Patent Grant
11459506
This application claims priority of Taiwan Patent Application No. 108102902, filed on Jan. 25, 2019, the entirety of which is incorporated by reference herein.
The present disclosure relates to an additive, a liquid-crystal composition, and a liquid-crystal display device using the additive.
Liquid-crystal display devices have been used in various applications, including personal computers, personal digital assistants (PDAs), mobile phones, televisions, and so on, because these devices have many advantages. These advantages include being light in weight, having low power consumption, and not emitting radiation.
In a liquid-crystal display device, the alignment of liquid-crystal molecules can be achieved with a polyimide film. Conventional liquid-crystal alignment layers are generally produced by coating a polyimide onto a substrate to form a film, and then mechanically rubbing it to form the desired liquid-crystal alignment groove on the surface of the polyimide film. However, after rubbing the alignment film, uneven alignment may occur, or serious brush marks may be produced. As a result, the product yield of the liquid-crystal display device is not good.
Furthermore, the procedure can also be simplified without an alignment layer. Therefore, manufacturers have begun to develop liquid-crystal display devices having no alignment layer. The liquid-crystal composition of such a liquid-crystal display device contains polar compounds, and the liquid-crystal molecules are vertically aligned by the function of the polar compounds. However, it is difficult for such polar compounds to be compatible with vertical alignment ability and a high voltage holding ratio. Furthermore, the stability of the alignment ability of such polar compounds also needs to be improved.
Accordingly, a liquid-crystal composition having excellent vertical alignment ability, a high voltage holding ratio, and a high stability of its alignment ability is still needed in this technical field.
In one embodiment of the present disclosure, an additive is provided. The additive includes an additive molecule having a structure represented by formula (I):
and
and at least one of X3, X4, X5 and X6 represents
K2 represents —L4—R5.
In other embodiments of the present disclosure, a liquid-crystal composition is provided. The liquid-crystal composition includes a first component and a second component. The first component includes at least one additive as mentioned above, and the second component includes at least one compound represented by formula (II):
wherein
each of R21 and R22 independently represents hydrogen, halogen, a C1-C15 alkyl group, or a C2-C15 alkenyl group, wherein the C1-C15 alkyl group or the C2-C15 alkenyl group is unsubstituted or at least one hydrogen atom of the C1-C15 alkyl group or the C2-C15 alkenyl group is substituted by a halogen atom, and/or at least one —CH2— of the C1-C15 alkyl group or the C2-C15 alkenyl group is substituted by —O—, and wherein the —O— does not directly bond to another —O—;
each of B1, B2, and B3 independently represents a 1,4-phenylene group, a 1,4-cyclohexylene group, a benzofuran-2,5-diyl group, a 1,3-dioxane-2,5-diyl group, a tetrahydropyran-2,5-diyl group, a divalent dioxabicyclo[2.2.2]octylene group, a divalent trioxabicyclo[2.2.2]octylene group, a tetrahydronaphthalene-2,6-diyl group, or a indane-2,5-diyl group, wherein the 1,4-phenylene group, the 1,4-cyclohexylene group, the 1,3-dioxane-2,5-diyl group, the benzofuran-2,5-diyl group, the tetrahydronaphthalene-2,6-diyl group, the indane-2,5-diyl group, or the tetrahydropyran-2,5-diyl group is unsubstituted or at least one hydrogen atom of the 1,4-phenylene group, the 1,4-cyclohexylene group, the 1,3-dioxane-2,5-diyl group, the benzofuran-2,5-diyl group, the tetrahydronaphthalene-2,6-diyl group, the indane-2,5-diyl group, or the tetrahydropyran-2,5-diyl group is substituted by a halogen atom or a —CN group, and/or at least one —CH2— of the 1,4-phenylene group, the 1,4-cyclohexylene group, the 1,3-dioxane-2,5-diyl group, the benzofuran-2,5-diyl group, the tetrahydronaphthalene-2,6-diyl group, the indane-2,5-diyl group, or the tetrahydropyran-2,5-diyl group is substituted by —O—, —N— or —S—, and wherein the —O—, —N—, and —S— do not directly bond to one another;
each of Z21 and Z22 independently represents a single bond, a C1-C4 alkylene group, a C2-C4 alkenylene group, or a C2-C4 alkynylene group, wherein the C1-C4 alkylene group, the C2-C4 alkenylene group, or the C2-C4 alkynylene group is unsubstituted or at least one hydrogen atom of the C1-C4 alkylene group, the C2-C4 alkenylene group, or the C2-C4 alkynylene group is substituted by a halogen atom or a —CN group, and/or at least one —CH2— of the C1-C4 alkylene group, the C2-C4 alkenylene group, or the C2-C4 alkynylene group is substituted by —O— or —S—, and wherein the —O— does not directly bond to —O— or —S—, and —S— does not directly bond to —S—; and
n21 represents 0, 1, or 2, and when n21 represents 2, the two B1 groups are identical to each other or different from each other.
In other embodiments of the present disclosure, a liquid-crystal display device is provided. The liquid-crystal display device includes a first substrate and a second substrate disposed opposite to the first substrate. The liquid-crystal display device also includes a liquid-crystal layer disposed between the first substrate and the second substrate. The liquid-crystal layer includes the above-mentioned additive.
Embodiments of the present disclosure provide an additive, and a liquid-crystal composition and a liquid-crystal display device using the additive, which can greatly improve the vertical alignment property, voltage holding ratio, and stability of the alignment ability of the liquid-crystal composition. Therefore, the performance and durability of the liquid-crystal display device can be improved.
To further simplify and clarify the foregoing contents and other objects, characteristics, and merits of the present disclosure, a detailed description is given in the following embodiments with reference to the accompanying drawings. It should be emphasized that many features are not drawn to scale according to industry standard practice. In fact, the dimensions of the various components may be arbitrarily increased or decreased for clarity of discussion.
The sole FIG. is a cross-sectional view showing a liquid-crystal display device in accordance with some embodiments of the present disclosure.
In the present specification, the term “about” or “approximately” means in a range of 20% of a given value or range, preferably 10%, and more preferably 5%. In the present specification, if there is no specific explanation, a given value or range means an approximate value which may imply the meaning of “about” or “approximately”.
