive particles in the first group being a first abrasive particle; and
a second group of abrasive particles, each of the abrasive particles in the second group being a second abrasive particle; and
wherein the body of the first abrasive particle includes at least one material from the group of oxides, carbides, nitrides, borides, oxycarbides, oxynitrides, oxyborides, natural minerals, synthetic materials, carbon-based materials, and a combination thereof.
Embodiment 151. The collection of abrasive particles of any one of embodiments 149 and 150, wherein the body comprises alumina.
Embodiment 152. The collection of abrasive particles of embodiment 151, wherein the body consists essentially of alumina.
Embodiment 153. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, wherein the body includes at least one oxide from the group of aluminum oxide, zirconium oxide, titanium oxide, yttrium oxide, chromium oxide, strontium oxide, silicon oxide, magnesium oxide, rare-earth oxides, or any combination thereof.
Embodiment 154. The collection of abrasive particles of embodiment 150, wherein the body of the second abrasive particle comprises a side surface portion that is substantially planar.
Embodiment 155. The collection of abrasive particles of embodiment 150, wherein the body of the second abrasive particle comprises a plurality of side surface portions, and wherein a majority of the side surface portions are substantially planar.
Embodiment 156. The collection of abrasive particles of embodiment 155, wherein all of the side surface portions of the body of the second abrasive particle are substantially planar.
Embodiment 157. The collection of abrasive particles of embodiment 155, wherein the body of the second abrasive particle comprises a side surface portion that has a curved contour.
Embodiment 158. The collection of abrasive particles of embodiment 155, wherein the body of the second abrasive particle comprises a side surface portion that has an irregular contour.
Embodiment 159. The collection of abrasive particles of embodiment 150, wherein the body of the first abrasive particle includes a plurality of side surface portions, and each of the side surface portions extend for a length of at least 5% of a length of the body or at least 10% or at least 15% or at least 20% or at least 25%.
Embodiment 160. The collection of abrasive particles of embodiment 159, wherein each of the side surface portions of the body of the first abrasive particle extend for a length of not greater than 80% of a length of the body or not greater than 70% or not greater than 60% or not greater than 50% or not greater than 40% or not greater than 30%.
Embodiment 161. The collection of abrasive particles of embodiment 150, wherein the first major surface of the body of the second abrasive particle comprises a first protrusion abutting the first side surface portion and extending along the first side surface portion.
Embodiment 162. The collection of abrasive particles of embodiment 161, wherein the first major surface of the body of the second abrasive particle comprises a first depression extending in a direction parallel to a first side surface portion.
Embodiment 163. The collection of abrasive particles of embodiment 161, wherein the first protrusion extends for at least 30% of a total length of the first side surface portion or at least 40% of the total length of the first side surface portion or at least 50% of the total length of the first side surface portion or at least 60% of the total length of the first side surface portion or at least 70% of the total length of the first side surface portion or at least 80% of the total length of the first side surface portion or at least 90% of the total length of the first side surface portion.
Embodiment 164. The collection of abrasive particles of embodiment 161, wherein the first side surface portion is defined as a portion of the side surface extending between two external corners of the body.
Embodiment 165. The collection of abrasive particles of embodiment 161, wherein the first side surface portion is a fraction of the total length of the side surface defining the perimeter of the body.
Embodiment 166. The collection of abrasive particles of embodiment 161, wherein the first protrusion extends for a fraction of the total length of the side surface defining the perimeter of the body.
Embodiment 167. The collection of abrasive particles of embodiment 161, the first side surface portion and the first protrusion have substantially the same contour as viewed in the plane of the first major surface.
Embodiment 168. The collection of abrasive particles of embodiment 161, wherein the first protrusion intersects a second side surface portion that is distinct from the first side surface portion.
Embodiment 169. The collection of abrasive particles of any one of embodiments 87, 89, 90, 91, and 92, wherein a majority of the abrasive particles of the collection of abrasive particles comprise a plurality of microridges along at least a portion of the side surface of the body.
Embodiment 170. The collection of abrasive particles of any one of embodiments 88 and 169, wherein at least 51% of the abrasive particles of the collection of abrasive particles include the plurality of microridges or at least 52% or at least 54% or at least 56% or at least 58% or at least 60% or at least 62% or at least 64% or at least 66% or at least 68% or at least 70% or at least 72% or at least 74% or at least 76% or at least 78% or at least 80% or at least 82% or at least 84% or at least 86% or at least 88% or at least 90% or at least 92% or at least 94% or at least 96% or at least 98% or at least 99% of the abrasive particles of the collection of abrasive particles.
