20200360900
The present invention relates to zirconia-multi-walled carbon nanocomposite, a method of manufacturing a zirconia multi walled carbon nanotube (MWCNT) composite and the use of a zirconia-multi-walled carbon nanocomposite as a photocatalyst for the production hydrogen from water.
Zirconia (ZrO2) has long been used in many applications. It has favorable mechanical properties such as toughness, hardness, impact strength and ionic properties, and is utilized in many applications such as structural reinforcements, dental implants, and sensors. The catalytic activity of zirconia has been utilized in numerous reactions [Srinivasan et al. “Zirconia: a review of a super ceramic”, in: D. L. Perry (Ed.), Materials Synthesis and Characterization, Springer, US, 1997, pp. 147-188; and Almeida et al. “Enhanced mechanical properties in ZrO2 multi-walled carbon nanotube nanocomposites produced by sol-gel and high-pressure” Nano-Structures & Nano-Objects, 4 (2015) 1-8]. With the advancement of nanomaterial synthesis, new approaches for the synthesis of zirconia based materials enabled tailoring the material for a specific purpose by enhancing certain desired properties. For example, Almeida et al. used the sol-gel approach to enhance the mechanical properties of ZrO2-multi-walled carbon nanotube nanocomposite. Amin et al. [“Electrocatalytic activity of PteZrO2 supported on different carbon materials for methanol oxidation in H2504 solution” International Journal of Hydrogen Energy 41 (2016) 1846-1858] describe the synthesis and electrolytic properties of Pt—ZrO2/MWCNTs and other compounds for methanol oxidation in sulfuric acid solution by a solid state reaction method utilizing intermittent microwave heating. Malolepszy et al. [“Deactivation resistant PdZrO2 supported on multiwall carbon nanotubes catalyst for direct formic acid fuel cells” International Journal of Hydrogen Energy 40 (2015) 16724-16733] utilized a microwave assisted hydrothermal method for the synthesis of Pd-ZrO2/MWCNT and used it to construct a formic acid fuel cell. Another fuel cell was built using a Pt catalyst supported on sulfated MWCNT-ZrO2. In the preparation of the nanocomposite, ammonia and sulfuric acid were used as precipitating and sulfating agents, respectively [Dao-Jun et al. “Synthesis of sulfated ZrO2/MWCNT composites as new supports of Pt catalysts for direct methanol fuel cell application” Applied Catalysis B: Environmental 89 (2009) 597-601]. Michalek et al. [Mechanical and functional properties of Al2O3—ZrO2-MWCNTs nanocomposites, Journal of the European Ceramic Society 34 (2014) 3329-3337] describes the mechanical and functional properties of Al2O3—ZrO2-MWCNT nanocomposites synthesized by a method that included the use of liquid nitrogen and freeze drying. A cobalt doped ZrO2 decorated multi-walled carbon nanotube catalyst was synthesized via a homogenous co-precipitation process and was utilized for the photo-degradation of indigo, carmine, and eosin Y dyes [Anku et al. “Cobalt doped ZrO2 decorated multi-walled carbon nanotube: A promising nanocatalyst for photo-degradation of indigo carmine and eosin Y dyes” Progress in Natural Science: Materials International 26 (2016) 354-361]. Anku et al. describes the synthesis of palladium-doped-ZrO2-MWCNTs nanocomposite employing a homogenous co-precipitation method and used the nanocomposite in water treatment [Palladium-doped-ZrO2-multiwalled carbon nanotubes nanocomposite: an advanced photocatalyst for water treatment, Appl. Phys. A (2016) 122:579]. Wang et al. [Fabrication and characterization of a zirconia/multi-walled carbon nanotube mesoporous composite, Materials Science and Engineering C 33 (2013) 3931-3934] reported the synthesis of a mesoporous MWCNT-ZrO2 nanocomposite via a hydrothermal method and the use of the cationic surfactant cetyltrimethylammonium bromide. Liu et al. [Controlling the Particle Size of ZrO2 Nanoparticles in Hydrothermally Stable ZrO2/MWCNT Composites, Langmuir 2012, 28, 17159-17167] describes a method of controlling particles size of ZrO2 in a composite of MWCNTs decorated with ZrO2 nanoparticles by a grafting method followed by high-temperature annealing.
