11725182
The demand for biologically produced and degradable plastics, bioplastics, has increased in recent years due to increasing public concern about the environment, climate change, and limited fossil fuel resources. Although the raw materials for bioplastics, biopolymers, are commercially produced, these biopolymers are not competitive against petroleum-based polymers economically due to their high cost of production and purification. As the result, the use of bioplastics in the market is limited. An example of the limitation can be found in Mardi Gras beads, those plastic necklaces thrown during the annual Carnival celebration in Louisiana and elsewhere. It is a tradition in Louisiana that riders of Mardi Gras parades (krewes) throw the beads to people in the streets. Although Mardi Gras beads are historically made of glass, recent Mardi Gras beads are made of petroleum-based polyethylene or polystyrene, known as mold-on-thread (MOT) beads in the industry. An analysis estimates that about 11 million tons of plastic ornaments, including MOT, are imported to New Orleans, the largest city in Louisiana, each year for the celebration, but many of them end up in landfills. Local organizations encourage recycling the beads and throwing eco-friendly beads (i.e., paper beads) to conserve resources while preserving the tradition. However, the impact of the efforts has been limited. Because people in the streets seek krewes to throw many beads and the budgets of the krewes are limited, so inexpensive Mardi Gras beads are widely used.
Mardi Gras beads are a big industry in Louisiana with over 25 million pounds of beads imported each year, bringing in about $12 million in sales annually. Mardi Gras beads contribute to the roughly 150 tons of waste produced from Mardi Gras each year. Beads pose environmental and health hazards since they contain lead. The majority of lead in the soil found in various parts of New Orleans was discovered to be located directly alongside the Mardi Gras parade routes, which translates to about 4,000 pounds of lead hitting the streets. The demand for affordable, biologically produced and degradable Mari Gras beads, such as bioplastic Mardi Gras beads, has increased in recent years due to increasing public concern about the environment, health, and limited fossil fuel resources. An example is that of Zombeads, a private company, which has created beads with recycled paper.
Various methods of manufacturing Mardi Gras beads have been investigated in the past. From the 1970s until now, there have been about 50 styles of machine-styled beads, including plastic and polystone medallions beads, and current trends such as lighted beads. Generally speaking, the bead making process takes 90 to 100 days and is very labor intensive. First, a plastic mold is manufactured. During the machine-tooled process, plastic is injected into the mold, forming the bead. From there, it is sent to the metallizer, where color is added. An employee then pulls the bead string out, which can be as long as half a mile, and cuts it to the appropriate size. In the next step, the two ends of the bead are fused together and any extra items, such as a medallion, are added. The beads are then hand-stapled into groups and bagged. From there, they are loaded into containers and shipped to the United States, with shipping taking 21 to 24 days.
Further aspects of the present disclosure will be more readily appreciated upon review of the detailed description of its various embodiments, described below, when taken in conjunction with the accompanying drawings.
Before the present disclosure is described in greater detail, it is to be understood that this disclosure is not limited to particular embodiments described, and as such may, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular embodiments only, and is not intended to be limiting, since the scope of the present disclosure will be limited only by the appended claims.
Where a range of values is provided, it is understood that each intervening value, to the tenth of the unit of the lower limit unless the context clearly dictates otherwise, between the upper and lower limit of that range and any other stated or intervening value in that stated range, is encompassed within the disclosure. The upper and lower limits of these smaller ranges may independently be included in the smaller ranges and are also encompassed within the disclosure, subject to any specifically excluded limit in the stated range. Where the stated range includes one or both of the limits, ranges excluding either or both of those included limits are also included in the disclosure.
Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. Although any methods and materials similar or equivalent to those described herein can also be used in the practice or testing of the present disclosure, the preferred methods and materials are now described.
All publications and patents that are specifically incorporated by reference herein, are incorporated by reference to disclose and describe the methods and/or materials in connection with which the publications are cited. The citation of any publication is for its disclosure prior to the filing date and should not be construed as an admission that the present disclosure is not entitled to antedate such publication by virtue of prior disclosure. Further, the dates of publication provided could be different from the actual publication dates that may need to be independently confirmed.
As will be apparent to those of skill in the art upon reading this disclosure, each of the individual embodiments described and illustrated herein has discrete components and features which may be readily separated from or combined with the features of any of the other several embodiments without departing from the scope or spirit of the present disclosure. Any recited method can be carried out in the order of events recited or in any other order that is logically possible.
Embodiments of the present disclosure will employ, unless otherwise indicated, techniques of chemistry, microbiology, material science, and the like, which are within the skill of the art.
The following examples are put forth so as to provide those of ordinary skill in the art with a complete disclosure and description of how to perform the methods and use the materials disclosed and claimed herein. Efforts have been made to ensure accuracy with respect to numbers (e.g., amounts, temperature, etc.), but some errors and deviations should be accounted for, Unless indicated otherwise, parts are parts by weight, temperature is in ° C., and pressure is at or near atmospheric. Standard temperature and pressure are defined as 20° C. and 1 atmosphere.
Before the embodiments of the present disclosure are described in detail, it is to be understood that, unless otherwise indicated, the present disclosure is not limited to particular materials, reagents, reaction materials, manufacturing processes, or the like, as such can vary. It is also to be understood that the terminology used herein is for purposes of describing particular embodiments only, and is not intended to be limiting. It is also possible in the present disclosure that steps can be executed in different sequence where this is logically possible.
It must be noted that, as used in the specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise.
