Patent Grant
11993003
The field of invention relates to multipurpose structural elements. More specifically, the field relates to the manufacture of multifaceted cement structural elements.
Cement is commonly used throughout the world as a building material because of its favorable compressive strength properties and widespread availability. However, conventional cement casting techniques, which generally involve pouring cement into simple molds or forms, limit applications to relatively simple geometric shapes.
Recently, additive manufacturing techniques have enabled the manufacture of more complex cement structures by direct printing (that is, selectively adding small amounts of material layer by layer). However, direct printing with cement requires specially formulated cement compositions that contain additives to cause the cement to gel quickly. Moreover, conventional structures made of cement are brittle and susceptible to catastrophic failure because cement has a relatively high Young's modulus, which results in limited fracture strain and toughness of the cement material.
Methods of making structural elements having controlled mechanical failure characteristics and structural elements having improved mechanical properties are disclosed.
In a first aspect, a process for making a layered multi-material structural element having controlled mechanical failure characteristics is provided. The process includes the steps of: supplying a cementitious layer and forming a polymer layer on the cementitious layer by additive manufacture such that the polymer layer has a first thickness and the cementitious layer has a second thickness; wherein the polymer layer comprises a polymer and the cementitious layer comprises a cementitious material; and allowing the polymer from the polymer layer to suffuse into the cementitious layer for a period of time to obtain a suffused zone in the cementitious layer such that the suffused zone has a third thickness that is less than half the second thickness.
According to at least one embodiment, the process can be repeated to obtain multiple polymer layers and multiple cementitious layers having suffused zones. According to some embodiments, the polymer can be selected from the group consisting of polyvinyl alcohol, polyvinylpyrrolidone, polylactic acid, liquid crystal elastomer, and combinations of the same. According to at least one embodiment, a stimulus can be used to manipulate the suffused zone. For example, the polymer can be a liquid crystal elastomer, and the stimulus can be selected from the group consisting of a temperature change, electric field, magnetic field, radiation, and any combination of the same. According to at least one embodiment, the first thickness can be between 0.05 millimeters (mm) and 10 mm. According to at least one embodiment, the second thickness can be between 0.05 mm and 100 mm. According to at least one embodiment, the polymer can include a conductive material. The conductive material can be selected from the group consisting of carbon fibers, polyaniline fibers, polythiophenes, carbon nanotubes, carbon nanofibers, copper, zinc, aluminum, nickel-aluminum alloys, and combinations of the same. According to at least one embodiment, the layered multi-material structural element includes a conductive material configured to provide a piezo-response to a changing load. According to at least one embodiment, the steps of the process are carried out in a wellbore.
In a second aspect, a process for making a multi-material structural element having controlled mechanical failure characteristics is provided. The process includes the steps of supplying a loaded projecting member and a soluble retaining member on the loaded projecting member, wherein the loaded projecting member comprises a polymer and is loaded with potential mechanical energy, and wherein the soluble retaining member is at least partially soluble in a cement slurry; contacting the soluble retaining member with a cement slurry such that the soluble retaining member is at least partially dissolved and the loaded projecting member is released and projects into the cement slurry to form a released projecting member; and curing the cement slurry such that a suffused zone is formed where the released projecting member contacts the cement slurry polymer to obtain the multi-material structural element having controlled mechanical failure characteristics.
According to at least one embodiment, the loaded projecting member includes a polymer selected from the group consisting of polyvinyl alcohol, polyvinylpyrrolidone, polylactic acid, liquid crystal elastomer, and combinations of the same. According to at least one embodiment, the soluble retaining member includes an alkaline-sensitive polymer. According to at least one embodiment, the soluble retaining member includes a polymer selected from the group consisting of polyvinyl acetate, polyvinyl alcohol, polylactic acid, and combinations of the same. According to at least one embodiment, the soluble retaining member includes a water-sensitive polymer. According to at least one embodiment, the soluble retaining member can have a thickness that is between 1 micrometer (μm) and 20 centimeters (cm).
In a third aspect, a process for making a layered structural element having controlled mechanical failure characteristics is provided. The process includes the steps of forming a sacrificial mold by additive manufacturing, the sacrificial mold having a negative geometric contour that defines a positive geometric void; supplying a cement slurry and filling the positive geometric void of the sacrificial mold with the cement slurry such that the cement slurry contacts the negative geometric contour directly and forms a positive geometric void that fits at least a portion of the negative geometric contour of the sacrificial mold; curing the cement slurry to form a cement-mold composite including the sacrificial mold and a cured cement shape such that a suffused zone is formed where the cement slurry and the cured cement shape meet; and partially dissolving the sacrificial mold from the cement-mold composite such that a portion of the sacrificial mold remains adhered to the cured cement shape and the structural element is obtained.
