Adhesives

Abstract

An adhesive, comprising (A) a polymeric MDI, (B) modified polyvinyl acetate emulsion, (C) aqueous polyvinyl alcohol solution, and (D) a filler. Preferably, amass ratio of A:B:C:D is 30:(60-160):(50-160):(10-140) provided that the aqueous polyvinyl alcohol solution (C) is in a concentration of 10% by mass.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to adhesives for wood materials for use in bonding woodmaterials, the adhesives being high in initial bond strength at room temperature and excellent in durability after application, and to prevent generation of volatile organic compounds such as formaldehyde.

[0003] This application is based on patent applications (Japanese Patent Application No. 2000-77047, Japanese Patent Application No. 2000-339640 and Japanese Patent Application No. 2001-29525) filed in Japan, the content of which is incorporated herein by reference.

[0004] 2. Description of the Related Art

[0005] As adhesives for woodwork, various adhesives such as urea resin based adhesives, melamine resin based adhesives, phenol resin based adhesives, resorcinol resin based adhesives, water based polymer-isocyanate adhesives, a-olefin based adhesives, and acetic acid vinyl emulsion based adhesives have heretofore been known.

[0006] However, use of such adhesives for woodwork is accompanied with various problems as described below. Urea resin based adhesives, melamine resin based adhesives, phenol resin based adhesives, resorcinol resin based adhesives and the like have a problem that a harmful substance such as formaldehyde could be generated during working or from the product. Water based polymer-isocyanate adhesives are relatively expensive, highly viscous and hence poor in workability, poor in initial bond strength, and easily foam.

[0007] α-Olefin based adhesives are relatively expensive and poor in adhesive strength at high temperatures. Polyvinyl acetate emulsion based adhesives are poor in water resistance and heat resistance.

[0008] As described above, the conventional adhesives for wood materials are excellent in one respect but poor in another respect. Few of them can satisfy the required properties within a wide range.

SUMMARY OF THE INVENTION

[0009] An object of the present invention is to provide an adhesive that quickly develops initial bond strength at room temperature without generating volatile harmful substances, has good heat resistance and water resistance and good durability, and is excellent in workability and less prone to foaming.

[0010] The above object can be achieved by an adhesive, comprising (A) a polymeric MDI, (B) modified polyvinyl acetate emulsion, (C) aqueous polyvinyl alcohol solution, and (D) a filler. Accordingly, the adhesive of the present invention can be used widely for bonding of wood materials including not only hard wood materials having a specific gravity of 0.6 or more, such as beech, oak, birch, maple, walnut, matoa, nato, and teak but also general wood and wood materials such as plywood, particleboard, MDF, and OSB.

DETAILED DESCRIPTION OF THE INVENTION

[0011] Hereinafter, the present invention will be described in detail.

[0012] As the polymeric MDI (Methylene Diphenyl Diisocyanate) (A), which serves as a main ingredient of the adhesive of the present invention, one having an isocyanate group content of from about 28% to about 35% and a viscosity of from about 100 to about 250 mPa·s(25° C.) is used.

[0013] As the modified polyvinyl acetate emulsion (B), modified polyvinyl acetate emulsion containing active functional group synthesized by emulsion polymerization and the like are used. Those having a resin content of from 40% to 65% and a viscosity of from 1,000 to 120,000 mPa·s (25° C.) are preferable. Also, those that are free of plasticizers are preferred.

[0014] The modified polyvinyl acetate emulsion (B) is added to increase room temperature initial bond strength, water resistance, and room temperature bond strength.

[0015] As the aqueous polyvinyl alcohol solution (C), a 10% by mass aqueous solution of partially saponified polyvinyl acetate is used and the degree of saponification is preferably from 85 to 92 mol %. This is used to adjust the initial bond strength and viscosity of the adhesive.

