Alkaline battery

Abstract

The present invention provides an alkaline battery suitable for use as a primary or secondary battery as a power source of electronic appliances. The battery is excellent in discharge characteristics under a heavy load and in cycle characteristics.

Description

TECHNICAL FIELD

The present invention relates to an alkaline battery using β-nickel oxy-hydroxide, or β-nickel oxy-hydroxide and manganese dioxide as active material for cathode. In particular, the present invention relates to an alkaline battery using β-nickel oxy-hydroxide having a mean particle size within a given range and obtained by a chemical oxidation method, or such the β-nickel oxy-hydroxide and manganese dioxide having a mean particle size within given range, as active material for the cathode, thereby enabling its discharge characteristics under a heavy load to be made excellent to operate the battery for a long period of time while the battery discharges large electricity. The present invention also relates to an alkaline battery in which a given quantity of a fluorinated resin is added as a binder into a cathode mix containing β-nickel oxy-hydroxide, thereby allowing its cycle characteristic to be made excellent.

Small size portable electronic appliances, for example, portable game machines and digital cameras in particular, have been remarkably spread in recent years. Since these appliances are supposed to be increasingly spread in near future, demands of batteries as power sources of these appliances are expected to be rapidly increased. While AA size cylindrical batteries have been mainly used for these appliances today, the power source should be excellent in discharge characteristics under a heavy load because each of the electronic appliances require a high operation voltage as well as a large electric current.

The most prevailing battery among these batteries satisfying such requirements is an alkaline-manganese battery using manganese dioxide for a cathode and zinc for anode, and a high concentration alkaline solution for an electrolyte. Since both manganese dioxide and zinc in this battery are inexpensive, and the battery has a high energy density per unit weight, it is widely used for the power source of small size portable electronic appliances.

For further improving the discharge characteristics of the alkaline manganese battery under a heavy load in view of the use thereof in these small size electronic appliances, various improvements have been attempted with respect to the materials of the battery and constructions of the battery. However, since discharge of manganese dioxide as the cathode active material depends on a uniform solid phase reaction in this battery system, the voltage is gradually decreased by discharge to give a discharge curve that descends with time.

A small portion of the requirements of the small size portable electronic appliances that require high voltage and large current may be satisfied by the discharge characteristics of the alkaline manganese battery as described above, and the time available for the use of the appliances is still short today even after applying various improvements. In addition, since the small size portable electronic appliances are often operated under a relatively high voltage and large current at the initial stage of debut in the market, a battery that is able to cope with such novel appliances and is excellent in heavy load characteristics becomes essential.

A nickel-zinc battery has been proposed as a battery satisfying such requirements. This battery uses nickel oxy-hydroxide for a cathode and zinc for an anode, and has a higher operation voltage than the alkaline manganese battery in addition to excellent heavy load characteristics. On the contrary, nickel oxy-hydroxide as a cathode active material is liable to generate oxygen while the amount of self-discharge is large.

For solving the problems, Japanese Patent Application Laid-Open Publication No. Hei10-214621 has disclosed, for example, an inside-out structure battery using γ-nickel oxy-hydroxide (γ-NiOOH) that exhibits a less amount of self-discharge for the cathode active material. Alternatively, an inside-out structure battery using β-nickel oxy-hydroxide (β-NiOOH) having a relatively high density for the cathode active material has been also disclosed.

However, although the storage battery composed of γ-nickel oxy-hydroxide exhibits less degree of self-discharge and a higher operation potential than the alkaline manganese battery due to its relatively low density of γ-nickel oxy-hydroxide, it is a problem that the discharge capacity of the battery is substantially small.

While the discharge capacity of the battery composed of β-nickel oxy-hydroxide has been improved since β-nickel oxy-hydroxide has a higher density than γ-nickel oxy-hydroxide, discharge characteristics under a heavy load are left behind yet as a problem to be improved.

Although the inside-out type alkaline battery (for example nickel-zinc battery) has a large discharge capacity, cycle characteristics of the battery is poor since the discharge capacity is largely decreased by repeating charge-discharge cycles, which is a problem.

It is one of the causes of the problem that a cathode active material having a hollow cylindrical shape is swelled by discharge, and the shape does not restore its original shape even by charging. Nickel hydroxide as a product of discharge has a lower density than that of nickel oxy-hydroxide, and has little conductivity. Accordingly, a carbon material having a binding action is added for improving conductivity of the cathode mix. However, while the carbon conductive material is responsible for binding the cathode mix, its action is so weak that an appropriate binder of the cathode mix is also required.

DISCLOSURE OF THE INVENTION

The object of the present invention is to provide an alkaline battery having discharge characteristics under a heavy load, which enable the battery to be operated for a long period of time even by discharging a large electricity, and having excellent cycle characteristics.

An alkaline battery relating to the present invention comprises a cathode mix containing β-nickel oxy-hydroxide as a cathode active material, an anode mix containing zinc as a main component of an anode active material, and an alkaline solution as an electrolyte, wherein β-nickel oxy-hydroxide is obtained by chemical oxidation of nickel hydroxide, and wherein the β-nickel oxy-hydroxide has a mean particle size in the range of 5 to 50 μm.

Preferably, the particle of β-nickel oxy-hydroxide is approximately spherical. The term “approximately spherical” is a concept including spherical and approximately spherical. The meaning is the same hereinafter.

β-nickel oxy-hydroxide prepared by chemical oxidation is used as a cathode active material in the present invention. The mean particle size of the β-nickel oxy-hydroxide is preferably in the range of 5 to 50 μm. A large quantity of the active material can be hardly packed in one battery due to a strong repulsive force among the particles in compression molding of the cathode, when the mean particle size of the β-nickel oxy-hydroxide is smaller than 5 μm, to result in a decrease of discharge characteristics under a heavy load. On the other hand, its discharge capacity decreases when the mean particle size of β-nickel oxy-hydroxide is larger than 50 μm also to result in a decrease of discharge characteristics under a heavy load. Accordingly, the alkaline battery excellent in the discharge characteristics under a heavy load may be obtained by restricting the mean particle size of β-nickel oxy-hydroxide in the range of 5 to 50 μm. Note that the β-nickel oxy-hydroxide can be packed in a higher density by forming the β-nickel oxy-hydroxide particles into spherical particles to enable a larger discharge capacity (battery capacity) to be obtained.

In another aspect, an alkaline battery relating to the present invention comprises a cathode mix containing β-nickel oxy-hydroxide and manganese dioxide as cathode active materials, an anode mix mainly comprising zinc as an anode active material, and an alkaline solution as an electrolyte wherein the β-nickel oxy-hydroxide is obtained by chemical oxidation of nickel hydroxide and wherein the β-nickel oxy-hydroxide has a mean particle size in the range of 5 to 50 μm, and wherein the manganese dioxide has a mean particle size in the range of 10 to 70 μm. The particles of β-nickel oxy-hydroxide are approximately spherical.

A cathode active material prepared by mixing β-nickel oxy-hydroxide produced by chemical oxidation and manganese dioxide is used in the present invention. The mean particle size of the β-nickel oxy-hydroxide is in the range of 5 to 50 μm, while the mean particle size of the manganese dioxide is in the range of 10 to 70μm.

Since the repulsive force among the particles is strong in compression molding of the cathode when the particle size distribution of the cathode active material falls in a small particle size range (the mean particle size of the β-nickel oxy-hydroxide is smaller than 5 μm, and the mean particle size of the manganese dioxide is smaller than 10 μm), it is difficult to pack the active material in one battery in a large quantity to decrease the discharge characteristics under a heavy load. On the other hand, the discharge capacity is decreased when the particle size is distributed in a larger range (the mean particle size of the β-nickel oxy-hydroxide is larger than 50 μm, and the mean particle size of the manganese dioxide is larger than 70 μm), and the discharge characteristics under a heavy load are also decreased.

Accordingly, an alkaline battery excellent in the discharge characteristics under a heavy load can be obtained by controlling the mean particle size of β-nickel oxy-hydroxide in the range of 5 to 50 μm, and the mean particle size of manganese dioxide in the range of 10 to 70 μm. The packing capacity of the cathode can be increased without reducing the reaction area between the cathode and anode using a mixture of the β-nickel oxy-hydroxide and the manganese dioxide, and the discharge capacity is increased. Forming the β-nickel oxy-hydroxide into a spherical shape allows the β-nickel oxy-hydroxide to be packed in a high density, thereby enabling a larger discharge capacity (cell capacity) thereof to be obtained. Using the manganese dioxide causes reduction of the production cost.

In a different aspect, an inside-out type alkaline battery relating to the present invention comprises a cathode mix containing β-nickel oxy-hydroxide and a conductive material as a cathode active material, an anode mix containing zinc as a main component of an anode active material, an alkaline solution as an electrolyte, and a separator disposed between a cathode comprising the cathode mix and an anode comprising the anode mix, wherein the β-nickel oxy-hydroxide is obtained by chemical oxidation of nickel hydroxide, and wherein the cathode mix includes a fluorinated resin as a binder.

According to the invention, the β-nickel oxy-hydroxide is used as the cathode active material. While a fluorinated resin such as polytetrafluoroethylene (PTFE), tetrafluoroethylene-hexafluoropropylene copolymer (FEP) or polychlorotrifluoroethylene (PCTFE) is added as a binder in the cathode mix containing the cathode active material, the amount of addition of the fluorinated resin is 0.1 to 1.0% by weight. Conductivity is reduced due to large charge transfer resistance in the cathode when the amount of addition is larger than 1.0% by weight, since the surface of the cathode active material is excessively covered with the binder. When the amount of addition of the binder is less than 1% by weight, on the other hand, the cycle characteristics are deteriorated since the effect of the binder becomes small. Accordingly, swelling of the cathode active material by discharge is suppressed by adding the fluorinated resin in an amount of 0.1 to 1.0% by weight to enable the alkaline battery to exhibit excellent cycle characteristics.

