Acidic catalyst described herein may be used in hydrocarbon reactions. Certain acidic catalyst disclosed herein demonstrate super acidity and may be capable of isomerizing alkanes at room temperature. Certain acidic catalyst disclosed herein may be useful in the oligomerization of methane.
Wet impregnation techniques may be used with various solvents to prepare acid catalysts. For example, supports may be impregnated by the dissolved aluminum halide precursors represented by the aluminum species of Table 1 in solvents of Table 1 at room temperature with reflux producing the initial catalyst species shown in Table 1. The resulting catalysts may then be filtered and dried under vacuum yielding solid acid catalysts represented by initial catalyst species Ai-Pi.
Vapor phase grafting techniques may also be used to prepare acid catalysts. For example, supports and aluminum halide, separated by quartz wool, may be heated up to 300° C. inside an air free vessel or under an inert atmosphere, allowing aluminum halide vapor to react with the surface species of support producing the initial catalyst species shown in Table 1. The resulting catalysts may then be separated from aluminum halide under vacuum yielding solid acid catalysts represented by initial catalyst species Ai-Pi. In one example, not shown in Table 1, AlBr3 was grafted onto ZSM-5 according to the method described above to produce an AlBr3 modified ZSM-5 initial catalyst.
The supports used are not limited to the supports described in Table 1. Other supports consistent with the present disclosure may include zeolites and other similar supports. Such supports may be microporous supports or mesoporous supports. Supports may be silica-based or they may be alumina based. Inorganic supports may be used particularly when elevated temperatures are contemplated for later uses of resulting catalyst.
Initial catalyst species Ai-Pi may then be treated with HBr to form acid sites analogous to [H+/AlBr4−] and [H+/AlCl3Br−]. Examples of HBr treatment that may be used to further acidify initial catalyst species Ai-Pi include contacting initial catalyst species Ai-Pi with a flow of between 1% and 10% HBr gas in an inert gas such as helium or argon for a duration between one and three hours at room temperature. HBr concentrations may more broadly range between 0.1% and 20% HBr. Each of the HBr treatments occur at room temperature but may be performed at higher temperatures potentially enhancing the acidity of the catalyst. For example, the HBr treatment may occur between 50° C. and 200° C. The product of the HBr treatment of initial catalyst species Ai-Pi is the augmented acid catalyst Aa-Pa. As an example, the silica gel based initial catalyst species Gi may react with HBr to yield Ga as follows:
Gi+HBr→Ga
That acidification of the initial catalyst to yield the augmented acid catalyst may be generally characterized by the reaction depicted in
The reactor set up of
Augmented acid catalysts may take the form of catalysts having reaction sites according to one or more of the following general formulas:
In general formulas 1-4, X may be Br or Cl and M may be either Si or Al. Further, M would be molecularly bound to a support structure such as those described herein. General formula 5 is a generalization of various forms of the described reaction sites.
MxOyAlBrzX]−H+ (5)
In general formula 5, x is selected from 1 and 2; y is selected from 1 and 2; z is selected from 1 and 2; X is selected from Br and Cl; and M is selected from Al and Si. Further, in general formula 5, one or more of M, O and Al would have a molecular bond with the metal oxide support structure.
Augmented acid catalysts with metal oxide support structures may take the form of catalysts having acidic reaction sites according to one or more of the following general formulas:
In the above general formulas 6-10, M1, M2, M3 and M4, when present, are selected from a first group in which M1 is Al, M2 is Al, M3 is Al and M4 is Al and a second group in which M1 is Si, M2 is selected from Si and Al, M3 is Si and M4 is Si. In those examples, the catalyst is selected from an aluminum oxide based catalyst and a silicon oxide based catalyst. Also, the AlCl3 may be the aluminum halide species used to create the augmented acid catalyst. Also, the open-ended bonds depicted in the general formulas connect the acidic reaction site to the metal oxide support structure. One or more of the compositions of general formulas 6-10 may be produced by the wet impregnation techniques of Example Set 1A combined with the Acidification of Example Set 2. One or more of the compositions of general formulas 6-10 are produced by the vapor phase grafting Example Set 1B combined with the Acidification of Example Set 2.
In a subset of the examples associated with general formulas 6-10, M1 may be Al, M2 may be Al, M3 may be Al and M4, when present, may be Al. Such examples may be present when Alumina is the substrate.
In a subset of the examples associated with general formulas 6-10, M1 may be Si, M2 may be Al, M3 may be Si and M4, when present, may be Si. Such examples may be present when one of MCM-41, SBA-15 or ZSM-5 is the substrate.
In a subset of the examples associated with general formulas 6-10, M1 may be Si, M2 may be Si, M3 may be Si and M4, when present, may be Si. Such examples may be present when one of MCM-41, SBA-15 or silica gel is the substrate.