[0016] As the filler (D), ground granulated mineral slags, such as ground granulated blast-furnace slag prescribed in JIS A6206 (1997), waste slag (black sand) when smelting aluminum, waste slag (green sand) when smelting nickel, fine powder of calcium carbonate, magnesium oxide, aluminum oxide, titanium oxide, silica, or the like, having an average particle diameter of from 2 to 20 μm, or mixtures of these are used. Among them, the filler (D) is preferably at least one selected from the ground granulated mineral slag and silica. The filler (D) plays a role of preventing foaming and adjusting the viscosity. If ground granulated mineral slag or silica is used, additionally, heat resistance is increased. As the filler (D), a powder of organic materials such as a powder of fiberous plants, a powder of cereals, or the like, is also preferably used. Examples of the powder of organic materials include starch such as cornstarch, potato-starch, tapioca-starch or the like, walnut powder, wheat flour, coconut powder, rice husk (chaff), wood powder, a powder of animal materials such as glue powder, and gelatin powder. If the powder of organic materials is used as the filler (D), it is easy to cut the resulting wood products whose members are bonded with the adhesive and with less damage to edge of the cutting machine. The powder of organic materials is less detrimental to the working environment than a powder of inorganic materials. Further, a standard of management of the powder of organic material is low relatively. If necessary, a mildew resistant agent may be used with the powder of organic materials.

[0017] For the purpose of increasing the initial bond strength, the adhesive of the present invention may contain in addition to the above blended components, adhesive mass such as styrene butadiene rubber (SBR) emulsion, natural rubber (NR) emulsion, chloroprene rubber (CR) emulsion, acrylic emulsion, EVA emulsion or the like, or a viscosity increasing agent, also called a tackifier, such as rosin, hydrogenated rosin, coumarone resin, terpene resin, ester gum or the like. The bond strength may be increased by blending a silane coupling agent to increase interaction between the filler, an inorganic component, and any other organic component. The silane coupling agent is particularly effective when at least silica is used as the filler (D) and is blended in the range of from 0.01 to 0.4% by mass based on the mass of silica. With less than 0.01% by mass, the bond strength is not increased sufficiently while with the above 0.4% by mass, the viscosity of the adhesive might be too high to avoid a decrease in usability and storability.

[0018] The equivalent ratio of the above blended components (B+C)/A is preferably from 30 to 120, more preferably from 45 to 100. The equivalent ratio as used herein is calculated as described below.

[0019] The NCO equivalent number is calculated as follows. First the mass of polymeric MDI is multiplied by the NCO content (%) of polymeric MDI, the product is divided by 100 to obtain an NCO amount, and this is divided by NCO equivalent (42) to obtain an NCO equivalent number.

[0020] On the other hand, total amount of water contained in the modified polyvinyl acetate emulsion (B) and the aqueous polyvinyl alcohol solution (C) is obtained in the same manner as above. Since one molecule of water reacts with two NCO groups, the equivalent of water is 18/2=9. Dividing the total amount of water by the equivalent of water, 9, an OH equivalent number is obtained.

[0021] The OH equivalent number thus obtained further divided by the NCO equivalent number is an equivalent ratio.

[0022] If the equivalent ratio is less than 30, the room temperature bond strength is insufficient and also the initial bond strength is insufficient. If it exceeds 120, the viscosity becomes too high, the foaminess is high, and the heat resistance is decreased. The equivalent ratio is more preferably from 46 to 100. By setting the equivalent ratio (B+C)/A to from 46 to 100, the initial bond strength (“the initial 40 minutes”),which is defined as a value of compressive shear strength for the initial 40 minutes after press bonding at 22° C. and 60% RH, can be made 50×0.1 MPa or more(JIS K6852(1994)).

[0023] The blending ratio of the above-described blended components in terms of mass ratio is preferably polymeric MDI (A):modified polyvinyl acetate emulsion (B):aqueous polyvinyl alcohol solution (C):filler (D)=30:(60-160):(50-160):(10-140).

[0024] When at least one selected from the ground granulated mineral slag and silica is used as the filler (D), the blending ratio is preferably 30:(70-160):(50-160):(50-140), more preferably 30:(100-150):(50-160):(80-140), provided that the concentration of the aqueous polyvinyl alcohol solution (C) is 10% by mass. By setting the blending ratio to 30:(100-150):(50-160):(80-140), the initial bond strength can be made 80×0.1 MPa or more.

[0025] When the powder of organic materials is used as the filler (D), the blending ratio is preferably 30:(60-160):(60-160):(10-40). By setting the blending ratio to the above range the initial bond strength can be made 50×0.1 MPa or more.

[0026] If the blending amount of the modified polyvinyl acetate emulsion (B) is less than 60, the initial bond strength, water resistance, and room temperature bond strength are insufficient, while if it exceeds 160, water resistance and heat resistance are decreased.

[0027] If the blending amount of 10% by mass aqueous polyvinyl alcohol solution (C) is less than 50, the viscosity is increased, the workability is decreased, and the pot life is shortened. If it exceeds 160, the water resistance and heat resistance are decreased.

