Acylated cyclodextrin derivatives

Abstract

A cyclodextrin derivative, wherein at least 60 percent of the free hydroxy groups of said cyclodextrin are acylated with acyl groups where at least one of said acyl groups comprise a free carboxylic group.

Description

BACKGROUND OF THE INVENTION

In 1904, Schardinger first characterized cyclodextrins as cyclic oligosaccharides. The .alpha., .beta., and .gamma.-cyclodextrins, which consist of six, seven, and eight glucose units, respectively, are the most common natural cyclodextrins.

Cyclodextrins have been used as inclusion complexes by complexing with a guest compound or molecule as a host compound or molecule. Such inclusion complexes have been used to mask the bitter taste or unpleasant odor of a guest compound, to solubilize a hardly soluble guest compound, to enlarge the stability of a guest compound against heat, light, or air, to stabilize emulsions, or as a sustained release preparation using a hydrophobic alkylated cyclodextrin. See U.S. Pat. No. 4,869,904. However, no one has attempted to make carboxyacylated cyclodextrins, or used such cyclodextrin derivatives to form ionic sustained release compositions.

SUMMARY OF THE INVENTION

In one aspect, the present invention features a cyclodextrin derivative, wherein at least 60 (e.g., between 75 and 100) percent of the free hydroxy groups of the cyclodextrin are acylated with acyl groups where at least one of the acyl groups comprises a free carboxylic group. What is meant by cyclodextrin is a cyclic oligosaccharide. Examples of cyclodextrins include .alpha.-cyclodextrin, .beta.-cyclodextrin, or .gamma.-cyclodextrin.

In one embodiment the acyl groups are selected from COE.sub.1, where E.sub.1 is selected from the group consisting of C.sub.2-32 carboxy alkyl, C.sub.3-33 carboxy alkenyl, C.sub.7-37 carboxyaryl, C.sub.8-38 carboxyaryl alkyl, and C.sub.9-39 carboxyaryl alkenyl, and COE.sub.2, where E.sub.2 is selected from the group consisting of C.sub.1-30 alkyl, C.sub.2-30 alkenyl, C.sub.6-36 aryl, C.sub.7-37 arylalkyl, and C.sub.8-38 arylalkenyl, wherein at least one of the acyl group is COE.sub.1. In a further embodiment, between 10 and 80 (e.g., between 30 and 80) percent of the free hydroxy groups of the cyclodextrin are acylated with COE.sub.1 and between 10 and 80 (e.g., between 15 and 60) percent of the cyclodextrin are acylated with COE.sub.2. In still a further embodiment, E.sub.1 is C.sub.2-10 carboxy alkyl (e.g., COE.sub.1 is CO(CH.sub.2).sub.n COOH (where n=2-3)) and E.sub.2 is C.sub.1-10 alkyl (e.g., COE.sub.2 is CO(CH.sub.2).sub.0 nCH.sub.3 (where n=0-5)).

In another aspect, the invention features a copolymer comprising the cyclodextrin derivative described above, wherein the cyclodextrin derivative comprises at least one free hydroxy group which is acylated with a polyester comprising hydroxy acid monomers. In one embodiment, the copolymer has an average molecular weight of between 500-40,000 daltons (e.g., 500-10,000). In a further embodiment, the polyester comprises hydroxy acid monomers selected from the group consisting of lactic acid, glycolic acid, hydroxy caprolic acid, or any optically active isomer thereof. Such polyesters can be manufactured by reacting said cyclodextrin derivative with lactide, glycolide, caprolactone, p-dioxanone, trimethyl carbonate, or any optically active isomer thereof.

