Patent Application
20230056141
The present invention relates to an acrylic rubber, a rubber composition and a crosslinked product thereof, a rubber hose, and a seal member.
Acrylic rubbers and crosslinked products thereof are excellent in physical properties such as heat resistance, oil resistance, and mechanical properties, and thus are used, for example, as materials for hoses, sealing members, and the like in engine rooms of automobiles. For example, Patent Document 1 discloses an acrylic rubber composition obtained by copolymerizing 100 parts b mass of a (meth)alkyl acrylate, 1 to 10 parts by mass of vinyl acetate, and 1 to 3 parts by mass of a crosslinking monomer, as an acrylic rubber composition excellent in heat resistance, particularly elongation at break after heat aging and elongation residual ratio without impairing, normal physical properties when formed into a crosslinked product.
In recent years, acrylic libbers have been required to have properties such as water resistance and copper damage resistance, which have not been considered so far, in addition to the above-described heat resistance and the like. That is, it is desirable that the acrylic rubber has a small volume change when contacting with water (excellent water resistance), and it is desirable that the acrylic rubber has a small change in characteristics (for example, elongation) due to copper when used together with a member fin-mod of copper (excel lent copper damage resistance).
An object of one aspect of the present invention is to provide an acrylic rubber capable of achieving both water resistance and copper damage resistance.
The present inventors have found that the content of the polyvinyl alcohol in the acrylic rubber affects water resistance and copper damage resistance of the acrylic rubber. That is, it has been found that even if the monomer composition of the acrylic rubber is the same, the copper damage resistance of the acrylic rubber is improved when the acrylic rubber contains a certain amount of the polyvinyl alcohol, whereas the water resistance is lowered when the content of the polyvinyl alcohol in the acrylic rubber is too large. Therefore, in an acrylic rubber having the same monomer composition, it is important to set the content of the polyvinyl alcohol in the acrylic rubber within the specific range in order to achieve both water resistance and copper damage resistance of the acrylic rubber (not to excessively deteriorate either one of them).
An aspect of the present invention is an acrylic rubber containing an alkyl acrylate, an alkyl methacrylate and ethylene as monomer units, wherein a content of a polyvinyl alcohol in the acrylic rubber is 0.5 to 2% by mass.
The all acrylate may contain: at least one selected from the group consisting of alkyl acrylates having an alkyl group having 1 to 3 carbon atoms; and at least one selected from the group consisting of alkyl acrylates having an alkyl group having 4 to 8 carbon atoms. The alkyl acrylate may contain ethyl acrylate and butyl acrylate. The alkyl methacrylate may contain an alkyl acrylate having an alkyl group having 1 to 4 carbon atoms.
A content of the alkyl acrylate may be 60 to 95% by mass based on a total amount of the monomer units. A content of the alkyl methacrylate may be 3 to 30% by mass based on a total amount of the monomer units. A content of the ethylene may be 0.5 to 4% by mass based on a total amount of the monomer units.
The acrylic rubber may further comprises a crosslinking monomer as the monomer units. The crosslinking monomer may be a crosslinking monomer having an epoxy group. The crosslinking monomer may be a crosslinking monomer having a carboxyl group. A content of the crosslinking monomer may be 0.5 to 10% by mass based on a total amount of the monomer units.
Another aspect of the present invention is a rubber composition containing the acrylic rubber described above. Another aspect of the present invention is a crosslinked product of the rubber composition. Another aspect of the present invention is a rubber hose containing, the crosslinked product. Another aspect of the present invention is a seal member containing the crosslinked product.
According to an aspect of the present invention, an acrylic rubber capable of achieving both water resistance and copper damage resistance may be provided.
One embodiment of the present invention is an acrylic rubber containing an alkyl acrylate, an alkyl methacrylate and ethylene as monomer units.
The alkyl acrylate serves as a skeleton of the acrylic rubber. The alkyl acrylate contains, for example, one or two or more alkyl acrylates having an alkyl group having 1 to 8 carbon atoms. The alkyl group may be linear or branched.