[0028] Further, if the blending amount of the filler (D) is less than 10, no sufficient foaming inhibitory power can be obtained so that heat resistance increasing effect cannot be obtained. If it exceeds 140, the viscosity is increased and the workability is decreased.

[0029] The adhesive of the present invention can be obtained by weighing the above-described respective blended components by predetermined amounts, and mixing and stirring them. The product contains water and is in the form of an aqueous paste. The viscosity of the composition is within the range from 1000 to 60,000 mPa·s (25° C.), preferably from 1000 to 45,000 mPa·s (25° C.). The pot life is 25 minutes or more, preferably 60 minutes or more. It is preferred that the blending ratio be set such that these conditions can be satisfied.

[0030] If the viscosity of the composition is less than 1000 mPa·s (25° C.), theadhesive prone to soak into the wood materials and the bond strength is lowered.

[0031] The adhesive is cured by the reaction between the isocyanate groups in the polymeric MDI (A) and the moisture and other hydroxyl groups contained in the modified polyvinyl acetate emulsion (B) and the aqueous polyvinyl alcohol solution (C) to develop bond strength.

[0032] Such an adhesive quickly develops adhesiveness at room temperature so that sufficient bond strength can be obtained in a short time after press bonding. It produces less foam when mixing, stirring and bonding, has appropriate viscosity, and can be used for a long time, so that it has a good workability. Furthermore, it has high bond strength as well as high heat resistance and water resistance, so that it is excellent in durability.

[0033] Since the adhesive contains no formaldehyde condensation polymerized resin such as urea resin, phenol resin, melamine resin, or resorcinol resin, which is a source of formaldehyde, there is no risk that volatile harmful substances such as formaldehyde will be released from the product after bonding.

[0034] The adhesive of the present invention is excellent in various properties such as “Standard atmosphere”, “Water resistance at 60° C.”, “Temperature resistance at 100° C.”, “The initial 40 minutes”, and viscosity. In particular, if the equivalent ratio of components A:(B+C) is set to 1:(30-120), the adhesive exhibits the following bonding properties as will be apparent from the specific examples described hereinbelow.

[0035] “Standard atmosphere”:130×0.1 MPa or more

[0036] “Water resistance at 60° C.”:40×0.1 MPa or more

[0037] “Temperature resistance at 100° C.” 90×0.1 MPa or more

[0038] “The Initial 40 minutes”:50×0.1 MPa or more viscosity 1,000˜60,000 mPa·s

[0039] “Standard atmosphere” indicates values obtained by leaving test pieces to stand for 72 hours or more after press bonding them at 22° C. and 60% RH for 2 hours and measuring them as they are after the standing.

[0040] “Water Resistance at 60° C” indicates values obtained by dipping test pieces, which were left to stand at 22° C. and 60% RH for 72 hours or more after the press bonding, in water at 60° C. for 3 hours and then taking out and measuring the bond strength at room temperature (22° C.).

[0041] “Temperature resistance at 100° C” indicates values obtained by leaving test pieces, which were left to stand at 22° C. and 60% RH for 72 hours or more after the press bonding, to stand in an oven at 100° C. for 24 hours and measuring at a measuring temperature of 100° C.

[0042] “The initial 40 minutes” indicates values of compressive shear strength for the initial 40 minutes after press bonding at 22° C. and 60% RH.

[0043] Accordingly, the adhesive of the present invention can be used widely for bonding wood materials such as wood, plywood, particleboard, MDF (Medium Density Fiber board), and OSB (Oriented Strand Board). In particular, it can be used for lamination of hard wood materials having a specific gravity of 0.6 or more such as beech, oak, birch, maple, walnut, matoa, nato, and teak, lamination, decorative application, assembly of parts and the like of wood products such as musical instruments, adhesion of wood materials and another materials such as plastics, metals, glasses, ceramics.

[0044] The wood products of the present invention include various wood products bonded with the above-described adhesive, for example, musical instruments, furniture, construction materials, and the like and have high mechanical strength at the bonded parts and high durability.

[0045] Embodiments

[0046] Hereinafter, the present invention will be described in more detail by examples. However, the present invention should not be construed as being limited thereto.

[0047] 26 types of adhesives having blending compositions (mass ratios) shown in Tables 1 to 4 were prepared and bonding tests were carried out using birch as an adherend.

