Patent Application
20180237675
This disclosure, in general, relates to methods and systems for forming structured abrasive articles. More particularly, this disclosure relates to shaped abrasive grains.
Abrasive articles, such as coated abrasives and bonded abrasives, are used in various industries to machine workpieces, such as by lapping, grinding, or polishing. Machining utilizing abrasive articles spans a wide industrial scope from optics industries, automotive paint repair industries, to metal fabrication industries. In each of these examples, manufacturing facilities use abrasives to remove bulk material or affect surface characteristics of products.
Surface characteristics include shine, texture, and uniformity. For example, manufacturers of metal components use abrasive articles to fine and polish surfaces, and oftentimes desire a uniformly smooth surface. Similarly, optics manufacturers desire abrasive articles that produce defect free surfaces to prevent light diffraction and scattering.
Manufactures also desire abrasive articles that have a high stock removal rate for certain applications. However, there is often a trade-off between removal rate and surface quality. Finer grain abrasive articles typically produce smoother surfaces, yet have lower stock removal rates. Lower stock removal rates lead to slower production and increased cost.
Particularly in the context of coated abrasive articles, manufactures of abrasive articles have introduced surface structures to improve stock removal rate, while maintaining surface quality. Coated abrasive articles having surface structures or patterns of raised abrasive layers, often called engineered or structured abrasives, typically exhibit improved useful life.
However, typical techniques for forming structured abrasive articles are unreliable and suffer from performance limitations. A typical process for forming a structured abrasive article includes coating a backing with a viscous binder, coating the viscous binder with a functional powder, and stamping or rolling structure patterns into the viscous binder. The functional powder prevents the binder from sticking to patterning tools. The binder is subsequently cured.
Imperfect coating of the viscous binder with functional powder leads to binder sticking on patterning tools. Binder sticking produces poor structures, leading to poor product performance and wasted product.
Selection of binders appropriate for typical structured abrasive formation techniques is limited by the process. Typical binders include high loading of traditional fillers that increase the viscosity of the binder. Such traditional fillers affect the mechanical characteristics of the binder. For example, high loading of traditional fillers may adversely affect tensile strength, tensile modulus, and elongation at break characteristics of the binder. Poor mechanical characteristics of the binder allow for loss of abrasive grains, leading to scratching and haze on surfaces and reducing abrasive article life.
Loss of grains also degrades the performance of abrasive articles, leading to frequent replacement. Frequent abrasive article replacement is costly to manufacturers. As such, improved abrasive articles and methods for manufacturing abrasive articles would be desirable.
An abrasive grain is disclosed and may include a body. The body may define a length (l), a height (h), and a width (w). In a particular aspect, the length is greater than or equal to the height and the height is greater than or equal to the width. Further, in a particular aspect, the body may include a primary aspect ratio defined by the ratio of length:height of at least about 1:1. The body may also include an upright orientation probability of at least about 50%.
In another aspect, an abrasive grain is disclosed and may include a body that has a length (l), a width (w), and a height (h). The length, width, and height may correspond to a longitudinal axis, a lateral axis, and a vertical axis, respectively, and the longitudinal axis, lateral axis, and vertical axis may define three perpendicular planes. In this aspect, the body may include an asymmetric geometry with respect to any of the three perpendicular planes.
In yet another aspect, an abrasive grain is disclosed and may include a body having a complex three-dimensional geometry including 3-fold symmetry in three perpendicular planes defined by a longitudinal axis, a lateral axis, and a vertical axis. Further, the body may include an opening that extends through the entire interior of the body along one of the longitudinal axis, lateral axis, or vertical axis.
In still another aspect, an abrasive grain is disclosed and may include a body having a complex three-dimensional geometry defined by a length (l), a width (w), and a height (h). The body may also include a center of mass and a geometric midpoint. The center of mass may be displaced from the geometric midpoint by a distance (Dh) of at least about 0.05(h) along a vertical axis of the body defining the height.
In another aspect, an abrasive grain is disclosed and may include a body that defines a length (l), a width (w), and a height (h). The body may include a base surface and an upper surface. Further, the base surface comprises a different cross-sectional shape than a cross-sectional shape of the upper surface.
In still another aspect, an abrasive grain is disclosed and may include a body that has a generally flat bottom and a dome shaped top extending from the generally flat bottom.
In another aspect, an abrasive grain is disclosed and may include a body comprising a length (l), a width (w), and a height (h). The length, width, and height may correspond to a longitudinal axis, a lateral axis, and a vertical axis, respectively. Further, the body may include a twist along a longitudinal axis defining the length of the body such that a base surface is rotated with respect to an upper surface to establish a twist angle.
In yet another aspect, an abrasive grain is disclosed and may include a body having a first end face and a second end face a, at least three adjacent side faces extending between the first end face and the second end face, and an edge structure established between each pair of adjacent side faces.
In another aspect, an abrasive grain is disclosed and may include a body having a central portion and at least three radial arms extending outwardly from the central portion along the entire length of the central portion.
In yet another aspect, an abrasive grain includes a body having a length (l), a width (w), and a height (h), wherein the body has a base surface end and an upper surface, and wherein the base surface includes a different cross-sectional shape than a cross-sectional shape of the upper surface.
For another aspect, an abrasive grain includes a body having a central portion and at least three radial arms extending outwardly from the central portion along the entire length of the central portion, wherein each radial arm includes an arrow shaped distal end.
According to another aspect, a shaped abrasive particle includes a body having a length (l), a width (w), and a height (h), wherein the body comprises a base surface end, an upper surface, and a side surface extending between the base surface and the upper surface, and wherein the base surface has a different cross-sectional shape than a cross-sectional shape of the upper surface.
In one aspect, a shaped abrasive particle includes a body having a length (l), a width (w), and a height (h), wherein the body has a three-pointed star including a first arm defining a first arm, a second arm defining a second arm, and a third arm defining a second arm, and wherein the first arm, second arm and third arm define a total angle of less than about 180 degrees, and wherein the body has a curling factor of not greater than about 10.
For another aspect, a shaped abrasive particle includes a body having a length (l), a width (w), and a height (h), wherein the body defines a four-pointed star having a first arm, second arm, third arm, and fourth arm extending from a central portion, and wherein the body has a curling factor of not greater than about 10.
According to yet another aspect, a shaped abrasive particle includes a body having a length (l), a width (w), and a height (h), wherein the body is defined by a base surface, an upper surface, and a side surface extending between the base surface and the upper surface, wherein the base surface comprises a cross shaped two-dimensional shape and the upper surface comprises a rounded quadrilateral two-dimensional shape.
For still another aspect, a shaped abrasive particle includes a body having a first layer having a first length and a second layer overlying the first layer, wherein the second layer has a length that is within a range between about 50% and about 90% of the length of the first layer.
The present disclosure may be better understood, and its numerous features and advantages made apparent to those skilled in the art by referencing the accompanying drawings.
The use of the same reference symbols in different drawings indicates similar or identical items.
The following is also directed to methods of forming shaped abrasive particles and features of such shaped abrasive particles. The shaped abrasive particles may be used in various abrasive articles, including for example bonded abrasive articles, coated abrasive articles, and the like. Alternatively, the shaped abrasive particles of the embodiments herein may be utilized in free abrasive technologies, including for example grinding and/or polishing slurries.
Referring initially to
In a particular embodiment, the binder formulation 106 may be provided in a slurry that includes the binder formulation and abrasive grains. In an alternative embodiment, the binder formulation 106 may be dispensed separate from the abrasive grains. Then, the abrasive grains may be provided following the coating of the backing 102 with the binder formulation 106, after partial curing of the binder formulation 106, after patterning of the binder formulation 106, or after fully curing the binder formulation 108. The abrasive grains may, for example, be applied by a technique, such as electrostatic coating, drop coating or mechanical projection. In a particular aspect, the abrasive grains may be any combination of one or more of the shaped abrasive grains described herein.
The binder formulation 106 may be cured after passing under an energy source 110. The selection of the energy source 110 may depend in part upon the chemistry of the binder formulation 106. For example, the energy source 110 may be a source of thermal energy or actinic radiation energy, such as electron beam, ultraviolet light, or visible light. The amount of energy used may depend on the chemical nature of the reactive groups in the precursor polymer constituents, as well as upon the thickness and density of the binder formulation 106. For thermal energy, an oven temperature of about 75.degree. C. to about 150.degree. C. and duration of about 5 minutes to about 60 minutes may be generally sufficient. Electron beam radiation or ionizing radiation may be used at an energy level of about 0.1 MRad to about 100 MRad, particularly at an energy level of about 1 MRad to about 10 MRad. Ultraviolet radiation includes radiation having a wavelength within a range of about 200 nanometers to about 400 nanometers, particularly within a range of about 250 nanometers to 400 nanometers. Visible radiation includes radiation having a wavelength within a range of about 400 nanometers to about 800 nanometers, particularly in a range of about 400 nanometers to about 550 nanometers. Curing parameters, such as exposure, are generally formulation dependent and can be adjusted via lamp power and belt speed.
In an exemplary embodiment, the energy source 110 may provide actinic radiation to the coated backing, partially curing the binder formulation 106. In another embodiment, the binder formulation 106 is thermally curable and the energy source 110 may provide heat for thermal treatment. In a further embodiment, the binder formulation 106 may include actinic radiation curable and thermally curable components. As such, the binder formulation may be partially cured through one of thermal and actinic radiation curing and cured to complete curing through a second of thermal and actinic radiation curing. For example, an epoxy constituent of the binder formulation may be partially cured using ultraviolet electromagnetic radiation and an acrylic constituent of the binder formulation may be further cured through thermal curing.
Once the binder formulation 106 is cured a structured abrasive article 112 is formed. Alternatively, a size coat may be applied over the patterned abrasive structures. In a particular embodiment, the structured abrasive article 112 may be rolled into a roll 114. In other embodiments, fully curing may be performed after rolling a partially cured abrasive article 112.
In one or more alternative embodiments, a size coat may be applied over the binder formulation 106 and abrasive grains. For example, the size coat may be applied before partially curing the binder formulation 106, after partially curing the binder formulation 106 or after further curing the binder formulation 106. The size coat may be applied, for example, by roll coating or spray coating. Depending on the composition of the size coat and when it is applied, the size coat may be cured in conjunction with the binder formulation 106 or cured separately. A supersize coat including grinding aids may be applied over the size coat and cured with the binder formulation 106, cured with the size coat or cured separately.
Referring to
In a particular aspect, the shaped abrasive grains 204 may be one or more of the shaped abrasive grains described herein. Further, the shaped abrasive grains may include one or more, or any combination, of the shaped abrasive grains described herein. Further, one or more of the shaped abrasive grains described herein may include an upright orientation probability. The upright orientation may be considered an orientation that corresponds to a favorable abrasive/cutting position for each shaped abrasive grain and the probability is a simple mathematical probability that the grain lands in the upright orientation.
In a particular aspect, the upright orientation is at least fifty percent (50%). In another aspect, the upright orientation is at least fifty-five percent (55%). In another aspect, the upright orientation is at least sixty percent (60%). In another aspect, the upright orientation is at least sixty-five percent (65%). In another aspect, the upright orientation is at least seventy percent (70%). In another aspect, the upright orientation is at least seventy-five percent (75%). In another aspect, the upright orientation is at least eighty percent (80%). In another aspect, the upright orientation is at least eighty-five percent (85%). In another aspect, the upright orientation is at least ninety percent (90%). In another aspect, the upright orientation is at least ninety-five percent (95%). In another aspect, the upright orientation is one hundred percent (100%).
