Adhesives for low surface energy materials

FIELD

This disclosure relates generally to adhesive formulations. More particularly, this disclosure relates to adhesive formulations that can be utilized in the roofing arts.

BACKGROUND

Current systems and methods for roofing protection of commercial and residential roofing often employ an adhesive-only system that provides good protection and has a long installed life, but can be difficult to achieve strong, enduring adhesion between the membrane materials and a roof substrate. Adhesive-only systems can be difficult to install, may use a fleecy layer to aid adhesion, and may utilize application of the adhesive to both the membrane and the roof substrate.

SUMMARY

In some embodiments, a roofing system includes a roofing membrane. In some embodiments, the roofing membrane has a surface energy of 40 mN/m or less. In some embodiments, the roofing system includes a roofing substrate; and an adhesive disposed between the roofing membrane and the roofing substrate. In some embodiments, the adhesive includes a styrenic block copolymer. In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive. In some embodiments, the adhesive includes asphalt. In some embodiments, the asphalt is present in an amount of 70 wt. % to 99.5 wt. % based on the total weight of the adhesive. In some embodiments, a ratio of the styrenic block copolymer to the asphalt in the adhesive is 1:11 to 1:3.

In some embodiments, the roofing substrate is a second roofing membrane.

In some embodiments, the roofing substrate is a cellulosic based material.

In some embodiments, the adhesive further comprises a filler. In some embodiments, the filler is calcium carbonate, barium sulfate, calcium sulfate, talc, limestone, perlite, silica, fumed silica, precipitated silica, quartz, aluminum trihydrate, magnesium hydroxide, colemanite, titanium dioxide, snow white, fly ash, graphene nanoparticles, carbon black, recycled rubber tires, recycled shingles, recycled thermoplastic resins, basalt, roofing granules, clay, ammonium polyphosphate, graphite, expandable graphite, or any combination thereof.

In some embodiments, a roofing system includes a roofing membrane. In some embodiments, the roofing membrane has a surface energy of 40 mN/m or less. In some embodiments, the roofing system includes a roofing substrate; and an adhesive disposed between the roofing membrane and the roofing substrate. In some embodiments, the adhesive includes a styrene-butadiene-styrene (SBS) copolymer. In some embodiments, the SBS copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive. In some embodiments, the adhesive includes a process oil. In some embodiments, the process oil is present in an amount of 20 wt. % to 70 wt. % based on a total weight of the adhesive. In some embodiments, asphalt is present in an amount of less than 1 wt. % based on the total weight of the adhesive. In some embodiments, a ratio of the SBS copolymer to the process oil in the adhesive is 1:10 to 1:3.

In some embodiments, the process oil is chosen from at least one paraffinic oil, at least one bio-oil, at least one petroleum extract, at least one vegetable oil, at least one naphthenic oil, at least one aromatic oil, at least one re-refined engine oil bottom (REOB), at least one engine oil residue (EOR), at least one re-refined heavy vacuum distillation bottom (RHVDB), at least one re-refined heavy vacuum distillation oil (RHVDO), at least one re-refined vacuum tower bottom (RVTB), at least one vacuum tower bottom (VTB), at least one blend of process oil and a plasticizer, or any combination thereof.

In some embodiments, the roofing substrate is a second roofing membrane.

In some embodiments, the roofing substrate is a cellulosic based material.

In some embodiments, the adhesive comprises a recycled asphalt shingle waste.

In some embodiments, a method includes obtaining a styrenic block copolymer; obtaining asphalt; and mixing the styrenic block copolymer with the asphalt to form an adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 70 wt. % to 99.5 wt. % based on a total weight of the adhesive formulation. In some embodiments, a ratio of the styrenic block copolymer to the asphalt in the adhesive formulation is 1:11 to 1:3.

In some embodiments, the method includes adding a filler. In some embodiments, the filler is calcium carbonate, barium sulfate, calcium sulfate, talc, limestone, perlite, silica, fumed silica, precipitated silica, quartz, aluminum trihydrate, magnesium hydroxide, colemanite, titanium dioxide, snow white, fly ash, graphene nanoparticles, carbon black, recycled rubber tires, recycled shingles, recycled thermoplastic resins, basalt, roofing granules, clay, ammonium polyphosphate, graphite, expandable graphite, or any combination thereof.

In some embodiments, the filler is present in an amount of 0.00001% to 70% by weight of the adhesive formulation.

In some embodiments, a method includes obtaining a styrene-butadiene-styrene (SBS) copolymer; obtaining a process oil; and mixing the SBS copolymer with the process oil to form an adhesive formulation. In some embodiments, the SBS copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive formulation. In some embodiments, the process oil is present in an amount of 20 wt. % to 70 wt. % based on a total weight of the adhesive formulation. In some embodiments, asphalt is present in an amount of less than 1 wt. % based on a total weight of the adhesive formulation. In some embodiments, a ratio of the SBS copolymer to the process oil in the adhesive formulation is 1:10 to 1:3.

