Additive Raw Material Composition and Additive for Superhard Material Product, Preparation Method of the Additive, Composite Binding Agent and Superhard Material Product, Self-Sharpening Diamond Grinding Wheel and Preparation Method of the Same

Abstract
Disclosed are an additive raw material composition and an additive for superhard material product, a composite binding agent, a superhard material product, a self-sharpening diamond grinding wheel and a method for manufacturing the same. The raw material composition consisting of components in following mass percentage: Bi2O3 25%˜40%, B2O3 25%˜40%, ZnO 5%˜25%, SiO2 2%˜10%, Al2O3 2%˜10%, Na2CO3 1%˜5%, Li2CO3 1%-5%, MgCO3 0%˜5%, and CaF2 1%˜5%. The composite binding agent is prepared from the additive and a metal composite binding agent. The self-sharpening diamond grinding wheel prepared from the composite binding agent has high self-sharpness, high strength, and fine texture, is uniformly consumed during the grinding process, does not need to be trimmed during the process of being used, and maintains good grinding force all the time, fundamentally solving the problems of long trimming time and high trimming cost of the diamond grinding wheel (FIG. 1).
Description
TECHNICAL FIELD

The present invention belongs to the technical field of superhard material product, and particularly relates to an additive raw material composition for superhard material product, meanwhile also relates to an additive for superhard material product made from the additive raw material composition and a preparation method of the same, and also relates to a composite binding agent containing the additive, a grinding wheel using the composite binding agent and a preparation method of the same, and specifically relates to an additive raw material composition and an additive for superhard material product, and a preparation method of the additive, a composite binding agent and a superhard material product, a self-sharpening diamond grinding wheel and a preparation method of the same.


BACKGROUND ART

Superhard materials mainly refer to diamond and cubic boron nitride, whose hardness is far higher than that of other materials. Superhard materials and products thereof are an emerging industry strongly supported by the nation. It is pointed out in Chinese “Twelfth Five-Year” Development Plan for National Strategic Emerging Industries that new functional materials should be vigorously developed, and high-purity graphite, artificial crystals, superhard materials and products thereof should be actively developed. According to the difference of types of binding agents, the superhard material products mainly include: superhard material products with metal binding agents, superhard material products with ceramic binding agents, superhard material products with resin binding agents, superhard material products with electroplated metal binding agents and so on.


As one of the main types of superhard material products, the superhard material products with metal binding agents have the advantages such as strong holding force to abrasive, high strength, good abrasion resistance, good performance of maintaining the shape of a working face, and long service life, and are widely applied to cutting, grinding and shaping and grinding-processing of inorganic non-metal hard and brittle materials such as stones, glasses, ceramics and artificial crystals. However, diamond products with metal binding agents have the problems such as poor self-sharpness, easy blockage, and low grinding efficiency, which limit their use and development.


With regard to the problems of the superhard material products with metal binding agents, numerous investigations and attempts have been made by scholars, primarily adding barren materials including graphite, ceramic, and iron oxide as additive. However, if an excessive quantity of these additives is added, the strength of an abrasive layer and the holding force of the binding agents to the abrasive will be severely reduced, significantly decreasing the service life and easily causing scratches; if the quantity added is too little, the function of improving the grinding performance and the grinding efficiency is not significant.


For example, in the prior art, a superhard abrasive grinding wheel with metal binding agent, which can be subjected to on-line electrolysis, is manufactured by a cold pressing sintering method. One or two from graphite and ferroferric oxide, which are used in the superhard abrasive grinding wheel as non-metal additive, have a small adhering function and relatively low strength (being quite different from the metal binding agent in strength), and are unfavorable to keeping the strength of the abrasive layer and the holding force to the abrasive.


Self-sharpness of grinding wheel means that when abrasive grains of the grinding wheel are blunted, the grinding force is also increased accordingly, so that the abrasive grains are broken or fall down, and sharp cutting edges appear again. During the process of grinding of the superhard material product grinding wheel, edges and corners of the abrasive grains of the grinding wheel are gradually rounded and blunted under the effects of friction and extrusion, and abrasive debris is often stuck on the surface of the grinding wheel so that the surface of the grinding wheel is blocked, and finally the grinding wheel loses the grinding ability. At this time, skidding will occur between the grinding wheel and a workpiece, and vibration may be induced and noise may appear, so that the grinding efficiency is decreased and the surface roughness becomes worse. Meanwhile, as the grinding force and the grinding heat are increased, the workpiece will be deformed and the grinding accuracy will be affected, and in severe cases the grinding surface will be burnt and tiny cracks will appear thereon. At this time, the grinding wheel has to be trimmed with a trimmer. The grinding wheel usually needs to be trimmed for tens of minutes or even several hours, severely affecting the manufacturing steps and lowering the producing efficiency; the trimmer is expensive, and the cost is high; in high-accuracy grinding, a machine tool needs to be further equipped with an in-process trimming device, which also increased the design difficulty and manufacturing cost of the machine tool. In the prior art, improvement on the self-sharpness of the diamond grinding wheel is merely limited to improvement on trimming gap, while the problems of long time and high cost of trimming the grinding wheel still cannot be solved. The grinding wheel with the composite binding agent uses a composite binding agent made from ceramic powder and bronze powder, but the ceramic powder, having a relatively high level of fire resistance, needs to be smelted at 1700° C., which is higher than the sintering temperature of the grinding wheel, and the ceramic powder is not easy to disperse uniformly during the sintering process, having limited function in improving the grinding efficiency and the service life of the grinding wheel.


DISCLOSURE OF THE INVENTION

One of the objects of the present invention is to provide an additive raw material composition for superhard material product, wherein the difference between the strength of the obtained additive and that of the metal binding agent is small, and the obtained additive has a low level of fire resistance, and can remarkably improve the grinding efficiency and the service life of the superhard material product with the metal binding agent.