The present disclosure describes the synthesis of a ZrO2-multi-walled carbon nanotube nanocomposite (MWCNT-ZrO2) using a templating agent. The method may be carried out using available laboratory equipment. The nanocomposite produced by the method is an efficient photocatalyst and can be utilized in a method for the production of hydrogen.
BRIEF SUMMARY OF THE INVENTION
According to a first aspect of the invention, the current disclosure relates to a method of making a ZrO2-multi-walled carbon nanotube nanocomposite (MWCNT-ZrO2), comprising:
In a preferred embodiment of the method, the templating agent is a non-ionic surfactant, preferably a poloxamer such as but not limited to Pluronic F-127, Pluronic P-123, Pluronic F-108, and Pluronic F-68. In a more preferred embodiment, the templating agent is Pluronic F127.
In another preferred embodiment, the zirconium alkoxide is zirconium methoxide, zirconium ethoxide, zirconium propoxide, zirconium isopropoxide, zirconium butoxide, zirconium isobutoxide, and zirconium t-butoxide. In a preferred embodiment, the zirconium alkoxide is zirconium isopropoxide.
In another preferred embodiment, the solvent is an alcohol, preferably methyl alcohol, ethyl alcohol, propyl alcohol, isobutyl alcohol, butyl alcohol, isobutyl alcohol, and t-butyl alcohol, and most preferably isopropyl alcohol.
In another preferred embodiment, the ratio of zirconium alkoxide to solvent to the templating agent is in the range of 0.2:10:0.1 to 3:10:0.5, preferably 0.5:10:0.2 to 1.5:10:0.4, more preferably 0.8:10:0:25. In the most preferred embodiment of the method, the ratio is 1:10:0.3.
In another embodiment, the produced MWCNT-ZO2 nanoparticle comprises MWCNT in the range 0.5%-8% by weight, preferably 0.7%-7% by weight of MWCNT, more preferably 0.8%-6% by weight of MWCNT, and even more preferably 1.0%-5.0% by weight of MWCNT. In the most preferred embodiment of the method, the produced MWCNT-ZO2 nanoparticle comprises 3% by weight of MWCNT.
Any acid may be used to precipitate the nanoparticles in any of the mentioned embodiments of the method. The preferred acid is a carboxylic acid such as acetic acid, propionic acid, butyric acid, oxalic acid, succinic acid, citric acid, and tartaric acid. In the most preferred embodiment of the method, acetic acid may be used.
In another preferred embodiment, the mixture is stirred at a temperature in the range of 20-80° C., preferably 30-70° C., more preferably, 40-65° C., and most preferably 50-60° C.
In some embodiments, the MWCNT-ZrO2 is filtered and dried under vacuum at about 60° C.
In some other preferred embodiment, the dried MWCNT-ZrO2 is calcined of at about 300° C. under nitrogen.
A second aspect of the invention is related to a MWCNT-ZrO2 nanocomposite, preferably prepared by the method described herein.
A preferred embodiment of the nanocomposite contains about 0.5-8% MWCNT by weight of MWCNT, preferably 0.7%-7%, more preferably 0.8%-6% by weight of MWCNT, and even more preferably 1.0%-5.0% by weight of MWCNT. In the most preferred embodiment of the method, the produced ZO2-MWCNT nanoparticle comprises 3% by weight of MWCNT.
In another preferred embodiment, the nanocomposite has a surface area in the range of 53.5±2 to 59.5±2 m2/g. A more preferred embodiment of the method, the nanocomposite has a surface area in the range of 56.5±1 to 59.5±1 m2/g. The most preferred embodiment, the nanocomposite has a surface area of 59.2±0.6 m2/g.
In another preferred embodiment, the nanocomposite is a photocatalyst having band gap energy in the range 3.33 to 2.63 eV. In a more preferred embodiment, the band gap is 2.67±0.05.
In another preferred embodiment, the nanocomposite contains MWCNT in an amount selected from the group consisting of 1 wt. %, 2 wt. %, 3 wt. %, 4 wt. %, and 5 wt. %. In the most preferred embodiment, the nanocomposite contains 3 wt. % MWCNT.