In still another aspect, the invention features a composition comprising the cyclodextrin derivative described above and a drug, the drug comprising at least one effective ionogenic amine, wherein at least 50 percent, by weight, of the polypeptide present in the composition is ionically bonded to the cyclodextrin derivative. In one embodiment, the composition comprises between 1 and 30 (e.g., between 10 and 20) percent, by weight, of the drug. In a further embodiment, the drug is a polypeptide. In still a further embodiment, the polypeptide comprises between 4 and 200 amino acids (e.g., between 4 and 50 amino acids). Examples of the polypeptide include somatostatin, bombesin, calcitonin, amylin, parathyroid hormone, parathyroid hormone related protein, gastrin releasing peptide, luteinizing hormone releasing hormone, growth hormone, growth hormone releasing factor, interferons, erythropoietin, granulocyte colony stimulating factor, granulocyte macrophage colony stimulating factor, pituitary adenylate cyclase activating polypeptide, vasoactive intestinal peptide, thyrotropin releasing hormone, corticotropin releasing hormone, Acetyl-Ser-Asp-Lys-Pro, arginine vasopressin, angiotensin, and any fragments, agonists, or antagonists thereof.

In yet another aspect, the invention features a composition comprising the copolymer described above and a drug, the drug comprising at least one effective ionogenic amine, wherein at least 50 percent, by weight, of the polypeptide present in the composition is ionically bonded to the cyclodextrin derivative. In one embodiment, the composition comprises between 1 and 30 (e.g., between 10 and 20) percent, by weight, of the drug. In a further embodiment, the drug is a polypeptide.

As used herein, "lower alkyl" is intended to include both branched and straight-chain saturated aliphatic hydrocarbon groups. Examples of lower alkyl groups include methyl, ethyl, propyl, isopropyl, butyl, t-butyl, isobutyl, sec-butyl, and the like. "Lower alkenyl" groups include those branched and straight chain aliphatic hydrocarbon groups having one or several double bonds. Examples of alkenyl groups include vinyl, allyl, isopropenyl, butenyl, pentenyl, hexenyl, 1-propenyl, 2-butenyl, 2-methyl-2-butenyl, isoprenyl, and the like. All alkyl, alkenyl, and alkynyl groups are noncyclic.

As used herein, "aryl" is intended to include any stable monocyclic, bicyclic, or tricyclic carbon ring(s) of up to 7 members in each ring, wherein at least one ring is aromatic. Examples of aryl groups include phenyl, naphthyl, anthracenyl, biphenyl, tetrahydronaphthyl, indanyl, phenanthreynl, and the like. The term "carboxy" is meant to include the recited chemical group (e.g., alkyl, alkenyl, aryl, arylalkyl, arylalkenyl) substituted with 1 to 3 carboxy groups.

Other features and advantages of the present invention will be apparent from the detailed description of the invention, and from the claims.

DESCRIPTION OF THE INVENTION

It is believed that one skilled in the art can, based on the description herein, utilize the present invention to its fullest extent. The following specific embodiments are, therefore, to be construed as merely illustrative, and not limitative of the remainder of the disclosure in any way whatsoever.

Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Also, all publications, patent applications, patents, and other references mentioned herein are incorporated by reference.

EXAMPLE 1

Preparation of Acylated .beta.-Cyclodextrin (ACD)

Cyclodextrin (Amaizo, American Maize Products Corp. Hammond, Ind.) was dried at 90.degree. C. under reduced pressure (0.1 mm Hg) to a constant weight. Dried cyclodextrin (CD) was then transferred to a reaction flask equipped for stirring. After purging with argon, the CD was heated at 50.degree. C. for 30 min. at 0.1 mm Hg, cooled to 25.degree. C., and repurged with dry argon. Calculated amount of the acylating reagent, as a liquid anhydride (except in ADC No. 1 where the anhydrides were dissolved in 15 ml of acetic acid), containing a catalytic amount (i.e., 1 percent by weight) of p-toluene sulfonic acid (except in ACD No. 1 and ACD No. 2 where 1 percent H.sub.2 SO.sub.4 was used instead of p-toluene sulfonic acid) was transferred to the reaction flask, mixed under a dry argon atmosphere, and then heated. The amount of CD and acylating agents used as well as the heating scheme is described in Table I. At the conclusion of the reaction, the resulting mixture was allowed to cool slightly and then poured on to a vigorously stirring ice-water mixture. The resulting precipitate was filtered, rinsed several times with cold water, and air dried. The product was then isolated and dried until constant weight under vacuum, first at 25.degree. C. and then 50.degree. C. The product was characterized for equivalent weight, as reported in Table I, by measuring titratable carboxylic acid functionally using benzyl alcohol solution of the product and potassium hydroxide in benzyl alcohol with bromophenol red as an indicator.