The body of each of the shaped abrasive grains described herein may include a polycrystalline material. The polycrystalline material may include abrasive grains. The abrasive grains may include nitrides, oxides, carbides, borides, oxynitrides, diamond, or a combination thereof. Further, the abrasive grains may include an oxide selected from the group of oxides consisting of aluminum oxide, zirconium oxide, titanium oxide, yttrium oxide, chromium oxide, strontium oxide, silicon oxide, and a combination thereof.
In another aspect, the abrasive grains may include alumina. In yet another aspect, the abrasive grains consist essentially of alumina. Further, the abrasive grains may have an average grain size of not greater than about 500 microns. Alternatively, the average grain size is not greater than about 250 microns. In another aspect, the average grain size is not greater than about 100 microns. In another aspect, the average grain size is not greater than about 50 microns. In another aspect, the average grain size is not greater than about 30 microns. In another aspect, the average grain size is not greater than about 20 microns. In another aspect, the average grain size is not greater than about 10 microns. In another aspect, the average grain size is not greater than about 1 micron.
In another aspect, the average grain size is at least about 0.01 microns. In another aspect, the average grain size is at least about 0.05 microns. In another aspect, the average grain size is at least about 0.08 microns. In another aspect, the average grain size is at least about 0.1 microns.
In another aspect, the body of each of the shaped abrasive grains described herein may be a composite that includes at least about 2 different types of abrasive grains.
As depicted in
As shown, each end face 302, 304 the shaped abrasive grain 300 may be generally triangular in shape. Each side face 310, 312, 314 may be generally rectangular in shape. Further, the cross section of the shaped abrasive grain 300 in a plane parallel to the end faces 302, 304 is generally triangular. It can be appreciated that the shaped abrasive grain 300 may include more than the three side faces 310, 312, 314 and three edges 320, 322, 324. It may be further appreciated that depending on the number of side faces 310, 312, 314, the end faces 302, 304 and cross section of the shaped abrasive grain 300 through a plane parallel to the end faces 302, 304 may have that shape of any polygon, e.g., a quadrilateral, a pentagon, a hexagon, a heptagon, an octagon, a nonagon, a decagon, etc. Further, the polygon may be convex, non-convex, concave, or non-concave.
As depicted in
As shown, each end face 502, 504 the shaped abrasive grain 500 may be generally triangular in shape. Each side face 510, 512, 514 may be generally rectangular in shape. Further, the cross-section of the shaped abrasive grain 500 in a plane parallel to the end faces 502, 504 is generally triangular.
As depicted in
As shown, each end face 702, 704 the shaped abrasive grain 700 may be generally triangular in shape. Each side face 710, 712, 714 may be generally rectangular in shape. Further, the cross-section of the shaped abrasive grain 700 in a plane parallel to the end faces 702, 704 is generally triangular.
As depicted in
As shown, each end face 902, 904 the shaped abrasive grain 900 may be generally triangular in shape. Each side face 910, 912, 914 may be generally rectangular in shape. Further, the cross-section of the shaped abrasive grain 900 in a plane parallel to the end faces 902, 904 is generally triangular.
In the exemplary embodiments shown in
Additionally, it may be appreciated that in each of the exemplary embodiments shown in
In particular, the base may comprise at least about thirty percent (30%) of the total surface area of the particle. In another aspect, the base may comprise at least about forty percent (40%) of the total surface area of the particle. In another aspect, the base may comprise at least about fifty percent (50%) of the total surface area of the particle. In another aspect, the base may comprise at least about sixty percent (60%) of the total surface area of the particle. In another aspect, the base may comprise no greater than ninety-nine percent (99%) of the total surface area of the particle. In another aspect, the base may comprise no greater than ninety-five percent (95%) of the total surface area of the particle. In another aspect, the base may comprise no greater than ninety percent (90%) of the total surface area of the particle. In another aspect, the base may comprise no greater than eighty percent (80%) of the total surface area of the particle. In another aspect, the base may comprise no greater than seventy-five percent (75%) of the total surface area of the particle.
Referring to
In a particular aspect, the hole 1104 may define a central axis 1106 that passes through a center of the hole 1104. Further, the shaped abrasive grain 1100 may also define a central axis 1108 that passes through a center of the shaped abrasive grain 1100. It may be appreciated that the hole 1104 may be formed in the shaped abrasive grain 1100 such that the central axis 1106 of the hole 1104 is spaced a distance 1110 above the central axis 1108 of the shaped abrasive grain 1100. As such, a center of mass of the shaped abrasive grain 1100 may be moved below the geometric midpoint of the shaped abrasive grain 1100. Moving the center of mass below the geometric midpoint of the shaped abrasive grain may ensure that the shaped abrasive grain 1100 lands on the same face, e.g., the bottom face 1102, when dropped, or otherwise deposited, onto a backing, such that the shaped abrasive grain has an upright orientation.
In a particular embodiment, the center of mass of is displaced from the geometric midpoint by a distance that is equal to 0.05 the height (h) along a vertical axis of the body 1102 defining a height. In another aspect, the center of mass may be displaced by a distance of at least about 0.1(h). In another aspect, the center of mass may be displaced by a distance of at least about 0.15(h). In another aspect, the center of mass may be displaced by a distance of at least about 0.18(h). In another aspect, the center of mass may be displaced by a distance of at least about 0.2(h). In another aspect, the center of mass may be displaced by a distance of at least about 0.22(h). In another aspect, the center of mass may be displaced by a distance of at least about 0.25(h). In another aspect, the center of mass may be displaced by a distance of at least about 0.27(h). In another aspect, the center of mass may be displaced by a distance of at least about 0.3(h). In another aspect, the center of mass may be displaced by a distance of at least about 0.32(h). In another aspect, the center of mass may be displaced by a distance of at least about 0.35(h). In another aspect, the center of mass may be displaced by a distance of at least about 0.38(h).
In another aspect, the center of mass is displaced a distance no greater than 0.5(h). In yet another aspect, the center of mass is displaced a distance no greater than 0.49 (h). In still another aspect, the center of mass is displaced a distance no greater than 0.48(h). In another aspect, the center of mass is displaced a distance no greater than 0.45(h). In still another aspect, the center of mass is displaced a distance no greater than 0.43(h). In yet still another aspect, the center of mass is displaced a distance no greater than 0.40(h). In another aspect, the center of mass is displaced a distance no greater than 0.39(h). In another aspect, the center of mass is displaced a distance no greater than 0.38(h).
Further, the center of mass may be displaced so that the center of mass is closer to a base, e.g., the bottom face 1102, of the body 1101, than a top of the body 1101 when the shaped abrasive grain 1100 is in an upright orientation as shown in
In another embodiment, the center of mass may be displaced from the geometric midpoint by a distance 1110 that is equal to 0.05 the width (w) along a horizontal axis of the of the body 1102 defining the width. In another aspect, the center of mass may be displaced by a distance of at least about 0.1(w). In another aspect, the center of mass may be displaced by a distance of at least about 0.15(w). In another aspect, the center of mass may be displaced by a distance of at least about 0.18(w). In another aspect, the center of mass may be displaced by a distance of at least about 0.2(w). In another aspect, the center of mass may be displaced by a distance of at least about 0.22(w). In another aspect, the center of mass may be displaced by a distance of at least about 0.25(w). In another aspect, the center of mass may be displaced by a distance of at least about 0.27(w). In another aspect, the center of mass may be displaced by a distance of at least about 0.3(w). In another aspect, the center of mass may be displaced by a distance of at least about 0.32(w). In another aspect, the center of mass may be displaced by a distance of at least about 0.35(w). In another aspect, the center of mass may be displaced by a distance of at least about 0.38(w).
In another aspect, the center of mass is displaced a distance no greater than 0.5(w). In yet another aspect, the center of mass is displaced a distance no greater than 0.49 (w). In still another aspect, the center of mass is displaced a distance no greater than 0.48(w). In another aspect, the center of mass is displaced a distance no greater than 0.45(w). In still another aspect, the center of mass is displaced a distance no greater than 0.43(w). In yet still another aspect, the center of mass is displaced a distance no greater than 0.40(w). In another aspect, the center of mass is displaced a distance no greater than 0.39(w). In another aspect, the center of mass is displaced a distance no greater than 0.38(w).
In another embodiment, the center of mass may be displaced from the geometric midpoint by a distance that is equal to 0.05 the length (l) along a longitudinal axis of the body 1102 defining a length. In another aspect, the center of mass may be displaced by a distance of at least about 0.1(l). In another aspect, the center of mass may be displaced by a distance of at least about 0.15(l). In another aspect, the center of mass may be displaced by a distance of at least about 0.18(l). In another aspect, the center of mass may be displaced by a distance of at least about 0.2(l). In another aspect, the center of mass may be displaced by a distance of at least about 0.22(l). In another aspect, the center of mass may be displaced by a distance of at least about 0.25(l). In another aspect, the center of mass may be displaced by a distance of at least about 0.27(l). In another aspect, the center of mass may be displaced by a distance of at least about 0.3(l). In another aspect, the center of mass may be displaced by a distance of at least about 0.32(l). In another aspect, the center of mass may be displaced by a distance of at least about 0.35(l). In another aspect, the center of mass may be displaced by a distance of at least about 0.38(l).
In another aspect, the center of mass is displaced a distance no greater than 0.5(l). In yet another aspect, the center of mass is displaced a distance no greater than 0.49 (l). In still another aspect, the center of mass is displaced a distance no greater than 0.48(l). In another aspect, the center of mass is displaced a distance no greater than 0.45(l). In still another aspect, the center of mass is displaced a distance no greater than 0.43(l). In yet still another aspect, the center of mass is displaced a distance no greater than 0.40(l). In another aspect, the center of mass is displaced a distance no greater than 0.39(l). In another aspect, the center of mass is displaced a distance no greater than 0.38(l).
As shown in
As shown in
In a particular aspect, the primary aspect ratio is at least 1:1. In another aspect, the primary aspect ratio is at least 2:1. In another aspect, the primary aspect ratio is at least 2.5:1. In another aspect, the primary aspect ratio is at least 3:1. In another aspect, the primary aspect ratio is at least 3.5:1. In another aspect, the primary aspect ratio is at least 4:1. In another aspect, the primary aspect ratio is at least 4.5:1. In another aspect, the primary aspect ratio is at least 5:1. In another aspect, the primary aspect ratio is at least 5.5:1. In another aspect, the primary aspect ratio is at least 6:1. In another aspect, the primary aspect ratio is at least 6.5:1. In another aspect, the primary aspect ratio is at least 7:1. In another aspect, the primary aspect ratio is at least 7.5:1. In another aspect, the primary aspect ratio is at least 8:1. In another aspect, the primary aspect ratio is at least 8.5:1. In another aspect, the primary aspect ratio is at least 9:1. In another aspect, the primary aspect ratio is at least 9.5:1. In another aspect, the primary aspect ratio is at least 10:1.
In a particular aspect, the secondary aspect ratio is at least 1:1. In another aspect, the secondary aspect ratio is at least 1.5:1. In another aspect, the secondary aspect ratio is 2:1. In another aspect, the secondary aspect ratio is at least 2.5:1. In another aspect, the secondary aspect ratio is at least 3:1. In another aspect, the secondary aspect ratio is at least 3.5:1. In another aspect, the secondary aspect ratio is at least 4:1. In another aspect, the secondary aspect ratio is at least 4.5:1. In another aspect, the secondary aspect ratio is at least 5:1. In another aspect, the secondary aspect ratio is at least 5.5:1. In another aspect, the secondary aspect ratio is at least 6:1. In another aspect, the secondary aspect ratio is at least 6.5:1. In another aspect, the secondary aspect ratio is at least 7:1. In another aspect, the secondary aspect ratio is at least 7.5:1. In another aspect, the secondary aspect ratio is at least 8:1. In another aspect, the secondary aspect ratio is at least 8.5:1. In another aspect, the secondary aspect ratio is at least 9:1. In another aspect, the secondary aspect ratio is at least 9.5:1. In another aspect, the secondary aspect ratio is at least 10:1.