According to at least one embodiment, the positive geometric void of the structural element can have a shape that includes a Schwarzite structure. According to at least one embodiment, the sacrificial mold can include a water-soluble polymer. According to at least one embodiment, the sacrificial mold includes a polymer selected from the group consisting of polyvinyl alcohol, polyvinylpyrrolidone, polylactic acid, and combinations of the same. According to at least one embodiment, the portion of the sacrificial mold that remains adhered to the cured cement shape has a uniform thickness between 10 and 1,000 μm. According to at least one embodiment, the step of curing the cement slurry includes allowing the cement slurry to cure for a period of time between two hours and seven days. According to at least one embodiment, the step of partially dissolving the sacrificial mold can be carried out using an aqueous solvent.
In a fourth aspect, a layered structural element having improved mechanical properties is provided. The layered structural element includes a cured cement shape; a polymer layer adhered to the cured cement shape; and a geometric shape that includes a Schwarzite structure. The structural element can have controlled mechanical failure characteristics. According to at least one embodiment, the polymer layer can have a uniform thickness between 10 and 1,000 μm. According to at least one embodiment, the polymer layer includes a polymer selected from the group consisting of polyvinyl alcohol, polyvinylpyrrolidone, polylactic acid, and combinations of the same.
The embodiments disclosed here will be understood by the following detailed description, along with the accompanying drawings. The embodiments shown in the figures only illustrate several embodiments of the disclosure. The disclosure admits of other embodiments not shown in the figures and is not limited to the content of the illustrations.
For certain embodiments, many details are provided for a thorough understanding of the various components or steps. In other instances, well-known processes, devices, compositions, and systems are not described in particular detail so that the embodiments are not obscured by detail. Likewise, illustrations of the various embodiments can omit certain features or details so that various embodiments are not obscured.
The drawings provide an illustration of certain embodiments. Other embodiments can be used, and logical changes can be made without departing from the scope of this disclosure. The following detailed description and the embodiments it describes should not be taken in a limiting sense. This disclosure is intended to disclose certain embodiments with the understanding that many other undisclosed changes and modifications can fall within the spirit and scope of the disclosure. The patentable scope is defined by the claims and can include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal language of the claims.
The description can use the phrases “in some embodiments,” “in various embodiments,” “in an embodiment,” “in at least one embodiment,” or “in embodiments,” which can each refer to one or more of the same or different embodiments. Furthermore, the terms “comprising,” “including,” “having,” and the like, as used with respect to embodiments of the present disclosure, are synonymous.
All numbers expressing quantities, percentages or proportions, and other numerical values used in the specification and claims are to be understood as being modified in all instances by the term “about” unless otherwise indicated. The term “about” applies to all numeric values, whether or not explicitly indicated. Values modified by the term “about” can include a deviation of at least ±5% of the given value unless the deviation changes the nature or effect of the value such that it is not operable to achieve its intended purpose.
Ranges can be expressed in this disclosure as from about one particular value and to about another particular value. With these ranges, another embodiment is from the one particular value to the other particular value, along with all combinations within the range. When the range of values is described or referenced in this disclosure, the interval encompasses each intervening value between the upper limit and the lower limit, as well as the upper limit and the lower limit; and includes lesser ranges of the interval subject to any specific exclusion provided.
Unless otherwise defined, all technical and scientific terms used in this specification and the appended claims have the same meanings as commonly understood by one of ordinary skill in the relevant art.
Where a method comprising two or more defined steps is recited or referenced in this disclosure or the appended claims, the defined steps can be carried out in any order or simultaneously except where the context excludes that possibility.
As used in this disclosure, the term “suffused zone” is defined as the region that is bounded by 100% cementitious material in cementitious layers or shapes and 100% polymer material in polymer layers, with a varying combination of cementitious material and polymer between the boundaries. The thickness of a suffused zone is the average thickness between these boundaries. A suffused zone can be formed by the suffusion of polymer into cement, cement into polymer, or both.
The methods disclosed here involve using additive manufacturing to form layered multi-material structural elements having controlled failure characteristics. The layered multi-material structural elements can include equilibrium suffused zones, and in some embodiments controlled suffused zones. The suffused zones can increase toughness, improve damping, distribute the load from an impact more evenly through the structure to prevent failure, and introduce controlled failure characteristics to the structural elements. According to at least one embodiment, the suffused zones can be controlled, manipulated, or augmented using a stimulus (e.g., temperature change, electric field, magnetic field, etc.). Advantageously, the methods disclosed here can be used to manufacture structures in a wellbore such that the structures have controlled failure characteristics and improved mechanical characteristics such as toughness.