In the present specification, when two or more functional groups using the same code are included in one chemical formula, the two groups may be identical to each other or different from each other. For example, in formula (1), when n1 is 2, two A1 groups may be identical to each other or different from each other, and two Z1 groups may also be identical to each other or different from each other. In other words, the description of “two A1 groups and Z1 groups are independently identical to each other or different from each other” may include all the following cases: (1) the two A1 groups are identical to each other, and the two Z1 groups are identical to each other; (2) the two A1 groups are different from each other, but the two Z1 groups are identical to each other; (3) the two A1 groups are identical to each other, but the two Z1 groups are different from each other; and (4) the two A1 groups are different from each other, and the two Z1 groups are different from each other.
In the present specification, the wavy line is used to indicate the atom to which this functional group is bonded to another functional group. For example, in the functional group,
the leftmost oxygen atom is the atom bonded to another functional group.
In some embodiments of the present disclosure, an additive is provided. The additive can greatly improve the vertical alignment degree, voltage holding ratio, and stability of the alignment ability of the liquid-crystal composition. In the present specification, the term “vertical alignment ability of the additive molecule” means the degree of vertical alignment of liquid-crystal molecules in a liquid-crystal composition when the additive is added to the liquid-crystal composition. More specifically, by adding the additive molecule to the liquid-crystal composition, most liquid-crystal molecules can be vertically aligned well without using a conventional alignment film (for example, a polyimide film). Furthermore, the liquid-crystal display device using the additive has a high voltage holding ratio and excellent performance.
In some embodiments, an additive is provided. The additive includes an additive molecule having a structure represented by formula (I):
and
and at least one of X3, X4, X5 and X6 represents
K2 represents —L4—R5.
In other embodiments, the additive includes an additive molecule having a structure represented by formula (I):
and
and
K2 represents —L4—R5.
The structure represented by formula (I) is substantially a rod-shaped structure. This rod-shaped structure has a first axial direction and a second axial direction. The first axial direction is the long axial direction of the rod-shaped structure, that is, the direction in which the functional group R1 and the functional group K1 are connected. The second axial direction is the short axial direction of the rod-shaped structure, that is, a direction perpendicular to the first axial direction.
In formula (I), at least one of the functional groups X1, X2, X3, X4, X5, and X6 may include an anchoring group. As a result, the additive molecules can be fixed to the substrate (for example, the first substrate 110 or the second substrate 120 shown in the FIG.). The anchoring group may be a functional group having a higher polarity. The anchoring group may generate a bond or a hydrogen bond with a substrate (for example, glass or ITO), and therefore, the additive molecules can be adsorbed (or fixed) on the substrate. For example, the anchoring group may include —OH,
In order to achieve a state in which the liquid-crystal molecules are well aligned vertically, the additive molecules may be fixed on the substrate in such a manner that the first axial direction is perpendicular to the top surface of the substrate. In some embodiments, the anchoring group is one of X1, X2, X3, X4, X5, and X6 that is closest to the right end of the molecule represented by formula (I) such that the first axis is perpendicular to the top surface of the substrate.
In some embodiments, each of the additive molecules has only one anchoring group. Therefore, each of the additive molecules has the same alignment direction on the substrate. In other words, the first axial directions of the different additive molecules are parallel to each other. As a result, the liquid-crystal molecules can be aligned in a uniform state, and defects (for example, local bright spots generated in the dark state) are not easy to generate. In other embodiments, each of the additive molecules has two anchoring groups. Therefore, it is helpful for the immobilization of the additive molecules on the substrate without being easy to detach. As a result, the occurrence of defects can also be reduced. In addition, in order to avoid the polarity of the additive molecules being too high to be dissolved in the liquid-crystal composition, the number of anchoring groups in one additive molecule is at most three.
In the above formula (I), the cyclic functional groups (i.e., A1 and A2) may be an aliphatic ring or an aromatic ring. The cyclic functional group contributes to the alignment of the liquid-crystal molecules. More specifically, the aromatic cyclic functional group may generate a π-π stacking so that the rod-shaped liquid-crystal molecules may be aligned in a specific direction. The aliphatic cyclic functional group can align the rod-shaped liquid-crystal molecules in a specific direction by steric hindrance. In some embodiments, the first axial direction of the additive molecules is perpendicular to the top surface of the substrate, and the long axis of the rod-shaped liquid-crystal molecules is parallel to the first axial direction of the additive molecules. Therefore, the long axis of the rod-shaped liquid-crystal molecules can be made perpendicular to the substrate by the additive molecules. In other words, the vertical alignment of the liquid-crystal molecules can be achieved.
Some negative ions (for example, fluoride ions) may remain in the liquid-crystal composition. These ions can cause residual current and reduce the voltage holding ratio during the operation of the display. More specifically, the higher concentration of the negative ions results in the lower the voltage holding ratio. Silicon atoms are more electron-poor than carbon atoms, and therefore, silicon atoms can attract (or capture) the negative ions in the liquid-crystal composition. As a result, the concentration of the negative ions in the liquid-crystal composition can be lowered, and the voltage holding ratio of the liquid-crystal display device can be increased. In other words, in the molecule represented by formula (I), the silicon atom has the function of increasing the voltage holding ratio. Furthermore, in order to attract the negative ions, the silicon atom in the molecule represented by formula (I) is not directly bonded to the oxygen atom. In addition, because the silicon atom is bonded to the alkyl group, the solubility of the molecule represented by formula (I) in the liquid-crystal composition can also be improved.
