Patent Grant
10899913
This invention relates to a method for producing a crosslinked gel comprising fragrance.
Gels consist of a solid three-dimensional network that spans the volume of a liquid medium and ensnares it through surface tension effects. This internal network structure may result from physical bonds (physical gels) or chemical bonds (chemical gels), as well as crystallites or other junctions that remain intact within the extending fluid. Gels have been used as vehicles for fragrance delivery, as in, e.g., US2015/0231295. However, this reference does not suggest the method described herein.
The problem solved by this invention is the need for improved controlled release of fragrances.
The present invention provides a method for producing a crosslinked gel; said method comprising steps of: (a) combining (i) water, (ii) alginic acid, alginates, or mixtures thereof, (iii) carboxymethylcellulose, (iv) a salt of calcium, magnesium or zinc, (v) a nonionic surfactant and (vi) fragrance to form a gel having a surface; and (b) contacting with the surface of said gel an aqueous solution of a salt of calcium, magnesium or zinc.
Percentages are weight percentages (wt. %) and temperatures are in ° C., unless specified otherwise. Operations were performed at room temperature (20-25° C.), unless specified otherwise. Percentages of gel components are based on the entire weight of the gel. A “gel” is a mixture of ingredients which will spontaneously form a gel or the formed gel.
A “fragrance” includes any hydrophobic component which provides a pleasant scent. Examples include scents that are floral, ambery, woody, leather, chypre, fougere, musk, vanilla, fruit, and/or citrus. Fragrance oils are obtained by extraction of natural substances or synthetically produced. Fragrances produced may be simple (one essence) or complex (a mélange of essences). Often, the fragrance oils are accompanied by auxiliary materials, such as fixatives, extenders, stabilizers and solvents.
Preferably, the carboxymethylcellulose has a molar degree of substitution MScarboxy from 0.3 to 1.8, preferably at least 0.5, preferably at least 0.6; preferably no more than 1.6, preferably no more than 1.5, preferably no more than 1.4. Typically, viscosities of 1% by weight aqueous carboxymethylcellulose solutions at 20° C., determined with a Brookfield viscometer, range from 20 to 50000 mPa·s, preferably from 500 to 2000 mPa·s, and more preferably from 2000 to 10000 mPa·s. Examples of commercially available carboxymethylcellulose that are useful in the present invention include WALOCEL™ CRT 50000 PA (MScarboxy=0.7, 1% by weight Brookfield viscosity=7000 mPa·s), and more preferably WALOCEL™ CRT 30000 (MScarboxy=0.9, 1% by weight Brookfield viscosity=3500 mP·s), available from The Dow Chemical Company, Midland, U.S.A. Preferably, carboxymethylcellulose is used in the form of the sodium salt.
Preferably, the composition is substantially free of any cellulose derivative other than carboxymethylcellulose, i.e., the total amount of other cellulose derivatives is no greater than 5 wt % of total weight of cellulose derivatives, preferably no greater than 2 wt %, preferably no greater than 1 wt %, preferably no greater than 0.5 wt %.
Preferably, the gel comprises alginic acid, alginates, or mixtures thereof. Alginic acid is a linear copolymer of (1-4)-linked β-D-mannuronic acid (M-unit) and α-L-guluronic acid (G-unit) which units are linked together in different sequences or blocks. The monomers can appear in homopolymeric blocks of consecutive G-units (G-blocks), consecutive M-units (M-blocks), alternating M- and G-units (MG-blocks), or randomly organized blocks. Alginate is the salt of Alginic acid, for example sodium and/or calcium alginate. Alginic acid/alginate is extracted from seaweeds, such as giant kelp (Macrocystis pyrifera).
The gel contains the salt of a divalent cation, Ca2+, Mg2+, and/or Zn2+, preferably Ca2+. Examples of suitable gel-promoting salts include calcium carbonate, calcium phosphate, calcium hydrogen phosphate, and mixtures thereof. More than one salt of a divalent cation may be present.