Preferably, a porous metal cylinder is provided between the cathode and the separator. The porous metal cylinder has a thickness of, for example, 50 to 200 μm. The porous metal cylinder is formed of any one of a hollow stainless steel cylinder, as well as a punching metal, a metal net, and an expand metal that are made of nickel, copper or tin. Such configuration permits an alkaline battery having improved cycle characteristics to be obtained, since water formed at the cathode by charging is pushed out to the anode to suppress swelling of the cathode by this water, and water formed at the cathode by charging is efficiently transferred to the anode to suppress deterioration of the capacity by charge-discharge cycles.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram for showing a configuration of an alkaline battery in the first embodiment;

FIG. 2 is a diagram for showing the relationship between the mean particle size of β-nickel oxy-hydroxide and discharge time;

FIG. 3 is a diagram for comparing the discharge time depending on the kinds of nickel oxy-hydroxide;

FIG. 4 is a diagram for showing the relationship between the mean particle size of manganese dioxide and discharge time;

FIG. 5 is a diagram for showing the relationship between the cumulative pore volume of β-NiOOH, and the charging time and self-discharge ratio;

FIG. 6 is a diagram for showing the relationship between the cumulative pore volume of β-NiOOH, and the charging time and self-discharge ratio when the proportion of blending of β-NiOOH in the cathode active material is 50% by weight;

FIG. 7 is a diagram for showing the relationship between the cumulative pore volume of β-NiOOH, and the charging time and self-discharge ratio when the proportion of blending of β-NiOOH in the cathode active material is 30% by weight;

FIG. 8 is a diagram for showing the relationship between the cumulative pore volume of β-NiOOH, and the charging time and self-discharge ratio when the proportion of blending of β-NiOOH in the cathode active material is 10% by weight;

FIG. 9 is a diagram for showing the relationship between the sulfuric acid radical content in β-nickel oxy-hydroxide, and the discharge time and self-discharge ratio under heavy load discharge;

FIG. 10 is a diagram for showing the relationship between the sulfuric acid radical content in β-nickel oxy-hydroxide, and the discharge time and self-discharge ratio under light load discharge;

FIG. 11 is a diagram for showing the relationship between the sulfuric acid radical content in β-nickel oxy-hydroxide, and the discharge time and self-discharge ratio under heavy load discharge when the blend ratio of β-nickel oxy-hydroxide is 50%;

FIG. 12 is a diagram for showing the relationship between the sulfuric acid radical content in β-nickel oxy-hydroxide, and the discharge time and self-discharge ratio under light load discharge when the blend ratio of β-nickel oxy-hydroxide is 50%;

FIG. 13 is a diagram for showing the relationship between the amount of addition of PTFE, and the discharge capacity and charge transfer resistance;

FIG. 14 is a diagram for showing the relationship between the amount of addition of FEP, and the discharge capacity and charge transfer resistance;

FIG. 15 is a diagram for showing the relationship between the amount of addition of PCTFE, and the discharge capacity and charge transfer resistance;

FIG. 16 is a diagram for showing a configuration of an alkaline battery in the fifth embodiment;

FIG. 17 is a diagram for showing the relationship between thickness of the porous metal cylinder and capacity retention ratio; and

FIG. 18 is a diagram for showing the relationship between kinds of the metal and capacity retention ratio.

BEST MODE FOR CARRYING OUT THE INVENTION

A first embodiment of the present invention will be described hereinafter. FIG. 1 shows a configuration of the alkaline battery 100 in the first embodiment. Approximately spherical β-nickel oxy-hydroxide particles prepared by chemical oxidation are used for a cathode active material in the alkaline battery 100.

The alkaline battery 100 comprises a battery can 2, a cathode mix 3, a separator 4, an anode mix 5, a current collector pin 6, a gasket 7, a neutral cover 8 and a negative terminal 9.

The battery can 2 is formed, for example, by presswork of a metal plate subjected to nickel plating. The battery can 2 also serves as a positive terminal of the alkaline battery 100.

The cathode mix 3 is formed into a hollow cylinder, and is placed within the battery can 2. For producing the cathode mix 3, β-nickel oxy-hydroxide as a cathode active material, a carbon powder as a conductive material, and an alkaline solution as an electrolyte are mixed together, and the mixture is molded into the hollow cylinder. A graphite powder is used for the carbon powder used as the conductive material. While potassium hydroxide solution is used for the alkaline solution, lithium hydroxide solution or sodium hydroxide solution, or a mixture of them may be used.

The cathode mix 3 is prepared as follows. First, β-nickel oxy-hydroxide, the graphite powder, and a 40% by weight KOH solution are weighed in a proportion of 10:1:1, and they are mixed under a stirring method such as the one using an impeller or a ball mill. Then, the mixed material is then press-molded into a hollow cylinder, thereby obtaining the cathode mix 3.

The separator 4 has a bottom-sealed cylinder shape, and is disposed at the inside of the cathode mix 3. For example, as the separator 4, a synthetic fiber nonwoven fabric having good liquid absorbing and retaining property and being excellent in alkali resistance is used.

The anode mix 5 is a gel, and is filled in the separator 4. The anode mix 5 is prepared by uniformly dispersing and mixing particles of zinc and zinc oxide as anode active materials in the potassium hydroxide solution as the electrolyte using a gelling agent.

An opening of the battery can 2 is hermetically sealed with the gasket 7 as an insulator, the neutral cover 8, and the negative terminal 9. The current collector pin 6 made of a metal is welded to the negative terminal 9.

The alkaline battery 100 shown in FIG. 1 is produced as follows. The cathode mix 3 formed into a cylinder by compression molding is inserted into the battery can 2. Then, the separator 4 of the bottom-sealed cylinder is inserted at the center of the cathode mix 3, and a gel of the anode mix 5 is filled into the separator 4. Finally, the insulator gasket 7, the neutral cover 8, and the negative terminal 9 are inserted into the battery can 2, and an edge of the opening of the battery can 2 is folded to the inside to fix the gasket 7. The current collector pin 6 welded to the negative terminal 9 is inserted into the gel of the anode mix 5 when the gasket 7 and the like are inserted into the battery can 2.

Current collection of the anode in the alkaline battery 100 shown in FIG. 1 is ensured by inserting the current collector pin 6 welded to the negative terminal 9 into the anode mix 5. Current collection of the cathode is also ensured by connecting the cathode mix 3 to the battery can 2. The outer circumference surface of the battery can 2 is covered with an external label 10, and the positive terminal 11 is located at the projection (the top of the alkaline battery 100 in the drawing) at the bottom of the battery can 2.

β-nickel oxy-hydroxide as the cathode active material in this embodiment will be further described hereinafter.

The β-nickel oxy-hydroxide is produced by chemical oxidation of nickel hydroxide. For example, it is produced by oxidizing nickel hydroxide in a liquid phase containing an appropriate oxidizing agent such as sodium hypochlorite and an appropriate alkali species such as lithium hydroxide, sodium hydroxide and potassium hydroxide. The oxidation reaction is as follows: 2Ni(OH)₂+ClO⁻→2NiOOH+Cl⁻+H₂O

By forming the β-nickel oxy-hydroxide by chemical oxidation as described above, impurity ions such as NO₃⁻ and CO₃²⁻ flow out into the liquid phase and are eliminated from the crystal to a certain extent during the reaction process. Consequently, β-nickel oxy-hydroxide exhibiting small amount of self-discharge, particularly β-nickel oxy-hydroxide more suitable for the active material of a primary battery, may be obtained. Self-discharge of the β-nickel oxy-hydroxide is considered to occur by decomposition of the impurity ions such as NO₃⁻ and CO₃²⁻ contained in the crystal within the battery.

The crystal structure of nickel oxy-hydroxide formed is different depending on the pH in the liquid phase. High-density β-nickel oxy-hydroxide (theoretical density: 4.68 g/cm³) is formed at a pH lower than a given value, while low-density γ-nickel oxy-hydroxide (theoretical density: 3.79 g/cm³) is formed at a pH higher than the given value above.

High-density nickel hydroxide having an approximately spherical shape of particle is used as nickel hydroxide as a starting material. As a result thereof, β-nickel oxy-hydroxide as the cathode active material in this embodiment has an approximately spherical shape of particle.

While usual nickel hydroxide is not spherical with a tap density of 1.4 to 1.8 g/cm³ and bulk density of 1.0 to 1.4 g/cm³, so-called high-density nickel hydroxide has approximately spherical particle with a tap density of 2.0 to 2.5 g/cm³ and bulk density of 1.4 to 1.8 g/cm³ that are higher than usual nickel hydroxide.

The tap density and the bulk density (also referred to as “powder density”) are measured as follows. The powder to be measured is filled by spontaneous falling in a specified vessel, the tap density and bulk density are calculated by the following equations bulk density=A/B(g/cm³) tap density=A/C(g/cm³) wherein the initial weight is represented by A (g), the initial volume is represented by B (cm³), and the volume after raising the vessel and lightly tapping the bottle thereof onto a desk or the like at 200 times is represented by C (cm³).

The tap density and bulk density of the β-nickel oxy-hydroxide as the cathode active material in this embodiment desirably falls within the following ranges. Namely, the tap density of the β-nickel oxy-hydroxide desirably falls within the ranges of 2.2 to 2.7 g/cm³. The bulk density of the β-nickel oxy-hydroxide desirably falls within the ranges of 1.6 to 2.2 g/cm³. This is because it is difficult to increase the discharge capacity when the tap density and the bulk density are smaller than the lower limits of the ranges described above. This is also because it is difficult to produce the β-nickel oxy-hydroxide having the tap density and the bulk density larger than the upper limits of the ranges described above.

A discharge time of the alkaline battery 100 after production shown in FIG. 1 was measured with a constant discharge power of 1.5 W under an atmosphere at 20° C. as a discharge condition until the final discharge voltage reaches 1.0 V.

Alkaline batteries in Examples 1 to 22 in the first embodiment t, and alkaline batteries in Comparative Examples 1 to 4 were measured therein.

β-nickel oxy-hydroxide used in the cathode mix 3 in each of the Examples 1 to 22 is produced by chemical oxidation, and the mean particle size of the approximately spherical particles was changed in the range of 1 to 70 μm so that the batteries were produced according to the manufacturing procedure of the alkaline battery described above. The β-nickel oxy-hydroxide having a particle size distribution range of ±20 μm as a center of a mean particle size value was used in this embodiment.

The batteries in Comparative Examples 1 to 4 were produced by the same method as in Examples 1 to 22, except that γ-nickel oxy-hydroxide produced by chemical oxidation was used for the cathode mix 3, and the mean particle size was changed in the range of 5 to 50 μm.

The results of the measurements in Examples 1 to 22 and Comparative Examples 1 to 4 measured under the conditions above are shown in Table 1.

TABLE 1
			Discharge time
	Crystal	Mean particle size of	immediately after
	structure	β-NiOOH (μm)	preparation* (min)
Example 1	β-NiOOH	1	12
Example 2		2	14
Example 3		3	20
Example 4		4	24
Example 5		5	45
Example 6		6	48
Example 7		7	49
Example 8		8	52
Example 9		9	52
Example 10		10	52
Example 11		11	52
Example 12		12	52
Example 13		20	53
Example 14		30	53
Example 15		40	53
Example 16		45	53
Example 17		48	54
Example 18		50	54
Example 19		52	30
Example 20		55	26
Example 21		60	22
Example 22		70	18
Comparative	γ-NiOOH	5	30
Example 1
Comparative		20	32
Example 2
Comparative		35	32
Example 3
Comparative		50	34
Example 4
*Discharge condition: temperature at 20° C., constant discharge power of 1.5 W, and discharge termination voltage at 1.0 V

The correlation curves between the mean particle size of β-nickel oxy-hydroxide produced by chemical oxidation and the discharge time as shown in FIG. 2 is obtained from the results of the measurements in Table 1. FIG. 2 shows that the mean particle size of the β-nickel oxy-hydroxide that enables the discharge time of the battery to be prolonged is in the range A in the diagram, or in the range of 5 to 50 μm. Accordingly, a large quantity of the active material can be hardly packed in one battery due to a strong repulsive force among the particles in compression molding of the cathode, when the mean particle size of the β-nickel oxy-hydroxide is less than 5 μm, to result in a shortness of discharge time and a deterioration of the discharge characteristics under a heavy load. The discharge characteristics under a heavy load are also deteriorated with a small discharge capacity when the mean particle size thereof exceeds 50 μm.

