Patent Grant
6840006
The invention relates to a mulching paper degradation process as well as to the mulching paper for implementing the process. As will be described below, the invention also relates to an enzymatic solution for implementing the said process.
In the rest of the description, the degradation process and the mulching paper of the invention are more particularly described in relation to the mulching of lettuces.
However, the paper applies to the mulching of all types of plants, such as strawberry plants, vines, tomatoes, courgettes, aubergines, peppers, cucumbers, shallots, etc.
Several mulching materials have been proposed.
Firstly, black plastic sheeting is known which has the advantage of being strong, despite its low weight per unit area, and thus being weather-resistant. However, such plastic sheeting has a certain number of drawbacks, especially that of not being biodegradable. For obvious environmental reasons, plastic cannot be buried in the soil. Consequently, when the harvesting has been completed and the grower wishes to plough his land, he must completely remove the plastic. The cost of this operation is estimated to be 20% of the total cost of the mulching.
Moreover, since the plastic heats up very quickly when exposed to solar rays, the lettuce leaves close to the ground adhere and remain adhered to the mulching film and therefore can only be removed with removal of this film. It is estimated that the removal of one ton of plastic entails the removal of one ton of plants and earth that have remained attached to the said plastic. Consequently, the plastic is virtually unrecyclable, the cost of washing it being unacceptably high for such an operation.
To solve these various problems, mulching papers have been developed at the same time. Such papers, more particularly described in documents FR-A-2,016,071, are treated with urea-formaldehyde resins so as to increase their wet strength and thus decrease the risk of tearing when used on the ground.
However, despite this treatment, the paper can break due to the effect of the watering phases, which expand the paper, and of the drying phases which retighten the paper.
Moreover, and above all, the treatment of the paper with hydrophobic resins inevitably results in its biodegradability slowing down. It has in fact been found that complete biodegradation of these types of paper is achieved only after 2 years.
In other words, one is faced with the complex problem of using a mulching paper which is weather resistant over a defined period but which at the same time can be degraded in a minimum time after harvesting.
To solve this problem, the Applicant has developed a process for the accelerated degradation of mulching paper whose cellulose fibres are impregnated with a hydrophobic resin giving the said paper a weather-resistant character, in which an enzymatic solution capable of degrading both the resin and the cellulose is sprayed on to the paper.
In other words, the process of the invention consists in depositing over the growing area a paper whose fibres are impregnated with a resin providing it with wet strength, and therefore making it non-tearable, while being compatible with the period of use. Thus with regard to strawberry plants, for example, the paper must be kept in place over the growing area for 9 months, whereas this period is only 6 weeks in the case of lettuces. After harvesting, the paper is degraded by spraying an enzymatic solution, the said solution allowing not only the rate of degradation of the cellulose to be considerably accelerated but also preventing any accumulation of resin in the soil by degradation of the resin. To further accelerate the degradation of the paper, the ground is then ploughed so as to bury the paper in the soil.
According to a first characteristic of the process of the invention, the hydrophobic resin is chosen from the group comprising urea-formaldehyde resins, melamine-formaldehyde resins, polyamide-amine-epichlorohydrin resins, polyethyleneimine resins and starch derivatives, by themselves or as a mixture.
These resins are known to those skilled in the art and are specifically described in document “le point sur . . . ”, No. 11, January 1986 from Centre Technique du Papier de Grenoble [Grenoble Paper Technical Centre].
In one advantageous embodiment, the chosen resins are polyamide-amine-epichlorohydrin resins.
Moreover, in order to degrade not only the resin but also the cellulose, the enzymatic solution comprises enzymes capable of catalyzing the hydrolysis of resin-resin, resin-cellulose and cellulose-cellulose bonds.
In the rest of the description and in the claims, the expression “resin-resin bonds” should be understood to mean the hydrolyzable bonds between monomers of the resin.
Likewise, the expression “resin-cellulose bonds” should be understood to mean the ester bonds linking the resin to the cellulose.
Finally, the expression “cellulose-cellulose bonds” should be understood to mean the glycosidic bonds of the cellulose.
To catalyze the hydrolysis of the ester bonds linking the resin to the cellulose, the enzyme chosen will be an esterase.
Likewise, to catalyze the hydrolysis of the glycosidic bonds of the cellulose, the enzyme will be a cellulase chosen from the group comprising exocellobiohydrolases, endoglucanases and β-glucosidases, alone or as a mixture.
Finally, the choice of enzyme capable of catalyzing the hydrolysis of the bonds between monomers forming the resin will be chosen depending on the nature of the said bonds.
In practice, with regard to polyamide-amine-epichlorohydrin resins, the enzyme will be chosen from the group comprising amidases and aminases.
As already stated, the invention also relates to the mulching paper for implementing the process described above.
Apart from the fact that the mulching paper of the invention must have a composition such that it can be degraded according to the process described above, it must also have a certain number of properties allowing it to be used as mulching material.