In a particular aspect, the tertiary aspect ratio is at least 1:1. In another aspect, the tertiary aspect ratio is at least 1.5:1. In another aspect, the tertiary aspect ratio is 2:1. In another aspect, the tertiary aspect ratio is at least 2.5:1. In another aspect, the tertiary aspect ratio is at least 3:1. In another aspect, the tertiary aspect ratio is at least 3.5:1. In another aspect, the tertiary aspect ratio is at least 4:1. In another aspect, the tertiary aspect ratio is at least 4.5:1. In another aspect, the tertiary aspect ratio is at least 5:1. In another aspect, the tertiary aspect ratio is at least 5.5:1. In another aspect, the tertiary aspect ratio is at least 6:1. In another aspect, the tertiary aspect ratio is at least 6.5:1. In another aspect, the tertiary aspect ratio is at least 7:1. In another aspect, the tertiary aspect ratio is at least 7.5:1. In another aspect, the tertiary aspect ratio is at least 8:1. In another aspect, the tertiary aspect ratio is at least 8.5:1. In another aspect, the tertiary aspect ratio is at least 9:1. In another aspect, the tertiary aspect ratio is at least 9.5:1. In another aspect, the tertiary aspect ratio is at least 10:1.
In a particular aspect, the shape of the shaped abrasive grain 1300 with respect to the primary aspect ratio is generally rectangular, e.g., flat or curved. Moreover, the shape of the shaped abrasive grain 1300 with respect to the secondary aspect ratio may be any polyhedral shape, e.g., a triangle, a square, a rectangle, a pentagon, etc. The shape of the shaped abrasive grain 1300 with respect to the secondary aspect ratio may also be the shape of any alphanumeric character, e.g., 1, 2, 3, etc., A, B, C. etc. Further, the shape of the shaped abrasive grain 1300 with respect to the secondary aspect ratio may be a character selected from the Greek alphabet, the modern Latin alphabet, the ancient Latin alphabet, the Russian alphabet, any other alphabet, or any combination thereof. Further, the shape of the shaped abrasive grain 1300 with respect to the secondary aspect ratio may be a Kanji character.
In another aspect of the shaped abrasive grain 1300, the width 1344 is greater than the height 1342 and the height 1342 is greater than the length 1340. In this aspect, the shaped abrasive grain 1300 may define a primary aspect ratio that is the ratio of the width 1344 to the height 1342 (width:height). Further, the shaped abrasive grain 1300 may define a secondary aspect ratio that is the ratio of the height 1342 to the length 1340 (height:length). Finally, the shaped abrasive grain 1300 may define a tertiary aspect ratio that is the ratio of the width 1342 to the length 1340 (width:length).
In a particular aspect, the primary aspect ratio is at least 2:1. In another aspect, the primary aspect ratio is at least 2.5:1. In another aspect, the primary aspect ratio is at least 3:1. In another aspect, the primary aspect ratio is at least 3.5:1. In another aspect, the primary aspect ratio is at least 4:1. In another aspect, the primary aspect ratio is at least 4.5:1. In another aspect, the primary aspect ratio is at least 5:1. In another aspect, the primary aspect ratio is at least 5.5:1. In another aspect, the primary aspect ratio is at least 6:1. In another aspect, the primary aspect ratio is at least 6.5:1. In another aspect, the primary aspect ratio is at least 7:1. In another aspect, the primary aspect ratio is at least 7.5:1. In another aspect, the primary aspect ratio is at least 8:1. In another aspect, the primary aspect ratio is at least 8.5:1. In another aspect, the primary aspect ratio is at least 9:1. In another aspect, the primary aspect ratio is at least 9.5:1. In another aspect, the primary aspect ratio is at least 10:1.
In a particular aspect, the secondary aspect ratio is at least 1.5:1. In another aspect, the secondary aspect ratio is 2:1. In another aspect, the secondary aspect ratio is at least 2.5:1. In another aspect, the secondary aspect ratio is at least 3:1. In another aspect, the secondary aspect ratio is at least 3.5:1. In another aspect, the secondary aspect ratio is at least 4:1. In another aspect, the secondary aspect ratio is at least 4.5:1. In another aspect, the secondary aspect ratio is at least 5:1. In another aspect, the secondary aspect ratio is at least 5.5:1. In another aspect, the secondary aspect ratio is at least 6:1. In another aspect, the secondary aspect ratio is at least 6.5:1. In another aspect, the secondary aspect ratio is at least 7:1. In another aspect, the secondary aspect ratio is at least 7.5:1. In another aspect, the secondary aspect ratio is at least 8:1. In another aspect, the secondary aspect ratio is at least 8.5:1. In another aspect, the secondary aspect ratio is at least 9:1. In another aspect, the secondary aspect ratio is at least 9.5:1. In another aspect, the secondary aspect ratio is at least 10:1.
In a particular aspect, the tertiary aspect ratio is at least 1.5:1. In another aspect, the tertiary aspect ratio is 2:1. In another aspect, the tertiary aspect ratio is at least 2.5:1. In another aspect, the tertiary aspect ratio is at least 3:1. In another aspect, the tertiary aspect ratio is at least 3.5:1. In another aspect, the tertiary aspect ratio is at least 4:1. In another aspect, the tertiary aspect ratio is at least 4.5:1. In another aspect, the tertiary aspect ratio is at least 5:1. In another aspect, the tertiary aspect ratio is at least 5.5:1. In another aspect, the tertiary aspect ratio is at least 6:1. In another aspect, the tertiary aspect ratio is at least 6.5:1. In another aspect, the tertiary aspect ratio is at least 7:1. In another aspect, the tertiary aspect ratio is at least 7.5:1. In another aspect, the tertiary aspect ratio is at least 8:1. In another aspect, the tertiary aspect ratio is at least 8.5:1. In another aspect, the tertiary aspect ratio is at least 9:1. In another aspect, the tertiary aspect ratio is at least 9.5:1. In another aspect, the tertiary aspect ratio is at least 10:1.
In a particular aspect, the shape of the shaped abrasive grain 1300 with respect to the secondary aspect ratio is generally rectangular, e.g., flat or curved. Moreover, the shape of the shaped abrasive grain 1300 with respect to the primary aspect ratio may be any polyhedral shape, e.g., a triangle, a square, a rectangle, a pentagon, etc. The shape of the shaped abrasive grain 1300 with respect to the primary aspect ratio may also be the shape of any alphanumeric character, e.g., 1, 2, 3, etc., A, B, C. etc. Further, the shape of the shaped abrasive grain 1300 with respect to the primary aspect ratio may be a character selected from the Greek alphabet, the modern Latin alphabet, the ancient Latin alphabet, the Russian alphabet, any other alphabet, or any combination thereof. Moreover, the shape of the shaped abrasive grain 1300 with respect to the primary aspect ratio may be a Kanji character.
Referring now to
In a particular aspect, the edges 1506, 1508, 1510, 1512, 1514 in the dome shaped top 1504 may be formed by injecting the material comprising the shaped abrasive grain 1500 through a generally star shaped nozzle. It may be appreciated that the shape of the shaped abrasive grain 1500 may facilitate orientation of the shaped abrasive grain 1500 as it is dropped, or otherwise deposited, on a backing. Specifically, the dome shaped top 1504 will allow the shaped abrasive grain 1500 to roll onto the flat bottom 1502 ensuring that the edges face out, or up, from the backing.
Referring now to
It may be appreciated that the X shaped hole 1906 may be formed along the longitudinal axis 1908 through the geometric midpoint 1910 of the shaped abrasive grain 1900. Further, it may be appreciated that the X shaped hole 1906 may be rotated forty-five degrees (45°) and in such a case the hole 1906 would appear to be generally + shaped. It may be appreciated that the hole 1906 formed in the shaped abrasive grain 1900 may have any shape: polygonal or otherwise.
As shown, the first end face 2102 and the second end face 2104 are parallel to each other. However, in a particular aspect, the first end face 2102 is rotated with respect to the second end face 2104 to establish a twist angle 2114. In a particular aspect, the twist angle 2114 is at least about one degree. In another aspect, the twist angle 2114 is at least about two degrees. In another aspect, the twist angle 2114 is at least about five degrees. In another aspect, the twist angle 2114 is at least about eight degrees. In another aspect, the twist angle 2114 is at least about ten degrees. In another aspect, the twist angle 2114 is at least about twelve degrees. In another aspect, the twist angle 2114 is at least about fifteen degrees. In another aspect, the twist angle 2114 is at least about eighteen degrees. In another aspect, the twist angle 2114 is at least about twenty degrees. In another aspect, the twist angle 2114 is at least about twenty-five degrees. In another aspect, the twist angle 2114 is at least about thirty degrees. In another aspect, the twist angle 2114 is at least about forty degrees. In another aspect, the twist angle 2114 is at least about fifty degrees. In another aspect, the twist angle 2114 is at least about sixty degrees. In another aspect, the twist angle 2114 is at least about seventy degrees. In another aspect, the twist angle 2114 is at least about eighty degrees. In another aspect, the twist angle 2114 is at least about ninety degrees.
It can be appreciated that the twist angle 2100 of the shaped abrasive grain may be a horizontal twist angle, i.e., along a longitudinal axis of the body 2101 defining a length. In another aspect, the twist angle 2100 of the shaped abrasive grain may be a vertical twist angle, i.e., along a vertical axis defining a height of the body 2101.
Referring to
As shown in
As shown in
As shown in
As shown in
As shown in
A generally triangular first radial arm 3410 may extend outwardly from the central portion 3402 of the shaped abrasive grain 3400 along the length of the central portion 3402. A generally triangular second radial arm 3412 may extend outwardly from the central portion 3402 of the shaped abrasive grain 3400 along the length of the central portion 3402. A generally triangular third radial arm 3414 may extend outwardly from the central portion 3402 of the shaped abrasive grain 3400 along the length of the central portion 3402. A generally triangular fourth radial arm 3416 may extend outwardly from the central portion 3402 of the shaped abrasive grain 3400 along the length of the central portion 3402. Further, a generally triangular fifth radial arm 3418 may extend outwardly from the central portion 3402 of the shaped abrasive grain 3400 along the length of the central portion 3402.
As further depicted in
In a particular aspect, the radial arms 3410, 3412, 3414, 3416, 3418, 3420, 3422, 3424, 3426, 3428 may be equally spaced around the central portion 3402 of the shaped abrasive grain to form a generally star shaped first end face 3430, a generally star shaped second end face 3432 and a generally star shaped cross section taken parallel to the end faces 3430, 3432.
Referring now to
As illustrated, the shaped abrasive grain 3600 may include a generally flat third side face 3614 extending between the first K shaped side face 3610 and the second K shaped side face 3612 and between the first end face 3602 and the second end face 3604. The shaped abrasive grain 3600 may also include a generally flat fourth side face 3616 extending between the first K shaped side face 3610 and the second K shape side face 3612 opposite the generally flat third side face 3614.
As shown, the shaped abrasive grain 3800 may also include a third side face 3810 extending between the first end face 3802 and the second end face 3804 and between the first side face 3806 and the second side face 3808. Further, the shaped abrasive grain 3800 may include a fourth side face 3812 extending between the first end face 3802 and the second end face 3804 opposite the third side face 3810.