Embodiment 171. The collection of abrasive particles of any one of embodiments 88 and 169, wherein not greater than 99% of the abrasive particles of the collection of abrasive particles include the plurality of microridges or not greater than 98% or not greater than 96% or not greater than 94% or not greater than 92% or not greater than 90% or not greater than 88% or not greater than 86% or not greater than 84% or not greater than 82% or not greater than 80% or not greater than 78% or not greater than 76% or not greater than 74% or not greater than 72% or not greater than 70% or not greater than 68% or not greater than 66% or not greater than 64% or not greater than 62% or not greater than 60% or not greater than 58% or not greater than 56% or not greater than 54% or not greater than 52% of the abrasive particles of the collection of abrasive particles.
Embodiment 172. The collection of abrasive particles of any one of embodiments 88 and 169, wherein a majority of the total surface area of the side surfaces of the abrasive particles in the collection of abrasive particles comprise a plurality of microridges.
Embodiment 173. The collection of abrasive particles of embodiment 172, wherein at least 51% of the total surface area of the side surfaces of the abrasive particles of the collection includes the plurality of microridges or at least 52% or at least 54% or at least 56% or at least 58% or at least 60% or at least 62% or at least 64% or at least 66% or at least 68% or at least 70% or at least 72% or at least 74% or at least 76% or at least 78% or at least 80% or at least 82% or at least 84% or at least 86% or at least 88% or at least 90% or at least 92% or at least 94% or at least 96% or at least 98% or at least 99%.
Embodiment 174. The collection of abrasive particles of embodiment 172, wherein not greater than 99% of the total surface area of the sides surfaces of the abrasive particles of the collection includes the plurality of microridges or not greater than 98% or not greater than 96% or not greater than 94% or not greater than 92% or not greater than 90% or not greater than 88% or not greater than 86% or not greater than 84% or not greater than 82% or not greater than 80% or not greater than 78% or not greater than 76% or not greater than 74% or not greater than 72% or not greater than 70% or not greater than 68% or not greater than 66% or not greater than 64% or not greater than 62% or not greater than 60% or not greater than 58% or not greater than 56% or not greater than 54% or not greater than 52%.
Embodiment 175. The collection of abrasive particles of any one of embodiments 88 and 169, wherein at least a portion of the plurality of microridges comprises a plurality of isolated microridges defined by microridges extending from the side surface and separated by generally smooth planar regions.
Embodiment 176. The collection of abrasive particles of embodiment 175, wherein the plurality of isolated microridges extend along the side surface in an irregular path.
Embodiment 177. The collection of abrasive particles of embodiment 175, wherein at least one of the isolated microridges of the plurality of isolated microridges comprises a head region and a tail region connected to and extending from the head region, wherein the head region has a rounded shape and the tail region has an elongated shape.
Embodiment 178. The collection of abrasive particles of any one of embodiments 88 and 169, wherein at least a portion of the plurality of microridges comprises a plurality of scaled microridges.
Embodiment 179. The collection of abrasive particles of embodiment 178, wherein at least a portion of the scaled microridges of the plurality of scaled microridges comprise a primary ridge and a plurality of wrinkles extending from the primary ridge.
Embodiment 180. The collection of abrasive particles of embodiment 179, wherein the primary ridge extends along the side surface in an irregular path.
Embodiment 181. The collection of abrasive particles of embodiment 179, wherein at least a portion of the plurality of wrinkles extend along the side surface in an irregular path away from the primary ridge.
Embodiment 182. The collection of abrasive particles of embodiment 179, wherein the wrinkles define grooves extending along the side surface along an irregular path.
Embodiment 183. The collection of abrasive particles of embodiment 179, wherein the wrinkles extend along a curved path.
Embodiment 184. The collection of abrasive particles of embodiment 179, wherein the plurality of scaled microridges includes a greater number of wrinkles compared to the number of primary ridges.
Embodiment 185. The collection of abrasive particles of embodiment 179, wherein the wrinkles extend in a different direction compared to one or more primary ridges, and the wrinkles extend between two or more primary ridges.
Embodiment 186. The collection of abrasive particles of embodiment 179, wherein the primary ridge includes at least one gap between elongated portions.
Embodiment 187. The collection of abrasive particles of embodiment 178, wherein at least a portion of the scaled microridges have a scaled appearance.
Embodiment 188. The collection of abrasive particles of embodiment 178, wherein at least a portion of the scaled microridges have a layered appearance.
Embodiment 189. The collection of abrasive particles of embodiment 178, wherein at least a portion of the scaled microridges include a plurality of raised portions with irregular shapes and wrinkles extending between the plurality of raised portions.