Another object of the present invention is to further provide an additive for superhard material product made by the above additive raw material composition and a preparation method thereof, and a composite binding agent containing the additive and a superhard material product using the composite binding agent.


Another object of the present invention is to further provide a self-sharpening diamond grinding wheel and a preparation method thereof.


In order to achieve the above objects, technical solutions used in the present invention are as follows:


an additive raw material composition for superhard material product consists of components in a mass percentage as follows:


Bi2O3 25%˜40%, B2O3 25%˜40%, ZnO 5%˜25%, SiO2 2%˜10%, Al2O3 2%˜10%, Na2CO3 1%˜5%, Li2CO3 1%˜5%, MgCO3 0%˜5%, and CaF2 1%˜5%.


In the above raw material composition, the purity of each of the raw materials is analytically pure.


An additive for superhard material product is made from raw materials in a mass percentage as follows:


Bi2O3 25%˜40%, B2O3 25%˜40%, ZnO 5%˜25%, SiO2 2%˜10%, Al2O3 2%˜10%, Na2CO3 1%˜5%, Li2CO3 1%˜5%, MgCO3 0%˜5%, and CaF2 1%˜5%.


The particle size of the additive is D90<200 nm.


A method for preparing the above additive includes the steps of:


1) mixing Bi2O3, B2O3, ZnO, SiO2, Al2O3, Na2CO3, Li2CO3, and MgCO3 of a formula ratio, heating up to 1200˜1400° C. and keeping the temperature for 1˜3 h to provide a mixture;


2) cooling the mixture obtained in Step 1) to 850˜950° C., adding CaF2 of the formula ratio to the mixture, and keeping the temperature for 1˜2 h to provide a sinter;


3) quenching the sinter obtained in Step 2) and then crushing the quenched sinter to make the quenched sinter in a particle size of D90<200 nm to provide the additive.


A composite binding agent consists of a metal binding agent and the above additive. The content of mass percentage of the additive in the composite binding agent is no more than 30%. The content of mass percentage of the additive in the composite binding agent is 1.1%˜30%.


A superhard material product uses the above composite binding agent; optionally, the superhard material product is a grinding wheel. In this grinding wheel, the weight of the additive is 1%˜10% of the total weight of the raw materials of the grinding wheel. The raw materials of the grinding wheel include the composite binding agent and an abrasive.


A self-sharpening diamond grinding wheel includes an abrasive block, raw materials of the abrasive block include a metal binding agent, MoS2, SG abrasive, diamond and the above additive; the mass percentage of the above additive in the raw materials of the abrasive block is 1%˜10%.


A method for manufacturing the above self-sharpening diamond grinding wheel includes the steps of:


a) mixing a metal binding agent, MoS2 powder, SG abrasive, diamond and additive to provide a mixture;


b) placing the mixture obtained in Step a) in a mold and pressing the mixture to provide a semifinished product;


c) placing the semifinished product obtained in Step b) in a mold, heating up to 580˜620° C. and keeping the temperature for 4˜10 min for sintering, followed by quenching, to provide the abrasive block.


The method for manufacturing the self-sharpening diamond grinding wheel further includes adhering the obtained abrasive block on a grinding wheel substrate to provide the self-sharpening diamond grinding wheel.


In the additive raw material composition for superhard material product of the present invention, Bi2O3, B2O3, ZnO, SiO2, Al2O3, Na2CO3, Li2CO3, and MgCO3 are used for compounding with CaF2, and the components coordinate and cooperate with each other; the additive made from the raw material composition has a microcrystalline structure, and its strength is greater than 200 MPa, which is not quite different from the metal bonding agent in strength, and will not remarkably lower the strength of the superhard material product of metal binding agent; the level of fire resistance of the additive is lower than 500° C., which is far lower than the sintering temperature of the superhard material product with metal binding agent, and when the superhard material product with metal binding agent is sintered, the additive is in a molten state, and is radially distributed between particles of the skeleton after the sintering; the additive, whose particle size reaches a submicron level, is uniformly dispersed in the product with fine texture, has less influence on the overall strength of the product, and can remarkably improve the grinding efficiency and the service life of the superhard material product with the metal binding agent.


The method for preparing additive for superhard material product of the present invention is mixing and smelting Bi2O3, B2O3, ZnO, SiO2, Al2O3, Na2CO3, Li2CO3, and MgCO3, then cooling and adding CaF2 to the mixture, keeping the temperature, and then quenching and crushing to provide the additive; the additive obtained has a microcrystalline structure, high strength, low fire resistance, and small particle size; this preparation method has a simple process, is easy to operate, and is suitable to large-scale industrialized manufacturing.


The additive shows uniform diffused radioactive distribution of a submicron level in the composite binding agent, the additive is compounded with a metal binding agent to form a composite binding agent. A superhard material product using the composite binding agent has less influence on the strength of the metal binding agent, improves the sharpness and service life of the product, and enhances the grinding performance of the product.


In the self-sharpening diamond grinding wheel of the present invention, raw materials of the abrasive block include a metal binding agent, MoS2, SG abrasive, diamond and additive, the additive is made from certain amounts of Bi2O3, B2O3, ZnO, SiO2, Al2O3, Na2CO3, Li2CO3, MgCO3 and CaF2, the additive has a microcrystalline structure, and its strength is greater than 200 MPa, the difference between the strength of it and that of the metal binding agent is small; the fire resistance of the additive is lower than 500° C., far lower than the sintering temperature of the superhard material product with metal binding agent, it is in a molten state when being sintered, radially distributed between particles of the skeleton after the sintering, and uniformly dispersed with fine texture.


