This is the U.S. National Stage of PCT/JP2017/006977, filed Feb. 24, 2017, which in turn claims priority to Japanese Patent Application No. 2016-036523, filed Feb. 29, 2016, Japanese Patent Application No. 2016-066957, filed Mar. 30, 2016 and Japanese Patent Application No. 2016-069859 filed Mar. 31, 2016, the contents of each of these applications being incorporated herein by reference in their entireties.
The present invention relates to, for example, an all-solid state secondary, battery with a lithium-ion conductive solid electrolyte and a method for manufacturing the same.
In recent years, lithium-ion conductive solid electrolytes have been used as electrolytes for all-solid state secondary batteries. Such an all-solid state secondary battery includes a positive-electrode mixture layer, a negative-electrode mixture layer, a solid electrolyte layer, a positive-electrode current collector, and a negative-electrode current collector. In this configuration, the positive-electrode mixture layer is made of a positive-electrode active material and a lithium-ion conductive solid electrolyte. The negative-electrode mixture layer is made of a negative-electrode active material and a lithium-ion conductive solid electrolyte. The solid electrolyte layer is disposed between the positive-electrode mixture layer and the negative-electrode mixture layer. The positive-electrode current collector is metallic and is provided on a surface of the positive-electrode mixture layer. The negative-electrode current collector is metallic and is provided on a surface of the negative-electrode mixture layer.
For example, such an all-solid state secondary battery is manufactured follows: a powder positive-electrode mixture layer is charged into a cylindrical mold, a powder solid electrolyte is charged into the mold, a powder negative-electrode mixture layer is charged into the mold, and then the layers are pressure-molded under a high pressure with a retainer, e.g., a press pin.
According to the manufacturing method, a high-pressure press may generate an internal stress in the positive-electrode mixture layer and the negative-electrode mixture layer (hereinafter may be collectively referred to as “electrode mixture layer”). If a pressing force is released, the electrode mixture layer receives a frictional force caused by a difference in extension rate between the positive-electrode mixture and the negative-electrode mixture and between the positive-electrode current collector and the negative-electrode current collector. This may bend the battery in the thickness direction.
In a method for preventing such a bend, electrode mixture layers to be symmetrically deformed are disposed on both surfaces of a positive-electrode current collector and a negative-electrode current collector (hereinafter may be collectively referred to as “electrode current collector”) so as to prevent bending of a battery (for example, see Patent Literature 1). If such a battery is manufactured as a dry-type battery, electrode mixture layers are formed on both surfaces of an electrode current collector by, for example, electrostatic coating.
In the manufacturing method of Patent Literature 1, the electrode mixture layers are formed on both surfaces of the electrode current collector by electrostatic coating. Thus, in actual manufacturing, one surface electrostatically coated with an electrode mixture and then the current collector is inverted to electrostatically coat the other surface with an electrode mixture. When the current collector is inverted to electrostatically coat the other surface with the electrode mixture, the electrode mixture applied on one surface by electrostatic coating may fall off. In order to avoid such a problem, the electrode mixture may be applied to both surfaces of an erected electrode current collector by electrostatic coating. However, this may lead to an extremely complicated operation.
An object of the present invention is to provide a method for manufacturing an all-solid state secondary battery so as to easily prevent bending of the manufactured all-solid state secondary battery.
In order to solve the problem, a method for manufacturing an all-solid state secondary battery according to the present invention is a method for manufacturing an all-solid state secondary battery including a plurality of provisional battery bodies, the method including: forming each of the provisional battery bodies by pressing a positive-electrode mixture, a solid electrolyte, and a negative-electrode mixture that are stacked between a pair of electrode current collectors; and pressure-molding the stacked provisional battery bodies with the electrode current collectors facing each other, in which the electrode current collectors facing each other have rough surfaces.