Certain augmented acid catalyst may be characterized as superacids based on the ability of those catalyst to isomerize n-butane into isobutane. As that term is used herein “superacid” designates compounds and catalysts capable of n-butane isomerization at room temperature. Such testing may be conducted in a continuous flow reactor in which n-butane flows over a bed of the subject catalyst at room temperature. In such testing, the augmented acid catalyst Ga, Ka and Oa demonstrated super acidity and Ca did not demonstrate super acidity.
Augmented acid catalyst Aa-Pa along with other similar catalysts may be subjected to methane oligomerization methods or test such as presented in
Augmented acid catalyst Ca, Ga, Ka and Oa, each prepared using the wet impregnation technique, have been tested for methane oligomerization and did not demonstrate measured methane oligomerization in preliminary tests. Augmented acid catalyst Aa, Ba, Da, Ea, Fa, Ha, Ia, Ja, La Ma, Na and Pa are each individually significant candidates for successful methane oligomerization and the prophetic methods of contacting the methane with the augmented acid catalyst Aa, Ba, Da, Ea, Fa, Ha, Ia, Ja, La, Ma, Na and Pa are directly intended as methods of the present disclosure. Oligomerization may have been masked by trace organic compounds in reaction tests using catalyst prepared with wet impregnation techniques and for that reason, augmented acid catalyst Ca, Ga, Ka and Oa may still be candidates for oligomerization. Methane oligomerization, as described herein may be generally characterized as the conversion of methane to higher molecular weight hydrocarbons and may proceed according to the following generalized reaction in which n is greater than or equal to 2:
nCH4→CnHm+xH2
Methane gas was co-fed with HBr into Tubular reactor 30, as described in
In four separate attempted oligomerization reactions, using the reaction setup of
Accordingly, oligomerization may occur using an initial catalyst with or without the co-feeding of HBr and oligomerization may occur using an augmented catalyst with or without the co-feeding of HBr.
As that phrase is used herein, a “mesoporous catalyst” is a catalyst having an average pore diameter between 2 and 50 nm. As that phrase is used herein, a “microporous catalyst” is a catalyst having an average pore diameter that is at most 2 nm. As that phrase is used herein, an “aluminum oxide based catalyst” is a metal oxide catalyst in which aluminum is the elemental metal having the greatest individual weight percent among all elemental metals present in the metal oxide catalyst. Alumina, for example would be an aluminum oxide based catalyst. As that phrase is used herein, a “silicon oxide based catalyst” is a metal oxide catalyst in which silicon is the elemental metal having the greatest individual weight percent among all elemental metals present in the metal oxide catalyst. Silica Gel, MCM-41 and SBA-15 would each be considered silicon oxide based catalyst as that phrase is used herein. The phrases aluminum oxide based catalyst and silicon oxide based catalyst as used herein are intended to encompass augmented acid catalyst Aa-Pa. Silica-alumina mixed oxide catalysts may be characterized as either aluminum oxide based catalyst or silicon oxide based catalyst as those phrases are used herein based on the weight of elemental metals present in the silica-alumina mixed oxide catalyst. For example, a zeolite according to the formula Na2Al2Si3O10.2H2O would be a silicon oxide based catalyst. As used herein Si is treated as a metal for the purposes of describing metal oxide catalyst, silicon oxide based catalyst, aluminum oxide based catalyst and the like.
Compositions of matter described herein may, for example, comprise a catalyst comprising a metal oxide support structure and an acidic reaction site such that the acidic reaction site has a composition according to a general formula,
MxOyAlBrzX]−H+;
in which x is 1 or 2; y is 1 or 2; z is 1 or 2; X is Br or Cl; M is Al or Si; one or more of M, O and Al has a molecular bond with the metal oxide support structure and the catalyst is an aluminum oxide based catalyst or a silicon oxide based catalyst. In a related example, the catalyst may be a mesoporous catalyst. In a related example, the catalyst may be a microporous catalyst. In a related example, the catalyst may be an aluminum oxide based catalyst. In a further related example, the catalyst may be a silicon oxide based catalyst. In a further related example, X may be Br. In a further related example, X may be Cl. In a further related example, M may be Al. In a still further related example, M may be Si. In a still further related example, M may be Si and X may be Br. In a still further related example, M may be Si and X may be Cl.
Compositions of matter described herein may, for example, comprise a catalyst comprising a metal oxide support structure and an acidic reaction site such that the acidic reaction site has a composition according to a general formula,
in which X is Br or Cl; M is Al or Si; one or more of M and O has a molecular bond with the metal oxide support structure and the catalyst is an aluminum oxide based catalyst or a silicon oxide based catalyst. In a related example, the catalyst may be a mesoporous catalyst. In a related example, the catalyst may be a microporous catalyst. In a related example, the catalyst may be an aluminum oxide based catalyst. In a further related example, the catalyst may be a silicon oxide based catalyst. In a further related example, X may be Br. In a further related example, X may be Cl. In a further related example, M may be Al. In a still further related example, M may be Si. In a still further related example, M may be Si and X may be Br. In a still further related example, M may be Si and X may be Cl.