As used herein, “triacylglycerol-accumulated Chlamydomonas” refers to Chlamydomonas that has been modified to produce increased triacylglycerol (TAG) through stress conditions, e.g. through centrifugation, nitrogen depletion, iron deficiency, high salinity, high temperature and the like. A triacylglycerol-accumulating microalgae (such as, but not limited to a triacylglycerol-accumulating Chlamydomonas) is a species of microalgae that will produce increased triacylglycerol (TAG) through stress conditions, as compared to the amount of TAG produced by the species of microalgae in normal (e.g., non-stress) conditions.
In accordance with the purpose(s) of the present disclosure, as embodied and broadly described herein, embodiments of the present disclosure, in some aspects, relate to bioplastics made from triacylglycerol-accumulated microalgae, methods for making triacylglycerol-accumulated microalgae, methods for making bioplastics from triacylglycerol-accumulated microalgae, methods for making alga-mixed plastics, and products including these bioplastics. As discussed above, the accumulation of plastics, such as the millions of pounds of Mardi Gras Beads produced each year, poses a plethora of environmental problems. Biodegradable plastics offer a possible alternative, but such plastics are not yet widespread due to cost of production and various drawbacks.
Biologically produced and degradable plastics can be based on bio-compounds such as starch, cellulose, protein, aliphatic polyesters. Triacylglycerol (TAG) is an esterified molecule derived from a glycerol and three fatty acids and can also provide a raw material for the production of bioplastics [7, 8]. Studies in chemical engineering show that TAG can be plasticized by crosslinking the molecule through the coupling of the free radicals that are formed from the decomposition of hydroperoxide. These bio-compounds are typically extracted and purified from plants or bacteria.
Algae offers an avenue for bioplastic production due to their high biomass yield, ability to be cultivated in a natural environment, reduced production cost and reduced impact on the food chain, unlike with plant-based bioplastics [34, 35]. It is technically feasible to incorporate dried algae refined to a small particle size (<150 μm) and added whole to thermoplastic blend formulations [36]. Various compositions of different algae species have been investigated for use as a bioplastic or thermoplastic as each species have different properties that may impact their effectiveness as a bioplastic. The enormous diversity in the algal lineages is due to their long evolutionary history. As a result, microalgae exhibit wide variation in both cellular architecture and biosynthetic capacity, and thus present the potential for a broad array of applications [37]. Adding synthetic polymers such as polyethylene to bioplastic compositions have also been investigated as an avenue to improve mechanical performance.
Zeller et al. [38], investigated bioplastics and thermoplastic blends made solely from Spirulina and Chlorella microalgae and the influence of blending with polyethylene on mechanical performance of Spirulina and Chlorella based thermoplastic blends.
Wang et al. (2016) investigated the protein modification of catfish algae (planktonic algae) and Nannochloropsis (microalgae) and also investigated the influence of various factors such as types of algae, scavenger materials (adsorbents), synthetic resin, and compatibilizer on the odor of plastics.
U.S. Pat. No. 8,524,811 (herein incorporated by reference) discloses a thermoplastic composition comprising Nannochloropsis, Spirulina, Chlorella, or a combination thereof mixed with a plant polymer. The disclosure teaches melting a microalgae powder composition consisting of Nannochloropsis, Spirulina, Chlorella, or a combination thereof; a plasticizer, and a plant polymer and extruding at about 80 Celsius degree to 190 Celsius degree under conditions of melt pressure 5-20 bar and torque 40-80%.
Additionally, various methods of producing algae based bioplastics or thermoplastics have been investigated. Wang [36] teaches the preparation of algae bioplastic composed of catfish algae (planktonic algae) and Nannochloropsis (microalgae) through thermomechanical compression molding using a benchtop press with electrically heated and water-cooled platens for a 20 min. cook time at +/−150° C., followed by 10 min. cooling period, and both performed under pressure greater than 24,000 Pa.
TAG production in microalgae has been also studied for industrial use because microalgae are capable of producing TAG efficiently [9]. Among the microalgae, Chlamydomonas reinhardtii has been studied as a model organism [10]. The studies on Chlamydomonas found that it produces TAG when it is in stress environments, such as nitrogen depletion [11], iron deficiency [12], high salinity [11], and high temperature [13].
Nevertheless, many challenges remain in the art before algae based bioplastics can be produced at commercially viable scale due to a high cost of the production and purification [37]. One of the solutions to reduce the production cost of the bioplastics is to mold crude bioplastics, a whole biomass accumulating the biopolymers, A study shows that a biomass of bacteria accumulating PHA (polyhydroxyalkanoate), the aliphatic polyester, can be molded without the extraction and purification of PHA [6].
Due to a lack of economic competitiveness of biologically produced polymers against the petroleum-based polymers, the Mardi Gras beads made of biopolymers are not yet commercially available, even if locals favor the conservation of resources. One of the solutions to reduce the production cost of the bioplastics is to mold crude bioplastics via a whole biomass accumulating the biopolymers without the need for extraction and purification. A study [6] shows that a biomass of bacteria accumulating polyhydroxyalkanoate (PHA), the biopolymer, can be molded without the extraction and purification of PHA.