According to the method for manufacturing the all-solid state secondary battery of the present invention, the stacked provisional battery bodies are pressure-molded such that the electrode current collectors with rough surfaces face each other, so that the rough surfaces are fit (or engaged) into each other and a force of separating the provisional battery bodies by bending is canceled out, achieving the all-solid state secondary battery that is not bent even if a molding pressure is removed. This can easily prevent bending of the all-solid state secondary battery during manufacturing.
An all-solid state secondary battery and a method for manufacturing the same according to an embodiment of the present invention will be described below in accordance with the accompanying drawings.
(Process of Forming a Provisional Battery Body)
First, as shown in
The positive-electrode mixture layer 2, the solid electrolyte layer 3, and the negative-electrode mixture layer 4 are powder layers. In
The laminate is pressed (temporarily pressed) with a required force (e.g., a force of 0.1 to 100 MPa) so as to form a provisional battery body 7. In this configuration, rough surfaces (hereinafter may be referred to as irregular parts) are formed on both sides (both surfaces) of the positive-electrode current collector 1 and both sides of the negative-electrode current collector 5. The press engages (or fits) a powder positive-electrode mixture and a powder negative-electrode mixture into the irregular parts on the inner surfaces (a surface in contact with the positive-electrode mixture layer 2 or the negative-electrode mixture layer 4) of the current collectors. At this point, the pressing force is large enough not to deform the provisional battery body 7, so that, the provisional battery body 7 is substantially flat.
(Pressure Molding Process)
Subsequently, as shown in
In this configuration, pressure molding on one of the provisional battery bodies 7 leads to bending of the provisional battery body 7. Referring to
In
In
In this configuration, an extension rate in the horizontal direction depends on the materials of the layers and the particle diameter and thickness of the electrode mixture layer. If the extension rate of the negative-electrode mixture layer 4 exceeds that of the positive-electrode mixture layer 2, the molding pressure p is removed and the horizontal internal stress b is released. Thus, as shown in
Thus, in the present embodiment, the pair of provisional battery bodies 7 is pressure-molded with the positive-electrode current collectors 1 in contact with each other as shown in
In this configuration, the positive-electrode mixture layer 2 is a mixture of a positive-electrode active material and a lithium-ion conductive inorganic solid electrolyte. The positive-electrode active material is an oxide, e.g., lithium cobalt oxide (LiCoO2), lithium nickel oxide (LiNiO2), or lithium manganese oxide (LiMnO2). The inorganic solid electrolyte is a sulfide, e.g., Li2S (80 mol %)-P2S5 (20 mol %). The mixture ratio of the positive-electrode active material and the solid electrolyte ranges from 95:5 to 30:70, e.g., 70:30.
The negative-electrode mixture layer 4 contains' a mixture of a negative-electrode active material and a lithium-ion conductive inorganic solid electrolyte. The negative-electrode active material is, for example, a natural graphite, a synthetic graphite, a graphite carbon fiber, a carbon material, e.g., a resin baked carbon, silicon, tin, or lithium. The solid electrolyte is Li2S (80 mol %)—P2S5 (20 mol %) like the positive-electrode mixture layer 2. The mixture ratio of the negative-electrode active material and the solid electrolyte ranges from 95:5 to 30:70, e.g., 60:40.
As has been discussed, the solid electrolyte layer 3 contains Li2S—P2S5 (a composition ratio of, for example, 80:20) that is an inorganic solid electrolyte of sulfide. The solid electrolyte has a distortion of at least 40% under compression at 1000 MPa.
The positive-electrode current collector 1 contains, for example, etched aluminum (also referred to as surface electrolization aluminum foil) having a thickness of 20 μm. Both surfaces of the etched aluminum are, roughened. Specifically, as shown in
The negative-electrode current collector 5 includes a thin copper plate having a thickness of about 18 μm with roughened surfaces, that is, irregular parts. Specifically, roughening is performed on the surface of the negative-electrode current collector 5 so as to deposit copper particles. The copper plate is also referred to as surface electrolization copper foil. In this case, the depth of the irregular parts can be set at to 20 μm (not larger than the thickness of the negative-electrode current collector 5 if the thickness is 20 μm or less) and is preferably set at 4 to 10 μm.