A third aspect of the invention is directed to a photochemical method for the production of hydrogen from water, the method comprising irradiating a reaction mixture comprising an aqueous solution and a photocatalyst comprising the MWCNT-ZrO2 nanocomposite with light to form hydrogen gas.
In a preferred embodiment, the photocatalyst is selected from the group consisting of 2 wt. % MWCNT-ZrO2, 3 wt. % MWCNT-ZrO2, 4 wt. % MWCNT-ZrO2, and 5 wt. % MWCNT-ZrO2.
In another preferred embodiment, the reaction mixture contains about 0.5-4.0 g/L photocatalyst, more preferably 1.0-3.0 g/L, and most preferably, 1.5-2.5 g/L.
In another preferred embodiment, the reaction mixture contains about 2.0±0.2 g/L of the photocatalyst.
In another preferred embodiment, reaction mixture comprises an alcohol wherein the alcohol is selected from the group consisting of methanol, ethanol, propanol, isopropanol, butanol, isobutanol, and t-butanol.
In a preferred embodiment, the reaction mixture contains alcohol in the range 2%-20%, preferably, 5%-15%, more preferably 8%-12%, and most preferably 9%-11%.
A more complete appreciation of the disclosure and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:
Embodiments of the present disclosure will now be described more fully hereinafter with reference to the accompanying drawings, in which some, but not all embodiments of the disclosure are shown. The present disclosure will be better understood with reference to the following definitions.
All publications mentioned herein are incorporated herein by reference in full for the purpose of describing and disclosing the methodologies, which are described in the publications, which might be used in connection with the description herein. The publications discussed above and throughout the text are provided solely for their disclosure prior to the filing date of the present application. Nothing herein is to be construed as an admission that the inventors are not entitled to antedate such disclosure by virtue of prior disclosure. Also, the use of “or” means “and/or” unless stated otherwise. Similarly, “comprise,” “comprises,” “comprising” “include,” “includes,” and “including” are interchangeable and not intended to be limiting.
As used herein, the terms “compound” is intended to refer to a chemical entity, whether in a solid, liquid or gaseous phase, and whether in a crude mixture or purified and isolated.
As used herein, the term “alkyl” unless otherwise specified refers to both branched and straight chain saturated aliphatic primary, secondary, and/or tertiary hydrocarbons of typically C1 to C10, and specifically includes, but is not limited to, methyl, trifluoromethyl, ethyl, propyl, isopropyl, cyclopropyl, butyl, isobutyl, t-butyl, pentyl, cyclopentyl, isopentyl, neopentyl, hexyl, isohexyl, cyclohexyl, cyclohexylmethyl, 3-methylpentyl, 2,2-dimethylbutyl, and 2,3-dimethylbutyl. As used herein, the term optionally includes substituted alkyl groups. Exemplary moieties with which the alkyl group can be substituted may be selected from the group including, but not limited to, hydroxyl, alkoxy, aryloxy, or combination thereof.
As used herein, the term “alcohol” unless otherwise specified refers to a chemical compound having an alkyl group bonded to a hydroxyl group. Many alcohols are known in the art including, but not limited to, methanol, ethanol, propanol, isopropanol, butanol, isobutanol and t-butanol, as well as pentanol, hexanol, heptanol and isomers thereof. Since the alkyl group may be substituted with one or more hydroxyl group, the term “alcohol” includes diols, triol, and sugar alcohols such as, but not limited to, ethylene glycol, propylene glycol, glycerol, and polyol.
As used herein, the term “about” refers to an approximate number within 20% of a stated value, preferably within 15% of a stated value, more preferably within 10% of a stated value, and most preferably within 5% of a stated value. For example, if a stated value is about 8.0, the value may vary in the range of 8±1.6, ±1.0, ±0.8, ±0.5, ±0.4, ±0.3, ±0.2, or ±0.1.
The present disclosure is further intended to include all isotopes of atoms occurring in the present compounds. Isotopes include those atoms having the same atomic number but different mass numbers. By way of general example, and without limitation, isotopes of hydrogen include deuterium and tritium. Isotopes of carbon include 13C and 14C. Isotopes of zirconium include 90Zr, 91Zr; 92Zr, 93Zr, 94Zr, and 96Zr. Isotopes of oxygen include 16O, 17O, and 18O. Isotopically labeled compounds of the invention can generally be prepared by conventional techniques known to those skilled in the art or by processes and methods analogous to those described herein, using an appropriate isotopically labeled reagent in place of the non-labeled reagent otherwise employed.
