Patent Application
20200368844
The present invention relates to a method and a device for aluminothermic welding of pipe members, such as pipes and pipe flanges used in wellbores or pipelines.
By a thermite or aluminothermic reaction, which is an exothermic reaction, high temperatures are achieved by converting a metal oxide with a more reactive metal. This reactive metal can then reduce the oxide such that the reactive metal bonds with the oxygen to a new metal oxide, while the initial metal in the oxide is extracted as pure metal. The reaction thus releases a high amount of heat. This heat can be utilized to melt the filling material. In such an exothermic reaction composition the reducing metal can be e.g. metallic aluminium.
Examples of metal oxides in such compositions are iron(III) oxide, zinc oxide, copper(I) oxide, manganic oxide and calcium oxide. Such a composition is called a thermite composition, and when it consists of aluminium and iron oxide in a fine grind such as a powder, the oxygen atoms are transferred from the iron to the aluminium, and a lot of heat is generated. Additional metal positioned in or adjacent the composition, e.g. iron, will melt and be liquefied. In the process, liquid iron and aluminium oxide (alumina) is formed.
While the iron forms a melt, alumina Al2O3 has a higher melting point and will therefore act as a solid oxide which will float on the surface of the melt as dross. The temperature in such reactions can reach 3000° C. depending on the composition proportions and environmental factors, such that both products can be in a liquid state. One example of such a transition is given by the following reaction equation:
2Al+Fe2O3=2Fe+Al2O3
Pure iron and alumina Al2O3 is thus formed. It is an advantage that the composition proportions between aluminium and iron oxide corresponds to the theoretical stoichiometric amount of these two substances, such that both substances are conversed approximately 100%.
Such thermite compositions are common in when welding steel constructions, such as in long welded rails.
Iron is heavier than aluminium oxide, and will sink in a melt composition of these two substances, i.e. when the reaction according to the conversion above is almost 100% to the right.
The exothermic reaction can be carried out in a container or crucible which is adapted to melting substances of high temperatures. The crucible is an incombustible melting pot which is non-porous, unaffected by chemical substances and can withstand high fluctuations of temperature. As a material for a crucible can be mentioned porcelain, platina, quartz sand and chamotte, graphite with clay as a fixing agent.
There are also some examples of thermite or aluminothermic welding of pipes.
U.S. Pat. No. 3,948,434 A discloses annular coupling members for welding together sections of pipe used, containing annular bodies of exothermic materials such as “Thermite” material, and upon being ignited, producing welding of the interfaces between the coupler and a pair of pipes welded thereto or between the two pipes directly.
U.S. Pat. No. 3,542,402 A, discloses a metal tube containing pyrotechnic material that liberates substantially no gas on burning is embedded in and adjacent a mating surface of an article of thermoplastic resin. The article is joined to another article of thermoplastic resin having a mating surface by bringing the mating surfaces together and igniting the pyrotechnic, forming a fused joint between the mating surfaces. A preferred pyrotechnic contains aluminium, boron, barium chromate and aluminium oxide.
A goal with the present invention is to overcome the problems of prior art, and to disclose a welding method and device where the resulting weld has less volumetric defects than pipe welds according to prior art.
It is further an objective of the invention to present a welding method and device where quality is increased, i.e. the same result can be obtained repeatedly as long as the same setup is used. This reduces the need for weld inspection and acceptance. Thus weld quality assurance can be shifted from a post-weld to a pre-weld approach.
From the above it is also evident that the quality of the resulting weld is less dependent on the skilled person involved in welding process.
In summary, the advantages defined above can lead to considerable reductions of time and cost for pipe welding.
The invention solving the above mentioned problems is a method for aluminothermic welding together of first and second pipe members comprising the steps of:
The invention is also an aluminothermic welding device for welding together of first and second pipe members comprising:
In the following description, various examples and embodiments of the invention are set forth in order to provide the skilled person with a more thorough understanding of the invention. The specific details described in the context of the various embodiments and with reference to the attached drawings are not intended to be construed as limitations. Rather, the scope of the invention is defined in the appended claims.
The invention is in the following described in relation to joining two pipes or pipe members, such as a pipe and a pipe flange. The invention may be applied to metal parts in general which are to be joined.
An embodiment of an aluminothermic welding device according to the invention is illustrated in
When the welding device is used for welding, it should be aligned properly to ensure the best result. For the remainder of the document, the device is defined to be in a welding position when it is aligned for welding.
One such welding position can be the one illustrated in
One of the main components of the welding device is the sleeve (30), which is configured to cover both pipe members (10, 12) and to form a cavity (33) surrounding the pipe members (10, 12) when it is in a welding position. The inside of the sleeve (30) fits tightly to pipe surfaces (11, 13), which can be provided by known means with different tightening means. The sleeve (30) can e.g. be in two parts and rotate about a hinge, where the free ends are moved towards each other and joined and tightened by means of screw connections or similarly such that the inside of the sleeve (30) is tightly fitted to the pipe surfaces (11, 13).