For example, the all-solid state secondary battery 10 is entirely circular or square in shape. The specific size of the all-solid state secondary battery 10 is about 30 to 300 mm (a diameter if the battery is circular). The all-solid state secondary battery 10 has a thickness of, for example, about 0.6 to 5.0 mm.
In the present embodiment, the provisional battery bodies 7 are pressure-molded while the positive-electrode current collectors 1 having the concave parts 8 face each other. The present invention is not limited to this configuration. For example, if the extension rate of the positive-electrode mixture layer 2 exceeds that of the negative-electrode mixture layer 4, a concave part is formed on the negative-electrode current collector 5. In this case, in order to place the concave parts facing each other, the negative-electrode current collectors 5 are caused to face each other instead of the positive-electrode current collectors 1.
The provisional battery bodies 7 are stacked with the concave parts facing each other. The present invention is not limited to this configuration. In other words, convex parts on the opposite sides from the concave parts may be stacked so as to face each other.
Moreover, the positive-electrode current collector 1 and the negative-electrode current collector 5 may face each other. In this case, in the pressure molding process, the pair of provisional battery bodies 7 tends to bend in the same direction and thus the bending of the all-solid state secondary battery may not be prevented. However, pressure molding on the provisional battery bodies 7 generates a frictional force between the electrode current collectors 1 and 5. The frictional force is generated when the rough surfaces of the electrode current collectors 1 and 5 bite into each other. When molding pressure is removed, an internal stress is released so as to bend the provisional battery bodies 7. This force is canceled out by the frictional force. Thus, the all-solid state secondary battery can be achieved without being bent.
Both surfaces of the electrode current collectors 1 and 5 are not always entirely roughened. Of the surfaces of the electrode current collectors 1 and 5, roughening may be performed only on the surfaces in contact with the electrode mixture layers 2 and 4 or the surfaces joined to the electrode current collectors 1 and 5 of the other provisional battery body 7. In other words, these surfaces need to be rough so that the powder of the electrode mixture layers 2 and 4 or the irregular parts of the electrode current collectors 1 and 5 of the other provisional battery body 7 bite into the irregular parts of the electrode current collectors 1 and 5 to obtain bonding power. Roughening is not necessary on the surfaces not in contact with the electrode mixture layers 2 and 4 and the surfaces not joined to the electrode current collectors 1 and 5 of the other provisional battery body 7.
A method for manufacturing an all-solid state secondary battery according to a second embodiment will be described below. The explanation of the same configurations as those of the first embodiment is omitted and different configurations will be mainly discussed below. In the first embodiment, the rough surfaces (irregular parts) are formed on the electrode current collectors 1 and 5. The irregular parts are fit into each other so as to prevent bending of the all-solid state secondary battery 10. In addition to this, in the second embodiment, as shown in
As described with
If the shape of the provisional battery body 7 is kept for a certain time without completely removing the molding pressure p, the residual stress is reduced without causing deformation.
Table 1 shows the relationship between a time during which the flat blocks 9 fixed with the screws S are left after the molding pressure p is removed (relaxation time) and a bending amount of the provisional battery body 7. In this case, the bending amount is a value determined by subtracting a battery thickness t from an overall height T (see
This result holds for the pair of provisional battery bodies 7 as well as the single provisional battery body 7. Thus, the method for manufacturing the all-solid state secondary battery according to the present embodiment includes the step of continuously applying a pressure (shape keeping pressure) not higher than the molding pressure p for at least two hours without completely removing the pressure after the step of pressure-molding the pair of provisional battery bodies 7. This reduces a residual stress on the pair of provisional battery bodies 7 without deforming the provisional battery bodies 7. Thus, the present embodiment can more effectively prevent bending of the pair of provisional battery bodies 7 than the first embodiment.
