Activated metathesis catalysts

Abstract

Process for preparing a supported catalyst (catalyst C) comprising a support (support S) and an active component (activator A), wherein

Description

[0001] The present invention relates to a process for preparing a supported catalyst (catalyst C) comprising a support (support S) and an active component (activator A), wherein

[0002] a) a catalyst precursor is prepared by applying an activator customary for the catalysis of metathesis reactions (activator precursor) to a customary support (step a),

[0003] b) the catalyst precursor prepared in step a) is brought into contact with a hydrocarbon compound at from −20 to 550° C. (step b) and

[0004] c) the catalyst precursor prepared in step b) is heated at from 410 to 850° C. in an inert gas atmosphere (step c).

[0005] Furthermore, the invention relates to catalysts (catalysts C) which are obtainable by this process and to a process for preparing unsaturated compounds by metathesis using a catalyst (C).

[0006] The metathesis of unsaturated compounds is a long-established method of breaking and rearranging C—C bonds (e.g. Mol, J. C., Chapt. 4.12.2 “Alkene Metathesis” in “Handbook of Heterogeneous Catalysis”, Eds. Ertl, G., Knözinger, H., Weitkamp, J., VCH, Weinheim 1997; Weissermehl, K., Arpe, H.-J., Chapt. 3.4 “Olefin-Metathese” in “Industrielle Organische Chemie”, 4th edition, VCH, Weinheim 1994).

[0007] Various types of catalysts have been described for heterogeneously catalyzed metathesis. For the temperature range up to 120° C., the use of supported R2O7 or Re(CO)10 catalysts is customary (Mol, J. C., Chapt. 4.12.2 “Alkene Metathesis” in “Handbook of Heterogeneous Catalysis”, Eds. Ertl, G., Knözinger, H., Weitkamp, J., VCH, Weinheim 1997). However, rhenium is a rare and relatively expensive element, so that the use of such a catalyst is often uneconomical. At somewhat higher temperatures up to 400° C., catalysts based on MoO3, CoO—MoO3, MoS2, Mo(CO)6 or various supported Mo complexes can be employed according to the literature, and at even higher temperatures up to 540° C., systems based on WO3, WS2, W(CO)6 or supported W complexes can be employed (Mol, J. C., Chapt. 4.12.2 “Alkene Metathesis” in “Handbook of Heterogeneous Catalysis”, Eds. Ertl, G., Knözinger, H., Weitkamp, J., VCH, Weinheim 1997; Weissermehl, K., Arpe, H.-J.,Chapt. 3.4 “Olefin-Metathese” in “Industrielle Organische Chemie”, 4th edition, VCH, Weinheim 1994; Heckelsberg, L. F., Banks, R. L., Bailey; G. C., Ind. Eng. Chem. Prod. Res. Develop. 8 (1969), 259-261). Although these are very inexpensive, they generally have a significantly lower activity and also display lower selectivities. The reduced selectivities are a consequence of double bond isomerization which proceeds in parallel to metathesis over the strongly acidic molybdenum and tungsten compounds at relatively high reaction temperatures, which leads to the formation of undesirable products.

[0008] To suppress the secondary reaction of double bond isomerization, U.S. Pat. No. 3,586,731 describes the addition of alkali metal salts or alkaline earth metal salts to silica-supported oxides, sulfides or hexacarbonyls of tungsten, molybdenum or rhenium. However, this can lead to a considerable decrease in the catalyst activity.

[0009] U.S. Pat. No. 4,024,201 proposes adding halogen-containing compounds or amines to the feed. to a supported WO3 catalyst. However, such polar compounds are at the same time known as catalyst poisons in metathesis, so that a greatly reduced activity may also be expected here.

[0010] It is an object of the present invention to prepare a catalyst having increased metathesis activity and selectivity.

[0011] We have found that this object is achieved by the process and catalysts defined at the outset.

[0012] The catalyst precursors which are prepared in step a) and are subsequently reacted further in steps b) and c) to give the catalysts C of the present invention are the supported catalysts customarily used in metathesis reactions. Such catalysts are described, for example, in “Handbook of Heterogeneous Catalysis”, edited by G. Ertl, H. Knözinger and J. Weitkamp, Volume 5, VCH Verlagsgesellschaft mbH, Weinheim, Chapter 4.12.2, Alkene Metathesis, pages 2387 to 2399.

