Patent Application
20230343977
This application claims under 35 U.S.C. § 119(a) the benefit of and priority to Korean Patent Application No. 10-2022-0051127, filed on Apr. 26, 2022, the entire contents of which are incorporated herein by reference.
The present disclosure relates to an additive for a polymer electrolyte membrane fuel cell, where the additive includes a perovskite compound. The disclosure further relates to a polymer electrolyte membrane fuel cell including such an additive.
The statements in this section merely provide background information related to the present disclosure and may not constitute prior art.
A polymer electrolyte membrane fuel cell (PEMFC) is a device that converts chemical energy into electrical energy. The polymer electrolyte membrane fuel cell includes an anode that is an oxidation electrode, a cathode that is a reduction electrode, and an electrolyte membrane interposed between the anode and the cathode.
A hydrogen oxidation reaction (HOR) and an oxygen reduction reaction (ORR) occur at the anode and the cathode respectively. However, because the rate of the oxygen reduction reaction (ORR) is slower than that of the hydrogen oxidation reaction (HOR), which greatly affects the performance of the fuel cell, many studies are being conducted to increase the reaction rate of the oxygen reduction reaction (ORR).
Meanwhile, the electrolyte membrane includes a perfluorinated sulfonic acid-based polymer such as Nafion. However, the perfluorinated sulfonic acid-based polymer has a detrimental effect on the performance of the fuel cell because moisture retention and hydrogen ion conductivity are lowered in a low-humidity environment. Further, free radicals resulting from hydrogen peroxide (H2O2) produced during the catalytic reaction attack the electrolyte membrane, and deterioration of the electrolyte membrane proceeds much faster under low-humidity conditions compared to humidified environments. In order to remove the free radicals, there is a study of introducing antioxidants such as cerium oxide (CeO2) and the like into the electrolyte membrane. However, antioxidants have problems in that they lower the hydrogen ion conductivity of the electrolyte membrane and cause leaching when the fuel cell is operated for a long time.
An object of the present disclosure is to provide a polymer electrolyte membrane fuel cell having excellent chemical durability and stability.
The objects of the present disclosure are not limited to the object mentioned above. The objects of the present disclosure become clearer from the following description, and are realized by means and combinations thereof described in the claims.
An additive for a polymer electrolyte membrane fuel cell according to one embodiment of the present disclosure may include a perovskite compound represented by Ce(ZrxTi1-x)O3, wherein x satisfies 0<x<1.
The additive may further include a carbon material having a predetermined shape, and the perovskite compound may be deposited on the carbon material.
The carbon material may include a spherical carbon material, a fibrous carbon material, or a combination thereof.
The perovskite compound may have an X-ray diffraction (XRD) peak on the (110) plane, (112) plane, (200) plane, (122) plane, and (220) plane.
The perovskite compound may have a peak at a (110) plane, a peak at a (112) plane, a peak at a (200) plane, a peak at a (122) plane, and a peak at a (220) plane as measured by X-ray diffraction (XRD),
A polymer electrolyte membrane fuel cell according to one embodiment of the present disclosure may include: an electrolyte membrane; a cathode disposed on one surface of the electrolyte membrane; and an anode disposed on the other surface of the electrolyte membrane, wherein the electrolyte membrane, the cathode, the anode, or a combination thereof may include the additive as disclosed herein.
The electrolyte membrane may include 98% by weight to 99.5% by weight of an ionomer and 0.5% by weight to 2% by weight of the additive.
The cathode may include: a catalyst in which an active metal is supported on a support; an ionomer; and the additive as disclosed herein.
A preparation method of an additive for a polymer electrolyte membrane fuel cell according to one embodiment of the present disclosure may include: preparing a starting material including a cerium precursor, a zirconium precursor, and a titanium precursor; spinning the starting material to obtain a product having a predetermined shape; and applying heat and pressure to the product to obtain an additive, wherein the additive may include a perovskite compound represented by Ce(ZrxTi1-x)O3, wherein x satisfies 0<x<1.
The starting material may further include a carbon precursor, wherein the additive may further include a carbon material having a predetermined shape, and the perovskite compound may be deposited on the carbon material.
The additive may be prepared by treating the product at a temperature in a range of 500° C. to 1,000° C. and at a pressure in a range of 200 bar to 760 bar.
According to the present disclosure, a polymer electrolyte membrane fuel cell having excellent chemical durability and stability can be obtained.
The effects of the present disclosure are not limited to the above-mentioned effect. It should be understood that the effects of the present disclosure include all effects that can be inferred from the following description.
In order that the disclosure may be well understood, there will now be described various forms thereof, given by way of example, reference being made to the accompanying drawings, in which:
The above objects, other objects, features, and advantages of the present disclosure are understood through the following embodiments related to the accompanying drawings. However, the present disclosure is not limited to the embodiments described herein and may be embodied in other forms. Rather, the embodiments introduced herein are provided so that the disclosed content may become thorough and complete, and the spirit of the present disclosure may be sufficiently conveyed to those skilled in the art.