As used herein a “polymer” or “polymeric resin” refers to a large molecule or macromolecule, of many repeating subunits and/or substances composed of macromolecules. As used herein a “monomer” refers to a molecule or compound that may bind chemically to other molecules to form a polymer. As used herein the term “repeat unit” or “repeating unit” refers to a part of the polymer or resin whose repetition would produce the complete polymer chain (excluding the end groups) by linking the repeating units together successively along the chain. The process by which monomers combine end to end to form a polymer is referred to herein as “polymerization” or “polycondensation”, monomers are molecules which can undergo polymerization, thereby contributing constitutional repeating units to the structures of a macromolecule or polymer. As used herein “resin” or “polymeric resin” refers to a solid or highly viscous substance or polymeric macromolecule containing polymers, preferably with reactive groups. As used herein a “copolymer” refers to a polymer derived from more than one species of monomer and are obtained by “copolymerization” of more than one species of monomer. Copolymers obtained by copolymerization of two monomer species may be termed bipolymers, those obtained from three monomers may be termed terpolymers and those obtained from four monomers may be termed quarterpolymers, etc. As used herein, “cross-linking”, “cross-linked” or a “cross-link” refers to polymers and resins containing branches that connect polymer chains via bonds that link one polymer chain to another. The cross-link may be an atom, a group of atoms, or a number of branch points connected by bonds, groups of atoms, or polymer chains. In the majority of cases, a cross-link is a covalent structure or covalent bond but the term may also describe sites of weaker chemical interactions, portion crystallites, and even physical interactions and entanglements. The cross-linking can alter the physical and mechanical properties of the polymer. Cross-linking may be formed by chemical reactions that are initiated by heat, pressure, change in pH, and/or radiation, with or without the presence of a cross-linking agent and/or catalyst. In certain embodiments, at least one diaminoalkane or di-dithiocarbamate alkane functions as a cross-linking agent for the cross-linked polymeric resin described herein. In a preferred embodiment, the diaminoalkane or di-dithiocarbamate chains function as cross-linking agents or monomers can be add to the polymer or a polymerization reaction to modify to increase the cross-linking of the polymer.
As used herein, the term “template” refers to as a structure directing agent and is stable under hydrothermal aging conditions and furthermore hydrophobic relative to the metal salts. Many templates used in the manufacturing nanoparticles are known in the art. They include all types of surfactants including anionic surfactants, cationic surfactants, and neutral surfactants as well as polymers with surfactant properties such as Poloxamer. The surfactant may act as a nucleation site for the formation of the nanoparticles. Alkyl ammonium salts are commonly used as templates to form structures in solution that interacts with the inorganic material in solution and serve as a template for the growth of nanoparticles. A commonly used template is tetrapropylammonium hydroxide, tetraethylammonium hydroxide, tetrabutylammonium hydroxide, or tetrapentylammonium hydroxide. Other known templates include cetyl trimethylammonium bromide, cetyl triethylammonium bromide, dodecyl triethylammonium bromide, Brij-56, or Brij-30. The template is usually decomposed during calcining at temperatures in the range 545-600° C. for 6-10 hours.
