The present disclosure relates to a control ring and, more particularly, to an improved advanced passive clearance control (APCC) control ring that can be produced by field assisted sintering technology.
In a gas turbine engine, an APCC system is often used to control tip clearance within a high-pressure turbine or HPT. To maximize the performance of the APCC system, the APCC is typically configured such that the control ring provides a slow thermal response to throttle changes. Generally, such a slow thermal response requires relatively high mass and reduced surface areas to be achievable.
Accordingly, a need exists for a production method that allows an improved APCC control ring to be produced.
According to an aspect of the disclosure, an advanced passive clearance control (APCC) control ring is provided. The APCC control ring includes first and second cover sections, first and second wall sections and a control ring. At least one of the first and second cover sections is bonded to corresponding edges of the first and second wall sections by field assisted sintering technology (FAST) processing along a bond surface to form an enclosure for the control ring.
In accordance with additional or alternative embodiments, both the first and second cover sections are bonded to corresponding edges of the first and second wall sections by the FAST processing along corresponding bond surfaces.
In accordance with additional or alternative embodiments, the control ring is a full-hoop control ring and the first and second cover sections and the first and second wall sections are fully annular.
In accordance with additional or alternative embodiments, the control ring is segmented and the first and second cover sections and the first and second wall sections are partially annular.
In accordance with additional or alternative embodiments, the enclosure forms a thermally isolated cavity therein.
In accordance with additional or alternative embodiments, a thermal barrier coating (TBC) is applied to exterior surfaces of the first and second cover sections and the first and second wall sections.
In accordance with additional or alternative embodiments, hook elements are attached to one of the first and second wall sections.
According to an aspect of the disclosure, an advanced passive clearance control (APCC) control ring is provided. The APCC control ring includes first and second cover sections, first and second wall sections and a control ring. At least one of the first and second cover sections is bonded to corresponding edges of the first and second wall sections by field assisted sintering technology (FAST) processing along a planar bond surface to form an enclosure for the control ring.
In accordance with additional or alternative embodiments, both the first and second cover sections are bonded to corresponding edges of the first and second wall sections by the FAST processing along corresponding planar bond surfaces.
In accordance with additional or alternative embodiments, the control ring is a full-hoop control ring and the first and second cover sections and the first and second wall sections are fully annular.
In accordance with additional or alternative embodiments, the control ring is segmented and the first and second cover sections and the first and second wall sections are partially annular.
In accordance with additional or alternative embodiments, the enclosure forms a thermally isolated cavity therein.
In accordance with additional or alternative embodiments, a thermal barrier coating (TBC) is applied to exterior surfaces of the first and second cover sections and the first and second wall sections.
In accordance with additional or alternative embodiments, hook elements are attached to one of the first and second wall sections.
According to an aspect of the disclosure, a method of assembling an advanced passive clearance control (APCC) system is provided. The method includes forming an enclosure to thermally isolate a control ring. The forming of the enclosure includes bonding first a cover ring to respective first edges of inner and outer rings by field assisted sintering technology (FAST) and bonding a second cover ring to respective second edges of the inner and outer rings by the FAST.
In accordance with additional or alternative embodiments, the control ring and the enclosure are annular.
In accordance with additional or alternative embodiments, the control ring is a full-hoop control ring.
In accordance with additional or alternative embodiments, the control ring is segmented.
In accordance with additional or alternative embodiments, the method further includes applying a thermal barrier coating to exterior surfaces of the inner and outer rings and the first and second cover rings.
In accordance with additional or alternative embodiments, the method further includes attaching hook elements to the inner ring.
Additional features and advantages are realized through the techniques of the present disclosure. Other embodiments and aspects of the disclosure are described in detail herein and are considered a part of the claimed technical concept. For a better understanding of the disclosure with the advantages and the features, refer to the description and to the drawings.
For a more complete understanding of this disclosure, reference is now made to the following brief description, taken in connection with the accompanying drawings and detailed description, wherein like reference numerals represent like parts:
The exemplary engine 20 generally includes a low speed spool 30 and a high speed spool 32 mounted for rotation about an engine central longitudinal axis A relative to an engine static structure 36 via several bearing systems 38. It should be understood that various bearing systems 38 at various locations may alternatively or additionally be provided, and the location of bearing systems 38 may be varied as appropriate to the application.