In some embodiments, the filler is present in an amount of 0.00001% to 70% by weight of the adhesive formulation.

In some embodiments, a roofing system includes a thermoplastic polyolefin (TPO) membrane. In some embodiments, the roofing system includes a roofing substrate. In some embodiments, the roofing system includes an adhesive disposed between the TPO membrane and the roofing substrate. In some embodiments, the adhesive includes a styrene-butadiene-styrene (SBS) copolymer. In some embodiments, the SBS copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive. In some embodiments, the adhesive includes asphalt. In some embodiments, the asphalt is present in an amount of 70 wt. % to 99.5 wt. % based on the total weight of the adhesive. In some embodiments, a ratio of the SBS copolymer to the asphalt in the adhesive is 1:11 to 1:3.

In some embodiments, a roofing system includes a thermoplastic polyolefin (TPO) membrane. In some embodiments, the roofing system includes a roofing substrate. In some embodiments, the roofing system includes an adhesive disposed between the TPO membrane and the roofing substrate. In some embodiments, the adhesive includes a styrene-butadiene-styrene (SBS) copolymer. In some embodiments, the SBS copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive. In some embodiments, the adhesive includes a process oil. In some embodiments, the process oil is present in an amount of 20 wt. % to 70 wt. % based on a total weight of the adhesive. In some embodiments, the asphalt is present in an amount of less than 1 wt. % based on the total weight of the adhesive. In some embodiments, a ratio of the SBS copolymer to the process oil in the adhesive is 1:10 to 1:3.

In some embodiments, a roofing system includes a first substrate. In some embodiments, the roofing system includes a second substrate. In some embodiments, the roofing system includes an adhesive disposed between the first substrate and the second substrate. In some embodiments, the adhesive includes a styrene-butadiene-styrene (SBS) copolymer. In some embodiments, the SBS copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive. In some embodiments, the adhesive includes asphalt. In some embodiments, the asphalt is present in an amount of 70 wt. % to 99.5 wt. % based on the total weight of the adhesive. In some embodiments, a ratio of the SBS copolymer to the asphalt in the adhesive is 1:11 to 1:3.

In some embodiments, a roofing system includes a first substrate. In some embodiments, the roofing system includes a second substrate. In some embodiments, the roofing system includes an adhesive disposed between the first substrate and the second substrate. In some embodiments, the adhesive includes a styrene-butadiene-styrene (SBS) copolymer. In some embodiments, the SBS copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive. In some embodiments, the adhesive includes a process oil. In some embodiments, the process oil is present in an amount of 20 wt. % to 70 wt. % based on a total weight of the adhesive. In some embodiments, the asphalt is present in an amount of less than 1 wt. % based on the total weight of the adhesive. In some embodiments, a ratio of the SBS copolymer to the process oil in the adhesive is 1:10 to 1:3.

In some embodiments, the first substrate and the second substrate are the same. In some embodiments, the first substrate and the second substrate are different. In some embodiments, the first substrate, the second substrate, or any combination thereof is a roofing shingle.

In some embodiments, the at least one process oil is chosen from at least one paraffinic oil, at least one petroleum extract, at least one vegetable oil, at least one naphthenic oil, at least one aromatic oil, at least one re-refined engine oil bottom (REOB), at least one engine oil residue (EOR), at least one re-refined heavy vacuum distillation bottom (RHVDB), at least one re-refined heavy vacuum distillation oil (RHVDO), at least one re-refined vacuum tower bottom (RVTB), at least one vacuum tower bottom (VTB), or any combination thereof.

In some embodiments, the at least one process oil is at least one tall oil.

In some embodiments, the at least one tall oil takes the form of tall oil pitch.

In some embodiments, the at least one tackifier is at least one rosin ester.

In some embodiments, the at least one rosin ester is at least one pentaerythritol rosin ester.

In some embodiments, the at least one rosin ester is at least one glycerol rosin ester.

In some embodiments, the adhesive formulation includes at least one second polymer, wherein the second polymer is a styrene-ethylene-butylene-styrene (SEBS) copolymer.

In some embodiments, the first substrate is a TPO substrate.

In some embodiments, the second substrate is an ETFE substrate.

In some embodiments, a method includes obtaining a styrene-butadiene-styrene (SBS) copolymer. In some embodiments, the method includes obtaining asphalt. In some embodiments, the method includes mixing the SBS copolymer with the asphalt to form an adhesive formulation. In some embodiments, the SBS copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 70 wt. % to 99.5 wt. % based on a total weight of the adhesive formulation. In some embodiments, a ratio of the SBS copolymer to the asphalt in the adhesive formulation is 1:11 to 1:3.

In some embodiments, the method includes adding a filler.