The polymer layers 110, cementitious layers 120, and suffused zones 125 have first thickness D1, second thickness D2, and fourth thickness D4, respectively. The first thickness D1 and second thickness D2 can be determined by the resolution and capabilities of the printer used to manufacture the layers. According to at least one embodiment, first thickness D1 can be less than second thickness D2. According to at least one embodiment, second thickness D2 can be less than first thickness D1. According to at least one embodiment, first thickness D1 can be between about 0.01 millimeters (mm) and about 10 mm, preferably between about 0.05 mm and about 5 (mm), more preferably between about 0.05 mm and about 2 mm, even more preferably between about 0.05 mm and about 1 mm. According to at least one embodiment, the polymer layer can have first thickness D1 that is about 500 μm.
The second thickness D2 can be determined by the material characteristics, and the resolution and capabilities of the printer, techniques, or both used to manufacture the layers. According to at least one embodiment, second thickness D2 can be between about 0.02 mm and about 100 mm, preferably between about 0.1 mm and about 40 mm, more preferably between about 0.1 mm and about 20 mm, even more preferably between about 0.1 mm and about 10 mm. The magnitude of the second thickness D2 can be between about 1 and 10 times the magnitude of the first thickness D1.
According to at least one embodiment, fourth thickness D4 is between about 0.01 and about 0.75 of second thickness D2, preferably between about 0.05 and less than about 0.5 of second thickness D2, more preferably between about 0.1 and about 0.3 of second thickness D2.
According to at least one embodiment, the polymer layers 110 can be discrete layers of polymeric material. The presence of a discrete layer of polymeric material in the structural element can provide the structural element with improved damping characteristics. According to at least one embodiment, the cement layer can be positioned between at least two of the polymer layers 110 and can have at least two corresponding suffused zones 125. The multi-material structural element 100 can include multiple layers alternating between polymer layers 110 and cementitious layers 120; each cementitious layer 120 positioned between two or more polymer layers 110 having at least two suffused zones 125. According to at least one embodiment, the polymer of the suffused zones 125 does not suffuse completely through the cementitious layer 120, such that there exists a region of 100% cementitious material. Designing the structural element so that the cementitious layers 120 have a region of 100% cementitious material has certain advantages, such as conserving the polymer.
According to at least one embodiment, the thickness of the suffused zones 125 can be minimized to allow for slip planes, or a region of relatively weak adhesion between the cementitious layer 120 and the polymer layer 110. Slip planes can be designed in the layered multi-material structural element 100 to help absorb impacts and mechanical shocks. Another method of regulating slippage between the cementitious layer 120 and the polymer layer 110 involves chemically modifying the polymer or selecting a polymer on the basis of its affinity for the cementitious material. In addition to influencing the degree of slippage between layers, a polymer's affinity for the cementitious material can affect the transfer of mechanical energy from one layer to the next; without being limited by theory, a polymer with a greater affinity for the cementitious material would likely result in increased transfer and decreased absorption of mechanical energy from one layer to the next, and a polymer with a lesser affinity for the cementitious material would likely result in decreased transfer and increased absorption of mechanical energy.
The polymer layers 110 and the cementitious layers 120 of the layered multi-material structural element 100 can be manufactured using additive manufacturing techniques. Additive manufacturing, also known as three-dimensional printing, involves using digital three-dimensional model data (such as computer-aided design data) to build up objects by depositing material. Fused deposition modeling is an additive manufacturing process that involves ejecting a thermoplastic material from a temperature-controlled nozzle to form an object layer by layer. Presently, commercial additive manufacturing printers are capable of a resolution of about 10 micrometers (μm) in the x-y Cartesian plane, and about 20 μm in the direction of the Cartesian z-axis using fused deposition modeling. Accordingly, commercial additive manufacturing printers are capable of printing detailed and relatively complex shapes.
Referring to
Referring now to
According to at least one embodiment, the equilibrium suffusion of polymer material into the cementitious material of cementitious layer 320 (or vice versa) can be carried out without an external stimulus. That is, unassisted suffusion is carried out to equilibrium resulting in an equilibrium suffused zone 315 having a third thickness D3. Step 3B shows equilibrium suffused zone 315 having third thickness D3. According to at least one embodiment, the polymer and cementitious material are allowed to cure to obtain a layered multi-material structural element 3200, having an equilibrium suffused zone 315.
