Claims
- 1. A process for producing an acrylic polymer, comprising:
- providing a monomer component that contains 51 to 100 percent by weight of an acrylic monomer having a CH.sub.2 .dbd.CHCO-- structure;
- providing a sulfur compound in proportion of 0.001 to 20 parts by weight per 100 parts by weight of said monomer component, wherein said sulfur compound is at least one member selected from the group consisting of a mercaptan, a disulfide compound, a thiuram compound and a trisulfide compound;
- mixing said monomer component and said sulfur compound to obtain a mixture; and
- heating the mixture, in the presence of an inactive gas and in the presence of a polymerization initiator in proportion by weight of one-third or less on the weight of the sulfur compound, to a temperature in the range of from 100.degree. C. to 150.degree. C. that results in a bulk polymerization reaction of said monomer component, and maintaining said temperature between 100.degree. C. to 150.degree. C. until the bulk polymerization reaction has been completed.
- 2. The process as claimed in claim 1, wherein the acrylic polymer obtained by the bulk polymerization reaction contains an acrylic monomer unit as a main component in said acrylic polymer and has a number-average molecular weight in a range of from 1,000 to 1,000,000, a glass transition temperature of -80.degree. C. or higher and a molecular weight distribution (Mw/Mn) of 5 or less.
- 3. The process as claimed in claim 2, wherein the acrylic polymer contains the acrylic monomer unit in proportion of from 60 to 100% by weight and a crosslinkable functional group in proportion of from 0.01 to 1.4 mmol/g in said acrylic polymer and has the number-average molecular weight in a range of from 200,000 to 1,000,000, the glass transition temperature in a range of from -80.degree. to 0.degree. C. and the molecular weight distribution (Mw/Mn) of 3 or less.
- 4. The process as claimed in claim 2, wherein the acrylic polymer contains the acrylic monomer unit in proportion of from 60 to 100% by weight and a crosslinkable functional group in proportion of from 0.005 to 1.4 mmol/g in said acrylic polymer and has the number-average molecular weight in a range of from 10,000 to 500,000 and the glass transition temperature in a range of from -80.degree. to -30.degree. C.
- 5. The process as claimed in claim 2, wherein the acrylic polymer contains the acrylic monomer unit in proportion of from 51 to 100% by weight in said acrylic polymer and has an acid value of 65 mg/g or higher, the number-average molecular weight in a range of from 5,000 to 200,000, the glass transition temperature of 0.degree. C. or higher and the molecular weight distribution (Mw/Mn) of 3 or less.
- 6. The process as claimed in claim 2, wherein the acrylic polymer contains the acrylic monomer unit in proportion of from 60 to 100% by weight in said acrylic polymer and has an acid value of 65 mg/g or higher, the number-average molecular weight in a range of from 10,000 to 500,000, the glass transition temperature of 0.degree. C. or higher and the molecular weight distribution (Mw/Mn) of 4 or less.
- 7. The process as claimed in claim 2, wherein the acrylic polymer contains the acrylic monomer unit in proportion of from 60 to 100% by weight in said acrylic polymer and has an acid value of 65 mg/g or higher, the number-average molecular weight in a range of from 5,000 to 200,000, the glass transition temperature of 70.degree. C. or higher and the molecular weight distribution (Mw/Mn) of 4 or less.
- 8. The process as claimed in claim 2, wherein the acrylic polymer contains the acrylic monomer unit in proportion of from 51 to 100% by weight in said acrylic polymer and has an acid value of 65 mg/g or higher, the number-average molecular weight in a range of from 1,000 to 50,000, the glass transition temperature of 30.degree. C. or higher and the molecular weight distribution (Mw/Mn) of 3 or less.
- 9. The process as claimed in claim 1, wherein the step of heating the mixture is carried out in the absence of said polymerization initiator.
- 10. The process as claimed in claim 1, wherein said sulfur compound is a mercaptan.
- 11. The process as claimed in claim 10, wherein said mixture contains said mercaptan in proportion of from 0.001 to 1.0 part by weight per 100 parts by weight of said monomer component.
- 12. The process as claimed in claim 1, wherein said acrylic monomer is at least one member selected from the group consisting of acrylic acid, salts of acrylic acid and acrylic acid esters.
- 13. The process as claimed in any one of claims 1 and 9-12, wherein said monomer component contains either one or both of acrylic acid and methacrylic acid in totality of from 10 to 100 percent by weight.
- 14. The process as claimed in any one of claims 1 and 9-12, wherein said monomer component contains a crosslinkable monomer having a crosslinkable functional group and the content of said crosslinkable monomer is in a range of from 0.05 to 10 percent by weight in said monomer component.
- 15. The process as claimed in claim 1, wherein said bulk polymerization reaction is continuously carried out by preliminarily polymerizing said monomer component in a tank type reaction vessel and then passing the obtained, preliminarily polymerized product through a piston flow type reaction vessel.
- 16. The process as claimed in claim 1, wherein said monomer component contains 60 to 100 percent by weight of said acrylic monomer.