In a specific configuration for keeping the shape of the pair of provisional battery bodies 7, as shown in
In the above description, the shape keeping pressure is continuously applied for at least two hours (relaxation time). The relaxation time depends on the size of the provisional battery body 7 and the extension rates of the configurations and is properly determined by these factors. According to the result of Table 1, particularly if the provisional battery body 7 is about 30 to 300 mm in width and is made of the foregoing materials, it is decided that the application of the shape keeping pressure is preferably continued for at least two hours.
A method for manufacturing an all-solid state secondary battery according to a third embodiment will be described below. The explanation of the same configurations as those of the first embodiment is omitted and different configurations will be mainly discussed below. In the first embodiment, the rough surfaces (irregular parts) are formed on the electrode current collectors 1 and 5. The irregular parts are fit into each other so as to join the electrode current collectors 1 and 5. In the third embodiment, as shown in
An all-solid state secondary battery 10a manufactured by this method includes the binder interposed between the electrode current collectors 1 and 5 facing each other in addition to the configurations of the all-solid state secondary batteries 10 manufactured by the methods of the first and second embodiments. According to the method for manufacturing the all-solid state secondary battery 10a of the present embodiment, the binder 11 is plastically deformed to bite into the irregular parts on the outer surface (the surface opposite from the surface bearing the positive-electrode mixture layer 2′) of the positive-electrode current collector 1 by the pressure molding process, thereby firmly joining the positive-electrode current collectors 1 by an anchor effect. Thus, the positive-electrode current collectors 1 are joined into a single unit via the binder 11. This can cancel out a force of bending the provisional battery bodies 7, achieving the all-solid state secondary battery 10a having no curves.
Also in the third embodiment, as shown in
The binder 11 is not limited to a plastically deformable material. Flowable materials such as adhesive and solder may be used instead. If the electrode current collectors 1 and 5 have irregular parts and the binder 11 is a fluid adhesive or solder, the binder 11 flown onto the irregular parts is hardened to generate bonding power by an anchor effect.
A method for manufacturing an all-solid state secondary battery according to a fourth embodiment will be described below. The explanation of the same configurations as those of the third embodiment is omitted and different configurations will be mainly discussed below. In the third embodiment, the rough surfaces (irregular parts) are formed on the electrode current collectors 1 and 5 and the stacked provisional battery bodies 7 are pressure-molded with the binder 11 interposed between the electrode current collectors 1 and 5. In the fourth embodiment, rough surfaces (irregular parts) are not formed on the electrode current collectors and 5 and stacked provisional battery bodies 7 are pressure-molded with a binder 11 interposed between the electrode current collectors 1 and 5.
If the surfaces of the electrode current collectors 1 and 5 are not roughened, bonding power generated by an anchor effect is not expected but the electrode current collectors 1 and 5 can be joined to each other by other joining methods using, for example, an electrostatic force, reduced-pressure suction, or chemical bonding. The electrostatic force can be obtained by triboelectrification on the binder 11. For example, the reduced-pressure suction is obtained using the principle of suckers such that the binder 11 having fine holes on its surface is pressed to discharge air from the fine holes to the outside. The chemical bonding is, for example, a Van der Waals force or a covalent bond. Alternatively, these joining methods may be combined to loin the electrode current collectors. The binder 11 of the present embodiment is, for example, double-faced tape. The adhesion of the tape joins the electrode current collectors 1 and 5, thereby achieving the all state secondary battery having no curves.
Also in the fourth embodiment, a pressure not higher than the pressure of pressure molding is continuously applied to the provisional battery bodies 7 after a pressure molding process, thereby more effectively preventing bending of the all-solid state secondary battery as in the second embodiment.
In the first to fourth embodiments, the all-solid state secondary battery 10 includes the two provisional battery bodies 7. The number of provisional battery bodies is not limited to two. The all-solid state secondary battery may include three or more provisional battery bodies 7. In the case of three or more provisional battery bodies, the negative-electrode current collectors 5 are also joined to each other as well as the positive-electrode current collectors 1 facing each other.
