The present application relates to the field of tools having internal channels, as well as to methods for manufacturing tools having internal channels.
Tools for manufacturing, such as metal forming/shaping tools or composite manufacturing tools, may be heated during the manufacturing process to cure pre-impregnated thermosets. Internal channels may be provided within such tools to provide a uniform tool surface temperature. A heated material, such as pressurized water (e.g., liquid water), propylene glycol, or steam, may flow through the channels to heat the tool.
A conformal channel approach may be used to improve manufacturing of pre-impregnated composites by providing more uniform heating of a tool surface. A conformal channel approach provides internal passages that generally conform to or follow the contour of a surface of the tool. Since the surface of a tool may have a complex shape, it can be challenging to provide conformal passages in a desired location within the tool.
Accordingly, those skilled in the art continue with research and development in the field of tools for manufacturing, which have internal channels, as well as in the field of methods for manufacturing tools having internal channels.
Disclosed are methods for manufacturing a tool having one or more internal channels.
In one example, the method includes forming one or more channel cores by additive manufacturing, coating a metal onto the one or more channel cores to form a metal tube on each of the one or more channel cores, positioning the one or more metal tubes into a casting mold having a shape of a tool, and casting a molten metal into the casting mold to form the tool having the one or more internal channels corresponding to the one or more channel cores.
In another example, the method includes forming one or more channel cores by additive manufacturing, positioning the one or more channel cores into a casting mold having a shape of a tool, and casting a molten metal into the casting mold to form the tool having the one or more internal channels corresponding to the one or more channel cores.
Also disclosed are tools that include a tool body comprising a surface, the surface comprising a surface contour, and a conforming internal channel having one or more directional changes and following the surface contour of the surface of the tool.
Other examples of the disclosed tools having internal channels and methods for manufacturing tools will become apparent from the following detailed description, the accompanying drawings and the appended claims.
This disclosure relates to tools having internal channels and methods for manufacturing such tools.
The channel core may be formed from any material suitable for forming by additive manufacturing. In particular, the channel core may include a polymer binder. In the case of casting a molten metal having a high melting temperature, the channel core may include a high temperature polymer binder, such as a phenolic binder, e.g., furan resin. Additionally, the channel core may include a higher temperature inorganic material, such as a refractory. For example, the channel core may include a refractory and a high temperature polymer binder, such as phenolic binder, as a binder for binding the refractory. An exemplary refractory may include a ceramic sand, such as sodium silicate.
The channel core may include a first end, a second end, and a cross-section. The cross-section of the channel core should correspond with an internal channel to be formed in the resulting tool. The cross-section of the channel core and may be, for example, a round cross-section or an oval cross-section. Further, the channel core may have, for example, a solid cross-section or a hollow cross-section.
Between the first end and the second end of the channel core, the channel core may include one or more directional changes. The directional changes may facilitate a conformal channel approach for provides internal channels that generally conform to or follow the surface contour of a surface of a resulting tool.
The channel core may further include one or more exterior reinforcements. The exterior reinforcements may help the channel core maintain a desired shape and position within the casting mold during a high temperature casting process that may tend to deform the channel core.
Forming the channel core by an additive manufacturing process facilitates providing a channel core having a complex shape to thereby provide complex conformal internal channels in a desired location within the tool and to provide exterior reinforcements to help the channel core maintain a desired shape and position within the casting mold. The channel core may be formed by any suitable additive manufacturing process. In an example, the channel core may be formed by a powder-based additive manufacturing method, such as selective laser sintering, electron beam melting, selective laser melting, etc. In another example, the channel core may be formed by filament-based additive manufacturing method, such as fused filament fabrication.
A powder-based additive manufacturing method may be particularly suitable for forming a channel core from a composite material of a high temperature polymer binder, such as a phenolic binder, and a higher temperature inorganic material, such as a refractory.
A metal may be coated onto the channel core to form a metal tube on the channel core.
The metal used for the step of coating metal onto the channel core to form a metal tube may include any metal compatible for use with the molten metal. For example, the metal used for the step of coating metal may be the same as the molten metal or the metal used for the step of coating metal may be a component material of the molten metal.