As depicted in
As shown, each end face 4002, 4004 the shaped abrasive grain 4000 may be generally diamond shaped. Each side face 4010, 4012, 4014, 4016 may be generally rectangular in shape. Further, the cross section of the shaped abrasive grain 4000 in a plane parallel to the end faces 4002, 4004 is generally diamond shaped. As shown, the shaped abrasive grain 4000 may also include a hole 4030 formed along a central longitudinal axis 4032. The hole 4030 may pass through the center of the shaped abrasive grain 4000. Alternatively, the hole 4030 may be offset from the center of the shaped abrasive grain 4000 in any direction.
As shown, the shaped abrasive grain 4200 may include continuous side face 4206 between the first end face 4202 and the second end face 4204. Accordingly, the shaped abrasive grain 4200 is generally frusto-conically shaped.
Referring now to
Further, the shaped abrasive grain 4400 may include a first side face 4410 extending between the first end face 4402 and the second end face 4404. A second side face 4412 may extend between the first end face 4402 and the second end face 4404 adjacent to the first side face 4410. As shown, the shaped abrasive grain 4400 may also include a third side face 4414 extending between the first end face 4402 and the second end face 4404 adjacent to the second side face 4412 and the first side face 4410.
As depicted in
Referring now to
Further, the shaped abrasive grain 4700 may include a first side face 4710 extending between the first end face 4702 and the second end face 4704. A second side face 4712 may extend between the first end face 4702 and the second end face 4704 adjacent to the first side face 4710. As shown, the shaped abrasive grain 4700 may also include a third side face 4714 extending between the first end face 4702 and the second end face 4704 adjacent to the second side face 4712. The shaped abrasive grain 4700 may also include a fourth side face 4716 adjacent to the third side face 4714 and the first side face 4710.
As depicted in
Further, the shaped abrasive grain 5000 may include a first side face 5010 extending between the first end face 5002 and the second end face 5004. A second side face 5012 may extend between the first end face 5002 and the second end face 5004 adjacent to the first side face 5010. As shown, the shaped abrasive grain 5000 may also include a third side face 5014 extending between the first end face 5002 and the second end face 5004 adjacent to the second side face 5012. The shaped abrasive grain 5000 may also include a fourth side face 5016 adjacent to the third side face 5014 and the first side face 5010.
As depicted in
As shown, the shaped abrasive grain 5300 may include a first side face 5310 extending between the first end face 5302 and the second end face 5304. A second side face 5312 may extend between the first end face 5302 and the second end face 5304 adjacent to the first side face 5310. As shown, the shaped abrasive grain 5300 may also include a third side face 5314 extending between the first end face 5302 and the second end face 5304 adjacent to the second side face 5312. The shaped abrasive grain 5300 may also include a fourth side face 5316 adjacent to the third side face 5314 and the first side face 5310.
As depicted in
Referring now to
As depicted, the shaped abrasive grain 5600 may include a first side face 5610 extending between the first end face 5602 and the second end face 5604. A second side face 5612 may extend between the first end face 5602 and the second end face 5604 adjacent to the first side face 5610. As shown, the shaped abrasive grain 5600 may also include a third side face 5614 extending between the first end face 5602 and the second end face 5604 adjacent to the second side face 5612 and the first side face 5610.
As shown in
Referring to
Further, the shaped abrasive grain 5900 may include a first side face 5910 extending between the first end face 5902 and the second end face 5904. A second side face 5912 may extend between the first end face 5902 and the second end face 5904 adjacent to the first side face 5910. As shown, the shaped abrasive grain 5900 may also include a third side face 5914 extending between the first end face 5902 and the second end face 5904 adjacent to the second side face 5912. The shaped abrasive grain 5900 may also include a fourth side face 5916 adjacent to the third side face 5914 and the first side face 5910.
As depicted in
One or more of the shaped abrasive grains described herein are configured to land in an upright orientation when deposited onto a backing. Further, one or more of the embodiments described herein may provide a relatively high aspect ratio associated with a particular length:height ratio, height:width ratio, length:width ratio, width:height ratio, height:length ratio, width:length ratio, or a combination thereof. A high aspect ratio enables the manufacture of a coated abrasive structure having an open coat, i.e., the distance between adjacent shaped abrasive grains may be increased. Further, the open coat provides greater space for chip clearance and may lower power consumption by making a better cut, or grind.
Moreover, in bonded abrasive and thin wheel applications shaped abrasive grains having high aspect ratios with sharp edges allows the manufacture of grinding wheels having greater porosity. Greater porosity provides more space for swarf and chip clearance and may enable more coolant to flow through the grinding wheel to provide greater efficiency.
The mixture 6201 can be formed to have a particular content of solid material, such as the ceramic powder material. For example, in one embodiment, the mixture 6201 can have a solids content of at least about 25 wt %, such as at least about 35 wt %, at least about 38 wt %, or even at least about 42 wt % for the total weight of the mixture 6201. Still, in at least one non-limiting embodiment, the solid content of the mixture 6201 can be not greater than about 75 wt %, such as not greater than about 70 wt %, not greater than about 65 wt %, or even not greater than about 55 wt %. It will be appreciated that the content of the solids materials in the mixture 6201 can be within a range between any of the minimum and maximum percentages noted above.
According to one embodiment, the ceramic powder material can include an oxide, a nitride, a carbide, a boride, an oxycarbide, an oxynitride, and a combination thereof. In particular instances, the ceramic material can include alumina. More specifically, the ceramic material may include a boehmite material, which may be a precursor of alpha alumina. The term “boehmite” is generally used herein to denote alumina hydrates including mineral boehmite, typically being Al2O3.H2O and having a water content on the order of 15%, as well as psuedoboehmite, having a water content higher than 15%, such as 20-38% by weight. It is noted that boehmite (including psuedoboehmite) has a particular and identifiable crystal structure, and accordingly unique X-ray diffraction pattern, and as such, is distinguished from other aluminous materials including other hydrated aluminas such as ATH (aluminum trihydroxide) a common precursor material used herein for the fabrication of boehmite particulate materials.
Furthermore, the mixture 6201 can be formed to have a particular content of liquid material. Some suitable liquids may include organic materials, such as water. In accordance with one embodiment, the mixture 6201 can be formed to have a liquid content less than the solids content of the mixture 6201. In more particular instances, the mixture 6201 can have a liquid content of at least about 25 wt % for the total weight of the mixture 6201. In other instances, the amount of liquid within the mixture 6201 can be greater, such as at least about 35 wt %, at least about 45 wt %, at least about 50 wt %, or even at least about 58 wt %. Still, in at least one non-limiting embodiment, the liquid content of the mixture can be not greater than about 75 wt %, such as not greater than about 70 wt %, not greater than about 65 wt %, not greater than about 60 wt %, or even not greater than about 55 wt %. It will be appreciated that the content of the liquid in the mixture 6201 can be within a range between any of the minimum and maximum percentages noted above.
Furthermore, to facilitate processing and forming shaped abrasive particles according to embodiments herein, the mixture 6201 can have a particular storage modulus. For example, the mixture 6201 can have a storage modulus of at least about 1×104 Pa, such as at least about 4×104 Pa, or even at least about 5×104 Pa. However, in at least one non-limiting embodiment, the mixture 6201 may have a storage modulus of not greater than about 1×107 Pa, such as not greater than about 1×106 Pa. It will be appreciated that the storage modulus of the mixture 6201 can be within a range between any of the minimum and maximum values noted above. The storage modulus can be measured via a parallel plate system using ARES or AR-G2 rotational rheometers, with Peltier plate temperature control systems. For testing, the mixture 6201 can be extruded within a gap between two plates that are set to be approximately 8 mm apart from each other. After extruding the get into the gap, the distance between the two plates defining the gap is reduced to 2 mm until the mixture 6201 completely fills the gap between the plates. After wiping away excess mixture, the gap is decreased by 0.1 mm and the test is initiated. The test is an oscillation strain sweep test conducted with instrument settings of a strain range between 0.1% to 100%, at 6.28 rad/s (1 Hz), using 25-mm parallel plate and recording 10 points per decade. Within 1 hour after the test completes, lower the gap again by 0.1 mm and repeat the test. The test can be repeated at least 6 times. The first test may differ from the second and third tests. Only the results from the second and third tests for each specimen should be reported.
Furthermore, to facilitate processing and forming shaped abrasive particles according to embodiments herein, the mixture 6201 can have a particular viscosity. For example, the mixture 6201 can have a viscosity of at least about 4×103 Pa s, at least about 5×103 Pa s, at least about 6×103 Pa s, at least about 8×103 Pa s, at least about 10×103 Pa s, at least about 20×103 Pa s, at least about 30×103 Pa s, at least about 40×103 Pa s, at least about 50×103 Pa s, at least about 60×103 Pa s, or even at least about 65×103 Pa s. In at least one non-limiting embodiment, the mixture 6201 may have a viscosity of not greater than about 1×106 Pa s, not greater than about 5×105 Pa s, not greater than about 3×105 Pa s, or even not greater than about 2×105 Pa s. It will be appreciated that the viscosity of the mixture 6201 can be within a range between any of the minimum and maximum values noted above. The viscosity can be calculated by dividing the storage modulus value by 6.28 s-l.
Moreover, the mixture 6201 can be formed to have a particular content of organic materials, including for example, organic additives that can be distinct from the liquid, to facilitate processing and formation of shaped abrasive particles according to the embodiments herein. Some suitable organic additives can include stabilizers, binders, such as fructose, sucrose, lactose, glucose, UV curable resins, and the like.
Notably, the embodiments herein may utilize a mixture 6201 that is distinct from slurries used in conventional tape casting operations. For example, the content of organic materials within the mixture 6201, particularly, any of the organic additives noted above may be a minor amount as compared to other components within the mixture 6201. In at least one embodiment, the mixture 6201 can be formed to have not greater than about 30 wt % organic material for the total weight of the mixture 6201. In other instances, the amount of organic materials may be less, such as not greater than about 15 wt %, not greater than about 10 wt %, or even not greater than about 5 wt %. Still, in at least one non-limiting embodiment, the amount of organic materials within the mixture 6201 can be at least about 0.1 wt %, such as at least about 0.5 wt % for the total weight of the mixture 6201. It will be appreciated that the amount of organic materials in the mixture 6201 can be within a range between any of the minimum and maximum values noted above.
Moreover, the mixture 6201 can be formed to have a particular content of acid or base distinct from the liquid, to facilitate processing and formation of shaped abrasive particles according to the embodiments herein. Some suitable acids or bases can include nitric acid, sulfuric acid, citric acid, chloric acid, tartaric acid, phosphoric acid, ammonium nitrate, ammonium citrate. According to one particular embodiment, the mixture 6201 can have a pH of less than about 5, and more particularly, within a range between about 2 and about 4, using a nitric acid additive.
Referencing
In certain systems, the die 6203 can include a die opening 6205 having a particular shape. It will be appreciated that the die opening 6205 may be shaped to impart a particular shape to the mixture 6201 during extrusion. In accordance with an embodiment, the die opening 6205 can have a rectangular shape. Furthermore, the mixture 6201 extruded through the die opening 6205 can have essentially the same cross-sectional shape as the die opening 6205. As further illustrated, the mixture 6201 may be extruded in the form of a sheet 6211 and onto a belt 6209 underlying the die 6203. In specific instances, the mixture 6201 can be extruded in the form of a sheet 6211 directly onto the belt 6209, which may facilitate continuous processing.
