Al-Mg-Si alloy having a high ductility and method of its manufacture

Abstract

An AlMgSi-alloy suitable for manufacturing components having a high ductility, characterized in that the alloy comprising, in wt. %: 1Mg0.3 to1.0Si0.3 to1.2Femax.0.35Mn>0.15 to0.4V0.05 to0.20Cumax.0.3Crmax.0.2Znmax.0.2Timax.0.1

Description

FIELD OF THE INVENTION

[0001] The invention relates to an AlMgSi-alloy suitable for manufacturing components having a high ductility and to a method for the manufacture of such a new aluminium alloy. Hot-worked products, in particular obtained by means of extrusion, of the alloy of this invention can be used for example in railway vehicles, or in welded structures, or can be further formed by means of hydroforming.

DESCRIPTION OF THE RELATED ART

[0002] Al—Mg—Si type aluminium alloys such as Aluminium Association 6xxx series aluminium alloys are widely used and favoured for their moderately high yield and tensile strength, low quench sensitivity, good corrosion resistance and favourable forming characteristics. AA6xxx series alloys are increasingly attractive to industries such as transportation because of these well-known properties. Further AA6xxx series alloys exhibit in general satisfactory welding characteristics, by which this type of alloy is also widely used for applications resulting in the construction of welded structures. Additional applications for AA6xxx series alloys would be possible when ductility is further increased.

[0003] Such an aluminium alloy is known from the international patent application no. WO 97/44501 (Alusuisse). The known alloy contains the alloying elements, in wt. %:

Si 0.4 to 0.8
Mg 0.4 to 0.7
Fe max. 0.30, and preferably 0.18 to 0.25
Cu max. 0.20, and preferably 0.12 to 0.16
Mn max. 0.15, and preferably 0.05 to 0.10
V  0.05 to 0.20
Cr max. 0.10 and preferably max. 0.01
Ti max. 0.10
Zn max. 0.10

[0004] inevitable impurities and balance aluminium.

[0005] Some other disclosures of Al—Mg—Si alloys found in the prior art literature will be mentioned below.

[0006] U.S. Pat. No. 4,525,326 (Alusuisse) describes an aluminium extrusion alloy, subsequently registered under designation AA 6008, consisting of, in wt. %:

Mg 0.3 to 1.0
Si 0.3 to 1.2
V  0.05 to 0.2, and preferably 0.06 to 0.14
Fe 0.1 to 0.5, and preferably 0.15 to 0.25
Cu up to 0.4
Mn 0.25 to 0.66 of the Fe-concentration, preferably 0.25 to 0.5
   of the Fe-concentration.

[0007] balance aluminium and impurities.

[0008] In a preferred embodiment the alloy further comprises the alloying element cobalt in a range of 0.25 to 0.5 of the Fe-level.

[0009] U.S. Pat. No. 5,527,404 (Alcoa) describes an aluminium extrusion alloy particularly useful in the manufacture of vehicle primary structures, consisting of, in wt. %:

Mg 0.45 to 0.7
Si 0.35 to 0.6
V  0.1 to 0.35
Fe 0.1 to 0.4

[0010] balance aluminium and impurities.

[0011] EP-A-0 676 480 (northwest Aluminum Co.) describes an aluminium alloy consisting of, in wt. %:

Si 0.2 to 2
Mg 0.3 to 1.7
Cu up to 1.2
Mn up to 1.1
Cr 0.01 to 0.4

[0012] and at least one of: 0.01 to 0.3 V, 0.01 to 0.1 Be, 0.01 to 0.1 Sr balance aluminium and impurities.

[0013] JP-A-04341546 (Sumitomo Light Metal Ind.) describes a method of subjecting an aluminium alloy containing, in wt. %:

Mg 0.4 to 1.5
Si 0.4 to 1.3
Cu 0.05 to 0.9

[0014] one or more selected from the group of

Mn 0.05 to 0.5
Cr 0.05 to 0.30
V  0.05 to 0.30
Zr 0.05 to 0.30

[0015] balance aluminium and impurities,

[0016] to homogenising at 520 to 560° C. for 6 to 10 hours, thereafter subjecting the alloy to superheating of 540 to 560° C., thereafter reducing the temperature to 460 to 520° C., and extruding the alloy at a temperature of 460 to 520° C., and subsequently executing press quenching. The described method relates to a multiple homogenisation cycle with a maximum temperature of 560° C.