The low speed spool 30 generally includes an inner shaft 40 that interconnects a fan 42, a low pressure compressor 44 and a low pressure turbine 46. The inner shaft 40 is connected to the fan 42 through a speed change mechanism, which in exemplary gas turbine engine 20 is illustrated as a geared architecture 48 to drive the fan 42 at a lower speed than the low speed spool 30. The high speed spool 32 includes an outer shaft 50 that interconnects a high pressure compressor 52 and high pressure turbine 54. A combustor 56 is arranged in exemplary gas turbine 20 between the high pressure compressor 52 and the high pressure turbine 54. An engine static structure 36 is arranged generally between the high pressure turbine 54 and the low pressure turbine 46. The engine static structure 36 further supports bearing systems 38 in the turbine section 28. The inner shaft 40 and the outer shaft 50 are concentric and rotate via bearing systems 38 about the engine central longitudinal axis A which is collinear with their longitudinal axes.
The core airflow is compressed by the low pressure compressor 44 then the high pressure compressor 52, mixed and burned with fuel in the combustor 56, then expanded over the high pressure turbine 54 and low pressure turbine 46. The turbines 46, 54 rotationally drive the respective low speed spool 30 and high speed spool 32 in response to the expansion. It will be appreciated that each of the positions of the fan section 22, compressor section 24, combustor section 26, turbine section 28, and fan drive gear system 48 may be varied. For example, gear system 48 may be located aft of combustor section 26 or even aft of turbine section 28, and fan section 22 may be positioned forward or aft of the location of gear system 48.
The engine 20 in one example is a high-bypass geared aircraft engine. In a further example, the engine 20 bypass ratio is greater than about six (6), with an example embodiment being greater than about ten (10), the geared architecture 48 is an epicyclic gear train, such as a planetary gear system or other gear system, with a gear reduction ratio of greater than about 2.3 and the low pressure turbine 46 has a pressure ratio that is greater than about five. In one disclosed embodiment, the engine 20 bypass ratio is greater than about ten (10:1), the fan diameter is significantly larger than that of the low pressure compressor 44, and the low pressure turbine 46 has a pressure ratio that is greater than about five 5:1. Low pressure turbine 46 pressure ratio is pressure measured prior to inlet of low pressure turbine 46 as related to the pressure at the outlet of the low pressure turbine 46 prior to an exhaust nozzle. The geared architecture 48 may be an epicycle gear train, such as a planetary gear system or other gear system, with a gear reduction ratio of greater than about 2.3:1. It should be understood, however, that the above parameters are only exemplary of one embodiment of a geared architecture engine and that the present disclosure is applicable to other gas turbine engines including direct drive turbofans.
A significant amount of thrust is provided by the bypass flow B due to the high bypass ratio. The fan section 22 of the engine 20 is designed for a particular flight condition—typically cruise at about 0.8 Mach and about 35,000 feet (10,688 meters). The flight condition of 0.8 Mach and 35,000 ft (10,688 meters), with the engine at its best fuel consumption—also known as “bucket cruise Thrust Specific Fuel Consumption (‘TSFC’”—is the industry standard parameter of lbm of fuel being burned divided by lbf of thrust the engine produces at that minimum point. “Low fan pressure ratio” is the pressure ratio across the fan blade alone, without a Fan Exit Guide Vane (“FEGV”) system. The low fan pressure ratio as disclosed herein according to one non-limiting embodiment is less than about 1.45. “Low corrected fan tip speed” is the actual fan tip speed in ft/sec divided by an industry standard temperature correction of [(Tram ° R)/(518.7 ° R)]0.5. The “Low corrected fan tip speed” as disclosed herein according to one non-limiting embodiment is less than about 1150 ft/second (350.5 m/sec).
Field assisted sintering technology (FAST) and spark plasma sintering (SPS) are consolidation processes that are executed at temperatures lower than the melting point of the subject materials. Similar to hot pressing, FAST forms bonds between materials but at temperatures ˜200° C. lower. FAST utilizes a high amperage pulsed direct current (DC) electrical current to heat the subject materials to be bonded through Joule heating while under uniaxial compression. The consolidation is a combination of solid-state transport mechanisms including primarily diffusion and creep. The result is a metallurgical bond between the materials to be joined. Consolidation or joining can be accomplished in a variety of conductive and non-conductive materials and forms.
Recently, FAST/SPS has been gaining acceptance starting in the 1990s for consolidation of powder materials into dense compacts with significantly greater efficiency than hot pressing. Due to the lower processing temperatures of FAST/SPS over other consolidation methods, FAST/SPS mitigates significant grain growth common in other diffusional bonding methods. In some cases, bonding two dense metallic materials using the FAST process has been demonstrated. Material pairs included a same alloy (e.g., PWA 1429) and dissimilar alloys (e.g., PWA 1429 to CM247). Additionally, the ability to bond both single crystal (SX) and equiaxed (EQ) materials and the ability to retain fine features along bond surfaces or lines have been demonstrated.