According to one particular embodiment, the belt can be formed to have a film overlying a substrate, wherein the film can be a discrete and separate layer of material configured to facilitate processing and forming of shaped abrasive particles. The process can include providing the mixture 6201 directly onto the film of the belt to form the sheet 6211. In certain instances, the film can include a polymer material, such as polyester. In at least one particular embodiment, the film can consist essentially of polyester.
In some embodiments, the belt 6209 can be translated while moving the mixture 6201 through the die opening 6205. As illustrated in the system 6200, the mixture 6201 may be extruded in a direction 6291. The direction of translation 6210 of the belt 6209 can be angled relative to the direction of extrusion 6291 of the mixture. While the angle between the direction of translation 6210 and the direction of extrusion 6291 are illustrated as substantially orthogonal in the system 6200, other angles are contemplated, including for example, an acute angle or an obtuse angle. The belt 6209 may be translated at a particular rate to facilitate processing. For example, the belt 6209 may be translated at a rate of at least about 3 cm/s, such as at least about 4 cm/s, at least about 6 cm/s, at least about 8 cm/s, or even at least about 10 cm/s. Still, in at least one non-limiting embodiment, the belt 6209 may be translated in a direction 6210 at a rate of not greater than about 5 m/s, such as not greater than about 1 m/s, or even not greater than about 0.5 m/s. It will be appreciated that the belt 6209 may be translated at a rate within a range between any of the minimum and maximum values noted above.
For certain processes according to embodiments herein, the rate of translation of the belt 6209 as compared to the rate of extrusion of the mixture 6201 in the direction 6291 may be controlled to facilitate proper processing. For example, the rate of translation of the belt 6209 can be essentially the same as the rate of extrusion to ensure formation of a suitable sheet 6211.
After the mixture 6201 is extruded through the die opening 6205, the mixture 6201 may be translated along the belt 6209 under a knife edge 6207 attached to a surface of the die 6203. The knife edge 6207 may facilitate forming a sheet 6211. More particularly, the opening defined between the surface of the knife edge 6207 and belt 6209 may define particular dimensions of the extruded mixture 6201. For certain embodiments, the mixture 6201 may be extruded in the form of a sheet 6211 having a generally rectangular cross-sectional shape as viewed in a plane defined by a height and width of the sheet 6211. While the extrudate is illustrated as a sheet, other shapes can be extruded, including for example cylindrical shapes and the like.
The process of forming the sheet 6211 from the mixture 6201 can include control of particular features and process parameters to facilitate suitable formation of shaped abrasive particles having one or more features as provided in the embodiments herein. For example, in certain instances, the process of forming a sheet 6211 from the mixture 6201 can include forming a sheet 6211 having a particular height 6281 controlled in part by a distance between the knife edge 6207 and a surface of the belt 6209. Moreover, it is noted that the height 6281 of the sheet 6211 can be controlled by varying a distance between the knife edge 6207 and the surface of the belt 6209. Additionally, forming the mixture 6201 into the sheet 6211 can include controlling the dimensions of the sheet 6211 based in part upon the viscosity of the mixture 6201. In particular, forming the sheet 6211 can include adjusting the height 6281 of the sheet 6211 based on the viscosity of the mixture 6201.
The sheet 6211 can have particular dimensions, including for example a length (l), a width (w), and a height (h). In accordance with an embodiment, the sheet 6211 may have a length that extends in the direction of the translating belt 6209, which can be greater than the width, wherein the width of the sheet 6211 is a dimension extending in a direction perpendicular to the length of the belt 6209 and to the length of the sheet. The sheet 6211 can have a height 6281, wherein the length and width are greater than the height 6281 of the sheet 6211.
Notably, the height 6281 of the sheet 6211 can be the dimension extending vertically from the surface of the belt 6209. In accordance with an embodiment, the sheet 6211 can be formed to have a particular dimension of height 6281, wherein the height may be an average height of the sheet 6211 derived from multiple measurements. For example, the height 6281 of the sheet 6211 can be at least about 0.1 mm, such as at least about 0.5 mm. In other instances, the height 6281 of the sheet 6211 can be greater, such as at least about 0.8 mm, at least about 1 mm, at least about 1.2 mm, at least about 1.6 mm, or even at least about 2 mm. Still, in one non-limiting embodiment, the height 6281 of the sheet 6211 may be not greater than about 10 mm, not greater than about 5 mm, or even not greater than about 2 mm. It will be appreciated that the sheet 6211 may have an average height within a range between any of the minimum and maximum values noted above.
According to one embodiment, the sheet 6211 can have a length (l), a width (w), and a height (h), wherein the length≥width≥height. Moreover, the sheet 6211 can have a secondary aspect ratio of length:height of at least about 10, such as at least about 100, at least about 1000, or even at least about 1000.
After extruding the mixture 6201 from the die 6203, the sheet 6211 may be translated in a direction 6212 along the surface of the belt 6209. Translation of the sheet 6211 along the belt 6209 may facilitate further processing to form precursor shaped abrasive particles. For example, the sheet 6211 may undergo a shaping process within the shaping zone 6213, which may In particular instances, the process of shaping can include shaping a surface of the sheet 6211, including for example, an upper major surface 6217 of the sheet 6211, which may be completed using a shaping article 6215. In other embodiments, other major surfaces of the sheet may undergo shaping, including for example, the bottom surface or side surfaces. For certain processes, shaping can include altering a contour of the sheet through one or more processes, such as, embossing, rolling, cutting, engraving, patterning, stretching, twisting, and a combination thereof.
In accordance with an embodiment, the process of forming a shaped abrasive particle can further include translation of the sheet along the belt 6209 through a forming zone 6221. In accordance with an embodiment, the process of forming a shaped abrasive particle can include sectioning the sheet 6211 to form precursor shaped abrasive particles 6223. For example, in certain instances, forming can include perforating a portion of the sheet 6211. In other instances, the process of forming can include patterning the sheet 6211 to form a patterned sheet and extracting shapes from the patterned sheet.
Particular processes of forming can include cutting, pressing, punching, crushing, rolling, twisting, bending, drying, and a combination thereof. In one embodiment, the process of forming can include sectioning of the sheet 6211. Sectioning of the sheet 6211 can include the use of at least one mechanical object, which may be in the form of a gas, liquid, or solid material. The process of sectioning can include at least one or a combination of cutting, pressing, punching, crushing, rolling, twisting, bending, and drying. Moreover, it will be appreciated that sectioning can include perforating or creating a partial opening through a portion of the sheet 6211, which may not extend through the entire height of the sheet 6211. In one embodiment, sectioning of the sheet 6211 can include use of a mechanical object including one or a plurality of a blade, a wire, a disc, and a combination thereof.
The process of sectioning can create different types of shaped abrasive particles in a single sectioning process. Different types of shaped abrasive particles can be formed from the same processes of the embodiments herein. Different types of shaped abrasive particles include a first type of shaped abrasive particle having a first two-dimensional shape and a second type of shaped abrasive particle having a different two-dimensional shape as compared to the first two-dimensional shape. Furthermore, different types of shaped abrasive particles may differ from each other in size. For example, different types of shaped abrasive particles may have different volumes as compared to each other. A single process which is capable of forming different types of shaped abrasive particles may be particularly suited for producing certain types of abrasive articles.
Sectioning can include moving the mechanical object through a portion of a sheet 6211 and creating an opening within the sheet 6211. In particular, the sheet can be formed to have an opening extending into the volume of the sheet and defined by certain surfaces. The opening can define a cut extending through at least a fraction of the entire height of sheet. It will be appreciated that the opening does not necessarily need to extend through the full height of the sheet. In certain instances, the method of sectioning can include maintaining the opening in the sheet. Maintaining the opening after sectioning the sheet has been sectioned by a mechanical object may facilitate suitable formation of shaped abrasive particles and features of shaped abrasive particles and features of a batch of shaped abrasive particles. Maintaining the opening can include at least partially drying at least one surface of the sheet defining the opening. The process of at least partially drying can include directing a drying material at the opening. A drying material may include a liquid, a solid, or even a gas. According to one particular embodiment, the drying material can include air. Controlled drying may facilitate the formation of shaped abrasive particles according to embodiments herein.
In certain instances, the process of sectioning can be conducted prior to sufficient drying of the sheet. For example, sectioning can be conducted prior to volatilization of not greater than about 20% of the liquid from the sheet as compared to the original liquid content of the sheet during initial formation of the sheet. In other embodiments, the amount of volatilization allowed to occur before or during sectioning can be less, such as, not greater than about 15%, not greater than about 12%, not greater than about 10%, not greater than about 8%, or even not greater than about 4% of the original liquid content of the sheet.
Referring again to
In one embodiment, the post-forming zone 6225 includes a heating process, wherein the precursor shaped abrasive particles 6223 may be dried. Drying may include removal of a particular content of material, including volatiles, such as water. In accordance with an embodiment, the drying process can be conducted at a drying temperature of not greater than 300° C. such as not greater than 280° C. or even not greater than about 250° C. Still, in one non-limiting embodiment, the drying process may be conducted at a drying temperature of at least 50° C. It will be appreciated that the drying temperature may be within a range between any of the minimum and maximum temperatures noted above.
Furthermore, the precursor shaped abrasive particles 6223 may be translated through a post-forming zone at a particular rate, such as at least about 0.2 feet/min and not greater than about 8 feet/min. Furthermore, the drying process may be conducted for a particular duration. For example, the drying process may be not greater than about six hours.
After the precursor shaped abrasive particles 6223 are translated through the post-forming zone 6225, the particles may be removed from the belt 6209. The precursor shaped abrasive particles 6223 may be collected in a bin 6227 for further processing.
In accordance with an embodiment, the process of forming shaped abrasive particles may further comprise a sintering process. The sintering process can be conducted after collecting the precursor shaped abrasive particles 6223 from the belt 6209. Sintering of the precursor shaped abrasive particles 6223 may be utilized to densify the particles, which are generally in a green state. In a particular instance, the sintering process can facilitate the formation of a high-temperature phase of the ceramic material. For example, in one embodiment, the precursor shaped abrasive particles 6223 may be sintered such that a high-temperature phase of alumina, such as alpha alumina is formed. In one instance, a shaped abrasive particle can comprise at least about 90 wt % alpha alumina for the total weight of the particle. In other instances, the content of alpha alumina may be greater, such that the shaped abrasive particle may consist essentially of alpha alumina.
As illustrated, the system 6300 can further include a die 6303 configured to conduct extrusion of a mixture 6301 contained within a reservoir 6302 of the die 6303. The process of forming a shaped abrasive particles can be initiated by forming a mixture 6301 including a ceramic material and a liquid as described herein.
The mixture 6301 can be provided within the interior of the die 6303 and configured to be extruded through a die opening 6305 positioned at one end of the die 6303. As further illustrated, extruding can include applying a force (or a pressure) on the mixture 6301 to facilitate extruding the mixture 6301 through the die opening 6305. In accordance with an embodiment, a particular pressure may be utilized during extrusion. For example, the pressure can be at least about 10 kPa, such as at least about 500 kPa. Still, in at least one non-limiting embodiment, the pressure utilized during extrusion can be not greater than about 4 MPa. It will be appreciated that the pressure used to extrude the mixture 6301 can be within a range between any of the minimum and maximum values noted above.
