Patent Application
20070240780
These figures are not drawn to scale and are intended only for illustrative purposes. While the invention is amenable to various modifications and alternative forms, specifics thereof have been shown by way of example in the drawings and will be described in detail. It should be understood, however, that the intention is not to limit the invention to the particular embodiments described. On the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the scope of the invention as defined by the appended claims.
Aspects of the present invention relate to an adhesion promoting end treatment system and method for protecting girth-welds. In particular, an adhesion promoting end treatment material can be applied, for example, in film or molten form, to the ends of pipes during the pipe manufacturing process in the factory. The factory applied adhesion promoting end treatment materials can be automatically applied to a pipe end immediately after a protective (e.g., three-layer) coating process and before the cutting and quenching of the protective coating applied to the pipe. After welding of the pipe ends in the field to form the girth-weld, a heat recoverable polymer-containing protective cover material, formed as e.g., a heat shrink sleeve or cover, can be placed over the girth-weld. The adhesion promoting end treatment material can thus provide a preferable adhesive surface for the polymer-containing protective cover material to adhere to in the field, as polymer-containing protective cover materials do not adhere well to standard protective coatings, such as, for example, polyolefin, especially polyethylene, coatings.
Pipe end 100 further includes an uncoated portion 104. After the coating process is complete (see details below), a portion of the pipe coating, about 2 to 10 inches in length from the pipe end, is removed, stripped, or sanded off to help promote better welding in the field. This stripping operation can be performed in the factory.
In an exemplary embodiment, the pipe end 100 further includes an adhesion promoting end treatment material 110 that is applied to the three layer coating 106 proximate to the pipe end region. The adhesion promoting end treatment can be a one-layer or multilayer construction. For example, a one-layer adhesion promoting end treatment can comprise at least one of: a polyolefin with a lower melting point than the mainline (topcoat) polyolefin coating, for example, a low-density polyethylene; EVA; formulated EVA hotmelt adhesive; a polyethylene copolymer, for example, ethylene maleic anhydride, ethylene carboxylic acid; and ethylene acrylic acid.
In another example, an exemplary multilayer adhesion promoting end treatment can include a “weldable” polyolefin layer and one or more adhesion promoting end treatment layers. The weldable polyolefin layer is bondable to the mainline polyolefin, especially when both are in a molten form, as in the mainline coating process (described below). The adhesion promoting end treatment layer or layers can comprise, for example, at least one of: a low-density polyethylene, EVA, formulated EVA hotmelt adhesive, a polyethylene copolymer, for example, ethylene maleic anhydride, ethylene carboxylic acid and ethylene acrylic acid.
As described in more detail below, in an exemplary aspect, the adhesion promoting end treatment material 110 can comprise a polymer film that is similar in structure to the polyolefin topcoat and that can bond a polymer-containing protective cover material, such as a heat shrink material, to the protective coating. The adhesion promoting end treatment material 110 can be applied to the pipe end region, as part of a manufacturing process, by, e.g., coextrusion with the mainline polyolefin, extrusion from multiple dies, by lamination of a nonwoven or woven film or a multilayer polyolefin/adhesion promoter construction, or by spraying the adhesion promoting end treatment on the polyolefin topcoat in the factory. The adhesion promoting end treatment material 110 adheres to the three layer coating 106 and to a polymer-containing protective cover material that is applied in the field and is utilized to protect the girth-weld.
As mentioned above, a conventional method to protect a girth-weld is utilizing a polymer-containing protective cover material, such as a heat shrink sleeve, to cover the girth-weld. However, conventionally installed heat shrink sleeves tend to provide diminished protection prior to the end of the expected service lifetime as the sleeves are susceptible to moving away from the weld, thereby leaving the joint only partially protected or unprotected. A current problem is that conventional heat shrink materials do not adhere well to conventional three layer coatings. However,
The adhesion promoting end treatment material 110 or 210 can be applied to a pipe end as part of a pipe coating process, in accordance with the process shown in
Optionally, the pipe 301 outer surface can be further cleaned using a grinding technique 306 that grinds surface defects. The pipe surface can be inspected in step 308.
The pipe segments 301 are transported end to end on the assembly line in step 310 for a final surface treatment 312, where the pipe can be acid washed to remove any remaining contamination. Prior to application of a protective coating, pipe segments 301 are heated in step 314. One preferred heating technique is the use of induction coils to bring the surface temperature of the pipe to an elevated temperature of about 180° C. to about 240° C.
A protective coating is then applied to the outer surface of pipe 301. In a preferred aspect, the protective coating is a three-layer coating such as described above. As would be understood by one of ordinary skill in the art given the present description, other protective coatings, such as two-layer coatings, and those described in the Kehr reference, cited above (see e.g., Chapter 4 and pages 234-246) (incorporated by reference herein), can also be utilized as the protective coat for pipe 301.