As will be described below, FAST is used to provide a bonded geometry that encloses a lightweight structure. A thermal barrier coating (TBC) is provided on exterior surfaces which do not contact other hardware and sliding interfaces to reduce response times. Internal features can be machined to reduce weight. An outer shell so formed and mated by FAST can be used to enclose and isolate interior surfaces from convective heat transfer.
In greater detail, there are APCC systems that minimize tip clearances between blades and blade outer air seals (BOASs) in gas turbine engines such as the gas turbine engine 20 of
With continued reference to
With reference to
As shown in
As shown in
For the embodiments of
Generally, it is to be understood that a requirement for FAST/SPS processing, as in the embodiments of
With reference to
Again, for the embodiments of
Generally, it is to be understood that a requirement for FAST/SPS processing, as in the embodiments of
With reference to
In an embodiment, a first alloy for use in the APCC control ring and the methods described herein may be a “high strength” metal alloy. Examples of the first alloy include PWA 1429, René N5, CMSX-4, CMSX-10, TMS-138 or TMS-162. The metal alloys are nickel-based metals that in addition to nickel comprise one or more of chromium, cobalt, molybdenum, aluminum, titanium, tantalum, niobium, ruthenium, rhenium, boron and carbon. The metal alloys contain one or more of the following metals in addition to nickel—2 to 10 wt % of chromium, 2 to 11 wt % of cobalt, 0.5 to 5 wt % molybdenum, 4 to 7.5 wt % of tungsten, 3-7 wt % of aluminum, 0 to 5 wt % of titanium, 3 to 10 wt % of tantalum and 2-8 wt % of rhenium. The metal alloys may also contain ruthenium, carbon and boron.
The composition of these alloys is defined to maximize mechanical properties in a single crystal form while maintaining an adequate level of environmental resistance. Table 1 and Table 2 shows preferred ranges (of the ingredients) for the compositions (in weight percent) that may be used for the first alloy. Table 2 contains broader ranges for some of the alloys (than those indicated in Table 1) that may be used in the first portion.
indicates data missing or illegible when filed
The high strength alloys can withstand stresses of greater than 800 MPa at temperatures greater than 600° C. and stresses of greater than 200 MPa at temperatures of greater than 800° C.
Second alloys for use in the APCC control ring and the methods described herein are selected for their ability to handle harsh environmental conditions and can include René 195 and René N2. These compositions were developed with an eye to improved environmental resistance. This can be seen in the Al and Cr levels as compared with Re, W, Mo shown in the Table 3. The cobalt to chromium ratios are lower for the second alloys, while the aluminum to cobalt ratio is much higher for the second alloys when compared with the first alloys.
The second alloys can be a nickel-based alloy that in addition to nickel includes one or more of chromium, cobalt, molybdenum, aluminum, titanium, tantalum, niobium, ruthenium, rhenium, boron and carbon. The metal alloys contain one or more of the following metals in addition to nickel—7 to 14 wt % of chromium, 3 to 9 wt % of cobalt, 0.1 to 0.2 wt % molybdenum, 3 to 5 wt % of tungsten, 6-9 wt % of aluminum, 0 to 5 wt % of titanium, 4 to 6 wt % of tantalum, 0.1 to 0.2 wt % of hafnium and 1-2 wt % of rhenium. The metal alloys may also contain ruthenium, carbon and boron.
The high strength alloys used in the second alloys can withstand stresses of at least 50% of the first alloys. In an embodiment, the high strength alloys used in the second alloys are environmentally resistant and withstand temperatures of greater than 1200° C. (under oxidation conditions) while undergoing less than 0.05 grams of weight loss per unit weight.
Technical effects and benefits of the present disclosure are the provision of FAST processing to produce a lightweight and slowly responding APCC control ring.
The corresponding structures, materials, acts, and equivalents of all means or step plus function elements in the claims below are intended to include any structure, material, or act for performing the function in combination with other claimed elements as specifically claimed. The description of the present disclosure has been presented for purposes of illustration and description, but is not intended to be exhaustive or limited to the technical concepts in the form disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope and spirit of the disclosure. The embodiments were chosen and described in order to best explain the principles of the disclosure and the practical application, and to enable others of ordinary skill in the art to understand the disclosure for various embodiments with various modifications as are suited to the particular use contemplated.
While the preferred embodiments to the disclosure have been described, it will be understood that those skilled in the art, both now and in the future, may make various improvements and enhancements which fall within the scope of the claims which follow. These claims should be construed to maintain the proper protection for the disclosure first described.
This application claims priority to U.S. Provisional Application No. 63/212,325 filed Jun. 18, 2021, and U.S. Provisional Application No. 63/232,967 filed Aug. 13, 2021, the contents of which are hereby incorporated by reference in their entirety.
Number | Date | Country | |
---|---|---|---|
63212325 | Jun 2021 | US | |
63232967 | Aug 2021 | US |