Actinide production

Abstract

The invention provides a process for reducing to metallic form oxides of uranium, or metals more noble than uranium, present in spent nuclear fuel comprising a mixture of metal oxides, the process comprising cathodically electrolysing the oxide in the presence of a molten salt electrolyte, the potential of the cathode being controlled so as to favour oxygen ionisation over deposition of the metal from the cations present in the molten salt, and to ensure than reduction of metals other than uranium or metals more noble than uranium does not occur. The invention allows for the reduction of uranium or metals more than uranium present in spent nuclear fuel comprising mixed metal oxides to a metallic form by the use of a single electrochemical process, with oxygen being produced as the only by-product.

Description

FIELD OF THE INVENTION

[0001] This invention relates to methods for the production of metals from oxides present in spent nuclear fuels and is particularly applicable to the production of actinides, specifically uranium and metals more noble than uranium, from actinide oxides which are present in irradiated nuclear fuels. Methods of the present invention can be used in the treatment of irradiated fuels for producing actinides in metallic form suitable for use as feeds in subsequent electrorefining processes.

BACKGROUND TO THE INVENTION

[0002] In the established art, two processes have been developed for the treatment of irradiated nuclear fuel making use of molten salts. As used herein, the term “molten salts” is intended to cover salts such as lithium chloride which melts at an elevated temperature and also ionic liquids which typically are liquid at room temperature or which melt at a temperature up to about 100° C.

[0003] The Dimitrovgrad SSC-RIAR process makes use of chemical oxidants (chlorine and oxygen gases) to react with powdered uranium dioxide fuel to form higher oxidation state compounds such as UO2Cl2 which are soluble in the molten salt. In an electrochemical cell the uranium compounds are reduced to UO2 at the cathode, forming a dendritic deposit. This process has both technical and environmental limitations.

[0004] The second process, developed by the Argonne National Laboratory (ANL) is fundamentally an electrorefining technology which uses current flow to anodically oxidise uranium to form uranium ions in the molten salt electrolyte. At the cathode the uranium is reduced and electrodeposited as uranium metal.

[0005] The ANL process requires a metal feed. If oxide fuels are to be treated, it is necessary to reduce the uranium oxide (usually UO2 pellets) to the metal. This reduction process is carried out chemically, using lithium metal in a LiCl or LiCl/KCl molten salt at 500 to 600° C. Alternatively, a salt transport process can be used involving a Cu—Mg—Ca alloy and molten CaCl2 salt. However, in both reduction methods the by-products, Li2O and CaO respectively, need to be recovered from the molten salt phase by an electrolysis step. Effectively this means a two stage process.

[0006] A disadvantage of the lithium reduction process for producing a metallic feed from an oxide is the production of Li2O by-product. This requires recycle to make the process economic, and this is done by an electrolytic recovery of lithium metal. Hence this is a two stage process, comprising a reduction step followed by a lithium recovery stage.

[0007] In co-pending patent application no. PCT/GB00/04604 there is disclosed a single step process for reducing to metallic form a metal oxide present in spent nuclear fuel, the process comprising cathodically electrolysing the oxide in the presence of a molten salt electrolyte, the potential of the cathode being controlled so as to favour oxygen ionisation over deposition of the metal from the cations present in the molten salt.

[0008] The process thereby involves the use of a single electrochemical process to reduce the metal oxide fuel to a metallic form, with oxygen produced as the only by-product. The potential of the cathode is maintained and controlled so that only oxygen ionisation occurs and not the deposition of the cations (eg Ca ions) in the fused salt. Typically, the oxide comprises an actinide oxide, such as uranium oxide or irradiated uranium oxide.

[0009] In the nuclear industry, however, it is often necessary to separate metals from a mixture of metal oxides such as occurs in spent nuclear fuel. Thus mixtures of uranium and plutonium oxides, together with the oxides of other actinide metals, may additionally be contaminated with oxides of other, chemically active, metals such as, for example, those associated with zircalloy cladding. The present invention seeks to provide a method for the treatment of irradiated fuel which allows for the separation of uranium, and metals more noble than uranium, from such mixtures as found in spent nuclear fuel, and to provide these metals in a form suitable for use as the feed in a molten salt electrorefining process, whilst ensuring that other, more electropositive, metals remain in the form of oxides.

STATEMENTS OF INVENTION

[0010] Thus, according to the present invention there is provided a process for reducing to metallic form oxides of uranium, or metals more noble than uranium, present in spent nuclear fuel comprising a mixture of metal oxides, the process comprising cathodically electrolysing the oxide in the presence of a molten salt electrolyte, the potential of the cathode being controlled so as to favour oxygen ionisation over deposition of metal from the cations present in the molten salt, and to ensure that reduction of metals other than uranium or metals more noble than uranium does not occur.

[0011] The invention provides a single electrochemical process to reduce the metal oxide fuel to a metallic form, with oxygen produced as the only by-product. The potential of the cathode is maintained and controlled so that only oxygen ionisation occurs and not the deposition of the cations (eg Ca ions) in the fused salt, and also to ensure that, whilst reduction of uranium or metals more noble than uranium occurs smoothly, the less noble metals are not reduced and remain in the anode as oxides. Typically, the mixture of oxides includes an actinide oxide, such as uranium oxide or irradiated uranium oxide, or mixed uranium/plutonium oxides. The uranium oxide is commonly uranium dioxide.

