The present invention relates to a method for forming a three-dimensional article according to the preamble of claim 1 and to an apparatus for forming a three-dimensional article according to the preamble of claim 11.
Freeform fabrication or additive manufacturing is a method for forming three-dimensional articles through successive fusion of chosen parts of powder layers applied to a worktable. A method and apparatus according to this technique is disclosed in US 2009/0152771.
Such an apparatus may comprise a start plate on which said three-dimensional article is to be formed, a powder dispenser, arranged to lay down a thin layer of powder on the start plate for the formation of a powder bed, a ray gun for delivering energy to the powder whereby fusion of the powder takes place, elements for control of the ray given off by the ray gun over said powder bed for the formation of a cross section of said three-dimensional article through fusion of parts of said powder bed, and a controlling computer, in which information is stored concerning consecutive cross sections of the three-dimensional article. A three-dimensional article is formed through consecutive fusions of consecutively formed cross sections of powder layers, successively laid down by the powder dispenser.
In US 2009/0152771 it is provided a camera for capturing an Infrared-radiation image, more particularly this camera is used for detecting irregularities in a newly applied powder layer. The irregularities may, according to US 2009/0152771, be caused by irregular applying of the powder on the working table or contamination in the powder dispenser or impurities in the powder as such. There is a need in the art for a method and apparatus in which the cause for irregular powder distribution may be detected for future repair in the additive manufacturing system.
An object of the invention is to provide a method and apparatus which solve the above mentioned need in the art.
The abovementioned object is achieved by the features in the method according to claim 1 and the apparatus according to claim 11.
In a first aspect of the invention it is provided a method for forming a three-dimensional article through successive fusion of parts of a powder bed, which parts corresponds to successive cross sections of the three-dimensional article, said method comprising the steps of: (a) providing a predetermined amount of powder for forming a first powder layer on a surface, (b) distributing said predetermined amount of powder for forming said first powder layer on said surface, (c) directing an energy beam over said first powder layer causing said first powder layer to fuse in selected locations according to a model to form a first cross section of said three-dimensional article, (d) capturing at least one image of the powder to be distributed with a camera at least one time during said distribution of said powder on said surface for forming said first powder layer, and (e) comparing at least one value of at least one parameter in said image detected by said camera with a corresponding reference parameter value.
An advantage of this embodiment is that an indication of an error in the build may be given already in the powder distribution phase. A message may be sent to the operator that the powder distribution may be incorrect and/or said position of the powder distributor and the number of the layer in which this happened may be stored in a control unit.
In one example embodiment of the present invention said predetermined amount of powder for forming a second powder layer on top of said first powder layer which is fused in selected locations may change if at least one parameter value in said image is deviating at least one Δ-value from a corresponding reference parameter value.
An advantage of this embodiment is that there may be a feed back to a powder provision mechanism in which the amount of powder is changed during building the article. Increasing the powder amount if there is an indication of too less powder during the powder distribution process and decreasing the powder amount if there is an indication that there is too much powder which is distributed over the start plate for forming a powder layer.
In another example embodiment according to the present invention a second predetermined amount of powder is provided for forming said first powder layer a second time and distributing said second predetermined amount of powder for forming said first powder layer said second time if at least one parameter value in said image is at least one Δ-value smaller than a corresponding reference parameter value when forming said first powder layer said first time.
An advantage of this embodiment is that any failure in the powder application mechanism may be corrected before starting to fuse the powder layer and thereby creating defects in the three-dimensional article because of a non-homogenous powder layer.
In another example embodiment of the present invention said parameter in said image may be one of the group of: shape of powder in front of a powder distributor; distance of powder front to a reference position; width of powder front and/or position of powder front.
An advantage of this embodiment is that a number of different parameters may be used in order to check the powder distribution process and the resulting powder layer that comes from this distribution process. Deviations from a predetermined reference value of anyone of said parameters may be an indication of an erroneous powder layer. In such a case one may start a second powder application process for such a layer, i.e., the erroneous powder layer may immediately started to be repaired before the powder layer is fused in selected locations.