Embodiment 190. The collection of abrasive particles of any one of embodiments 88 and 169, wherein the plurality of microridges is a conchoidal fracturing feature.
Embodiment 191. The collection of abrasive particles of any one of embodiments 88 and 169, wherein the plurality of microridges is formed during fracturing of the side surface.
Embodiment 192. The collection of abrasive particles of any one of embodiments 88 and 169, wherein the plurality of microridges includes a precipice region.
Embodiment 193. The collection of abrasive particles of any one of embodiments 87, 88, 89, 90, 91, and 92, wherein the side surface of the body includes side surface portions, and wherein each side surface portion extends between external corners of the body, and wherein at least 45% of the side surface portions include the plurality of microridges.
Embodiment 194. The collection of abrasive particles of embodiment 193, wherein the body includes at least three side surface portions including the plurality of microridges.
Embodiment 195. The collection of abrasive particles of embodiment 193, wherein all of the side surface portions include the plurality of microridges.
Embodiment 196. The collection of abrasive particles of embodiment 193, wherein, wherein at least 52% of the side surface portions of the body include the plurality of microridges, or at least 54% or at least 56% or at least 58% or at least 60% or at least 62% or at least 64% or at least 66% or at least 68% or at least 70% or at least 72% or at least 74% or at least 76% or at least 78% or at least 80% or at least 82% or at least 84% or at least 86% or at least 88% or at least 90% or at least 92% or at least 94% or at least 96% or at least 98% or at least 99%.
Embodiment 197. The collection of abrasive particles of embodiment 193, wherein the body includes at least one side surface portion that does not include the plurality of microridges.
Embodiment 198. The collection of abrasive particles of embodiment 193, wherein at least 10% of the abrasive particles of the collection have at least 45% of the side surface portions including the plurality of microridges.
Embodiment 199. The collection of abrasive particles of embodiment 193, wherein each of the abrasive particles of the collection has at least 45% of the side surface portions including the plurality of microridges.
A variety of abrasive particles were made according to the following conditions.
A first sample, Sample S1, was initially formed from a mixture including approximately 37-43 wt % boehmite, water and nitric acid. One may use a commercially available boehmite, such as Disperal from Sasol Corp. The nitric acid-to-boehmite ratio was approximately 0.035. The boehmite was mixed and seeded with 1% alpha alumina seeds relative to the total alumina content of the mixture. The alpha alumina seeds were made by milling of corundum using conventional techniques, described for example in U.S. Pat. No. 4,623,364. The ingredients were mixed in a planetary mixer of conventional design and mixed under reduced pressure to remove gaseous elements from the mixture (e.g., bubbles).
The mixture was then cast onto a belt using an extruder. The mixture formed a layer having a width of approximately 8 cm and a height of approximately 0.4 mm. The surface of the belt in contact with the mixture was Invar 36. The extrusion and formation of the mixture into a layer was conducted under standard ambient conditions of temperature, pressure, and atmosphere.
After forming the mixture, various modifications were conducted to create different samples of abrasive particles. In particular, the layer was shaped with various different forms having different features.
The mixture was formed into a layer as described above and the upper surface of the layer was modified using a form having square-shaped openings, such as the form illustrated in
The modified body was conveyed to a drying zone including two 4000W IR lamps mounted in parallel, side-by-side over the upper surface of the modified body. Each lamp was 40 inches long, 2.5 inch wide, and was used at 35% of the maximum power (i.e., 1400W). The drying temperature within the drying zone was set for 70° C., which was controlled by a thermocouple placed approximately 1 cm above the upper surface of the modified body. Air having a relative humidity of approximately 50% (+15%) was flowed into the drying zone at a flow rate of approximately 1.5 m/s. The drying zone was partially enclosed, having openings at opposite ends to allow air to flow through the enclosure. The enclosure was 2 meters in length, 0.5 meters in height, and 0.5 meters wide.
Drying was conducted under the conditions noted above to achieve controlled cracking of the body and formation of precursor abrasive particles. That is, after modifying the body with the form, the drying conditions were sufficient to crack the modified body in a manner to create a plurality of precursor abrasive particles from the body. The nature of the pattern in the body that was created by the form influenced the cracking behavior during the drying process to facilitate the formation of the precursor abrasive particles.
The dried abrasive particles were then sintered at a sintering temperature of approximately 1400° C. for 10 minutes in a rotary tube furnace of standard atmospheric pressure and an atmosphere of air.