Comparative results of the discharge times of the batteries produced using different kinds of nickel oxy-hydroxide are shown in FIG. 3 based on the results of the measurements in Table 1.

FIG. 3 shows a comparison between the discharge times immediately after the production thereof when β-nickel oxy-hydroxide and γ-nickel oxy-hydroxide are used as the cathode active materials. As shown in FIG. 3, the discharge time of the battery comprising γ-nickel oxy-hydroxide produced by chemical oxidation is shorter than the discharge time of the battery comprising β-nickel oxy-hydroxide. This may be comprehended that the discharge capacity of the battery is decreased due to a small packing capacity of the γ-nickel oxy-hydroxide in a given volume of the cathode of the battery since the density of γ-nickel oxy-hydroxide is low.

Accordingly, an alkaline battery having excellent discharge characteristics under a heavy load can be obtained by using β-nickel oxy-hydroxide that is produced as the cathode active material by chemical oxidation and has a mean particle size in the range of 5 to 50 μm. The density of β-nickel oxy-hydroxide is more increased by forming β-nickel oxy-hydroxide particles into an approximately spherical shape to enable a larger discharge capacity (battery capacity) to be obtained.

While the discharge capacity is decreased when the β-nickel oxy-hydroxide particles are not spherical, this may be conjectured to be the effect of the specific particle size distribution as described above.

Subsequently, the alkaline batteries in Examples 23 to 122 in the first embodiment were investigated.

The cathode mix 3 in each of the alkaline batteries in Examples 23 to 122 is prepared by mixing approximately spherical β-nickel oxy-hydroxide prepared by chemical oxidation and manganese dioxide as cathode active materials, a carbon powder as a conductive material, and an alkaline solution as an electrolyte, followed by molding the mixture into a hollow cylinder. The other configuration and manufacturing method are the same as the alkaline battery 100 shown in FIG. 1.

The characteristics of the alkaline batteries in Examples 23 to 122 were evaluated under the test conditions as described above.

β-nickel oxy-hydroxide used in the cathode mix 3 in each of the Examples 23 to 62 was produced by chemical oxidation with its particles having an approximately spherical shape, and the mean particle size thereof being changed in the range of 5 to 50 μm. Further, the manganese dioxide was used with its articles having a mean particle size in the range of 8 to 80 μm. The blend ratio of β-nickel oxy-hydroxide and manganese dioxide was 30% by weight relative to the total amount of the cathode active material. The other specifications were the same as those in Examples 1 to 22, and the batteries were produced by the same procedure as described above.

The results of the measurements in Examples 23 to 62 obtained under the test conditions above are shown in Table 2.

TABLE 2
	Blend
	ratio of	Mean	Mean
	β-NiOOH	particle	particle	Discharge time
	(% by	size (μm)	size (μm)	immediately after
	weight)	of MnO2	of β-NiOOH	preparation* (min)
Example 23	30%	8	5	18
Example 24			20	20
Example 25			35	21
Example 26			50	22
Example 27		9	5	32
Example 28			20	33
Example 29			35	34
Example 30			50	34
Example 31		10	5	45
Example 32			20	46
Example 33			35	47
Example 34			50	47
Example 35		20	5	47
Example 36			20	47
Example 37			35	48
Example 38			50	48
Example 39		40	5	48
Example 40			20	48
Example 41			35	48
Example 42			50	48
Example 43		60	5	48
Example 44			20	48
Example 45			35	48
Example 46			50	48
Example 47		70	5	46
Example 48			20	47
Example 49			35	47
Example 50			50	47
Example 51		72	5	33
Example 52			20	35
Example 53			35	35
Example 54			50	34
Example 55		75	5	19
Example 56			20	20
Example 57			35	21
Example 58			50	20
Example 59		80	5	15
Example 60			20	16
Example 61			35	16
Example 62			50	16
*Discharge condition: temperature at 20° C., constant discharge power of 1.5 W, and discharge termination voltage at 1.0 V

In Examples 63 to 92, the batteries were manufactured by the same specification and manufacturing procedure as in Examples 23 to 62 except that the proportion of β-nickel oxy-hydroxide in the total amount of the cathode active material is controlled to be 50% by weight.

The results of the measurements measured under the test conditions above in Examples 63 to 92 are shown in Table 3.

TABLE 3
	Blend
	ratio of	Mean	Mean
	β-NiOOH	particle	particle	Discharge time
	(% by	size (μm)	size (μm)	immediately after
	weight)	of MnO2	of β-NiOOH	preparation* (min)
Example 63	50%	8	5	26
Example 64			25	26
Example 65			50	27
Example 66		9	5	38
Example 67			25	38
Example 68			50	39
Example 69		10	5	50
Example 70			25	51
Example 71			50	51
Example 72		20	5	52
Example 73			25	52
Example 74			50	52
Example 75		40	5	52
Example 76			25	52
Example 77			50	52
Example 78		60	5	52
Example 79			25	52
Example 80			50	53
Example 81		70	5	53
Example 82			25	53
Example 83			50	53
Example 84		72	5	36
Example 85			25	36
Example 86			50	37
Example 87		75	5	27
Example 88			25	27
Example 89			50	26
Example 90		80	5	18
Example 91			25	18
Example 92			50	17
Discharge condition: temperature at 20° C., constant discharge power of 1.5 W, and discharge termination voltage at 1.0 V

In Examples 93 to 122, the batteries were manufactured by the same specification and manufacturing procedure as in Examples 23 to 62 except that the proportion of β-nickel oxy-hydroxide in the total amount of the cathode active material is controlled to be 10% by weight.

The results of the measurements measured under the test conditions above in Examples 93 to 122 are shown in Table 4.

TABLE 4
	Blend
	ratio of	Mean	Mean
	β-NiOOH	particle	particle	Discharge time
	(% by	size (μm)	size (μm)	immediately after
	weight)	of MnO2	of β-NiOOH	preparation* (min)
Example 93	10%	8	5	11
Example 94			25	11
Example 95			50	11
Example 96		9	5	15
Example 97			25	16
Example 98			50	16
Example 99		10	5	27
Example 100			25	28
Example 101			50	28
Example 102		20	5	29
Example 103			25	29
Example 104			50	29
Example 105		40	5	30
Example 106			25	30
Example 107			50	30
Example 108		60	5	30
Example 109			25	30
Example 110			50	30
Example 111		70	5	31
Example 112			25	31
Example 113			50	31
Example 114		72	5	18
Example 115			25	17
Example 116			50	17
Example 117		75	5	14
Example 118			25	14
Example 119			50	13
Example 120		80	5	12
Example 121			25	12
Example 122			50	12
*Discharge condition: temperature at 20° C., constant discharge power of 1.5 W, and discharge termination voltage at 1.0 V

Correlation curves between the mean particle size of manganese dioxide and the discharge time, as shown in FIG. 4, are obtained on the basis of the results of the measurements in Tables 2 to 4. The blend proportions of β-nickel oxy-hydroxide in the cathode active material were 50, 30 and 10% by weight, respectively and the mean particle size thereof was 50 μm. FIG. 5 shows that the mean particle size of manganese dioxide that prolongs the discharge time is in the range B in the diagram, or in the range of 10 to 70μm. Thus, a large quantity of the active material can be hardly packed in one battery due to a strong repulsive force among the particles in compression molding of the cathode, when the mean particle size of the manganese dioxide is less than 10 μm, to result in a shortness of discharge time and a deterioration of the discharge characteristics under a heavy load. The discharge characteristics under a heavy load are also deteriorated with a small discharge capacity when the mean particle size thereof exceeds 70 μm.

While the results when the mean particle size of the β-nickel oxy-hydroxide is 50 μm are shown in FIG. 4, the same results are obtained in other examples in which the mean particle size of the β-nickel oxy-hydroxide is in the range of 5 to 50 μm.

It was confirmed from FIG. 4 that the discharge time is longer when the blend ratio of β-nickel oxy-hydroxide is 50% by weight than when the blend ratio of β-nickel oxy-hydroxide is 30% and 10% by weight.

An alkaline battery using a mixture of β-nickel oxy-hydroxide prepared by chemical oxidation and manganese dioxide as the cathode active materials, by adjusting the mean particle size of the β-nickel oxy-hydroxide particles in the range of 5 to 50 μm, and by adjusting the mean particle size of the manganese dioxide particles in the range of 10 to 70 μm allows its discharge characteristics under a heavy load to be excellent. It is also possible to increase the packing capacity of the cathode without decreasing any reaction areas of the cathode/anode by using a mixture of β-nickel oxy-hydroxide and manganese dioxide as the cathode active material. Reduction of the production cost of the battery is also possible by using inexpensive manganese dioxide. Since the β-nickel oxy-hydroxide particles are formed into approximately spherical, the β-nickel oxy-hydroxide can be packed in a higher density to enable a larger discharge capacity (battery capacity) to be obtained.

The second embodiment of the present invention will be described hereinafter.

The configuration of the alkaline battery in the second embodiment is the same as the configuration of the alkaline battery 100 in the first embodiment (see FIG. 1).

The alkaline batteries in Examples 1 to 13 in the second embodiment are described below.

The alkaline batteries in Examples 1 to 13 were produced according to the above manufacturing procedure of the alkaline battery 100 using β-nickel oxy-hydroxide prepared by chemical oxidation for the cathode mix 3 with its particles having approximately spherical shape and cumulative pore volume in connection with pore sizes of not larger than 0.5 μm in the particles thereof being changed in the range of 5 to 70 μl/g.

Characteristics of the alkaline batteries in Examples 1 to 13 were evaluated under two test conditions. In condition 1, the discharge time was measured until the discharge termination voltage reaches 1.0 V with a constant discharge power of 1.5 W at the ambient temperature of 20° C. Immediately after producing the battery. In condition 2, the battery was stored at the ambient temperature of 60° C. for 20 days and, after resuming the temperature at 20° C., the discharge time was measured until the discharge termination voltage reaches 1.0 V with a constant discharge power of 1.5 W.

The results obtained in Examples 1 to 13 under these two conditions are shown in Table 5.