Preferably, the gel comprises from 86 to 96 wt % water; preferably at least 87 wt %, preferably at least 88 wt %, preferably at least 89 wt %, preferably at least 90 wt %, preferably at least 91 wt %; preferably no more than 95 wt %, preferably no more than 94 wt %. Preferably, the gel comprises from 0.3 to 2.5 wt. % carboxymethylcellulose; preferably at least 0.5 wt %, preferably at least 0.6 wt %, preferably at least 0.7 wt %, preferably at least 0.8 wt %; preferably no more than 2 wt %, preferably no more than 1.5 wt %, preferably no more than 1.3 wt %. Preferably, the gel comprises from 0.3 to 2.5 wt. % Alginic acid, alginates, or mixtures thereof; preferably at least 0.5 wt %, preferably at least 0.6 wt %, preferably at least 0.7 wt %, preferably at least 0.8 wt %; preferably no more than 2 wt %, preferably no more than 1.5 wt %, preferably no more than 1.3 wt %. Preferably, the gel comprises from 0.1 to 1 wt % of a salt of calcium, magnesium or zinc, or a combination thereof; preferably at least 0.15 wt %, preferably at least 0.2 wt %, preferably at least 0.25 wt %; preferably no more than 0.8 wt %, preferably no more than 0.7 wt %, preferably no more than 0.6 wt %, preferably no more than 0.5 wt %, preferably no more than 0.4 wt %. Preferably the salt is a calcium salt.
Preferably, the gel comprises from 1 to 6 wt % of one or more fragrances; preferably at least 1.5 wt %, preferably at least 2 wt %; preferably no more than 5 wt %, preferably no more than 4.5 wt %, preferably no more than 4 wt %. Preferably, the fragrance is added to the gel at a temperature from 15 to 60° C., preferably from 15 to 50° C., preferably from 15 to 45° C.
Preferably, the gel comprises from 0.2 to 2 wt % of a nonionic surfactant; preferably at least 0.4 wt %, preferably at least 0.5 wt %, preferably at least 0.6 wt %, preferably at least 0.7 wt %; preferably no more than 1.8 wt %, preferably no more than 1.6 wt %, preferably no more than 1.4 wt %. More than one nonionic surfactant may be present. Preferably, the nonionic surfactant either (i) has the structure RaO-(AO)z—H, wherein Ra is aryl (e.g., phenyl), or linear or branched C6-C24 alkyl, AO at each occurrence is independently ethyleneoxy, propyleneoxy, butyleneoxy, or random or block mixtures thereof, and z is from 1 to 50;
(ii) is an alkyl polyglucoside of the formula:
wherein m is from 1 to 10 and n is from 3 to 20; or (iii) is a polyethylene glycol HO—[—CH2CH2O—]n-hydrogentated castor oil derivative, where n is from 20-60. The primary component of castor oil, the ricinoleate triglyceride, is ethoxylated. Preferably, AO is ethyleneoxy or propyleneoxy. Preferably, the nonionic surfactant comprises a C6-C18 alkyl group, an average of 2-8 moles polymerized units of propylene oxide and an average of 3-15 moles polymerized units of ethylene oxide. In a preferred embodiment, the nonionic surfactant has the following structure:
RO(CH2CH(CH3)O)x(CH2CH2O)yH
where R is a C6-C12 alkyl group, x is from 3-7 and y is from 5-12. The numbers x and y are average values derived from a mixture of compounds. Preferably, R is a C6-C10 alkyl group, preferably C7-C9 alkyl group, preferably a C8 alkyl group, preferably a 2-ethylhexyl group. Preferably, R is a branched alkyl group. Preferably, x is 4-6, preferably about 5. Preferably, y is 5-10, preferably 6-10, preferably 6-9, preferably 8-10, preferably about 9.
Preferably, the gel further comprises from 0.1 to 1 wt % glucono-delta-lactone; preferably at least 0.2 wt %, preferably at least 0.25 wt %, preferably at least 0.3 wt %, preferably at least 0.35 wt %; preferably no more than 0.9 wt %, preferably no more than 0.8 wt %, preferably no more than 0.7 wt %.
Preferably, the aqueous solution of a salt of calcium, magnesium or zinc which is applied to the surface of said gel has a concentration of the salt of calcium, magnesium or zinc from 2 to 20 wt %; preferably at least 3 wt %, preferably at least 4 wt %, preferably at least 5 wt %, preferably at least 6 wt %, preferably at least 7 wt %; preferably no greater than 16 wt %, preferably no greater than 14 wt %, preferably no greater than 13 wt %. Preferably, the amount of the aqueous solution applied to the surface is from 0.1 to 1 wt %; preferably at least 0.15 wt %, preferably at least 0.2 wt %, preferably at least 0.25 wt %; preferably no more than 0.8 wt %, preferably no more than 0.6 wt %, preferably no more than 0.5 wt %, preferably no more than 0.4 wt %. In one preferred embodiment of the invention, the additional aqueous solution of a salt of calcium, magnesium or zinc is coated on the inside of the mold prior to addition of the mixture of ingredients which will form the gel (gel precursor); if the mold is not closed and part of the gel surface is not in contact with the mold, additional aqueous solution of a salt of calcium, magnesium or zinc is applied to that part of the gel surface (e.g., by spraying, brushing, rolling, etc.), preferably at a temperature from 15 to 40° C., preferably 15 to 30° C. In another preferred embodiment of the invention, the formed gel is removed from the mold and the entire surface is then coated with the aqueous solution of a salt of calcium, magnesium or zinc. In this embodiment, preferably the solution is not applied to the mold.