- 17. A process for producing an acrylic polymer which comprises the steps of preparing a mixture containing a monomer component containing 51 to 100% by weight of an acrylic monomer having a CH.sub.2 .dbd.CHCO-- structure, 0.001 to 20 parts by weight of at least one sulfur compound, selected from the group consisting of mercaptans, disulfides, thiurams and trisulfides, per 100 parts by weight of the monomer component; and heating the mixture to a temperature in the range of from 100.degree. C. to 150.degree. C., in the absence of a polymerization initiator and in the presence of an inactive gas, to bulk polymerize the monomer component, wherein the process does not comprise a step of adding a non-polymerizable organic solvent to a mixture to be polymerized and said temperature of from 100.degree. C. to 150.degree. C. is maintained until the bulk polymerization has been completed.
- 18. The process as claimed in claim 17, wherein the monomer component contains 60 to 100% by weight of the acrylic monomer.
- 19. The process as claimed in claim 17, wherein the sulfur compound is a mercaptan.
- 20. The process as claimed in claim 19, wherein the mixture contains from 0.001 to 1.0 part by weight of the mercaptan per 100 parts by weight of the monomer component.
- 21. The process as claimed in claim 17, wherein the acrylic monomer is at least one member selected from the group consisting of acrylic acid, salts of acrylic acid and esters of acrylic acid.
- 22. The process as claimed in claim 17, wherein the monomer component contains from 0.05 to 10 percent by weight of a monomer having a crosslinkable functional group.
- 23. The process as claimed in claim 17, wherein the bulk polymerization reaction is continuously carried out by preliminarily polymerizing the mixture of the monomer component and the sulfur compound in a tank type reaction vessel and then passing the preliminarily polymerized product through a piston flow type reaction vessel.
- 24. A process for producing an acrylic polymer which comprises the steps of preparing a mixture containing a monomer component containing 51 to 100% by weight of an acrylic monomer having a CH.sub.2 .dbd.CHCO-- structure, 0.001 to 20 parts by weight of at least one sulfur compound, selected from the group consisting of mercaptans, disulfides, thiurams and trisulfides, per 100 parts by weight of the monomer component, and up to 1/3 by weight of a polymerization initiator based on the weight of the sulfur compound; and heating the mixture to a temperature in the range of from 100.degree. C. to 150.degree. C., in the presence of an inactive gas, to bulk polymerize the monomer component, wherein the process does not comprise a step of adding a non-polymerizable organic solvent to a mixture to be polymerized and said temperature of from 100.degree. C. to 150.degree. C., is maintained until the bulk polymerization has been completed.
- 25. The process as claimed in claim 24, wherein the monomer component contains 60 to 100% by weight of the acrylic monomer.
- 26. The process as claimed in claim 24, wherein the sulfur compound is a mercaptan.
- 27. The process as claimed in claim 26, wherein the mixture contains from 0.001 to 1.0 part by weight of the mercaptan per 100 parts by weight of the monomer component.
- 28. The process as claimed in claim 24, wherein the acrylic monomer is at least one member selected from the group consisting of acrylic acid, salts of acrylic acid and esters of acrylic acid.
- 29. The process in claim 24, wherein the monomer component contains from 0.05 to 10% by weight of a monomer having a crosslinkable functional group.
- 30. The process as claimed in claim 24, wherein the bulk polymerization reaction is continuously carried out by preliminarily polymerizing the mixture of the monomer component and the sulfur compound in a tank type reaction vessel and then passing the preliminarily polymerized product through a piston flow type reaction vessel.
- 31. The process as claimed in claim 17, wherein the mixture is heated to about 120.degree. C. and a polymerization intermediate is continuously removed, the bulk polymerization of said removed polymerization intermediate being continued at a temperature of about 110.degree. C.
- 32. The process as claimed in claim 24, wherein the mixture is heated to about 120.degree. C. and a polymerization intermediate is continuously removed, the bulk polymerization of said removed polymerization intermediate being continued at a temperature of about 110.degree. C.
- 33. The process as claimed in claim 1, wherein the temperature of said bulk polymerization reaction is maintained constant.
- 34. The process as claimed in claim 17, wherein the temperature of said bulk polymerization reaction is maintained constant.
- 35. The process as claimed in claim 24, wherein the temperature of said bulk polymerization reaction is maintained constant.
Priority Claims (4)
Number |
Date |
Country |
Kind |
4-183997 |
Jul 1992 |
JPX |
|
4-185519 |
Jul 1992 |
JPX |
|
4-204129 |
Jul 1992 |
JPX |
|
5-094404 |
Apr 1993 |
JPX |
|
Parent Case Info
This application is a continuation of application Ser. No. 08/177,796 filed Jan. 5, 1994, now abandoned which is a divisional of application Ser. No. 08/086,909 filed Jul. 7, 1993, now abandoned.
US Referenced Citations (6)
Foreign Referenced Citations (9)
Number |
Date |
Country |
2145498 |
Feb 1973 |
FRX |
55401 |
Jul 1971 |
JPX |
59-48121 |
Mar 1984 |
JPX |
60-219204 |
Nov 1985 |
JPX |
61-272206 |
Dec 1986 |
JPX |
62-41523 |
Sep 1987 |
JPX |
63-210113 |
Aug 1988 |
JPX |
2-55448 |
Nov 1990 |
JPX |
845672 |
Aug 1960 |
GBX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
86909 |
Jul 1993 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
177796 |
Jan 1994 |
|