	TABLE 5
	cumula-
	tive pore
	volume in	Discharge time*
		connection		After
		with		storage
		pore sizes		for
		of not	Immediatly	20 days	Self-
	Cathode	larger than	after	at	discharge
	active	0.5 μm	production	60° C.	ratio
	material	(μl/g)	(min)	(min)	(%)
Example 1	β-NiOOH	5	18	17	6
Example 2		8	29	26	10
Example 3		10	40	35	13
Example 4		15	52	41	21
Example 5		20	52	41	21
Example 6		30	52	41	21
Example 7		40	52	41	21
Example 8		50	54	41	24
Example 9		55	54	40	26
Example 10		60	54	39	28
Example 11		62	56	28	50
Example 12		65	56	20	64
Example 13		70	57	14	75
*Discharge condition: temperature at 20° C., constant discharge power of 1.5 W, and discharge termination voltage at 1.0 V

Correlation curves in FIG. 5 between the cumulative pore volume of β-nickel oxy-hydroxide prepared by chemical oxidation, and the discharge time and self-discharge ratio are obtained from the results of the measurements in Table 5. The cumulative pore volume in connection with of pore size of 0.5 μm or less in the β-nickel oxy-hydroxide particles, which permits the discharge time to be prolonged and the self-discharge ratio to be low, is within the range A, or within the range of 10 to 60 μl/g. While the battery has excellent discharge characteristics under a heavy load when the cumulative pore volume in connection with of pore size of 0.5 μm or less in the β-nickel oxy-hydroxide particles exceeds 60 μl/g, storage characteristics are largely decreased due to considerable increase of the self-discharge ratio. While the storage characteristics are improved (low self-discharge ratio) when the volume is less than 10 μl/g, the discharge characteristics under a heavy load are also largely decreased.

An alkaline battery using, as the cathode active material, β-nickel oxy-hydroxide that is prepared by chemical oxidation and has a cumulative pore volume in connection with the pore sizes of 0.5 μm or less in the particles in the range of 10 to 60 μl/g allows its discharge characteristics under a heavy load and storage characteristics to be excellent. Since the particles of β-nickel oxy-hydroxide are approximately spherical, the β-nickel oxy-hydroxide may have a higher density to enable a larger discharge capacity (battery capacity) to be obtained.

Alkaline batteries in Examples 14 to 52 in the second embodiment will be described hereinafter.

The cathode mix 3 in each of the alkaline batteries in Examples 14 to 52 comprises approximately spherical β-nickel oxy-hydroxide particles prepared by chemical oxidation and manganese dioxide as cathode active materials, carbon powder as a conductive material, and an alkaline solution as an electrolyte, which materials are mixed, and molded into a hollow cylinder. The other configuration and production procedure are the same as in the alkaline batteries in Exarmples 1 to 13.

A mixture of β-nickel oxy-hydroxide and manganese dioxide was used as the cathode mix 3 in Examples 14 to 52. The cumulative pore volume in connection with pore size of 0.5 μm or less in the β-nickel oxy-hydroxide particles was changed in the range of 5 to 70 μl/g. Approximately spherical β-nickel oxy-hydroxide produced by chemical oxidation was used in the mixture. The blend ratio of β-nickel oxy-hydroxide and manganese dioxide to the total amount of the cathode active material was 50% by weight in Examples 14 to 26, 30% in Examples 27 to 39, and 10% in Examples 40 to 52, respectively. The batteries were prepared by the same specification as in Examples 1 to 13 according to the production procedure as described above.

The characteristics of the alkaline batteries in Examples 14 to 52 were evaluated under the two conditions described above. The results of the measurements under the test conditions in Examples 14 to 52 are shown in Table 6.

	TABLE 6
	cumulative
	pore volume in
	connection	Discharge time*
	Blend ratio	with pore	Immediately	After storage	Self-
	of β-NiOOH	sizes of not	after	for 20 days at	discharge
	(% by	larger than	production	60° C.	ratio
	weight)	0.5 μm (μl/g)	(min)	(min)	(%)
Example 14	50%	5	16	14	13
Example 15		8	28	24	14
Example 16		10	46	38	17
Example 17		15	48	40	17
Example 18		20	50	40	20
Example 19		30	50	40	20
Example 20		40	50	40	20
Example 21		50	50	40	20
Example 22		55	52	40	23
Example 23		60	52	40	23
Example 24		62	54	25	54
Example 25		65	54	18	67
Example 26		70	56	12	79
Example 27	30%	5	14	12	14
Example 28		8	28	24	14
Example 29		10	42	35	17
Example 30		15	44	36	18
Example 31		20	46	36	22
Example 32		30	47	36	23
Example 33		40	47	36	23
Example 34		50	47	36	23
Example 35		55	47	36	23
Example 36		60	47	36	23
Example 37		62	48	26	46
Example 38		65	48	22	54
Example 39		70	49	15	69
Example 40	10%	5	5	4.5	10
Example 41		8	16	13	19
Example 42		10	23	18	22
Example 43		15	25	19	24
Example 44		20	27	20	26
Example 45		30	27	20	26
Example 46		40	27	20	26
Example 47		50	27	20	26
Example 48		55	27	20	26
Example 49		60	28	20	29
Example 50		62	29	14	52
Example 51		65	30	10	67
Example 52		70	30	6	80
*Discharge condition: temperature at 20° C., constant discharge power of 1.5 W, and discharge termination voltage at 1.0 V

Correlation curves in FIGS. 6 to 8 between the cumulative pore volume in connection with pore size of 0.5μ or less in mixed particles of β-nickel oxy-hydroxide and manganese dioxide, and the discharge time and self-discharge ratio in FIGS. 6 to 8 are obtained from the results of the measurements in Table 6. FIG. 6 shows the relationship between the cumulative pore volume, and the discharge time and self-discharge ratio when the blend ratio of β-nickel oxy-hydroxide in the cathode active material is 50% by weight. FIG. 7 shows the relationship between the cumulative pore volume, and the discharge time and self-discharge ratio when the blend ratio of β-nickel oxy-hydroxide in the cathode active material is 30% by weight. FIG. 8 shows the relationship between the cumulative pore volume, and the discharge time and self-discharge ratio when the blend ratio of β-nickel oxy-hydroxide in the cathode active material is 10% by weight.

FIGS. 6 to 8 show that the cumulative pore volume in connection with pore sizes of 0.5 μm or less in the mixed particles of β-nickel oxy-hydroxide and manganese dioxide, which permits the discharge time of the battery to be prolonged and the self-discharge ratio to be low, is within the range B in the diagram, or within the range of 10 to 60 μl/g. While the discharge characteristics under a heavy load are excellent when the cumulative pore volume in connection with pore sizes of 0.5 μm or less in the particles exceeds 60 μl/g as in the case using only β-nickel oxy-hydroxide as the cathode active material in FIG. 5, the storage characteristics are considerably decreased due to a large increase of the self-discharge ratio. While the storage characteristics are improved (low self-discharge ratio) when the fine volume is less than 10 μl/g, the discharge characteristics under a heavy load are largely decreased.

Accordingly, an alkaline battery using the cathode active material comprising a mixture of β-nickel oxy-hydroxide produced by chemical oxidation and manganese dioxide, and by controlling the cumulative pore volume in connection with pore size of 0.5 μm or less in the mixed particles of β-nickel oxy-hydroxide and manganese dioxide in the range of 10 to 60 μl/g allows its discharge characteristics under a heavy load and storage characteristics to be excellent. The packing capacity of the cathode can be increased without decreasing the reaction areas of the cathode/anode while the discharge capacity is increased, by using a mixture of β-nickel oxy-hydroxide and manganese dioxide as the cathode active materials. The production cost of the battery can be reduced using inexpensive manganese dioxide. The approximately spherical β-nickel oxy-hydroxide particles permit β-nickel oxy-hydroxide to have a high density, thereby permitting a larger discharge capacity (battery capacity) to be obtained.

The third embodiment of the present invention will be described hereinafter.

The configuration of the alkaline battery in the third embodiment is the same as the configuration of the alkaline battery 100 in the first embodiment (see FIG. 1).

The alkaline batteries in Examples 1 to 16 in the third embodiment will be described below.

In Exarmples 1 to 16 of this embodiment, the batteries were respectively produced according to the same production procedure of the alkaline battery 100 described above using, as β-nickel oxy-hydroxide to be used in cathode mix 3, β-nickel oxy-hydroxide produced by chemical oxidation and having an approximately spherical shape of particle, with content of sulfuric acid radical contained in the β-nickel oxy-hydroxide altering from 0.005 to 0.7% by weight.

Characteristics of these alkaline batteries were evaluated under four test conditions. In condition 1, the discharge time until reaching a discharge termination voltage of 1.0 V was measured after the production of the battery at the ambient temperature of 20° C. with a constant discharge power of 1.5W. In condition 2, the discharge time until reaching a discharge termination voltage of 1.0 V was measured after the production of the battery at the ambient temperature of 20° C. with a constant discharge power of 0.1 W. In condition 3, the discharge time until reaching a discharge termination voltage of 1.0 V was measured with a constant discharge power of 1.5 W by resuming the ambient temperature of 20° C. after storing the battery at the ambient temperature of 60° C. for 20 days. In condition 4, the discharge time until reaching a discharge termination voltage of 1.0 V was measured with a constant discharge power of 0.1 W by resuming the ambient temperature of 20° C. after storing the battery at the ambient temperature of 60° C. for 20 days.

The results of the measurements under the four test conditions in Examples 1 to 16 are shown in Table 7.

	TABLE 7
	Discharge time under		Discharge time under
	heavy load*		light load**
				After			After
		Content of	Immediately	storage at	Self-	Immediately	storage at	Self-
	Cathode	sulfuric acid	after	60° C. for	discharge	after	60° C. for	discharge
	active	radical (% by	production	20 days	ratio	production	20 days	ratio
	material	weight)	(min)	(min)	(%)	(h)	(h)	(%)
Example 1	β-NiOOH	0.005	52	38	27	27	22	19
Example 2		0.01	52	38	27	27	22	19
Example 3		0.03	52	38	27	27	22	19
Example 4		0.05	52	38	27	27	22	19
Example 5		0.11	52	38	27	27	22	19
Example 6		0.24	52	38	27	27	22	19
Example 7		0.38	52	38	27	27	22	19
Example 8		0.4	52	38	27	27	22	19
Example 9		0.47	52	36	31	27	22	19
Example 10		0.51	52	31	40	27	20	26
Example 11		0.53	52	27	48	27	18	33
Example 12		0.55	52	24	54	27	14	48
Example 13		0.58	52	20	62	27	10	63
Example 14		0.61	52	18	65	27	9	67
Example 15		0.64	52	16	69	27	8	70
Example 16		0.7	52	14	73	27	7	74
*Discharge condition: temperature at 20° C., constant discharge power of 1.5 W, and discharge termination voltage at 1.0 V
**Discharge condition: temperature at 20° C., constant discharge power of 0.1 W, and discharge termination voltage at 1.0 V

Correlation curves between the content of the sulfuric acid radical contained in β-nickel oxy-hydroxide, and the discharge time and self-discharge ratio after storage at 600C for 20 days as shown in FIGS. 9 and 10 are obtained from the results of the measurements in Table 7. FIG. 9 shows the relationship between the content of the sulfuric acid radical, and the discharge time and self-discharge ratio by heavy load discharge. FIG. 10 shows the relationship between the content of the sulfuric acid radical, and the discharge time and self-discharge ratio by light load discharge.