[0048] As the polymeric MDI, the one prepared by Sumitomo Bayer Urethane Co., Ltd. was used. As the aqueous polyvinyl alcohol solution, 10% by mass solution of the one prepared by Unitika Corporation was used.

[0049] As the filler, ground granulated blast furnace slag (Esument Super 6000, average particle diameter: 8 μm, produced by Shin Nittetsu Chubu Esument Co., Ltd.), silica (Sibelite M3000, purity 99%, average particle diameter: 12 μm, produced by Sibelco Co., Ltd.), rice husk (SARON fiber AA type 200 mesh under, produced by SARON FILER LTD.) was used.

[0050] The bonding was performed by pressing under the conditions of coating amount of 190˜200 g/m2, temperature of 22˜23° C., humidity of 55˜60% RH, pressure of 5˜7 kg/cm2 for 2 hours.

[0051] The tests were performed in accordance with JIS K6852 (1994) “Testing methods for shear strength of adhesive bonds by compression loading”. Also, the pot life and viscosity of the adhesives after the mixing and stirring were measured.

[0052] The results of tests are shown in Table 5 and 6.

	TABLE 1
	Test	Test	Test	Test	Test
	Example 1	Example 2	Example 3	Example 4	Example 5
(A) Poly-	30	30	30	30	30
meric MDI
(B) Modified	60	70	100	140	100
polyvinyl
emulsion
(C) PVA	50	50	50	50	100
10%
(D) Ground	80	50	120	120	100
granulated
furnace slag
SBR	0	0	36	18	0
Emulsion
Equivalent	36.94	39.41	46.80	56.65	68.96
ratio

[0053]

	TABLE 2
	Test	Test	Test	Test	Test	Test
	Exam-	Exam-	Exam-	Exam-	Exam-	Exam-
	ple 6	ple 7	ple 8	ple 9	ple 10	ple 11
(A) Poly-	30	30	30	30	30	30
meric MDI
(B) Modified	140	100	150	150	30	200
polyvinyl
emulsion
(C) PVA 10%	100	150	140	160	30	180
(D) Ground	80	80	130	130	30	100
granulated
furnace slag
SBR Emulsion	36	18	0	0	0	0
Equivalent	78.81	91.13	99.01	107.88	20.69	129.06
ratio

[0054]

	TABLE 3
	Test	Test	Test	Test	Test	Test	Test
	Example 12	Example 13	Example 14	Example 15	Example 16	Example 17	Example 18
(A) Polymeric MDI	30	30	30	30	30	30	30
(B)Modified	60	100	100	100	150	30	200
polyvinyl emulsion
(C)PVA 10%	50	50	100	150	160	30	180
(D)Silica	80	120	100	80	130	30	100
*Silane coupling	0.1	0.1	0.1	0.1	0.1	0.1	0.1
agent
Equivalent ratio	36.94	46.80	68.96	91.13	107.88	20.69	129.06
*In Table 3, the amount of silane coupling agent is based on silica.

[0055]

	TABLE 4
	Test	Test	Test	Test	Test	Test	Test	Test
	Example 19	Example 20	Example 21	Example 22	Example 23	Example 24	Example 25	Example 26
(A) Polymeric MDI	30	30	30	30	30	30	30	30
(B) Modified	84	78	64	100	156	145	101	126
polyvinyl emulsion
(C) PVA 10%	67	93	113	100	85	100	155	155
(D)Rice husk	12	26	22	20	18	33	25	25
Equivalent ratio	50.32	60.40	65.80	68.96	76.11	80.08	93.25	99.44

[0056]

