The present invention relates to the use of alkoxylated polyglycerols preparable by polycondensation of glycerol and subsequent alkoxylation for demulsifying water-oil emulsions, in particular in the production of crude oil.
During its recovery, crude oil is produced as an emulsion with water. Before the crude oil is further processed, these crude oil emulsions must be demulsified into the oil and water constituents. For this purpose, use is generally made of petroleum demulsifiers. Petroleum demulsifiers are interface-active compounds which are able to effect the required separation of the emulsion constituents within a short time.
Disclosed petroleum demulsifiers are, in U.S. Pat. No. 321,146, alkylene oxide block copolymers and, in U.S. Pat. No. 5,445,765, alkoxylated polymines. These can be used as individual components, in mixtures with other demulsifiers, or else as crosslinked products. Crosslinkings are generally carried out by reactions of the individual demulsifier components with bifunctional compounds such as diepoxides or diisocyanates. Such crosslinked compounds are disclosed in U.S. Pat. Nos. 5,759,409 and 5,981,687.
The use of alkoxylated glycerol as demulsifying constituent in lubricating oils has been described in DD-229006. Here, glycerol is reacted with alkylene oxides either to give a block copolymer or a random copolymer.
Alkoxylated polyglycerols are known per se. They are described in the prior art for various applications. For example, in U.S. Pat. No. 5,502,219, alkoxylated polyglycerols were esterified in order to prepare a low-calorie substitute for plant oils. In U.S. Pat. No. 4,061,684, the alkoxylated polyglycerols were esterified and used as gels which swell in water. Alkoxylated polyglycerols which have been reacted with alpha-olefin epoxides act, according to WO-98/03243, as antifoams. The sulfation of alkoxylated polyglycerols leads to substances which are used in hair shampoos, as disclosed in U.S. Pat. No. 4,263,178. However, alkoxylated polyglycerols have still not been used as demulsifiers.
The various properties (e.g. asphaltene and paraffin content) and proportions of water in various crude oils make it imperative to further develop the existing petroleum demulsifiers. In particular, a low dosing rate of the demulsifier to be used as well as the relatively high effectiveness to be strived for is at the forefront from an economic and ecological point of view.
The object was thus to develop novel petroleum demulsifiers which are superior in their effect to the already known alkoxylated polyalkylene glycols or polymines, and can be used in an even lower concentration. Surprisingly, it has been found that alkoxylated polyglycerols exhibit an excellent effect as petroleum demulsifiers even at a very low concentration. The invention therefore provides for the use of alkoxylated polyglycerols with a molecular weight of from 250 to 100,000 units which comprise 2 to 100 glycerol units whose free OH groups are alkoxylated with C2–C4-alkylene oxide groups or a mixture of such alkylene oxide groups so that the alkoxylated polyglycerol has a degree of alkoxylation of from 1 to 100 alkylene oxide units per free OH group, for demulsifying oil/water emulsions in amounts of from 0.0001 to 5% by weight, based on the oil content of the emulsion to be demulsified.
These alkoxylated polyglycerols are obtainable from polyglycerols having 2 to 100 glycerol units by alkoxylation of the free OH groups with a C2–C4-alkylene oxide or a mixture of such alkylene oxides in molar excess, such that the alkoxylated polyglycerol has said degree of alkoxylation.
The preparation of polyglycerol is known in the prior art and takes place generally by acid- or alkali-catalyzed condensation of glycerol. The reaction temperature is generally between 150 and 300° C., preferably 200 to 250° C. The reaction is normally carried out at atmospheric pressure. Examples of catalyzing acids are HCl, H2SO4, sulfonic acids or H3PO4, and bases which may be mentioned are NaOH or KOH, which are used in amounts of from 0.1 to 50% by weight, based on the weight of the reaction mixture. The condensation generally requires 3 to 10 hours. Polyglycerols can be depicted by formula 1.
In formula 1, n is the degree of condensation, i.e. the number of glycerol units. n increases with increasing reaction time and is determined by means of the OH number.
The polyglycerols obtained from the condensation are then alkoxylated with one or more C2–C4-alkylene oxides, preferably ethylene oxide (EO) or propylene oxide (PO). The alkoxylating agent is used in molar excess. The alkoxylation takes place, as known in the prior art, by reaction of the polyglycerols with an alkylene oxide under an increased pressure of generally 1.1 to 20 bar at temperatures of from 50 to 200° C. The alkoxylation takes place on the free OH groups of the polyglycerols. The amount of alkylene oxide used is sufficient for the average degree of alkoxylation to be between 1 and 100 alkylene oxide units per free OH group. Average degree of alkoxylation is understood here as meaning the average number of alkoxy units which is positioned on each free OH group. It is preferably 2 to 70, in particular 5 to 50.