In some embodiments, in the above formula (I), at least one of the functional groups X1, X2, X3, X4, X5, and X6 may include a polymerizable group. The polymerizable group may undergo the polymerization reaction with another polymerizable group by irradiation or heating, and the two polymerizable groups may be bonded to each other. When a plurality of additive molecules are fixed on the substrate, the polymerizable group of the additive molecule undergoes the polymerization reaction with the polymerizable group of the adjacent additive molecule. In this way, a plurality of the additive molecules that are perpendicular to the substrate and arranged in parallel with each other can form a network structure. This network structure can avoid the tilt of the additive molecules. As a result, the degree of vertical alignment of the liquid-crystal molecules is further improved, and the stability of the alignment ability is improved. The polymerizable group may include an acrylic group, a methacrylic group, or a derivative thereof. In some embodiments, at least one of the functional groups X1, X2, X3, X4, X5, and X6 is a polymerizable group having the following structure or
and wherein Y1 represents —OH, a C1-C8 alkyl group, or a C2-C8 alkenyl group, and at least one hydrogen atom of the C1-C8 alkyl group or the C2-C8 alkenyl group is substituted by —OH; and Y2 represents hydrogen, halogen, a C1-C8 alkyl group, or a C2-C8 alkenyl group, wherein the C1-C8 alkyl group or the C2-C8 alkenyl group is unsubstituted or at least one hydrogen atom of the C1-C8 alkyl group or the C2-C8 alkenyl group is substituted by a halogen atom.
In other embodiments, the additive includes the first additive molecule, and the first additive molecule has a structure represented by formula (I):
and
and the definitions of Y1 and Y2 are respectively the same as the definitions of Y1 and Y2 defined in this paragraph;
In other embodiments, the additive includes the second additive molecule, and the second additive molecule has a structure represented by formula (I):
and
and the definitions of Y1 and Y2 are respectively the same as the definitions of Y1 and Y2 defined in this paragraph;
Specific exemplary first additive molecules are shown in Table 1 below. Specific exemplary second additive molecules are shown in Table 2 below.
Referring to Table 1, in the first additive molecule, the functional group at the end of the molecular main chain includes a polymerizable group and an anchoring group. Therefore, the first additive molecule can be adsorbed (or fixed) on the substrate in such a manner that the first axial direction is perpendicular to the top surface of the substrate, thereby obtaining good vertical alignment ability. Furthermore, a plurality of first additive molecules that are perpendicular to the substrate and arranged in parallel with each other can form the above-mentioned network structure. This network structure can further improve the degree of vertical alignment of the liquid-crystal molecules and improve the stability of the alignment ability.
Referring to Table 2, in the second additive molecule, the molecular side chain includes at least one polymerizable group. The second additive molecule may form the above-mentioned network structure with the adjacent second additive molecule or the first additive molecule. As a result, the stability of the alignment ability can be improved.
In some embodiments, the additive includes a first additive molecule. Therefore, this additive can have excellent vertical alignment ability and good stability of the alignment ability. In other embodiments, the additive includes a second additive molecule. In still other embodiments, the additive includes a first additive molecule and a second additive molecule. In such embodiments, the first additive molecules may be vertically fixed on the substrate, and the first additive molecules may be bonded to adjacent first additive molecules or second additive molecules to form the above-mentioned network structure. Therefore, this additive can have excellent vertical alignment ability and excellent stability of the alignment ability. In some embodiments, the additive includes a first additive molecule and a second additive molecule, and when the amount of the first additive molecule is set to 1 part by weight, the amount of the second additive molecule is 0.1-60 parts by weight. In other embodiments, when the amount of the first additive molecule is set to 1 part by weight, the amount of the second additive molecule is 0.5-50 parts by weight. In still other embodiments, when the amount of the first additive molecule is set to 1 part by weight, the amount of the second additive molecule is 1-30 parts by weight.
In other embodiments, a liquid-crystal composition is provided. The liquid-crystal composition includes a first component and a second component. The first component includes at least one additive as mentioned above, and the second component includes at least one compound represented by formula (II):
In accordance with some embodiments, the above-mentioned second component includes at least one compound represented by formula (II-1) or formula (II-2):
Because the cyclic group of the compound of formula (II-1) has no fluorine atom, the viscosity of the liquid-crystal composition can be lowered, and the response speed of the liquid-crystal molecules can be improved when a voltage is applied. The compound of formula (II-2) includes at least one phenylene group, and two hydrogen atoms on the same side of this phenylene group are substituted by fluorine atoms. The compound of formula (II-2) can be used to adjust the dielectric anisotropy (Δε) of the liquid-crystal composition.
In accordance with some embodiments, the above-mentioned liquid-crystal composition further includes a third component, and the third component includes at least one compound represented by formula (III), formula (IV), or formula (V):
The compound of the third component includes at least one polymerizable group, and the polymerizable group may include an acrylic group, a methacrylic group, or a derivative thereof. More specifically, each of the compounds represented by formula (IV) and formula (V) has a polymerizable group at one end of the molecule. Each of the compounds represented by formula (III) has a polymerizable group at both ends of the molecule. By irradiation or heating, the polymerizable group of the third component may undergo the polymerization reaction with another polymerizable group of the above-mentioned additive molecules represented by formula (I). In this way, it is helpful to form the above-mentioned network, and the degree of vertical alignment of the liquid-crystal molecules can be further improved.
If the content of the first component is too low, the degree of vertical alignment and the voltage holding ratio of the liquid-crystal composition may not be effectively improved. On the contrary, if the content of the first component is too high, the first component may not dissolve well in the liquid-crystal composition, and it may precipitate. Such a liquid-crystal composition cannot be used. Furthermore, when the first component exceeds the specific content, even if the first component is further increased, the degree of vertical alignment of the liquid-crystal composition cannot be further improved. Furthermore, the first component has the group (for example, an anchoring group) having a relatively high polarity. Therefore, if the content of the first component is too high, the voltage holding ratio of the liquid-crystal composition may be lowered. As described above, in order to balance the degree of vertical alignment and the voltage holding ratio of the liquid-crystal composition, the content of the first component may be controlled within an appropriate range.
In some embodiments, the liquid-crystal composition includes a first component and a second component. In such embodiments, when the total weight of the second component is 100 parts by weight, the first component is 0.01-10 parts by weight. In other embodiments, when the total weight of the second component is 100 parts by weight, the first component is 0.05-5 parts by weight. In still other embodiments, when the total weight of the second component is 100 parts by weight, the first component is 0.1-3 parts by weight.
In some embodiments, the liquid-crystal composition includes a first component, a second component, and a third component. In such embodiments, when the total weight of the second component is 100 parts by weight, the first component is 0.01-10 parts by weight, and the third component is 0.01-10 parts by weight. In other embodiments, when the total weight of the second component is 100 parts by weight, the first component is 0.04-3.5 parts by weight, and the third component is 0.04-3.5 parts by weight. In still other embodiments, when the total weight of the second component is 100 parts by weight, the first component is 0.07-2 parts by weight, and the third component is 0.07-2 parts by weight.