In the methods of manufacturing the all-solid state secondary battery 10 (or 10a) according to the first to fourth embodiments, the laminate is temporarily pressed to form the provisional battery bodies 7 and then the pair of provisional battery bodies 7 is further pressure-molded, achieving the all-solid state secondary battery (or 10a). Alternatively, the all-solid state secondary battery 10 (10a) may be obtained by pressure-molding a pair of laminates without temporarily pressing the formed laminates. In other words, instead of temporarily pressing the laminates to form the individual provisional battery bodies 7, the pair of stacked laminates is pressed to obtain the all-solid state secondary battery 10 while forming the pair of provisional battery bodies 7. The manufacturing methods of the first to fourth embodiments require three presses: a temporary press on one of the provisional battery bodies 7, a temporary press on the other provisional battery body 7, and a press (pressure molding) on the stacked provisional battery bodies 7. According to the alternative manufacturing method, the all-solid state secondary battery 10 can be achieved by a single press (pressure molding), thereby improving the productivity of the all-solid state secondary battery.
In the foregoing explanation, for the clarity, the electrode current collectors 1 and 5, the electrode mixture layers 2 and 4, and the solid electrolyte layer are simply stacked in the descriptions and drawings. More specifically, the layers are stacked in a cross-sectional structure shown in
Number | Date | Country | Kind |
---|---|---|---|
JP2016-036523 | Feb 2016 | JP | national |
JP2016-066957 | Mar 2016 | JP | national |
JP2016-069859 | Mar 2016 | JP | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/JP2017/006977 | 2/24/2017 | WO | 00 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2017/150354 | 9/8/2017 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
5612152 | Bates | Mar 1997 | A |
7153611 | Minami et al. | Dec 2006 | B2 |
20040185336 | Ito | Sep 2004 | A1 |
20050186473 | Mitchell | Aug 2005 | A1 |
20070081299 | Zhong | Apr 2007 | A1 |
20080070113 | Kondo et al. | Mar 2008 | A1 |
20090081553 | Kondo | Mar 2009 | A1 |
20100040952 | Kimura | Feb 2010 | A1 |
20100075209 | Kimura | Mar 2010 | A1 |
20100112456 | Kimura et al. | May 2010 | A1 |
20130040206 | Yoshida | Feb 2013 | A1 |
20130149592 | Hayashi et al. | Jun 2013 | A1 |
20140193689 | Takami et al. | Jul 2014 | A1 |
20150340741 | Kim et al. | Nov 2015 | A1 |
20160181615 | Van Duren | Jun 2016 | A1 |
20170179519 | Okamoto et al. | Jun 2017 | A1 |
Number | Date | Country |
---|---|---|
101136496 | Mar 2008 | CN |
101657918 | Feb 2010 | CN |
102859780 | Jan 2013 | CN |
2894705 | Jul 2015 | EP |
2001-126756 | May 2001 | JP |
2009-252548 | Oct 2009 | JP |
2010-15782 | Jan 2010 | JP |
2010-231969 | Oct 2010 | JP |
2011-154900 | Aug 2011 | JP |
5131686 | Jan 2013 | JP |
2015-060721 | Mar 2015 | JP |
2017-073374 | Apr 2017 | JP |
2012020700 | Feb 2012 | WO |
2013035525 | Mar 2013 | WO |
2013140565 | Sep 2013 | WO |
2015147122 | Oct 2015 | WO |
Entry |
---|
International Search Report PCT/JP2017/006977 dated Mar. 28, 2017 with English translation. |
Extended European Search Report dated Aug. 21, 2019 issued in corresponding EP Application No. 17759820.8. |
Notice of Reasons for Refusal dated Jan. 7, 2020 issued in corresponding Japanese Patent Application No. 2016-066957 with English translation (6 pgs.). |
EP Communication pursuant to Article 94(3) dated Jul. 21, 2020 issued in corresponding European Patent Application No. 17 759 820.8. |
Office Action dated Nov. 2, 2020 issued in corresponding Chinese Patent Application No. 201780011523.8 with English translation (16 pgs.). |
Number | Date | Country | |
---|---|---|---|
20190051935 A1 | Feb 2019 | US |