In the self-sharpening grinding wheel of the present invention, the coefficient of linear expansion of the additive used well matches with the diamond, the additive shows uniform diffused radioactive distribution of a submicron level in the grinding wheel, has less influence on the overall strength of the grinding wheel, and can remarkably improve the self-sharpness and service life of the diamond grinding wheel of metal binding agent; the MoS2 powder has a stable chemical property and a very strong adhesion force between metals, has a lubrication function, and also serves an anti-oxidation function in powders; the SG abrasive has the functions of site-occupying and assisting the grinding in the grinding wheel, prevents the grinding wheel from being blocked, and meanwhile can improve the performance of maintaining the shape of the diamond grinding wheel, and avoid loss of accuracy of shape of the grinding wheel. The self-sharpening grinding wheel of the present invention, with the abrasive block taking a metal binding agent, SG abrasive, diamond and the above additive as raw materials, has high self-sharpness, high strength, high processing efficiency, and fine texture, is uniformly consumed during the grinding process, and does not need to be trimmed during the process of being used in the whole life cycle, moreover, during the grinding process, it maintains good grinding force all the time, fundamentally solving the problems of long trimming time and high trimming cost of the diamond grinding wheel, and possessing good economic benefit.


Further, the self-sharpening diamond grinding wheel of the present invention uses the metal binding agent made from certain amounts of Cu powder, Sn powder, Co powder, Al powder, Fe powder, Cr powder, and Ti powder; in the metal binding agent, the Al powder, which has a relatively high activity, is quite easy to oxidize, can preferentially react with oxygen in air during the sintering process, so as to prevent oxidization of other metal powders and diamond, thus the sintering process can be carried out in an air atmosphere, greatly reducing the cost; the Cr powder and the Ti powder can form carbides with the abrasive, improving the adhering strength of the diamond plated with the binding agent.


In the method for manufacturing the self-sharpening diamond grinding wheel of the present invention, the raw materials are mixed, then the mixture is firstly pressed into a semifinished product, and then sintered; after the hot pressing sintering, the mold is quickly placed in water to be quenched, which can prevent the crystal grains from growing excessively, so that the grinding wheel has fine texture, thus a diamond grinding wheel with high strength and high self-sharpness is obtained, moreover, the grinding wheel is uniformly consumed during the grinding process. This manufacturing method has a simple process, easy operation, low sintering temperature, and low cost, and is easy to be controlled automatically and suitable to large-scale industrialized manufacturing.





BRIEF DESCRIPTION OF DRAWINGS

In order to more clearly illustrate technical solutions of examples of the present invention, figures which are needed in the examples will be introduced briefly below. It should be understood that the figures below merely show some examples of the present invention, and therefore should not be considered as limiting the scope. A person ordinarily skilled in the art still can obtain other relevant figures according to these figures, without paying inventive effort.



FIG. 1 is a diagram of distribution of particle size of an additive for a superhard material product obtained in Example 1;



FIG. 2 is a schematic diagram of distribution of the additive obtained in Example 1 in a composite binding agent,





wherein 1—skeleton material, 2—additive.


DETAILED DESCRIPTION OF EMBODIMENTS

Below, the present invention is further described in combination with embodiments.


An additive raw material composition for superhard material product consists of components in a mass percentage as follows:


Bi2O3 25%˜40%, B2O3 25%˜40%, ZnO 5%˜25%, SiO2 2%˜10%, Al2O3 2%˜10%, Na2CO3 1%˜5%, Li2CO3 1%˜5%, MgCO3 0%˜5%, and CaF2 1%˜5%.


In the above raw material composition, the purity of respective raw materials is analytically pure.


An additive for superhard material product is made from raw materials of in a mass percentage as follows:


Bi2O3 25%˜40%, B2O3 25%˜40%, ZnO 5%˜25%, SiO2 2%˜10%, Al2O3 2%˜10%, Na2CO3 1%˜5%, Li2CO3 1%˜5%, MgCO3 0%˜5%, and CaF2 1%˜5%.


Optionally, the particle size of the additive is D90<200 nm.


A method for preparing the above additive includes the steps of:


1) mixing Bi2O3, B2O3, ZnO, SiO2, Al2O3, Na2CO3, Li2CO3, and MgCO3 of a formula ratio, heating up to 1200˜1400° C. and keeping the temperature for 1˜3 h to provide a mixture;


2) cooling the mixture obtained in Step 1) to 850˜950° C., adding CaF2 of the formula ratio to the mixture, and keeping the temperature for 1˜2 h to provide a sinter;


3) quenching the sinter obtained in Step 2) and then crushing the quenched sinter to make the quenched sinter in a particle size of D90<200 nm to obtain the additive.


Optionally, in Step 1), a rate of the heating is 8˜12° C./min. The mixed raw materials are put in a quartz crucible, and placed in a high-temperature resistance furnace to be heated.


Optionally, in Step 2), a rate of the cooling is 4˜6° C./min.


Optionally, in Step 3), the quenching refers to quenching the obtained sinter in water, to provide a bulk material. The water preferably is water at a room temperature.


Optionally, the crushing refers to mixing the obtained bulk material with ethanol and ball-milling them. The bulk material is put into a ball-mill tank together with ethanol to be ball-milled on a high-energy ball-milling machine; they are ball-milled until the obtained powder has a particle size of D90<200 nm; optionally, the ball-milling time is 40˜60 h. Optionally, a volume ratio of the material to ethanol is 1:3.


The composite binding agent consists of a metal binding agent and the above additive. The content of mass percentage of the additive in the composite binding agent is no more than 30%. The content of mass percentage of the additive in the composite binding agent is 1.1%˜30%.


Optionally, the metal binding agent is a bronze binding agent or a Co-based binding agent.