FIG. 9 shows that the content of the sulfuric acid radical in β-nickel oxy-hydroxide that permits the discharge time to be prolonged and the self-discharge ratio to be low in a case of the heavy load discharge is in the range of 0.5% or less by weight. In other words, the storage characteristics of the battery is deteriorated due to a high self-discharge ratio when the content of the sulfuric acid radical in β-nickel oxy-hydroxide exceeds 0.5% by weight.

FIG. 10 shows that the content of the sulfuric acid radical in β-nickel oxy-hydroxide that permits the discharge time to be prolonged and the self-discharge ratio to be low by heavy load discharge is also in the range of 0.5% or less by weight.

An alkaline battery excellent in the storage characteristics can be obtained by using β-nickel oxy-hydroxide produced by chemical oxidation and containing the sulfuric acid radical in the range of 0.5% or less by weight. Making particle of β-nickel oxy-hydroxide approximately spherical shape permits the β-nickel oxy-hydroxide to have a high density, thereby permitting a larger discharge capacity (battery capacity) to be obtained.

It is also confirmed from the results in Table 7 that the discharge time of the alkaline battery immediately after the production is not affected by the content of the sulfuric acid radical.

The alkaline batteries in Examples 17 to 64 in the third embodiment will be next described below.

In Examples 17 to 32, as β-nickel oxy-hydroxide to be used in cathode mix 3, β-nickel oxy-hydroxide produced by chemical oxidation and having an approximately spherical shape of particle was used, with content of sulfuric acid radical contained in the β-nickel oxy-hydroxide altering from 0.005 to 0.7% by weight. The blend ratio of β-nickel oxy-hydroxide to the total amount of the cathode active material comprising the β-nickel oxy-hydroxide and manganese dioxide was 50% by weight. The batteries were produced with the same specification and the same production procedure as in Examples 1 to 16.

The results of measurements in Examples 17 to 32 under the conditions above are shown in Table 8.

	TABLE 8
	Discharge time under		Discharge time under
	heavy load*		light load**
				After			After
	Blend ratio	Content of	Immediately	storage at	Self-	Immediately	storage at	Self-
	of β-NiOOH	sulfuric acid	after	60° C. for	discharge	after	60° C. for	discharge
	(% by	radical (% by	production	20 days	ratio	production	20 days	ratio
	weight)	weight)	(min)	(min)	(%)	(h)	(h)	(%)
Example 17	50%	0.005	48	36	25	25	21	16
Example 18		0.01	48	36	25	25	21	16
Example 19		0.03	48	36	25	25	21	16
Example 20		0.05	48	36	25	25	21	16
Example 21		0.11	48	36	25	25	21	16
Example 22		0.24	48	36	25	25	21	16
Example 23		0.38	48	36	25	25	21	16
Example 24		0.4	48	36	25	25	21	16
Example 25		0.47	48	36	25	25	21	16
Example 26		0.51	48	36	25	25	19	24
Example 27		0.53	48	31	35	25	16	36
Example 28		0.55	48	25	48	25	12	52
Example 29		0.58	48	20	58	25	10	60
Example 30		0.61	48	17	65	25	9	64
Example 31		0.64	48	15	69	25	8	68
Example 32		0.7	48	13	73	25	8	68
*Discharge condition: temperature at 20° C., constant discharge power of 1.5 W, and discharge termination voltage at 1.0 V
**Discharge condition: temperature at 20° C., constant discharge power of 0.1 W, and discharge termination voltage at 1.0 V

In Examples 33 to 48, the batteries were produced by the same specification as the one in Example 17 to 32 according to the same production procedure as described above, except that the proportion of β-nickel oxy-hydroxide in the total amount of the cathode active material was adjusted to 30% by weight.

The results of the measurements in Examples 33 to 48 under the test conditions described above are shown in Table 9.

	TABLE 9
	Discharge time under		Discharge time under
	heavy load*		light load**
				After			After
	Blend ratio	Content of	Immediately	storage at	Self-	Immediately	storage at	Self-
	of β-NiOOH	sulfuric acid	after	60° C. for	discharge	after	60° C. for	discharge
	(% by	radical (% by	production	20 days	ratio	production	20 days	ratio
	weight)	weight)	(min)	(min)	(%)	(h)	(h)	(%)
Example 33	30%	0.005	42	32	24	24	21	13
Example 34		0.01	42	32	24	24	21	13
Example 35		0.03	42	32	24	24	21	13
Example 36		0.05	42	32	24	24	21	13
Example 37		0.11	42	32	24	24	21	13
Example 38		0.24	42	32	24	24	21	13
Example 39		0.38	42	32	24	24	21	13
Example 40		0.4	42	32	24	24	21	13
Example 41		0.47	42	32	24	24	20	17
Example 42		0.51	42	27	36	24	19	21
Example 43		0.53	42	21	50	24	15	38
Example 44		0.55	42	17	60	24	13	46
Example 45		0.58	42	16	62	24	12	50
Example 46		0.61	42	15	64	24	11	54
Example 47		0.64	42	14	67	24	10	58
Example 48		0.7	42	12	71	24	10	58
*Discharge condition: temperature at 20° C., constant discharge power of 1.5 W, and discharge termination voltage at 1.0 V
**Discharge condition: temperature at 20° C., constant discharge power of 0.1 W, and discharge termination voltage at 1.0 V

In Examples 49 to 64, the batteries were produced by the same specification as the one in Examples 17 to 32 according to the production procedure described above, except that the proportion of β-nickel oxy-hydroxide in the total amount of the cathode active material was adjusted to 10% by weight.

The results of the measurement in Examples 49 to 64 under the test conditions described above are shown in Table 10.

	TABLE 10
	Discharge time under		Discharge time under
	heavy load*		light load**
				After			After
	Blend ratio	Content of	Immediately	storage at	Self-	Immediately	storage at	Self-
	of β-NiOOH	sulfuric acid	after	60° C. for	discharge	after	60° C. for	discharge
	(% by	radical (% by	production	20 days	ratio	production	20 days	ratio
	weight)	weight)	(min)	(min)	(%)	(h)	(h)	(%)
Example 49	10%	0.005	30	22	27	24	22	8
Example 50		0.01	30	22	27	24	22	8
Example 51		0.03	30	22	27	24	22	8
Example 52		0.05	30	22	27	24	22	8
Example 53		0.11	30	22	27	24	22	8
Example 54		0.24	30	22	27	24	22	8
Example 55		0.38	30	22	27	24	22	8
Example 56		0.4	30	22	27	24	22	8
Example 57		0.47	30	22	27	24	22	8
Example 58		0.51	30	18	40	24	20	17
Example 59		0.53	30	13	57	24	17	29
Example 60		0.55	30	11	63	24	15	38
Example 61		0.58	30	10	67	24	14	42
Example 62		0.61	30	10	67	24	13	46
Example 63		0.64	30	9	70	24	12	50
Example 64		0.7	30	9	70	24	12	50
*Discharge condition: temperature at 20° C., constant discharge power of 1.5 W, and discharge termination voltage at 1.0 V
**Discharge condition: temperature at 20° C., constant discharge power of 0.1 W, and discharge termination voltage at 1.0 V

Correlation curves as shown in FIGS. 11 and 12 between the content of the sulfuric acid radical contained in β-nickel oxy-hydroxide, and the discharge time and self-discharge ratio after storage at 60° C. for 20 days are obtained from the results of the measurements in Table 8. FIG. 11 shows the relationship between the content of the sulfuric acid radical, and the discharge time and self-discharge ratio by heavy load discharge, while FIG. 12 shows the relationship between the content of the sulfuric acid radical, and the discharge time and self-discharge ratio by light load discharge.

FIG. 11 shows that the content of the sulfuric acid radical in β-nickel oxy-hydroxide that permits the discharge time to be prolonged and self-discharge ratio to be low by heavy load discharge is in the range of 0.5% or less by weight. In other words, the storage characteristics of the battery are deteriorated due to a high self-discharge ratio when the content of the sulfuric acid radical in β-nickel oxy-hydroxide exceeds 0.5% by weight.

FIG. 12 shows that the content of the sulfuric acid radical in β-nickel oxy-hydroxide that permits the discharge time to be prolonged and self-discharge ratio to be low by light load discharge is also in the range of 0.5% or less by weight.

The effect of restricting the content of the sulfuric acid radical (0.5% or less by weight) can be confirmed from the results of the measurements in Tables 9 and 10 when the blend ratio of β-nickel oxy-hydroxide is changed to 30% and 10% by weight.

As described above, using the cathode active material prepared by mixing β-nickel oxy-hydroxide produced by chemical oxidation and manganese dioxide, and controlling the content of the sulfuric acid radical in β-nickel oxy-hydroxide in the range of 0.5% or less by weight allows an alkaline battery excellent in the storage characteristics to be obtained. Using the mixture of β-nickel oxy-hydroxide and manganese dioxide as the cathode active material permits the packing density of the cathode to be large without decreasing the reaction area in the cathode/anode. Using inexpensive manganese dioxide enables the production cost of the battery to be reduced. Since the approximately spherical particle of β-nickel oxy-hydroxide makes it possible to have a higher density of the β-nickel oxy-hydroxide, a larger discharge capacity (battery capacity) may be obtained.

It is confirmed from the results of the measurements in Tables 8 to 10 that the discharge time immediately after the production of the alkaline battery is not affected by the content of the sulfuric acid radical.

The fourth embodiment of the present invention will be described hereinafter.

The configuration of the alkaline battery in the fourth embodiment is the same as configuration of the alkaline battery 100 in the first embodiment (see FIG. 1).

The alkaline batteries in Examples 1 to 4 in the fourth embodiment and Comparative Examples 1 and 2 were investigated.

A battery can 2 of LR6 (AA) size made of a nickel-plated iron plate on the surface was used in Example 1. Organic paint containing graphite powder and binder was sprayed and dried on the inner surface of the battery can 2 to form a conductive paint film.

As cathode mix 3, β-nickel oxy-hydroxide prepared by chemical oxidation and having approximately spherical shape of particle and graphite powder were mixed in a dry state in a proportion of 10:1 and PTFE was then mixed to the mixture of the β-nickel oxy-hydroxide and the graphite powder in an amount of 0.1% by weight followed by adding to it a 40% by weight potassium hydroxide solution in an amount of 8% by weight under a stirring method using an impeller, a ball mill or the like. The mixture was press-molded into a hollow cylinder.