In another aspect of the invention it is provided an apparatus for forming a three-dimensional article through successive fusion of parts of a powder bed, which parts corresponds to successive cross sections of the three-dimensional article, said apparatus comprising: (a) means for providing a predetermined amount of powder for forming a first powder layer on a surface, (b) a powder distributor for distributing said predetermined amount of powder for forming said first powder layer, (c) means for directing an energy beam over said first powder layer causing said first powder layer to fuse in selected locations according to a model to form a first cross section of said three-dimensional article, (d) a camera for capturing at least one image of the powder to be distributed at least one time during said distribution of said powder on said surface for forming said first powder layer, and (e) means for comparing at least one value of at least one parameter in said image detected by said camera with a corresponding reference parameter value.
Further example embodiment of the apparatus is evident from the description, figures and dependent claims. The advantage of the different embodiments of the apparatus is similar to the advantage of the corresponding method and need therefore not to be repeated in this context.
The invention will be further described in the following, in a non-limiting way with reference to the accompanying drawings. Same characters of reference are employed to indicate corresponding similar parts throughout the several figures of the drawings:
a depicts a flow chart of a first example embodiment of the method according to the present invention;
b depicts a flow chart of a second example embodiment of the method according to the present invention;
c depicts a flow chart of a third example embodiment of the method according to the present invention;
To facilitate the understanding of this invention, a number of terms are defined below. Terms defined herein have meanings as commonly understood by a person of ordinary skill in the areas relevant to the present invention. Terms such as “a”, “an” and “the” are not intended to refer to only a singular entity, but include the general class of which a specific example may be used for illustration. The terminology herein is used to describe specific embodiments of the invention, but their usage does not delimit the invention, except as outlined in the claims.
The term “three-dimensional structures” and the like as used herein refer generally to intended or actually fabricated three-dimensional configurations (e.g. of structural material or materials) that are intended to be used for a particular purpose. Such structures, etc. may, for example, be designed with the aid of a three-dimensional CAD system.
The term “electron beam” as used herein in various embodiments refers to any charged particle beam. The source of a charged particle beam can include an electron gun, a linear accelerator and so on.
The vacuum chamber 320 is capable of maintaining a vacuum environment by means of a vacuum system, which system may comprise a turbo molecular pump, a scroll pump, an ion pump and one or more valves which are well known to a skilled person in the art and therefore need no further explanation in this context. The vacuum system may be controlled by a control unit 270, 370.
The electron gun 302 is generating an electron beam which is used for melting or fusing together powder material 318 provided on the start plate 316. At least a portion of the electron gun 302 may be provided in the vacuum chamber 320. A control unit 270, 370 may be used for controlling and managing the electron beam emitted from the electron beam gun 302. At least one focusing coil (not shown), at least one deflection coil and an electron beam power supply may be electrically connected to said control unit 270, 370. In an example embodiment of the invention said electron gun generates a focusable electron beam with an accelerating voltage of about 60 kV and with a beam power in the range of 0-3 kW. The pressure in the vacuum chamber may be in the range of 10−3-10−6 mBar when building the three-dimensional article by fusing the powder layer by layer with the energy beam.
Instead of melting the powder material with an electron beam a laser beam may be used.
The powder hoppers 306, 307 comprise the powder material to be provided on the start plate 316 in the build tank 312. The powder material may for instance be pure metals or metal alloys such as titanium, titanium alloys, aluminum, aluminum alloys, stainless steel, Co—Cr—W alloy, etc.
The powder distributor 310 is arranged to lay down a thin layer of the powder material on the start plate 316. During a work cycle the build platform 314 will be lowered successively in relation to the ray gun after each added layer of powder material. In order to make this movement possible, the build platform 314, 206 is in one embodiment of the invention arranged movably in vertical direction, i.e., in the direction indicated by arrow P. This means that the build platform 314, 206 starts in an initial position, in which a first powder material layer of necessary thickness has been laid down on said start plate 316. A first layer of powder material may be thicker than the other applied layers. The reason for starting with a first layer which is thicker than the other layers is that one does not want a melt-through of the first layer onto the start plate. The build platform is thereafter lowered in connection with laying down a new powder material layer for the formation of a new cross section of a three-dimensional article. Means for lowering the build platform 314, 206 may for instance be through a servo engine equipped with a gear, adjusting screws etc.