Triacylglycerol (TAG) is an esterified molecule derived from a glycerol and three fatty acids and can be a raw material for the bioplastics. The studies in chemical engineering show that TAG can be plasticized by crosslinking the molecule through the coupling of the free radicals that are formed from the decomposition of hydroperoxide. TAG production in microalgae has been widely studied for industrial use because microalgae are capable of producing TAG efficiently [9]. Among the microalgae, Chlamydomonas reinhardtii has been studied as a model organism. The studies on Chlamydomonas found that it produces TAG when it is in stressful environments, such as nitrogen depletion, iron deficiency, high salinity, and high temperature. The present disclosure demonstrates that microalgae accumulating TAG will be an economically sustainable crude bioplastic because they can produce not only bioplastic materials but also commercially valuable carotenoids, By sequentially producing carotenoids and crude-bioplastics from the same microalgal culture, a cost of the bioplastic production can be reduced.
In general, embodiments of the present disclosure provide for methods of producing triacylglycerol-accumulated microalgae, methods for making bioplastics from triacylglycerol-accumulated microalgae, methods for making alga-mixed plastics, and products including these bioplastics.
The present disclosure includes a bioplastic mass including triacylglycerol-accumulated Chlamydomonas. Advantageously, the bioplastic mass is renewable and biodegradable, with low production costs, low impact on the food chain, and high yield.
Embodiments of the present disclosure include a bioplastic mass as above, wherein the bioplastic mass does not contain thermoplastics. The bioplastic mass can be an algae biomass molded without other thermoplastic materials.
Embodiments of the present disclosure include a bioplastic mass as above, wherein the triacylglycerol-accumulated Chlamydomonas is crosslinked.
Embodiments of the present disclosure include a bioplastic mass as above, further comprising Chlorella, wherein the triacylglycerol-accumulated Chlamydomonas is crosslinked with the Chlorella.
Embodiments of the present disclosure include a bioplastic mass as above, wherein the crosslinking is performed under heated conditions of about 120° C.
Embodiments of the present disclosure include a bioplastic mass as above, further including at least one additive to strengthen the bioplastic. In embodiments, the additive is an oxidizer (such as, but not limited to ammonium persulfate, hydrogen peroxide, Sodium persulfate). In other embodiments, the additive is a plasticizer (such as, but not limited to polyethylene, glycerol).
Embodiments of the present disclosure include a bioplastic mass as above, wherein the triacylglycerol-accumulated Chlamydomonas is produced by centrifugation.
The present disclosure includes methods for making bioplastics including culturing one or more genus of microalgae, wherein at least one of the genera is a triacylglycerol-accumulating microalgae; centrifuging the microalgae during the stationary phase to induce polymer compound accumulation; extracting precipitate (also referred to as biomass or algal biomass) formed during centrifugation; incubating and dehydrating the precipitate; grinding the precipitate to form a powder and mixing with water to form a mixture; and adding at least one additive to form the bioplastic, wherein the additive is selected from an oxidizer, a plasticizer, and a combination thereof.
Embodiments of the present disclosure include a method as above, wherein the triacylglycerol-accumulating microalgae includes Chlamydomonas. In other embodiments, the microalgae can include diatom species, Nannochloris, and Botryococcus.
Embodiments of the present disclosure include a method as above, wherein the microalgae further comprises Chlorella.
Embodiments of the present disclosure include a method as above, wherein when the microalgae is Chlamydomonas reinhardtii, the accumulated polymer is triacylglycerol, and when the microalgae is Chlorella vulgaris, the accumulated polymer is selected from starch, triglyceride, cellulose, proteins, and a combination thereof.
Embodiments of the present disclosure include a method as above, wherein the additive is selected from ammonium persulfate, glycerol, and a combination thereof.
Embodiments of the present disclosure include a method as above, wherein the additive is from about 5% w/dw to about 15% w/dw, or about 10% w/dw of the biomass (e.g. the precipitate).
Embodiments of the present disclosure include a method as above, wherein the method further comprises eluting carotenoids from supernatant generated during the centrifugation. Advantageously, the method sequentially produces carotenoids, commercially valuable bioactive-compounds, and bioplastics from the same microalgal culture. The carotenoids can be isolated from an algae, and the leftover algae biomass molded into a bioplastic without mixing thermoplastics (see
The present disclosure includes a method for making bioplastics including culturing one or more genus of microalgae, wherein at least one of the genera is a triacylglycerol-accumulating microalgae; centrifuging the microalgae during the stationary phase to induce polymer compound accumulation; extracting precipitate formed during centrifugation; incubating and dehydrating the precipitate; grinding the precipitate to form a powder and mixing with water to form a mixture; adding at least one additive to the mixture to form the bioplastic, wherein the additive can be an oxidizer, a plasticizer, or a combination thereof; heating the mixture to about 120° C.; and molding the mixture into a shape.
Embodiments of the present disclosure include a method as above, wherein the microalgae comprises Chlamydomonas and optionally includes Chlorella.
Embodiments of the present disclosure include a method as above, wherein when the microalgae is Chlamydomonas reinhardtii, the accumulated polymer is triacylglycerol, and when the microalgae is Chlorella vulgaris, the accumulated polymer is selected from starch, triglyceride; cellulose, proteins, and a combination thereof.
Embodiments of the present disclosure include a method as above, wherein the additive is selected from ammonium persulfate, glycerol, and a combination thereof.
Embodiments of the present disclosure include a method as above, wherein the additive is from about 5% w/dw to about 15% w/dw of the biomass.
Embodiments of the present disclosure include a method as above, wherein the method further comprises eluting carotenoids from supernatant generated during the centrifugation. Advantageously, the method sequentially produces carotenoids, commercially valuable bioactive-compounds, and bioplastics from the same microalgal culture.