TABLE I______________________________________Preparation and Properties of Acylated .beta.-Cyclodextrins (ACD) HEATING EQUIV- SCHEME ALENTACD Temp (.degree. C.) WEIGHTNo. REACTANTS.sup.1 Time (min.) (Da)______________________________________1 51.0 g CD, 55.0 g A, 28.7 g S 95/180 11042 25.5 g CD, 28.1 g A, 14.4 g S 95/135 8743 12.8 g CD, 9.69 g A, 10.8 g G 95/120 5614 12.8 g CD, 18.0 g P, 8.20 g G 95/15; 100/30; 829 and 105/305 12.7 g CD, 12.2 g P, 10.7 g G 90/60 6576 12.7 g CD, 10.1 g P, 13.9 g G 70/20 5247 12.7 g CD, 10.1 g P, 13.9 g G 60/10 and 65/30 5118 12.7 g CD, 12.3 g B, 13.9 g G 60/10 and 65/45 5749 12.7 g CD, 8.90 g B, 20.5 g G 65/10 and 60/50 40110 12.7 g CD, 5.31 g B, 20.4 g G 65/5 and 60/50 346______________________________________ .sup.1 CD is Cyclodextrin, A is Acetic Anhydride, P is Propionic Anhydride, B is Butyric Anhydride, S is Succinic Anhydride, and G is Glutaric Anhydride

EXAMPLE 2

Grafting Acylated Cyclodextrin (G-ACD) with Lactones

Predetermined amounts of the above acylated cyclodextrin derivative (ACD), lactone or mixture of lactones, and a catalytic amount (i.e., <0.2 percent by weight) of stannous octoate were transferred to a dry polymerization flask equipped for stirring, under an inert dry atmosphere. The amount of ACD and lactones used are described in Table II. The mixture was then heated under vacuum at about 45.degree. C. for 30 min., cooled to room temperature, and then purged with dry argon. The reactants were then heated while stirring as described in Table II. At the conclusion of the reaction, the temperature was lowered to abut 110.degree. C., and vacuum was applied for 0.5 to 1 hr. to remove distillable volatiles. The polymerization flask was cooled to room temperature and purged with argon. The grafted copolymer product (G-ACD) was isolated, dissolved in acetone, and then precipitated in ice water. The precipitate was filtered and air dried. The resulting powder was further dried under vacuum to a constant weight. The product was characterized for equivalent weight, as reported in Table II, by measuring titratable carboxylic acid functionality.

TABLE II______________________________________Preparation of Lactone-Grafted ACD (G-ACD) HEATING EQUIV-G- SCHEME ALENTACD Temp (.degree. C.)/ WEIGHTNo. REACTANTS.sup.1 Time (Hr.) (Da)______________________________________1 2.50 ACD No. 4, 7.90 g L, 2.10 g G 150/6 20602 2.50 ACD No. 3, 7.90 g L, 2.10 g G 150/7 10553 4.00 ACD No. 7, 6.32 g L, 1.68 g G 150/6.5 11004 2.67 ACD No. 7, 6.32 g L, 1.68 g G 150/10.5 11485 3.30 ACD No. 7, 6.27 g CL, 0.34 g G 150/10 10726 2.66 ACD No. 8, 6.32 g L, 1.68 g G 150/7 9457 5.34 ACD No. 9, 12.65 g L, 3.37 g G 150/3.5 681______________________________________ .sup.1 G is glycolide, L is D,LLactide, and CL is Caprolactone

EXAMPLE 3

Preparation of Polypeptide Composition Containing of Acylated p-Cyclodextrin (U-CON)