In some embodiments, the filler is calcium carbonate, barium sulfate, calcium sulfate, talc, limestone, perlite, silica, fumed silica, precipitated silica, quartz, aluminum trihydrate, magnesium hydroxide, colemanite, titanium dioxide, snow white, fly ash, graphene nanoparticles, carbon black, recycled rubber tires, recycled shingles, recycled thermoplastic resins, basalt, roofing granules, clay, ammonium polyphosphate, graphite, expandable graphite, or any combination thereof.

In some embodiments, the filler is present in an amount of 0.00001% to 70% by weight of the adhesive formulation.

In some embodiments, a method includes obtaining a styrene-butadiene-styrene (SBS) copolymer. In some embodiments, the method includes obtaining a process oil. In some embodiments, the method includes mixing the SBS copolymer with the process oil to form an adhesive formulation. In some embodiments, the SBS copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive formulation. In some embodiments, the process oil is present in an amount of 20 wt. % to 70 wt. % based on a total weight of the adhesive formulation. In some embodiments, asphalt is present in an amount of less than 1 wt. % based on a total weight of the adhesive formulation. In some embodiments, a ratio of the SBS copolymer to the process oil in the adhesive formulation is 1:10 to 1:3.

In some embodiments, the method includes adding a filler.

In some embodiments, the filler is present in an amount of 0.00001% to 70% by weight of the adhesive formulation.

BRIEF DESCRIPTION OF THE DRAWINGS

References are made to the accompanying drawings that form a part of this disclosure and that illustrate embodiments in which the systems and methods described in this Specification can be practiced.

FIG. 1 shows a flowchart for a method of forming an adhesive formulation, according to some embodiments.

FIG. 2 shows a flowchart for a method of forming an adhesive formulation, according to some embodiments.

FIG. 3 shows an example system using an adhesive formulation, according to some embodiments.

Like reference numbers represent the same or similar parts throughout.

DETAILED DESCRIPTION

In some embodiments, an adhesive formulation comprises a styrenic block copolymer. In some embodiments, the styrenic block copolymer is chosen from or is selected from the group consisting of at least one of a styrene-butadiene-styrene (SBS) copolymer, at least one styrene-isoprene-styrene copolymer (SIS), at least one styrene-ethylene-butylene-styrene (SEBS) copolymer, or any combination thereof.

In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 25 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 20 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 15 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 10 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 5 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 1 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 1 wt. % to 30 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 5 wt. % to 30 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 10 wt. % to 30 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 15 wt. % to 30 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 20 wt. % to 30 wt. % based on the total weight of the adhesive formulation. In some embodiments, the styrenic block copolymer is present in an amount of 25 wt. % to 30 wt. % based on the total weight of the adhesive formulation.

In some embodiments, the adhesive formulation comprises asphalt.

In some embodiments, the asphalt is present in an amount of 70 wt. % to 99.5 wt. % based on a total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 70 wt. % to 99 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 70 wt. % to 95 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 70 wt. % to 90 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 70 wt. % to 85 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 70 wt. % to 80 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 70 wt. % to 75 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 75 wt. % to 99.5 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 80 wt. % to 99.5 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 85 wt. % to 99.5 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 90 wt. % to 99.5 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 95 wt. % to 99.5 wt. % based on the total weight of the adhesive formulation. In some embodiments, the asphalt is present in an amount of 99 wt. % to 99.5 wt. % based on the total weight of the adhesive formulation.

In some embodiments, the adhesive formulation comprises at least one process oil.

In some embodiments, the at least one process oil is chosen from or is selected from the group consisting of: at least one paraffinic oil, at least one bio-oil, at least one petroleum extract, at least one vegetable oil, at least one naphthenic oil, at least one aromatic oil, at least one re-refined engine oil bottom (REOB), at least one engine oil residue (EOR), at least one re-refined heavy vacuum distillation bottom (RHVDB), at least one re-refined heavy vacuum distillation oil (RHVDO), at least one re-refined vacuum tower bottom (RVTB), at least one vacuum tower bottom (VTB), at least one tall oil, or any combination thereof.

In some embodiments, the at least one bio-oil is chosen from or is selected from the group consisting of: oils isolated from plants, oils isolated from animals, oils isolated from microorganisms, or any combination thereof.

In some embodiments, the at least one process oil is chosen from or is selected from the group consisting of at least one paraffinic oil, at least one petroleum extract, at least one vegetable oil, at least one naphthenic oil, at least one aromatic oil, at least one re-refined engine oil bottom (REOB), at least one engine oil residue (EOR), at least one re-refined heavy vacuum distillation bottom (RHVDB), at least one re-refined heavy vacuum distillation oil (RHVDO), at least one re-refined vacuum tower bottom (RVTB), at least one vacuum tower bottom (VTB), or any combination thereof.

In some embodiments, the at least one process oil, comprises, consists essentially of, or consists of at least one tall oil. In some embodiments, the at least one tall oil comprises consists essentially of, or consists of tall oil pitch.

In some embodiments, the at least one process oil comprises saturates, aromatics, resins, asphaltenes, or any combination thereof.