SUMMARY OF THE INVENTION

[0017] An object of the invention is to provide a new aluminium alloy suitable for the manufacture of a product made of components having a higher ductility than manufactured from the aluminium alloy known from WO 97/44501, and further that the aluminium alloy has improved welding properties. A further object of the invention is to provide a method for the manufacture of a product made of the new aluminium alloy.

[0018] According to the invention, there is provided an aluminium alloy consisting of the alloying elements, in wt. %:

	Si	0.3 to	1.2
	Mg	0.3 to	1.0
	Fe	max.	0.35
	Mn	<0.15 to	0.4
	V	0.05 to	0.20
	Cu	max.	0.3
	Cr	max.	0.2
	Zn	max.	0.2
	Ti	max.	0.1

[0019] impurities max. 0.05% each, total max. 0.15%, balance aluminium.

[0020] By the invention we can provide alloy plate or extrusions having good strength, improved ductility, good resistance to corrosion and, in particular in the case of extruded products, exhibits a uniform surface, absence of die pick-up, good longitudinal weld seams, and the possibility to extrude complicated shaped sections which can be both thin and/or thick walled and can be processed at economic extrusion rates. In particular the increased manganese content in the aluminium alloy in accordance with the invention attributes to an improved ductility and a better welding behaviour. Further the aluminium alloy has improved properties after welding and is less sensitive for hot-cracking during welding and after extrusion and heat-treatments has a fine-grained recrystallized microstructure. And further the aluminium alloy has a lower quench-sensitivity than aluminium alloys from the AA6005 A-series type.

[0021] In a preferred embodiment the aluminium alloy in accordance with the invention has a manganese content in a range of >0.15 to 0.30 wt. %. In this range an optimum in mechanical properties and extrudibility is obtained.

[0022] The aluminium alloy in accordance with the invention has preferably a Mn/Fe ratio in a range of 0.45 to 1.0, and more preferably in a range of 0.67 to 1.0.

[0023] The magnesium content is preferably in a range of 0.5 to 0.7 wt. %, in which range the strength is optimised, in particular when used in combination with a silicon content in a range of 0.4 to 0.7 wt. %. A magnesium content below 0.3 wt. % does not provide sufficient strength in the component obtained from the alloy of the invention.

[0024] In another embodiment of the alloy in accordance with the invention the silicon content is in a range of 0.5 to 0.6 wt. % and the magnesium content is a range of 0.4 to 0.7 wt. % and more preferably the magnesium content is in a range of 0.45 to 0.55 wt. %. In this particular embodiment of the alloy the mechanical properties of the manufactured component are comparable to those made of an AA6106-alloy.

[0025] In this type of aluminium alloys vanadium is added to enhance recrystallisation and is present in a range of 0.05 to 0.2 wt. %, and more preferably in a range of 0.05 to 0.15 wt. %. It should be mentioned that U.S. Pat. No. 4,525,326 (Alusuisse) discloses an aluminium alloy for the manufacture of extruded products were the quench sensitivity with respect to strength can be improved by the addition of vanadium. The aluminium alloy contains 0.05 to 0.2% vanadium, and further manganese in a concentration equal to ¼ to ⅔ of the iron concentration.

[0026] Copper should be not more than 0.3 wt. %. Copper levels above 0.3 wt. % gives rise to unacceptable corrosion resistance of products made of the alloy of the invention. A more preferred maximum for copper is 0.2 wt. %.

[0027] Chromium improves the corrosion resistance of the alloy. However, chromium limits the solubility of manganese and further reduces the extrudibility of the aluminium alloy. Therefor, to avoid formation of coarse primaries and to improve extrusion capability, the chromium content must not be more than 0.2 wt. %, preferably not more than 0.1 wt. %, and more preferably not more than 0.06 wt. %.

[0028] Zinc is considered to be an impurity element and can be tolerated up to 0.2 wt. %, but is preferably less than 0.1 wt. %.