The content of the alkyl acrylate may be 60% by mass or more, 70% by mass or more, or 80% by mass or more, and 95% by mass or less, 92% by mass or less, or 90% by mass or less, and may be 60 to 95% by mass, 60 to 92% by mass, 60 to 90% by mass, 70 to 95% by mass, 70 to 92% by mass, 70 to 90% by mass, 80 to 95% by mass, 80 to 92% by mass, or 80 to 90% by mass, based on the total amount of monomer units contained in the acrylic rubber.
The alkyl acrylate, for example, may contain an alkyl acrylate having alkyl groups having 1 to 3 carbon atoms (hereinafter also referred to as “C1-C3 alkyl acrylate”) and may contain an alkyl acrylate having alkyl groups having 4 to 8 carbon atoms (hereinafter also referred to as “C4-C8 alkyl acrylate”).
Examples of the C1-C3 alkyl acrylates include methyl acrylate, ethyl acrylate, and n-propyl acrylate. From the viewpoint of improving the tensile strength of the acrylic rubber, the alkyl acrylate contains preferably at least one selected from the group consisting of methyl acrylate and ethyl acrylate, and more preferably ethyl acrylate.
The content of the C1-C3 alkyl acrylate may be 30% by mass or more, 40% by mass or more, or 50% by mass or more, may be 80% by mass or less, 70% by mass or less, or 60% by mass or less, and may be 30 to 80% by mass, 30 to 70% by mass, 30 to 60% by mass, 40 to 80% by mass, 40 to 70% by mass, 40 to 60% by mass, 50 to 80% by mass, 50 to 70% by mass, or 50 to 60% by mass, based on the total amount of the monomer units contained in the acrylic rubber.
Examples of the C4-C8 alkyl acrylate include n-butyl acrylate, isobutyl acrylate, n-pentyl acrylate, isoamyl acrylate, n-hexyl acrylate, 2-methylpentyl acrylate, n-octyl acrylate, and 2-ethylhexyl acrylate. From the viewpoint of improving cold resistance of the acrylic rubber, the C4-C8 alkyl acrylate contains preferably butyl acrylate, and more preferably n-butyl acrylate.
The content of C4-C8 alkyl acrylate may be 10% by mass or more, 20% by mass or more, or 30% by mass or more, 60% by mass or less, 50% by mass or less, or 40% by mass or less, and 10 to 60% by mass, 10 to 50% by mass, 10 to 40% by mass, 20 to 60% by mass, 20 to 50% by mass, 20 to 40% by mass, 30 to 60% by mass, 30 to 50% by mass, or 30 to 40% by mass, based on the total amount of the monomer units contained in the acrylic rubber.
The alkyl acrylate preferably contains at least one selected from the group consisting of the C1-C3 alkyl acrylates and at least one selected from the group consisting of the C4-C8 alkyl acrylates, more preferably contains ethyl acrylate and butyl acrylate, and still more preferably contains ethyl acrylate and n-butyl acrylate.
The alkyl methacrylate contains, for example, one or two or more alkyl acrylates having an alkyl group having 1 to 12 carbon atoms. The alkyl group may be linear or branched. The alkyl methacrylate preferably contains an alkyl group having 1 to 8 carbon atoms, and more preferably contains an alkyl group having 1 to 4 carbon atoms.
Examples of the alkyl methacrylate include methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, n-butyl methacrylate, isobutyl methacrylate, n-pentyl methacrylate, n-hexyl methacrylate, n-octyl methacrylate, 2-ethylhexyl methacrylate, n-decyl methacrylate, and n-dodecyl methacrylate.
The alkyl methacrylate preferably contains at least one selected from the group consisting of methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, n-decyl methacrylate, and n-dodecyl methacrylate, more preferably contains at least one selected from the group consisting of methyl methacrylate, ethyl methacrylate, and n-butyl methacrylate, and still more preferably contains methyl methacrylate.
