Patent Application
20190067684
The present invention relates to an all-solid-state lithium rechargeable cell, also referred to as an “all-solid-state lithium rechargeable battery” (hereinafter abbreviated to “ASSLRB”).
All-solid-state lithium rechargeable batteries contain exclusively solid materials, and in particular solid-state electrolytes. However. ASSLRBs having traditional oxide materials (such as LiCoO2) as cathodes often suffer from low theoretical capacities, as well as high interfacial resistance and lows energy densities. Therefore, it is essential to develop new cathode materials for ASSLRBs, which possess high energy density on material level to meet the requirements for energy storage systems and/or electric vehicles.
After intensive study, the inventors have surprisingly found that a composite of VS4 and graphene (hereinafter abbreviated to “VS4/graphene composite”) can be used to provide a novel cathode for all-solid-state lithium rechargeable batteries.
Based on such discovery, an all-solid-state lithium rechargeable cell is provided which comprises:
a) a cathode, wherein the cathode comprises:
b) a lithium-based anode.
Optionally, the cathode may further comprise: a3) a conductive additive and/or a4) a binder.
Optionally, the cell may further comprise a solid electrolyte located between the cathode and the anode.
For the first time, the inventors propose that VS4/graphene composite can be used in the cathodes of ASSLRBs. In particular, the inventors provide a novel ASSLRB by employing a VS4/graphene composite in combination with a solid catholyte as the cathode, and employing a lithium-based material as the anode. Surprisingly, it is found that the ASSLRBs of the present disclosure exhibit high initial discharge capacities, high initial Coulombic efficiencies, good reversible capacities, excellent cycling stabilities, high energy densities as well as outstanding safeties.
These and other features, aspects and advantages of the present disclosure will become evident to those skilled in the art from the following description of various examples taken in conjunction with the accompanying drawings.
These drawings are shown here to help illustrate various examples of the disclosure, and as such, are not necessarily drawn to scale.
Throughout this disclosure, all the scientific and technical terms, unless otherwise indicated, shall have the same meanings as those known to a person skilled in the art. Where there is inconsistency, the definition provided in the present disclosure should be taken.
It should be understood that the detailed description of all materials, processes, examples and drawings are presented for the purposes of illustration, and therefore, unless expressly specified otherwise, are not construed as limitations of the present disclosure.
Herein, the terms “cell” and “battery” may be interchangeably used. The terms “all-solid-state lithium rechargeable cell (or battery)” may also be abbreviated to “cell”, “battery” or “ASSLRB”.
Herein, the term “comprising” means that other ingredients or other steps which do not affect the final effect can be included. This term encompasses the terms “consisting of” and “consisting essentially of”. The product and process according to the present disclosure can comprise, consist of, and consist essentially of the essential technical features and/or limitations of the present disclosure described herein, as well as any additional and/or optional ingredients, components, steps, or limitations described herein.
The use of the terms “a”. “an” and “the” and similar referents in the context of describing the subject matter of this application (especially in the context of the following claims) are to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context.
The term “electrolyte” means an electrolyte located between the cathode and the anode. The term “catholyte” specifically means an electrolyte contained in the cathode. The “catholyte” and the “electrolyte” in the same cell may be formed from the same or different materials.
Unless otherwise specified, every numerical range in this context intends to include both endpoints and any numbers and sub-ranges falling within said numerical ranges.
Unless specially indicated, all materials and agents used in the present disclosure are commercially available.
Examples of the present disclosure are described in detail as follows.
a): Cathode
The cathode may comprise:
Optionally, the cathode may further comprise: a3) a conductive additive and/or a4) a binder.
According to some examples of the present disclosure, the cathode comprises:
According to some examples of the present disclosure, the cathode comprises:
a1): VS4/graphene composite
According to some examples of the present disclosure, the cathode may comprise component a1): a VS4/graphene composite as the cathode active material. Owing to the high theoretical capacity of VS4 and the high conductivity of graphene, the VS4/graphene composite exhibits a high energy density.