[0029] Titanium is important as a grain refiner during solidification of both ingots and welded joints produced using the alloy of the invention. The preferred range for titanium is not more than 0.1 wt. %.

[0030] The balance is Al and inevitable impurities. Typically each impurity element is present at 0.05 wt. % maximum and the total of impurities is 0.15 wt. % maximum.

[0031] In addition, the invention is embodied in a method for manufacturing a product of the aluminium alloy in accordance with the invention, wherein the method comprises the steps of, in succession,

[0032] (a) casting the alloy into ingots;

[0033] (b) homogenising the cast ingot;

[0034] (c) hot-working in the homogenised ingot into a product;

[0035] (d) ageing of the product.

[0036] In this way, it is achieved that the product acquires excellent properties against a reasonable cost level for the applications which the inventors have in mind.

[0037] For casting the aluminium alloy into ingots or extrusion billets both continuous and semi-continuous casting processes can be used. It has surprisingly been found that during semi-continuous Direct Chill (DC)-casting of billets the aluminium alloy is significantly less sensitive for cracking during casting. The reduced crack sensitivity is mainly attributed to the increased Mn content over the known aluminium alloy.

[0038] After casting, the aluminium alloy is homogenised. The aim of the homogenising treatment is amongst other things, to homogenise the microstructure, to dissolve the magnesium and silicon, to level off possible residual stresses resulting from the casting process, and to spheroidize sharp or needle shaped intermetallic compounds formed during solidification of the aluminium alloy. A homogenisation for of 8 to30 hours in a temperature in the range of 530° C. to just below the melting temperature of the aluminium alloy is sufficient. A longer homogenisation time is not disadvantageous, but is not required and only serves to raise the costs of production. Preferably, the alloy is homogenised for 8 to 20 hours in a temperature range of 580° C. to just below the melting temperature of the aluminium alloy. More preferably, the alloy is homogenised for 8 to 16 hours in a temperature range of 590 to 605° C. It has been found that such a high homogenisation temperature is advanteaous for hot-working the alloy by means of extrusion into complex shaped sections which can be both thin walled or thick walled. In this manner an acceptable extrusion rate can be maintained despite of the relatively high Mn-content. Further due to the relatively high homogenisation treatment the final product has a fine-grained fully recrystallized microstructure.

[0039] After homogenisation, the alloy is hot-worked into sheets, rods, profiles or wire or other shaped materials suitable for processing into products. Hot-working includes rolling, forging and hydroforming. The invention is preferably characterised by the ingot or extrusion billet being processed into products via an extrusion process, wherein either direct or indirect extrusion may be used. The ingot temperature during extrusion is preferably in the temperature range of 450 to 580° C. Using an extrusion process the aluminium alloy in accordance with the invention can be processed into e.g. T-shaped profiles with a wall-thickness of up to 20 mm, and multi-hollow-sections with wall-thickness in a range of 1.5 to 4.0 mm.

[0040] After hot extrusion, the alloy of the invention will be quenched, by means of water, or water spray or elevated air. This is also designated by the term “ press-quenching”.

[0041] In another embodiment of the method the alloy of the invention will first cool down after the hot extrusion. The cooling rate is not so important here. Cooling will typically take place in air. Thereafter, the alloy is heat treated by keeping it for 0.5 to 3 hours in a temperature range of 400 to 565° C. The aim of this heat treatment, also known as solution heat treatment, is to dissolve, amongst other things, the silicon and magnesium. This solution heat treatment preferably takes place for 0.5 to 1.5 hours in a temperature range of 400 to 560° C. Immediately after the solution heat treatment, the alloy is preferably cooled to under 100° C., preferably by means of quenching in water, in order to minimise uncontrolled precipitation.

[0042] In a following step, the material is aged to the desired level of mechanical and physical properties. The ageing step can be performed by means of natural ageing or artificial ageing by 6 to 30 hours annealing in a temperature range of 130 to 180° C. This annealing preferably takes place for 8 to 12 hours in a temperature range of 160 to 180° C., after which cooling to room temperature takes place via cooling to the air.

