Patent Grant
7091250
The invention relates to an additive for producing a positive active material for lead-acid storage batteries on the basis of finely divided tetrabasic lead sulfate, a method for producing this additive, as well as a method of using the additive for the described purpose.
In the production of lead-acid storage batteries of the art, the positive plates are matured and dried in batches or continuously in so-called maturing and drying chambers after pasting the grids with the positive active material. From the main ingredients in the form of lead oxide, water, and lead sulfate, tribasic (3PbOPbSO4) and/or tetrabasic (4PbOPbSO4) lead sulfates are formed by maturation. Predominantly, the plates are laid in stacks on pallets without being separated. They are less often placed upright on pallets without separation, or hung with external lugs loosely in frames as occurs in the special case of double grids.
For the maturing to a tribasic lead sulfate with crystal sizes less than 10 μm, it is common practice to mature and subsequently dry the plates at about 55° C. over a period of time from 12 to 24 hours. Depending on the type of oxide that is used, as well as the desired residual moisture, drying can take as long as a few days.
For maturing to a tetrabasic lead sulfate, it is common practice to mature the plates in water vapor at a temperature of normally greater than 80° C., and to dry them thereafter in the same way as the plates that are matured to tribasic form. A great disadvantage in the case of such a maturing by the action of water vapor is the development of coarse-crystalline tetrabasic lead sulfate crystals. In this instance, there may be crystal sizes greater than 50 μm.
During the subsequent formation, the matured active material of the positive plates is electrochemically converted to lead dioxide. Along with the increasing crystal size, the conversion of the basic lead sulfates becomes costlier and lengthier. The required amount of electric energy for converting a coarse-crystalline structure is by more than 25% higher than that of a fine-crystalline structure. In this instance, a “fine-crystalline” structure is understood as material of a crystal size less than 10 μm. In the case of a coarse-crystalline structure, crystals greater than 30 μm are present. For a complete formation, it is moreover necessary to include residence times. By applying larger amounts of energy and the necessity of residence times that are to be included, the formation of coarse-crystalline, tetrabasic lead sulfate will as a rule take a substantially longer time.
The maturing into tetrabasic lead sulfates is advantageous in the case of lead-acid storage batteries with antimony-free alloys for the positive grids. Lead-acid storage batteries with antimony-free alloys for the positive grids and positive active materials that are matured into tetrabasic form, exhibit a stable capacity during a cyclical load, and they have a clearly longer service life. Lead-acid storage batteries with antimony-containing alloys of the positive grids are increasingly replaced with antimony-free grids, since these lead-acid storage batteries have moreover a longer shelf life as well as a visibly smaller water consumption.
For this reason, there exists a great interest in methods and possibilities of maturing positive plates into small-crystalline tetrabasic lead sulfates. In the art, two methods stand out:
According to a common production practice, the plates are first matured to become tribasic and dried to advantageously less than 0.5 wt. % residual moisture. Subsequently, a water vapor treatment occurs over several hours at temperatures of normally greater than 80° C. During this phase, the tribasic lead sulfate is converted into tetrabasic lead sulfate. In this process the crystal size remains almost unchanged, provided the moisture does not exceed about 2 wt % during the water vapor treatment of the plates. In the case of too moist plates, a growth to coarse-crystalline tetrabasic lead sulfate will occur. In the case of a properly conducted process, plates with small-crystalline tetrabasic lead sulfate are present after a subsequent, renewed drying process. A great disadvantage of this method lies in the long process time. Moreover, the paste-grid bonding is inferior to the positive plates that are matured in water vapor directly to coarse-crystalline tetrabasic lead sulfate.
In a second known method, previously finely ground tetrabasic lead sulfate is added to the active positive material during the production process. The maturation occurs in the same manner as in the case of the described maturation into coarse-crystalline tetrabasic lead sulfate by the action of water vapor and preferably at temperatures above 80° C. The added, finely ground tetrabasic lead sulfate crystals having a diameter less than 1 μm act as nucleators and allow individual plates a controlled crystal growth to a fine-crystalline tetrabasic crystal structure. Preferably, this method is carried out continuously.