The content of the alkyl methacrylate may be 3% by mass or more, 5% by mass or more, or 7% by mass or more, may be 30% by mass or less, 20% by mass or less, or 10% by mass or less, and may be 3 to 30% by mass, 3 to 20% by mass, 3 to 10% by mass, 5 to 30% by mass, 5 to 20% by mass, 5 to 10% by mass, 7 to 30% by mass, 7 to 20% by mass, or 7 to 10% by mass, based on the total amount of the monomer units contained in the acrylic rubber.
The content of the ethylene may be 0.5% by mass or more, 0.8% by mass or more, or 1% by mass or more, may be 4% by mass or less, 3% by mass or less, or 2% by mass or less, and may be 0.5 to 4% by mass, 0.5 to 3% by mass, 0.5 to 2% by mass, 0.8 to 4% by mass, 0.8 to 3% by mass, 0.8 to 2% by mass, 1 to 4% by mass, 1 to 3% by mass, or 1 to 2% by mass, based on the total amount of monomer units contained in the acrylic rubber.
The acrylic rubber may further contain a crosslinking monomer as the monomer units. The crosslinking monomer is a monomer that is copolymerizable with the alkyl acrylate and alkyl methacrylate and ethylene, and has a functional group that forms a crosslinking site (also referred to as a crosslinking point). The crosslinking monomer has a polymerizable carbon-carbon double bond and has, for example, an acryloyl group, a methacryloyl group, an allyl group, a methallyl group, a vinyl group, or an alkenylene group. Examples of the functional group include an epoxy group, a carboxyl group, and an active chlorine group. The crosslinking monomer may have one or two or more of these functional groups.
In one embodiment, the crosslinking monomer has, as the functional group, preferably an epoxy group, more preferably a glycidyl group. Examples of the crosslinking monomer having an epoxy group include glycidyl acrylate, glycidyl methacrylate, allyl glycidyl ether, and methallyl glycidyl ether.
In another embodiment, the crosslinking monomer preferably has a carboxyl group as the functional group. The number of carboxyl groups in the crosslinking monomer may be one, two, or three or more. Examples of the crosslinking monomer having a carboxyl group include acrylic acid, methacrylic acid, crotonic acid, 2-pentenoic acid, maleic acid, fumaric acid, itaconic acid, and a monoalkyl maleate.
Examples of the crosslinking monomer having an active chlorine group include 2-chloroethyl vinyl ether, 2-chloroethyl acrylate, vinylbenzyl chloride, vinyl chloroacetate, and allyl chloroacetate.
The content of the crosslinking monomer may be 0.5% by mass or more, 0.8% by mass or more, or 1% by mass or more, may be 10% by mass or less, 5% by mass or less, or 3% by mass or less, and may be 0.5 to 10% by mass, 0.5 to 5% by mass, 0.5 to 3% by mass, 0.8 to 10% by mass, 0.8 to 5% by mass, 0.8 to 3% by mass, 1 to 10% by mass, 1 to 5% by mass, or 1 to 3% by mass, based on the total amount of the monomer units contained in the acrylic rubber.
The acrylic rubber may further contain, as monomer units, additional monomers copolymerizable with each of the monomers described above. Examples of the additional monomer include an alkoxyalkyl (meth)acrylate, a fluorine-containing (meth)acrylate, a hydroxyl group-containing (meth)acrylate, a tertiary amino group-containing (meth)acrylate, an alkyl vinyl ketone, a vinyl ether, a vinyl ester, an allyl ether, an aromatic vinyl compound, a vinyl nitrile, a halogenated vinyl, and a halogenated vinylidene.
Examples of the alkoxyalkyl (meth)acrylate include 2-methoxyethyl (meth)acrylate, 2-ethoxyethyl (meth)acrylate, 2-(n-propoxy)ethyl (meth)acrylate, 2-(n-butoxy)ethyl (meth)acrylate, 3-methoxypropyl (meth)acrylate, 3-ethoxypropyl (meth)acrylate, 2-(n-propoxy)propyl (meth)acrylate, and 2-(n-butoxy) propyl (meth)acrylate.