Predetermined amount of the above acylated .beta.-cyclodextrin (ACD) was dissolved in a minimum volume of acetone (from 5-15 weight/volume percent) and filtered through a micro-syringe with 0.45 .mu.m porous filter. The filtrate was cooled and a 1N sodium hydroxide aqueous solution was added to neutralize carboxylic groups in the ACD. A concentrated, cold solution (3-15 weight/volume percent) of the acetate salts of the polypeptides Lanreotide.TM. (D-Nal-c�Cys-Tyr-D-Trp-Lys-Val-Cys!-Thr-NH.sub.2 ; Kinerton Ltd., Dublin, Ireland) or Decapeptyl.TM. (pGlu-His-Trp-Ser-Tyr-D-Trp-Leu-Arg-Pro-Gly-NH.sub.2 ; Kinerton Ltd.) was added to acetone solution of the neutralized ACD dropwise with stirring. The product was left at 25.degree. C. for 0.5-1 hr. and then precipitated in a stirring ice-water bath. The resulting precipitate was filtered, rinsed thoroughly with water, and air dried. The product was then isolated and dried under vacuum to constant weight at room temperature. The weight of the dried composition was determined, and the composition was characterized for percent content of peptide, as measured by elemental analysis of the percent of nitrogen present in the composition (Quantitative Technologies, Inc., Whitehouse, N.J.), as reported in Table III. The particulate product was reduced in size by grinding to achieve an average particle size of about 100.mu. before storage under reduced pressure.

TABLE III______________________________________Preparation and Properties of Polypeptide/Acylated .beta.-Cyclodextrin Conjugates (U-CON)U-CON PERCENT PERCENTNo. REACTANTS.sup.1 NITROGEN PEPTIDE______________________________________1 0.11 g ACD No. 1, 0.01 g L 0.54 3.842 0.10 g ACD No. 2, 0.02 g L 1.40 9.963 0.035 g ACD No. 4, 0.016 g L 1.42 10.114 0.08 g ACD No. 3, 0.028 g L 2.47 17.585 0.074 g ACD No. 5, 0.028 g L 2.72 19.366 0.819 g ACD No. 5, 0.215 g L 2.18 15.507 0.811 g ACD No. 5, 0.212 g L 2.00 14.208 0.803 g ACD No. 4, 20.199 g L 2.42 17.209 3.00 g ACD No. 5, 0.502 g L 2.20 15.6010 2.005 g ACD No. 4, 0.500 g D 2.49 17.7011 0.201 g ACD No. 7, 0.051 g D 2.19 12.1012 0.402 g ACD No. 6, 0.131 g D 3.75 20.7213 0.??? ACD No. 8, 0.202 g D 3.68 20.3314 2.004 g ACD No. 8, 0.671 g L 1.45 10.3215 0.601 g ACD No. 9, 0.202 g D 3.34 18.4516 1.2015 g ACD No. 10, 0.401 g D 4.45 24.5817 2.055 g ACD No. 9, 0.671 g L 2.57 18.29______________________________________ .sup.1 L is Lanreotide .TM. and D is Decapeptyl

EXAMPLE 4

Preparation of Polypeptide Conjugates of Lactone-Grafted Acylated .beta.-Cyclodextrin (G-CON)

Predetermined amount of the grafted ACD (G-ACD) was converted to a peptide composition following the same procedure used in preparing the U-CON's in Example 3. Reaction composition and characterization data of the different G-CON's are reported in Table IV.

TABLE IV______________________________________Preparation and Properties of Polypeptide/Lactone-Grafted ACD Conjugates (G-CON)G-CON PERCENT PERCENTNo. REACTANTS.sup.1 NITROGEN PEPTIDE______________________________________1 0.079 g G-ACD No. 1, 0.027 g L 0.62 4.412 0.077 g G-ACD No. 2, 0.028 g L 1.00 7.123 1.00 g G-ACD No. 3, 0.252 g L 0.96 6.804 1.99 g G-ACD No. 4, 0.502 g L 0.74 5.306 0.202 g G-ACD No. 4, 0.051 g D 0.53 2.927 2.003 g G-ACD No. 5, 0.5019 g L 1.16 8.268 1.206 g G-ACD No. 6, 0.4015 g D 1.98 10.939 1.2035 g G-ACD No. 7, 0.4036 g D 3.56 19.6710 2.0078 g G-ACD No. 6, 0.6706 g L 1.69 12.03______________________________________ .sup.1 L is Lanreotide .TM. and D is Decapeptyl