In an example embodiment said start plate 316 may be said build platform 314, 206. In such case said build platform 314, 206 is removable from the build tank 312.
In an example embodiment of a method, a three-dimensional article may be formed through successive fusion of parts of a powder bed, which parts corresponds to successive cross sections of the three-dimensional article, comprising a step of providing a model of said three dimensional article. Said model may be generated via a CAD (Computer Aided Design) tool.
A predetermined amount of powder may be provided at a powder table 230, 340 denoted by step 402 in
Instead of providing the powder from said powder hopper on said powder table an arrangement according to
A first powder layer may be provided on the start plate 316. In an example embodiment the first powder layer is provided on a surface which may be a start plate or a powder bed.
In a first example embodiment powder may be collected by a powder distributor or a rake 202, 310 by moving the rake 202, 310 with its first surface 290 a predetermined distance in a first direction into the scree of powder 220 allowing a predetermined amount of powder to fall over a top of said rake 202. The rake 202 is then moved in a second direction, opposite to said first direction, and thereby removing said predetermined amount of powder which has fallen over the top of said rake 202, 310 from said scree of powder with a second surface 291 of said rake 202, 310.
In an alternative method said powder to be distributed over said start plate 316 may be collected from a powder container 360 with a movable bottom as described in connection with
The powder removed from the scree of powder 220 or scraped off from the powder container 360 or provided by any other suitable mechanism in front of the rake 202 may be moved over the build tank 312, 240 by means of said rake 202, 310, thereby distributing the powder over the start plate 316 or said build platform 314, 206 denoted by step 404 in
The distance between a lower part of the rake and the upper part of the start plate or previous powder layer determines the thickness of powder distributed over the start plate. The powder layer thickness can easily be adjusted by adjusting the height of the build platform 314, 206.
An energy beam may be directed over said start plate 316 causing said first powder layer to fuse in selected locations to form a first cross section of said three-dimensional article according to said model generated via said CAD tool denoted with step 406 in
The energy beam may be an electron beam or a laser beam. The beam is directed over said start plate 316 from instructions given by the control unit 270, 370. In the control unit 270, 370 instructions for how to control the beam gun for each layer of the three-dimensional article may be stored.
After a first layer is finished, i.e., the fusion of powder material for making a first layer of the three-dimensional article, a second powder layer is provided on said start plate 316. The second powder layer is preferably distributed according to the same manner as the previous layer. However, there might be alternative methods in the same additive manufacturing machine for distributing powder onto the work table 316. For instance, a first layer may be provided by means of a first powder distributor, a second layer may be provided by another powder distributor. The design of the powder distributor is automatically changed according to instructions from the control unit. A powder distributor in the form of a single rake system, i.e., where one rake is catching powder fallen down from both a left powder hopper 306 and a right powder hopper 307, the rake as such can change design.
After having distributed the second powder layer on the work table 316, the energy beam is directed over said work table 316 causing said second powder layer to fuse in selected locations to form a second cross section of said three-dimensional article. Fused portions in the second layer may be bonded to fused portions of said first layer. The fused portions in the first and second layer may be melted together by melting not only the powder in the uppermost layer but also remelting at least a fraction of a thickness of a layer directly below said uppermost layer.
An image may be captured of the powder to be distributed with a camera at least one time during the distribution of powder over the work table 316 for forming a powder layer denoted by 408 in
At least one image may be taken during the distribution of powder for forming a powder layer on the start plate 316. In an example embodiment images are taken at the start of powder distribution and at the end of powder distribution. In another example embodiment images may also be taken at any position between said start and finish of the powder distribution.