Examples of the fluorine-containing (meth)acrylate include 1,1-dihydroperfluoroethyl (meth)acrylate, 1,1-dihydroperfluoropropyl (meth)acrylate, 1,1,5-trihydroperfluorohexyl (meth)acrylate, 1,1,2,2-tetrahydroperfluoropropyl (meth)acrylate, 1,1,7-trihydroperfluoroheptyl (meth)acrylate, 1,1-dihydroperfluorooctyl (meth)acrylate, and 1,1-dihydroperfluorodecyl (meth)acrylate.
Examples of the hydroxyl group-containing (meth)acrylate include 1-hydroxypropyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, and hydroxyethyl (meth)acrylate. Examples of the tertiary amino group-containing (meth)acrylate include diethylaminoethyl (meth)acrylate and dibutylaminoethyl (meth)acrylate.
Examples of the alkyl vinyl ketone include methyl vinyl ketone. Examples of the vinyl ether include vinyl ethyl ether. Examples of the vinyl ester include vinyl acetate. Examples of the allyl ether include allyl methyl ether. Examples of the aromatic vinyl compound include styrene, α-methylstyrene, chlorostyrene, and vinyltoluene. Examples of the vinyl nitrile include acrylonitrile and methacrylonitrile. Examples of the vinyl halide include vinyl chloride and vinyl fluoride. Examples of the vinylidene halide include vinylidene chloride and vinylidene fluoride.
The content of the additional monomer may be 1% by mass or more and may be 10% by mass or less, based on the total amount of monomer units contained in the acrylic rubber.
The acrylic rubber is obtained by copolymerizing the monomers described above by a known method such as an emulsion polymerization or a suspension polymerization, and more specifically, for example, is obtained by the following method.
First, a monomer mixture containing the alkyl acrylate and alkyl methacrylate is mixed with an aqueous solution of a polyvinyl alcohol in a reactor to prepare a suspension. Subsequently, after the inside of the reactor is replaced with nitrogen gas, ethylene is injected into the reactor at a pressure of, for example, 0.5 to 5 MPa. Thereafter, a polymerization initiator is added to the suspension while stirring the suspension to initiate polymerization, and the polymerization is allowed to proceed, for example, at 40 to 100° C. for 1 to 24 hours. An aqueous sodium borate solution (coagulant) is added to the obtained copolymer to solidify the copolymer, and then washing, dehydrating and drying processes of the copolymer with water are performed in this order to obtain an acrylic rubber.
The monomer mixture may further contain the above-described monomers constituting the acrylic rubber (excluding gaseous monomers such as ethylene) in addition to the alkyl acrylate and alkyl methacrylate, if necessary.
The amount of the polyvinyl alcohol added, for example, may be 0.1 parts by mass or more and may be 10 parts by mass or less, with respect to 100 parts by mass of the total amount of the monomers constituting the acrylic rubber. The polyvinyl alcohol may be a completely saponified polyvinyl alcohol or a partially saponified polyvinyl alcohol, and is preferably a partially saponified polyvinyl alcohol from the viewpoint of easily adjusting the content of the polyvinyl alcohol in the acrylic rubber to the range described below. The degree of saponification of the polyvinyl alcohol is preferably 60% by mole or more, more preferably 70% by mole or more, and even more preferably 80% by mole or more, and is preferably 100% by mole or less, more preferably 99% by mole or less, and even more preferably 90% by mole or less, from the viewpoint of easily adjusting the content of the polyvinyl alcohol-type emulsifier in the acrylic rubber to the range described below. The saponification degree of the polyvinyl alcohol means a value measured in accordance with JIS K6726 “3.5 Saponification degree”.
A pH adjusting agent may be further added to the suspension. The pH adjuster may be, for example, an alkali metal salt such as sodium acetate, sodium hydroxide, potassium hydroxide, sodium phosphate, or sodium citrate, and is preferably sodium acetate. The amount of the pH adjuster added, for example, may be 0.1 parts by mass or more, and may be 5 parts by mass or less, with respect to 100 parts by mass of the total amount of monomers constituting the acrylic rubber.