Preferably, the VS4/graphene composite may have a structure that VS4 particles chemically bond with or physically embed in graphene sheets. Preferably, VS4 particles are uniformly distributed on the graphene sheets. Preferably. VS4 is a vanadium sulfide in patronite form.
According to some examples of the present disclosure, the graphene is a reduction product of graphene oxide.
Preferably. VS4/graphene composite is in the form of powders.
According to some examples of the present disclosure, the content of the graphene may be more than 0% by weight but no more than 20% by weight, and the content of the VS4 particles may be no less than 80% by weight but less than 100% by weight, based on the total weight of the VS4/graphene composite.
a2): Solid Catholyte
According to some examples of the present disclosure, the cathode may comprise component a2): a solid catholyte. The solid catholyte may advantageously improve the transport of lithium ions through the aforementioned VS4/graphene composite and also through the whole cathode.
There is no specific limitation to the solid catholyte, and those which are known for use in lithium rechargeable batteries may be used so long as they are lithium ion-conducting materials. For example, the solid catholyte may be polyethylene oxide (PEO), a lithium ion-conducting sulfide, a lithium ion-conducting chloride or their combination. In some examples, the lithium ion-conducting sulfides may be composites comprising lithium sulfides and phosphorus sulfides, and the composite may be optionally doped with some oxides for modification, such as Li10GeP2S12, Li3PS4. Li7P3S11, Li8P2S9. Li3.25Ge0.25P0.75S4, Li10GeP2S12, 70 Li2S-29P2S5-1P2O5, Li2S—P2S5 and any combinations thereof. Li7La3Zr2O12 is another example of the solid catholyte.
Preferably, the solid catholyte is in the form of powders, or is ground into powders.
a3): Conductive Additive
Optionally, the cathode according to the present disclosure may comprise component a3): a conductive additive. The conductive additive may increase the conductivity and/or capacity of the cathode.
There is no specific limitation to the conductive additives, and those which are known for use in lithium rechargeable batteries may be used. Preferably, the conductive additive may be selected from carbon black, super P, acetylene black, Ketjen black, graphite, graphene, carbon nanotubes, vapour grown carbon fibers (VGCF) and their combinations; with super P being more preferable. For example, super P may be commercially available from Timical.
Preferably, the conductive additive is in the form of powders, or is ground into powders.
a4): Binder
Optionally, the cathode according to the present disclosure may comprise component a4): a binder. With the help of the binder, not only the components of the cathode are firmly bound together, but also the whole cathode is adhesively connected with the anode or solid electrolyte (if present). Such adhesion may suppress the volumetric change of the cathode as well as the whole ASSLRB during repeated charge/discharge cycles, and thus improves the electrochemical properties, especially the cycling performance of the ASSLRB.
Preferably, the binder may be selected from polyvinylidone fluoride (PVDF), polyacrylic acid (PAA) and their combination. Preferably, binders suitable for the present disclosure do not contain carboxymethyl cellulose (CMC) since CMC is often used in the form of an aqueous solution.
b): Anode
There is no specific limitation to the anode material suitable for the present disclosure, and those lithium-based electrode materials which are known for use in lithium rechargeable batteries may be used so long as they are compatible with and do not adversely influence the effect of the cathode according to the present disclosure. Examples of useful lithium-based anode include, but not limited to, lithium metal; lithium alloys, such as Li—In alloy; stacks consisting of a layer of lithium metal and one or more layers of other metals which are different from lithium, such as Li—In stack; pre-lithiated graphite, for example, graphite which contains a desired amount of lithium intercalated or absorbed therein; pre-lithiated silicon, for example, silicon which contains a desired amount of lithium intercalated or absorbed therein.
For example, in the case where Li metal is used as the anode, the discharge capacity and discharge platform may be increased, and thus the energy density may be improved.
c): Solid Electrolyte
Optionally, the ASSLRBs according to the present disclosure may comprise a solid electrolyte located between the cathode and the anode. The solid electrolyte and the aforementioned solid catholyte may be formed from identical or different materials.