	TABLE 5
	Basic Adhesion Properties
	Shear Strength of Adhesive Bonds by Compression Loading
	(×0.1 MPa)	Workability
			Temperature			Pot Life
	Standard	Water Resistance	resistance at	Initial 40	Viscosity	Minutes
	atmosphere	at 60° C.	100° C.	minutes	mPa · s(25° C.)	(25° C.)
Standard Value	130 or more	40 or more	90 or more	50 or more	Less than 60,000	25 or more
Test Example 1	139	52	127	50	58,000	60
Test Example 2	148	67	155	56	31,000	60
Test Example 3	148	48	113	82	48,000	60
Test Example 4	147	43	105	86	45,000	60
Test Example 5	157	53	124	93	25,500	60
Test Example 6	145	46	108	88	18,500	60
Test Example 7	141	42	102	85	12,000	60
Test Example 8	158	43	128	99	39,000	60
Test Example 9	148	43	98	74	35,000	60
Test Example 10	74	84	136	16	21,500	60
Test Example 11	152	28	88	76	66,000	60
Test Example 12	135	56	137	50	54,000	60
Test Example 13	144	50	111	81	46,000	60
Test Example 14	146	55	135	93	20,000	60
Test Example 15	139	41	104	86	11,000	60
Test Example 16	148	42	121	78	33,000	60
Test Example 17	78	75	139	17	17,500	60
Test Example 18	152	23	74	81	63,000	60
Resorcinol	172	103	131	0	1,500	30
Urea	143	86	127	0	3,000	30
Aqueous polymer	169	86	99	38	30,000	60
Isocyanate
α-Olefin	158	32	65	55	45,000	90

[0057]

	TABLE 6
	Basic Adhesion Properties
	Shear Strength of Adhesive Bonds by Compression Loading
	(×0.1 MPa)	Workability
			Temperature			Pot Life
	Standard	Water Resistance	resistance at	Initial 40	Viscosity	Minutes
	atmosphere	at 60° C.	100° C.	at minutes	mPa ·s(25° C.)	(25° C.)
Standard Value	130 or more	40 or more	90 or more	50 or more	Less than 60,000	25 or more
Test Example 19	131	57	93	52	6,000	60
Test Example 20	134	45	99	52	11,500	60
Test Example 21	136	68	115	51	40,000	60
Test Example 22	146	44	92	66	21,500	60
Test Example 23	143	49	91	54	12,000	60
Test Example 24	161	43	94	57	32,500	60
Test Example 25	132	45	91	55	18,750	60
Test Example 26	135	45	107	54	30,000	60

[0058] In Tables 5 and 6, the meanings of “Water Resistance at 60° C.”, “Temperature resistance at 100° C.”, “The initial 40 minutes” and “Standard atmosphere” are mentioned above.

[0059] “Pot Life” indicates where adhesion properties are satisfied, at the maximum time that has passed after stirring.

[0060] Table 5 also shows the results of measurement on four conventional adhesives for wood materials for comparison.

[0061] From Table 5 and 6, it can be seen that among the adhesives of the test examples, those of Test Examples 4, 5, 6, 13, 14, 15 and 22 exhibit excellent properties.

[0062] Using the adhesive of Test Example 3 described above, a laminated wood was fabricated. Beechwoods of 100 mm in width, 600 mm in length and 25 mm in thickness were provided. An adhesive was coated on them in an amount of 200 g/m2 for each adhesive layer and 8 beechwoods were superposed and press bonded under a load of 1.5 MPa at room temperature (22° C.) and 60% RH for 2 hours and then left to stand for 7 days. The resulting laminated wood was subjected to hot-cold cycle testing (by repeating 10 times the heat cycle of -20° C. for 16 hours and +50° C. for 8 hours) and to dry-wet cycle testing (repeating twice the cycle of 35° C., 95% RH for 2 days and 35° C., 20% RH for 5 days). As a result, no separation of adhesive was observed so that lamination wood having good durability was obtained.

Claims

1. An adhesive, comprising (A) a polymeric MDI, (B) modified polyvinyl acetate emulsion, (C) aqueous polyvinyl alcohol solution, and (D) a filler.

2. An adhesive according to claim 1, wherein an equivalent ratio of A:(B+C) is from 1:30 to 1:120.

3. An adhesive according to claim 1, wherein a mass ratio of A:B:C:D is 30:(60-160):(50-160):(10-140) provided that the aqueous polyvinyl alcohol solution (C) is in a concentration of 10% by mass.

4. An adhesive according to claim 1, wherein the filler (D) is at least one selected from ground granulated mineral slag, and silica.

5. An adhesive according to claim 1, wherein the filler (D) is a powder of organic materials.

6. An adhesive according to claim 4, wherein a mass ratio of A:B:C:D is 30:(70-160):(50-160):(50-140) provided that the aqueous polyvinyl alcohol solution (C) is in a concentration of 10% by mass.

7. An adhesive according to claim 5, wherein a mass ratio of A:B:C:D is 30:(60-160):(60-160):(10-40) provided that the aqueous polyvinyl alcohol solution (C) is in a concentration of 10% by mass.

8. Wood products whose members are bonded with an adhesive according to claim 1.