Step 3C shows a stimulus 380 being used to manipulate suffusion of the polymer or cementitious material to obtain a controlled suffused zone 325. Depending on the type of stimulation, the stimulus can be provided before, during, or after the polymer cures. The stimulus 380 can be any stimulus capable of altering the suffusion of the polymer or cementitious material. Nonlimiting examples of suitable stimuli include those capable of producing a temperature change, electric field, magnetic field, radiation, or any combination of the same. For materials that do not include particulates that obscure or scatter light the way many cementitious materials do, the stimulus can be ultraviolet, visible, or near-infrared light. According to at least one embodiment, the polymer material can include a liquid crystal elastomer that is sensitive to changes in temperature, and the stimulus 380 can be heat provided by a heat source, so that heat causes the liquid crystal elastomer to suffuse further into the cementitious layer 320. Once the desired suffusion has been carried out, the equilibrium suffused zone 315 can have a fourth thickness D4 that is different from third thickness D3. According to at least one embodiment, the fourth thickness D4 is greater than third thickness D3. The difference between D3 and D4 will depend on the materials, stimulus, and geometry used. According to at least one embodiment, the difference between D3 and D4 can be between about 1 nanometer (nm) and 100 centimeters (cm), alternately between about 1 nm and about 50 cm, alternately between about 1 nm and 20 cm, alternately between about 1 nm and about 10 cm, alternately between about 1 nm and about 5 cm, alternately between about 1 nm and about 1 cm, alternately between about 1 micrometer (μm) and 100 cm, alternately between about 1 μm and 50 cm, alternately between about 1 μm and about 20 cm, alternately between about 1 μm and about 10 cm, alternately between about 1 μm and 5 cm, alternately between about 1 μm and 1 cm, alternately between about 1 mm and 100 cm, alternately between about 1 mm and 50 cm, alternately between about 1 mm and 20 cm, alternately between about 1 mm and 10 cm, alternately between about 1 mm and 5 cm, alternately between about 1 cm and 100 cm, alternately between about 1 and 50 cm, alternately between about 1 and 20 cm, alternately between about 1 and 10 cm, alternately between about 1 and 5 cm. The structural element obtained by this process is referred to in this disclosure as a layered multi-material structural element 3300 having a controlled suffused zone 325.
Conventional methods for casting cement structural elements typically involve pouring cement into simple molds or forms. Shapes having inner surfaces are particularly difficult to achieve using conventional techniques, sometimes requiring complex mold assemblies with multiple parts or casting multiple simple cement structural elements and assembling them after they have cured. Direct printing with cement enables the manufacture of more complex structures, but generally requires special additives that cause the cement to gel quickly. Also disclosed are methods that involve using additive manufacturing to form sacrificial molds for casting complex shapes, such as Schwarzite structures, having suffused zones. Sacrificial molds made from a polymer can be partially (that is, incompletely) dissolved after curing such that a layer of polymer remains on the surface of the cured cement shape. According to at least one embodiment, the layer of polymer that remains on the surface of the cured cement shape can facilitate the formation of suffused zones in the cured cement shape.
Advantageously, structural elements having a Schwarzite structure made by the disclosed method demonstrate controlled failure characteristics. Compared to conventional cement blocks, which fail suddenly and catastrophically, structural elements having a Schwarzite structure generally incrementally fail in stages as compressive stress increases. In addition to failing incrementally in stages, structural elements having a Schwarzite structure demonstrate moderate damping behavior. It has also been found that structural elements made according to certain embodiments disclosed have greater toughness and deformation recovery after unloading than conventional cement blocks. Moreover, structural elements having a Schwarzite structure require less cement material than conventional solid cement blocks.
Schwarzite structures are three-dimensional porous structures having periodic Schwarzite unit shapes, the periodic Schwarzite unit shapes having a negatively curved surface. In at least one embodiment, the Schwarzite structure can have a primitive structure, which includes two intertwined congruent networks of passages, each having a shape that resembles an inflated tubular version of a simple cubic lattice. In at least one embodiment, the Schwarzite structure can have a gyroid structure, which is an embedded member of the Schwarz family that includes an infinitely integrated triply periodic minimal surface in the absence of straight lines and reflectional symmetries. By way of example and not limitation, an example of a layered multi-material structural element 100 having a primitive Schwarzite structure is shown in
The method of making a structural element having controlled mechanical failure characteristics includes manufacturing a sacrificial mold by additive manufacture. According to at least one embodiment, the sacrificial mold is manufactured by additive manufacturing that includes fused deposition modeling with a polymer.
By way of example and not limitation,
According to at least one embodiment, the sacrificial mold can be manufactured from a polymer using fused deposition modeling. The polymer can be soluble in a solvent. The type of polymer depends on the type of solvent that is used to dissolve the polymer, and vice versa. In at least one embodiment, the solvent can be an aqueous solvent. By way of example and not limitation, the polymer can be a water-soluble polymer such as polyvinyl alcohol, polyvinylpyrrolidone, polylactic acid, etc. Polyvinyl alcohol is particularly suitable for use with an aqueous solvent because it is relatively hydrophilic and soluble in water. One of ordinary skill will understand that some additive manufacturing printers are capable of printing multiple materials (such as metals, ceramics, powders, carbon fibers, etc.). It is contemplated that a sacrificial mold may include a polymer and at least one other material. In such embodiments, the polymer should define the negative geometric contour of the sacrificial mold such that the cement slurry contacts the polymer when it is poured into the sacrificial mold.