The coating process used for coating metal onto the channel core to form a metal tube may include any process suitable for coating onto the material used to form the channel core. In particular, suitable coating processes include kinetic fusion and electroless deposition.
The thickness of the coated metal should be sufficient to withstand the molten metal such that a shape and position of the channel core is maintained during the casting step. A minimum thickness may depend on the selection of the coated metal and the selection of the molten metal.
The channel core may be positioned into a casting mold having a shape of a tool such that the channel core is positioned within the casting mold to correspond with a desired position of an internal channel of the tool. In this case, the channel core may be uncoated or may be coated with a metal. Alternatively, the channel core may be removed from the metal tube, and the metal tube may be positioned into a casting mold having a shape of a tool such that the metal tube is positioned within the casting mold to correspond with a desired position of an internal channel of the tool.
The channel core and/or metal tube may be positioned into a casting mold having a shape of a tool such that the channel core and/or metal tube is positioned within the casting mold to correspond with a desired position of a channel of the tool. The metal tube may be positioned into the cast mold while the metal tube is still coated onto the channel core, or the channel core may be removed from the metal tube prior to positioning the metal tube into the casting mold, or the channel core may be positioned into the cast mold without the metal tube. Retaining the channel core within the metal tube during the positioning and the casting may be advantageous for helping the metal tube to retain the desired position within the casting mold during the casting process. When the channel core is formed from high temperature materials, such as phenolic binder and/or refractory, the channel core may help the metal tube to retain the desired position within the casting mold during the casting process when a high temperature metal is used as the molten metal.
The channel core, such as polymer channel core, may be removed before, during, or after casting the molten metal. The channel core (e.g., polymer channel core) may be removed by, for example, melting the channel core, burning the channel core, or decomposing the channel core. By removing the channel core from the metal tube, the metal tube provides the resulting cast tool with a channel therein corresponding to the removed channel core.
Alternatively, the channel core may be formed from metal. The metal used for the channel core may include any metal compatible for use with the molten metal used in the casting step. For example, the metal used for the channel core may be the same as the molten metal or the metal used for the channel core may be a component material of the molten metal.
In an aspect, the channel core or metal tube may be supported at first and second ends by the casting mold itself. Support of the channel core or metal tube by the casting mold may be sufficient for small tools having small channels. However, for large tools having large channels, the support of the channel core or metal tube by the casting mold may be insufficient to retain the desired position of the channel core or metal tube within the casting mold, and additional supports may be included.
In an aspect, the channel core or metal tube may be supported using metal supports positioned within the casting mold. The metal supports may include any metal compatible for use with the molten metal. For example, the metal used for the metal supports may be the same as the molten metal or the metal used for the metal supports may be a component material of the molten metal. The shape of the metal supports should be sufficient to withstand the molten metal such that the channel core or metal tube is supported during the casting step. The required shape of the metal supports may depend on the selection of the metal used for the metal supports and the selection of the molten metal.
In an aspect, the channel core includes one or more integrated supports, and positioning the channel core or metal tube into the casting mold may include supporting the channel core or metal tube using the integrated supports of the channel core. The one or more integrated supports may be formed from, for example, the same material as the channel core. The one or more integrated supports may be coated during the coating step for coating the channel core. The shape of the integrated supports should be sufficient to withstand the molten metal such that the channel core or metal tube is supported during the casting step. The required shape of the integrated supports may depend on the selection of the material used for the integrated supports and the selection of the molten metal.
The molten metal used for casting may include any metal suitable for used for the resulting tool. An exemplary molten metal may include, for example, steel.
The casting mold may include any material suitable for use for a casting mold for the selected molten metal, such as a die mold. An exemplary casting mold may include a sand casting mold.
Referring to
Referring to
The method of the present description may be used to form a tool. The material used for forming a tool body of the tool may include any material suitable for used for the desired application for the tool. An exemplary tool body material may include, for example, steel.
Although various examples of the disclosed tools having internal channels and methods for manufacturing tools have been shown and described, modifications may occur to those skilled in the art upon reading the specification. The present application includes such modifications and is limited only by the scope of the claims.