Claims
- 1. A raw batch composition comprising a mixture of:
- A. an aggregate material;
- B. a hardenable phenolic resole resin having a pH of about 5 to 9, a resin solids content of about 50% to 90% by weight of said resin, and a viscosity of about 100 to 4,000 cps at 25.degree. C.;
- C. from about 5% to 40% by weight of the resin of a magnesium hardening agent selected from the group consisting of magnesium hydroxide and lightburned magnesium oxide, said magnesium oxide having a surface area of at least 10 square meters per gram;
- D. an accelerator in an amount sufficient to accelerate the hardening of said mixture, said accelerator selected from the group consisting of:
- (a) a 2,4-di(dialkylaminomethyl)phenol, a 2,6-di(dialkylaminomethyl)phenol, or a 2,4,6-tris(dialkylaminomethyl)phenol wherein each alkyl group has from 1 to 3 carbon atoms;
- (b) a 1,3,5-tri(lower alkyl)hexahydro-1,3,5-triazine wherein each alkyl group has from 1 to 3 carbon atoms;
- (c) 1,4-diazabicyclo[2.2.2]octane; and
- (d) a compound of the formula: ##STR5## wherein: each of R.sup.1 and R.sup.2 is a member selected from the group consisting of alkyl having 1 to 3 carbon atoms, and R.sup.1 and R.sup.2 when taken together with the nitrogen to which they are attached, represent a member selected from the group consisting of piperidino, piperazino, morpholino, thiomorpholino, and pyrrolidino;
- X is a member selected from the group consisting of (--CH.sub.2 --).sub.n wherein n is an integer of 1 to 6, --CH.dbd.CH--CH.sub.2 --, --CH.sub.2 --CH.dbd.CH--CH.sub.2 --, ##STR6## and each of R.sup.3 and R.sup.4 is a member selected from the group consisting of hydrogen, alkyl of 1 to 3 carbon atoms, and R.sup.3 and R.sup.4 when taken together with the nitrogen to which they are attached represent a member selected from the group consisting of piperazino, morpholino, thiomorpholino, piperidino, and pyrrolidino.
- 2. The composition of claim 1 wherein: the pH of the resin is from about 5 to 8.5; the quantity of resin is from about 3% to 20% by weight based on the aggregate; and the mixture includes an ester functional hardening agent in an amount sufficient to increase the rate of hardening of the mixture.
- 3. A composition of claim 2 which has been hardened at ambient temperature.
- 4. The composition of claim 2 wherein: the magnesium hardening agent is magnesium oxide having a surface area of about 10 to 200 square meters per gram; and the mixture includes fibers in an amount sufficient to improve the flexural strength of the composition on hardening.
- 5. The composition of claim 4 wherein: the aggregate is sand; and the composition includes from about 0.1% to 1.5% based on the weight of resin of a silane adhesion promoter and from about 0.005% to 0.1% an air detraining agent.
- 6. A thermally cured composition of claim 2.
- 7. The composition of claim 2 wherein the aggregate is a member selected from the group consisting of: refractory grade magnesia; alumina; zirconia; silica; silicon carbide; silicon nitride; boron nitride; bauxite; quartz; corumdum; zircon sand; olivine sand; and mixtures thereof.
- 8. The composition of claim 2 wherein the phenolic resole resin is the condensation product of phenol and formaldehyde.
- 9. The composition of claim 7 which further includes from about 5% to 25% of graphite based on the weight of the aggregate and from about 1% to 5% by weight of the aggregate of a metal powder selected from the group consisting of aluminum, magnesium, and silicon.
- 10. A composition of claim 9 which has been hardened at ambient temperature.
- 11. A composition of claim 9 which has been thermally cured.
- 12. The composition of claim 1 wherein the magnesium hardening agent is lightburned magnesium oxide.
- 13. The composition of claim 12 wherein X in the formula ##STR7## is alkylene having from 1 to 6 carbon atoms.
- 14. The composition of claim 12 wherein the accelerator is a 2,4,6-tris(dialkylaminomethyl)phenol having from 1 to 3 carbon atoms in each alkyl group.
- 15. The composition of claim 12 wherein the accelerator is 1,3,5-tri(lower alkyl) hexahydro-1,3,5-triazine wherein each alkyl group has from 1 to 3 carbon atoms.
- 16. The composition of claim 12 wherein the accelerator is 1,4-diazabicyclo[2.2.2]octane.