A method of making a structural element having controlled mechanical failure characteristics includes supplying a cement slurry. The cement slurry can be prepared using conventional techniques known to a person of ordinary skill in the art. The type of cement used to prepare the cement slurry is not particularly limited. By way of example and not limitation, an example of a suitable cement is Portland cement.
Once the sacrificial mold is formed, the cement slurry can be introduced to the sacrificial mold such that the cement slurry contacts the negative geometric contour of the sacrificial mold and fills the positive geometric void. According to at least one embodiment, a pressure differential across the cement slurry can be used to draw the cement slurry into the positive geometric void. By way of example and not limitation, an at least partial vacuum can be formed in the positive geometric void using a vacuum pump to pull the cement slurry into the positive geometric void, pressure outside of the positive geometric void can be increased to push the cement slurry into the positive geometric void, or both. The sacrificial mold can also be shaken or vibrated to cause the cement slurry to settle into spaces in the positive geometric void.
The cement slurry is cured for a period of time after being introduced to the sacrificial mold to obtain a cement-mold composite that includes the sacrificial mold and a cured cement shape. In the process of curing the cement shape, cement slurry can suffuse into the polymer of the sacrificial mold to form suffused zones. According to at least one embodiment, the curing process can be carried out at ambient temperature for a period of time that is between about 2 hours and 7 days. The cured cement shape can have any structural shape. According to at least one embodiment, the cured cement shape can have a honeycomb structure (that is, a pattern with identical periodic repeating hexagonal units having shared sides). According to at least one embodiment, the cured cement shape can have a Schwarzite structure. According to at least one embodiment, a stimulus can be used to manipulate or control suffusion of the cement slurry into the polymer of the sacrificial mold.
After the cement-mold composite is obtained, it can be treated with a solvent to partially (that is, incompletely) dissolve the mold from the cement-mold composite such that a portion of the sacrificial mold remains adhered to the cured cement shape and the structural element is obtained. The cement-mold composite can be exposed to a solvent for a period of time to partially dissolve the sacrificial mold. In some embodiments, the cement-mold composite includes a polymer, such as polyvinyl alcohol, that suffuses into curing cement such that the portion of the polymer that suffuses is fused with the cement and remains adhered to the cement when exposed to a solvent and the bulk of the polymer is dissolved. According to at least one embodiment, an elastomer can be used to make the sacrificial mold. According to at least one embodiment, a liquid crystal elastomer can be used to make the sacrificial mold or a component of the sacrificial mold. In some embodiments, the degree of dissolution of the sacrificial mold can be controlled by varying the amount of time that the sacrificial mold is exposed to the solvent, varying the temperature of the solvent, varying the pH of the solvent, varying the thickness of layers of polymer during printing, or any combination of the same.
By way of example and not limitation, a cement-mold composite having a sacrificial mold that includes a water-soluble polymer can be immersed in water for a period of time to dissolve the water-soluble polymer and the bulk of the sacrificial mold, and then removed from the water before the sacrificial mold is completely dissolved such that a layer of the water-soluble polymer remains adhered to the cured cement shape. The process of partially dissolving the sacrificial polymer can include heating the solvent. According to at least one embodiment, a sacrificial mold that includes polyvinyl alcohol can be partially dissolved by soaking the cement-mold composite in warm water (that is, water having a temperature between about 40° C. and 90° C.) for a period of time that is between about 12 hours and 96 hours.
The remaining portion of the sacrificial mold can be firmly adhered to the cured cement shape. According to at least one embodiment, the remaining portion of the sacrificial mold can be a substantially uniform layer of polymer having average thickness between about 1 μm and 1,000 μm. Advantageously, the remaining portion of the sacrificial mold improves the mechanical resilience of the structural element. For example, the remaining portion of the sacrificial mold can increase toughness and improve the damping ability of the structural element.
Like the cured cement shape, the structural element can have any three-dimensional geometric shape. According to at least one embodiment, the structural element can have a honeycomb shape with periodic repeating units. According to at least one embodiment, the structural element can have a Schwarzite structure. In at least one embodiment, the Schwarzite structure can have periodic repeating units arranged in horizontal layers and vertical columns.
Structural elements having a Schwarzite structure (including both primitive and gyroid Schwarzite structures) can have controlled failure characteristics. Failure in structural elements having controlled failure characteristics occurs incrementally in stages. By way of example and not limitation, an increasing uniaxial compressive load in the vertical direction on a structural element having a Schwarzite structure with multiple rows and columns can cause fractures to substantially propagate through successive rows of unit shapes in the horizontal direction, rather than randomly. Compared with cement blocks and honeycomb structures, which fracture randomly and catastrophically, the structural element under a uniaxial compressive load in the vertical direction fails in a controlled manner, row-by-row, or layer-by-layer, with fractures propagating horizontally.