A superhard material product uses the above composite binding agent; the superhard material product is a grinding wheel. In the grinding wheel, the weight of the additive is 1%˜10% of the total weight of the raw materials of the grinding wheel. The raw materials of the grinding wheel include the composite binding agent and an abrasive. Preferably, the abrasive is a diamond abrasive.


The self-sharpening diamond grinding wheel includes an abrasive block, raw materials of the abrasive block include a metal binding agent, MoS2, SG abrasive, diamond and the above additive; the content of mass percentage of the above additive in the raw materials of the abrasive block is 1%˜10%.


A method for manufacturing the above self-sharpening diamond grinding wheel includes the steps of:


a) mixing the metal binding agent, the MoS2 powder, the SG abrasive, the diamond and the additive to provide a mixture;


b) loading the mixture obtained in Step a) in a mold and pressing the mixture to provide a semifinished product;


c) placing the semifinished product obtained in Step b) in a mold, heating up to 580˜620° C. and keeping the temperature for 4˜10 min for sintering, followed by quenching, to provide the abrasive block.


Optionally, in Step a), the mixing is pouring the raw materials in a three-dimensional mixer to mix the materials for 2˜4 h.


Optionally, in Step b), a pressure of the pressing is 150˜200 MPa. The mold used in the pressing preferably is a steel mold; the device used in the pressing preferably is an oil hydraulic press.


Optionally, in Step c), the heating refers to firstly heating up to 350˜450° C. at a heating rate of 100° C./min and keeping the temperature for 1˜3 min, and then heating up to 580˜620° C. at a heating rate of 50° C./min. The function of firstly heating up to 350˜450° C. and keeping the temperature is to promote Sn having a low melting point to melt completely so as to perform alloying reaction.


Optionally, in Step c), the mold used in the sintering preferably is a graphite mold; the device used in the sintering preferably is a hot pressed sintering machine. The sintering process can be carried out in an air atmosphere. After completing the temperature keeping at 580˜620° C., the mold is placed in water to be quenched. The water preferably is water at a room temperature.


Optionally, the method for preparing the self-sharpening diamond grinding wheel further includes adhering the obtained abrasive block on a grinding wheel substrate to obtain the self-sharpening diamond grinding wheel.


In the embodiments, all the raw materials used in the raw material composition are analytical pure.


Example 1

An additive raw material composition for superhard material product in the present example consists of components of mass percentage as follows:


Bi2O3 35%, B2O3 35%, ZnO 10%, SiO2 5%, Al2O3 3%, Na2CO3 2%, Li2CO3 4%, MgCO3 2%, and CaF2 4%.


An additive for superhard material product in the present example is made from the above raw material composition, and a method for preparing the additive includes the steps of:


1) mixing Bi2O3, B2O3, ZnO, SiO2, Al2O3, Na2CO3, Li2CO3, and MgCO3 of a formula ratio and evenly mixing them, then pouring the mixture in a quartz crucible, and placing the quartz crucible in a high-temperature resistance furnace to be heated at a rate of 10° C./min to 1250° C. and keeping the temperature for 2 h to provide a mixture;


2) cooling the mixture obtained in Step 1) to 850° C. at a rate of 5° C./min, adding CaF2 of the formula ratio to the mixture and stirring, and keeping the temperature for 2 h to provide a sinter;


3) pouring the sinter obtained in Step 2) into cold water to be quenched to provide a bulk material; putting the obtained bulk material and ethanol, at a volume ratio of 1:3 of the material to ethanol, into a ball-mill tank to be ball-milled on a high-energy ball-milling machine for 60 h, to obtain a powder, i.e. the additive, having a particle size of D90<200 nm (the particle size of the powder was detected via a laser particle analyzer, and the particle size distribution was as shown in FIG. 1).


The composite binding agent in the present example consists of a metal binding agent and the above additive. The content of mass percentage of the additive in the composite binding agent is 10%. The metal binding agent is a bronze binding agent, and consists of components of mass percentage as follows: Cu powder 71%, Sn powder 21%, Co powder 7%, and Ni powder 1%.


The grinding wheel in the present example was made by evenly mixing the above composite binding agent with a diamond abrasive, followed by pressing the mixture at 150 MPa into a semifinished product, and then placing the semifinished product in a corresponding mold to be subjected to sintering at 580° C. The weight of the additive is 8% of the total weight of the raw materials of the grinding wheel (the composite binding agent and the diamond abrasive).



FIG. 2 is a schematic diagram of distribution of the additive in the composite binding agent. It can be seen from FIG. 2 that the additive shows uniform diffused radioactive distribution of a submicron level in the composite binding agent, and the distribution of the additive in the superhard material product is also consistent. Wherein the skeleton material refers to a refractory component in the metal binding agent, and is a part of the composite binding agent.


The grinding wheel obtained in Example 1 is used for grinding of hard alloy, and the grinding effect thereof is as listed in Table 1, where Comparative Example 1 uses a diamond grinding wheel of bronze binding agent without additive, and the rest parts are the same with those in Example 1.









TABLE 1







Comparison Table of Grinding Effects of the Grinding Wheel


Obtained in Example 1













Removal
Trimming



Grinding
Strength
Rate
Frequency (Kg
Service Life of


Wheel
(MPa)
(g/min)
each time)
Grinding Wheel














Comparative
280
3
2.5
30


Example 1


Example 1
260
4
4
42









Example 2

An additive raw material composition for superhard material product in the present example consists of components of mass percentage as follows:


Bi2O3 30%, B2O3 40%, ZnO 10%, SiO2 5%, Al2O3 3%, Na2CO3 4%, Li2CO3 4%, and CaF2 4%.