The disadvantage of this method is the necessity of separating the plates, for example, by hanging double plates in spaced relationship or by a climatic diaphragm between individual plates. It is currently common practice in the production of plates for lead-acid storage batteries to stack them, after pasting, without spacers, and to mature them while being stacked. The necessity of singling the plates thus represents a considerable extra expenditure. As a result, it is not possible to use present systems and techniques for the plate production without new, additional devices or considerable modifications. The separation of the plates by spaces therebetween or climatic diaphragms leads to the need of more floor space, thereby reducing the capacity of plates in existing maturing and drying chambers.
It is an object of the invention to eliminate the problems shown with reference to the art, in particular to present a technical proposal that shows, how it is possible to mature plates in stacks to fine-crystalline tetrabasic lead sulfate.
In accordance with the invention, this object is accomplished by an additive for producing the positive active material for lead-acid storage batteries on the basis of finely divided tetrabasic lead sulfate, which is characterized in that it contains a tetrabasic lead sulfate of an average particle size of less than about 3 μm and finely distributed hydrophobic silicic acid for preventing agglomeration of the particles of the tetrabasic lead sulfate.
The use of the additive in accordance with the invention has shown that it will be possible to realize especially satisfactory effects and advantages, when the average particle size of the tetrabasic lead sulfate is in particular less than about 1.5 μm. The range from about 0.2 to about 0.9 μm turns out to be especially advantageous. Going below the value of 0.2 μm would economically bring no advantage. An increasing average particle size will make it necessary to increase the quantity of the additive, so that likewise in this instance, it is necessary to adjust the upper value for economical reasons. Suitably, the average particle size of the finely divided silicic acids ranges from about 10 to about 120 nm, in particular from about 20 to about 80 nm, with the range from about 40 to about 60 nm being especially advantageous. If the value falls below about 10 nm, the desired action of preventing the particles of the tetrabasic lead sulfate from agglomerating will not occur. In individual cases, it would basically be possible to also exceed the value of 120 nm, although the desired effects are best seen within the foregoing range from about 40 to about 60 nm.
If the silicic acid particles are too small, they will result in a wide grain distribution of tetrabasic lead sulfate crystals of different sizes during maturation. With the use of such silicic acids, it is not possible to prevent the formation of tetrabasic lead sulfate crystals with a particle size greater than 10 μm. They will appear in part individually distributed, in part in clusters, and they may reach crystal sizes as are normally found in matured coarse-crystalline plates. Within the foregoing range of the particle size in particular from 20 to 80 nm, and quite particularly from 40 to 60 nm, the agglomeration of the finely ground tetrabasic seed crystals is prevented. Moreover, it is ensured that very homogeneous, fine-crystalline tetrabasic lead sulfate crystal structures develop during the maturation. The end size of the tetrabasic lead sulfate crystals is controlled by the quantity of the added micro sulfate. For economic reasons, it has been found advantageous to determine the quantity such that a fine-crystalline tetrabasic crystal structure is obtained with crystal sizes of a bandwidth from 4 to 10 μm. Such a distribution will need a simple formation. In the case of closed lead-acid storage batteries, a shift toward smaller crystal sizes while increasing the quantity of micro sulfate can be advantageous. Accordingly, the desired effect is controlled by the quantity of added micro sulfate and not by process parameters of a normal proceeding (temperature, moisture, and time).
Within the scope of the invention, the skilled person is not subjected to any significant limitation with respect to the selection of the finely divided hydrophobic silicic acid. In this connection, the term “silicic acid” has the broadest meaning and also includes the so-called “silica gels.” The only, essential additional requirement consists in that in the present system, it must act in a “hydrophobic” way. This applies in particular to “X-amorphous” silicic acids. Accordingly, they are high-polymeric silicic acids, which are insoluble in water. Within the scope of the invention, hydrophobic pyrogenic silicic acids are very suitable. The silicic acids need not exhibit the hydrophobicity per se. Instead, one may also proceed from substances that are per se hydrophilic, and are to undergo hydrophobing. This is easily possible for the person of skill in the art.