Referring to
As shown in step 6D, a stimulus 680 can be used to manipulate or augment suffusion of the polymer into the cement shape 620 to obtain a controlled suffused zone 625. The process of manipulating or augmenting the suffused zone can be carried out using the methods and techniques described previously for obtaining a controlled suffused zone in a layered multi-material structural element. According to at least one embodiment, the polymer material can include a liquid crystal elastomer that is sensitive to changes in temperature, and the stimulus 680 can be heat provided by a heat source, so that heat causes the liquid crystal elastomer to suffuse further into the cement shape 620. Once the desired polymer suffusion has been carried out, the equilibrium suffused zone 615 can have a seventh thickness D7 that is not equal to sixth thickness D6. According to at least one embodiment, the seventh thickness D7 is greater than sixth thickness D6. The difference between D7 and D6 will depend on the materials, geometry, and stimulus used. According to at least one embodiment, the difference between D7 and D6 can be between about 1 nanometer (nm) and 100 cm, alternately between about 1 nm and about 50 cm, alternately between about 1 nm and 20 cm, alternately between about 1 nm and about 10 cm, alternately between about 1 nm and about 5 cm, alternately between about 1 nm and about 1 cm, alternately between about 1 micrometer (μm) and 100 cm, alternately between about 1 μm and 50 cm, alternately between about 1 μm and about 20 cm, alternately between about 1 μm and about 10 cm, alternately between about 1 μm and 5 cm, alternately between about 1 μm and 1 cm, alternately between about 1 mm and 100 cm, alternately between about 1 mm and 50 cm, alternately between about 1 mm and 20 cm, alternately between about 1 mm and 10 cm, alternately between about 1 mm and 5 cm, alternately between about 1 cm and 100 cm, alternately between about 1 and 50 cm, alternately between about 1 and 20 cm, alternately between about 1 and 10 cm, alternately between about 1 and 5 cm. The structural element obtained by this process is referred to in this disclosure as a layered multi-material structural element 6400 having a controlled suffused zone 625.
In
The soluble retaining member 720 can be dissolved by a variety of suitable mechanisms. For example, the soluble retaining member 720 can be made of a polymer that is sensitive to alkaline (i.e., pH greater than 7) conditions such as those found in cement slurry. Nonlimiting examples of alkaline-sensitive polymers include polyvinyl acetate polymer, polyvinyl alcohol, polylactic acid, and combinations of the same. Another example could include using a water-soluble polymer to make at least a portion of the soluble retaining member 720. In another embodiment, the soluble retaining member 720 can be made of a heat-sensitive polymer, and can be actuated by subjecting the soluble retaining member 720 to a thermal load. According to at least one embodiment, the soluble retaining member 720 is a layer of polymer. The layer can have a thickness that is sufficient to retain the loaded projecting member 710 but is thin enough to dissolve, or at least partially dissolve, before the cementitious material or cement slurry 750 cures so that the loaded projecting member 710 can be released and project into the cementitious material or cement slurry 750. In some embodiments, the soluble retaining member 720 includes a layer of polymer having a thickness that is between about 1 μm and 20 cm, alternately between about 1 μm and 10 cm, alternately between about 1 μm and about 3 cm, alternately between about 100 μm and 3 cm, alternately between about 500 μm and 3 cm, alternately between about 1 mm and about 3 cm.
The loaded projecting member 710 can be designed to project into the cementitious material or cement slurry 750 upon its release and before the cementitious material or cement slurry 750 has cured. According to at least one embodiment, the loaded projecting member 710 can be made using a polymer such as polyvinyl alcohol, polyvinyl acetate, polyvinylpyrrolidone, polylactic acid, liquid crystal elastomers, etc. According to at least one embodiment, the cementitious material or cement slurry 750 and the released projecting member 740 can form a suffused zone where they contact each other as described previously so that a multi-material structural element having controlled failure characteristics is obtained.
In
The inert retaining member 830 can be made of any material suitable for retaining the loaded projecting member 840 in the presence of the cementitious material or cement slurry 850. According to at least one embodiment, the inert retaining member includes a polymer that is neither readily soluble in water, nor sensitive to alkaline conditions. That is, the polymer does not dissolve sufficiently to release the loaded projecting member 840 before the cementitious material or cement slurry 850 cures.
Suffused zones can be formed where the cementitious material or cement slurry 850 contacts the released projecting member 840, the inert retaining member 830, or both as described previously so that a multi-material structural element having controlled failure characteristics is obtained.