[0043] After the complete heat treatment cycle, the material can be processed into products of many kinds. The aluminium alloy is preferably suitable for application to components which, amongst other things, require a high capacity for absorbing kinetic energy by plastic deformation, such as components suitable for application in railway vehicles. The aluminium alloy is further suitable to be applied in welded constructions, in particular in vehicle constructions. Further the aluminium alloy is suitable to be applied in hydroformed structures.

[0044] The invention is now illustrated by some examples, which do not limit the scope of the invention.

EXAMPLES

[0045] Table 1 lists the chemical composition in weight percent of some comparative materials (alloys 1 to 3) and alloys which fall within the scope of the invention (alloys 4-5). These alloys were processed by the steps of

[0046] (i) DC-casting of 344 mm diameter extrusion billets;

[0047] (ii) homogenisation, see Table 2;

[0048] (iii) extrusion at 480° C.;

[0049] (iv) press-quench;

[0050] (v) ageing for 9 hours at 160° C.

[0051] Table 2 lists the homogenisation treatment applied for each alloy. The billets were extruded to the following shapes:

[0052] (a) T-shaped profile with a wall-thickness of 20 mm;

[0053] (b) Multihollow-section with wall-thickness between 2.5 and 4.0 mm.

[0054] All results (microstructures, mechanical properties) on front end, middle, and back end on each investigated extruded products of every type of alloy showed in the extrusion direction, only very small variations and therefore a further differentiation within one variant was not necessary. The following results are in each and every case mean values out of the different parts of the material.

[0055] The microstructure in the T-shaped thick walled extrusion product (a) showed in case of alloy 1 a non-recrystallized center and a layer of coarse grains with a diameter of about 1 mm at the surface. Alloy 4 showed a non-recrystallized center, and a layer with a thickness of 3 to 4 mm of coarse grains near the surface. Alloy 5 showed across the whole cross-section of the product a fully recrystallised microstructure with uniform fine grains. The microstructure of alloy 2 was very similar to the microstructure of alloy 4. The same applied for alloy 3 and alloy 5.

[0056] The microstructure in the multihollow profile (b) showed in case of alloy 1 a combination of small and coarse grains and also some non-recrystallized sections. Alloy 4 showed a fully recrystallized microstructure and large differences in the grain size. Alloy 5 showed a fully recrystallized microstructure and a more uniform grain size than with alloy 4. The microstructure of alloy 2 was very similar to the microstructure of alloy 4. The same applied for alloy 3 and alloy 5.

[0057] Table 3 lists the results of the testing for mechanical properties, where Rm is the ultimate tensile strength, Rp 0.2 is the 0.2% yield strength and A is the elongation at fracture (A5 in accordance with German standards).

[0058] From Table 3 it can be seen that an increase of the Mn content to above 0.15% has a significant effect on the ductility of the extruded product. For the T-shaped thick walled extrusions it has to mentioned that the specimens for tensile testing have been taken out of the centre of the profiles (10 mm diameter specimens) and therefore show in the case of alloy 1,2 and 4 an increase in the tensile properties due to the non-recrystallized parts present in the centre. It has to be considered however, that the mechanical values show significant differences in thickness direction across the shape. The values in the center part—as presented in table—are quite high for alloys 1, 2 and 4. This is due to the positive effect of testing the non-recrystallized zones. The properties close to the surface in the recrystallized parts are considerably lower in these cases. Alloys 3 and 5 as fully recrystallized extrusions are showing the most consistent behaviour.

[0059] Table 4 lists the mechanical properties of the extruded profiles after welding using a fully automatic MIG-device and AlMg4.5MnZr filler wire with a thickness of 1.6 mm. The T-shaped profiles (a) have 6 layers and the weld bead overfill was removed prior to testing. The multi-hollow profiles (b) have 1 layer (at wall thickness of 4 mm) and the weld bead was not removed prior the testing. In all cases the cracks during tensile testing were observed in the heat-effected zone.

[0060] The weldments were showing the normal behaviour concerning the formation of grain boundary openings. The amount and size of grain boundary openings are strongly dependent on the grain size of the parent material. Alloy 5 as the variant with the smaller and most uniform grain size showed the best properties, followed by alloy 4. Alloy 1—namely in the case of the multi-hollow section—exhibited a significantly for the formation of grain boundary openings.