In particular instances, the mixture 6301 can be extruded through a die opening 6305 at the end of the die 6303 proximate to the screen 6351. The screen 6351 may be translated in a direction 6353 at a particular rate to facilitate suitable processing. Notably, the screen 6351 can be translated through the application zone 6383 including the die opening 6305 to facilitate the formation of precursor shaped abrasive particles. The screen 6351 may be translated through the application zone at a rate of at least about 3 cm/s, such as at least about 4 cm/s, at least about 6 cm/s, at least about 8 cm/s, or even at least about 10 cm/s. Still, in at least one non-limiting embodiment, the screen 6351 may be translated in a direction 6353 at a rate of not greater than about 5 m/s, such as not greater than about 1 m/s, or even not greater than about 0.5 m/s. It will be appreciated that the screen 6351 may be translated at a rate within a range between any of the minimum and maximum values noted above.
Additionally, the belt 6309 can be translated in a direction 6316 at a particular rate to facilitate suitable processing. For example, the belt 6309 can be translated at a rate of at least about 3 cm/s, such as at least about 4 cm/s, at least about 6 cm/s, at least about 8 cm/s, or even at least about 10 cm/s. Still, in at least one non-limiting embodiment, the belt 6309 may be translated in a direction 6316 at a rate of not greater than about 5 m/s, such as not greater than about 1 m/s, or even not greater than about 0.5 m/s. It will be appreciated that the belt 6309 may be translated at a rate within a range between any of the minimum and maximum values noted above.
In accordance with a particular embodiment, the screen 6351 may be translated at a particular rate as compared to the rate of translation of the belt 6309. For example, within the application zone 6383, the screen 6351 may be translated at substantially the same rate of translation of the belt 6309. That is, the difference in rate of translation between the screen and the belt may be not greater than about 5%, such as not greater than about 3%, or even not greater than about 1% based on the rate of the translation of the screen 6351.
As illustrated, the system 6300 can include an application zone 6383, including the die opening 6305. Within the application zone 6383, the mixture 6301 may be extruded from the die 6303 and directly onto the screen 6351. More particularly, a portion of the mixture 6301 may be extruded from the die opening 6305, and further extruded through one or more openings in the screen 6351 and onto the underlying belt 6309.
Referring briefly to
Certain aspects of processing were found to facilitate the formation of shaped abrasive particles according to embodiments herein. Notably, the orientation of the openings relative to the die head was found to have an effect on the shape of the shaped abrasive particles. In particular, it was noted, that when the openings are aligned as illustrated in
Referring again to
After extruding the mixture 6301 into the openings 6352 of the screen 6351, the belt 6309 and screen 6351 may be translated to a release zone 6385, wherein the belt 6309 and screen 6351 can be separated to facilitate the formation of precursor shaped abrasive particles. In accordance with an embodiment, the screen 6351 and belt 6309 may be separated from each other within the release zone 6385 at a particular release angle 6355. In accordance with specific embodiment, the release angle 6355 can be a measure of the angle between a lower surface 6354 of the screen 6351 and an upper surface 6356 of the belt 6309.
Notably, the mixture 6301 can be forced through the screen 6351 in rapid fashion, such that the average residence time of the mixture 6301 within the openings 152 can be less than about 2 minutes, less than about 1 minute, less than about 40 second, or even less than about 20 seconds. In particular non-limiting embodiments, the mixture 6301 may be substantially unaltered during printing as it travels through the screen openings 6352, thus experiencing no change in the amount of components, and may experience no appreciable drying in the openings 6352 of the screen 6351.
In an alternative embodiment, the process of forming can include a molding process. The molding process may utilize some of the same components of the system 6300, however, the screen can be replaced with a molding blank having openings within a substrate material for molding the mixture 6301. Notably, unlike a screen, the molding blank can have openings that extend partially through the entire thickness of the blank, such that the openings are not apertures extending from one major surface to the opposite major surface of the blank. Instead, the mold openings can have a bottom surface within the interior volume, which are intended to form a major surface of the precursor shaped abrasive particle formed therein. Moreover, a molding system may not necessarily utilize a belt underlying the molding blank.
The forming process may also utilize a particular drying process to facilitate formation of shaped abrasive particles having features of the embodiments herein. In particular, the drying process may include drying under conditions including humidity, temperature, and atmospheric pressure and composition suitable for limiting distortions to the shaped abrasive particles.
It was found that unlike the formation of shaped abrasive particles having typical polygonal shapes, the process of forming complex shapes, particularly using replication processes, required control of one or more process parameters, including drying conditions, amount and type of lubricant, pressure applied to the mixture during extrusion, material of the blank or belt, and the like. In particular instances, it was found that a belt or blank of stainless steel or polycarbonate polymer could be used. Moreover, it was found that the use of a natural oil material (e.g., canola oil) as a lubricant on the openings of the blank or belt may facilitate improved forming of shaped abrasive particles.
The body of the shaped abrasive particles may include additives, such as dopants, which may be in the form of elements or compounds (e.g., oxides). Certain suitable additives can include alkali elements, alkaline earth elements, rare-earth elements, hafnium (Hf), zirconium (Zr), niobium (Nb), tantalum (Ta), molybdenum (Mo), and a combination thereof. In particular instances, the additive can include an element such as lithium (Li), sodium (Na), potassium (K), magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), scandium (Sc), yttrium (Y), lanthanum (La), cesium (Ce), praseodymium (Pr), niobium (Nb), hafnium (Hf), zirconium (Zr), tantalum (Ta), molybdenum (Mo), vanadium (V), chromium (Cr), cobalt (Co), iron (Fe), germanium (Ge), manganese (Mn), nickel (Ni), titanium (Ti), zinc (Zn), and a combination thereof.
The body of a shaped abrasive article may include a specific content of additive (e.g., dopant). For example, the body of a shaped abrasive particle may include not greater than about 12 wt % additive for the total weight of the body. In still other embodiments, they amount of additive may be less, such as not greater than about 11 wt %, not greater than about 10 wt %, not greater than about 9 wt %, not greater than about 8 wt %, not greater than about 7 wt %, not greater than about 6 wt %, or even not greater than about 5 wt %. Still, the amount of additive in at least one non-limiting embodiment can be at least about 0.5 wt %, such as at least about 1 wt %, at least about 1.3 wt %, at least about 1.8 wt %, at least about 2 wt %, at least about 2.3 wt %, at least about 2.8 wt %, or even at least about 3 wt %. It will be appreciated that the amount of additive within a body of a shaped abrasive particle may be within a range between any of the minimum and maximum percentages noted above.
The shaped abrasive particle 6500 can have a body 6501 in the form of a three-pointed star defined by the first arm 6503, second arm 6504, and the third arm 6505 extending from the central portion 6502. According to one particular embodiment, at least one of the arms, including for example, the first arm 6503, can have a midpoint width 6513 that is less than a central portion width 6512. The central portion 6502 can be defined as a region between the midpoints 6551, 6552, and 6553 of the first side surface 6554, second side surface 6555, and third side surface 6556, respectively. The central portion width 6512 of the first arm 6503 can be the width of the dimension between the midpoints 6551 and 6552. The midpoint width 6513 can be the width of the line at a midpoint between the line of the central portion width 6510 and the tip 6506 of the first arm 6503 along a first axis 6560. In certain instances, the midpoint width 6513 can be not greater than about 90% of the central portion width 6512, such as not greater than about 80%, not greater than about 70%, not greater than about 65%, or even not greater than about 60%. Still, the midpoint width 6513 can be at least about 10%, such as at least about 20%, at least about 30%, or even at least about 40% of the central portion width 6510. It will be appreciated that the midpoint width 6513 can have a width relative to the central portion width 6512 within a range between any of the above minimum and maximum percentages.
Moreover, the body 6501 can have at least one arm, such as the first arm 6503, having a tip width 6514 at the tip 6506 of the first arm 6503 that is less than a midpoint width 6513. In such instances wherein the tip 6506 is sharply formed, the tip width 6514 may be considered 0. In instances wherein the tip 6506 has a radius of curvature, the tip width 6514 may be considered the diameter of the circle defined by the radius of curvature. According to one embodiment, the tip width 6514 can be not greater than about 90% of the midpoint width 6513, such as not greater than about 80%, not greater than about 70%, not greater than about 60%, not greater than about 50%, not greater than about 40%, not greater than about 30%, not greater than about 20%, or even not greater than about 10%. Still, in certain non-limiting embodiments, the tip width 6514 can be at least about 1%, such as at least about 2%, at least about 3%, at least about 5%, or even at least about 10% of the midpoint width 6513. It will be appreciated that the tip width 6514 can have a width relative to the midpoint width 6513 within a range between any of the above minimum and maximum percentages.
As further illustrated, the body 6501 can have a first arm 6503 including a first tip 6506 defining a first tip angle 6521 between the first side surface 6554 and the second side surface 6555. According to an embodiment, the first tip angle can be less than about 60 degrees, such as not greater than about 55 degrees, not greater than about 50 degrees, not greater than about 45 degrees, or even not greater than about 40 degrees. Still, the first tip angle can be at least about 5 degrees, such as at least about 8 degrees, at least about 10 degrees, at least about 15 degrees, at least about 20 degrees, at least about 25 degrees, or even at least about 30 degrees. The first tip angle can be within a range between any of the minimum and maximum values noted above.
The body 6501 can include a second arm 6504 having a second tip 6507 defining a second tip angle 6522 between the second side surface 6555 and third side surface 6556. The second tip angle can be substantially the same as the first tip angle, such as within 5% of the angle numerical value. Alternatively, the second tip angle can be substantially different relative to the first tip angle.
The body 6501 can include a third arm 6505 having a third tip 6508 defining a third tip angle 6523 between the first side surface 6554 and third side surface 6556. The third tip angle can be substantially the same as the first tip angle or second tip angle, such as within 5% of the angle numerical value. Alternatively, the third tip angle can be substantially different relative to the first tip angle or the second tip angle.
The body 6501 can have a total angle, which is a sum of the value of the first tip angle, second tip angle, and third tip angle which can be less than about 180 degrees. In other embodiments, the total angle can be not greater than about 175 degrees, such as not greater than about 170 degrees, not greater than about 165 degrees, not greater than about 150 degrees, such as not greater than about 140 degrees, not greater than about 130 degrees, not greater than about 125 degrees, or even not greater than about 120 degrees. Still, in one non-limiting embodiment, the body 6501 can have a total angle of at least about 60 degrees, such as at least about 70 degrees, at least about 80 degrees, at least about 90 degrees, such as at least about 95 degrees, at least about 100 degrees, or even at least about 105 degrees. It will be appreciated that the total sum angle can be within a range between any of the minimum and maximum values noted above.
As noted herein, the body 6501 can have a first side surface 6554 extending between the first arm 6506 and the third arm 6508. In certain instances, the first side surface 6554 can have an arcuate contour. For example, turning briefly to
Referring again to
The first side section 6558 can extend for a significant portion of the length of the first side surface 6554. For example, the first side section 6558 can extend for at least about 20%, such as at least about 25%, at least about 30%, at least about 35%, or even at least about 40% of a total length of the first side surface 6554. Still, in one non-limiting embodiment, the first side section 6558 can have a length (ls1) between the midpoint 6551 and the first tip 6506 of not greater than about 80%, such as not greater than about 75%, not greater than about 70%, or even not greater than about 65% of the total length of the side surface 6554. It will be appreciated that the length of the first side section 6558 can be within a range between any of the minimum and maximum percentages noted above.
The second side section 6559 can extend for a significant portion of the length of the first side surface 6554. For example, the second side section 6559 can extend for at least about 20%, such as at least about 25%, at least about 30%, at least about 35%, or even at least about 40% of a total length of the first side surface 6554. Still, in one non-limiting embodiment, the second side section 6559 can have a length (ls2) between the midpoint 6551 and the third tip 6508 of not greater than about 80%, such as not greater than about 75%, not greater than about 70%, or even not greater than about 65% of the total length of the side surface 6554 as a straight line between the first tip 6506 and the third tip 6508. It will be appreciated that the length of the second side section 6559 can be within a range between any of the minimum and maximum percentages noted above.