- 17. A raw batch composition comprising a mixture of:
- A. an aggregate material;
- B. a hardenable phenolic resole resin having a pH of about 4.5 to 9.5, a solids content of about 50% to 90% by weight of the resin, and a viscosity of about 100 to 4,000 cps at 25.degree. C.;
- C. from about 5% to 50% by weight of the resin of lightburned magnesium oxide having a surface area of at least about 10 square meters per gram; and
- D. from about 0.5% to 5% by weight of the resin of an accelerator compound which has a water solubility of at least 1% by weight at 25.degree. C. and provides to the mixture an accelerator selected from the group consisting of:
- (a) a 2,4-di(dialkylamonomethyl)phenol, a 2,6-di(dialkylaminomethyl)phenol, or a 2,4,6-tris(dialkylaminomethyl)phenol wherein each alkyl group has from 1 to 3 carbon atoms;
- (b) a 1,3,5-tri(lower alkyl)hexahydro-1,3,5-triazine wherein each alkyl group has from 1 to 3 carbon atoms;
- (c) 1,4-diazabicyclo[2.2.2]octane; and
- (d) a compound of the formula: ##STR8## each of R.sup.1 and R.sup.2 is a member selected from the group consisting of alkyl having 1 to 3 carbon atoms, and R.sup.1 and R.sup.2 when taken together with the nitrogen to which they are attached, represent a member selected from the group consisting of piperidino, piperazino, morpholino, thiomorpholino, and pyrrolidino;
- X is a member selected from the group consisting of (--CH.sub.2 --).sub.n wherein n is an integer of 1 to 6, --CH.dbd.CH--CH.sub.2 --, --CH.sub.2 --CH.dbd.CH--CH.sub.2 --, ##STR9## each of R.sup.3 and R.sup.4 is a member selected from the group consisting of hydrogen, alkyl of 1 to 3 carbon atoms, and R.sup.3 and R.sup.4 when taken together with the nitrogen to which they are attached represent a member selected from the group consisting of piperazino, morpholino, thiomorpholino, piperidino, and pyrrolidino.
- 18. The composition of claim 17 wherein the accelerator is 2,4,6-tris(dimethylaminomethyl)phenol.
- 19. The composition of claim 17 wherein: the pH of the resin is from about 5 to 8.5; and the mixture includes an ester functional hardening agent in an amount sufficient to increase the rate of hardening of the mixture, said ester functional hardening agent selected from the group consisting of a lactone, a cyclic organic carbonate, a carboxylic acid ester, and mixtures thereof.
- 20. The composition of claim 19 wherein the ester is a lactone.
Parent Case Info
This application is a divisional of my application Ser. No. 07/995,968 which was filed on Dec. 23, 1992, now Pat. No. 5,223,554 which in turn is a divisional of my application Ser. No. 07/943,065 which was filed on Sep. 10, 1992, now Pat. No. 5,214,079 which in turn is a divisional of my application Ser. No. 07/616,879 which was filed on Nov. 21, 1990, now U.S. Pat. No. 5,182,346 of Jan. 26, 1993, which in turn is a continuation-in-part of my patent application Ser. No. 07/562,206 which was filed on Aug. 2, 1990, now U.S. Pat. No. 5,096,983 of Mar. 17, 1992.
US Referenced Citations (18)
Foreign Referenced Citations (6)
Number |
Date |
Country |
0094165 |
Nov 1983 |
EPX |
0202004 |
Nov 1986 |
EPX |
0243172 |
Oct 1987 |
EPX |
60-90251 |
May 1985 |
JPX |
8901526 |
Jun 1990 |
WOX |
1316994 |
Jun 1987 |
SUX |
Non-Patent Literature Citations (2)
Entry |
Roczniak, Kryatyna "Selected Crosslinking Catalytic Polycondensation Compounds" Polimery, 29(3); 95-99 Mar. 1984. |
Rozniak, Kryatyna "Selected Crosslinking Catalytic Polycondensation Compounds" Zesz. Nauk-Wyzsza Szk. Inz. Radomiu Materialozn. Chem., vol. 8, p. 283, 1985. |
Divisions (3)
|
Number |
Date |
Country |
Parent |
995968 |
Dec 1992 |
|
Parent |
943065 |
Sep 1992 |
|
Parent |
616879 |
Nov 1990 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
562206 |
Aug 1990 |
|