The present disclosure includes a bioplastic mass formed by the steps of: culturing one or more genus of microalgae; wherein at least one of the genera is a triacylglycerol-accumulating microalgae; centrifuging the microalgae during the stationary phase to induce polymer compound accumulation; extracting compounds from precipitate formed during centrifugation; incubating and dehydrating the precipitate; grinding the precipitate to form a powder and mixing with water to form a mixture; and adding at least one additive to form the bioplastic, wherein the additive is selected from an oxidizer, a plasticizer, and a combination thereof.
Embodiments of the present disclosure include a method as above, further formed by the additional steps of: heating the mixture to about 120° C.; and molding the mixture into a shape.
Embodiments of the present disclosure include a method as above, wherein the microalgae comprises Chlamydomonas and optionally includes Chlorella.
Embodiments of the present disclosure include a method as above, wherein when the microalgae is Chlamydomonas reinhardtii, the accumulated polymer is triacylglycerol, and when the microalgae is Chlorella vulgaris, the accumulated polymer is selected from starch, triglyceride, cellulose, proteins, and a combination thereof.
Embodiments of the present disclosure include a method as above, wherein the additive is selected from ammonium persulfate, glycerol, and a combination thereof.
Embodiments of the present disclosure include a method as above, wherein the additive is from about 5% w/dw to about 15% w/dw of the biomass.
The present disclosure includes an algae mixed plastic comprising triacylglycerol-accumulated microalgae and polyethylene.
Embodiments of the present disclosure include a method as above, wherein the triacylglycerol-accumulated microalgae is Chlamydomonas.
Embodiments of the present disclosure include a method as above, further comprising Chlorella.
Embodiments of the present disclosure include a method as above, further comprising an additive selected from ammonium persulfate, glycerol, and a combination thereof.
Embodiments of the present disclosure include a method as above, wherein the triacylglycerol-accumulated Chlamydomonas is produced by centrifugation.
Embodiments of the present disclosure include a method as above, comprising: selecting and culturing a species of microalgae capable of triacylglycerol accumulation from centrifugation; centrifuging the cultured microalgae during the stationary phase of growth; extracting compounds from precipitate formed during centrifugation; and incubating the precipitate, resulting in triacylglycerol-accumulated microalgae.
Embodiments of the present disclosure include a method as above, wherein the cultured species of microalgae is from the genus Chlamydomonas.
Embodiments of the present disclosure include a method as above, wherein the amount of triacylglycerol accumulated in the microalgae after incubation is from about 200% to about 400% higher than triacylglycerol accumulation produced by microalgae subjected to stress conditions other than centrifugation.
Embodiments of the present disclosure include a method as above, wherein the microalgae contains less C18 fatty acid methyl esters than in a comparable sample produced by nitrogen depletion.
Now having described the embodiments of the disclosure, in general, the examples describe some additional embodiments. While embodiments of the present disclosure are described in connection with the example and the corresponding text and figures, there is no intent to limit embodiments of the disclosure to these descriptions. On the contrary, the intent is to cover all alternatives, modifications, and equivalents included within the spirit and scope of embodiments of the present disclosure.
The demand for bioplastics has increased in recent years, yet their application in industries has been limited. One of the reasons is the high cost of producing and purifying biopolymers, the raw materials for the bioplastics. The present disclosure demonstrates that Chlamydomonas reinhardtii, a model microalga, produces increased amounts of the biopolymer triacylglycerol (TAG) when the cells are left overnight after centrifugation. The centrifuged cells produce triacylglycerol about 3-fold higher than those cultured in a nitrogen depletion condition in the first 24 hours. The chloroplast membranes of the centrifuged cells are largely disrupted. In addition, the accumulated triacylglycerol rarely contains C18:1 (11) and C18:3 (5,9,12) fatty acids that are normally found in triacylglycerol in the cells cultured in the nitrogen depletion condition. Advantageously, different triacylglycerols can be produced using the centrifugation methods described herein than can be produced using nitrogen depletion without genetic modification. These suggest that the centrifuged cells produce triacylglycerol differently from those cultured in the nitrogen depletion condition. It was also found that the centrifuged cells, the biomass, can be molded to a bead that cracks at 1.7 MPa. The methods developed in this study provide methods to produce economically viable disposable-bioplastics.
During a time-course experiment, when the centrifuged biomass was accidentally left on a laboratory bench overnight, it was unexpectedly found that Chlamydomonas produces TAG. During the characterization of the mechanism of the centrifugation-induced TAG production, the Chlamydomonas accumulating TAG was also investigated as a material for production of crude bioplastics, uses of which could include the economically sustainable production of biodegradable Mardi Gras beads and other biodegradable plastic items. The present disclosure provides methods for producing the centrifugation-induced TAG production and its application provide methods for sustainable and cost-effective production of crude bioplastics.