For those skilled in the art, it should be understood that the liquid-crystal composition may further include other components other than the above-mentioned first component, second component, and third component. For example, other conventional liquid-crystal compounds or other additives in appropriate amounts. In some embodiments, the above-mentioned other additives may include, for example, chiral dopants, UV stabilizers, antioxidants, free radical scavengers, nanoparticles, and so on.
In the present disclosure, a liquid-crystal display device using the above-mentioned liquid-crystal composition is also provided. The FIG. is a cross-sectional view showing a liquid-crystal display device 100 in accordance with some embodiments of the present disclosure.
Referring to the FIG., the liquid-crystal display device 100 includes a first substrate 110 and a second substrate 120 disposed opposite to the first substrate 110. The liquid-crystal display device 100 also includes a liquid-crystal layer 130 disposed between the first substrate 110 and the second substrate 120. The first substrate 110 and the second substrate 120 are respectively a conventional thin film transistor substrate and a conventional color filter substrate. In order to simplify the description, the materials, structures, and manufacturing methods of the first substrate 110 and the second substrate 120 will not be described in detail herein.
The liquid-crystal layer 130 of the liquid-crystal display device 100 of the present disclosure uses the above-mentioned liquid-crystal composition, and the liquid-crystal composition includes the additive represented by formula (I). As described above, the additive represented by the formula (I) can greatly improve the degree of vertical alignment, the voltage holding ratio, and the stability of the alignment ability of the liquid-crystal composition. By adding the additive represented by formula (I) to the liquid-crystal composition, the liquid-crystal molecules can be vertically aligned well without using a conventional alignment film. On the other hand, the liquid-crystal display device 100 using the additive of the present disclosure has the advantages of high voltage holding ratio and good durability. The liquid-crystal composition of the present disclosure can be applied to all kinds of liquid-crystal display devices.
In order to further simplify and clarify the foregoing contents and other objects, characteristics, and merits of the present disclosure, a few examples are given to explain the additives and the liquid-crystal compositions of the present disclosure. The chemical structures and contents corresponding to the compounds of the second component and the third component used in the liquid-crystal compositions of the Examples are shown in Table 3 below. The additive molecules of the Examples and the Reference Examples are shown in Table 1, Table 2 (shown above), and Table 4 below.
The synthesis methods of the additive molecules of the Examples and the Reference Examples are described as follows.
Compound 1 (35 g, 89.5 mmol) and anhydrous tetrahydrofuran (550 mL) were placed in a 1000 mL reaction flask and stirred to dissolve. Then, n-butyllithium (2.5 M, solvent: tetrahydrofuran; 39.4 mL, 98.5 mmol) was slowly added to the reaction flask at −78° C., and the reaction was carried out for 1 hour. Next, dimethylchlorosilane (10.16 g, 107.4 mmol) was added to the reaction flask at −78° C., and the reaction was carried out at room temperature (20-30° C.) for 2 hours. After the reaction was completed, dilute hydrochloric acid (1 N, 30 mL) was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 2.
Compound 2 (8.0 g, 21.6 mmol), toluene (60 mL) and platinum-containing catalyst (Pt/C, Pt content: 5 wt %, 0.84 g) were placed in a 250 mL double-necked flask, and nitrogen gas was introduced. Then, diethyl diallylmalonate (5.2 g, 25.6 mmol) was added and heated to 80° C. for 8 hours to carry out the reaction. After the reaction was completed, the platinum-containing catalyst was removed by filtration. Then, an extraction was performed by using toluene and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 3.
Lithium aluminum hydride (LAH, 2.66 g, 70.1 mmol) and anhydrous tetrahydrofuran (160 mL) were placed in a 500 mL reaction flask and stirred to dissolve. Then, Compound 3 (20.0 g, 35.0 mmol) was slowly added to the reaction flask at 0° C., and the reaction was carried out for 1 hour. Next, the reaction was carried out at room temperature (20-30° C.) for 6 hours. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 4.
Compound 4 (2.0 g, 4.1 mmol), methacrylic acid (0.35 g, 4.1 mmol), 4-dimethylaminopyridine (DMAP, 0.25 g, 2.0 mmol), and dichloromethane (100 mL) were placed in a 250 mL reaction flask and stirred to dissolve. Then, N,N′-dicyclohexylcarbodiimide (DCC, 1.0 g, 4.9 mmol) was added to the reaction flask at 0° C., and the reaction was carried out at room temperature (20-30° C.) for 8 hours. After the reaction was completed, water was added. Then, an extraction was performed by using dichloromethane and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 5.
Compound 5 (1.2 g, 2.2 mmol), acrylic acid (0.62 g, 8.7 mmol), 4-dimethylaminopyridine (0.13 g, 1.1 mmol), and dichloromethane (60 mL) were placed in a 250 mL reaction flask and stirred to dissolve. Then, N,N′-dicyclohexylcarbodiimide (0.54 g, 2.6 mmol) was added to the reaction flask at 0° C., and the reaction was carried out at room temperature (20-30° C.) for 8 hours. After the reaction was completed, water was added. Then, an extraction was performed by using dichloromethane and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 6.
Compound 6 (0.6 g, 1.0 mmol), paraformaldehyde (0.24 g, 7.9 mmol), 1,4-diazabicyclo[2.2.2]octane (0.42 g, 3.7 mmol), water (7 mL), and tetrahydrofuran (20 mL) were placed in a 100 mL reaction flask and stirred to dissolve. Then, the reaction was carried out at 70° C. for 8 hours. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain the additive molecule Exp-A1.
The additive molecule Exp-A1 was analyzed by nuclear magnetic resonance spectroscopy, and the obtained spectral information was as follows: 1H NMR (CDCl3, 400 MHz): δ 0.23 (s, 6H), 0.73-0.74 (m, 2H), 0.86-1.43 (m, 25H), 1.72-1.92 (m, 12H), 2.05-2.15 (m, 1H), 2.30-2.50 (m, 2H), 4.09-4.17 (m, 4H), 4.31 (d, J=5.6 Hz, 2H), 5.56 (s, 1H), 5.83 (s, 1H), 6.08 (s, 1H), 6.23 (s, 1H), 7.19 (d, J=8.0 Hz, 2H), 7.40 (d, J=8.0 Hz, 2H).
