Claims
- 1. A ceramic-metal article comprising:
- about 44-93% of a granular first hard phase consisting essentially of alumina and from 0% to less than 5% of one or more oxides selected from magnesia, zirconia, yttria, hafnia, and silica;
- about 4-44% of a granular second hard phase consisting essentially of one or more ceramic materials selected from the group consisting of the hard refractory carbides, nitrides, and borides, and combinations thereof; and
- about 2-20% of a metal phase consisting essentially of a combination of nickel and aluminum having a ratio of nickel to aluminum of from about 85:15 to about 88:12 by weight and 0-5% of an additive selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, cobalt, boron, or carbon, or combinations thereof;
- wherein said article has a density of at least about 95% of theoretical, and all unspecified component percents are expressed in % by volume.
- 2. An article in accordance with claim 1 wherein said metal phase comprises about 4-12% of said article.
- 3. An article in accordance with claim 1 wherein said metal phase comprises a combination of a Ni.sub.3 Al ordered crystal structure, or a Ni.sub.3 Al ordered crystal structure coexistent with or modified by said additive, and one or more nickel-aluminum alloys.
- 4. An article in accordance with claim 3 wherein said metal phase combination comprises about 40-80 v/o of said Ni.sub.3 Al ordered crystal structure of said Ni.sub.3 Al ordered crystal structure coexistent with or modified by said additive.
- 5. An article in accordance with claim 1 wherein said first hard phase consists essentially of alumina and from 0% to less than 5% of magnesia.
- 6. An article in accordance with claim 1 wherein said one or more ceramic materials of said second hard phase are selected from the group consisting of the hard refractory carbides and nitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, and tungsten; titanium diboride; boron carbide; and combinations thereof.
- 7. An article in accordance with claim 1 wherein said hard phases have an average grain size of about 0.5-20 .mu.m.
- 8. An article in accordance with claim 1 wherein said article is coated with one or more adherent, compositionally distinct layers, each layer being a material or solid solution of materials selected from the group consisting of carbides, nitrides, and carbonitrides of titanium, tantalum, and hafnium, oxides of aluminum and zirconium, and diamond.
- 9. An article in accordance with claim 8 wherein said hard phases have an average grain size of about 1-3 .mu.m, and said article is of a geometry suitable for use as a cutting tool.
- 10. A ceramic-metal article comprising:
- about 44-92% of a granular first hard phase consisting essentially of alumina and from 0% to less than 5% of one or more oxides selected from magnesia, zirconia, yttria, hafnia, and silica;
- about 4-44% of a granular second hard phase consisting essentially of one or more ceramic materials selected from the group consisting of hard refractory titanium carbide, hafnium carbide, tantalum carbide, tantalum nitride, tungsten carbide, titanium diboride, and boron carbide, and combinations thereof; and
- about 4-12% of a metal phase consisting essentially of a combination of nickel and aluminum having a ratio of nickel to aluminum of from about 85:15 to about 88:12 by weight and 0-5% of an additive selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, cobalt, boron, and carbon, and combinations thereof;
- wherein said article has a density of at least about 95% of theoretical, and all unspecified component percents are expressed in % by volume.
- 11. An article in accordance with claim 10 wherein said metal phase comprises a combination of a Ni.sub.3 Al ordered crystal structure and one or more nickel-aluminum alloys, or a combination of a Ni.sub.3 Al ordered crystal structure coexistent with or modified by said additive and one or more nickel-aluminum alloys.
- 12. An article in accordance with claim 11 wherein said metal phase combination comprises about 40-80 v/o of said Ni.sub.3 Al ordered crystal structure or said Ni.sub.3 Al ordered crystal structure coexistent with or modified by said additive.
- 13. An article in accordance with claim 10 wherein said article is coated with one or more adherent, compositionally distinct layers, each layer being a material or solid solution of materials selected from the group consisting of carbides, nitrides, and carbonitrides of titanium, tantalum, and hafnium, oxides of aluminum and zirconium, and diamond.
- 14. An article in accordance with claim 13 wherein said hard phases have an average grain size of about 1-3 .mu.m, and said article is of a geometry suitable for use as a cutting tool.
- 15. A ceramic-metal article in accordance with claim 6 wherein said one or more ceramic materials of said second hard phase have an average aspect ratio between 1:1 and 20:1.
- 16. A ceramic-metal article having a density of at least about 95% of theoretical, and comprising:
- about 88-98% by volume of granular hard phases consisting essentially of (a) a major hard phase portion consisting essentially of alumina with about 0-2% by volume of one or more oxides selected from the group consisting of magnesia, zirconia, yttria, hafnia, and silica; and (b) a minor hard phase portion selected from the group consisting of the hard refractory carbides, nitrides, carbonitrides, and borides, and combinations thereof; and
- about 2-12% by volume of a metal phase consisting essentially of (a) a combination of nickel and aluminum having a ratio of nickel to aluminum of from about 85:15 to about 88:12 by weight; and (b) 0-5% by volume of an additive selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, cobalt, boron, and carbon, and combinations thereof; and
- wherein:
- said metal phase is a non-continuous, dispersed metal phase; and
- at least a major portion of said non-continuous, dispersed metal phase is segregated at triple points defined by grain surfaces of said granular hard phases.
- 17. An article in accordance with claim 16 wherein said metal phase comprises about 4-12% by volume of said cutting tool.
- 18. An article in accordance with claim 16 wherein said metal phase comprises a combination of a Ni.sub.3 Al ordered crystal structure and one or more nickel-aluminum alloys, or a combination of a Ni.sub.3 Al ordered crystal structure coexistent with or modified by said additive and one or more nickel-aluminum alloys.
- 19. A method in accordance with claim 18 wherein said metal phase combination comprises about 40-80 v/o of said Ni.sub.3 Al ordered crystal structure, or said Ni.sub.3 Al ordered crystal structure coexistent with or modified by said additive.
CROSS REFERENCE TO RELATED APPLICATIONS
This application is a continuation-in-part of commonly assigned, copending U.S. patent application Ser. No. 07/595,065 filed Oct. 10, 1990, now abandoned, by the same Applicants.
US Referenced Citations (5)
Number |
Name |
Date |
Kind |
4497228 |
Sarin et al. |
Feb 1985 |
|
4919718 |
Tiegs et al. |
Apr 1990 |
|
4990181 |
Pierotti et al. |
Feb 1991 |
|
5015290 |
Tiegs et al. |
May 1991 |
|
5089047 |
Buljan et al. |
Feb 1992 |
|
Foreign Referenced Citations (3)
Number |
Date |
Country |
0062311 |
Oct 1982 |
EPX |
49127806 |
Dec 1974 |
JPX |
2071908 |
Mar 1990 |
JPX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
595065 |
Oct 1990 |
|