Claims
- 1. An adhesive composition which comprises:
- (a) a neutralized sulfonate containing polymer having about 0.2 to 3 weight percent of chemically combined sulfur wherein said neutralized sulfonated co- or terpolymer comprises at least 80% by weight of at least one conjugated diene having from 4 to 12 carbon atoms and a minor proportion of a metal or amine neutralized sulfonate monomer characterized by the formula: ##STR6## where X is (CH.sub.2).sub.n, or aromatic, wherein n=0, 1, 2, 3, 4, and Y is a cation selected from Groups IA, IIA, IB and IIB of the periodic table or an amine of the formula: ##STR7## where R.sub.1 and R.sub.2 can be aliphatic groups of C.sub.1 to C.sub.12 or hydrogen, said co- or terpolymer being water insoluble; and
- (b) about 25 to about 200 parts by weight of a hydrocarbon tackifying resin based on a petroleum or coal tar distillate per 100 parts by weight of said sulfonate containing polymer.
- 2. An adhesive composition according to claim 1, wherein said adhesive composition is a hot melt adhesive composition.
- 3. A composition according to claim 1, wherein said sulfonate containing monomer is a metal neutralized sulfonated styrene.
- 4. A composition according to claim 1 or 3, wherein said conjugated diene is selected from the group consisting of 1,3-butadiene, isoprene and chloroprene and mixtures thereof.
- 5. A composition according to claim 3, wherein said conjugated diene is isoprene.
- 6. A composition according to claim 3, wherein said conjugated diene is 1,3-butadiene.
- 7. A hot melt adhesive according to claim 1 or 2, further including about 3 to about 75 parts by weight of an ionic preferential plasticizer per 100 parts by weight of said neutralized sulfonated co- or terpolymer, wherein said preferential plasticizer is selected from the group consisting of carboxylic acids having about 8 to about 22 carbon atoms, metallic salts of said carboxylic acids, amides having an aliphatic group of about 8 to about 22 carbon atoms, amines, ureas and thioureas and mixtures thereof.
- 8. A hot melt adhesive according to claim 7, wherein said preferential plasticizer is said metallic salt of said carboxylic acid.
- 9. A hot melt adhesive composition according to claim 8, wherein said metallic salt of said carboxylic acid is zinc stearate.
- 10. A hot melt adhesive composition according to claims 1 or 2 further including about 5 to about 800 parts by weight of a filter per 100 parts by weight of said sulfonate containing polymer, said filler being selected from the group consisting of calcium carbonates, silicas, carbon blacks, clays and talcs and mixtures thereof and/or less than about 100 parts by weight of an oil having less than 2 wt. % polars per 100 parts by weight of said sulfonate containing polymer.
- 11. A hot melt adhesive composition according to claims 1 or 2 wherein said hydrocarbon resin has about 5 to about 6 carbon atoms and consists of aliphatic dienes, mono and di-olefins and cyclic olefins.
- 12. An adhesive composition according to claim 1 further including a solvent.
CROSS REFERENCE TO RELATED APPLICATIONS
This is a continuation-in-part application of U.S. Ser. No. 196,213, filed Oct. 14, 1980 and now abandoned which is based on P.M. CRL-190-78.
US Referenced Citations (13)
Foreign Referenced Citations (1)
Number |
Date |
Country |
1422124 |
Jan 1976 |
GBX |
Non-Patent Literature Citations (4)
Entry |
Derwent Abst. 13124 Y/08 (DT2536397), Feb. 1977. |
Derwent Abst. 76473 Y/43 (J50126038), Oct. 1975. |
Derwent Abst. 55633 A/31 (J53071139), Jun. 1978. |
Chem. Abs. 94-104176 (14), Lundberg et al., 1980. |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
196213 |
Oct 1980 |
|