Thus, the paper must be resistant to the weather, such as rain and wind, and to extreme temperature conditions, such as cold and hot conditions, and consequently must have excellent mechanical properties.
Consequently, the Applicant was set the objective of obtaining a paper having a bursting strength of between 150 and 250 kPa.
Another characteristic that the paper must have is that of being permeable to water in so far as the spraying water must be able to irrigate the soil and the roots of the plants. However, the pores in the paper must have a volume such that they limit the evaporation of water lying beneath the mulching so as to preserve sufficient moisture in the soil.
To obtain such properties, the Applicant set the objective of obtaining a paper having an air permeability of between 1500 and 3500 cm3 over an area of 10 cm2 under a vacuum of 1 kPa in sixty seconds.
To achieve all these objectives, the mulching paper of the invention is characterized in that it comprises a fibrous composition containing, by weight:
The unbleached kraft paper pulps and their method of manufacture are well known to those skilled in the art. Likewise, the deinked packaging pulps are known as resulting from packaging residues.
According to another characteristic, the mulching paper furthermore contains from 0.5 to 15% resin, advantageously from 7 to 8%, resin by weight with respect to the weight of the paper.
For a resin concentration of less than 0.5% by weight, the paper does not have a sufficiently high wet strength and it tears during spraying or when it rains. For a resin concentration of greater than 15% by weight, a paper having optimized mechanical properties is not obtained, so that the paper becomes economically less advantageous.
Moreover, to avoid the development of microorganisms on the surface of the paper, the paper furthermore contains a fungistatic agent.
In one advantageous embodiment, the fungistatic agent is distributed only over those areas of the paper sheet which are intended to be buried. In this case, the fungistatic agent is deposited at the wet end of the paper machine by spraying it using air-pressurized nozzles.
In addition, in order to increase the extensibility of the paper when the crops are sprayed, while still preventing it from breaking when drying out, the paper is in creped form. This pleating obtained by a creping operation on the paper machine furthermore makes it possible to adapt the paper, on the one hand, to the contour of the ground by accepting the slight curvatures in the latter and, on the other hand, to its dimensional variations due to the action of the successive spraying and drying phases.
The invention also relates to the enzymatic solution for implementing the accelerated mulching paper degradation process described above.
Of course, and as has been already stated, the composition of the said enzymatic solution will vary depending on the resin used and on the nature of the sites at which the said enzymes must act.
However, and in practice, the solution always contains cellulases capable of breaking the cellulose-cellulose bonds and esterases capable of breaking the resin-cellulose bonds.
According to an advantageous embodiment, the enzymatic solution contains, by weight:
In practice, the enzymatic solution is sprayed in an amount of 0.01 to 1 g, advantageously 0.3 to 0.4 g, of pure enzyme per m2.
In another embodiment of the invention, the enzymatic solution may be incorporated directly into the paper, within microcapsules.
Consequently, the mulching paper will be degraded after harvesting, after being buried in the soil, especially by ploughing, that is to say when the walls of the microcapsules containing the enzymatic solution have broken due to the mechanical action.
In other words, the invention also relates to a mulching paper capable of rapidly degrading after being buried in the soil, the cellulose fibres of which are impregnated with a hydrophobic resin giving the said paper a weather-resistant character, characterized in that it furthermore comprises microcapsules filled with an enzymatic solution, the walls of which microcapsules are broken during burying in the soil, thus releasing the enzymes capable of catalyzing both the hydrolysis of the resin and that of the cellulose.
The manufacture of the enzymatic solution microcapsules and their incorporation into the paper constitute known operations within the scope of those skilled in the art and will not be described below any further.
Moreover, and as previously, the enzymatic solution contains enzymes capable of catalyzing the hydrolysis of the resin-resin, resin-cellulose and cellulose-cellulose bonds.
Advantageously, the enzymes are chosen from the group comprising esterases, cellulases, amidases and aminases.
In order for the paper to be sufficiently weather resistant, it comprises from 0.5 to 15%, advantageously from 7 to 8%, by weight of resin with respect to the weight of the paper.
The invention and the advantages which stem therefrom will become more apparent from the following illustrative examples.
a shows, boxed in, the amide bonds which link the monomers of the resin and the hydrolysis of which, during spraying, is catalyzed by enzymes of the amidase type.
b shows, boxed in, the amine bonds which link the monomers of the resin and the hydrolysis of which, during spraying, is catalyzed by enzymes of the aminase type.
Likewise,
Finally,
A mulching paper with the following composition was prepared:
Fibrous Composition:
Colorant:
Additives:
Next, a sheet of paper is formed from the fibrous suspension on a Fourdrinier-type wire-table paper machine, the paper having the mechanical properties given in the table below:
A mulching paper with the following composition was prepared:
Fibrous Composition:
Additives:
The mechanical properties of the paper sheet are given in the table below:
To increase the resistance of the paper to the bacteria and fungi contained in the soil, a fungistatic product (FONGICIDE B-350, sold by Intace S.A.) is sprayed, in an amount of 1200 ppm of active substance, in the water line located on the wire of the paper machine.