[0013] Possible supports (support S) for the preparation of catalyst precursors are all materials customarily used for the preparation of supported catalysts, for example metal oxides, nitrides, borides, carbides, silicates, activated carbon, graphite. Preference is given to compounds of main group elements or elements of transition group VI or 11 and also mixtures of the abovementioned compounds. Particular preference is given to Al2O3, aluminosilicates, Ga2O3, SiO2, GeO2, TiO2, ZrO2, SnO2 and mixtures of the abovementioned compounds. Suitable supports typically have a specific surface area of 10-500 m2/g, preferably 100-400 m2/g. The preferred pore volume (determined by means of mercury porosimetry) is from 0.3 to 1.3 ml/g. The preferred water absorption is from 0.5 to 1.5 mug. The supports are usually shaped bodies such as spheres, granules, extrudates or pellets. The support may have additionally been pretreated with acids.

[0014] The active components (activator precursors) applied to the support (S) in step a) include the customarily used compounds and mixtures thereof. These are generally compounds of the metals of transition groups V, VI and VII, in particular compounds of rhenium, tungsten or molybdenum. Possible compounds are the sulfides, oxides, nitrides, carbides, oxycarbides, carbonyls, organic complexes, halides, acids, polyacids, heteropolyacids and salts of the acids, polyacids and heteropolyacids. Such salts are preferably alkali metal or ammonium salts. In the present context, organic complexes are, for example, dialkyl complexes, acyl compounds, acetylacetonates or allyl complexes. Particular preference is given to molybdenum oxide and tungsten oxide. The term salts also includes substoichiometric bronzes. The term oxide extends not only to the stoichiometric compounds such as MoO3, WO3, MoO2 and WO2 but also includes substoichiometric phases of the type MO3-2. As support for tungsten or molybdenum compounds, very particular preference is given to SiO2.

[0015] In general, the preparation of the customary catalysts comprising oxides as activator precursors and serving as catalyst precursors is carried out in step a) by impregnating the support S with a solution of the abovementioned compounds. In the case of tungsten oxide, a solution of, for example, ammonium metatungstate, tungstic acid or tungsten pentachloride can be employed for this purpose. The impregnated supports are then usually dried in air at from 100 to 200° C. for a number of hours. This is usually followed by a calcination step. For this purpose, the impregnated and dried supports are usually heated in an oxygen-containing gas atmosphere, e.g. in air, at from 400 to 850° C. for a period of from about half an hour to 5 hours. The catalyst precursors prepared in this way can also be pretreated by means of heating steps in inert gas, for example N2, CO2 or noble gases, or be partially reduced in reducing gas mixtures comprising, for example, hydrogen, CO, ammonia or hydrazine.

[0016] To prepare the customary supported catalysts with carbides or oxycarbides as activator precursors which are included among the catalysts precursors, it is usual to start from the catalyst precursors comprising oxides as active component which have been prepared by the above method. In the carbiding step, the appropriate catalyst precursors comprising metal oxide are heated at from 550 to 800° C. in a hydrocarbon-containing stream, e.g. a methane stream, in the presence of hydrogen for, in general, a number of hours. The preparation of tungsten carbides typically requires temperatures about 50-200° C. higher than those for preparing molybdenum carbides. The properties of the carbides are also influenced by the H2/CH4 ratio which is typically 80/20. The appropriate carbiding methods are known and described, for example, in Oyama, S. T., Catal. Today, 15 (1992), 179.

[0017] After the carbiding step, these catalyst precursors have to be stored under an inert gas atmosphere because of their sensitivity to air, or they are passivated by means of dilute oxygen and then reactivated in the synthesis reactor. A further possibility is taking out the freshly prepared carbides under a liquid which substantially protects the carbide surface from atmospheric oxygen.

[0018] Furthermore, the following processes are also suitable for preparing catalyst precursors comprising carbides as activator precursors:

[0019] In J. Catal. 128, 126 (1991), Lee et al. describe the preparation of Al2O3-supported molybdenum carbides by (i) reduction followed by carbiding, (ii) direct carbiding in CH4/H2 or (iii) nitriding by means of NH3 followed by carbiding.