In some embodiments, the at least one process oil is present in an amount of 20 wt. % to 70 wt. % based on a total weight of the adhesive formulation. In some embodiments, the at least one process oil is present in an amount of 20 wt. % to 60 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one process oil is present in an amount of 20 wt. % to 50 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one process oil is present in an amount of 20 wt. % to 40 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one process oil is present in an amount of 20 wt. % to 30 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one process oil is present in an amount of 30 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one process oil is present in an amount of 40 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one process oil is present in an amount of 50 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one process oil is present in an amount of 60 wt. % to 70 wt. % based on the total weight of the adhesive formulation.

In some embodiments, the adhesive formulation comprises at least one plasticizer. In some embodiments, the at least one plasticizer comprises at least one of polyethylene glycol, polypropylene glycol, polyether diol, iso-decyl benzoate, triethylene glycol bis (2-ethylhexanoate), ethoxylated castor oil, oleic acid ethoxylate, alkylphenol ethoxylates, copolymers of ethylene oxide (E0) and propylene oxide (PO), silicone polyether copolymers, terephthalates, polyethylene terephthalates (PET), or any combination thereof.

In some embodiments, a mixture including the at least one plasticizer and the at least one process oil is present in an amount of 20 wt. % to 70 wt. % based on a total weight of the adhesive formulation. In some embodiments, the mixture including the at least one plasticizer and the at least one process oil is present in an amount of 20 wt. % to 60 wt. % based on the total weight of the adhesive formulation. In some embodiments, the mixture including the at least one plasticizer and the at least one process oil is present in an amount of 20 wt. % to 50 wt. % based on the total weight of the adhesive formulation. In some embodiments, the mixture including the at least one plasticizer and the at least one process oil is present in an amount of 20 wt. % to 40 wt. % based on the total weight of the adhesive formulation. In some embodiments, the mixture including the at least one plasticizer and the at least one process oil is present in an amount of 20 wt. % to 30 wt. % based on the total weight of the adhesive formulation. In some embodiments, the mixture including the at least one plasticizer and the at least one process oil is present in an amount of 30 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the plasticizer and the at least one process oil are present in a combined amount of 40 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the plasticizer and the at least one process oil are present in a combined amount of 50 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the plasticizer and the at least one process oil are present in a combined amount of 60 wt. % to 70 wt. % based on the total weight of the adhesive formulation.

In some embodiments, the at least one plasticizer is combined with the at least one process oil to form a mixture, the at least one plasticizer is present in the mixture in an amount not exceeding 50 wt. % based on a total weight of the mixture. In some embodiments, the at least one plasticizer is present in the mixture in an amount not exceeding 45 wt. % based on the total weight of the mixture. In some embodiments, the at least one plasticizer is present in the mixture in an amount not exceeding 40 wt. % based on the total weight of the mixture. In some embodiments, the at least one plasticizer is present in the mixture in an amount not exceeding 35 wt. % based on the total weight of the mixture. In some embodiments, the at least one plasticizer is present in the mixture in an amount not exceeding 30 wt. % based on the total weight of the mixture. In some embodiments, the at least one plasticizer is present in the mixture in an amount not exceeding 25 wt. % based on the total weight of the mixture. In some embodiments, the at least one plasticizer is present in the mixture in an amount not exceeding 20 wt. % based on the total weight of the mixture. In some embodiments, the at least one plasticizer is present in the mixture in an amount not exceeding 15 wt. % based on the total weight of the mixture. In some embodiments, the at least one plasticizer is present in the mixture in an amount not exceeding 10 wt. % based on the total weight of the mixture. In some embodiments, the at least one plasticizer is present in the mixture in an amount not exceeding 5 wt. % based on the total weight of the mixture. In some embodiments, the at least one plasticizer is present in the mixture in an amount not exceeding 1 wt. % based on the total weight of the mixture.

In some embodiments, the adhesive formulation includes less than 1 wt. % asphalt based on a total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes less than 0.75 wt. % asphalt based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes less than 0.5 wt. % asphalt based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes less than 0.25 wt. % asphalt based on the total weight of the adhesive formulation.

In some embodiments, the adhesive formulation comprises at least one fire retardant.

In some embodiments, the at least one fire retardant comprises colemanite, aluminum trihydrate, magnesium hydroxide, expandable graphite, ammonium polyphosphate, triphenyl phosphate, resorcinol bis(diphenylphosphate), bisphenol A diphenyl phosphate, tricresyl phosphate, dimethyl methylphosphonate, aluminium diethyl phosphinate, decabromodiphenyl ether, decabromodiphenyl ethane, at least one brominated polystyrene, at least one brominated carbonate oligomer, at least one brominated epoxy oligomer, tetrabromophthalic anyhydride, tetrabromobisphenol A, hexabromocyclododecane, antimony trioxide, antimony pentoxide, at least one chlorinated paraffin, huntite, hydromagnesite, red phosphorous, zinc borate, sodium borate, lithium borate, boric acid, tris(1,3-dichloro-2-propyl)phosphate, (tetrakis(2-chlorethyl)dichloroisopentyldiphosphate, or any combination thereof.