EXAMPLE 5

In Vivo Release Assay

Male Sprague-Dawley rats (200-225 g; Taconic Farms) were injected intermuscularly with approximately 3 ml of either 7.differential.mg of G-CON-19 or 922 mg of U-CON-16 or 966 mg of U-CON-16 administered in a vehicle of 2% carboxymethyl cellulose/1% Tween 20/saline. Blood samples were taken by 6 hours, 2 days, 7 days, 15 days and 22 days following administration. The concentration of Lanreotide.TM. in the blood was measured by standard radioimmunoassay and is reported in the following Table V.

TABLE V______________________________________Lanreotide .TM. Release in Rate Plasma PLASMA LANREOTIDE (pg/ml)COMPOSITION 6 HRS. DAY 2 DAY 7 DAY 15 DAY 22______________________________________U-CON-19 67006 33921 19690 6115 1691U-CON-16 61338 24347 7649 1621 766______________________________________ Thus, both the ungrafted composition U-CON-19 and the grafted composition U-CON-16 released the drug Lanreotide.TM. over a period of at least 22 days.

Other Embodiments

It is to be understood that while the invention has been described in conjunction with the detailed description thereof, that the foregoing description is intended to illustrate and not limit the scope of the invention, which is defined by the scope of the appended claims. Other aspects, advantages, and modifications are within the claims.

Claims

1. A cyclodextrin derivative, wherein at least 60 percent of the free hydroxy groups of said cyclodextrin are acylated with acyl groups where at least one of said acyl groups comprises a free carboxylic group, provided that at least one of said acyl groups does not comprise a free carboxylic group.

2. A cyclodextrin derivative of claim 1, wherein said cyclodextrin is .alpha.-cyclodextrin, .beta.-cyclodextrin, or .gamma.-cyclodextrin.

3. A cyclodextrin derivative of claim 2, wherein said acyl groups are selected from COE.sub.1, where E.sub.1 is selected from the group consisting of C.sub.2-32 carboxy alkyl, C.sub.3-32 carboxy alkenyl, C.sub.7-37 carboxyaryl, C.sub.8-38 carboxyaryl alkyl, and C.sub.9-39 carboxyaryl alkenyl and COE.sub.2, where E.sub.2 is selected from the group consisting of C.sub.1-30 alkyl, C.sub.2-30 alkenyl, C.sub.6-36 aryl, C.sub.7-37 anylakyl, and C.sub.8-38 aryl alkenyl, wherein at least one of said acyl group is COE.sub.1.

4. A cyclodextrin derivative of claim 3, wherein between 10 and 80 percent of said free hydroxy groups of said cyclodextrin are acylated with COE.sub.1 and between 10 and 80 percent of said free hydroxy groups of said cyclodextrin are acylated with COE.sub.2.

5. A cyclodextrin derivative of claim 4, wherein COE.sub.1 is CO(CH.sub.2).sub.n COOH (where n=2-3) and COE.sub.2 is CO(CH.sub.2).sub.n CH.sub.3 (where n=0-5) and said cyclodextrin is .beta.-cyclodextrin.

6. A copolymer comprising said cyclodextrin derivative of claim 1, wherein said cyclodextrin derivative comprises at least one free hydroxy group which is acylated with a polyester comprising hydroxy acid monomers.

7. A copolymer of claim 6, wherein said copolymer has an average molecular weight of between 500-40,000 daltons.

8. A copolymer of claim 7, wherein said polyester comprises hydroxy acid monomers selected from the group consisting of lactic acid, glycolic acid, hydroxy caprolic acid, or any optically active isomer thereof.

9. A copolymer comprising said cyclodextrin derivative of claim 5, wherein said cyclodextrin derivative comprises at least one free hydroxy group which is acylated with a polyester comprising hydroxy acids.

10. A copolymer of claim 9, wherein said polyester comprises hydroxy acid monomers selected from the group consisting of lactic acid, glycolic acid, hydroxy caprolic acid, or any optically active isomer thereof and said copolymer has an average molecular weight of between 500-40,000 daltons.