In this disclosure, the terms “poloxamer” and “Pluronic” have the same meaning and are used interchangeably. Poloxamers or Pluronics are nonionic triblock copolymers composed of a central hydrophobic block of polypropylene glycol flanked by two hydrophilic blocks of polyethylene glycol (PEG) having the formula:
wherein “a” is any value in the range 2-130 and “b” is any value in the range 15 and 67. Poloxamers are also known by their trade name SynperonicsTm, Pluronicslm and Kolliphorrm. Because the lengths of the polymer blocks may be customized, many different poloxamers exist having slightly different properties. For the generic term “poloxamer”, these copolymers are commonly named with the letter “P” (for poloxamer) followed by three digits: the first two digits multiplied by IN give the approximate molecular mass of the polyoxypropylene core, and the last digit multiplied by 10 gives the percentage polyoxyethylene content, e.g. P407=poloxamer with a polyoxypropylene molecular mass of 4,000 g/mole and a 70% polyoxyethylene content. For the Pluronic and Synperonic tradenames, coding of these copolymers starts with a letter to define its physical form at room temperature (L=liquid, P=paste, F=flake (solid)) followed by two or three digits, The first digit (two digits in a three-digit number) in the numerical designation, multiplied by 300, indicates the approximate molecular weight of the hydrophobe; and the last digit×10 gives the percentage polyoxyethylene content (e.g., L61 indicates a polyoxypropylene molecular mass of 1,800 g/mol and a 10% polyoxyethylene content). In the example given, poloxamer 181 (P181)=Pluronic L61 and Synperonic PE/L 61. Pluronic F127, also known as poloxamer 407, is a hydrophilic non-ionic surfactant wherein “a” and “b” are approximately block length of 101 and 56, respectively. Pluronic P123 has the same chemical formula as that of Pluronic F127 except that a=20 and b=70. Many commercially available Pluronics including but not limited to are Pluronic P108, Pluronic P103, Pluronic P104, and Pluronic P105.
Multi-walled carbon nanotubes (MWCNT) consist of multiple concentric rolled layers of graphene tubes. There are two models that can be used to describe the structures of MWCNT. In the Russian Doll model, sheets of graphite are arranged in concentric cylinders, for example, a single-walled nanotube within a larger single-walled nanotube. In the Parchment model, a single sheet of graphite is rolled in around itself, resembling a scroll of parchment or a rolled newspaper. The interlayer distance in MWCNT is close to the distance between graphene layers in graphite of approximately 3.4 Å. The Russian Doll structure is observed more commonly.
A first aspect of the invention is directed to a method of preparing MWCNT-ZrO2 nanocomposite. The method comprises preparing a mixture by suspending a zirconium alkoxide and MWCNT in an alcohol containing a templating agent and sonicating. While agitating and heating the mixture, a solution in the range of 1%-10%, preferably 1%-6%, more preferably 1%-4% and most preferably 2%-3% acetic acid in water is added dropwise until a precipitate is formed. The mixture may be heated at a temperature in the range 40-80° C., preferably in the range 50-70° C., and more preferably in the range 55-60° C.
Any zirconium alkoxide may be utilized in the method including but not limited to zirconium methoxide, zirconium ethoxide, zirconium propoxide, zirconium isopropoxide, zirconium butoxide, zirconium isobutoxide, and zirconium t-butoxide. Similarly, any solvent or combination of solvents may be used in the method. In some embodiment, the solvent is miscible with water including but not limited to acetonitrile, dimethyl sulfoxide, dimethyl-formamide, and alcohols with alkyl group having 1-6 carbon atoms. In some more preferred embodiments, the solvent is an alcohol including methanol, ethanol, propanol, isopropanol, butanol, isobutanol, and t-butanol as well as pentanol and hexanol and isomers thereof. In the most preferred embodiment, the alcohol is methanol, ethanol, propanol, and/or isopropanol. In some other preferred embodiments, the alcohol and zirconium alkoxide have the same alkyl group. For example, zirconium isopropoxide and isopropanol are used together.
The precipitate may be separated from the mixture by filtration, decantation, or centrifugation and washed several times with water and low boiling point alcohols such as methanol or ethanol. The resulting powder may be dried in vacuum at a temperature in the range 50-90° C., preferably in the range of 55-75° C., more preferably in the range of 60-70° C. Following the drying, the powder may be calcined at a temperature in the range of 200-700° C., more preferably in the range of 250-600° C., and most preferably in the range of 300-500° C.
A second aspect of the invention is the MWCNT-ZrO2 nanocomposite prepared by the method described herein.
In some embodiments, the MWCNT-ZrO2 nanocomposite contains MWCNT of the invention in the range from 0.1 wt. % to 8.0 wt. %, preferably 0.5 wt. % to 6.0 wt. %, more preferably 1.0 wt. % to 5.0 wt. %, and most preferably 2.0 wt. % to 3 wt. % relative to the total weight of the MWCNT-ZrO2 nanocomposite. In particular preferred embodiment, the MWCNT-ZrO2 nanocomposite contains MWCNT in an amount selected from the group consisting of 1%, 2%, 3%, and 5% relative to the total weight of the MWCNT-ZrO2 nanocomposite.