In some embodiments, the adhesive formulation further comprises at least one filler.

In some embodiments, the at least one filler is calcium carbonate, barium sulfate, calcium sulfate, talc, limestone, perlite, silica, fumed silica, precipitated silica, quartz, aluminum trihydrate, magnesium hydroxide, colemanite, titanium dioxide, snow white, fly ash, graphene nanoparticles, carbon black, recycled rubber tires, recycled shingles, recycled thermoplastic resins, basalt, roofing granules, clay, ammonium polyphosphate, graphite, expandable graphite, or any combination thereof.

Some embodiments of the present disclosure relate to a method of using an adhesive formulation that is free or substantially free of asphalt.

In some embodiments, the method comprises applying the adhesive formulation to at least one surface of a substrate. In some embodiments, the substrate is a roof substrate. In some embodiments, the substrate or roof substrate is a plywood substrate, a glass substrate, a fiberglass substrate, (e.g., a fiberglass mat), a cellulosic substrate, a shingle (e.g., a roofing shingle), an underlayment, a roofing membrane (e.g., a thermoplastic polyolefin (TPO) or polyvinyl chloride (PVC) membrane), a roof deck, a photovoltaic (PV) panel, a modified bitumen (MODBIT) substrate, an ethylene tetrafluoroethylene (ETFE) substrate, a roll good, or any combination thereof.

In some embodiments, the method further comprises forming the adhesive formulation into at least one adhesive sheet, forming the adhesive into at least one adhesive strip, or any combination thereof. In some embodiments, the forming of the adhesive formulation into at least one adhesive sheet, the forming the adhesive into at least one adhesive strip, or any combination thereof comprises casting the adhesive formulation into the at least one adhesive sheet, casting the adhesive formulation into the at least one adhesive strip, or any combination thereof. In some embodiments, the casting is performed with a roller mill.

In some embodiments, the roofing membrane is a low surface energy roofing membrane. In some embodiments, the low surface energy roofing membrane has a surface energy of 40 mN/m or less. In some embodiments, a low surface energy roofing membrane has a surface energy of 35 mN/m or less. In some embodiments, a low surface energy roofing membrane has a surface energy of 30 mN/m or less. In some embodiments, a low surface energy roofing membrane has a surface energy of 25 mN/m or less. In some embodiments, a low surface energy roofing membrane has a surface energy of 20 mN/m or less. In some embodiments, a low surface energy roofing membrane has a surface energy of 15 mN/m or less. In some embodiments, a low surface energy roofing membrane has a surface energy of 10 mN/m or less.

In some embodiments, the roofing membrane includes at least one of thermoplastic polyolefins, polyvinyl chlorides, cyclopiazonic acid, chlorinated polyethylene resins, ethylene interpolymers, nitrile butadiene polymers, polyisobutylene, atactic-polypropylene, APP-modified bitumen, poly(styrene-butadiene-styrene), styrene ethylene butylene styrene, ethylene propylene diene monomers, chlorosulfonated polyethylene rubbers, polychloroprene, extracellular region membranes, polycarbonate, nylon, polyvinyl acetate, polystyrene, polytetrafluoroethylene, polyvinylidene fluoride, polyurethane, epoxy, or combinations thereof.

In some embodiments, the roofing substrate includes at least one of silicone, plywood, cement, concrete, asphaltic shingles, compressed fiberboard, gypsum, oriented strand board, concrete masonry units, masonry blocks, bricks, polyiso foam, polyisocyanurate, steel, aluminum, copper, minerals, limestone, thermoplastic polyolefin, polyvinyl chloride, silicone, polyvinylidene fluoride, polymethyl methacrylate, acrylic, or combinations thereof.

In some embodiments, the roofing membrane includes a thermoplastic polyolefin, and the roofing substrate includes a thermoplastic polyolefin.

In some embodiments, the roofing membrane includes a thermoplastic polyolefin, and the roofing substrate includes a polyisocyanurate.

In addition, conventional membrane materials, such as those made from thermoplastic polyolefins (TPO) or polyvinyl chloride (PVC) for example, often require an adhesion-assisting layer coupled to the membrane material in order to achieve proper adhesion to the roof substrate. Such adhesion-assisting layers includes a fleece material (e.g., “fleece-backed membranes”) a texturing layer, a solvent-treated layer, or the like. Adding adhesion-assisting layers can lead to time-consuming manufacturing, a more costly membrane product, and can add to both the weight and bulkiness of roofing systems. Conventional membrane materials can also be treated, e.g., chemically, to provide texture and/or provide a slight increase in surface energy such that the membrane will adhere to the roof substrate, however, these surface treatments often increase overall hazardous chemical use during manufacturing of the membrane and often lead to weaker and less uniform adhesion than membranes including adhesion assigning layers.