The polymerization initiator may be, for example, an azo compound such as azobisisobutyronitrile, an organic peroxide such as tert-butyl hydroperoxide, cumene hydroperoxide, and benzoyl peroxide, or an inorganic peroxide such as sodium persulfate or ammonium persulfate, and is preferably tert-butyl hydroperoxide. The amount of the polymerization initiator added, for example, may be 0.01 parts by mass or more, and may be 2 parts by mass or less, with respect to 100 parts by mass of the total amount of the monomers constituting the acrylic rubber.
The solidified copolymer is washed with water in order to adjust the content of the polyvinyl alcohol in the finally obtained acrylic rubber. Specifically, for example, water is added to the copolymer, and the copolymer and water are mixed for a specific period of time to perform washing. The content of the polyvinyl alcohol in the acrylic rubber can be adjusted by the temperature of the water used for washing. The higher the temperature of the water, the lower the content of polyvinyl alcohol in the acrylic rubber.
In order to adjust the content of the polyvinyl alcohol in the acrylic rubber to the range described below, the temperature of the water is preferably higher than 10° C., more preferably 20° C. or higher, even more preferably 30° C. or higher, and particularly preferably 40° C. or higher, and is preferably 90° C. or lower, more preferably 80° C. or lower, even more preferably 70° C. or lower, and particularly preferably 60° C. or lower. The washing time, for example, may be 5 minutes or more, 10 minutes or more, or 20 minutes or more, and may be 1 hour or less, 50 minutes or less, or 40 minutes or less.
The content of the polyvinyl alcohol in the acrylic rubber obtained as described above, based on the total amount of the acrylic rubber. is 0.5% by mass or more from the viewpoint of excellent copper damage resistance, and is preferably 0.6% by mass or more, more preferably 0.8% by mass or more, still more preferably 1% by mass or more, and particularly preferably 1.1% by mass or more, from the viewpoint of further excellent copper damage resistance. The content of the polyvinyl alcohol in the acrylic rubber, based on the total amount of the acrylic rubber, is 2% by mass or less from the viewpoint of excellent water resistance, and is preferably 1.8% by mass or less, more preferably 1.6% by mass or less, still more preferably 1.4% by mass or less, and particularly preferably 1.3% by mass or less, from the viewpoint of further excellent water resistance.
The content of the polyvinyl alcohol in the acrylic rubber, based on the total amount of the acrylic rubber, is 0.5 to 2% by mass from the viewpoint of achieving both water resistance and copper damage resistance, and is preferably 0.5 to 1.8% by mass, 0.5 to 1.6% by mass, 0.5 to 1.4% by mass, 0.5 to 1.3% by mass, 0.6 to 2% by mass, 0.6 to 1.8% by mass, 0.6 to 1.6% by mass, 0.6 to 1.4% by mass, 0.6 to 1.3% by mass, 0.8 to 2% by mass, 0.8 to 1.8% by mass, 0.8 to 1.6% by mass, 0.8 to 1.4% by mass, 0.8 to 1.3% by mass, 1 to 2% by mass, 1 to 1.8% by mass, 1 to 1.6% by mass, 1 to 1.4% by mass, 1 to 1.3% by mass, 1.1 to 2% by mass, 1.1 to 1.8% by mass, 1.1 to 1.6% by mass, 1.1 to 1.4% by mass, or 1.1 to 1.3% by mass, from the viewpoint of further easily achieving both water resistance and copper damage resistance.
The content of the polyvinyl alcohol in the acrylic rubber is measured by a pyrolysis GC-MS. More specifically, the acrylic rubber is thermally decomposed at 550° C. by a double shot pyrolyzer (PY-2020D manufactured by Frontier Laboratories Inc.), and crotonaldehyde, which is a decomposition product of polyvinyl alcohol, is quantitatively determined by gas chromatography mass spectrometry (JMS-DX303 manufactured by JEOL Ltd., agilent capillary column DB-5, carrier gas: helium, inlet temperature: 280° C., temperature rising condition: holding at 70° C. for 2 minutes and then rising to 280° C. at 12° C./min) using an absolute calibration curve method, thereby measuring the content of the polyvinyl alcohol in the acrylic rubber.