In an exemplary embodiment, in step 316, an epoxy layer, such as a fusion bonded epoxy (FBE) powder is applied to the heated outer surface of pipe 316. In a preferred aspect, the FBE is applied through an electrostatic process. Once the FBE is applied to the heated pipe, it melts and flows onto the metal surface, resulting in a coating having a thickness of about 4 mils to about 10 mils. In step 318, an adhesive layer, such as a copolymer, is applied to the FBE. Preferably, the copolymer is applied using a conventional extrusion process, as the pipe 301 is rotated during the coating process. In step 320, the polyolefin top coating is applied. Preferably, a polyolefin, such as polypropylene or polyethylene, is applied using an extrusion process.
In one aspect of the invention, in step 322, an adhesion promoting end treatment material is applied to at least a portion of the coated pipe surface, at or near the pipe ends. The adhesion promoting end treatment material, which can be a one layer or multilayer construction, can be applied as a film or as a molten material. In one aspect, a film, such as a homogeneous polymer film, can be applied to the heated polyolefin layer using an extrusion process, as the adhesion promoting end treatment material can sufficiently adhere to the molten polyolefin. The residual heat from the pipe 301 can melt the adhesion promoting end treatment material and permit it to fuse with the polyolefin as they both cool.
For example, the homogeneous polymer film can be applied using a lamination process. For example, a two-foot wide film could be laminated to straddle the joint between the pipe ends. The film can either be pre-sectioned in a length equal to the pipe circumference or a continuous roll that can be sectioned or cut after one full rotation of the pipe. This adhesion promoting end treatment material film can be laminated to the polyolefin coated pipe in an intermittent fashion.
In a further alternative, the adhesion promoting end treatment material comprises a homogeneous polymer film that can be coextruded with the polyolefin coating.
In a further alternative, the adhesion promoting end treatment material is applied to the protective coating directly as a molten material instead of as a film. For example, a coating die or melt spray system can apply the molten material, followed by a wipe process. The molten material is preferably applied intermittently to only cover a portion of the pipe end, for example about 8 to about 16 inches on each pipe end.
In a preferred aspect, the adhesion promoting end treatment material comprises a one-layer or multilayer construction, such as described above. In a further preferred aspect, the adhesion promoting end treatment material has a chemical structure similar to that of the top coating it is applied to (e.g., a polyethylene or a copolymer of polyethylene). For exemplary coextruded or laminated films, one side of the adhesion promoting end treatment material can comprise a polyethylene or a copolymer of polyethylene and the other side can comprise a textured polymeric material, such as, PVC, phenoxy resin, polycarbonate, nylon, or polypropylene, which adheres to mastic or modified polyolfin materials that comprise the heat shrink adhesive. The texture can be imparted by embossing, patterned printing, subtractive methods, such as grinding or cutting. As would be understood by one of ordinary skill in the art given the present description, the formulation of the adhesion promoting end treatment material can be tailored to the particular type of girth-weld cover being utilized in the field. For example, as noted above, exemplary adhesion promoting end treatment materials can include EVA, formulated EVA hotmelt adhesive, or other copolymers of polyethylene.
Alternatively, for girth-weld cover systems that utilize a thermoset corrosion coating as an adhesive between the polyethylene coated pipe and the girth-weld wrap or cover, the adhesion promoting end treatment material can comprise a laminated multilayer construction such as EVA or polyethylene, disposed on one side and a fabric disposed on the other. The fabric can comprise a woven, non-woven, or knit material. This fabric wrap can wrapped around the pipe end and pressed into the molten polyolefin while still at elevated temperature.
Referring back to
Referring back to
After the optional coating 222 is applied and/or at least partially cured, sleeve or cover 220 is slid down to cover weld 204. In an alternative aspect, adhesion promoting end treatment material 210 is applied to the pipe ends as a pressure sensitive adhesive, such as a dual-sided tape. An exemplary dual sided tape is a VHB tape, available from 3M Company (St. Paul, Minn.). The adhesion promoting end treatment material 210 can further include a release liner that is removed just prior to placement of the heat shrink sleeve or cover 220 over the girth-weld 204. The release liner can cover the adhesive wrap for extra protection during shipping of the pipe.
To conform a heat shrink sleeve 220 to the surface of the girth-weld 204, heat is applied (e.g., via a hot air gun or torch) to sleeve 220. In one exemplary embodiment, the protective sleeve comprises a sheet that is wrapped around the pipe (to cover the girth-weld), then sealed longitudinally (e.g., by heating the overlap region). The sleeve can then be shrunk by applying heat. A technician, for example, can start at the center of the sleeve (with the weld seam being directly underneath the sleeve) and can seal the sleeve around the pipe by heating radially, working outward (longitudinally) from the middle—alternating in each direction—to completely shrink the sleeve. The adhesion promoting end treatment material 210 thus bonds the heat shrink cover or sleeve 220 in place, thus substantially reducing the likelihood of the disbandment or movement of the sleeve 220 from the pipe ends.
While the present invention has been described with a reference to exemplary preferred embodiments, the invention may be embodied in other specific forms without departing from the scope of the invention. Accordingly, it should be understood that the embodiments described and illustrated herein are only exemplary and should not be considered as limiting the scope of the present invention. Other variations and modifications may be made in accordance with the scope of the present invention.
This application claims the benefit of U.S. Provisional Patent Application No. 60/744,964, filed Apr. 17, 2006, the disclosure of which is incorporated by reference herein in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 60744964 | Apr 2006 | US |