Compound 4 (5.0 g, 10.3 mmol), acrylic acid (4.1 g, 56.5 mmol), 4-dimethylaminopyridine (1.25 g, 10.3 mmol), and dichloromethane (200 mL) were placed in a 500 mL reaction flask and stirred to dissolve. Then, N,N′-dicyclohexylcarbodiimide (5.1 g, 24.7 mmol) was added to the reaction flask at 0° C., and the reaction was carried out at room temperature (20-30° C.) for 24 hours. After the reaction was completed, water was added. Then, an extraction was performed by using dichloromethane and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain the additive molecule Exp-B2.
The additive molecule Exp-B2 was analyzed by nuclear magnetic resonance spectroscopy, and the obtained spectral information was as follows: 1H NMR (CDCl3, 400 MHz): δ 0.23 (s, 6H), 0.72-0.74 (m, 2H), 0.86-1.44 (m, 26H), 1.72-1.90 (m, 8H), 2.02-2.15 (m, 1H), 2.35-2.45 (m, 1H), 4.08-4.18 (m, 4H), 5.82 (dd, J1=10.4 Hz, J2=1.6 Hz, 2H), 6.10 (dd, J1=17.2 Hz, J2=10.4 Hz, 2H), 6.38 (dd, J=17.2 Hz, J2=1.6 Hz, 2H), 7.19 (d, J=8.0 Hz, 2H), 7.40 (d, J=8.0 Hz, 2H).
The additive molecule Exp-B2 (1.5 g, 2.5 mmol), paraformaldehyde (0.68 g, 22.7 mmol), 1,4-diazabicyclo[2.2.2]octane (1.1 g, 10.0 mmol), water (15 mL), and tetrahydrofuran (30 mL) were placed in a 100 mL reaction flask and stirred to dissolve. Then, the reaction was carried out at 70° C. for 8 hours. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain the additive molecule Exp-A2.
The additive molecule Exp-A2 was analyzed by nuclear magnetic resonance spectroscopy, and the obtained spectral information was as follows: 1H NMR (CDCl3, 400 MHz): δ 0.24 (s, 6H), 0.72-1.43 (m, 30H), 1.72-1.92 (m, 8H), 2.05-2.17 (m, 1H), 2.21-2.32 (m, 2H), 2.36-2.48 (m, 1H), 4.10-4.22 (m, 4H), 4.31 (d, J=5.6 Hz, 2H), 5.84 (s, 2H), 6.23 (s, 2H), 7.19 (d, J=8.0 Hz, 2H), 7.40 (d, J=8.0 Hz, 2H).
Compound 4 (3.0 g, 6.2 mmol), methacrylic acid (2.1 g, 24.7 mmol), 4-dimethylaminopyridine (0.75 g, 6.2 mmol), and dichloromethane (60 mL) were placed in a 250 mL reaction flask and stirred to dissolve. Then, N,N′-dicyclohexylcarbodiimide (3.0 g, 14.7 mmol) was added to the reaction flask at 0° C., and the reaction was carried out at room temperature (20-30° C.) for 24 hours. After the reaction was completed, water was added. Then, an extraction was performed by using dichloromethane and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain the additive molecule Exp-B1.
The additive molecule Exp-B1 was analyzed by nuclear magnetic resonance spectroscopy, and the obtained spectral information was as follows: 1H NMR (CDCl3, 400 MHz): δ 0.24 (s, 6H), 0.73-0.77 (m, 2H), 0.89-1.46 (m, 26H), 1.77-1.95 (m, 14H), 2.11-2.14 (m, 1H), 2.41-2.45 (m, 1H), 4.09-4.19 (m, 4H), 5.57 (s, 2H), 6.10 (s, 2H), 7.19 (d, J=8.0 Hz, 2H), 7.40 (d, J=8.0 Hz, 2H).
Compound 1 (24.7 g, 63.2 mmol) and anhydrous tetrahydrofuran (400 mL) were placed in a 1000 mL reaction flask and stirred to dissolve. Then, n-butyllithium (2.5 M, solvent: tetrahydrofuran; 26.5 mL, 66.2 mmol) was slowly added to the reaction flask at −78° C., and the reaction was carried out for 1 hour. Next, trichloro(methyl)silane (9.0 g, 60.2 mmol) was added to the reaction flask at −78° C., and the reaction was carried out at room temperature (20-30° C.) for 3 hours. Then, allylmagnesium chloride (concentration: 2.0M, solvent: tetrahydrofuran; 63.2 mL, 126.4 mmol) was added, and the mixture was heated (100° C.) to reflux for 8 hours to carry out the reaction. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 7.
Compound 7 (17.0 g, 38.9 mmol) and tetrahydrofuran (550 mL) were placed in a 1000 mL reaction flask and stirred to dissolve. Then, borane-dimethyl sulfide complex (concentration: 2.0M, solvent: tetrahydrofuran; 42.8 mL, 85.6 mmol) was added to the reaction flask at 0° C., and the reaction was carried out for 3 hours. Then, sodium hydroxide (4.2 g, 105.1 mmol) was dissolved in 34 mL of pure water at 0° C. and stirred for 0.5 hour. Then, hydrogen peroxide (30%, 55 mL) was added to the reaction flask at 0° C., and the reaction was carried out at room temperature (20-30° C.) for 5 hours. After the reaction was completed, saturated potassium carbonate aqueous solution was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 8.
Compound 8 (6.0 g, 12.7 mmol), acrylic acid (4.6 g, 63.5 mmol), 4-dimethylaminopyridine (1.5 g, 12.7 mmol), and tetrahydrofuran (120 mL) were placed in a 500 mL reaction flask and stirred to dissolve. Then, N,N′-dicyclohexylcarbodiimide (6.3 g, 30.5 mmol) was added to the reaction flask at 0° C., and the reaction was carried out at room temperature (20-30° C.) for 24 hours. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 9.