An additive for superhard material product in the present example is made from the above raw material composition, and a method for preparing the additive includes the steps of:


1) mixing Bi2O3, B2O3, ZnO, SiO2, Al2O3, Na2CO3, and Li2CO3 of a formula ratio and evenly mixing them, then pouring the mixture in a quartz crucible, and placing the quartz crucible in a high-temperature resistance furnace to be heated at a rate of 10° C./min to 1300° C. and keeping the temperature for 1 h to provide a mixture;


2) cooling the mixture obtained in Step 1) to 850° C. at a rate of 5° C./min, adding CaF2 of the formula ratio to the mixture and stirring, and keeping the temperature for 2 h to provide a sinter;


3) pouring the sinter obtained in Step 2) into cold water to be quenched to provide a bulk material; putting the obtained bulk material and ethanol, at a volume ratio of 1:3 of the material to ethanol, into a ball-mill tank to be ball-milled on a high-energy ball-milling machine for 50 h, to obtain a powder, i.e. the additive, having a particle size of D90<200 nm (the particle size of the powder was detected via a laser particle analyzer).


The composite binding agent in the present example consists of a metal binding agent and the above additive. The content of mass percentage of the additive in the composite binding agent is 3.8%. The metal binding agent is a Co-based binding agent, and consists of components of mass percentage as follows: Co 64%, Cu 21%, Sn 10%, and WC 5%.


The grinding wheel in the present example was made by evenly mixing the above composite binding agent with a diamond abrasive, followed by pressing the mixture at 200 MPa into a semifinished product, and then placing the semifinished product in a corresponding mold to be subjected to sintering at 620° C. The weight of the additive is 3% of the total weight of the raw materials of the grinding wheel (the composite binding agent and the diamond abrasive).


The grinding wheel obtained in Example 2 is used for grinding of iron-based powder metallurgical workpiece, which is assembly line work, and the grinding effect thereof is as listed in Table 2, where Comparative Example 2 uses a diamond grinding wheel of Co-based binding agent without additive, and the rest parts are the same with those in Example 2.









TABLE 2







Comparison Table of Grinding Effects of the Grinding Wheel


Obtained in Example 2













Processing
Trimming
Service Life of


Grinding
Strength
Cycle Time
Frequency
Grinding


Wheel
(MPa)
(sec)
(piece each time)
Wheel (piece)





Comparative
260
18
3200
28000


Example 2


Example 2
250
14
5800
42000









The composition of the additive raw material compositions for superhard material product in Examples 3-6 is as listed in Table 3.









TABLE 3







Composition of the Additive Raw Material Compositions for


Superhard Material Product in Examples 3-6 (mass percentage)











Component
Example 3
Example 4
Example 5
Example 6














Bi2O3
25%
30%
40%
25%


B2O3
40%
25%
30%
25%


ZnO
5%
19%
5%
25%


SiO2
2%
10%
8%
6%


Al2O3
8%
2%
5%
10%


NaCO3
1%
5%
3%
2%


LiCO3
3%
1%
5%
2%


MgCO3
5%
3%
1%
3%


CaF2
1%
5%
3%
2%









The additives for superhard material product in Examples 3-6 are made from the above raw material compositions, respectively. Technical parameters of preparing methods are as listed in Table 4, and the rest parts are the same with those in Example 1.









TABLE 4







Table of Parameters of Methods for Preparing the Additives for


Superhard Material Product in Examples 3-6














Ex-





Step
Parameter
ample 3
Example 4
Example 5
Example 6















1)
temperature being
1200
1300
1400
1350



kept at, ° C.



temperature-keeping
3
2
1
1.5



time, h


2)
temperature being
850
950
900
900



kept at, ° C.



temperature-keeping
2
1
1.5
1



time, h


3)
ball-milling time, h
40
45
50
55









composite binding agents in Examples 3-6 consist of the above additives and metal binding agents, respectively, and the rest parts are the same with those in Example 1. The grinding wheels in Examples 3-6 are made from the above composite binding agents and diamond abrasives, respectively, and the rest parts are the same with those in Example 1.


Grinding effects of the grinding wheels in Examples 3-6 are detected, and results are as listed in Table 5.









TABLE 5







Detection Results of Grinding Effects of the Grinding Wheels


Obtained in Examples 3-6













Removal
Trimming
Service Life of



Strength
Rate
Frequency (Kg
Grinding


Grinding Wheel
(MPa)
(g/min)
each time)
Wheel (Kg)














Comparative
280
3
2.5
30


Example 1


Example 3
277
3.9
3.9
40


Example 4
273
4
3.6
35


Example 5
270
4.2
3
33


Example 6
269
3.3
5
45









It can be seen from Table 5 that, of substantially maintaining the original strength, the grinding wheel products using the additive in the present invention have improved sharpness, service life, and grinding performance.


Example 7

A self-sharpening diamond grinding wheel in the present example includes a grinding wheel substrate and an abrasive block, and the abrasive block is made from raw materials in a mass percentage as follows: Cu 28%, Sn 12%, Co 30%, Al 5%, Fe 3%, Cr 2%, Ti 2%, MoS2 3%, SG abrasive 2%, diamond 10%, and additive 3%.


The additive is made from raw materials in a mass percentage as follows: Bi2O3 35%, B2O3 35%, ZnO 10%, SiO2 5%, Al2O3 3%, Na2CO3 2%, Li2CO3 4%, MgCO3 2%, and CaF2 4%.


A method for preparing the additive includes the steps of:


1) mixing Bi2O3, B2O3, ZnO, SiO2, Al2O3, Na2CO3, Li2CO3, and MgCO3 of a formula ratio and evenly mixing them, then pouring the mixture in a quartz crucible, and placing the quartz crucible in a high-temperature resistance furnace to be heated at a rate of 10° C./min to 1250° C. and keeping the temperature for 2 h to provide a mixture;


2) cooling the mixture obtained in Step 1) to 850° C. at a rate of 5° C./min, adding CaF2 of the formula ratio to the mixture and stirring, and keeping the temperature for 2 h to provide a sinter;


3) pouring the sinter obtained in Step 2) into cold water (room temperature) to be quenched to provide a bulk material; putting the obtained bulk material and ethanol into a ball-mill tank to be ball-milled on a high-energy ball-milling machine for 60 h, to obtain a powder, i.e. the additive, having a particle size of D90<200 nm.