When compared with liquid electrolytes, solid-state electrolytes imparts several advantages to the ASSLRBs. For example, comparing with liquid-electrolyte lithium ion rechargeable batteries which inevitably contain at least 30 vol. % to 35 vol. % of pores, the ASSLRBs show the possibility of higher volumetric energy density since ASSLRBs could be 100% dense. The ASSLRBs could also show a higher gravimetric energy density because of the possible usage of high energy lithium-based anodes. The high operation temperature, e.g., about 80 to about 100° C., of ASSLRBs additionally contributes to an even higher energy density. In addition, higher safety is another important advantage of the ASSLRBs over liquid-electrolyte lithium ion rechargeable batteries.
In addition, the solid electrolyte may also serve as a separator between the cathode and anode. The solid electrolyte may also improve the transport of lithium ions between the cathode and the anode.
Furthermore, since the ASSLRBs of the present disclosure contain no liquid electrolyte, undesirable reactions between a liquid electrolyte and a cathode and/or an anode may thus be avoided and a higher level of safety is ensured.
There is no specific limitation to the solid electrolyte, and those which are known for use in lithium rechargeable batteries may be used so long as they are lithium ion-conducting materials. For example, the solid catholyte may be polyethylene oxide (PEO), a lithium ion-conducting sulfide, a lithium ion-conducting chloride or their combination. The examples described above for the solid catholyte also apply to the solid electrolyte.
Preferably, the solid electrolyte c) may be in the form of a single-layer. The solid electrolyte c) may also be in the form of a two-layer stack, or a multi-layer stack containing three or more layers, wherein these layers may be formed from identical or different layers, preferably from different layers. For example, the solid electrolyte may be a two-layer stack consisting of a layer of Li10GeP2S12 and a layer of lithium sulfide-phosphorus sulfide-phosphorus oxide (Li2S—P2S5—P2O5). Preferably, the lithium sulfide-phosphorus sulfide-phosphorus oxide may be 70 Li2S-29 P2S5-1 P2O5. In the case where a two-layer or multi-layer stack is adopted for the solid electrolyte, a polarization phenomenon may be effectively solved.
All-Solid-State Lithium Rechargeable Battery
The all-solid-state lithium rechargeable cell is provided which comprises:
a) a cathode, wherein the cathode comprises:
b) a lithium-based anode.
Optionally, the cathode may further comprise a solid electrolyte located between the cathode and the anode.
In addition, the ASSLRBs of the present disclosure may optionally contain further additives, so long as they do not adversely affect the electrochemical properties of the batteries. The further additives may be contained within or between any of the cathode, the anode and the solid electrolyte (if present).
The ASSLRBs according to the present disclosure may be used in energy storage systems and electric vehicles.
[Synthesis of Graphene Oxide Solution]
1.5 g of graphite powder (SP-1, Bay carbon) and 1.5 g of KNO3 (Sigma Aldrich, ≥99.0%) were taken in 69 ml of H2SO4 (Sigma Aldrich, 98.0%) at 0° C., and 9 g of KMnO4 (Sigma Aldrich, ≥99.0%) was added gradually. The mixture was then stirred at 35° C. for 6 h. and 120 ml of deionized (DI) water was added. After 15 min, the reaction was terminated by the addition of a solution of 300 ml of deionized water and 9 ml of H2O2(SAMCHUN pure chemical, 34.5% extra pure), and the color of the mixture changed to yellow. The mixture was filtered and washed with 500 ml of HCl (SAMCHUN pure chemical, 10% by weight) solution. The resulting graphite oxide was suspended in 200 ml of distilled water again, followed by dialysis (dialysis membrane: Spectrum Laboratories. MWCO-21-14.000) to remove excess HCl. The graphite oxide is exfoliated to give about 2.15 mg/mL graphene oxide solution by a high-pressure homogenizer at 15,000 psi. After exfoliation, the solution was centrifuged at 400 rpm for 10 min to remove the non-exfoliated graphite oxide, and the top supernatant graphene oxide solution was used for the synthesis of VS4/graphene composite.