Materials and Methods
Chlamydomonas Strains and Culture Conditions
Chlamydomonas reinhardtii strain D66 was obtained from Dr. James Moroney at Louisiana State University. Strains CC-124, 17, and BAFJ5, were obtained from the Chlamydomonas Resource Center. Chlorella vulgaris was obtained from Culture Collection of Autotrophic Organisms in Czech Republic (Stock #: CCALA 924). Chlamydomonas strains and Chlorella strain were cultured in 250 mL flasks containing 100 mL TAP, Tris-acetate-phosphate, medium (Gorman & Levine [15], 1965) and BBM medium (Bold [16], 1949), (both incorporated herein by reference). The cultures were kept at 23±2° C. under fluorescence light (60 μmol/m2/s) and constantly shaken on an orbital shaker at 180 rpm. Every 7 days, 100 μl of the culture solution was transferred to a freshly prepared 100 ml medium. When Chlamydomonas or Chlorella was subjected to centrifugation-induced TAG productions, 10 ml of the 7 days old culture was collected in a 15 ml conical screw cap centrifuge tube (USA Scientific, CAT #1475-0511). The tube was centrifuged at 4,000 g for 5 min. The tube with the cap was left on a laboratory bench at room temperature after supernatant was decanted and remained precipitate. When Chlamydomonas was subjected to nitrogen or nutrient starvation, the cells in the 7 days old culture were transferred to a 250 mL flask containing 100 mL TAP-N medium (nitrogen resources were removed from the TAP medium) or 100 ml of water, respectively. When Chlamydomonas was subjected to oxygen deficiency, Chlamydomonas was first cultured in 100 ml of TAP medium for 7 days. One third of the cells were then transferred to a 250 mL flask containing 30 ml of TAP medium. The culture was bubbled with compressed nitrogen (UN1066) to purge oxygen from the medium.
Counting Cell Numbers
The number of cells in cultures was counted using a hemocytometer (Hausser Scientific Partnership) after the cells were immobilized with 150 mM of potassium chloride.
Lipid Extraction
The previously published method was followed (Kato et al., 2013 [14], incorporated herein by reference). Briefly, Chlamydomonas cells in the 10 ml culture were re-suspended in a solution containing 1 mL of 50 mM dipotassium phosphate, 2 mL of methanol and 1 mL of chloroform and vortexed. The organic phase was transferred into a 2 mL microcentrifuge tube, and the organic solvent was evaporated.
Carotenoids Extraction
Chlamydomonas cells in the 10 ml culture were re-suspended in 2 ml diethyl ether, the solvent. The resulting mixture was vortexed and centrifuged at 4,800 g for 2-3 min. The supernatant was then collected. The extraction was repeated 3 times. The supernatants from each extract were collected in a 15 ml conical tube and heating it at 70° C. to evaporate the solvent.
Thin Layer Chromatograph (TLC) Analysis
The previously published method was followed for triacylglycerol analysis [14]. Briefly, the extracted lipids were analyzed on a 250 μm layer silica plate (Whatman) in a TLC tank that consisted of 220 mL hexane, 80 mL diethyl ether and 1 mL glacial acetic acid. Triacylglycerols were visualized by charring the plate with 1 N sulfuric acid, Amounts of triacylglycerols in samples were calculated by scanning the charred plate through a scanner (EPSON 4180 PHOTO) and quantifying intensities of spots through FIJI imaging software. Spots of triolein (Sigma-Aldrich) where 5 μg, 10 μg, and 25 μg were applied, respectively, were used to generate a standard curve. When carotenoids were analyzed, the extracted carotenoids were dissolved in diethyl ether and spotted on a 250 μm layer silica plate (Mikami & Hosokawa [17], incorporated herein by reference). The plate was then developed in a TLC tank that consisted of 210 ml petroleum ether and 90 ml acetone. Lutein (CVS pharmacy) was used as a standard.
Transmission Electron Microscopy Analysis
The previously published method was followed [14]. Briefly, 1 mL aliquot of culture was transferred to 1.5 mL microcentrifuge tubes (USA Scientific). The tubes were centrifuged to harvest the cells and the cells were fixed, sliced and imaged.
Fatty Acid Methyl Esters (FAME) Analysis
Triacylglycerol spots in a TLC plate were scraped and eluted with hexane. The FAMEs were prepared and analyzed by gas chromatography-flame ionization detector (GC-FID) as described in Siaut et al. [11] (herein incorporated by reference).
Algal Bead Molding
Chlamydomonas and Chlorella were cultured in 2 L flasks containing 1 L culture medium, TAP and BBM, respectively. The cultures were kept at 23±2° C. under fluorescence light (60 μmol/m2/s) and constantly shaken on an orbital shaker at 180 rpm. The culture was centrifuged in 4×250 ml centrifuge bottles (Nalgene) at 4,000 g for 5 min. The bottles with the cap were left on a laboratory bench at room temperature after the supernatant was decanted. The biomass (0.1 g each) of Chlamydomonas and Chlorella were mixed on a microscope slide (Corning 294875X25) and 10% (weight/dry weight biomass) of ammonium persulfate or glycerol was mixed. The biomass was autoclaved at 121° C. for 20 min. The biomass was then molded into beads manually. The beads were left at room temperature overnight.
Compressive Strength Test on Beads
Compressive strength test was conducted with Material Testing System Model 810 (MTS Systems Corporation). The vertical compression load was applied to each bead with a compression rate at 0.02 mm/sec. The applied force in megapascal (MPa) was continually monitored with the TestWare-SX software.
A Protocol of Centrifugation-Induced Triacylglycerol Production was Established
During a time course experiment for Chlamydomonas triacylglycerol (TAG) production [14], it was unexpectedly found that Chlamydomonas accumulated TAG when a centrifuged biomass was accidentally left in a tube overnight at room temperature. Based on the finding, a protocol was established in which 10 ml of 7 days old culture was subjected to centrifugation-induced TAG production (
Triacylglycerol Production is Induced by Centrifugation but not by Lack of Nutrients or Oxygen
The amount of TAG accumulated in Chlamydomonas subjected to the centrifugation-induced TAG production was compared to the amount of TAG accumulated in Chlamydomonas subjected to nitrogen starvation, which is known to induce the TAG production in Chlamydomonas [11] (
It was initially believed that Chlamydomonas accumulates TAG after centrifugation due to environmental stress, namely lacking nutrients and/or oxygen as previously reported in microalgae [18, 19] and a plant [20], respectively. However, in the above experiment in which Chlamydomonas was subjected to total limitation of nutrients (water culture) and oxygen limitation (nitrogen purge) for 24 h showed little production of TAG. This result suggests that limitation of nutrients or oxygen, alone, does not produce TAG efficiently in Chlamydomonas.