In the acrylic rubber, a boron element derived from sodium borate used as a coagulant may remain. The content of the boron element in the acrylic rubber is preferably 100 ppm by mass or less, more preferably 90 ppm by mass or less, still more preferably 80 ppm by mass or less, and particularly preferably 70 ppm by mass or less, based on the total amount of the acrylic rubber. The content of boron is measured by ICP emission spectrometry.
The Mooney viscosity of the acrylic rubber, for example, may be 10 or more, 20 or more, or 30 or more, and may be 70 or less, 60 or less, or 50 or less. The Mooney viscosity of the acrylic rubber is a value measured in accordance with the method specified in JIS K6300, and specifically, refers to a value measured at 100° C. after preheating for 1 minute and after 4 minutes from the start of rotation using an L-type rotor.
The acrylic rubber described above is used as a rubber composition in combination with other components as necessary. That is, another embodiment of the present invention is a rubber composition containing the above-described acrylic rubber (and other components used as necessary). The content of the acrylic rubber, for example, may be 50% by mass or more, 55% by mass or more, or 60% by mass or more, and may be 90% by mass or less, based on the total amount of the rubber composition.
Other components that may be contained in the rubber composition include, for example, a filler, a lubricant, an anti-aging agent, a surfactant, a crosslinking agent, and a crosslinking accelerator.
Examples of the filler include a carbon black, a silica, a talc, and calcium carbonate. The content of the filler, for example, may be 30 parts by mass or more, and may be 100 parts by mass or less, with respect to 100 parts by mass of the acrylic rubber.
Examples of the lubricant include a liquid paraffin, stearic acid, a stearylamine, a zinc fatty acid, a fatty acid ester, and an organosilicone. The content of the lubricant, for example, may be 0.1 parts by mass or more, and may be 10 parts by mass or less, with respect to 100 parts by mass of the acrylic rubber.
Examples of the anti-aging agent include an aromatic amine compound and a phenol compound. The content of the anti-aging agent, for example, may be 0.1 parts by mass or more, and may be 10 parts by mass or less, with respect to 100 parts by mass of the acrylic rubber.
Examples of the surfactant include an alkyl sulfate ester salt. The content of the surfactant, for example, may be 0.1 parts by mass or more, and may be 10 parts by mass or less, with respect to 100 parts by mass of the acrylic rubber.
When the acrylic rubber contains a crosslinking monomer as the monomer units, examples of the crosslinking agent include an imidazole compound and a diamine compound. When the acrylic rubber does not contain a crosslinking monomer as the monomer units, examples of the crosslinking agent include a polyfunctional (meth)acrylate compound. The content of the crosslinking agent, for example, may be 0.1 parts by mass or more, and may be 10 parts by mass or less, with respect to 100 parts by mass of the acrylic rubber.
The crosslinking accelerator is preferably used when the rubber composition contains a crosslinking agent. Examples of the crosslinking accelerator include a trimethylthiourea compound, a phenothiazine compound, and a guanidine compound. The content of the crosslinking accelerator, for example, may be 0.1 parts by mass or more, and may be 10 parts by mass or less, with respect to 100 parts by mass of the acrylic rubber.
The rubber composition is suitably used in a crosslinked state (as a crosslinked product). That is, another embodiment of the present invention is a crosslinked product of the above rubber composition. The crosslinked product is obtained by crosslinking the rubber composition. In the case where the acrylic rubber contains a crosslinking monomer as the monomer units, crosslinking between the acrylic rubbers is formed by crosslinking sites (crosslinking points) of the crosslinking monomer. In this case, when the rubber composition contains a crosslinking agent, crosslinking between the acrylic rubbers is further formed by the crosslinking agent. Alternatively, in the case where the acrylic rubber does not contain a crosslinking monomer as the monomer units and the rubber composition contains a crosslinking agent, crosslinking between acrylic rubbers is formed by the crosslinking agent.
The method of crosslinking the rubber composition may be a known method, and may contain, for example, a first crosslinking step of heating and pressurizing the rubber composition, and a second crosslinking step of further heating the rubber composition after the first crosslinking step.