As anode mix 5, gelled potassium hydroxide solution containing 65% by weight of zinc particles and 2% by weight of zinc oxide were used, and 5 g of the mix was filled.

The battery was produced according to the same production procedure as the one of the alkaline battery 100 described above using the battery can 2, the cathode mix 3, and the anode mix 5.

In Example 2, the battery was produced by the same method as one in Example 1, except that 0.3% by weight of the fluorinated PTFE resin was added in the cathode mix 3.

In Example 3, the battery was produced by the same method as one in Example 1, except that 0.5% by weight of the fluorinated PTFE resin was added in the cathode mix 3.

In Example 4, the battery was produced by the same method as one in Example 1, except that 1.0% by weight of the fluorinated Hose resin was added in the cathode mix 3.

In Comparative Example 1, the battery was produced by the same method as one in Example 1, except that no fluorinated PTFE resin was added in the cathode mix 3.

In comparative Example 2, the battery was produced by the same method as one in Example 1, except that 5.0% by weight of the fluorinated PTFE resin was added in the cathode mix 3.

The cycle characteristics of these alkaline batteries were evaluated by measuring their discharge capacities and charge transfer resistances under the following test conditions.

In the measurement of the discharge capacity, the discharge condition comprised discharging of 100 mA and cut-off at 1.0 V, and the charge condition comprised charging at a constant current of 180 mA and a constant voltage of 1.95 V for 10 hours, and the charge-discharge cycles were repeated. The discharge capacities after 1 cycle and 100 cycles were measured.

In the measurement of the charge transfer resistance, the charge transfer resistance after 100 cycles of charge-discharge was measured under an alternating current impedance method. For the measurement, a 1280B-type impedance analyzer (manufactured by Solartron Analytical) is used. The test condition was 0.1 to 20,000 Hz of the frequency range and 10 mV of the applied voltage. The charge transfer resistance after 100 cycles was measured.

The discharge capacities and charge transfer resistance of the batteries in Examples 1 to 4 and Comparative example 1 and 2 were measured under the test conditions above. The results are shown in Table 11.

TABLE 11
		Discharge	Discharge
		capacity	capacity
	Amount	after 1	after 100	Charge transfer
	of added	cycle	cycles of	resistance after
	PTFE	of discharge	discharge	100 cycles of
	(% by weight)	(mAh)	(mAh)	discharge (mΩ)
Example 1	0.1	1770	1100	130
Example 2	0.3	1760	1200	120
Example 3	0.5	1750	1250	100
Example 4	1	1740	1100	135
Comparative	0	1800	1080	150
Example 1
Comparative	5	1650	850	250
Example 2

Correlation curves between the amount of added PTFE, and the discharge capacity and charge transfer resistance as shown in FIG. 13 are obtained from the results of the measurements in Table 11. FIG. 13 shows that the amount of added PTFE in which the discharge capacity is large after 100 cycles of discharge, or the rate of change of the discharge capacity is smaller as compared to the discharge capacity after 1 cycle of discharge and the charge transfer resistance is reduced, is within the range of 0.1 to 1.0% by weight, preferably 0.3 to 0.5% by weight. In other words, the charge transfer resistance in the cathode is increased to decrease conductivity when the amount of added PTFE exceeds 1.0% by weight since the surface of the cathode active material is excessively covered with the binder. The cycle characteristics are deteriorated due to the decrease of the effect of the binder when the amount of added PTFE is less than 0.1% by weight. The charge transfer resistance is more decreased while the discharge capacity after 100 cycles of discharge is more increased when the amount of added PTFE is in the range of 0.3 to 0.5% by weight. Accordingly, swelling of the cathode active material by discharge is suppressed to enable an alkaline battery excellent in the cycle characteristics to be obtained by restricting the amount of added PTFE in the range of 0.1 to 1.0% by weight. By adding the PTFE in the range of 0.3 to 0.5% by weight, the alkaline battery becomes more excellent in its cycle characteristics.

Consequently, adding the fluorinated resin PTFE as binder to the cathode mix using β-nickel oxy-hydroxide as the cathode active material in the range of 0.1 to 1.0% by weight, preferably in the range of 0.3 to 0.5% by weight allows an alkaline battery excellent in its cycle characteristics to be obtained.

Electrical and chemical stability and dispersability required for the binder may be obtained by using the fluorinated resin PTFE as the binder.

The approximately spherical shape of particle of the β-nickel oxy-hydroxide permits β-nickel oxy-hydroxide to have a high density and a larger discharge capacity (battery capacity) to be obtained.

Next, a case where FEP as a binder is added in the cathode mix 3 will be described below.

Since FEP contains tetrafluoroethylene in the structure, FEP is considered to have the same effect as PTFE.

Alkaline batteries in Examples 5 to 8 in the fourth embodiment and in Comparative Examples 1 and 3 were investigated.

The batteries were respectively prepared by the same specification as one in Example 1 according to the production procedure as described above in Examples 5 to 8, except that the fluorinated resin FEP was added as the binder, and the amount of added FEP altered in the range of 0.1 to 1.0% by weight relative to the amount of the mixture of β-nickel oxy-hydroxide and graphite powder.

In Example 5, the fluorinated resin FEP was added to the cathode mix 3 in an amount of 0.1% by weight.

In Example 6, the fluorinated resin FEP was added to the cathode mix 3 in an amount of 0.3% by weight.

In Example 7, the fluorinated resin FEP was added to the cathode mix 3 in an amount of 0.5% by weight.

In Example 8, the fluorinated resin FEP was added to the cathode mix 3 in an amount of 1.0% by weight.

In Comparative Example 1, the battery was produced by the same method as one in Example 1, except that no fluorinated resin FEP was added to the cathode mix 3.

In Comparative Example 3, the battery was produced by the same method as one in Example 1, except that the fluorinated resin FEP was added to the cathode mix 3 in an amount of 5.0% by weight.

The alkaline batteries 100 comprising FEP added in the cathode mix 3 as the binder was subjected to cycle characteristic evaluation.

The results of the measurements of the discharge capacities and charge transfer resistances in Examples 5 to 8 and Comparative Examples 1 and 3 under the above test conditions are shown in Table 12.

TABLE 12
		Discharge	Discharge
		capacity	capacity
	Amount	after 1	after 100	Charge transfer
	of added	cycle	cycles of	resistance after
	FEP	of discharge	discharge	100 cycles of
	(% by weight)	(mAh)	(mAh)	discharge (mΩ)
Example 5	0.1	1790	1150	120
Example 6	0.3	1780	1250	115
Example 7	0.5	1760	1230	110
Example 8	1	1740	1120	140
Comparative	0	1800	1080	150
Example 1
Comparative	5	1660	850	250
Example 3

Correlation curves between the amount of added FEP, and the discharge capacity and charge transfer resistance as shown in FIG. 14 are obtained from the results of the measurements in Table 12. FIG. 14 shows that the amount of added PTFE in which the discharge capacity is large after 100 cycles of discharge, or the rate of change of the discharge capacity is smaller as compare by the discharge capacity after 1 cycle of discharge, and the charge transfer resistance is reduced, is within the range of 0.1 to 1.0% by weight, preferably 0.3 to 0.5% by weight. In other words, the charge transfer resistance in the cathode is increased to decrease conductivity when the amount of added FET exceeds 1.0% by weight since the surface of the cathode active material is excessively covered with the binder. The cycle characteristics are deteriorated due to the decrease of the effect of the binder when the amount of added FEP is less than 0.1% by weight. The charge transfer resistance is more decreased while the discharge capacity after 100 cycles of discharge is more increased when the amount of added FEP is in the range of 0.3 to 0.5% by weight. Accordingly, swelling of the cathode active material by discharge is suppressed to enable an alkaline battery excellent in the cycle characteristics to be obtained by restricting the amount of added FEP in the range of 0.1 to 1.0% by weight. Further, the cycle characteristics of the alkaline battery becomes more excellent by adding FEP in the range of 0.3 to 0.5% by weight.

Consequently, adding the fluorinated resin FEP as the binder to the cathode mix 3 using β-nickel oxy-hydroxide as the cathode active material in the range of 0.1 to 1.0% by weight, preferably in the range of 0.3 to 0.5% by weight allows an alkaline battery excellent in the cycle characteristics to be obtained.

Electrical and chemical stability and dispersability required for the binder may be obtained by using the fluorinated resin FEP as the binder.

Next, a case where PCTFE as a binder is added in the cathode mix 3 will be described below.

Since PCTFE contains tetrafluoroethylene in the structure as in FEP, PCTFE is considered to have the same effect as PTFE and FEP.

Alkaline batteries in Examples 9 to 12 in the fourth embodiment and in Comparative Examples 1 and 4 were then investigated.

In Examples 9 to 12, the batteries were respectively prepared by the same specification as one in Example 1 according to the production procedure as described above, except that the fluorinated resin PCTFE was added as the binder, and the amount of added PCTFE was changed in the range of 0.1 to 1.0% by weight relative to the amount of the mixture of β-nickel oxy-hydroxide and graphite powder.

In Example 9, the fluorinated resin PCTFE was added to the cathode mix 3 in an amount of 0.1% by weight.

In Example 10, the fluorinated resin PCTFE was added to the cathode mix 3 in an amount of 0.3% by weight.

In Example 11, the fluorinated resin PCTFE was added to the cathode mix 3 in an amount of 0.5% by weight.

In Example 12, the fluorinated resin PCTFE was added to the cathode mix 3 in an amount of 1.0% by weight.

In Comparative Example 1, the battery was produced by the same method as in Example 1, except that no fluorinated resin PCTFE was added to the cathode mix 3.

In Comparative Example 4, the battery was produced by the same method as in Example 1, except that the fluorinated resin PCTFE was added to the cathode mix 3 in a proportion of 5.0% by weight.

The alkaline batteries comprising PCTFE added in the cathode mix 3 as the binder was subjected to cycle characteristic evaluation.

The results of the measurements of the discharge capacities and charge transfer resistance in Examples 9 to 12 and Comparative Examples 1 and 4 are shown in Table 13.