The body 6501 can further include a fractured region 6570 on at least a portion of one side surface. For example, the body 6501 can have a fractured region 6570 on a portion of the side surface 6554 between the midpoint 6551 and the third tip 6508. The fracture region 6570 can be intersecting at least a portion of an edge defining the base surface 6511. Alternatively, or additionally, the fracture region 6570 can be intersecting at least a portion of an edge defining the upper surface 6510. The fractured region can be characterized by having a surface roughness greater than a surface roughness of at least the upper surface 6510 or the base surface 6511 of the body 6501. The fractured region 6570 can define a portion of the body extending from the base surface 6511. In certain instances, the fractured region 6570 can be characterized by irregularly shaped protrusions and grooves extending from the base surface 6511 along the first side surface 6554. In certain instances, the fractured region 6570 can appear as and define a serrated edge. A fracture region 6583 is also illustrated on the side surface 6582 of the shaped abrasive particle of
In certain instances, the fracture region 6570 can be preferentially located at or near the tips of the arms of the body. The fractured region 6570 can extend from the bottom surface 1703 and extend vertically for a fraction of the entire height of the side surface or even for the entire height of the side surface.
While the foregoing body 6501 of the three-pointed star has been shown to have an upper surface 6510 having a two-dimensional shape, as viewed in the plane of the length and width of the body, that is substantially the same as the two-dimensional shape of the base surface 6511 of the body 6501, other shapes are contemplated. For example, in one embodiment, the cross-sectional shape of the body at the base surface can define a base surface shape from the group consisting of a three-pointed star, a four pointed star, a cross-shape, a polygon, ellipsoids, numerals, Greek alphabet characters, Latin alphabet characters, Russian alphabet characters, complex shapes having a combination of polygonal shapes, and a combination thereof. Moreover, the cross-sectional shape of the body at the upper surface can define an upper surface shape, which can be different than the base surface shape and selected from the group of a three-pointed star, a four pointed star, a cross-shape, a polygon, ellipsoids, numerals, Greek alphabet characters, Latin alphabet characters, Russian alphabet characters, complex shapes having a combination of polygonal shapes, and a combination thereof.
In particular instances, the upper surface shape can have an arcuate form of the base surface shape. For example, the upper surface shape can define an arcuate three-pointed two-dimensional shape, wherein the arcuate three-pointed two-dimensional shape defines arms having rounded ends. In particular, the arms as defined at the base surface can have a smaller radius of curvature at the tip as compared to the radius of curvature of the corresponding tip at the upper surface.
As described in other embodiments herein, it will be appreciated that at least one of the arms of the body 6501 may be formed to have a twist, such that the arm twists around a central axis. For example, the first arm 6503 may twist around the axis 6560. Moreover, the body 6501 can be formed such that at least one arm extends in an arcuate path from the central region.
The shaped abrasive particle 6600 can have a body 6601 in the form of a four-pointed star defined by the first arm 6603, a second arm 6604, a third arm 6605, and the fourth arm 6606 extending from the central portion 6602. The body 6601 can have any of the features described in the embodiments herein. For example, according to one particular embodiment, at least one of the arms, including for example, the first arm 6603, can have a midpoint width that is less than a central portion width, as described in accordance with the embodiment of
In one aspect, the body 6601 can have a first arm 6603 including a first tip 6607 defining a first tip angle 6621 between the first side surface 6654 and the second side surface 6655. According to an embodiment, the first tip angle can be less than about 60 degrees, such as not greater than about 55 degrees, not greater than about 50 degrees, not greater than about 45 degrees, or even not greater than about 40 degrees. Still, the first tip angle 6621 can be at least about 5 degrees, such as at least about 8 degrees, at least about 10 degrees, at least about 15 degrees, or even at least about 20 degrees. The first tip angle 6621 can be within a range between any of the minimum and maximum values noted above. Likewise, any of the other tips, including the second tip 6608 of the second arm 6604, the third tip 6609 of the third arm 6605, or fourth tip 6610 of the fourth arm 6606 can have a tip angle having the same features described in accordance with the first tip angle 6621 above.
According to one embodiment the second tip 6608 can define a second tip angle that is substantially the same as the first tip angle 6621, such as within 5% of the angle numerical value. Alternatively, the second tip angle can be substantially different relative to the first tip angle 6621. The third tip 6609 can define a third tip angle that is substantially the same as the first tip angle 6621, such as within 5% of the angle numerical value. Alternatively, the third tip angle can be substantially different relative to the first tip angle 6621. The fourth tip 6610 can define a fourth tip angle that is substantially the same as the first tip angle 6621, such as within 5% of the angle numerical value. Alternatively, the fourth tip angle can be substantially different relative to the first tip angle 6621.
According to one embodiment, the body 6601 can include a first arm 6603, second arm 6604, third arm 6605, and fourth arm 6606 that are substantially evenly spaced apart with respect to each other. As illustrated, the arms 6603-6606 can be spaced substantially evenly around the central portion 6602. In one particular embodiment, the arms 6603-6606 can be spaced apart from each other at substantially orthogonal angles relative to each other. In other embodiments, the first arm 6603 and second arm 6604 can be spaced apart from each other based on the spacing angle 6631 defined by the angle between the axis 6690 extending between opposite tips 6609 and 6607 and through the midpoint 6609 relative to the axis 6691 extending between tips 6608 and 6610 and through the midpoint 6609. The first arm 6603 and second arm 6604 can be spaced apart from each other as define by the spacing angle 6631 by at least about 45 degrees, such as at least about 60 degrees, or even at least about 70 degrees. Still, in other embodiments, the spacing angle 6631 can be not greater than about 120 degrees, such as not greater than about 110 degrees, or even approximately 90 degrees. The spacing angle 6631 can be within a range between any of the minimum and maximum values noted above.
In certain instances, the body 6601 can be formed such that at least one side surface, such as the first side surface 6654 can have an arcuate contour. In more particular embodiments, at least one side surface can have a concave curvature for at least a portion of the length of the entire side surface.
In still another embodiment, at least one side surface of the body 6601, such as the first side surface 6654, can have a first section 6625 and a second section 6626, which can be joined together at a first side surface midpoint 6627 and defining a first interior angle 6628. According to one embodiment, the first interior angle can be greater than about 90 degrees, such as greater than about 95 degrees, greater than about 100 degrees, greater than about 130 degrees, greater than about 160 degrees, greater than about 180 degrees, or even greater than about 210 degrees. Still, in one non-limiting embodiment, the first interior angle can be not greater than about 320 degrees, not greater than about 300 degrees, or even not greater than about 270 degrees. The first interior angle can be within a range between any of the minimum and maximum values noted above. Moreover, the body can include a second interior angle 6629 at the second side surface 6655, a third interior angle 6632 at the third side surface 6656, and a fourth interior angle 6633 at the fourth side surface 6657. Each of the interior angles can have the features described with respect to the first interior angle 6628. Moreover, each and any of the second side surface 6655, the third side surface 6656, and the fourth side surface 6657 can have any of the features of the first side surface 6654.
The body 6601 can have a first arm 6603 and the third arm 6605 extending in opposite directions from the central portion 6602 of the body 6601 relative to each other. Moreover, the second arm 6604 and the fourth arm 6606 can extend in opposite directions relative to each other. According to one embodiment, the second arm 6604 can have a length, as measured between from the boundary of the central portion 6602 to the tip 6608 along the axis 6691 that can be substantially the same as a length of the fourth arm 6606. In yet another instance, the second arm 6604 can have a length that is substantially different than (e.g., less than or greater than) a length of the first arm 6603 or third arm 6605.
While the foregoing body 6601 of the four-pointed star has been shown to have an upper surface 6640 having a two-dimensional shape, as viewed in the plane of the length and width of the body, that is substantially the same as the two-dimensional shape of the base surface 6641 of the body 6501, other shapes are contemplated. For example, in one embodiment, the cross-sectional shape of the body at the base surface can define a base surface shape from the group consisting of a three-pointed star, a four pointed star, a cross-shape, a polygon, ellipsoids, numerals, Greek alphabet characters, Latin alphabet characters, Russian alphabet characters, complex shapes having a combination of polygonal shapes, and a combination thereof. Moreover, the cross-sectional shape of the body at the upper surface can define an upper surface shape, which can be different than the base surface shape and selected from the group of a three-pointed star, a four pointed star, a cross-shape, a polygon, ellipsoids, numerals, Greek alphabet characters, Latin alphabet characters, Russian alphabet characters, complex shapes having a combination of polygonal shapes, and a combination thereof.
In particular instances, the upper surface shape can have an arcuate form of the base surface shape. For example, the upper surface shape can define an arcuate four-pointed two-dimensional shape, wherein the arcuate four-pointed two-dimensional shape defines arms having rounded ends. In particular, the arms as defined at the base surface can have a smaller radius of curvature at the tip as compared to the radius of curvature of the corresponding tip at the upper surface.
According to one particular aspect, the body can be formed to have limited deformation or warping of the body. For example, the body can have a curling factor (ht/hi) of not greater than about 10, wherein the curling factor is defined as a ratio between the greatest height of the body at one tip of an arm (ht) as compared to a smallest dimension of height of the body at the interior (hi) (e.g., within the central portion 6602). For example, turning to a side-view illustration of a shaped abrasive particle of
The body 6701 can have at least one arm, such as the first arm 6703 having a midpoint width 6714 that is substantially the same as a central portion width 6712 of the first arm 6703. Moreover, the length of the arm between points 6715 and 6716 on the axis 6790 defining the width of the body 6701 can be less than the width of the first arm 6703. In particular instances, the length can be not greater than about 90% of the width, such as not greater than about 80%, not greater than about 70%, not greater than about 60%. Still, in one non-limiting embodiment, the length of the first arm 6703 can be at least about 10%, such as at least about 20% of the width of the first arm 6703. The length can have a dimension relative to the width within a range between any of the minimum and maximum percentages noted above. Reference to the width of the first arm 6703 can be reference to the central portion width 6712, or midpoint width 6714. Any of the arms of the body 6701 can have the same features of the first arm 6703.
In the particular embodiment of
In one embodiment, the plateau region 6902 can have a lateral distance 6921, which can be defined as the greatest distance between an edge 6907 between the upper surface 6910 of the first layer 6902 and a side surface 6904 of the first layer to the side surface 6905 of the second layer. Analysis of the lateral distance 6921 may be facilitated by a top-view image of the body 6901, such as shown in
The second layer 6903 can have a particular length 6909, which is the longest dimension of a side, such as shown in
The foregoing shaped abrasive particle of
Moreover, in certain instances, the first screen and second screen can be used at the same time as a composite screen to shape the mixture. In such instances, the first screen and second screen may be affixed to each other to facilitate proper and continuous alignment between the openings of the first screen and second screen. The second screen can be oriented on the first screen to facilitate alignment between the openings in the first screen and openings in the second screens to facilitate suitable delivery of the mixture into the openings of the first screen and second screen.
Still, the first screen and second screen may be used in separate processes. For example, wherein the first mixture is provided in the first screen at a first time and the second mixture is provided in the second screen at a second time. More particularly, the first mixture can be provided in the openings of the first screen, and after the first mixture has been formed in the openings of the first screen, the second mixture can be provided on the first mixture. Such a process may be conducted while the first mixture is contained in the first openings of the first screen. In another instance, the first mixture may be removed from the openings of the first screen to create precursor shaped abrasive particles of the first mixture. Thereafter, the precursor shaped abrasive particles of the first mixture can be oriented with respect to openings of the second screen, and the second mixture can be placed in the openings of the second screen and onto the precursor shaped abrasive particles of the first mixture to facilitate formation of composite precursor shaped abrasive particles including the first mixture and the second mixture. The same process may be used with one mold and one screen. Moreover, the same process may be completed using first and second molds to form the first and second layers, respectively.