In some embodiments, the MWCNT-ZrO2nanocomposite of the invention may have a surface area is in the range of 51.0±2 to 65.0±2 m2/g, more preferably the surface area is in the range of 53.0±2 to 60,0±2 m2/g, and most preferably 54.0±2 to 58.0±2 m2/g. In a particular preferred embodiment of the invention, the surface area is 59.2±2 m2/g.
Another preferred embodiment, the MWCNT-ZrO2nanocomposite of the invention is a photocatalyst with a band gap ranging from 3.35 eV to 2.50 eV, preferably ranging from 3.0 eV to 2.60 eV, more preferably ranging from 2.80 eV to 2.60 eV. In particularly preferred embodiment, the MWCNT-ZrO2 nanocomposite has a band gap selected from the group consisting of about 2.81 eV, 2.70 eV, 2.69 eV, and 2.66 eV.
A third aspect of the invention is related to a photochemical method of producing hydrogen gas from water. The method comprises suspending MWCNT-ZrO2 nanocomposite in alcohol aqueous solution to form a composition and irradiating the composition with light source and collecting the evolved hydrogen. The light source may be any light source including, but not limited to a lamp such as tungsten lamp, xenon lamp or fluorescent lamp, or sun light. The method may require dissipating the heat produced by the lamp or the sun. Thus, the method may utilize a cooling system such as circulating water bath and the like or adding ice.
Any water miscible alcohol such as but not limited to methanol, ethanol, propanol, and isopropanol may be used. The amount of alcohol in the aqueous solution may be in the range of 1% to 30% (v/v), preferably in the range of 5% to 20% (v/v), more preferably in the range of 8% to 15% (v/v), most preferably in the range of 9% to 12% (v/v). In a particular preferred embodiment, the amount of alcohol is 10% (v/v). The water used in the method may be treated or untreated sea water, river water, or underground water. It may be filtered to remove solid materials such as sand, clay, and other solids or biological materials.
In a preferred embodiment of the method, the amount of photocatalyst present in the aqueous solution is in the range from 0.5 g/L to 3.0 g/L, more preferably in the range of 1.0 g/L to 2.5 g/L, and most preferably in the range of 1.5 g/L to 2.5 g/L. In a particularly preferred embodiment, the amount of photocatalyst added to the aqueous solution is 2.0 g/L. The photocatalyst is stable and may be recycled as long as it displays catalytic activity of at least 50%, preferably at least 70%, more preferably at least 80%, and most preferably at least 90% of the catalytic activity observed in the first use. In a preferred embodiment, the photo catalyst may be recycled in the range 2 to 10 times, more preferably in the range 3-500, and most preferably in the range 500-10,000.
Any of the MWCNT-ZrO2 nanocomposites of the invention may be utilized in a method to produce hydrogen. In a preferred embodiment of the method, the photocatalyst comprises MWCNT in an amount of 1%, 2%, 3%, 4%, and 5% relative to the total weight of the MWCNT-ZrO2 nanocomposite.
The examples below are intended to further illustrate protocols for the preparation and characteristics of the MWCNT-ZrO2 nanocomposite described above, and are not intended to limit the scope of the claims.
Transmission electron microscopy (TEM) of suspension of nanocomposite in methanol of the nanocomposites was carried out by JEOL-JEM-1230. A Nova 2000 series Chromatech was used to observe the surface area of the composite from N2-adsorption desorption measurements. Crystalline phase of the composites was determined by Bruker axis D8 with Cu Kα radiation (λ=1.540 Å) at room temperature. The band gap was calculated from diffuse reflectance spectra (UV-Vis-DRS). Photoluminescence emission spectra (PL) were recorded on a Shimadzu RF-5301 fluorescence spectrophotometer. Transient photocurrent was recorded by electrochemical workstation, Zahner Zennium, Germany.
Preparation of ZrO2 nanoparticles: Solution A was prepared by dispersing zirconium isopropoxide in isopropyl alcohol and Pluronic F127 for 1 h using ultrasonic cleaner bath. The ratio of zirconium isopropoxide to isopropyl alcohol to Pluronic F127 was kept at 1:10: 0.3. Solution B was prepared by adding 100 ml of deionized water to 2 ml of acetic acid. Solution B was added dropwise to solution A while stirring for 1 h at 333° K until a precipitate is formed. The obtained powder was separated by filtration, washed several times with deionized water and ethanol, and dried under vacuum at 333° K for 10 h. Finally, the powder was calcined for 3 h under nitrogen gas at 573 K.