According to at least one embodiment, the multi-material structural elements of this disclosure can include one or more layers of conductive materials. The one or more layers of conductive materials can be used to improve to provide structural reinforcement and to sense changing load through the materials by a piezoresponse. Suitable conductive materials can include carbon fibers, polyaniline fibers, polythiophenes, carbon nanotubes, carbon nanofibers, or similar materials, and combinations of the same; as well as metals such as copper, zinc, aluminum, nickel-aluminum alloys, or similar materials, and combinations of the same. The conductive materials can be applied so that there is a continuous conductive path through the multi-material structural element. As the load on a given conductive material layer changes, conductivity through the conductive material layer also changes. The difference in conductivity through the conductive material layer can be measured and correlated with the changing load so that a load measurement can be obtained.
Efficient embedded antennas are needed to assist with wireless monitoring of structural integrity and identification of radio frequencies. According to at least one embodiment, alternating layers of conductive materials can be manufactured into the multi-material structural elements of this disclosure to be used as an antenna, electrical circuit, capacitor, or battery. Conducting materials can also be used in the multi-material structural elements of this disclosure to reduce the shielding effectiveness of the concrete or cement material in the multi-material structural element. Generally, cement structures do not enable good propagation of wireless signals within, and in and out of the structures. Poor propagation of wireless signals affects antennas in air as well as antennas embedded in the structures. To address this problem, nanomaterials can be dispersed in the printed cement along with the design of embedded antenna. Nanomaterials such as those used to make an antenna can be mixed into the cement material or cement slurry. Alternatively, an antenna can be printed in using a material that includes a polymeric substance with the nanomaterial blended in as a conductive filler.
The following examples are included to demonstrate embodiments of the disclosure, and should be considered nonlimiting. The techniques and compositions disclosed in the examples which follow represent techniques and compositions discovered to function well in the practice of the disclosure, and thus can be considered to constitute modes for its practice. However, changes can be made to the embodiments disclosed in the examples without departing from the spirit and scope of the disclosure.
An example of a process of making a layered multi-material structural element is provided. Alternating layers of polyvinyl alcohol and Portland cement were manufactured using direct ink writing additive manufacturing technology; each polyvinyl alcohol layer having a uniform thickness of 0.5 mm and each layer of cement being formed by four deposited layers of cement having uniform thickness of 0.5 mm each for a total thickness of 2 mm. Class G Portland cement was used as the cement material, and each layer was printed at 30 minutes per layer. Suffused zones were formed in the cement and polymer layers as the structural element cured in the absence of an external stimulus. The suffused zone was realized thermally using ambient heat, or the heat of hydration of the cement slurry as it set, and was estimated to be 10 nm thick.
The layered multi-material structural element prepared and described in Example 1 was analyzed and compared with a reference element. The reference element was prepared using direct ink writing additive manufacturing technology to successive layers of cement in the absence of a polymer. The cement used to prepare the reference element was the same type of cement used to prepare the layered multi-material structural element of Example 1. The reference element was allowed to cure for a period of time.
The layered multi-material structural element and the reference element were each subjected to a uniaxial compressive load to observe the quasi-static mechanical characteristics of the samples. The specific energy absorption was calculated from measurements of the mass and energy absorption of each sample. Fracture strain and compressive strain measurements were also recorded, and photographs were taken as the compressive load increased.
A low-velocity impact test was carried out using a layered multi-material structural element as prepared in Example 1 and a reference element prepared using the same method described previously. The samples were subjected to force from an impact resulting from a hemispherical impactor having the same weight dropped from the same height. Photographs of the samples were taken before and after the impact, and deformation of the samples was compared.
An example is provided for making a structural element having a Schwarzite structure and controlled mechanical characteristics. A one-piece sacrificial mold was printed by fused deposition modeling using polyvinyl alcohol and a printer having a resolution of about 10 μm in the x-y Cartesian plane, and about 20 μm in the direction of the Cartesian z-axis. The one-piece sacrificial mold had a negative geometric contour that defined a positive geometric void in the shape of a primitive Schwarzite structure having three rows and two columns of repeating unit shapes. A cement slurry was prepared using Portland cement, and poured into the one-piece sacrificial mold to fill the positive geometric void and obtain a cement-mold composite. A vacuum pump was used to create suction a lower portion of the one-piece sacrificial mold as it was filled to assist with evenly distributing the cement slurry and filling voids. The cement slurry was allowed to cure at room temperature for about three days.
After curing, the cement-mold composite was washed with water to remove a portion of the one-piece sacrificial mold, leaving a thin layer (between about 10 μm and about 1,000 μm thick) of polymer from the one-piece sacrificial mold adhered to the cement shape, and then dried in a vacuum oven for a period of time. The thin layer of polymer adhered to the cement shape was found to be fused with the cement matrix. Washing with hot water (about 70° C.), and annealing at about 90° C. had no discernible effect on the thin layer of polymer.