Preferably, the alkoxylation is carried out with a mixture of EO and PO. The ratio of EO to PO in the alkoxylated polyglycerol is preferably between 1:2 and 1:10.
The alkoxylated polyglycerol obtained following condensation and alkoxylation preferably has a molecular weight of from 500 to 50,000 units, preferably from 1,000 to 10,000 units.
The alkoxylated polyglycerols prepared by the described process can be depicted by the following structure (formula 2):
(AO)k,l,mO are the alkoxylated OH radicals in which AO is a C2–C4-alkylene oxide unit and k, l, m are the degrees of alkoxylation. n is the degree of condensation of the glycerol. n is preferably a number from 3 to 50, particularly preferably 4 to 30.
The present invention preferably provides for the use of the alkoxylated polyglycerol as demulsifiers for oil/water emulsions in the recovery of crude oil.
For use as crude oil demulsifiers, the alkoxylated polyglycerols are added to the water-oil emulsions, which preferably takes place in solution. Preferred solvents for the alkoxylated polyglycerols are paraffinic or aromatic solvents. The alkoxylated polyglycerols are used in amounts of from 0.0001 to 5% by weight, preferably 0.0005 to 2% by weight, in particular 0.0008 to 1% by weight and specifically 0.001 to 0.1% by weight, based on the oil content of the emulsion to be demulsified.
Preparation of Pentadecaglycerol
100.0 g of glycerol and 3.7 g of NaOH (18% strength) were mixed in a 500 ml three-necked flask fitted with contact thermometer, stirrer and water separator. With stirring and nitrogen blanketing, the reaction mixture was heated rapidly to 240° C. At this temperature, the water of reaction was distilled off over 8 h. The product was evaporated to dryness on a rotary evaporator (yield: 67.3 g) and the molar mass was analyzed by GPC (with standard polyethylene glycol). The chain length n was determined via the OH number.
Preparation of Decaglycerol
100.0 g of glycerol and 3.7 g of NaOH (18% strength) were mixed in a 500 ml three-necked flask fitted with contact thermometer, stirrer and water separator. With stirring and nitrogen blanketing, the reaction mixture was heated rapidly to 240° C. At this temperature, the water of reaction was distilled off over 5 h. The product was evaporated to dryness on a rotary evaporator (yield: 74.9 g) and analyzed by GPC. The chain length n was determined via the OH number.
Preparation of Pentaeicosaglycerol
100.0 g of glycerol and 3.7 g of NaOH (18% strength) were mixed in a 500 ml three-necked flask fitted with contact thermometer, stirrer and water separator. With stirring and nitrogen blanketing, the reaction mixture was heated rapidly to 240° C. At this temperature, the water of reaction was 10 distilled off over 12 h. The product was evaporated to dryness on a rotary evaporator (yield: 58.4 g) and analyzed by GPC. The chain length n was determined via the OH number.
Pentacontanglycerol
100.0 g of glycerol and 3.7 g of NaOH (18% strength) were mixed in a 500 ml three-necked flask fitted with contact thermometer, stirrer and water separator. With stirring and nitrogen blanketing, the reaction mixture was heated rapidly to 240° C. At this temperature, the water of reaction was distilled off over 20 h. The product was evaporated to dryness on a rotary evaporator (yield: 54.9 g) and analyzed by GPC. The chain length n was determined via the OH number.
Alkoxylation of the Polyglycerols
Ethylene Oxide
The polyglycerols described above were introduced into a 1 l glass autoclave and the pressure in the autoclave was adjusted to about 0.2 bar above atmospheric pressure with nitrogen. Heating was slowly carried out to 140° C. and, after this temperature had been reached, the pressure was again adjusted to 0.2 bar above atmospheric pressure. Then, at 140° C., the desired amount of EQ was metered in, during which the pressure did not exceed 4.5 bar. When the addition of EO was complete, the mixture was left to after-react for a further 30 minutes at 140.degree. C.