Compound 9 (3.0 g, 5.2 mmol), paraformaldehyde (1.4 g, 46.5 mmol), 1,4-diazabicyclo[2.2.2]octane (2.3 g, 20.7 mmol), water (22 mL), and tetrahydrofuran (45 mL) were placed in a 250 mL reaction flask and stirred to dissolve. Then, the reaction was carried out at 70° C. for 24 hours. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain the additive molecule Exp-A3.
The additive molecule Exp-A3 was analyzed by nuclear magnetic resonance spectroscopy, and the obtained spectral information was as follows: 1H NMR (CDCl3, 400 MHz): δ 0.29 (s, 3H), 0.80-1.46 (m, 26H), 1.68-1.92 (m, 12H), 2.33-2.36 (m, 2H), 2.42-2.45 (m, 1H), 4.15 (t, J=6.8 Hz, 4H), 4.34 (d, J=6.4 Hz, 4H), 5.84 (s, 2H), 6.26 (s, 2H), 7.20 (d, J=8.0 Hz, 2H), 7.40 (d, J=8.0 Hz, 2H).
Compound 8 (3.0 g, 6.3 mmol), methacrylic acid (2.2 g, 25.4 mmol), 4-dimethylaminopyridine (0.77 g, 6.3 mmol), and tetrahydrofuran (100 mL) were placed in a 250 mL reaction flask and stirred to dissolve. Then, N,N′-dicyclohexylcarbodiimide (3.1 g, 15.2 mmol) was added to the reaction flask at 0° C., and the reaction was carried out at room temperature (20-30° C.) for 24 hours. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain the additive molecule Exp-B3.
The additive molecule Exp-B3 was analyzed by nuclear magnetic resonance spectroscopy, and the obtained spectral information was as follows: 1H NMR (CDCl3, 400 MHz): δ 0.29 (s, 3H), 0.80-1.46 (m, 26H), 1.66-1.96 (m, 18H), 2.42-2.46 (m, 1H), 4.10 (t, J=6.8 Hz, 4H), 5.56 (s, 2H), 6.10 (s, 2H), 7.20 (d, J=8.0 Hz, 2H), 7.40 (d, J=8.0 Hz, 2H).
Compound 1 (24.2 g, 61.8 mmol) and anhydrous tetrahydrofuran (400 mL) were placed in a 1000 mL reaction flask and stirred to dissolve. Then, n-butyllithium (2.5 M, solvent: tetrahydrofuran; 25.9 mL, 64.7 mmol) was slowly added to the reaction flask at −78° C., and the reaction was carried out for 1 hour. Next, tetrachlorosilane (10.0 g, 58.9 mmol) was added to the reaction flask at −78° C., and the reaction was carried out at room temperature (20-30° C.) for 3 hours. Then, allylmagnesium chloride (concentration: 2.0M, solvent: tetrahydrofuran; 100.0 mL, 200.0 mmol) was added, and the mixture was heated (100° C.) to reflux for 8 hours to carry out the reaction. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 10.
Compound 10 (14.0 g, 30.3 mmol) and tetrahydrofuran (470 mL) were placed in a 1000 mL reaction flask and stirred to dissolve. Then, borane-dimethyl sulfide complex (concentration: 2.0M, solvent: tetrahydrofuran; 53.0 mL, 106.0 mmol) was added to the reaction flask at 0° C., and the reaction was carried out for 3 hours. Then, sodium hydroxide (4.8 g, 121.2 mmol) was dissolved in 42 mL of pure water at 0° C. and stirred for 0.5 hour. Then, hydrogen peroxide (30%, 80 mL) was added to the reaction flask at 0° C., and the reaction was carried out at room temperature (20-30° C.) for 5 hours. After the reaction was completed, saturated potassium carbonate aqueous solution was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, the purificatoin was performed by recrystallization (ethyl acetate/n-hexane) to obtain Compound 11.
Compound 11 (8.0 g, 15.5 mmol), acrylic acid (11.2 g, 155.0 mmol), 4-dimethylaminopyridine (2.8 g, 23.3 mmol), and tetrahydrofuran (190 mL) were placed in a 500 mL reaction flask and stirred to dissolve. Then, N,N′-dicyclohexylcarbodiimide (11.5 g, 55.8 mmol) was added to the reaction flask at 0° C., and the reaction was carried out at room temperature (20-30° C.) for 24 hours. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 12.
Compound 12 (2.2 g, 3.2 mmol), paraformaldehyde (0.9 g, 30.0 mmol), 1,4-diazabicyclo[2.2.2]octane (1.5 g, 13.0 mmol), water (15 mL), and tetrahydrofuran (40 mL) were placed in a 250 mL reaction flask and stirred to dissolve. Then, the reaction was carried out at 70° C. for 48 hours. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain the additive molecule Exp-A4.
The additive molecule Exp-A4 was analyzed by nuclear magnetic resonance spectroscopy, and the obtained spectral information was as follows: 1H NMR (CDCl3, 400 MHz): δ 0.81-1.46 (m, 28H), 1.68-1.95 (m, 14H), 2.44-2.47 (m, 4H), 4.16 (t, J=6.8 Hz, 6H), 4.34 (d, J=6.0 Hz, 6H), 5.85 (s, 3H), 6.26 (s, 3H), 7.21 (d, J=8.0 Hz, 2H), 7.39 (d, J=8.0 Hz, 2H).
Compound 13 (30 g, 91.3 mmol), diisopropylamine (1.3 g, 12.8 mmol), N-bromosuccinimide (NBS, 33.3 g, 187.2 mmol), and dichloromethane (400 mL) were placed in a 1000 mL reaction flask and stirred to dissolve. The reaction was carried out at room temperature (20-30° C.) for 6 hours. After the reaction was completed, water was added. Then, an extraction was performed by using dichloromethane and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 14.
Sodium hydride (NaH, 4.2 g, 173 mmol), dimethylformamide (DMF, 200 mL), and Compound 14 (24.0 g, 49.4 mmol) were placed in a 500 mL double-necked flask and stirred for 30 minutes. Then, iodoethane (23.1 g, 148.1 mmol) was added at 0° C., and the reaction was carried out at 100° C. for 8 hours. After the reaction was completed, water was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 15.