In the present specification, terms such as “comprise,” “have,” etc. are intended to designate that a feature, number, step, operation, component, part, or a combination thereof described in the specification exists, but it should be understood that the terms do not preclude the possibility of the existence or addition of one or more other features, numbers, steps, operations, components, parts, or combinations thereof. Further, when a part of a layer, film, region, plate, etc. is said to be “on” other part, this includes not only the case where it is “directly on” the other part but also the case where there is another part in the middle thereof. Conversely, when a part of a layer, film, region, plate, etc. is said to be “under” other part, this includes not only the case where it is “directly under” the other part, but also the case where there is another part in the middle thereof.
Unless otherwise specified, because all numbers, values, and/or expressions expressing quantities of components, reaction conditions, polymer compositions and formulations used in the present specification are approximate values reflecting various uncertainties of the measurement that arise in obtaining these values among others in which these numbers are different, they should be understood as being modified by the term “about” in all cases. Further, when a numerical range is disclosed in this description, such a range is continuous, and includes all values from a minimum value of such a range to a maximum value including the maximum value, unless otherwise indicated. Furthermore, when such a range refers to an integer, all integers including from a minimum value to a maximum value including the maximum value are included, unless otherwise indicated.
The additive may include a carbon material having a predetermined shape and a perovskite compound deposited on the carbon material.
The carbon material may have at least one shape of a spherical shape and a fibrous shape. When a carbon material having a spherical and/or a fibrous shape is added to the cathode 20 and/or the anode 30, the dispersibility of the catalyst may be increased, and pores may be easily formed. Due to this, the speed of mass transfer within the electrode may be increased, and the problems of flooding phenomenon occurred when humidity is high and a drop in moisture retention occurred when humidity is low may be solved.
The perovskite compound may include one represented by Ce(ZrxTi1-x)O3, wherein x may satisfy 0<x<1.
The perovskite compound may increase the reaction rate of the oxygen reduction reaction (ORR) because the compound can be an oxygen reservoir while providing a site for ions to stay as an oxygen vacancy.
Meanwhile, the perovskite compound includes three or more metal elements, and due to different material properties and ionic sizes of the respective metal elements, the perovskite compound has more oxygen vacancies compared to the conventional perovskite material including two metal elements. Accordingly, the perovskite compound may further increase the reaction rate of oxygen reduction reaction (ORR). Further, the self-oxidation reduction ability of the cerium (Ce) element is improved depending on the amount of oxygen vacancies, and thus the antioxidant properties of the additive are improved.
The cerium (Ce) element included in the perovskite compound has self-oxidation reduction properties, and thus serves as a radical scavenger. The zirconium (Zr) element increases chemical stability and hygroscopicity. The titanium (Ti) element may increase mechanical stability and water retention capacity.
The preparation method of the additive according to the present disclosure may include preparing a starting material including a carbon precursor, a cerium precursor, a zirconium precursor, and a titanium precursor; spinning the starting material to obtain a product having a predetermined shape; and applying heat and pressure to the product to obtain the additive.
The carbon precursor is not particularly limited. For example, it may include polyacrylonitrile (PAN).
The cerium precursor is not particularly limited. For example, it may include cerium (III) acetylacetonate.
The zirconium precursor is not particularly limited. For example, it may include titanium (IV) oxyacetylacetonate.
The titanium precursor is not particularly limited. For example, it may include zirconium (IV) acetylacetonate.
The starting material may be prepared by adding the carbon precursor into a solvent, and adding the cerium precursor, the zirconium precursor, and the titanium precursor in appropriate amounts suitably for the desired composition of the perovskite compound.
The solvent is not particularly limited. For example, it may include dimethylformamide (N,N-Dimethylformamide, DMF).
The product having a predetermined shape may be prepared by spinning the starting material. The spinning method is not particularly limited, and the product may be obtained through wet electrospinning. During electrospinning, the product may be formed in a spherical shape, or a linear product may be formed in a spherical shape by pulverizing it under appropriate conditions.
Thereafter, heat and pressure may be applied to the product to synthesize a perovskite compound. Specifically, the additive may be prepared by treating the product at a temperature in a range of 500° C. to 1000° C. and at a pressure in a range of 200 bar to 760 bar under an oxygen-lean airflow. The oxygen-lean airflow may be formed by injecting an inert gas such as nitrogen, argon, or the like, and then sealing a reactor. The method of applying heat and pressure is not particularly limited, but the product may be sealed through, for example, a Swagelok system, and then heat and pressure may be applied thereto.
When the additive according to the present disclosure is applied to the electrolyte membrane 10, the chemical durability and hydrogen ion conductivity of the electrolyte membrane may be increased. Further, when the additive is applied to the cathode 20, the performance of the fuel cell may be improved by increasing the reaction rate of the oxygen reduction reaction (ORR).
The electrolyte membrane 10 may include an ionomer and the additive.
The ionomer may include a perfluorinated sulfonic acid-based polymer such as Nafion.