In the first crosslinking step, the heating temperature, for example, may be 150° C. or more, and may be 220° C. or less. The pressure of the pressurization, for example, may be 0.4 MPa or more, and may be 20 MPa or less. The heating and pressurizing time, for example, may be 5 minutes or more, and may be 2 hours or less.
In the second crosslinking step, the heating temperature, for example, may be 150° C. or more, and may be 220° C. or less. The heating time, for example, may be 30 minutes or more and may be 24 hours or less.
The crosslinked product of the rubber composition is particularly suitably used as a rubber hose or a seal member such as a gasket, a packing, and the like. That is, another embodiment of the present invention is a rubber hose or a seal member containing the crosslinked product. The rubber hose and the seal member may consist of only the crosslinked product of the rubber composition, or may contain the crosslinked product and another member.
Examples of the rubber hose include a transmission oil cooler hose, an engine oil cooler hose, an air duct hose, a turbo intercooler hose, a hot air hose, a radiator hose, a power steering hose, a fuel system hose, and a drain system hose for automobiles, construction machines, hydraulic equipment, and the like.
Examples of the seal member include an engine head cover gasket, an oil pan gasket, an oil seal, a lip seal packing, an O-ring, a transmission seal gasket, a crankshaft, a camshaft seal gasket, a valve stem, a power steering seal belt cover seal, a boot material for a constant-velocity joint, a rack-and-pinion boot material.
Hereinafter, the present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples.
A pressure-resistant reactor having an internal volume of 40 liters was charged with 11 kg of a monomer mixed liquid containing monomers shown in Tables 1 and 2 (excluding ethylene), 17 kg of 4% by mass of an aqueous polyvinyl alcohol solution (degree of saponification of the polyvinyl alcohol: 88% by mole), and 22 g of sodium acetate, and these were thoroughly mixed in advance with a stirrer to prepare uniform suspensions. Then, after the upper portion of the reactor was replaced with nitrogen, ethylene was injected into the upper portion of the reactor by 3 MPa. After stirring was continued and the temperature in the reactor was maintained at 55° C., 2 liters of an aqueous t-butyl hydroperoxide solution (0.25% by mass) was added to initiate polymerization. The temperature inside the reactor was maintained at 55° C., and the reaction was terminated after 6 hours. To the obtained copolymer, 7 liters of an aqueous sodium borate solution (3.5% by mass) was added to solidify the copolymer. Next, a step of adding 450 parts by mass of pure water having a temperature shown in Tables 1 and 2 to 100 parts by mass of the solidified copolymer, stirring the mixture in the reactor for 5 minutes, and discharging the water from the reactor was repeated 4 times to perform water washing. Thereafter, dehydration and drying were performed to obtain an acrylic rubber.
The compositions of the monomer units contained in the obtained acrylic rubbers are shown in Tables 1 and 2. The content of the monobutyl maleate monomer unit was measured by dissolving the acrylic rubber in toluene and performing neutralization titration using potassium hydroxide. The contents of the other monomer units were measured by nuclear magnetic resonance spectroscopy.
In addition, the content of the polyvinyl alcohol and boron in the obtained acrylic rubber and the Mooney viscosity ML (1+4) 100° C. were measured. The results are shown in Tables 1 and 2.
The content of the polyvinyl alcohol in the acrylic rubber was measured by a pyrolysis GC-MS. More specifically, the acrylic rubber was thermally decomposed at 550° C. by a double shot pyrolyzer (PY-2020D manufactured by Frontier Laboratories Inc.), and crotonaldehyde, which was a decomposition product of polyvinyl alcohol, was quantitatively determined by gas chromatography mass spectrometry (JMS-DX303 manufactured by JEOL Ltd., agilent capillary column DB-5, carrier gas: helium, inlet temperature: 280° C., temperature rising condition: holding at 70° C. for 2 minutes and then rising to 280° C. at 12° C./min) using an absolute calibration curve method, thereby measuring the content of the polyvinyl alcohol in the acrylic rubber. The content of boron was measured by ICP emission spectrometry. The Mooney viscosity ML (1+4) 100° C. was measured according to the method specified in JIS K6300.