Centrifugation Induces Triacylglycerol Production in Chlamydomonas Strains but not in a Chlorella Strain
The Chlamydomonas strain originally used for the centrifugation-induced TAG production was a mutant strain, D66, that lacks cell wall [14]. To investigate the effect of Chlamydomonas mutations in the centrifugation-induced TAG production, several different mutant strains were analyzed, namely 17 and BAFJ5, which lack production of starch [11], as well as CC-124, which lacks unknown-functional protein AGG1 [21]. Analysis of Chlorella vulgaris [22] was also performed to understand whether the centrifugation-induced TAG production is commonly observed in the Chlorophyta taxonomic division. Our TLC analysis using samples 24 h after centrifugation revealed that all Chlamydomonas mutant strains produce a similar amount of TAG while C. vulgaris does not produce TAG (
A previous report indicates that applying 10-15 bar pressure for 2 h on C. vulgaris induces TAG production [23]. This suggests that centrifugation does not provide the pressure stress on the cells. On the other hand, another previous report indicates that compressive distortion of a single Chlamydomonas cell by a microfluid device induces TAG production [24]. This suggests that cells may not perceive all stresses similarly to induce TAG production. Further study may elucidate how Chlorophyta organisms (i.e., Chlamydomonas and Chlorella) perceive pressure and compressive stresses differently.
Centrifugation Induces the Triacylglycerol Production within 6 h while it does not Alternate the Carotenoid Production
To investigate the kinetics of the TAG production after centrifugation, a time-course experiment was conducted in which samples were collected at certain time points within 48 h after centrifugation (
Because a previous study indicated that carotenoid production has a negative correlation with the TAG production in microalgae [25], changes in carotenoid production in Chlamydomonas subjected to the centrifugation-induced TAG production were investigated. TLC analysis found that the carotenoid production, which can be identified as yellow spots on the TCL plate [17], are not changed qualitatively during centrifugation-induced TAG production (
This suggests that centrifugation does not affect carotenoid synthetic pathway while it upregulates the TAG synthetic pathway. From an applied science point of view, this also suggests that co-productions of lutein, which is a commercially valuable compound, in Chlamydomonas [26, 27] and TAG would be possible with centrifugation.
Centrifugation-Induced Triacylglycerol Production Disrupts the Chloroplast Membranes
Chlamydomonas gradually accumulates TAG in the lipid droplets, organelles composed of a single layer of phospholipid, for 5 to 7 days when it is exposed to a nitrogen-depletion condition [28], To investigate the localization where rapidly produced TAG is accumulated by the centrifugation, transmission electron microscopy was conducted (
Triacylglycerol Produced by Centrifugation Contains Trivial Amounts of C18:1 (11) and C18:3 (5,9,12) Fatty Acids
Rapid accumulation of TAG and disruption of the chloroplast membranes are prominent differences between centrifuged and nitrogen-depleted Chlamydomonas (
Together with the result from transmission electron microscopy (
Moreover, the FAME analysis revealed TAGs synthesized by centrifugation contain more saturated fatty acids than that synthesized in stress conditions (
Centrifuged Chlamydomonas Biomass can Form Crude Bioplastics
The present disclosure provides a protocol that allows formation of molded beads directly from the Chlamydomonas biomass accumulating TAG (
For the proof-of-concept, 1 L culture of Chlamydomonas D66 was used. A mixed 1 L culture of the Chlorella vulgaris was also used that was subjected to centrifugation-induced TAG production. As found in the experiment (
Algal Beads Maintain Strength
The appearance and physical strength of the molded beads (algal beads), were compared to petroleum-based Mardi Gras beads thrown by a krewe during a Mardi Gras parade in Louisiana (
The same test with the petroleum-based Mardi Gras bead revealed the cracking point is 12.08 MPa (24.7% strain). These suggest that the strength of the algal bead is about 14% of that made from the petroleum and similar to mud bricks that are used for non-industrial constructions [32]. This indicates that the algal beads maintain certain physical strengths when they are molded with ammonium persulfate. When the algal bead is molded with 10% (w/d·w. biomass) of glycerol, the stress and strain are linearly correlated, but the slope is much lower than that with ammonium persulfate. This indicates that the bead is elastic and suggests that adding a different additive in the biomass could change the physical characteristics of the final products.
Although the algal beads generated in this study may not be strong enough for industrial use, they may be sufficient for use in applications such as MOT beads and other uses with further research development. As shown in this study, microalgae produce both commercially valuable carotenoids (
It was also found that the algaplastics can be mixed with polyethylene, a conventional plastic, to produce alga-mixed plastics (
A method that turns microalgal cultures into bioplastics is disclosed. The method includes 1) a selection of microalgal strains, 2) a procedure to make the microalgae convert the cellular components into bioplastic materials (algaplastics), and 3) a chemical reaction to alternate the physical character of the algaplastics. Microalgal strains that are suitable for algaplastic production were identified.
Microalgae, Chlorella vulgaris and Chlamydomonas reinhardtii, were cultured in water containing nutrients necessary for their growth (
Various aspects of the present disclosure are described below in the following clauses.