As regards a quantity ratio of basic lead sulfate to finely divided hydrophobic silicic acid in the additive of the invention, there exists no critical limitation. Naturally, it is necessary to select the percentage of finely divided hydrophobic silicic acid so high that the desirable effect of preventing the particles of the tetrabasic lead sulfate from agglomerating occurs to a desirable extent. Suitably however, the composition of the additive according to the invention is adjusted such that, when related to the total weight of tetrabasic lead sulfate and finely divided hydrophobic silicic acid, finely divided hydrophobic silicic acid is present from about 0.05 to 20 wt %, in particular about 0.1 to 8 wt. %. In a very particular manner, the range from about 0.1 to 1 wt. % is selected. Below the value of 0.05 wt. % of finely divided hydrophobic silicic acid, the agglomeration is no longer prevented to an adequate extent. At a value of more than 20 wt. %, this desired effect does no longer increase.
According to the method of the present invention, which is described further below, the additive is obtained in the form of an aqueous suspension. The latter is also preferred in the case of possible uses as are described further below. It is likewise possible to dry the obtained aqueous suspensions to a powder, which is produced preferably by spray drying the aqueous suspension. It has turned out advantageous that the aforesaid aqueous suspension, which is added to the intended use without drying, has a solids content from about 10 to 70 wt. %, in particular from about 20 to 50 wt. %. If the aforesaid highest value of 70 wt. % is exceeded, the homogeneous incorporation into the positive active material will become complicated or impossible. However, the evenness or homogeneity of the finished, positive active material is necessary to achieve by maturing a homogeneous grain size distribution of a narrow bandwidth. Hypothetically, the lower limitation of the solids content of the aqueous suspension in accordance with the invention is limited as regards the water content, only by the formulation of the paste.
Furthermore, it is an object of the invention to provide a method of producing the additive according to the invention, as has been described above. This method is characterized in that tetrabasic lead sulfate is wet ground in an aqueous medium down to a particle size of less than about 3 μm, with a finely divided hydrophobic silicic acid of the above-described type being added to the ground or to-be-ground tetrabasic lead sulfate. Preferably, the wet grinding occurs in agitating ball mills, in particular in closed agitating ball mills. The closed agitating ball mills have the advantage that the grinding energy is applied in an optimized way.
In the following, the method of the invention as well as the advantageous uses of the additive according to the invention are described in greater detail, also with respect to achievable advantages.
According to the invention, a suspension, hereafter “micro sulfate” is produced by grinding tetrabasic lead sulfate in an aqueous medium, while adding special, finely divided silicic acid. A commercially available tetrabasic lead sulfate or a tetrabasic lead sulfate obtained from plates matured into tetrabasic form, is ground as basic substance in a wet grinding process, for example, with agitating ball mills, in particular of the closed type, preferably to an average crystal size of less than 1 μm. An essential point in this process is that the parameters as addressed with respect to the “silicic acid” be maintained. Thus, the silicic acid must be finely divided and have a hydrophobic character. Preferred in this connection is the aforesaid pyrogenic silicic acid. This pyrogenic silicic acid has the special advantage that it exhibits a desirable purity, so that no foreign substances interfere with the operation of the lead-acid storage battery. In this connection, it is advantageous that the finely divided hydrophobic silicic acid is added already during the preparation to the tetrabasic lead sulfate that is to be ground. While a subsequent dosage in a suitable metering system is also possible, it leads to an additional economic expenditure and a prolongation of the entire process time.