Preferably, part of the carboxymethylcellulose, alginate and divalent metal salt are dissolved in water to form a first solution and part of the carboxymethylcellulose and the gluco-delta-lactone are dissolved in water to form a second solution. The solutions are combined, preferably by adding the first solution to the second solution. Preferably, the solutions are formed at a temperature from 20 to 85° C.; preferably at least 30° C., preferably at least 40° C., preferably at least 50° C., preferably at least 60° C.; preferably no more than 80° C., preferably no more than 75° C. Preferably, surfactant and fragrance are added to the combined aqueous solutions at a temperature from 15 to 60° C., preferably from 15 to 50° C., preferably from 15 to 45° C. Preferably, the gel is contacted with a salt of calcium, magnesium or zinc at a temperature from 15 to 40° C., preferably from 15 to 35° C., preferably from 15 to 30° C.
Without being bound by theory, it is believed that the method of this invention produces a gel having a higher degree of crosslinking near the surface.
Methods: TA Texture Analyzer
The TA.Texture Analyzer was used to perform tests in both tension and compression for cycling, flexure, constant strain and stress relaxation on such products as food, pharmaceuticals, cosmetics, packaging, leather, and adhesives. It has many built in test procedures to meet most product testing requirements and materials testing standards
Hardness:
The Hardness value is the peak force that occurs during the first compression. The hardness need not occur at the point of deepest compression, although it typically does for most products.
Method for Normal Procedure for Air Gel Preparation (Table 1-3) Units in Grams:
The external crosslinking enhanced the overall gel strength compared to non-coated gels.
Process Variants can significantly alter the gel strength.
Modification to Procedure for Air Gel Preparation, Units in Grams:
Procedure Variation (Samples Table 4-5)
Sample JT25: phase A and phase B were separately mixed for 60 min. Then A & C combined and mixed for 5 min. Then A (+C) & B combined and mixed for 5 min.
Fragrance Longevity was tracked vs time using four fragrance trackers from the perfume. The fragrance trackers chosen: Ethyl butyrate, Ethyl 2-methylbutyrate, Dihydromyrcenol, and Linalool. Two were high notes with high volatility and two were lower notes with lower volatility. These were tracked over two months. Results indicate that all four fragrance trackers were still available from the air gel with the lower volatility being predominately unchanged from their initial values. This is significantly better than commercial air gels currently on the market that last 2-3 weeks. See charts below. The last chart indicates the fragrance loss at 2 week and 4 week aging of the samples treated externally with CaHPO4 vs samples that were not treated externally with CaHPO4. Specifically the samples with external treatment appear to withhold or contain the fragrance longer than the samples without it.
Fragrance trackers monitored with time in Table 7 to 11.
Procedure for Fragrance Trackers Using GC-MS:
Heat to 33° C. for 0.5 min of heating prior to introduction into GC-MS (to understand VOCs that might contribute to odor
Use Column: DB-Wax (30 m×0.25 mm×0.50 μm)
Analysis by GC-MS-Olfactory
VOCs were collected by inserting a SPME fiber through the septum of a 22 mL headspace vial containing the air gels. SPME (Solid-phase microextraction) collection, 1-4 hours at room temperature, SPME injected into the hot injection port of the GC-MS-O. Analysts sniffed the GC effluent as it eluted from the GC column and recorded the retention time of the odor markers. The Column: Rtx-5MS (30 m×0.25 mm×0.25 μm). Units are ppm, vol/vol
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2017/024759 | 3/29/2017 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2017/176526 | 10/12/2017 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4125478 | Sullivan et al. | Nov 1978 | A |
| 5541234 | Unger | Jul 1996 | A |
| 7488471 | Mercier | Feb 2009 | B2 |
| 20050037080 | Lynch et al. | Feb 2005 | A1 |
| 20120230936 | Mikkelsen | Sep 2012 | A1 |
| 20130157922 | Mikkelsen et al. | Jun 2013 | A1 |
| 20140158788 | Mikkelsen et al. | Jun 2014 | A1 |
| 20150231295 | Yun et al. | Aug 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 0140370 | Jun 2001 | WO |
| 03090718 | Nov 2003 | WO |
| 2011008365 | Jan 2011 | WO |
| 2012051131 | Apr 2012 | WO |
| 2014063358 | May 2014 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20200148859 A1 | May 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62319028 | Apr 2016 | US |