A method for manufacturing the self-sharpening diamond grinding wheel in the present example includes the steps of:


a) mixing Cu powder, Sn powder, Co powder, Al powder, Fe powder, Cr powder, Ti powder, MoS2 powder, SG abrasive, diamond and additive of a formula ratio, pouring them into a three-dimensional mixer to be mixed for 2 h, to provide a mixture;


b) loading the mixture obtained in Step a) into a steel mold, shaving and flattening the mixture, and placing the steel mold on an oil hydraulic press to be pressed at a pressure of 150 MPa, to provide a semifinished product.


c) loading the semifinished product obtained in Step b) in a graphite mold, and placing the graphite mold in a hot pressing sintering machine in an air atmosphere to be sintered, specifically: heating up to 400° C. at a heating rate of 100° C./min and keeping the temperature for 2 min, to promote the complete melting of Sn with a low melting point, so as to perform alloying reaction, and then heating up to 600° C. at a heating rate of 50° C./min and keeping the temperature for 8 min; after completing the temperature keeping, placing the mold in cold water (room temperature) to be quenched, to provide the abrasive block;


d) adhering the abrasive block obtained in Step c on a grinding wheel substrate to obtain the self-sharpening diamond grinding wheel.


Example 8

A self-sharpening diamond grinding wheel in the present example includes a grinding wheel substrate and an abrasive block, and the abrasive block is made from raw materials in a mass percentage as follows: Cu 44%, Sn 10%, Co 25%, Al 3%, Fe 2%, Cr 1%, Ti 3%, MoS2 1%, SG abrasive 5%, diamond 5%, and additive 1%.


The additive is made from raw materials in a mass percentage as follows: Bi2O3 25%, B2O3 40%, ZnO 5%, SiO2 2%, Al2O3 8%, Na2CO3 1%, Li2CO3 3%, MgCO3 5%, and CaF2 1%.


A method for preparing the additive includes the steps of:


1) mixing Bi2O3, B2O3, ZnO, SiO2, Al2O3, Na2CO3, Li2CO3, and MgCO3 of a formula ratio and evenly mixing them, then pouring the mixture in a quartz crucible, and placing the quartz crucible in a high-temperature resistance furnace to be heated at a rate of 10° C./min to 1300° C. and keeping the temperature for 1 h to provide a mixture;


2) cooling the mixture obtained in Step 1) to 850° C. at a rate of 5° C./min, adding CaF2 of the formula ratio to the mixture and stirring, and keeping the temperature for 2 h to provide a sinter;


3) pouring the sinter obtained in Step 2) into cold water (room temperature) to be quenched to provide a bulk material; putting the obtained bulk material and ethanol into a ball-mill tank to be ball-milled on a high-energy ball-milling machine for 50 h, to obtain a powder, i.e. the additive, having a particle size of D90<200 nm.


A method for manufacturing the self-sharpening diamond grinding wheel in the present example includes the steps of:


a) mixing Cu powder, Sn powder, Co powder, Al powder, Fe powder, Cr powder, Ti powder, MoS2 powder, SG abrasive, diamond and additive of a formula ratio, pouring them into a three-dimensional mixer to be mixed for 3 h, to provide a mixture;


b) loading the mixture obtained in Step a) into a steel mold, shaving and flattening the mixture, and placing the steel mold on an oil hydraulic press to be pressed at a pressure of 200 MPa, to provide a semifinished product.


c) loading the semifinished product obtained in Step b) in a graphite mold, and placing the graphite mold in a hot pressing sintering machine in an air atmosphere to be sintered, specifically: heating up to 450° C. at a heating rate of 100° C./min and keeping the temperature for 1 min, to promote the complete melting of Sn with a low melting point, so as to perform alloying reaction, and then heating up to 580° C. at a heating rate of 50° C./min and keeping the temperature for 10 min; after completing the temperature keeping, placing the mold in cold water (room temperature) to be quenched, to provide the abrasive block;


d) adhering the abrasive block obtained in Step c on a grinding wheel substrate to obtain the self-sharpening diamond grinding wheel.


Example 9

A self-sharpening diamond grinding wheel in the present example includes a grinding wheel substrate and an abrasive block, and the abrasive block is made from raw materials in a mass percentage as follows: Cu 25%, Sn 5%, Co 30%, Al 7%, Fe 1%, Cr 2%, Ti 1%, MoS2 2%, SG abrasive 6%, diamond 15%, and additive 6%.


The additive is made from raw materials in a mass percentage as follows: Bi2O3 30%, B2O3 25%, ZnO 19%, SiO2 10%, Al2O3 2%, Na2CO3 5%, Li2CO3 1%, MgCO3 3%, and CaF2 5%. A method for preparing the additive is the same as that in Example 7.