It will be appreciated that any of the characteristics of the embodiments herein can be attributed to a batch of shaped abrasive particles. A batch of shaped abrasive particles can include, but need not necessarily include, a group of shaped abrasive particles made through the same forming process. In yet another instance, a batch of shaped abrasive particles can be a group of shaped abrasive particles of an abrasive article, such as a fixed abrasive article, and more particularly, a coated abrasive article, which may be independent of a particular forming method, but having one or more defining features present in a particular population of the particles. For example, a batch of particles may include an amount of shaped abrasive particles suitable for forming a commercial grade abrasive product, such as at least about 20 lbs. of particles.
Moreover, any of the features of the embodiments herein (e.g., aspect ratio, multiple portions, number of arms, midpoint width to central portion width, two-dimensional shape, curling factor, etc.) can be a characteristic of a single particle, a median value from a sampling of particles of a batch, or an average value derived from analysis of a sampling of particles from a batch. Unless stated explicitly, reference herein to the characteristics can be considered reference to a median value that is a based on a statistically significant value derived from a random sampling of suitable number of particles of a batch. Notably, for certain embodiments herein, the sample size can include at least 10, and more typically, at least 40 randomly selected particles from a batch of particles.
Any of the features described in the embodiments herein can represent features that are present in at least a portion of a batch of shaped abrasive particles. The portion may be a minority portion (e.g., less than 50% and any whole number integer between 1% and 49%) of the total number of particles in a batch, a majority portion (e.g., 50% or greater and any whole number integer between 50% and 99%) of the total number of particles of the batch, or even essentially all of the particles of a batch (e.g., between 99% and 100%). The provision of one or more features of any shaped abrasive particle of a batch may facilitate alternative or improved deployment of the particles in an abrasive article and may further facilitate improved performance or use of the abrasive article.
A batch of particulate material can include a first portion including a first type of shaped abrasive particle and a second portion including a second type of shaped abrasive particle. The content of the first portion and second portion within the batch may be controlled at least in part based upon certain processing parameters. Provision of a batch having a first portion and a second portion may facilitate alternative or improved deployment of the particles in an abrasive article and may further facilitate improved performance or use of the abrasive article.
The first portion may include a plurality of shaped abrasive particles, wherein each of the particles of the first portion can have substantially the same features, including for example, but not limited to, the same two-dimensional shape of a major surface. The batch may include various contents of the first portion. For example, the first portion may be present in a minority amount or majority amount. In particular instances, the first portion may be present in an amount of at least about 1%, such as at least about 5%, at least about 10%, at least about 20%, at least about 30%, at least about 40%, at least about 50%, at least about 60%, or even at least about 70% for the total content of portions within the batch. Still, in another embodiment, the batch may include not greater than about 99%, such as not greater than about 90%, not greater than about 80%, not greater than about 70%, not greater than about 60%, not greater than about 50%, not greater than about 40%, not greater than about 30%, not greater than about 20%, not greater than about 10%, not greater than about 8%, not greater than about 6%, or even not greater than about 4% of the total portions within the batch. The batch can include a content of the first portion within a range between any of the minimum and maximum percentages noted above.
The second portion of the batch can include a plurality of shaped abrasive particles, wherein each of the shaped abrasive particles of the second portion can have substantially the same feature, including for example, but not limited to, the same two-dimensional shape of a major surface. The second portion can have one or more features of the embodiments herein, which can be distinct compared to the plurality of shaped abrasive particles of the first portion. In certain instances, the batch may include a lesser content of the second portion relative to the first portion, and more particularly, may include a minority content of the second portion relative to the total content of particles in the batch. For example, the batch may contain a particular content of the second portion, including for example, not greater than about 40%, such as not greater than about 30%, not greater than about 20%, not greater than about 10%, not greater than about 8%, not greater than about 6%, or even not greater than about 4%. Still, in at least on non-limiting embodiment, the batch may contain at least about 0.5%, such as at least about 1%, at least about 2%, at least about 3%, at least about 4%, at least about 10%, at least about 15%, or even at least about 20% of the second portion for the total content of portions within the batch. It will be appreciated that the batch can contain a content of the second portion within a range between any of the minimum and maximum percentages noted above.
Still, in an alternative embodiment, the batch may include a greater content of the second portion relative to the first portion, and more particularly, can include a majority content of the second portion for the total content of particles in the batch. For example, in at least one embodiment, the batch may contain at least about 55%, such as at least about 60% of the second portion for the total portions of the batch.
It will be appreciated that the batch can include other portions, including for example a third portion, comprising a plurality of shaped abrasive particles having a third feature that can be distinct from the features of the particles of the first and second portions. The batch may include various contents of the third portion relative to the second portion and first portion. The third portion may be present in a minority amount or majority amount. In particular instances, the third portion may be present in an amount of not greater than about 40%, such as not greater than about 30%, not greater than about 20%, not greater than about 10%, not greater than about 8%, not greater than about 6%, or even not greater than about 4% of the total portions within the batch. Still, in other embodiments the batch may include a minimum content of the third portion, such as at least about 1%, such as at least about 5%, at least about 10%, at least about 20%, at least about 30%, at least about 40%, or even at least about 50%. The batch can include a content of the third portion within a range between any of the minimum and maximum percentages noted above. Moreover, the batch may include a content of diluent, randomly shaped abrasive particles, which may be present in an amount the same as any of the portions of the embodiments herein.
A mixture in the form of a gel is obtained having approximately 42% solids loading of boehmite commercially available as Catapal B from Sasol Corp. combined with 58 wt % water containing a minority content of nitric acid and organic additives. The gel has a viscosity of approximately 3×103 to 4×104 Pa·s and a storage modulus of 3×104 to 2×105 Pa.
The gel is extruded from a die using a pressure of up to 80 psi (552 kPa) onto a mold blank of polycarbonate and into a plurality of openings, wherein each of the openings are in the shape of a three-pointed star. The surfaces of the openings within the mold blank have been coated with canola oil. The openings define three-pointed star two-dimensional shapes having a length of approximately 5-7 mm, a width of 3-5 mm, and a depth of approximately 0.8 mm. The openings have tip angles of approximately 35 degrees, and an interior angle between the three arms of approximately 225 degrees.
The gel is extruded into the openings and the gel is then dried for approximately 24-48 hours in air under atmospheric conditions and within the mold to form precursor shaped abrasive particles. The precursor shaped abrasive particles were calcined in a box furnace at approximately 600° C. for an 1 hour and then, the precursors shaped abrasive particles were sintered in a tube furnace up to 1320° C. for 3 to 20 minutes.
The process of Example 1 was used with the exception that the mold blank utilized openings defining a four-point star shaped two-dimensional shape having a length of approximately 7-9 mm, a width of 7-9 mm, and a depth of approximately 0.8 mm. The openings have tip angles of approximately 25 degrees, and an interior angle between the three arms of approximately 250 degrees.
The process of Example 1 was used with the exception that the mold blank utilized openings defining a cross-shaped two-dimensional shape having a length of approximately 5-6 mm, a width of 5-6 mm, and a depth of approximately 0.8 mm. The arms have a width of approximately 2 mm and a length of approximately 1 mm.
The present application represents a departure from the state of the art. While the industry has recognized that shaped abrasive particles may be formed through processes such as molding and screen printing, the processes of the embodiments herein are distinct from such processes. Moreover, the resulting shaped abrasive particles have one or a combination of distinct features from particles formed according to conventional approaches. The shaped abrasive particles of the embodiments herein can have a particular combination of features distinct from other conventional particles including, but not limited to, aspect ratio, composition, additives, two-dimensional shape, three-dimensional shape, stepped configuration, curling factor, tip angles, interior angles, and the like. Notably, the embodiments herein include a combination of features facilitating the formation of batches of shaped abrasive particle having particular features. And in fact, one or more such features facilitate alternative deployment of the particles in abrasive articles, and further, may facilitate improved performance in the context of fixed abrasives, such as bonded abrasives or coated abrasives.
The above-disclosed subject matter is to be considered illustrative, and not restrictive, and the appended claims are intended to cover all such modifications, enhancements, and other embodiments, which fall within the true scope of the present invention. Thus, to the maximum extent allowed by law, the scope of the present invention is to be determined by the broadest permissible interpretation of the following claims and their equivalents, and shall not be restricted or limited by the foregoing detailed description.
The Abstract of the Disclosure is provided to comply with Patent Law and is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims. In addition, in the foregoing Detailed Description, various features may be grouped together or described in a single embodiment for the purpose of streamlining the disclosure. This disclosure is not to be interpreted as reflecting an intention that the claimed embodiments require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive subject matter may be directed to less than all features of any of the disclosed embodiments. Thus, the following claims are incorporated into the Detailed Description, with each claim standing on its own as defining separately claimed subject matter.
This application is a continuation of U.S. Non-Provisional patent application Ser. No. 15/681,796, filed Aug. 21, 2017, entitled “ABRASIVE PARTICLES HAVING COMPLEX SHAPES AND METHODS OF FORMING SAME,” naming inventor Doruk O. Yener et al. which is a continuation of U.S. Non-Provisional patent application Ser. No. 15/402,860, filed Jan. 10, 2017, entitled “ABRASIVE PARTICLES HAVING COMPLEX SHAPES AND METHODS OF FORMING SAME” naming inventor Doruk O. Yener et al., which is a continuation of U.S. Non-Provisional patent application Ser. No. 14/964,229, filed Dec. 9, 2015, now U.S. Pat. No. 9,567,505, issued Feb. 14, 2017, entitled “ABRASIVE PARTICLES HAVING COMPLEX SHAPES AND METHODS OF FORMING SAME” naming inventor Doruk O. Yener et al., which is a continuation of U.S. Non-Provisional patent application Ser. No. 14/201,436, filed Mar. 7, 2014, now U.S. Pat. No. 9,238,768, issued Jan. 19, 2016, entitled “ABRASIVE PARTICLES HAVING COMPLEX SHAPES AND METHODS OF FORMING SAME” naming inventor Doruk O. Yener et al., which is a continuation of U.S. Non-Provisional patent application Ser. No. 13/738,890, filed Jan. 10, 2013, now U.S. Pat. No. 8,753,742, issued Jun. 17, 2014, entitled “ABRASIVE PARTICLES HAVING COMPLEX SHAPES AND METHODS OF FORMING SAME” naming inventor Doruk O. Yener et al., and claims priority from U.S. Provisional Patent Application No. 61/584,998, filed Jan. 10, 2012, entitled “ABRASIVE PARTICLES HAVING COMPLEX SHAPES AND METHODS OF FORMING SAME” naming inventor Doruk O. Yener et al., which applications are incorporated by reference herein in their entireties.
| Number | Date | Country | |
|---|---|---|---|
| 61584998 | Jan 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15681796 | Aug 2017 | US |
| Child | 15962838 | US | |
| Parent | 15402860 | Jan 2017 | US |
| Child | 15681796 | US | |
| Parent | 14964229 | Dec 2015 | US |
| Child | 15402860 | US | |
| Parent | 14201436 | Mar 2014 | US |
| Child | 14964229 | US | |
| Parent | 13738890 | Jan 2013 | US |
| Child | 14201436 | US |