The spraying is carried out by means of air-pressurized nozzles and controlled so as to deposit on the surface of the paper protective strips which are more resistant than the untreated areas. The product will diffuse into the bulk of the paper together with the water sucked out during the dewatering step. Consequently, when the paper is placed over the growing area, the treated areas will be buried in the soil, whereas the untreated areas will remain on the surface of the soil.
Using the papers manufactured according to Examples 1 and 2, it was also found that they allowed the variations in soil temperature between night and day to be reduced by approximately 4 to 5° C.
Thus, a temperature measurement taken 5 cm from the surface of the cultivated soil for a plastic mulching and for a mulching as proposed in Examples 1 and 2 gives the following temperature variations:
Such a property of the paper is highly advantageous insofar as the smaller the temperature variations between day and night the greater the growth of the plants.
Various tests were carried out to evaluate the mechanical properties of the paper of the invention.
To do this, trays were filled with compost on which the mulching sheet of the invention was positioned, each of its ends being buried in the earth.
The mulching sheet therefore had a part called the “out-of-the-soil” part and a buried part.
Various parameters, namely the tensile strength and the development of fungi, were evaluated on the out-of-the-soil part.
The tearing strength of the paper level with the surface of the soil, the tensile strength, the degradation and the development of fungi were evaluated on the buried part.
These various parameters were studied under specific conditions, namely a temperature of 28° C. and a moisture-saturated atmosphere having a relative humidity of greater than 95%.
The measurements were carried out every three days. This corresponds in an open-field test to a measurement every nine days. The results are given in the table shown in FIG. 2.
As this table shows, the presence of a fungicide in the composition of the paper prevents any development of fungi over a period of ten growing days, i.e. thirty days in an open field.
Likewise, the tearing strength of the buried part is still satisfactory after thirty growing days, as is the tensile strength.
On the other hand, no degradation of the buried part of the paper was observed, thereby confirming that the resin considerably increases the weather-resistance of the paper.
An enzymatic solution having the following composition by weight was prepared:
The solution obtained is diluted to 1% and then sprayed over the paper and the plant residues after harvesting in an amount of 10 to 100 g/m2. The ground was then ploughed.
All of the mulching paper had degraded in less than 15 days.
The invention and the advantages which stems therefrom are clearly apparent from the above description.
In particular, it will be noted that the paper of the invention provides, because of its composition and especially of the presence of resin, the advantage of giving it weather resistance, while still being able to be degraded very rapidly in about fifteen days after harvesting, either by spraying an enzymatic solution or by the bursting of the microcapsules of the said enzymatic solution contained in the paper after the ground has been ploughed.
Consequently, the grower has clean ground for a very much lower cost insofar as there is no longer a question of removing the mulching after harvesting. On the contrary, reincorporation into the soil of the plant waste constitutes an excellent green fertilizer.
| Number | Date | Country | Kind |
|---|---|---|---|
| 99 12600 | Oct 1999 | FR | national |
This application is a divisional of U.S. patent application Ser. No. 09/680,372, filed Oct. 5, 2000, now U.S. Pat. No. 6,578,315, which claims priority from French Patent Application No. 99.12600, filed on Oct. 5, 1999, the entire disclosures of which are incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3950282 | Gilbert et al. | Apr 1976 | A |
| 4944734 | Wallach | Jul 1990 | A |
| 4980023 | Salkinoja-Salonen | Dec 1990 | A |
| 5133909 | Suominen | Jul 1992 | A |
| 5262208 | Krapivina et al. | Nov 1993 | A |
| 5350783 | Reich | Sep 1994 | A |
| 5391423 | Wnuk et al. | Feb 1995 | A |
| 5478386 | Itoh et al. | Dec 1995 | A |
| 5545547 | Kolattukudy et al. | Aug 1996 | A |
| 5672434 | Dalebroux et al. | Sep 1997 | A |
| 5720803 | Itoh et al. | Feb 1998 | A |
| 5762678 | Hiles | Jun 1998 | A |
| 5866269 | Dalebroux et al. | Feb 1999 | A |
| 5885602 | Levy | Mar 1999 | A |
| 5936045 | Warzelhan et al. | Aug 1999 | A |
| 6071711 | Koch | Jun 2000 | A |
| 6255451 | Koch et al. | Jul 2001 | B1 |
| 6312823 | El-Afandi et al. | Nov 2001 | B1 |
| 6312826 | Shogren | Nov 2001 | B1 |
| 6578315 | Dussaud et al. | Jun 2003 | B1 |
| Number | Date | Country |
|---|---|---|
| 2125815 | Sep 1995 | CA |
| 1124085 | Jun 1996 | CN |
| 1217351 | May 1999 | CN |
| 0421413 | Apr 1991 | EP |
| 1664938 | Jul 1991 | SU |
| WO 0125536 | Apr 2001 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20030192236 A1 | Oct 2003 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09680372 | Oct 2000 | US |
| Child | 10426197 | US |