A method for manufacturing the self-sharpening diamond grinding wheel in the present example includes the steps of:


a) mixing Cu powder, Sn powder, Co powder, Al powder, Fe powder, Cr powder, Ti powder, MoS2 powder, SG abrasive, diamond and additive of a formula ratio, pouring them into a three-dimensional mixer to be mixed for 4 h, to provide a mixture;


b) loading the mixture obtained in Step a) into a steel mold, shaving and flattening the mixture, and placing the steel mold on an oil hydraulic press to be pressed at a pressure of 170 MPa, to provide a semifinished product.


c) loading the semifinished product obtained in Step b) in a graphite mold, and placing the graphite mold in a hot pressing sintering machine in an air atmosphere to be sintered, specifically: heating up to 400° C. at a heating rate of 100° C./min and keeping the temperature for 1 min, to promote the complete melting of Sn with a low melting point, so as to perform alloying reaction, and then heating up to 620° C. at a heating rate of 50° C./min and keeping the temperature for 4 min; after completing the temperature keeping, placing the mold in cold water (room temperature) to be quenched, to provide the abrasive block;


d) adhering the abrasive block obtained in Step c on a grinding wheel substrate to obtain the self-sharpening diamond grinding wheel.


Example 10

A self-sharpening diamond grinding wheel in the present example includes a grinding wheel substrate and an abrasive block, and the abrasive block is made from raw materials in a mass percentage as follows: Cu 25%, Sn 20%, Co 20%, Al 5%, Fe 5%, Cr 3%, Ti 1%, MoS2 2%, SG abrasive 3%, diamond 7%, and additive 9%.


The additive is made from raw materials in a mass percentage as follows: Bi2O3 40%, B2O3 30%, ZnO 5%, SiO2 8%, Al2O3 5%, Na2CO3 3%, Li2CO3 5%, MgCO3 1%, and CaF2 3%. A method for preparing the additive is the same as that in Example 7.


A method for manufacturing the self-sharpening diamond grinding wheel in the present example includes the steps of:


a) mixing Cu powder, Sn powder, Co powder, Al powder, Fe powder, Cr powder, Ti powder, MoS2 powder, SG abrasive, diamond and additive of a formula ratio, pouring them into a three-dimensional mixer to be mixed for 4 h, to provide a mixture;


b) loading the mixture obtained in Step a) into a steel mold, shaving and flattening the mixture, and placing the steel mold on an oil hydraulic press to be pressed at a pressure of 160 MPa, to provide a semifinished product.


c) loading the semifinished product obtained in Step b) in a graphite mold, and placing the graphite mold in a hot pressing sintering machine in an air atmosphere to be sintered, specifically: heating up to 350° C. at a heating rate of 100° C./min and keeping the temperature for 3 min, to promote the complete melting of Sn with a low melting point, so as to perform alloying reaction, and then heating up to 610° C. at a heating rate of 50° C./min and keeping the temperature for 3 min; after completing the temperature keeping, placing the mold in cold water (room temperature) to be quenched, to provide the abrasive block;


d) adhering the abrasive block obtained in Step c on a grinding wheel substrate to obtain the self-sharpening diamond grinding wheel.


Example 11

A self-sharpening diamond grinding wheel in the present example includes a grinding wheel substrate and an abrasive block, and the abrasive block is made from raw materials in a mass percentage as follows: Cu 30%, Sn 5%, Co 35%, Al 10%, Fe 3%, Cr 3%, Ti 2%, MoS2 1%, SG abrasive 2%, diamond 5%, and additive 4%.


The additive is made from raw materials in a mass percentage as follows: Bi2O3 25%, B2O3 25%, ZnO 25%, SiO2 6%, Al2O3 10%, Na2CO3 2%, Li2CO3 2%, MgCO3 3%, and CaF2 2%. A method for preparing the additive is the same as that in Example 7.


A method for manufacturing the self-sharpening diamond grinding wheel in the present example includes the steps of:


a) mixing Cu powder, Sn powder, Co powder, Al powder, Fe powder, Cr powder, Ti powder, MoS2 powder, SG abrasive, diamond and additive of a formula ratio, pouring them into a three-dimensional mixer to be mixed for 2 h, to provide a mixture;


b) loading the mixture obtained in Step a) into a steel mold, shaving and flattening the mixture, and placing the steel mold on an oil hydraulic press to be pressed at a pressure of 180 MPa, to provide a semifinished product.


c) loading the semifinished product obtained in Step b) in a graphite mold, and placing the graphite mold in a hot pressing sintering machine in an air atmosphere to be sintered, specifically: heating up to 450° C. at a heating rate of 100° C./min and keeping the temperature for 2 min, to promote the complete melting of Sn with a low melting point, so as to perform alloying reaction, and then heating up to 590° C. at a heating rate of 50° C./min and keeping the temperature for 8 min; after completing the temperature keeping, placing the mold in cold water (room temperature) to be quenched, to provide the abrasive block;


d) adhering the abrasive block obtained in Step c on a grinding wheel substrate to obtain the self-sharpening diamond grinding wheel.


Self-sharpening diamond grinding wheels in Examples 12-16 use the abrasive blocks obtained in Examples 7-11 as the grinding blocks, respectively. It is also possible to omit the grinding wheel substrate.


Experimental Example

In the present Experimental Example, functional performances of the self-sharpening diamond grinding wheels obtained in Examples 7-11 are detected, and results are as listed in Table 6.


Wherein raw materials of an abrasive block of the conventional grinding wheel consist of components of mass percentage as follows: Cu 50%, Sn 25%, Co 15%, and diamond 10%; a manufacturing method is the same as that in Example 4.









TABLE 6







Detection Results of Functional Performances of Self-sharpening


Diamond Grinding Wheels Obtained in Examples 7-11




















Spindle Motor




Grinding
Trimming
Trimming
Total
Processing
Current Mean


Item
Object
Mode
Time
Hours
Amount
Value
Yield





Conventional
sapphire
manual
6 times/12
60 h
153 pieces
35 A
98.7%


grinding wheel

trimming
0 min


Example 7
sapphire
none
0
60 h
183 pieces
33 A
98.6%


Example 8
sapphire
none
0
60 h
189 pieces
34 A
98.8%


Example 9
sapphire
none
0
60 h
177 pieces
28 A
98.7%


Example 10
sapphire
none
0
60 h
180 pieces
27 A
98.9%


Example 11
sapphire
none
0
60 h
175 pieces
29 A
99.1%





Notes:


the bigger a spindle motor current, the bigger a load.