Compound 15 (8.0 g, 15.6 mmol) and anhydrous tetrahydrofuran (100 mL) were placed in a 500 mL reaction flask and stirred to dissolve. Then, n-butyllithium (2.5 M, solvent: tetrahydrofuran; 22.4 mL, 56.0 mmol) was slowly added to the reaction flask at −78° C., and the reaction was carried out for 1 hour. Next, dimethylchlorosilane (5.3 g, 56.0 mmol) was added to the reaction flask at −78° C., and the reaction was carried out at room temperature (20-30° C.) for 2 hours. After the reaction was completed, dilute hydrochloric acid (1 N, 60 mL) was added. Then, an extraction was performed by using ethyl acetate and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain Compound 16.
Compound 16 (1.0 g, 2.1 mmol), toluene (15 mL) and platinum-containing catalyst (Pt/C, Pt content: 5 wt %, 0.2 g) were placed in a 100 mL double-necked flask, and nitrogen gas was introduced. Then, allyl methacrylate (1.1 g, 8.5 mmol) was added and heated to 100° C. for 8 hours to carry out the reaction. After the reaction was completed, the platinum-containing catalyst was removed by filtration. Then, an extraction was performed by using toluene and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain the additive molecule Exp-B4.
The additive molecule Exp-B4 was analyzed by nuclear magnetic resonance spectroscopy, and the obtained spectral information was as follows: 1H NMR (CDCl3, 400 MHz): δ 0.32 (s, 12H), 0.83-1.45 (m, 29H), 1.65-1.96 (m, 18H), 2.39-2.45 (m, 1H), 3.78 (q, J=7.2 Hz, 2H), 4.12 (t, J=6.8 Hz, 4H), 5.55 (s, 2H), 6.11 (s, 2H), 7.26 (s, 2H).
Compound 2 (6.0 g, 16.2 mmol), toluene (50 mL) and platinum-containing catalyst (Pt/C, Pt content: 5 wt %, 0.63 g) were placed in a 250 mL double-necked flask, and nitrogen gas was introduced. Then, allyl methacrylate (3.1 g, 24.3 mmol) was added and heated to 90° C. for 8 hours to carry out the reaction. After the reaction was completed, the platinum-containing catalyst was removed by filtration. Then, an extraction was performed by using toluene and water, and the organic phase was collected. The solvent of the collected organic phase was removed by using a rotary concentrator. Then, column chromatography was performed to obtain the additive molecule Exp-C.
The additive molecule Exp-C was analyzed by nuclear magnetic resonance spectroscopy, and the obtained spectral information was as follows: 1H NMR (CDCl3, 400 MHz): δ 0.24 (s, 6H), 0.74-0.78 (m, 2H), 0.89-1.50 (m, 24H), 1.68-1.95 (m, 11H), 2.42-2.49 (m, 1H), 4.11 (t, J=8.0 Hz, 2H), 5.57 (s, 1H), 6.10 (s, 1H), 7.19 (d, J=8.0 Hz, 2H), 7.40 (d, J=8.0 Hz, 2H).
The additive molecule Ref can be synthesized in accordance with the procedure for synthesizing Compound 15 by using Compound 13 as starting material, and the synthesis step is as shown in the above flow chart.
In the following Examples and Reference Examples, all of the liquid-crystal compositions were prepared by forming the mother liquid formed by 100 parts by weight of the molecules of formula (II) in accordance with Table 3, and then, 0.3 parts by weight of molecule of formula (III) shown in Table 3 was added. Next, the additive molecules shown in Tables 1, 2, and 4 were additionally added to the above liquid-crystal composition in accordance with the amount that was added, shown in Table 5. For example, the liquid-crystal composition of Example 6 is 100 parts by weight of the mother liquid formed by the molecules of formula (II) shown in Table 3, and 0.3 parts by weight of the molecule of formula (III), 0.2 parts by weight of the additive molecule Exp-A2, and 0.5 parts by weight of the additive molecule Exp-B2 is further added. Furthermore, in the liquid-crystal compositions of Reference Example and Examples 1-5 shown in Table 5, only one kind of the additive molecules shown in Tables 1, 2, and 4 was added.
Production of the Liquid-Crystal Display Device
In 100 parts by weight of the mother liquid formed by the molecules of formula (II), 0.3 parts by weight of the molecule of formula (III) shown in Table 3 and the additive molecules shown in Tables 1, 2, and 4 (the amounts that were added are shown in Table 5) were added, and the mixture was uniformly mixed and heated to the clearing point. Then, it was cooled to room temperature to form a liquid-crystal composition of a Reference Example or an Example. The liquid-crystal composition of the Example or the Reference Example is injected between two indium tin oxide (ITO) substrates having an interval of 3.5 μm and having no alignment layer to form the liquid-crystal display element of the Example or the Reference Example, respectively. A DC voltage of 12 V and irradiation of ultraviolet light (peak wavelength: 313 nm) were applied to the liquid-crystal display element to form the liquid-crystal display device of the Example or the Reference Example.
Properties of the Liquid-Crystal Composition
[Vertical Alignment]
The liquid-crystal display device was disposed in a polarizing microscope in which a polarizing element and an analyzer were arranged orthogonally. The element was irradiated with light from below, and the presence or absence of light leakage was observed to judge the vertical alignment. The experimental results of vertical alignment were shown in Table 6.
◯: Light does not pass through any part of the element (the whole piece is uniform and has no light transmission). This result indicates that the device has vertical alignment.
X: Light passes through all parts of the element (the whole piece is uniformly transmitted by light). This result indicates that the device has no vertical alignment.
[Voltage Holding Ratio]
A DC voltage (charge voltage of 5 V, operating frequency of 0.6 Hz) was applied to the liquid-crystal display of the Example or the Reference Example at an ambient temperature of 60° C. The voltage value V2 after the application was released to 1.667 sec was measured by the liquid-crystal physical parameter measuring instrument (product number: ALCT-IV1, manufactured by INSTEC Co., Ltd.). The experimental results of voltage holding ratio were shown in Table 6. The formula for calculating the voltage holding ratio (VHR) of the liquid-crystal display device is as follows:
VHR═(V2/applied voltage value)×100%.