In the production of lead-acid storage batteries, it is technically advantageous to use as addition to the mixing process of the active positive materials, suspensions that are produced during the grinding process. Thus, it is easily possible to add the suspension to the mixing process by means of a simple metering device. To dry and produce a powder on the suspension is possible and useful in special applications, in particular within the scope of spray drying. Due to the additional expenditure and observation of workmen's protection rules, the production of a powder as compared with the use of an aqueous suspension is in general not to be recommended in view of possible dust exposures.
After adding the suspension obtained in accordance with the invention to the positive active material during the mixing process, in particular fine-crystalline tetrabasic lead sulfate develops during the subsequent maturation in the case of the below-described embodiments. This results in the advantage that existing production lines can be advantageously used without modifications with the use of the additive according to the invention. In this connection, it is preferred to use the above-described additive in the positive active material for the maturing and drying of single and multiple (i.e. non singled) plates in the production of lead-acid storage batteries. In a particularly advantageous manner, maturing of the plates occurs in stacks, lying, standing, or hanging, by the action of water vapor, at a temperature higher than about 60° C., in particular at a temperature from about 80 to 95° C., within approximately one hour. However, it is also possible to obtain good results, when the plates undergo maturing in stacks, lying, standing, or hanging in batch chambers or by the action of vapor at temperatures below about 60° C. and within 12 to 24 hours.
However, the plates can also be matured in a continuous maturing and drying process. Especially good results will be achieved, when the plates are matured in stacks, lying, standing, or hanging, in a continuous maturing and drying process by the action of water vapor within approximately one, hour at about 80 to 95° C. In the described continuous maturing and drying process, it is highly preferred that maturing and drying occur in a multistage process at rising temperatures. In this connection, it has been found especially advantageous that drying at rising temperatures starts at about 50° C., and continues to as high as about 90° C. during approximately 1 to 4 hours, in particular during about 2 to 3 hours.
The excellent dispersibility of the tetrabasic seed crystals in the positive active material by the finely divided silicic acids leads during the maturation to a tetrabasic crystal structure that is characterized by a particularly narrow bandwidth of crystal sizes, and which is very homogeneously composed. This applies to plates that are both stacked and separated during maturation. As a result of the narrow bandwidth of tetrabasic crystal sizes a greater surface is achieved at the same pore volume, or said otherwise, a larger pore volume at the same surface of the tetrabasic crystals. The advantage lies in an increase in the quantity of sulfuric acid that is received in the free pores of the plate. This allows improving the electric power data. For the user of micro sulfate, this results as an economic advantage, in the possibility of saving active positive material with unchanged electric power data of the lead-acid storage batteries.
The use of the teaching according to the invention covers the entire spectrum of current systems engineering and common process sequences. Current pasting lines with downstream stacking systems, as well as all common maturing and drying chambers are usable without modification. Moreover, it is possible to present a continuous maturing and drying technique in a total period of time from about 3 to 4 hours. In all addressed applications, the end product is formed by fine-crystalline tetrabasic lead sulfates with crystal sizes less than 10 μm. The thus-produced plates are also as easy to form as are those produced from tribasic lead sulfates.
| Number | Date | Country | Kind |
|---|---|---|---|
| 102 61 049 | Dec 2002 | DE | national |
| 103 09 842 | Mar 2003 | DE | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4415410 | Reich | Nov 1983 | A |
| 5202196 | Wang et al. | Apr 1993 | A |
| 5252105 | Witherspoon et al. | Oct 1993 | A |
| 20020124388 | Chen et al. | Sep 2002 | A1 |
| 20030175203 | Nitsche et al. | Sep 2003 | A1 |
| Number | Date | Country |
|---|---|---|
| 3 532 697 | Apr 1987 | DE |
| 0 592 028 | Apr 1994 | EP |
| 1 223 627 | Jul 2002 | EP |
| 1235287 | Aug 2002 | EP |
| 2 767 224 | Feb 1999 | FR |
| 1396308 | Jun 1975 | GB |
| 63006743 | Jan 1988 | JP |
| 01200558 | Aug 1989 | JP |
| 05242887 | Sep 1993 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20040121233 A1 | Jun 2004 | US |