[0020] Volpe, Boudart, J. Solid State Chem. 59, 332 (1985) and Volpe, Boudart, J. Solid State Chem. 59, 348 (1985) describe the nitriding/carbiding of MoO3 and WO3 in more detail.

[0021] The reduction of MoO3 on carbon supports by means of hydrogen, which is coupled with carbiding by the carbon support above 530° C., is described, for instance, in Liang et al., Chem. Mater. 2002, 14, 3148.

[0022] Oxycarbides which can be used as activator precursors are described, for example, in Pham-Huu et al., Appl. Catal. A 132 (1995), 77. They can be prepared from the oxides by only partial carbiding. The oxycarbides are also formed under suitable conditions during the reaction when the oxide is used as starting material and a hydrocarbon/H2 mixture is then passed over the catalyst at elevated temperatures (for instance: H2/n-hexane=150, T=350° C.

[0023] The oxycarbides can also be prepared by treatment of carbides with oxygen. In Ledoux et al., New Frontiers in Catalysis, 1993, p. 955, Guczi, L. et al. (editors), Elsevier Science Publishers B.V., the carbide is firstly treated with air at 350° C. and then with hydrogen at the same temperature.

[0024] In step b), the catalyst precursors which have been prepared in this way are brought into contact with a hydrocarbon compound. Suitable hydrocarbon compounds are, in particular, aromatics, alkanes, cycloalkanes, alkynes, cycloalkynes, olefins or cycloolefins having from 1 to 20 carbon atoms. Particular preference is given to C3-C12-olefins, very particularly preferably butenes and octenes, e.g. 1-butene and n-1-octene.

[0025] In the treatment of the catalyst precursor with the hydrocarbon compound, the latter can be either in liquid or gaseous form. The treatment time is not critical and is usually 1 min-24 h, preferably 5 min-4 h. The temperature during the treatment is generally from −20 to 550° C., but is not critical. The latter also applies to the pressure, which is generally from 0.5 to 40 bar.

[0026] The catalyst precursor which has been treated with the hydrocarbon is subsequently heated to from 410 to 850° C., preferably from 500 to 850° C., in an inert gas atmosphere in step c). Suitable inert gases are, in particular, nitrogen, CO2 and the noble gases. The treatment in step c) is usually carried out for from 5 minutes to 100 hours, preferably from 30 minutes to 24 hours, with the pressure once again being noncritical and usually being from 0.5 to 40 bar.

[0027] The catalysts (C) of the present invention may further comprise promoters. These are generally cobalt, alkali metal or alkaline earth metal compounds. They are generally applied to the catalyst by adding appropriate salts, e.g. nitrates or hydroxides, to the impregnation solutions for preparing the catalyst precursors, or by doping the catalysts afterward with an appropriate impregnation solution and calcining the catalysts once again to immobilize the dopant.

[0028] The proportion of activator (A) in the catalyst (C) is usually from 0.1 to 30% by weight.

[0029] The catalyst (C) particularly preferably comprises WO3 in tetragonal form, as activator (A) and SiO2 as support (S).

[0030] The catalysts of the present invention are particularly useful for the metathesis of unsaturated compounds such as alkenes or alkynes. Such processes are generally known and are described, for example, in “Industrielle Organische Chemie”, Klaus Weissermel, Hans-Jürgen Erpel, 5th edition, Wiley, VCH, 1998, Chapter 3.4 and “Handbook of Heterogeneous Catalysis”, edited by G. Ertl, H. Knözinger and J. Weitkamp, Volume 5, VCH Verlagsgesellschaft mbH, Weinheim, Chapter 4.12.2, Alkene Metathesis, pages 2387 to 2399. However, they can also be used for the metathesis of unsaturated esters, nitriles, ketones, aldehydes, acids or ethers, as described, for example, in Xiaoding, X., Imhoff, P., von den Aardweg, C. N., and Mol, J. C., J. Chem. Soc., Chem. Comm. (1985), p. 273. In the reaction of substituted olefins, use is frequently made of a cocatalyst, for example tin, lead or aluminum alkyls, to increase the activity further.