[Stability of the Alignment Ability]
A voltage of 0V to 10V was continuously applied to the liquid-crystal display device, and the light transmittance of the liquid-crystal display device corresponding to different voltages was measured. The light transmittance was recorded every 0.1V, and a graph of voltage versus transmittance was drawn based on the experimental results. The voltage corresponding to a liquid-crystal display device having a transmittance of 1% is defined as V(th,i). Next, a deterioration experiment was performed on the liquid-crystal display device. The steps of the deterioration experiment are as follows. The liquid-crystal display device was placed in an oven (temperature: 60° C.), and a voltage (AC, 10 V) was applied for a duration of 4 days. After the deterioration experiment was performed, the liquid-crystal display device was subjected to the experiment described above, and a graph of voltage versus transmittance was drawn. The voltage corresponding to a liquid-crystal display device having a transmittance of 1% is defined as V(th,f). The AVth value (unit: Volts) of the liquid-crystal display device is calculated according to the following formula. The smaller the absolute value of AVth, the better the stability of the alignment ability of the additive molecules. The experimental results of the AVth value were shown in Table 6.
ΔVth=V(th,f)−V(th,i)
Referring to the Reference Example of Table 6, the Reference Example includes the additive molecule Ref Because the additive molecule Ref does not have the silicon atom and the polymerizable group, the voltage holding ratio of the liquid-crystal composition of the Reference Example is not good. Furthermore, because the additive molecule Ref does not have the polymerizable group, the stability of the vertical alignment ability of the liquid-crystal composition of the Reference Example is not good.
Referring to Examples 1-12 of Table 6, each of Examples 1-12 includes at least one additive molecule represented by formula (I). The results show that the liquid-crystal molecules of Examples 1-12 are all vertically aligned, and the voltage holding ratio (for example, the voltage holding ratio greater than 80%) and the stability of the vertical alignment ability are significantly improved.
Referring to Examples 1-4 of Table 6, each of Examples 1-4 includes one of the first additive molecules, and all of the first additive molecules include both the anchoring group and the polymerizable group. The results show that the liquid-crystal molecules of Examples 1-4 are all vertically aligned. In particular, in Examples 2, 3, and 4, the liquid-crystal molecules can be vertically aligned well in the condition that only a small amount of the additive molecules (for example, the amount that was added is less than 0.5 parts by weight) is added. Accordingly, the first additive molecule can significantly improve the degree of vertical alignment of the liquid-crystal molecules, and can also significantly improve the voltage holding ratio.
Referring to Example 5 of Table 6, Example 5 includes one of the second additive molecules, and the second additive molecule includes two polymerizable groups at the side chain and/or main chain of the molecule. The results show that the liquid-crystal molecules of Example 5 are vertically aligned, and the stability of their alignment ability is excellent. Accordingly, the second additive molecule can significantly improve the degree of stability of the vertical alignment ability of the liquid-crystal molecules.
Referring to Examples 6-9 of Table 6, each of Examples 6-9 includes one of the first additive molecules and one of the second additive molecules, and all of the second additive molecules include two polymerizable groups at the side chain and/or main chain of the molecule. The results show that the liquid-crystal molecules of Examples 6-9 are all vertically aligned, and the stability of their alignment ability is excellent. In particular, in Example 9, the total amount of the first additive molecule and the second additive molecule added is 0.7 parts by weight. In Example 9, the voltage holding ratio is 98.4%, and the A Vth value is −0.022 V. Accordingly, the voltage holding ratio and the stability of the alignment ability can be further improved by simultaneously using the first additive molecule and the second additive molecule.
Referring to Examples 10-12 of Table 6, each of Examples 10-12 includes one of the first additive molecules and the compound represented by formula (V), and the compound represented by formula (V) includes one polymerizable group at the end of the molecule. The results show that the liquid-crystal molecules of Examples 10-12 are all vertically aligned, and the stability of their alignment ability is excellent. In particular, in Example 10, the total amount of the first additive molecule that is added and the compound represented by formula (V) is 0.7 parts by weight. In Example 10, the voltage holding ratio is 98.0%, and the ΔVth value is −0.010 V. In Example 11, the voltage holding ratio is 96.9%, and the ΔVth value is −0.050 V. Accordingly, the voltage holding ratio and the stability of the alignment ability can also be further improved by simultaneously using the first additive molecule and the compound represented by formula (V) having the polymerizable group.
In summary, the additive molecule of the present disclosure can have excellent vertical alignment ability while having a high voltage holding ratio. By adding the above-mentioned additive molecule to the liquid-crystal composition, it is possible to realize a state in which most of the liquid-crystal molecules are vertically aligned well without using a conventional alignment film. In order to balance the voltage holding ratio and the stability of the alignment ability of the liquid-crystal composition, the content of the first additive molecule and/or the second additive molecule may be adjusted. Furthermore, the liquid-crystal display device using the additive molecules of the embodiments of the present disclosure can have a high voltage retention rate (for example, the voltage retention rate greater than 80%) and excellent stability of the alignment ability. As a result, the performance and durability of the liquid-crystal display device can be significantly improved.
Although the disclosure has been described by way of example and in terms of the preferred embodiments, it should be understood that various modifications and similar arrangements (as would be apparent to those skilled in the art) can be made herein without departing from the spirit and scope of the disclosure as defined by the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 108102902 | Jan 2019 | TW | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4748087 | Davidson | May 1988 | A |
| 20190292463 | Yano | Sep 2019 | A1 |
| 20190338190 | Wu | Nov 2019 | A1 |
| 20200087240 | Hosono | Mar 2020 | A1 |
| 20200224098 | Mamiya | Jul 2020 | A1 |
| Number | Date | Country |
|---|---|---|
| DD262865 | Dec 1988 | DE |
| 201807175 | Mar 2018 | TW |
| Entry |
|---|
| English translation of DD262865. (Year: 1988). |
| Office Action issued in corresponding TW application No. 108102902 dated Apr. 20, 2020. |
| Number | Date | Country | |
|---|---|---|---|
| 20200239773 A1 | Jul 2020 | US |