Other conventional membrane materials are mechanically fastened to the roof substrate using screws or other fasteners at discrete points across the surface of the membrane material. The process of mechanically fastening the membrane material to the roof substrate can be relatively faster than adhesive-only membrane materials, however, mechanically fastened membrane materials often degrade, tear, wear, erode, thin, separate, delaminate, or otherwise fail at one or more of the discrete fastening points during long-term use.

In other words, conventional mechanical fastening approaches are often faster and cheaper to install when compared to adhesive-only approaches but tend to fail earlier than adhesive-only approaches. Adhesive-only approaches typically result in longer-lasting protection for the roof, but are more costly and time-consuming to install, and result in heavier and bulkier membranes. In addition, conventional solvent surface treatments typically produce more toxic chemical waste than the mechanical fastening approach. Therefore, there is a need in the market for an adhesive-only roofing membrane that is superior to mechanically fastened membranes, easier and quicker to install than conventional adhesive-only membrane materials, and that does not require an adhesion-assisting layer.

In some embodiments, the adhesive formulation includes at least one second polymer chosen from: at least one polyolefin, oxidized polyethylene (OPE), polyethylene-polypropylene elastomer, ground tire rubber (GTR), isotactic polypropylene (IPP), atactic polypropylene (APP), or any combination thereof.

In some embodiments, the at least one second polymer is present in an amount of 0.1 wt. % to 20 wt. % based on a total weight of the adhesive formulation. In some embodiments, the at least one second polymer is present in an amount of 0.1 wt. % to 15 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one second polymer is present in an amount of 0.1 wt. % to 10 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one second polymer is present in an amount of 0.1 wt. % to 5 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one second polymer is present in an amount of 0.1 wt. % to 1 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one second polymer is present in an amount of 1 wt. % to 20 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one second polymer is present in an amount of 5 wt. % to 20 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one second polymer is present in an amount of 10 wt. % to 20 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one second polymer is present in an amount of 15 wt. % to 20 wt. % based on the total weight of the adhesive formulation.

In some embodiments, the adhesive formulation further includes at least one filler in an amount of 10 wt. % to 70 wt. % based on a total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 65 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 60 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 55 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 50 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 45 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 40 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 35 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 30 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 25 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 20 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 10 wt. % to 15 wt. % based on the total weight of the adhesive formulation.

In some embodiments, the at least one filler is present in amount of 15 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 20 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 25 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 30 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 35 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 40 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 45 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 50 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 55 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 60 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the at least one filler is present in amount of 65 wt. % to 70 wt. % based on the total weight of the adhesive formulation.

In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.00001 wt. % to 70 wt. % based on a total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.001 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.01 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.1 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 1 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 5 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 10 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 15 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 20 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 25 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 30 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 35 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 40 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 45 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 50 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 55 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 60 wt. % to 70 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 65 wt. % to 70 wt. % based on the total weight of the adhesive formulation.

In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 65 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 60 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 55 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 50 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 45 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 40 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 35 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 30 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 25 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 20 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 15 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 10 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 5 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 1 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 0.1 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 0.01 wt. % based on the total weight of the adhesive formulation. In some embodiments, the adhesive formulation includes at least one additive in an amount of 0.0001 wt. % to 0.001 wt. % based on the total weight of the adhesive formulation.

In some embodiments, the at least one additive is at least one wax, at least one antioxidant, ethylene-bis-stearamide (EBS), or any combination thereof.

In some embodiments, the substrate is a plywood substrate, a glass substrate, a cellulosic substrate, a roofing shingle, an underlayment, a roofing membrane, a roof deck, a photovoltaic (PV) panel, a modified bitumen (MODBIT) substrate, a roll good, or any combination thereof.

In some embodiments, the adhesive formulation is formed into at least one adhesive sheet, at least one adhesive strip, or any combination thereof.

In some embodiments, forming of the adhesive formulation into at least one adhesive sheet, the forming the adhesive into at least one adhesive strip, or any combination thereof includes casting the adhesive formulation into the at least one adhesive sheet, casting the adhesive formulation into the at least one adhesive strip, or any combination thereof.

FIG. 1 shows a flowchart for a method 100 of forming an adhesive formulation, according to some embodiments.

In some embodiments, the method 100 includes obtaining a stryenic block copolymer at block 102. In some embodiments, the styrenic block copolymer includes at least one of a styrene-butadiene-styrene (SBS) copolymer, a styrene-isoprene-styrene copolymer (SIS), a styrene-ethylene-butylene-styrene (SEBS) copolymer, suitable combinations thereof, or the like.

In some embodiments, the method 100 includes obtaining asphalt at block 104.

In some embodiments, the method 100 includes mixing the styrenic block copolymer with the asphalt to form an adhesive formulation at block 106.

In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive formulation.