[0031] The catalysts (C) of the present invention can be used in the same way as the known metathesis catalysts which are prepared as described in step a) of the process of the present invention and serve as catalyst precursors for the catalysts C of the present invention.

[0032] The catalysts of the present invention can be particularly advantageously used in metathesis processes for preparing propene by metathesis of a mixture comprising 2-butene and ethylene or 1-butene and 2-butenes, or for preparing 3-hexene and ethylene by metathesis of 1-butene. Appropriate processes are described in detail in DE-A-19813720, EP-A-1134271, WO 02/083609, DE-A-10143160.

[0033] The abovementioned C4 starting compounds are usually supplied in the form of a raffinate II. The raffinate II is a C4 fraction which generally has a butene content of from 30 to 100% by weight, preferably from 40 to 98% by weight. Apart from butenes, saturated C4-alkanes in particular can also be present. The way in which such raffinates 11 are obtained is generally known and is described, for example, in EP-A-1134271.

[0034] In particular, it is possible to use 1-butene which is obtained by distilling off a 1-butene-rich fraction from raffinate II. 1-Butene can likewise be obtained from the remaining 2-butene-rich fraction by subjecting the 2-butene-rich fraction to an isomerization reaction and subsequently fractionally distilling the product to give a 1-butene-rich fraction and a 2-butene-rich fraction. This process is described in DE-A-10311139.

[0035] The rhenium-containing catalysts of the present invention are particularly useful for reactions in the liquid phase at from 10 to 150° C. and a pressure of from 5 to 100 bar.

[0036] The tungsten- or molybdenum-containing catalysts of the present invention are 5 generally used in gas-phase reactions. The temperature here is generally from 150 to 500° C. The pressure is generally 5-50 bar.

[0037] Experimental Part

[0038] A. Preparation of the Catalysts

[0039] A. 1. Preparation of the Catalyst Precursors

EXAMPLE 1

Preparation of WO3/SiO2 catalyst—cats A—E

[0040] SiO2 supports were in each case impregnated with aqueous, dilute ammonium metatungstate solution to incipient wetness. The extrudates were then dried at 120° C. in a drying oven for 16 hours. The catalyst was finally treated under the conditions indicated in a rotary tube furnace and cooled under dry nitrogen (20 I/h). The catalyst C1 was then additionally impregnated with a 0.5 M NaOH solution and once again dried and calcined under the abovementioned conditions, as a result of which the Na content in the finished catalyst was increased from 1 100 to 4 500 ppm (=sample C2). Further details regarding the preparative conditions and the catalyst precursors themselves are given in table 1.

TABLE 1
	WO3
	content		Conditions in rotary tube
Cat	[wt %]	Support	furnace
A	12.1	BASF D11-10, 1.5 mm extrudates	1 h in air (20 l/h), 593° C.
		(171 m2/g)
B	13.9	BASF D11-10, 1.5 mm extrudates	1 h in air (20 l/h), 593° C.
		(171 m2/g)
C1	12.5	BASF D11-10, 1.5 mm extrudates	1 h in air (20 l/h), 593° C.
		(171 m2/g)
D	11.2	Shell X970 CY, 3 mm extrudates	1 h in air (20 l/h), 593° C.
		(326 m2/g)
E1	15.0	Solvay Siligel BR 5155/1, 0.8-2 mm	1 h in air (20 l/h), 593° C.
		spheres (350 m2/g)
E2	15.0	Solvay Siligel BR 5155/1, 0.8-2 mm	1 h in air (20 l/h), 593° C. + 2.5 h
		spheres (350 m2/g)	in N2 (20 l/h), 850° C.
F	12.2	BASF D11-10, 0.5-0.8 mm granules	1 h in air (20 l/h), 593° C.
		(171 m2/g)