TABLE 13
		Discharge	Discharge
		capacity	capacity
	Amount	after 1	after 100	Charge transfer
	of added	cycle	cycles of	resistance after
	PCTFE	of discharge	discharge	100 cycles of
	(% by weight)	(mAh)	(mAh)	discharge (mΩ)
Example 9	0.1	1760	1100	135
Example 10	0.3	1750	1150	130
Example 11	0.5	1720	1170	125
Example 12	1	1690	1110	135
Comparative	0	1800	1080	150
Example 1
Comparative	5	1660	1000	260
Example 4

Correlation curves between the amount of added PCTFE, and the discharge capacity and charge transfer resistance as shown in FIG. 15 are obtained from the results of the measurements in Table 13. FIG. 15 shows that the amount of added PCTFE in which the discharge capacity is large after 100 cycles of discharge, or the rate of change of the discharge capacity is smaller as compared to the discharge capacity after 1 cycle of discharge, and the charge transfer resistance is reduced, is within the range of 0.1 to 1.0% by weight, preferably 0.3 to 0.5% by weight. In other words, the charge transfer resistance is increased to decrease conductivity when the amount of added PCTFE exceeds 1.0% by weight since the surface of the cathode active material is excessively covered with the binder. The cycle characteristics are deteriorated due to decrease of the effect of the binder when the amount of added PCTFE is less than 0.1% by weight. The charge transfer resistance is more decreased while the discharge capacity after 100 cycles of discharge is more increased when the amount of added PCTFE is in the range of 0.3 to 0.5% by weight. Accordingly, swelling of the cathode active material by discharge is suppressed to enable an alkaline battery excellent in the cycle characteristics to be obtained by restricting the amount of added PCTFE in the range of 0.1 to 1.0% by weight. By adding the PCTFE in the range of 0.3 to 0.5% by weight, the alkaline battery more excellent in the cycle characteristics thereof is obtained.

Consequently, adding the fluorinated resin PCTFE to the cathode mix 3 using β-nickel oxy-hydroxide as the cathode active material in the range of 0.1 to 1.0% by weight, preferably in the range of 0.3 to 0.5% by weight allows an alkaline battery excellent in its cycle characteristics to be obtained.

Electrical and chemical stability and dispersability required for the binder may be obtained by using the fluorinated resin PCTFE as the binder.

The fifth embodiment of the present invention will be described hereinafter.

FIG. 16 shows the configuration of the alkaline battery 100A in the fifth embodiment of the present invention. This alkaline battery 100A is a size AA battery having an inside-out structure. The parts corresponding to those in FIG. 1 are given the same reference numerals as in FIG. 16.

The alkaline battery 100A comprises a battery can 2, a cathode mix 3, a separator 4, an anode mix 5, a current collector pin 6, a gasket 7, a neutral cover 8, a negative terminal 9, and a porous metal cylinder 12.

The battery can 2 is formed, for example, by presswork of a metal plate subjected to nickel plating. The battery can 2 also serves as a positive terminal of the alkaline battery 100A.

The cathode mix 3 is a hollow cylinder, and is disposed within the battery can 2. For producing the cathode mix 3, β-nickel oxy-hydroxide as a cathode active material, a carbon powder as a conductive material and an alkaline solution as an electrolyte solution are mixed together, and the mixture is molded into the hollow cylinder. A graphite powder is used for the carbon powder used as the conductive material. While potassium hydroxide solution is used as the alkaline solution, lithium hydroxide solution or sodium hydroxide solution, or a mixture thereof may be also used.

The cathode mix 3 is prepared as follows. First, β-nickel oxy-hydroxide, the graphite powder and a 40% by weight potassium hydroxide (KOH) solution are weighed in a proportion of 10:1:1, and they are mixed under a stirring method using an impeller or a ball mill. The mixed material is then press-molded into a hollow cylinder to obtain the cathode mix 3.

The separator 4 is a bottom-sealed cylinder, and is disposed at the inside of the cathode mix 3. For example, as the separator 4, a synthetic fiber nonwoven fabric having good liquid absorbing and retaining property and being excellent in alkali resistance is used.

The anode mix 5 is a gel, and is filled in the separator 4. The anode mix 5 is prepared by uniformly dispersing and mixing particles of zinc and zinc oxide as anode active material in the potassium hydroxide solution as the electrolyte using a gelling agent.

The porous metal cylinder 12 is disposed between the cathode mix 3 and the separator 4. The porous metal cylinder comprises a punching metal, a metal net, and an expand metal made of a metal such as stainless steel, nickel, copper and tin.

Since the metal available for the porous metal cylinder depends on the kind of the electrolyte of the battery and the kind of the positive and negative electrodes, the metal available changes according to changes of the battery system. For example, metal such as stainless steel, nickel, copper and tin that do not react with the alkaline solution and the cathode may be used in the nickel-zinc storage battery.

An opening of the battery can 2 is hermetically sealed with the gasket 7 as an insulator, the neutral cover 8, and a negative terminal 9. A metallic current collector pin 6 is welded to the negative terminal 9.

The alkaline battery 100A shown in FIG. 16 is manufactured as follows. The cathode mix 3 press-molded into a hollow cylinder is inserted into the battery can 2. Then, the porous metal cylinder 12 is inserted into the inside of the cathode mix formed into the hollow cylinder. Subsequently, the bottom-sealed cylinder of the separator 4 is inserted into the inside of the porous metal cylinder 12, and the gelled anode mix 5 is filled in the separator 4. Finally, the gasket 7 as the insulator, the neutral cover 8 and the negative terminal 9 are inserted into the battery can 2, and the edge of the opening of the battery can 2 is folded into the inside to fix the gasket 7 so that the gasket 7 is fixed. The current collector pin 6 welded to the negative terminal 9 is inserted into the gelled anode mix 5 when the gasket 7 and other members are inserted into the battery can 2.

Charge collection of the negative electrode in the cylindrical storage battery 100A shown in FIG. 16 is ensured by inserting the current collector pin 6 welded to the negative terminal 9 into the anode mix 5. Charge collection of the cathode is also ensured by connecting the cathode mix 3 to the battery can 2. The outer circumference face of the battery can 2 is covered with an external label 10 on which name of the manufacturer, the kind of the battery and notices are printed, and the positive terminal 11 is located at the projection (the top of the cylindrical storage battery 100A in the drawing) at the bottom of the battery can 2.

The cycle characteristics of the alkaline battery 100A shown in FIG. 16 was evaluated by measuring the discharge capacity under the test conditions below.

After discharging 10 batteries with a current of 100 mA until the voltage is reduced to 1 V, the capacity retention ratios were compared with each other after 50 cycles of discharge by defining the process for charging up to 1.9 V as 1 cycle in the charge-discharge test.

The capacity retention ratio is defined by the proportion (%) of the discharge capacity to the initial discharge capacity represented by the following equation: capacity retention ratio (%) at 50^th cycle=[(discharge capacity at 50^th cycle)/(initial discharge capacity)]×100

Here, the alkaline batteries 100A in Comparative Example 1 and Examples 1 to 21 in the fifth embodiment were measured.

The alkaline battery in Comparative Example 1 has the same specification as the one of the alkaline battery 100, and as β-nickel oxy-hydroxide to be used for the cathode mix 3, the β-nickel oxy-hydroxide prepared by chemical oxidation and having approximately spherical shape of particle, which was dissolved at least one of the elements selected from Zn, Co and Mg, was used. The cathode mix 3 was prepared by mixing β-nickel oxy-hydroxide, graphite powder and 40% by weight KOH electrolyte in a proportion of 10:1:1. The cathode mix 3 (10 g) was molded into a hollow cylinder with an outer diameter of 13.3 m, an inner diameter of 9.0 mm and a height of 40 mm. After inserting the separator with a thickness of 0.2 mm and injecting 1.5 g of the electrolyte into the hollow cylinder, 5 g of anode mix prepared by mixing the zinc powder, gelling agent an 40% by weight KOH electrolyte in a proportion of 65:1:3 together with a small quantity of additives was filled into the cylinder to prepare an alkaline battery according to the same production procedure as that of the alkaline battery 100 as described above.

In Examples 1 to 6, the β-nickel oxy-hydroxide prepared by chemical oxidation and having approximately spherical shape of particle, in which at least one of the elements selected from Zn, Co and Mg was dissolved, was used for the cathode mix 3. The cathode mix 3 was prepared by mixing β-nickel oxy-hydroxide, graphite powder and 40% by weight KOH electrolyte in a proportion of 10:1:1. The cathode mix 3 (10 g) was molded in the cathode can 2 into a hollow cylinder with an outer diameter of 13.3 mm, an inner diameter of 9.0 mm and a height of 40 mm. Then, each stainless steel punching metal with a thickness of 30, 50, 100, 150, 200 or 250 μm formed into a hollow cylinder with an outer diameter of 9.0 mm and a height of 40 mm was inserted into the inside of the cathode mix formed into a hollow cylinder. The separator with a thickness of 0.2 mm was inserted into the hollow cylinder and, after injecting 1.5 g of the electrolyte in the cylinder, 5 g of the cathode mix prepared by mixing the zinc powder, gelling agent and 40% by weight KOH electrolyte in a proportion of 65:1:34 together with minute quantities of additives was filled in the bottom-sealed cylinder of the separator to produce respective batteries according to the same production procedure as that of the cylindrical storage battery 100A as described above.

These results of the measurements in Comparative Example 1 and Examples 1 to 6 under the test conditions described above are described in Table 14.

	TABLE 14
			Capacity
		Thickness of stainless	retention
		punching metal (μm)	ratio (%)
	Example 1	30	58
	Example 2	50	70
	Example 3	100	79
	Example 4	150	82
	Example 5	200	72
	Example 6	250	50
	Comparative	None	57
	Example 1

In Examples 7 to 12, each metal net made of stainless steel with a thickness of 30, 50, 100, 150, 200 and 250 μm formed into a hollow cylinder with an outer diameter of 9.0 mm and a height of 40 mm was disposed between the hollow cylinders of cathode mix 3 and separator 4. Alkaline batteries were produced by the same specification as one in Examples 1 to 6 except the conditions above according to the same production procedure as that of the alkaline battery 100A as described above.

The results of the measurements in Examples 7 to 12 under the test condition above are shown in Table 15. Comparative Example 1 in Table 15 is the same as described above.

	TABLE 15
			Capacity
		Thickness of stainless steel	retention
		net (μm)	ratio (%)
	Example 7	30	57
	Example 8	50	65
	Example 9	100	70
	Example 10	150	74
	Example 11	200	66
	Example 12	250	55
	Comparative	None	57
	Example 1

In Examples 13 to 18, each stainless steel expand metal with a thickness of 30, 50, 100, 150, 200 and 250 μm formed into a hollow cylinder with an outer diameter of 9.0 mm and a height of 40 mm was disposed between the hollow cylinders of cathode mix 3 and separator 4. Alkaline batteries were produced by the same specification as one in Examples 1 to 6 except the conditions above according to the same production procedure as that of the alkaline battery 100A as described above.

The results of the measurements in Examples 13 to 18 under the test condition above are shown in Table 16. Comparative Example 1 in Table 16 is the same as described above.