In order to correlate the macroscopic deformation in the structural element with mechanical properties of the microscopic regions, nanoindentation studies on the developed Schwarzite structure were carried out.
The structural element prepared and described in Example 3 was analyzed and compared with a structural element having a honeycomb structure and a reference element (i.e., cement block). The reference element and structural element having a honeycomb structure were prepared from the same Portland cement slurry used in Example 3. The cement block sample was prepared using conventional casting techniques, and the structural element having a honeycomb structure was cast using the techniques described in Example 3; only the negative geometric contour and positive geometric void of the sacrificial mold, and the resulting cement shape, had a honeycomb geometric shape.
The three samples were subjected to a uniaxial compressive load, and the specific energy absorption was calculated from measurements of the mass and energy absorption of each sample. Fracture strain and compressive strain measurements were also recorded, and photographs were taken as the compressive load increased.
As shown in
Photographs showing the cement block sample, structural element having a honeycomb structure, and the structural element having a Schwarzite structure under uniaxial compressive stress are shown in
In
In
The structural element of
Notably, both the structural element having a Schwarzite structure and the structural element having a honeycomb structure achieved greater strain than the cement block sample (that is, about 35, 8, and 2.5 ε % respectively).
A multi-material structural element made of cement and graphite, and having a built-in antenna, was developed by depositing layer-by-layer using additive manufacturing. The direct ink writing (DIW) technique was used to print conductive ink (graphite) between cement layers as shown in
The present application is a divisional application of U.S. patent application Ser. No. 16/874,449, filed on May 14, 2020, the entire disclosure of which is incorporated here by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 7455805 | Oriakhi et al. | Nov 2008 | B2 |
| 9388078 | Rael | Jul 2016 | B2 |
| 9902108 | Wurmfeld | Feb 2018 | B1 |
| 20070138678 | Khoshnevis | Jun 2007 | A1 |
| 20080029685 | West | Feb 2008 | A1 |
| 20140291886 | Mark et al. | Oct 2014 | A1 |
| 20150001761 | Bratton et al. | Jan 2015 | A1 |
| 20160001461 | Gardiner et al. | Jan 2016 | A1 |
| 20160136891 | Benthien et al. | May 2016 | A1 |
| 20160137839 | Rolland et al. | May 2016 | A1 |
| 20160243721 | Tew | Aug 2016 | A1 |
| 20160264461 | Peng et al. | Sep 2016 | A1 |
| 20160362959 | Zhou | Dec 2016 | A1 |
| 20170054191 | Williams | Feb 2017 | A1 |
| 20180079134 | Tomko et al. | Mar 2018 | A1 |
| 20190099945 | Hsing et al. | Apr 2019 | A1 |
| 20190112517 | Dahi Taleghani et al. | Apr 2019 | A1 |
| 20190135707 | Krasnoff et al. | May 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 107901185 | Apr 2018 | CN |
| 29916239 | Dec 1999 | DE |
| 1491516 | Jul 2011 | EP |
| H1086117 | Apr 1998 | JP |
| 2000094553 | Apr 2000 | JP |
| 3734186 | Jan 2006 | JP |
| 4914974 | Apr 2012 | JP |
| 20170120762 | Nov 2017 | KR |
| 2662838 | Jul 2018 | RU |
| 9841707 | Sep 1998 | WO |
| 2009030802 | Mar 2009 | WO |
| 2018136475 | Jul 2018 | WO |
| 2019112893 | Jun 2019 | WO |
| 2019168621 | Sep 2019 | WO |
| Entry |
|---|
| Asprone et al., “3D Printing of Reinforced Concrete Elements: Technology and Design Approach,” Construction and Building Materials, vol. 165, pp. 218-231, Mar. 20, 2018. |
| Gibbons et al., “3D Printing of Cement Composites”, University of Warwick, 2010, pp. 1-8GIBBONS et al., “3D Printing of Cement Composites”, University of Warwick, 2010, pp. 1-8. |
| Hilal, et al., “On Void Structure and Strength of Foamed Concrete Made Without/With Additives,” Construction and Building Materials, vol. 85, pp. 157-164, Jun. 15, 2015. |
| Invitation to Pay Additional Fees and Partial International Search Report of PCT Application No. PCT/US2021/070554 dated Aug. 6, 2021: pp. 1-12. |
| Sajadi et al., “Direct Ink Writing of Cement Structures Modified with Nanoscale Additive”, Advanced Engineering Materials, 2019, pp. 1-10. |
| Number | Date | Country | |
|---|---|---|---|
| 20230330922 A1 | Oct 2023 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16874449 | May 2020 | US |
| Child | 18337866 | US |