Abrasive particles were formed using the process of creating the mixture as noted above and using the conditions provided in Example 1, except that the body was modified using a form as depicted in
Abrasive particles were formed using the process of creating the mixture as noted above and using the conditions outlined in Example 1, except that the body was modified using a form as depicted in
Abrasive particles were formed using the process of Example 1, with the exception that the mixture was patterned from a form made of PEEK and the form was pressed against the surface of the mixture via a motor-driven roller. These abrasive particles of this sample formed a collection and are referred to herein as Sample S4. A representative image of an abrasive particle from the collection is provided in
An analysis was completed on other types of conventional abrasive particles to evaluate the differences between such particles and the representative particles of Sample S4. A first conventional collection of particles, Sample CS1, was obtained and is representative of a triangular shaped abrasive particle available from 3M as Cubitron II.
A second collection of conventional particles, Sample CS2, was obtained and is representative of conventional crushed abrasive particles.
Finally, a third collection of conventional abrasive particles, Sample CS3, was obtained and is representative of particles that were casted into a layer of material that was later cut by blades.
The abrasive particles of Sample CS1 had a MAF of approximately 0.64, an Anisotropy Factor Standard Deviation of approximately 0.49, a Mean Non-Convexity Factor of 3.32, a Non-Convexity Factor Standard Deviation of 0.73, and an average height of the body of 290 microns.
As the abrasive particles of Sample CS1 are shaped abrasive particles presumably made through a molding process, the sidewalls of the particles did not exhibit noticeably different regions, such as a first region and second region as was demonstrated by the representative abrasive particles of Sample S4.
The collection of abrasive particles of Sample CS2 had a MAF of approximately 1.21, an Anisotropy Factor Standard Deviation of approximately 0.72, a Mean Non-Convexity Factor of 12.9, a Non-Convexity Factor Standard Deviation of 3.65, an average height of the body of 514 microns, a standard deviation of height of approximately 106 microns. As the abrasive particles of Sample CS2 are crushed abrasive particles, the sidewalls of the particles did not exhibit noticeably different regions, such as a first region and second region as was demonstrated by the representative abrasive particles of Sample S4.
The collection of abrasive particles of Sample CS3 had a Mean Non-Convexity Factor of 9.40, a Non-Convexity Factor Standard Deviation of 2.33. The MAF was not measured, but given what is provided in the images, the majority of the sidewall regions would likely have a MAF less than the representative abrasive particles of Sample S4. The same is expected of the Anisotropy Factor Standard Deviation. As illustrated in
The present application represents a departure from the state of the art. While the industry has recognized that abrasive particles may be formed through processes such as molding and screen printing, the processes of the embodiments herein are distinct from such processes. Notably, the embodiments herein utilize a combination of process features that facilitate the formation of abrasive particles having one or a combination of unique features. Such features can include, but are not limited to, shape, size, features in one or more major surfaces, composition, and others as described in the embodiments herein. Moreover, the processes of the embodiments herein facilitate the formation of a shaped abrasive particle or a batch of abrasive particles, having one or more characteristics, including one or more combination of the features of the abrasive particles. Certain abrasive particles and batches containing abrasive particles of the embodiments herein may have features that enable enhanced performance in the context of fixed abrasive articles.
The above-disclosed subject matter is to be considered illustrative, and not restrictive, and the appended claims are intended to cover all such modifications, enhancements, and other embodiments, which fall within the true scope of the present invention. Thus, to the maximum extent allowed by law, the scope of the present invention is to be determined by the broadest permissible interpretation of the following claims and their equivalents, and shall not be restricted or limited by the foregoing detailed description.
The Abstract of the Disclosure is provided to comply with Patent Law and is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims. In addition, in the foregoing Detailed Description, various features may be grouped together or described in a single embodiment for the purpose of streamlining the disclosure. This disclosure is not to be interpreted as reflecting an intention that the claimed embodiments require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive subject matter may be directed to less than all features of any of the disclosed embodiments. Thus, the following claims are incorporated into the Detailed Description, with each claim standing on its own as defining separately claimed subject matter.
This application is a continuation of and claims priority to U.S. Non-Provisional patent application Ser. No. 15/591,929, entitled “ABRASIVE PARTICLES AND METHODS OF FORMING SAME,” by Jennifer H. CZEREPINSKI et al., filed on May 10, 2017, which claims priority under 35 U.S.C. § 119(e) to U.S. Provisional Patent Application No. 62/334,298, entitled “ABRASIVE PARTICLES AND METHOD OF FORMING SAME,” by Jennifer H. CZEREPINSKI et al., filed May 10, 2016, which are assigned to the current assignee hereof and incorporated herein by reference in their entireties.
| Number | Date | Country | |
|---|---|---|---|
| 62334298 | May 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15591929 | May 2017 | US |
| Child | 16987900 | US |