Preparation of MWCNT-ZrO2 nanocomposites: In a ratio of 1:10:0.3 (w/w/w), zirconium isopropoxide was dispersed in isopropyl alcohol and Pluronic F127 for 1 h using ultrasonic cleaner bath. For 1% preparation, 0.24 g of MWCNTs was added to 100 mL of the dispersion and sonicated for another 3 h to form solution A. Solution B was prepared by adding 100 ml of deionized water to 2 ml of acetic acid. Solution B was added dropwise to solution A while stirring for 1 h at 333° K (30° C.) until a precipitate was formed. The precipitate was separated by filtration, washed several times with deionized water, and ethanol, and dried under vacuum at 333° K (30° C.) for 10 h. Finally, the powder was calcined for 3 h under nitrogen gas at 573° K (60° C.). The same method was used to prepare 2 wt. % MWCNT-ZrO2, 3 wt. % MWCNT-ZrO2, 4 wt. % MWCNT-ZrO2 and 5 wt. % MWCNT-ZrO2 by using the appropriate amount of MWCT.
Hydrogen production application: Hydrogen production experiments were carried out using ZrO2, 1, 2, 3, 4, and 5 wt. % MWCNT-ZrO2 nanocomposites. In a typical experiment, 2 g/L of catalyst was added to 450 mL aqueous solution (10 vol. % methanol). The reaction system was equipped with quartz cooler to dissipate the heat generated by the 500W Xenon lamp. The lamp irradiated the reaction mixture while stirring and the evolved hydrogen produced was quantified by Agilent GC 7890A system. Also, control experiments containing the reaction mixture without the photocatalyst were carried out.
The XRD patterns of MWCNT, ZrO2, and MWCNT-ZrO2 containing 1-5% MWCNT are shown in
The morphology of ZrO2, MWCNT, 1 wt. % MWCNT-ZrO2, 2 wt. % MWCNT-ZrO2, 3 wt. % MWCNT-ZrO2, 4 wt. % MWCNT-ZrO2 and 5 wt. % MWCNT-ZrO2 is examined by TEM.
BET surface area values of ZrO2, MWCNT, 1 wt. % MWCNT-ZrO2, 2 wt. % MWCNT-ZrO2, 3 wt. % MWCNT-ZrO2, 4 wt. % MWCNT-ZrO2 and 5 wt. % MWCNT-ZrO2 samples are shown in Table 1. The increase of the amount of MWCNT from 0 to 3 wt. % improves the BET surface area of ZrO2 from 50 m2/g to 59.2 m2/g. Above 3 wt. %, increasing MWCNT has no significant effect on BET surface area.
Photoluminescence emission spectra (PL) of ZrO2 and 1-5 wt % MWCNT-ZrO2 nanocomposites (
Transient photocurrent responses of ZrO2 and 3 wt % MWCNT-ZrO2 photocatalyst are shown in
Recycling and reuse of 3 wt. % MWCNT-ZrO2 photocatalyst on amount of hydrogen evaluation is examined using 2.0 g/L of 3 wt. % MWCNT-ZrO2 photocatalyst in 450 mL aqueous solution irradiated with 500W xenon lamp 9 h.
The present disclosure describes a method for the synthesis of ZrO2 nanoparticles and MWCNT-ZrO2 nanocomposites in the presence of a poloxamer template at room temperature. The photocatalytic activity of 3 wt. % MWCNT-ZrO2 nanocomposites is significantly better photocatalyst than ZrO2, 1 wt. % MWCNT-ZrO2, 2 wt. % MWCNT-ZrO2, 4 wt. % MWCNT-ZrO2 and 5 wt. % MWCNT-ZrO2 for hydrogen production by 64.1, 3.2, 1.6, 1.2 and 1.1 times, respectively. The photocatalyst 3 wt. % MWCNT-ZrO2 displays photocatalytic stability and can be recycled in a method for the production of hydrogen from water.