The electrolyte membrane 10 may include 98% by weight to 99.5% by weight of the ionomer and 0.5% by weight to 2% by weight of the additive.
The cathode 20 may include a catalyst in which an active metal is supported on a support, an ionomer, and the additive as disclosed herein.
The type of the support is not particularly limited, but the support may include, for example, carbon black, carbon nanotube, graphite, graphene, carbon fiber, carbon nanowire, or combinations thereof.
The type of the active metal is not particularly limited, but the active metal may include, for example, noble metals such as platinum (Pt), palladium (Pd), iridium (Ir), and/or ruthenium (Ru). Further, the active metal may further include transition metals such as copper (Cu), cobalt (Co), nickel (Ni), and/or iron (Fe). The active metal may include mixtures of the noble metals and the transition metals, or alloys thereof.
The ionomer may include a perfluorinated sulfonic acid-based polymer such as Nafion.
The anode 30 may include a catalyst in which an active metal is supported on a support, an ionomer, and the additive.
The type of the support is not particularly limited, but the support may include, for example, carbon black, carbon nanotube, graphite, graphene, carbon fiber, carbon nanowire, or combinations thereof.
The type of the active metal is not particularly limited, but the active metal may include, for example, noble metals such as platinum (Pt), palladium (Pd), iridium (Ir), and/or ruthenium (Ru). Further, the active metal may further include transition metals such as copper (Cu), cobalt (Co), nickel (Ni), and/or iron (Fe). The active metal may include mixtures of the noble metals and the transition metals, or alloys thereof.
The ionomer may include a perfluorinated sulfonic acid-based polymer such as Nafion.
Hereinafter, the present disclosure is described in more detail through Examples. However, the following Examples are merely examples to help the understanding of the present disclosure, and the scope of the present disclosure is not limited thereto.
1 g of polyacrylonitrile (PAN), 0.1124 g of cerium (III) acetylacetonate, 0.0749 g of titanium (IV) oxyacetylacetonate, and 0.0140 g of zirconium (IV) acetylacetonate were put into 9 ml of dimethylformamide (DMF) as a solvent to prepare a starting material.
A product was prepared by electrospinning the starting material. An additive was prepared by applying heat and pressure to the product using a Swagelok system. At this time, the internal temperature of the Swagelok system was about 1000° C., the preparation process was carried out at an arbitrary pressure in a range of 200 bar to 760 bar depending on the temperature.
An additive was prepared in the same manner as in Preparation Example except that the zirconium precursor was not put.
Referring to
Nafion, which is an ionomer, was mixed with the additive according to Preparation Example, sonicated for about 1 hour, and then stirred for about 7 hours. In this process, interaction between the sulfonic acid group of Nafion and the perovskite compound of the additive occurs. The amount of the additive was adjusted to 0.5% by weight. After finishing stirring, the resulting product was cast on a glass plate, and the solvent was completely evaporated to obtain an electrolyte membrane.
A fuel cell was manufactured by attaching a cathode and an anode including a catalyst and an ionomer to both surfaces of the electrolyte membrane.
Table 1 below is one obtained by measuring the hydrogen ion conductivity of the electrolyte membrane according to Example.
Table 2 below shows a result of evaluating the performance of the fuel cell according to Example under 80° C. and 100% relative humidity conditions. Table 3 shows a result of evaluating the performance of the fuel cell according to Example under 80° C. and 20% relative humidity conditions. The performance of the fuel cell was conditioned on a catalyst loading amount of 0.5 mg/cm2 for the anode and the cathode respectively under a gas flow condition of H2:O2 of 1:1. Further, the area of the fuel cell was 5 cm2.
As a comparative group, an antioxidant commonly used in a large amount was added instead of the additive according to Preparation Example and evaluated in the same manner.
In Tables 2 and 3, MPD refers to a maximum power density, PD refers to a power density, and MCD refers to a maximum current density.
Referring to Table 1, it can be seen that the electrolyte membrane according to Example exhibits the most excellent hydrogen ion conductivity when the relative humidity is 100%.
Referring to Tables 2 and 3, it can be seen that the performance of the fuel cell according to Example is significantly superior to those of Comparative Examples to which other antioxidants are added.
Table 4 below is one in which the characteristics of the electrolyte membrane according to Example are evaluated.
The electrolyte membrane of Example showed the smallest degree of swelling at the same time as proper moisture control, and this is because the characteristic of dimensional stability was expressed from the perovskite compound.
The oxidation stability is a comparison between the mass of the first electrolyte membrane and the mass of the electrolyte membrane when radicals are made with a Fenton's reagent and reacted with each electrolyte membrane for 12 hours. Example showed the highest oxidative stability while maintaining a weight close to 100% up to about 24 hours beyond 12 hours.
As the Preparation Example and Example of the present disclosure have been described in detail above, the right scope of the present disclosure is not limited to the above-described Preparation Example and Example, and various modifications and improved forms by those skilled in the art using the basic concept of the present disclosure as defined in the following claims are also included in the right scope of the present disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2022-0051127 | Apr 2022 | KR | national |