At least one value of at least one parameter in at least one image which may be detected with said camera may be compared with a corresponding reference parameter value denoted with 410 in
The shape of powder in front of the powder distributor and/or the distance to back or front of the powder distributor to a powder front 120 may be examples of said parameter in said image. Reference images of shapes of powder in front of the powder distributor may be stored in the control unit for comparison with the actual shape. If the shape is deviating more than a predetermined amount from any one of the stored images a warning message may be sent out and/or stored in the control unit 270. The reference shape may for instance be a suitable mathematical expression, such as a polynomial or a parabola or any other shape that is desired for the powder front to be at any given time during the powder distribution process. This mathematical expression may be compared to the actual image taken of the powder front. In a look up table it may be stored the desired shape of the powder front at a given time. This shape from the look up table may be compared with the actual value and any difference that is deviating more than a Δ-value from the desired shape may be a sign of a failure in the powder distribution process. The shape of the powder front in the image may be approximated with a given mathematical expression such as A+BX+CX2+DX3, where A, B, C and D are constants. If any one of the constants in the approximated polynomial from said image is deviating more than a Δ-value from a corresponding constant in the reference polynomial, this may be a sign of a failure in the powder distribution process. Said Δ-value may be different for different constants in a given polynomial. The value of Δ may be set depending on the tolerance of a difference between desired and actual shape of the powder front, larger Δ-value indicated a larger tolerance for differences than a smaller Δ-value.
Any other parameter than the shape may be stored in a look up table such as the distances mentioned below. As with the shape said distances have a desired value for any given time and may be compared with the actual value. If there is a difference larger than a Δ-value between said desired value and said actual value such a difference may be an indication of a failure in the powder distribution process.
In
In said control unit 270 there may also be several values stored for said distance of powder front to said powder distributor which may be compared with actual distances of the powder front 120 to the powder distributor. In an example embodiment several measurements of said distance of said powder front to said powder distributor 202 may be taken from a single image, i.e., at several positions along the powder distributor 202. By taking more than one measurement of said distance one may make assure that the powder is not unevenly distributed in front of the powder distributor 202. Unevenly distributed powder may possibly be the cause for unevenly distributed powder, i.e., less or no powder at a specific location. If the measured distance of the powder front to said powder distributor 202 for any distance of the powder distributor 202 and any position along the powder distributor 202 is deviating more than a predetermined value from a reference value of a corresponding reference distance of the powder front to the powder distributor 202 a warning message may be sent out and/or said position of said powder distributor 202 together with said position along said powder distributor 202 may be stored in said control unit 270.
b depicts another example embodiment of the method according to the present invention. The steps 402, 404, 406, 408 and 410 are equal to the steps in
In step 414 a different amount of powder is provided on the worktable. A different amount of powder could be provided by changing the distance that said powder distributor 202 is travelling into the scree of powder 220 before being stopped. Alternatively a different amount of powder could be provided by changing the distance said movable floor 362 is lifted. A less distance will provide less powder and a longer distance will provide more powder. In step 416 the changed amount of powder is distributed on the start plate 316 for forming layer N+1. In an example embodiment the amount of powder at the end of the powder distribution process may indicate a superfluous amount of powder in front of the powder distributor although the powder distribution has been finished. In such case the amount of powder may be reduced for the following layer.
As disclosed above the powder distributor 202 may be set to travel a less distance into the scree of powder 220 in order to let a less amount of powder to fall over the top of the powder distributor. On the other hand, if the measurement indicates that the powder in front of the powder distributor is decreasing, the settings of the powder distributor may be changed in order to collect more powder from the scree of powder 220. As an alternative to provide less powder in front of the powder distributor, said floor in said powder tank may be set to travel a less distance upwards thereby providing a less amount of powder which is possible to be raked off by the powder distributor and to be distributed on said start plate 206, 314.