It can be seen from Table 6 that since the diamond grinding wheels in Examples 7-11 have good self-sharpening ability, the trimming step is omitted, thus the trimming cost is saved, and the trimming time is transferred to the processing of the workpiece; during the same period of time, the processing amount is increased by about 17%, and the processing efficiency is improved; moreover, during the grinding process, the grinding load (resistance) is decreased, the sharpness of the grinding wheel is improved, and the yield is comparable. The detection results show that the diamond grinding wheels in the present invention have high self-sharpness, high strength, and high processing efficiency, is uniformly consumed during the grinding process, and do not need to be trimmed during the process of being used in the whole life cycle, moreover, during the grinding process, they maintain good grinding force all the time, fundamentally solving the problems of long trimming time and high trimming cost of the diamond grinding wheel, and possessing good economic benefit.

Claims
  • 1. An additive for a superhard material product, made from raw materials in a mass percentage as follows: Bi2O3 25%˜40%, B2O3 25%˜40%, ZnO 5%˜25%, SiO2 2%˜10%, Al2O3 2%˜10%, Na2CO3 1%˜5%, Li2CO3 1%˜5%, MgCO3 0%˜5%, and CaF2 1%˜5%.
  • 2. A self-sharpening diamond grinding wheel, comprising an abrasive block, wherein raw materials of the abrasive block comprise a metal binding agent, MoS2, SG abrasive, diamond and the additive of claim 1; and the content of mass percentage of the additive in the raw materials of the abrasive block is 1%˜10%.
  • 3. The self-sharpening diamond grinding wheel according to claim 2, wherein the additive is made from raw materials in a mass percentage as follows: Bi2O3 25%˜35%, B2O3 25%˜35%, ZnO 5%˜10%, SiO2 5%˜10%, Al2O3 5%˜10%, Na2CO3 1%˜5%, Li2CO3 1%˜5%, MgCO3 1%˜5%, and CaF2 1%˜5%.
  • 4. The self-sharpening diamond grinding wheel according to claim 2, wherein the additive is prepared by a method comprising steps of: 1) mixing Bi2O3, B2O3, ZnO, SiO2, Al2O3, Na2CO3, Li2CO3, and MgCO3 of a formula ratio, raising a temperature to 1200˜1400° C. and keeping temperature for 1˜3 h to provide a mixture;2) cooling the mixture obtained in Step 1) to 850˜950° C., adding CaF2 of the formula ratio and mixing, and keeping temperature for 1˜2 h to provide a sinter;3) quenching the sinter obtained in Step 2) and then crushing the quenched sinter to make the quenched sinter in a particle size of D90<200 nm to provide the additive.
  • 5. The self-sharpening diamond grinding wheel according to claim 2, wherein the metal binding agent consists of components in parts by weight as follows: Cu 25˜45 parts, Sn 5˜20 parts, Co 20˜35 parts, Al 3˜10 parts, Fe 1˜5 parts, Cr 1˜3 parts, and Ti 1˜3 parts.
  • 6. The self-sharpening diamond grinding wheel according to claim 2, wherein in the raw materials of the abrasive block, a mass ratio of the SG abrasive to the diamond is (2˜6):(5˜15).
  • 7. The self-sharpening diamond grinding wheel according to claim 6, wherein the abrasive block is made from raw materials in a mass percentage as follows: Cu 25%˜45%, Sn 5%˜20%, Co 20%˜35%, Al 3%˜10%, Fe 1%˜5%, Cr 1%˜3%, Ti 1%˜3%, MoS2 1%˜3%, SG abrasive 2%˜6%, diamond 5%˜15%, and additive 1%˜10%.
  • 8. The self-sharpening diamond grinding wheel according to claim 2, further comprising a grinding wheel substrate, wherein the abrasive block is adhered onto the grinding wheel substrate.
  • 9. A method for manufacturing the self-sharpening diamond grinding wheel according to claim 2, comprising steps of: a) mixing a metal binding agent, MoS2 powder, SG abrasive, diamond and the additive of claim 1 to provide a mixture;b) placing the mixture obtained in Step a) in a mold and pressing the mixture to provide a semifinished product;c) placing the semifinished product obtained in Step b) in a mold, raising a temperature to 580˜620° C. and keeping temperature for 4˜10 min for sintering, followed by quenching, to provide the abrasive block.
  • 10. The method for manufacturing the self-sharpening diamond grinding wheel according to claim 9, wherein in Step b), a pressure of the pressing is 150˜200 MPa.
  • 11. The method for manufacturing the self-sharpening diamond grinding wheel according to claim 9, wherein in Step c), the raising temperature refers to firstly raising the temperature to 350˜450° C. at a heating rate of 100° C./min and keeping temperature for 1˜3 min, and then raising the temperature to 580˜620° C. at a heating rate of 50° C./min.
  • 12. The method for manufacturing the self-sharpening diamond grinding wheel according to claim 9, further comprising adhering the obtained abrasive block on a grinding wheel substrate to provide the self-sharpening diamond grinding wheel.
Priority Claims (1)
Number Date Country Kind
PCT/CN2017/082264 Apr 2017 CN national
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of allowed U.S. application Ser. No. 15/561,143, filed Sep. 25, 2017, entitled “Additive Composition And Composition Binding Agent For Superhard Material And Preparation Thereof, And Self-Sharpening Diamond Grinding Wheel And Preparation Thereof” of which the full disclosure of this application is incorporated herein by reference for all purposes.

Divisions (1)
Number Date Country
Parent 15561143 Sep 2017 US
Child 16520778 US