Clause 1. A bioplastic mass comprising triacylglycerol-accumulated Chlamydomonas.
Clause 2. The bioplastic mass of clause 1, wherein the triacylglycerol-accumulated Chlamydomonas is crosslinked.
Clause 3, The bioplastic mass of clause 2, further comprising Chlorella, wherein the triacylglycerol-accumulated Chlamydomonas is crosslinked with Chlorella.
Clause 4. The bioplastic mass of any one of the preceding clauses, wherein the crosslinking is performed under heated conditions of about 120° C.
Clause 5. The bioplastic mass of any one of the preceding clauses, further comprising an additive.
Clause 6. The bioplastic mass of clause 5, wherein the additive is selected from ammonium persulfate, hydrogen peroxide, sodium persulfate, polyethylene, glycerol, and a combination thereof.
Clause 7. The bioplastic mass of any one of the preceding clauses, wherein the triacylglycerol-accumulated Chlamydomonas is produced by centrifugation.
Clause 8. A method for making bioplastics comprising:
culturing one or more genus of microalgae, wherein at least one of the genera is a triacylglycerol-accumulating microalgae;
centrifuging the microalgae during the stationary phase to induce polymer compound accumulation;
extracting compounds from precipitate formed during centrifugation;
incubating and dehydrating the precipitate;
grinding the precipitate to form a powder and mixing with water to form a mixture; and
adding at least one additive to form the bioplastic, wherein the additive is selected from an oxidizer, a plasticizer, and a combination thereof.
Clause 9. The method of clause 8, wherein the microalgae comprises Chlamydomonas.
Clause 10. The method of clause 9, wherein the microalgae further comprises Chlorella.
Clause 11. The method of clause 10, wherein triacylglycerol-accumulating microalgae is Chlamydomonas reinhardtii, and the Chlorella is Chlorella vulgaris;
and wherein the accumulated polymer produced by Chlorella vulgaris is selected from starch, triglyceride, cellulose, proteins, and a combination thereof.
Clause 12. The method of clause 8, wherein the additive is selected from ammonium persulfate, hydrogen peroxide, sodium persulfate, polyethylene, glycerol, and a combination thereof.
Clause 13. The method of clause 8, wherein the additive is from about 5% w/dw to about 15% w/dw of the biomass.
Clause 14. The method of clause 8, wherein the method further comprises eluting carotenoids from supernatant generated during the centrifugation.
Clause 15. A method for making bioplastics comprising:
culturing one or more genus of microalgae, wherein at least one of the genera is a triacylglycerol-accumulating microalgae;
centrifuging the microalgae during the stationary phase to induce polymer compound accumulation;
extracting precipitate formed during centrifugation;
incubating and dehydrating the precipitate;
grinding the precipitate to form a powder and mixing with water to form a mixture;
adding at least one additive to the mixture to form the bioplastic.
heating the mixture to about 120° C.; and
molding the mixture into a shape.
Clause 16. The method of clause 15, wherein the microalgae comprises Chlamydomonas and optionally includes Chlorella.
Clause 17. The method of clause 16, wherein when the microalgae comprises Chlamydomonas reinhardtii, and optionally includes Chlorella vulgaris;
wherein the accumulated polymer from Chlamydomonas reinhardtii is triacylglycerol, and
wherein the accumulated polymer from Chlorella vulgaris is selected from starch, triglyceride, cellulose, proteins, and a combination thereof.
Clause 18. The method of clause 15, wherein the additive is selected from ammonium persulfate, hydrogen peroxide, sodium persulfate, polyethylene, glycerol, and a combination thereof.
Clause 19. The method of clause 15, wherein the additive is from about 5% w/dw to about 15% w/dw of the biomass.
Clause 20. The method of clause 15, wherein the method further comprises eluting carotenoids from supernatant generated during the centrifugation.
Clause 21. A bioplastic mass formed by the steps of:
culturing one or more genus of microalgae, wherein at least one of the genera is a triacylglycerol-accumulating microalgae;
centrifuging the microalgae during the stationary phase to induce polymer compound accumulation;
extracting compounds from precipitate formed during centrifugation;
incubating and dehydrating the precipitate;
grinding the precipitate to form a powder and mixing with water to form a mixture; and
adding at least one additive to form the bioplastic, wherein the additive is selected from an oxidizer, a plasticizer, and a combination thereof.
Clause 22. The bioplastic mass of clause 21, further formed by the additional steps of:
heating the mixture to about 120° C.; and
molding the mixture into a shape.
Clause 23. The bioplastic mass of clauses 21 or 22, wherein the microalgae comprises Chlamydomonas and optionally includes Chlorella.
Clause 24. The bioplastic mass of clauses 23, wherein when the microalgae comprises Chlamydomonas reinhardtii and Chlorella vulgaris:
wherein the accumulated polymer from Chlamydomonas reinhardtii is triacylglycerol; and wherein the accumulated polymer from Chlorella vulgaris is selected from starch; triglyceride, cellulose, proteins, and a combination thereof.
Clause 25. The bioplastic mass of any one of clauses 21-24, wherein the additive is selected from ammonium persulfate, hydrogen peroxide, sodium persulfate, polyethylene, glycerol, and a combination thereof.
Clause 26. The bioplastic mass of any one of clauses 21-25, wherein the additive is from about 5% w/dw to about 15% w/dw of the biomass.
Clause 27. The bioplastic mass of any one of claims 21-25, wherein the extracted compound comprises carotenoids.
Clause 28. An alga mixed plastic comprising triacylglycerol-accumulated microalgae and polyethylene.