c depicts yet an alternative example embodiment of the method according to the present invention. If there is no difference between the actual measured parameter value and a predetermined reference parameter value, the next powder layer may be started to be distributed with the same settings as the previous powder layer indicated in
If the measured parameter value is in fact more than a predetermined value from the reference parameter value, then the next question may be, denoted in
In step 420 a second predetermined amount of powder may be provided on said powder table for forming layer N. Said second predetermined amount of powder may be different to said predetermined amount of powder in step 402. Since a second powder distribution is taking place after providing the second predetermined amount of powder for forming layer N a relatively small amount of powder is needed to fill in the possible holes/gaps in the layer already provided at the first instance. A smaller amount of powder may be collected from the scree of powder by letting the powder distributor travelling a less distance into the scree of powder than normally, i.e., in the case when said predetermined amount of powder is provided on said powder table said powder distributor is travelling a first distance into the scree of powder and when said second amount of powder may be provided on said powder table said powder distributor may be travelling a second distance into the scree of powder. Here the second distance may be less than said first distance in order to collect less powder in the second collection for distribution over the start plate 316 a second time for forming layer N. Alternatively a different amount of powder could be provided by changing the distance said movable floor 362 may be lifted upwards.
A feedback signal may be generated if there is a mismatch between the measured parameter value and a corresponding reference parameter value. The feedback signal may go from the control unit 270 to a powder provision apparatus for changing the amount of powder provided on said powder table. In an example embodiment no powder table may be present. The amount of powder provided may in such case be achieved by changing the distance said movable floor 362 is lifted upwards.
In another aspect of the invention it is provided an apparatus for forming a three-dimensional article through successive fusion of parts of a powder bed, which parts corresponds to successive cross sections of the three-dimensional article. Said apparatus may comprise means for providing a predetermined amount of powder at a powder table for forming a first powder layer on a start plate. Said means for providing a predetermined amount of powder at said powder table may be a powder hopper as indicated in
Said apparatus further comprising a camera for capturing at least one image of the powder to be distributed at least one time during said distribution of said powder on said start plate for forming said first powder layer and means for comparing at least one value of at least one parameter in said image detected by said camera with a reference parameter value.
The means for comparing parameter values from the image with reference values may be a software program which makes analysis and measurements at predetermined image locations and comparing these measurements with stored reference values. Said apparatus may further be provided with a feature which provides for an alarm if the measured value and the reference value differs more than a predetermined value from each other. Another feature that said apparatus may be provided with is a storing function which stores the location of the powder distributor if the measured value and the reference value differs more than a predetermined value from each other.
In another example embodiment of said apparatus there is provided means for changing said predetermined amount of powder for forming a second powder layer on said start plate if at least one parameter value in said image is deviating from said reference parameter value. Said means may be programmable instructions sent from the control unit 270 to the powder distributor indicating that the distance of travel into the scree of powder is changed. In an alternative design of said provision of powder, e.g., in case of a shutter in front of the bottom opening of a powder hopper, the time and/or the area of opening of said shutter may be changed in order to change the predetermined amount of powder.
In still another example embodiment said apparatus comprises means for providing a second predetermined amount of powder for forming said first powder layer and distributing said second predetermined amount of powder for forming said first powder layer if at least one parameter value is less than a reference parameter value. The means may be the same as disclosed above for providing the second predetermined amount of powder, i.e., it may be a question of settings of the powder distributor or shutter which determines the amount of powder provided on said powder table. A second powder distribution for forming one and the same powder layer may take place if there may be an indication that there may be one or more places of nonsufficient powder.
The energy beam, which may be a laser beam or an electron beam, not only melts the last applied powder layer but also at least the layer of material below the powder layer resulting in a melt comprising the powder material and already melted material from a previous fusion process.
The invention is not limited to the above-described embodiments and many modifications are possible within the scope of the following claims. Such modifications may, for example, involve using a different source of ray gun than the exemplified electron beam such as laser beam. Other materials than metallic powder may be used such as powders of polymers and powder of ceramics.
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/EP2013/074092 | 11/18/2013 | WO | 00 |
Number | Date | Country | |
---|---|---|---|
61738203 | Dec 2012 | US |