Compositions of matter described herein may, for example, comprise a catalyst comprising a metal oxide support structure and an acidic reaction site such that the acidic reaction site has a composition according to a general formula,
in which X is Br or Cl; M is Al or Si; one or more of M and O has a molecular bond with the metal oxide support structure and the catalyst is an aluminum oxide based catalyst or a silicon oxide based catalyst. In a related example, the catalyst may be a mesoporous catalyst. In a related example, the catalyst may be a microporous catalyst. In a related example, the catalyst may be an aluminum oxide based catalyst. In a further related example, the catalyst may be a silicon oxide based catalyst. In a further related example, X may be Br. In a further related example, X may be Cl. In a further related example, M may be Al. In a still further related example, M may be Si. In a still further related example, M may be Si and X may be Br. In a still further related example, M may be Si and X may be Cl.
Compositions of matter described herein may, for example, comprise a catalyst comprising a metal oxide support structure and an acidic reaction site such that the acidic reaction site has a composition selected from the general formulas:
M1, M2, M3 and M4, when present, may be selected from: a first group in which M1 is Al, M2 is Al, M3 is Al and M4 is Al, a second group in which M1 is Si, M2 is Si, M3 is Si and M4 is Si and a third group in which M1 is Si, M2 is Al, M3 is Si and M4 is Si; the catalyst may be selected from an aluminum oxide based catalyst and a silicon oxide based catalyst and such that the open-ended bonds depicted in the general formulas connect the acidic reaction site to the metal oxide support structure.
As that phrase is used herein, a “light hydrocarbon composition,” is a composition comprising a one to four carbon atom hydrocarbon. Thus, natural gas would be an example of a light hydrocarbon composition.
Methods of reacting hydrocarbons described herein may comprise providing a light hydrocarbon composition having a first constituent molecule and a second constituent molecule; providing a catalyst; bringing the catalyst in contact with the light hydrocarbon composition and conducting a chemical reaction in which the first constituent molecule reacts with the second constituent molecule to produce a product molecule having a higher molecular weight than the first constituent molecule; such that the catalyst is selected from an aluminum oxide based catalyst and a silicon oxide based catalyst and such that the catalyst is an acidic catalyst. In a related example, the catalyst may be a mesoporous catalyst. In a related example, the catalyst may be a microporous catalyst. In a related example, the catalyst may be an aluminum oxide based catalyst. In a related example, the catalyst may be a silicon oxide based catalyst. In a related example, the conducting of the chemical reaction may be done in the presence of HBr. In a related example, the first constituent molecule is methane and the second constituent molecule is methane.
The above-described embodiments have a number of independently useful individual features that have particular utility when used in combination with one another including combinations of features from embodiments described separately. There are, of course, other alternate embodiments which are obvious from the foregoing descriptions, which are intended to be included within the scope of the present application.
This application is a continuation of prior application Ser. No. 15/867,920 filed Jan. 11, 2018 and entitled Acidic Catalyst which claims the benefit of U.S. Provisional Application No. 62/488,466 filed on Apr. 21, 2017 and entitled Acidic Catalyst.
his invention was made with government support under grant award number CBET-1644895 awarded by the National Science Foundation. The government has certain rights in the invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2519034 | Elmore | Aug 1950 | A |
| 2678957 | Fontana | May 1954 | A |
| 3182013 | Myers | May 1965 | A |
| 3914383 | Kirsch et al. | Oct 1975 | A |
| 5294578 | Ho | Mar 1994 | A |
| 5451704 | Ho | Sep 1995 | A |
| 20020183465 | Babcock | Dec 2002 | A1 |
| 20180304241 | Spivey | Oct 2018 | A1 |
| Number | Date | Country |
|---|---|---|
| 10 4447846 | Mar 2015 | CN |
| Entry |
|---|
| Vasireddy, Sivakumar Direct conversion of methane to higher hydrocarbons using AlBr3—HBr superacid catalyst, ChemComm, Nov. 17, 2010, http://pubs.rsc.org. |
| Dissertation by Wu, “Acidity and Catalytic Activity of Zeolite Catalysts Bound With Silica and Alumina”, Texas A&M University, Dec. 2003, Abstract. (Year: 2003). |
| Number | Date | Country | |
|---|---|---|---|
| 20190262813 A1 | Aug 2019 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62488466 | Apr 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15867920 | Jan 2018 | US |
| Child | 16403172 | US |