In some embodiments, the asphalt is present in an amount of 70 wt. % to 99.5 wt. % based on a total weight of the adhesive formulation. In some embodiments, a ratio of the SBS copolymer to the asphalt in the adhesive formulation is 1:11 to 1:3.

In some embodiments, the method 100 includes adding a filler at block 108.

In some embodiments, the filler is present in an amount of 0.00001% to 70% by weight of the adhesive formulation.

FIG. 2 shows a flowchart for a method 150 of forming an adhesive formulation, according to some embodiments.

In some embodiments, the method 150 includes obtaining a styrenic block copolymer at block 152.

In some embodiments, the method 150 includes obtaining a process oil at block 154.

In some embodiments, the method 150 includes mixing the styrenic block copolymer with the process oil to form an adhesive formulation at block 156.

In some embodiments, the styrenic block copolymer is present in an amount of 0.5 wt. % to 30 wt. % based on a total weight of the adhesive formulation.

In some embodiments, the process oil is present in an amount of 20 wt. % to 70 wt. % based on a total weight of the adhesive formulation.

In some embodiments, asphalt is present in an amount of less than 1 wt. % based on a total weight of the adhesive formulation. In some embodiments, a ratio of the styrenic block copolymer to the process oil in the adhesive formulation is 1:10 to 1:3.

In some embodiments, the method 150 includes adding a filler at block 158.

In some embodiments, the filler is present in an amount of 0.00001% to 70% by weight of the adhesive formulation.

Example formulations of three example adhesives A, B, and C are shown in Table 1 below.

TABLE 1

Formulations
Units
A
B
C

Hydrocarbon oil
wt. %
50
50
50

SBS
wt. %
10
10
10

TiO₂
wt. %

10

Filler
wt. %

30

Limestone Filler
wt. %
40

Recycled Asphalt
wt. %

40

Total Weight Percentage
wt. %
100
100
100

Properties of the three adhesives A, B, and C are shown in Table 2 below.

TABLE 2

ASTM D1970 Compound Properties

A
B
C

Viscosity @ 374 F. (LVT)
cP
4600
5100
6000

Penetration @ 73 F.
dmm
96
83
73

Penetration @ 140 F.
dmm
99
112
82

Softening Point (Ring and Ball)
F
200
199
211

Table 3 shows peel strengths in a 180° peel test at two different temperatures for a TPO to TPO bonded using adhesives A, B, and C. Samples were adhered using Formulations A, B, and C and the peel strength is at 180°. The results are shown in Table 3. The adhesives were applied between a first TPO substrate and a second TPO substrate to form the samples. The peel strength at 180° was obtained by lifting the second TPO substrate at 180° from the first TPO substrate. An example of the samples is shown in FIG. 3. As shown in side view, a first substrate 202 (here a TPO substrate) is fixed to a second substrate 204 (here a TPO substrate). Adhesive 206 is applied between the first substrate 202 and the second substrate 204.

TABLE 3

A
B
C

Tested @ 40 F.
lb./ft.
50
52
64

Tested @ 73 F.
lb./ft.
9
10
18

Table 4 shows peel strengths in a 180° peel test at two different temperatures for a TPO to ISO bonded using various adhesives. The results are shown in Table 4. The adhesives were applied between a TPO substrate and an ISO substrate to form the samples. The peel strength at 180° was obtained by lifting the ISO substrate at 180° from the TPO substrate. The adhesive was applied in a 2 inch strip and a 1 inch strip on 3 inch samples of the TPO substrate and the ISO substrate. Failure modes are also displayed in Table 4.

TABLE 4

2″ strip
1″ strip

Max load (lbf)
14
8

Mode of failure
facer
facer

custom character

2″ strip
1″ strip

Max load (lbf)
11
8

Mode of failure
facer
facer

custom character

2″ strip
1″ strip

Max load (lbf)
11
6

Mode of failure
facer
facer

Adhesive - A
RT 2″ strip
40F 2″ strip

Max load (lbf)
10
7

Mode of failure
facer
facer

custom character

RT 2″ strip
40F 2″ strip

Max load (lbf)
5
6

Mode of failure
facer
facer

custom character

RT 2″ strip
40F 2″ strip

Max load (lbf)
5
8

Mode of failure
facer
facer

Table 5 shows peel strengths in a 180° peel test at two different temperatures for a TPO to PDVF. The results are shown in Table 5. The adhesive was applied between a TPO substrate and a PVDF substrate to form the sample. The peel strength at 180° was obtained by lifting the PVDF substrate at 180° from the TPO substrate. The adhesive was applied in a 2 inch strip and on a 3 inch sample of the TPO substrate and the PVDF substrate. Failure mode is also displayed in Table 5.

TABLE 5

91% Asphalt +

Surface Free Energy of

9% Kraton 1191
2″ strip
PVDF 33 mN/m

Max load (lbf)
34
Surface Free Energy of

TPO back 24 mN/m

Mode of failure
PVDF to Adhesive

Table 6 shows peel strengths in a T-peel test various substrates with Adhesive A at a 27 mil thickness. The results are shown in Table 6. The T-peel strength was obtained by progressively lifting the substrates from each other.