EXAMPLE 2

Preparation of the Tungsten Carbide Catalyst—Cat G

[0041] To prepare catalyst G, 70 ml of the WO3/SiO2 catalyst A were placed in a glass reactor through which gas was passed from the top downward. The glass reactor was heated from the outside by means of an electric furnace, and the catalyst bed was located approximately in the middle of the heating zone on a glass frit. After the catalyst had been installed and the reactor had been closed, the plant was firstly flushed with nitrogen (30 min, 20 I/h). A gas stream comprising 3.9 I/h of methane and 15 I/h of hydrogen were subsequently passed over the catalyst. The reactor was then heated to 750° C. over a period of 180 minutes and held at 750° C. for 6 hours. It was then cooled to 500° C. over a period of 1 hour and this temperature was held for 2 hours. The reactor was then cooled and the methane/hydrogen stream was replaced by a stream of nitrogen. After the reactor had been flushed, the reactor inlet and outlet were closed and the reactor was removed from the plant in such a way that the catalyst could be transferred into a glove box without coming into contact with air. Contact with air was likewise avoided in subsequent handling of the catalyst, for instance the installation of the catalyst in the reactor or its introduction into analytical instruments.

[0042] An XRD (X-ray diffraction) pattern of the catalyst removed from the reactor after the metathesis reaction shows the compounds WC and W2C together with traces of metallic tungsten. WOx compounds are not observed.

EXAMPLE 3

Preparation of an MoO3/SiO2 Catalyst—Cat H

[0043] SiO2 (BASF D11-10, 1.5 mm extrudates) was impregnated with an aqueous, dilute solution of (NH4)6Mo7O24*4H2O to incipient wetness. The extrudates were then dried at 120° C. in a drying oven for 16 hours. The catalyst was finally calcined at 593° C. in air (20 I/h) for 1 hour in a rotary tube furnace and cooled under dry nitrogen. The MoO3 content was 11.1% by weight.

EXAMPLE 4

Preparation of a WO3/SiO2 Catalyst—Cat J

[0044] 508.2 g of SiO2 (Shell X970 CY, 3 mm extrudates) were predried at 500° C. (air, 50 I/h). The cooled extrudates were impregnated with a solution of 70 g of WCl6 in 1 200 ml of ethanol under a nitrogen atmosphere. The catalyst was subsequently dried in a stream of air (300 I/h, about 30 min) and calcined at 550° C. in air (50 I/h) for 2 hours. The catalyst was subsequently heated for another 2 hours at 850° C. under N2 (50 I/h). The WO3 content was 7.3%.

[0045] A.2 Activation of the Catalyst Precursors from Steps b) and c)

EXAMPLE 5

Activation of the Catalysts (Methods 0-VII)

[0046] The catalysts were, with the exception of the compartive methods 0 and VII, each firstly brought into contact with a hydrocarbon, either directly in the reactor or by wetting with a liquid before installation of the catalyst. The catalysts which had been moistened with hydrocarbons were, with the exception of the comparative methods 0 and VI, subsequently heated under flowing nitrogen (30 I/h) to the temperature indicated for the time indicated and subsequently cooled to the reaction temperature under nitrogen. The conditions are reported in detail in table 2.

TABLE 2
			Time for
			which the
			hydrocarbon		Heat
			is	T (heat	treatment
			allowed to	treatment)1)	time
Method	Hydrocarbon	T (wetting) [° C.]	act	[° C.]	[h]
0 (comp.)	Not	Not	Not	Not	Not
	applicable	applicable	applicable	applicable	applicable
I (comp.)	1-Butene	1901)	3 h	300	18
II (comp.)	1-Butene	1901)	3 h	400	17
III	1-Butene	1901)	3-5 h	510	16-20
IV	n-1-Octene	Room temp.	10 min	510	15
V	n-Octane	Room temp.	10 min	510	15
VI (comp.)	n-1-Octene	Room temp.	10 min	Not	Not
				applicable	applicable
VII (comp.)	Not	Not	Not	510	17
	applicable	applicable	applicable
1)The temperature reported is that at the entrance to the bed. As a result of a nonuniform temperature distribution of the heating, the temperature increases through to the end of the bed where it is about 10-15% higher.

[0047] In-situ XRD measurement on catalysts F/0 and F/IV

[0048] Measurement on Catalyst F/0

[0049] Catalyst F/0 is a catalyst of the prior art and was prepared as described under point A.1, example 1 (method 0 in table 2). The catalyst F/0 was pulverized. The sample was introduced into the XRD measurement chamber on a heated alumina plate (depth: 0.8 mm). The measuring instrument is a model D8 Advance (from Bruker/AXS) equipped with a heated camera HTK 1200 from Paar. The measurement was carried out using Cu-Kα radiation in θ/θ geometry with a primary- and secondary-side Göbel mirror in the range 2θ=15°−52° at 6s/step at selected temperatures.