[0012] The oxide may be in any physical form, and this is generally dependent on the particular chemical nature of the spent nuclear fuel and the processing to which the material has previously been subjected. For example, the fuel may comprise a powder, an amorphous mass, or a dense solid agglomerate. In any event, the material may be treated according to the method of the present invention by connection to an electrical circuit such that it serves as the cathode during electrolysis. Connection to the circuit may be effected by any of the standard means well known to those skilled in the art.

[0013] Preferably the oxide fuel is in contact with the cathode of an electrochemical cell. The cathode could be in the form of a mesh basket. The molten salt electrolyte may be any suitable molten salt or mixture of such salts, for instance chloride salts, preferably CaCl2 and/or BaCl2.

[0014] The anode may be any suitable inert anode, such as carbon. In a process of the present invention the oxide fuel may be first treated mechanically to remove its zircaloy cladding before it is added to the electrolytic cell. Alternatively, the zircaloy cladding may be treated with the fuel. The fuel may require to be sheared into sections of small length prior to treatment in order to expose the oxide fuel to the molten salt.

DETAILED DESCRIPTION OF THE INVENTION

[0015] In order to carry out an embodiment of the present invention, an electrolytic cell is assembled which has a carbon anode and a mesh basket cathode. Irradiated oxide fuel is placed in the mesh basket. The electrolyte consists of a molten salt or a mixture of such salts comprising, for example, chloride salts such as CaCl2 or BaCl2. A voltage is applied between the cathode and the anode. At the cathode the reaction involves the diffusion of oxygen atoms to the surface of the solid, followed by ionisation according to the reaction:

O+2e−→O2−.

[0016] The oxide ions which are produced dissolve in the electrolyte and are transferred to the anode where they are re-oxidised to produce oxygen gas. The potential at the cathode is controlled, via a third reference electrode, to ensure that the reaction occurring at the cathode is oxygen ionisation and not deposition of the cations in the fused salt, and that only selected metal oxides—specifically those of uranium and of metals more noble than uranium—are reduced. Electrolysis at elevated temperatures results in an increased rate of oxygen diffusion, thereby also encouraging ionisation rather than metal deposition.

[0017] After electrolysis the irradiated fuel is left in the form of a metal/metal oxide solid mixture at the cathode, with uranium and more noble metals having been reduced to the metallic form, whilst the less noble metals remain in the form of their oxides. This metallic/metal oxide product, which contains fission products, can be removed and used directly as the feed for an electrorefining process. The remaining components of the cell may be re-used immediately without the need for any cleaning.

[0018] In the electrorefining step, a potential is applied to the metal/metal oxide mixture at the anode such that only uranium metal enters the salt, whilst the less noble metals remain behind as oxides. Insufficient potential is applied to encourage the dissolution of metals more noble than uranium.

[0019] Thus, only uranium and metals with similar electronegativities enter the salt and the uranium deposited at the cathode is of a higher purity. Contamination of the cathode product with fission product impurities is also substantially reduced.

[0020] In an alternative embodiment in accordance with the present invention the electrolytic ionisation of oxygen and the electrorefining processes are carried out in the same cell and the same salt system.

[0021] It is to be emphasised that the advantage of the process of the present invention is that it is effectively a single stage process. It is used for the treatment of irradiated mixed metal oxide nuclear fuel, possibly in the form of pellets and, most particularly, is applied to fuels which contain uranium oxide, and mixed uranium and plutonium fuels.

Claims

1. A process for reducing to metallic form oxides of uranium, or metals more noble than uranium, present in spent nuclear fuel comprising a mixture of metal oxides, comprising: cathodically electrolysing the metal oxides in the presence of a molten salt electrolyte; and controlling the potential of a cathode so as to favour oxygen ionisation over deposition of the metal from the cations present in the molten salt, and to ensure that reduction of metals other than uranium or metals more noble than uranium does not occur.

2. A process according to claim 1 wherein the metal oxides comprise fuel pellets which include uranium oxide, irradiated uranium oxide and/or of mixed uranium/plutonium oxide.

3. A process according to claim 2 wherein the uranium oxide comprises uranium dioxide.

4. A process according to claim 1 wherein the metal oxides are located in a mesh basket which forms the cathode.

5. A process according to claim 1 wherein the molten salt electrolyte comprises at least one chloride salt.

6. A process as claimed in claim 5 wherein the chloride salt is CaCl2 or BaCl2.

7. A process according to claim 1 wherein an anode is a carbon anode.

8. A process according to claim 1 wherein the fuel is treated together with its cladding.

9. A process according to claim 8 wherein the cladding is removed from the fuel prior to treatment.

10. A process according to claim 1 wherein a metal/metal oxide mixture resulting from the process is used as the feed for an electrorefining process.

11. A process according to claim 1 wherein the potential applied during the electrorefining process is such that only uranium metal enters the salt.

12. A process according to claim 11 wherein the electrorefining process is carried out in the same electrolytic cell as an electrolytic reduction process.