[Synthesis of VS4/Graphene Composite]
1.1 g of sodium orthovanadate (Na3VO4, Sigma-Aldrich, ≥90%) and 2.25 g of thioacetamide (C2H5NS, aladdin, ≥99%) were dissolved in 20 ml of deionized water. Then, 37 ml of graphene oxide solution (2.15 mg/ml) was added to the mixture and a total volume of the solution was adjusted to 80 ml. After that, the solution was transferred to a 100 ml Teflon-lined stainless steel autoclave and heated to 160° C. for 24 h. After cooling naturally, the product was filtered, washed with DI water, and dried in vacuum at 110° C. for 24 h.
[Determination and Characterization of the Structure of the VS4/Graphene Composite]
The obtained sample was detected to demonstrate and characterize its structure. The detection results are summarized as below:
As shown in
In the high-resolution TEM (HRTEM) image shown in
As shown in
In
Therefore, the combination of
[Preparation of a Cathode]
45 mg of VS4/graphene, 50 mg of solid electrolyte Li10GeP2S12 and 5 mg of Super P (40 nm, available from Timical) were mixed together. The resultant mixture was ground by hand in a mortar placed in a glovebox under argon atmosphere so as to obtain a composite cathode material.
[Preparation of a Cell]
An all-solid-state cell for electrochemical measurements was fabricated as follow. The following two kinds of sulfide electrolytes (SEs): Li10GeP2S12 and 70 Li2S-29 P2S5-1 P2O5, were used to form a bilayer SE. The double SE layers was constructed by cold-pressing 50 mg 70 Li2S-29 P2S5-1 P2O5 SE on the top of 100 mg of cold pressed Li10GeP2S12 at 100 MPa, with the thickness of Li10GeP2S12 layer being 0.67 mm, and the thickness of 70 Li2S-29 P2S5-1 P2O5 layer being 0.23 mm, 5 mg of the composite cathode material was evenly spread on the top of the Li10GeP2S12 SE layer and pelletized by cold-pressing at 100 MPa. Lithium foil was then attached to the 70 Li2S-29 P2S5-1 P2O5 SE side at 200 MPa. Stainless steel plates were used as current collectors for both of the working electrode (i.e., the cathode) and the counter electrode (i.e., the anode). All pressing and experimental operations were done in a glovebox under argon. A cell is thus obtained.
[Electrochemical Measurements]
The cell thus obtained was galvanostatically cycled at room temperature within a voltage range of 0.5 to 3.0 V (vs. Li/Li+) at a current density of 0.1 mA cm−1. The cyclic voltammogram profiles and discharge/charge profiles of the cell in Example 1 were plotted in
Based on the CV test result and the discharge/charge profiles described later, the possible electrochemical reaction process of the VS4/graphene in the ASSLRB is shown as follow:
At initial discharge (see the 1st discharge curve):
2.0 V:VS4+3Li++3e−→Li3VS4
1.8/0.6 V:Li3VS4+5Li++5e−→4Li2S+V
Followed by (see the 1st to 3rd charge curves, as well as the 2nd and 3rd discharge curves):
1.9V/2.4 V:Li2S↔S+2Li++2e−
An ASSLiB was prepared in the same way as described above for Example 1, except that the weight ratio of VS4/graphene:Li10GeP2S12:Super P in the cathode is 5:5:0.
The electrochemical properties of the ASSLiB were measured in the same way as described above for Example 1. The measurement result is depicted in
An ASSLiB was prepared in the same way as described above for Example 1, except that the weight ratio of VS4/graphene:Li10GeP2S12:Super P in the cathode is 3:6:2.
The electrochemical properties of the ASSLiB were measured in the same way as described above for Example 1. The measurement result is depicted in
It can be seen that the ASSLRBs according to the present disclosure achieve high initial CEs and initial discharge capacities. Furthermore, the cycling performances of the ASSLRBs according to the present disclosure are also excellent.
Many modifications and variations of this disclosure can be made without departing from its spirit and scope, as will be apparent to those skilled in the art. The specific embodiments described herein are offered by way of example only, and the disclosure is to be limited only by the terms of the appended claims, along with the full scope of equivalents to which such claims are entitled.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2015/094126 | 11/9/2015 | WO | 00 |