[0050] At room temperature, the sample in each case comprised monoclinic WO3 and amorphous SiO2 (FIG. 1). The sample was heated in air. At 400, 500 and 600° C., no change was observed. Only at 850° C. did tetragonal WO3 form. The sample was then cooled to 200° C., resulting in the WO3 transforming back into the monoclinic phase.

[0051] Measurement on catalyst F/IV

[0052] The catalyst F/0 was pulverized and wetted with 1-octene. The sample was then introduced into the measuring apparatus described above and heated under a nitrogen atmosphere. Tetragonal WO3 was formed at a temperature as low as 400° C. (FIG. 2). This phase remains stable at 500 and 600° C. In contrast to catalyst F/0, no transformation into the monoclinic phase occurred even after cooling to 200° C. It can be concluded from this that the catalyst F/0 has been changed irreversibly by the process of the present invention.

[0053] B. Metathesis Reactions

EXAMPLES 6-25

[0054] About 35 g of catalyst were placed in an electrically heated tube reactor. The temperature specified was set at the entrance to the catalyst bed. A nonuniform temperature distribution of the heating led to a rise in temperature through to the end of the catalyst bed (in each case reported in brackets). As feed pure 1-butene was fed in. The reaction pressure was 9.7 bar. Analysis of the output from the reactor was carried out on-line using a GC. Before the actual measurement, the catalysts had each been activated by the specified procedure 0-VI. The results are shown in table 3.

TABLE 3
				1-Butene
	Cat./	T	WHSV	conversion		Hexenes	Propenes	C6 selectivity
Ex.	meth.	[° C.]	h−1	[%]	Isomerization1)	[mol %]	[mol %]	[mol %] 2)
5	B/0	190	7.9	66.6	66.4	0	0	0
(comp.)		(256)
6	C2/0	190	7.9	24.7	24.5	0	0	0
(comp.)		(249)
7	D/0	190	7.6	43.6	43.4	0	0.1	0
(comp.)		(268)
8	E1/0	190	8.0	60.3	59.9	0.1	0.2	0.2
(comp.)		(263)
9	G/0	190	8.7	52.6	51.5	0.2	0.8	0.8
(comp.)		(303)
10	H/0	190	7.8	79.9	79.6	0.1	0.3	0.1
(comp.)		(269)
11	J/0	189	15.1	14.0	13.0	0.3	0.2	7.9
(comp.)		(242)
12	A/VII	189	8.0	65.7	49.3	6.3	7.7	19.3
(comp.)		(274)
13	C1/	190	9.3	53.4	53.4	0	0	0
(comp.)	VI	(247)
14	B/I	190	8.1	77.4	76.0	0.4	1.4	0.9
(comp.)		(280)
15	B/II	190	8.1	75.0	60.1	5.0	6.9	13.3
(comp.)		(270)
16	B/III	190	8.1	62.4	43.1	7.8	9.6	24.9
		(256)
17	A/III	189	8.0	63.0	32.7	11.5	16.1	36.4
		(274)
18a	C2/	189	4.0	37.0	6.9	15.6	2.8	84.1
	III	(208)
18b	C2/	190	6.0	32.5	5.7	12.8	2.1	78.5
	III	(231)
18c	C2/	190	8.0	29.9	4.3	13.1	1.5	87.9
	III	(240)
19	D/III	200	7.6	47.8	11.5	16.8	7.8	70.3
		(244)
20	E1/	190	7.4	46.5	13.5	14.6	7.3	62.8
	III	(251)
21	E2/0	190	7.7	43.5	23.0	8.7	7.4	40.0
(comp.)		(228)
22	E2/	190	7.2	47.0	12.8	16.6	6.5	70.5
	III	(228)
23a	G/III	155	4.3	44.1	13.9	13.5	6.9	61.1
		(238)
23b	G/III	190	8.8	52.8	22.5	13.4	10.2	50.8
		(293)
24	H/III	190	7.6	64.0	57.0	2.4	3.4	7.6
		(263)
25a	J/III	189	4.0	41.2	8.2	17.9	4.3	86.0
		(212)
25b	J/III	190	10.0	33.9	6.1	15.1	2.8	86.7
		(237)
25c	J/III	190	14.9	38.7	4.8	16.7	2.6	86.3
		(240)
25d	J/III	170	14.9	26.9	2.5	13.3	1.1	98.9
		(217)
26	E1/	190	7.7	43.2	14.8	12.2	6.9	56.7
	IV	(247)
27	B/V	190	7.7	64.5	38.4	10.1	13.5	31.2
		(250)
1)Sum of the allyl fragments formed = [propene]/2 + 2-butene + pentenes
2)C6-Selectivity = 2 * C6 yield/conversion (1-butene)