TABLE 1
Alloy	Invention	Si	Fe	Cu	Mn	Mg	Cr	Zn	V	Ti	Mn/Fe
1	out	0.63	0.24	0.09	0.10	0.64	0.05	0.06	—	<0.1	0.41
2	out	0.58	0.23	0.13	0.02	0.58	0.05	0.04	0.09	<0.1	0.08
3	out	0.58	0.23	0.13	0.02	0.58	0.05	0.04	0.09	<0.1	0.08
4	in	0.58	0.23	0.13	0.18	0.57	0.05	0.04	0.09	<0.1	0.78
5	in	0.58	0.23	0.13	0.18	0.57	0.05	0.04	0.09	<0.1	0.78

[0061]

TABLE 2
Alloy Homogenisation
1     10 hours at 565° C.
2     10 hours at 565° C.
3     10 hours at 600° C.
4     10 hours at 565° C.
5     10 hours at 600° C.

[0062]

	TABLE 3
	T-shaped section	Multi-hollow section
	Rm	Rp 0.2	A	Rm	Rp 0.2	A
Alloy	[MPa]	[MPa]	[%]	[MPa]	[MPa]	[%]
1	335	302	17	277	251	7
2	329	296	17	284	247	10
3	289	256	18	287	250	10
4	322	287	17	280	243	11
5	278	244	19	279	241	11

[0063]

	TABLE 4
	T-shaped section	Multi-hollow section
	Rm	Rp 0.2	A	Rm	Rp 0.2	A
Alloy	[MPa]	[MPa]	[%]	[MPa]	[MPa]	[%]
1	228	162	4.5	164	130	3.5
4	215	153	4.0	168	129	3.9
5	211	150	5.1	201	142	4.5

Claims

1. An AlMgSi-alloy suitable for manufacturing components having a high ductility, characterised in that the alloy consists of, in wt. %: 13Mg0.3 to 1.0Si0.3 to 1.2Femax. 0.35Mn>0.15 to 0.4V0.05 to 0.20Cumax. 0.3Crmax. 0.2Znmax. 0.2Timax. 0.1impurities max. 0.05% each, total max. 0.15%, balance aluminium.

2. An AlMgSi-alloy in accordance with claim 1, characterised in that the Mn content is in a range of >0.15 to 0.30 wt. %.

3. An AlMgSi-alloy in accordance with claim 1, characterised in that the Mg content is in a range of 0.5 to 0.7 wt. %.

4. An AlMgSi-alloy in accordance with 1, characterised in that the Si content is in a range of 0.4 to 0.7 wt. %.

5. An AlMgSi-alloy in accordance with claim 1, characterised in that the Si content is in a range of 0.5 to 0.6 wt. % and the Mg content is in a range of 0.4 to 0.7 wt. %.

6. An AlMgSi-alloy in accordance with claim 1, characterised in that the Si content is in a range of 0.5 to 0.6 wt. % and the Mg content is in a range of 0.45 to 0.55 wt. %.

7. Method of producing a product of an AlMgSi-alloy in accordance with claim 1, characterised in that the method comprises the steps of subsequently: (a) casting the alloy into ingots; (b) homogenising the cast ingot; (c) hot-working in the homogenised ingot into a product; (d) ageing of the product.

8. Method in accordance with claim 7, characterised in that hot-working comprises extrusion.

9. Method in accordance with claim 7, characterised in that homogenising comprises holding the cast ingot for 8 to 30 hours in a temperature range of 530° C. to just below melting temperature of the alloy.

10. Method in accordance with claim 7, characterised in that homogenising comprises holding the cast ingot for 8 to 20 hours in a temperature range of 580° C. to just below melting temperature of the alloy.

11. Method in accordance with claim 7, characterised in that homogenising comprises holding the cast ingot for 8 to 16 hours in a temperature range of 590 to 605° C.

12. Method of use of a component made from the AlMgSi-alloy in accordance with claim 1 or obtained from the method in accordance with claim 7 in a railway vehicle.

13. Welded structure comprising at least one welded plate or extrusion made of aluminium-magnesium-silicon alloy according to claim 1.

14. Hydroformed structure comprising a component made from the AlMgSi-alloy in accordance with claim 1 or obtained from the method in accordance with claim 7.