Subsequently, each of the obtained acrylic rubbers and each component shown below were used in the compositions shown in Tables 1 and 2, and kneading was performed with an 8-inch open roll to obtain a rubber composition.
Filler: carbon black (Seast SO manufactured by Tokai Carbon Co., Ltd.) Lubricant a: stearic acid (Lunac S-90 manufactured by Kao Corporation) Lubricant b: stearylamine (Farmin 80 manufactured by Kao Corporation) Anti-aging agent: 4,4′-bis(α,α-dimethylbenzyl) diphenylamine (Naugard #445 manufactured by Addivant)
Surfactant: sodium laurylsulfate (Emal 0 manufactured by Kao Corporation) Crosslinking agent a: 2,2-bis[4-(4-aminophenoxy) phenyl] propane (BAPP manufactured by Wakayama Seika Kogyo Co., Ltd.)
Crosslinking agent b: 1-(2-cyanoethyl)-2-methylimidazole (CN-25 manufactured by Shikoku Chemicals Corporation)
Crosslinking accelerator a: 1,3-di-o-tolylguanidine (NOCCELER DT manufactured by Ouchi Shinko Chemical Industrial Co., Ltd.)
Crosslinking accelerator b: ammonium benzoate (VALKNOCK AB manufactured by Ouchi Shinko Chemical Industrial Co., Ltd.)
The obtained rubber composition was dispensed into a sheet having a thickness of 2.4 mm, and then heated and pressurized at 170° C. and 10 MPa for 20 minutes using a press vulcanizer. Subsequently, heating was carried out in a gear oven at 170° C. for 4 hours to obtain a crosslinked product of the rubber composition.
(Evaluation of Properties of Crosslinked Product)
The tensile strength and elongation of the crosslinked product were measured in accordance with JIS K6251-2010. Further, the hardness of the crosslinked product was measured using a type A durometer in accordance with JIS K6253-2006.
(Evaluation of Water Resistance)
In accordance with the “immersion test” of JIS K6258-2010, the crosslinked product was subjected to an immersion test with pure water, and the volume change rate of the crosslinked product before and after the test was calculated based on the following formula.
Volume change rate (%)=(volume after test−volume before test)/volume before test×100
(Evaluation of Copper Damage Resistance)
A crosslinked product molded into a No. 3 dumbbell shape was used as a test piece. 5 g of a slurry obtained by mixing engine oil (Mobil 1 5W-30 manufactured by EMG Lubricanz Performance Materials Inc.) and copper powder (CE-1110 manufactured by Fukuda Metal Foil & Powder Co., Ltd.) at a ratio of engine oil/copper powder=3/1 (mass ratio) was applied using a brush so as to completely cover the marked lines of the test piece, and dried at room temperature for 12 hours. Subsequently, the copper damage resistance test was performed by heating the test piece in a gear oven at 150° C. for 500 hours. Thereafter, the copper-containing paste was peeled off from the test piece using a spatula, and the elongation of the test piece was measured in accordance with JIS K6251-2010. The elongation change rate (%) before and after the test was calculated based on the following formula.
Elongation change rate (%)=(elongation after test−elongation before test)/elongation before test×100
As can be seen from Table 1, in the acrylic rubber in which the crosslinking monomer having an epoxy group is used as the crosslinking monomer, when the content of the polyvinyl alcohol in the acrylic rubber is within the specific range, both of the water resistance and copper damage resistance can be achieved (any one of them is not excessively deteriorated). Similarly, as can be seen from Table 2, in the acrylic rubber in which the crosslinking monomer having a carboxyl group is used as the crosslinking monomer, when the content of the polyvinyl alcohol in the acrylic rubber is within the specific range, both of the water resistance and copper damage resistance can be achieved (any one of them is not excessively deteriorated).
| Number | Date | Country | Kind |
|---|---|---|---|
| 2019-189531 | Oct 2019 | JP | national |
| 2019-189539 | Oct 2019 | JP | national |
| 2019-189548 | Oct 2019 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2020/026389 | 7/6/2020 | WO |