TABLE 6

RT Peel
Mode of

Substrates
Adhesive
Top Layer
LBF/FT
Failure

Plywood
Adhesive-
Polyolefin NW top +
23
Adhesive to

A-27 mil
Polyolefin EVA back

Substrate

34 mN/m* (adhesion

between the plywood

Polyolefin EVA Back

coat)

Plywood
Adhesive-
Polyolefin NW top
31
Adhesive to

A-27 mil
laminated to Al-foil

Substrate

(adhesion between

plywood and Al-foil)

Plywood
Adhesive-
Film made out of
20
Adhesive to

A-27 mil
Polypropylene and

Substrate

EVA blend 34 mN/m*

Plywood
Adhesive-
Filled polyolefin
7
Adhesive to

A-27 mil
composite 29 mN/m*

Substrate &

Adhesive to

Top Layer

Plywood
Adhesive-
Synthetic
18
Adhesive to

A-27 mil
underlayment back

Substrate

Polypropylene

32 mN/m*

Plywood
Adhesive-
Synthetic
8
Adhesive to

A-27 mil
underlayment

Substrate

Propylene Elastomer

26.5 mN/m*

Plywood
Adhesive-
PVC KEEE
10
Adhesive to

A-27 mil

Top Layer

Plywood
Adhesive-
Base sheet made out of
22
Adhesive to

A-27 mil
SBS modified asphalt

Substrate

(ASTM D 6163 Type I-

Ruberoid 20)

Plywood
Adhesive-
Polyethylene (Back of
24
Adhesive to

A-27 mil
ASTM D 6163 Heat

Substrate

Weld Cap sheet-

Ruberoid HW)

Plywood
Adhesive-
Oxidized asphalt with
6
Adhesive to

A-27 mil
sand

Top Layer

Table 7 shows peel strengths in a T-peel test various substrates with Adhesive A at a 33 mil thickness. The results are shown in Table 7. The T-peel strength was obtained by progressively lifting the substrates from each other.

TABLE 7

RT Peel
Mode of

Substrates
Adhesive
Top Layer
LBF/FT
Failure

Polypropylene
Adhesive-
Polyolefin EVA
16
Adhesive to

NW (Stormguard
A-33 mil
compound 34

Substrate

with blue top)

mN/m*

Polypropylene
Adhesive-
Polypropylene
10
Adhesive to

NW with Al-foil
A-33 mil
NW with Al-foil

Substrate &

back

back (Al-foil to

Adhesive to

Al-foil)

Top Layer

TPO Treated
Adhesive-
TPO Treated Back
24
Adhesive to

BACK
A-33 mil
(Back to back)

Substrate &

Adhesive to

Top Layer

Polypropylene
Adhesive-
Propylene
10
Adhesive to

NW (Felt Buster
A-33 mil
Elastomer 26.5

Substrate

top)

mN/m*

TPO Face 29
Adhesive-
TPO Back 24
11
Adhesive to

mN/m*
A-33 mil
mN/m*

Substrate

The terminology used herein is intended to describe embodiments and is not intended to be limiting. The terms “a,” “an,” and “the” include the plural forms as well, unless clearly indicated otherwise. The terms “comprises” and/or “comprising,” when used in this Specification, specify the presence of the stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, and/or components.

It is to be understood that changes may be made in detail, especially in matters of the construction materials employed and the shape, size, and arrangement of parts without departing from the scope of the present disclosure. This Specification and the embodiments described are examples, with the true scope and spirit of the disclosure being indicated by the claims that follow.

Number	Name	Date	Kind
4755545	Lalwani	Jul 1988	A
5380552	George et al.	Jan 1995	A
9574117	Ma et al.	Feb 2017	B2
20040172899	Paradise et al.	Sep 2004	A1
20060286347	Mehta et al.	Dec 2006	A1
20090105376	Korenstra et al.	Apr 2009	A1
20100162657	Swei	Jul 2010	A1
20140373754	Luccarelli et al.	Dec 2014	A1
20170008233	Vontorcik, Jr. et al.	Jan 2017	A1
20200095478	Young et al.	Mar 2020	A1
20200224419	Boss et al.	Jul 2020	A1
20220064501	Rufus	Mar 2022	A1
20220356707	Yu	Nov 2022	A1
20230092077	Lorenzen	Mar 2023	A1

Number	Date	Country
2015127562	Sep 2015	WO
2022051619	Mar 2022	WO

Adhesives for low surface energy materials

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

Field of Search

US

CPC

International Classifications

Abstract

Description

Claims

CROSS-REFERENCE TO RELATED APPLICATIONS

US Referenced Citations (14)

Foreign Referenced Citations (2)

Non-Patent Literature Citations (1)

Related Publications (1)

Provisional Applications (1)