	TABLE 16
			Capacity
		Thickness of stainless steel	retention
		expand metal (μm)	ratio (%)
	Example 13	30	58
	Example 14	50	69
	Example 15	100	74
	Example 16	150	81
	Example 17	200	71
	Example 18	250	48
	Comparative	None	57
	Example 1

Correlation curves in FIG. 17 between the thickness of the porous metal cylinder and capacity retention ratio are obtained from the results of the measurement in Tables 14 to 16. FIG. 17 shows that the thickness of the porous metal cylinder 12 that permits the capacity retention ratio of the alkaline battery 100A to be large after 50 cycles of charge-discharge is in the range of 50 to 200 μm. A higher capacity retention ratio is obtained when the thickness is in the range of 100 to 150 μm particularly in the range described above. While deterioration of the capacity due to the charge-discharge cycles depends on the thickness of the porous metal cylinder 12, the cathode active material is swelled as if there is no porous metal cylinder 12 when the thickness of the cylinder is less than 50 μm. Since the distance between the cathode mix 3 and separator 4 is large when the thickness is larger than 200 μm, it is difficult to transfer water efficiently from the cathode to the anode. Accordingly, restricting the thickness of the porous metal cylinder 12 to the range of 50 to 200 μm allows swelling of the cathode due to water generated at the cathode in the charging process to be suppressed while water generated by charging to be efficiently transferred to the anode, thereby obtaining an alkaline battery having improved cycle characteristics.

The alkaline batteries 100A in Examples 19 to 21 comprising different materials of the porous metal cylinder 12 were measured.

In Example 19, a nickel punching metal having a thickness of 100 μm and formed into a hollow cylinder with an outer diameter of 9.0 mm and a height of 40 mm as the porous metal cylinder 12 was disposed between the cathode mix 3 and separator 4 each formed into a hollow cylinder. Battery was produced by the same specification as one in Examples 1 to 6, except for the material of the cylinder described above, according to the same production procedure as that of the alkaline battery 100A as described above.

In Example 20, a copper punching metal having a thickness of 100 μm and formed into a hollow cylinder with an outer diameter of 9.0 mm and a height of 40 mm as the porous metal cylinder 12 was disposed between the cathode mix 3 and separator 4 each formed into a hollow cylinder. Battery was produced by the same specification as one in Examples 1 to 6, except for the material of the cylinder described above, according to the same production procedure as that of the alkaline battery 100A as described above.

In Example 21, a tin punching metal having a thickness of 100 μm and formed into a hollow cylinder with an outer diameter of 9.0 mm and a height of 40 mm as the porous metal cylinder 12 was disposed between the cathode mix 3 and separator 4 each formed into a hollow cylinder. Battery was produced by the same specification as one in Examples 1 to 6, except for the material of the cylinder described above, according to the same production procedure as that of the alkaline battery 100A as described above.

The results of the measurements of the batteries in Examples 19 to 21 under the test conditions above are shown in Table 17. Comparative example 1 in Table 17 is the same as described above.

	TABLE 17
		Capacity
	Material of porous metal	retention
	cylinder (thickness 100 μm)	ratio (%)
	Example 19	Nickel punching metal	81
	Example 20	Copper punching metal	76
	Example 21	Tin punching metal	73
	Comparative	None	57
	Example 1

The relationship between the kinds of the metal of the porous metal cylinder 12 and capacity retention ratio in FIG. 18 is obtained from the results of the measurements in Table 17 and Example 3. FIG. 18 clearly shows that the capacity retention ratio is increased by using each kind of the metal as compared to the capacity retention ratio in Comparative Example 1. The capacity retention ratio is higher by using the nickel punching metal and stainless steel punching metal among the metals described above.

Thus, the alkaline battery is composed of a cathode comprising the cathode mix 3 formed into a hollow cylinder and an anode comprising the anode mix 5 filled in the hollow part of the cathode with interposition of the bottom-sealed separator 4 so that swelling of the cathode due to water generated at the cathode in the charging process can be suppressed by providing the porous cylinder 12 comprising a punching metal, a metal net or an expand metal made of stainless steel, nickel, copper and tin with a thickness of 50 to 200 μm between the cathode mix 3 and separator 4. This allows water generated at the cathode by charging to be efficiently transferred to the anode, thereby suppressing the deterioration of the capacity by the charge-discharge cycles to obtain an alkaline battery improved in the cycle characteristics.

The alkaline batteries in the embodiments above can be applied for primary and secondary batteries.

While the discharge capacity decreases when the β-nickel oxy-hydroxide has no spherical shape of particle, an effect for improving the charge characteristics under a heavy load can also be obtained by specifying the particle diameter distribution within a specified range as described above.

While the cylindrical alkaline batteries have been described in the embodiments above, the present invention is also applicable to other alkaline battery such as a flat alkaline battery.

The effect obtained by specifying the particle diameter distribution as described in the embodiments above can be valid in the measurer rent under the light load discharge conditions.

While fluorinated resins PTFE, FEP and PCTFE have been used in the third embodiment above, the resin is not restricted thereto, and other fluorinated resins may be used.

While the punching metal, metal net and expand metal have been used for the porous metal cylinder in the fifth embodiment, the metal material is not restricted thereto, and other porous metal cylinders may be used.

While stainless steel, nickel, copper and tin have been used alone in the fifth embodiment, the same effect is obtainable by using a metal coated with another metal on the surface such as stainless steel plated with nickel.

While the alkaline batteries having a cathode comprising the cathode mix 3 formed into a hollow cylinder and an anode comprising the anode mix 5 filled in the hollow part of the cathode with interposition of a bottom-sealed cylindrical separator 4 have been described in the embodiments above, the alkaline battery according to the invention is not restricted thereto. Instead, the present invention is applicable to an alkaline battery having an anode comprising an anode mix formed into a hollow cylinder and a cathode comprising a cathode mix filled in the hollow part of the anode with interposition of a bottom-sealed cylindrical separator.

In the alkaline battery according to the present invention, the β-nickel oxy-hydroxide produced by chemical oxidation and having mean particle size in the range of 5 to 50 μm is used as the cathode active material, thereby obtaining the alkaline battery having excellent discharge characteristics under a heavy load.

In the alkaline battery according to the present invention, a cathode active material comprising a mixture of β-nickel oxy-hydroxide produced by chemical oxidation and manganese dioxide is used, the β-nickel oxy-hydroxide particles have a mean particle size in the range of 5 to 50 μm, and the manganese dioxide particles have a mean particle size in the range of 10 to 70 μm, thereby obtaining an alkaline battery excellent in discharge characteristics under a heavy load, increasing the charge capacity of the cathode without decreasing the reaction area in the cathode/anode, and reducing the production cost of the alkaline battery by using manganese dioxide.

The discharge characteristics under a heavy load and storage characteristics are also improved by adjusting the cumulative pore volume in connection with pore sizes of not larger than 0.5 μm in the β-nickel oxy-hydroxide particles in the range of 10 to 60 μl/g.

The discharge characteristics under a heavy load and storage characteristics are improved by using the cathode active material as a mixture of β-nickel oxy-hydroxide and manganese dioxide, and by adjusting the cumulative pore volume in connection with pore sizes of not larger than 0.5 μm in the β-nickel oxy-hydroxide particles in the range of 10 to 60 μl/g.

An alkaline battery excellent in storage characteristics is obtained by using β-nickel oxy-hydroxide prepared by chemical oxidation and having approximately spherical shape of particle as the cathode active material and by restricting a sulfuric acid radical content therein in the range of 0.5% or less by weight.

The alkaline battery excellent in the cycle characteristics according to the present invention is obtained by adding a given quantity of a fluorinated resin in the cathode mix containing β-nickel oxy-hydroxide as a binder.

Swelling of the cathode due to water generated at the cathode in the charging process is suppressed by providing a porous metal cylinder with a given thickness between the cathode and separator. Consequently, the water generated at the cathode is efficiently transferred to the anode to enable deterioration of the capacity by the charge-discharge cycle to be suppressed and the cycle characteristics to be improved.

Industrial Applicability

As described above, the alkaline battery according to the present invention is favorable for applying it to primary and secondary storage batteries as power sources of electronic appliances and the like.

Claims

1. An alkaline battery comprising a cathode mix containing β-nickel oxy-hydroxide as a cathode active material, an anode mix containing zinc as a main component of an anode active material, and an alkaline solution as an electrolyte, wherein said β-nickel oxy-hydroxide is obtained by chemical oxidation of nickel hydroxide; wherein said β-nickel oxy-hydroxide has a mean particle size in the range of 5 to 50 μm; and wherein said β-nickel oxy-hydroxide has an approximately spherical shape of particle.

2. The alkaline battery according to claim 1, wherein cumulative pore volume in connection with pore sizes of not larger than 0.5 μm in said β-nickel oxy-hydroxide particles is in the range of 10 to 60 μl/g.

3. The alkaline battery according to claim 1, wherein proportion of sulfuric acid radial contained in said β-nickel oxy-hydroxide is in the range of not larger than 0.5% by weight.

4. The alkaline battery according to claim 1, wherein a bottom-sealed cylindrical battery is formed.

5. An alkaline battery comprising a cathode mix containing β-nickel oxy-hydroxide and manganese dioxide as cathode active materials, an anode mi containing zinc as a main component of an anode active material, and an alkaline solution as an electrolyte, wherein said β-nickel oxy-hydroxide is obtained by chemical oxidation of nickel hydroxide; wherein said β-nickel oxy-hydroxide has a mean particle size in the range of 5 to 50 μm; and wherein said manganese dioxide has a mean particle size in the range of 10 to 70 μm.

6. The alkaline battery according to claim 5, wherein said β-nickel oxy-hydroxide has an approximately spherical shape of particle.

7. The alkaline battery according to claim 6, wherein cumulative pore volume in connection with pore sizes of not larger than 0.5 μm in mixed particles of said β-nickel oxy-hydroxide particles and said manganese dioxide is in the range of 10 to 60 μl/g.

8. The alkaline battery according to claim 6, wherein proportion of sulfuric acid radial contained in said 1-nickel oxy-hydroxide is in the range of not larger than 0.5% by weight.

9. The alkaline battery according to claim 6, wherein a bottom-sealed cylindrical battery is formed.

10. An alkaline battery comprising a cathode mix containing β-nickel oxy-hydroxide and a conductive material as a cathode active material, an anode mix containing zinc as a main component of an anode active material, an alkaline solution as an electrolyte, and a separator disposed between a cathode comprising said cathode mix and an anode comprising said anode mix, wherein said β-nickel oxy-hydroxide is obtained by chemical oxidation of nickel hydroxide, and wherein said cathode mix includes a fluorinated resin as a binder.

11. The alkaline battery according to claim 10, wherein an amount of said added fluorinated resin is in the range of 0.1 to 1.0% by weight.

12. The alkaline battery according to claim 10, wherein said fluorinated resin is any one of polytetrafluorcethylene (PTFE), tetrafluoroethylene-hexafluoropropylene copolymer (FEP) and polychlorotrifluoroethylene (PCTFE).

13. The alkaline battery according to claim 10, wherein a porous metal cylinder is provided between said cathode and said separator.

14. The alkaline battery according to claim 13, wherein said porous metal cylinder has a thickness of 50 to 200 μm, and is formed of at least a kind of metal selected from the group constituting of stainless steel, nickel, copper, and tin.

15. The alkaline battery according to claim 13, wherein said porous metal cylinder comprises any one of punching metal, metal net, and expand metal.