Claims

1. A process for preparing a supported catalyst (catalyst C) comprising a support (support S) and an active component (activator A), wherein a) a catalyst precursor is prepared by applying an activator customary for the catalysis of metathesis reactions (activator precursor) to a customary support (step a), b) the catalyst precursor prepared in step a) is brought into contact with a hydrocarbon compound at from −20 to 550° C. (step b) and c) the catalyst precursor prepared in step b) is heated at from 410 to 850° C. in an inert gas atmosphere (step c).

2. A process as claimed in claim 1, wherein the support (S) is selected from among oxides, phosphates, silicates, carbides, borides and nitrides of main group elements and elements of transition groups VI and II and mixtures of the abovementioned compounds.

3. A process as claimed in either of the preceding claims, wherein the support (S) is selected from the group consisting of Al2O3, aluminosilicates, Ga2O3, SiO2, GeO2, TiO2, ZrO2, SnO2 and mixtures of the abovementioned compounds.

4. A process as claimed in any of the preceding claims, wherein the activator precursor comprises compounds containing elements of transition groups V, VI and VII.

5. A process as claimed in claim 4, wherein the compounds of elements of transition groups V, VI and VII are selected from the group consisting of sulfides, oxides, nitrides, carbides, oxycarbides, carbonyls, organic complexes, halides, acids, polyacids, heteropolyacids and salts of the acids, polyacids and heteropolyacids.

6. A process as claimed in any of the preceding claims, wherein the activator precursor comprises compounds selected from the group consisting of rhenium, tungsten and molybdenum compounds.

7. A process as claimed in any of the preceding claims, wherein the activator precursor comprises compounds selected from the group consisting of molybdenum oxides, tungsten carbides and tungsten oxides.

8. A process as claimed in any of the preceding claims, wherein the activator precursor comprises compounds selected from the group consisting of compounds of metals of transition groups V, VI and VII and a promoter selected from the group consisting of cobalt, alkali metal and alkaline earth metal compounds.

9. A process as claimed in any of the preceding claims, wherein step (a) is carried out by impregnating the support (S) with a solution of the activator precursor and subsequently drying it and, if desired, calcining it.

10. A process as claimed in any of the preceding claims, wherein the hydrocarbon compound used in step (b) is selected from the group consisting of C1-C20-alkanes, -cycloalkanes, -olefins, -cycloolefins, -alkynes, -cycloalkynes, aromatics and mixtures of the abovementioned compounds.

11. A process as claimed in any of the preceding claims, wherein the inert gas used in step (c) is selected from the group consisting of nitrogen, carbon dioxide and noble gases and mixtures thereof.

12. A catalyst (C) obtainable by a process as claimed in any of claims 1 to 11.

13. A catalyst (C) as claimed in claim 12 comprising from 0.1 to 30% by weight of WO3 in tetragonal form.

14. A catalyst (C) as claimed in claim 13, wherein the support S consists essentially of SiO2.

15. A process for preparing unsaturated compounds by metathesis using a catalyst (C).

16. A process as claimed in claim 15, wherein 3-hexene and ethylene are prepared by bringing 1-butene into contact with a catalyst (C) at from 50 to 500° C.

17. A process as claimed in claim 11, wherein propene is prepared by bringing a mixture of 2-butenes with ethylene or 1-butene into contact with a catalyst (C) at from 50 to 500° C.