Propylene Oxide
The polyglycerols described above were introduced into a 1 l glass autoclave and the pressure in the autoclave was adjusted to about 0.2 bar above atmospheric pressure with nitrogen. Heating was slowly carried out to 130° C. and, after this temperature had been reached, the pressure was again adjusted to 0.2 bar above atmospheric pressure. Then, at 130° C. , the desired amount of PO was metered in, during which the pressure did not exceed 4.0 bar. When the addition of PO was complete, the mixture was left to after-react for a further 30 minutes at 130°C.
The degree of alkoxylation was determined by means of 13C-NMR
Determination of the Demulsifying Effectiveness of Petroleum Demulsifiers
To determine the effectiveness of a demulsifier, the water separation from a crude oil emulsion per time, and also the dewatering and desalting of the oil were determined. For this, demulsifying glasses (tapered, graduated glass bottles with screw lids) were charged in each case with 100 ml of the crude oil emulsion, in each case a defined amount of the demulsifier was metered in just below the surface of the oil emulsion using a micropipette, and the demulsifier was mixed into the emulsion by intensive shaking. The demulsifying glasses were then placed in a conditioning bath (30° C. and 50° C.) and water separation was monitored.
During demulsification and after it had finished, samples were taken from the oil from the upper section of the demulsifying glass (so-called top oil), and the water content was determined in accordance with Karl Fischer and the salt content was determined conductometrically. In this way, it was possible to assess the novel demulsifiers according to water separation and also dewatering and desalting of the oil.
Demulsifying action of the demulsifiers described
| Number | Date | Country | Kind |
|---|---|---|---|
| 101 07 880 | Feb 2001 | DE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP02/01376 | 2/9/2002 | WO | 00 | 8/7/2003 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO02/066136 | 8/29/2002 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2499365 | De Groote et al. | Mar 1950 | A |
| 2552528 | De Groote | May 1951 | A |
| 2944982 | De Groote et al. | Jul 1960 | A |
| 3110736 | De Groote et al. | Nov 1963 | A |
| 3110737 | De Groote et al. | Nov 1963 | A |
| 3752657 | Richardson | Aug 1973 | A |
| 3954808 | Elliott et al. | May 1976 | A |
| 4061684 | Helfert et al. | Dec 1977 | A |
| 4263178 | Guth | Apr 1981 | A |
| 4265774 | Langdon | May 1981 | A |
| 4321146 | McCoy et al. | Mar 1982 | A |
| 4342657 | Blair, Jr. | Aug 1982 | A |
| 4414035 | Newberry et al. | Nov 1983 | A |
| 4431565 | Billenstein et al. | Feb 1984 | A |
| 4537701 | Oppenlaender et al. | Aug 1985 | A |
| 5021498 | Stephenson et al. | Jun 1991 | A |
| 5322886 | Sauterey | Jun 1994 | A |
| 5445765 | Elfers et al. | Aug 1995 | A |
| 5460750 | Diaz-Arauzo | Oct 1995 | A |
| 5494607 | Manek et al. | Feb 1996 | A |
| 5502219 | Harris | Mar 1996 | A |
| 5525201 | Diaz-Arauzo et al. | Jun 1996 | A |
| 5759409 | Knauf et al. | Jun 1998 | A |
| 5981687 | Breen et al. | Nov 1999 | A |
| 6025427 | Cabrera | Feb 2000 | A |
| 6465528 | Holtrup et al. | Oct 2002 | B1 |
| 20030235598 | Klug et al. | Dec 2003 | A1 |
| Number | Date | Country |
|---|---|---|
| 1 184 865 | Apr 1985 | CA |
| 2029465 | May 1991 | CA |
| 2075749 | Feb 1993 | CA |
| 23 60 020 | Jun 1975 | DE |
| 229 006 | Oct 1985 | DE |
| 42 06 429 | Sep 1993 | DE |
| 195 03 099 | Aug 1995 | DE |
| 0 279 384 | Aug 1988 | EP |
| 0 457 642 | Nov 1991 | EP |
| 0 894 809 | Feb 1999 | EP |
| 1 044 996 | Oct 2000 | EP |
| 2 118 937 | Nov 1983 | GB |
| 2089593 | Sep 1997 | RU |
| 2151780 | Jun 2000 | RU |
| 2152976 | Jul 2000 | RU |
| 2154090 | Aug 2000 | RU |
| WO 9803243 | Jan 1998 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20040072916 A1 | Apr 2004 | US |