Clause 29. The alga mixed plastic of clause 28, wherein the triacylglycerol-accumulated microalgae is Chlamydomonas.
Clause 30, The alga mixed plastic of any one of the preceding clauses, further comprising Chlorella.
Clause 31. The alga mixed plastic of any one of the preceding clauses, further comprising an additive selected from ammonium persulfate, glycerol, and a combination thereof.
Clause 32. The alga mixed plastic of any one of the preceding clauses, wherein the triacylglycerol-accumulated Chlamydomonas is produced by centrifugation.
Clause 33. A method of producing triacylglycerol-accumulated microalgae, comprising:
selecting and culturing a species of microalgae capable of triacylglycerol accumulation from centrifugation;
centrifuging the cultured microalgae during the stationary phase of growth;
extracting precipitate formed during centrifugation;
incubating the precipitate, resulting in triacylglycerol-accumulated microalgae.
Clause 34. The method of clause 33, wherein the cultured species of microalgae is from the genus Chlamydomonas.
Clause 35. The triacylglycerol-accumulated microalgae of clause 33, wherein the amount of triacylglycerol accumulated in the microalgae after incubation is from about 200% to about 400% higher than triacylglycerol accumulation produced by microalgae subjected to stress conditions other than centrifugation.
Clause 36. The triacylglycerol-accumulated microalgae of clause 33, wherein the microalgae contains less C18 fatty acid methyl esters than in a comparable sample produced by nitrogen depletion.
Clause 37. Alga mixed plastic beads formed by the process of:
culturing one or more genus of microalgae, wherein at least one of the genera is a triacylglycerol-accumulating microalgae;
centrifuging the microalgae during the stationary phase to induce polymer compound accumulation;
extracting precipitate formed during centrifugation;
incubating and dehydrating the precipitate;
grinding the precipitate to form a powder and mixing with water to form a mixture;
adding at least one additive to the mixture to form the bioplastic.
heating the mixture to about 120° C.; and
molding the mixture into a shape.
Clause 38. The alga mixed plastic beads of claim 37, wherein the microalgae comprises Chlamydomonas and optionally includes Chlorella.
Clause 39. The alga mixed plastic beads of any one of the preceding clauses, wherein the accumulated polymer from Chlamydomonas reinhardtii is triacylglycerol; and
wherein the accumulated polymer from Chlorella vulgaris is selected from starch, triglyceride, cellulose, proteins, and a combination thereof.
Clause 40. The alga mixed plastic beads of any one of the preceding clauses; wherein the additive is selected from ammonium persulfate, hydrogen peroxide, sodium persulfate, polyethylene, glycerol, and a combination thereof.
Clause 41. The alga mixed plastic beads of any one of the preceding clauses, wherein the additive is from about 5% w/dw to about 15% w/dw of the biomass.
Clause 42. A thermoplastic including the bioplastic mass of any one of clauses 21-27.
It should be noted that ratios, concentrations, amounts, and other numerical data may be expressed herein in a range format. It is to be understood that such a range format is used for convenience and brevity, and thus, should be interpreted in a flexible manner to include not only the numerical values explicitly recited as the limits of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited. To illustrate, a concentration range of “about 0.1% to about 5%” should be interpreted to include not only the explicitly recited concentration of about 0.1 wt % to about 5 wt %, but also include individual concentrations (e.g., 1%, 2%, 3%, and 4%) and the sub-ranges (e.g., 0.5%, 1.1%, 2.2%, 3.3%, and 4.4%) within the indicated range. In an embodiment, “about 0” can refer to 0, 0.001, 0.01, or 0.1. In an embodiment, the term “about” can include traditional rounding according to significant figures of the numerical value. In addition, the phrase “about ‘x’ to ‘y’” includes “about ‘x’ to about ‘y’”.
It should be emphasized that the above-described embodiments of the present disclosure are merely possible examples of implementations, and are set forth only for a clear understanding of the principles of the disclosure. Many variations and modifications may be made to the above-described embodiments of the disclosure without departing substantially from the spirit and principles of the disclosure. All such modifications and variations are intended to be included herein within the scope of this disclosure.
This application is the 35 U.S.C. § 371 national stage of PCT application having serial number PCT/US2018/054928, filed on Oct. 9, 2018. This application also claims the benefit of and priority to U.S. Provisional Application Ser. No. 62/569,871, having the title “ALGAE-BASED BIOPLASTICS AND METHODS OF MAKING”, filed on Oct. 9, 2017, the disclosure of which is incorporated herein by reference in its entirety.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2018/054928 | 10/9/2018 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2019/074876 | 4/18/2019 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 8026301 | Sumanam | Sep 2011 | B2 |
| 8526811 | Xie et al. | Sep 2013 | B2 |
| 20130220173 | Sharma et al. | Aug 2013 | A1 |
| 20130236937 | Harlin | Sep 2013 | A1 |
| 20140134685 | Benning | May 2014 | A1 |
| 20170009197 | Harlin et al. | Jan 2017 | A1 |
| 20170073711 | Iwai et al. | Mar 2017 | A1 |
| Entry |
|---|
| Yao et al. “Microalgae Lipid Characterization”, Journal of Agricultural and Food Chemistry, vol. 63, pp. 1773-1787 (Year: 2015). |
| International Search Report for International Application No. PCT/US2018/054928, dated Jan. 28, 2019. |
| Number | Date | Country | |
|---|---|---|---|
| 20200263125 A1 | Aug 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62569871 | Oct 2017 | US |