The welding device also comprises a crucible (50), where the exothermic reaction can be carried out. The crucible is adapted to melting substances of high temperatures according to prior art as described previously.
Further, the welding device comprises an input channel (54) connected to the crucible (54) where melt can flow into the cavity (33) and a drain channel (44) where resulting gases and dross can be drained or extracted from the cavity (33).
The drain channel (44) is connected to a second opening (45) in a wall of the sleeve (30), in an upper part of the sleeve (30), and the input channel (54) is arranged between the crucible (50) and the cavity (33), wherein the input channel (54) enters into the cavity (33) through a first opening (35) in a wall of the sleeve (30) in a lower part of the sleeve (30) when the sleeve is in the welding position.
In an embodiment the first opening (35) is arranged at the top of said cavity (33). In an embodiment the second opening (45) is arranged in at the bottom of said cavity (33).
In an embodiment the first and/or second opening (35, 45) are arranged along a vertical line through a center of said sleeve (35).
In an embodiment, the crucible (50) is arranged above the cavity (33) when the sleeve (30) is in the welding position.
In an embodiment, at least a portion of the input channel (54) runs inside the wall of the sleeve (30) between an upper part of the sleeve and the first opening ( ). The sleeve (30) may be seen as a mold for the welding where the first opening (35) and the input channel (54) constitute a single channel running inside the mold.
In an embodiment, an inner surface of the sleeve (30) has a groove (32) forming an outer wall of the cavity (33).
In an embodiment, the pipe members (10, 12) have tapered ends, configured towards and adjacent each other forming an inner wall of the cavity (33).
The groove (32) in the sleeve (30) can in an embodiment be combined with the tapered ends of the pipe member s (10, 12). The groove (32) together with the slot defined by the tapered ends forms a surrounding drop shaped volume, i.e. the cavity (33), which is to be filled with melted welding material.
In an embodiment, the sleeve (30) has a circular inner cross section and the cavity (33) is annular.
In an embodiment, the welding device comprises a support ring (38) configured to be arranged inside the first pipe member (10) before welding. The support ring prevents melt to enter into the inner diameter between the two adjacent pipe members (10, 12).
In an embodiment, the welding device comprises a cooling mantle as illustrated in
The cooling mantle (60) is arranged about the sleeve (30) and forms a cooling cavity (66) between the cooling mantle (60) and the sleeve (30). In a further detailed embodiment the end portions of the mantle (60) is closely fitted to the surface (11, 13) of the pipes (10, 12) by means of suitable packings marked as (63) and (65).
The cooling mantle can be made of different tyoes of materials. In an embodiment, the cooling mantle (60) is made of steel.
An inlet is illustrated as pipe socket (61), and a corresponding outlet is shown as pipe socket (62). The roof or wall portions of the cooling mantle (60) comprise openings for the crucible (50) and the drain channel (44).
An annealing fluid such as a gas or a liquid can, in ways known in the art, be supplied to the cooling cavity (66) through pipe socket (61), flow through the cooling cavity (66) and further be exhausted through outlet (62).
Although the previous embodiments have been illustrated with pipes, one or both of the pipe members (10, 12) may also be pipe flanges (70) as illustrated in
Depending on the specific pipe flange, the cooling mantel may have to be adapted, as will be understood by a person skilled in the art.
Embodiments of the welding method according to the invention will be described with reference to
As previously noted the invention is also a method for aluminothermic welding together of first and second pipe members (10, 12).
One step to be performed, is to arrange the input channel (54) between a crucible (50) and the cavity (33), such that the input channel (54) enters into the cavity (33) through a first opening (35) in a wall of the sleeve (30) in a lower part of the sleeve (30) when the sleeve is in the welding position. Please see above for definition of welding position. The first opening (35) is allows melt from the crucible (50) to be in fluid communication with the cavity (33) via the input channel (54).
The crucible (50) is filled with an exothermic mixture, such as a thermite mixture. The exothermic mixture is ignited, or inflamed to create a melt (36), which can now flow freely down the input channel (54), through the first opening (35) before it continues to flow up through the cavity on both sides of the pipe members (10, 12), until the cavity (33) is filled up with the melt (36).
At the same time the oxidation product is secreted as a solid dross floating upwards to the top of the cavity (33). This is due to iron in a liquid state has a higher density than the oxides and will sink, while the oxide phase and dross phase will float. This dross phase will float to the top and be diverted together with the gas which also could be released by the exothermic conversion draining gases and dross, out of a second opening (45) in a wall of the sleeve (30) in an upper part of the sleeve (30).
The purpose of the second opening (45) is that a need for ventilation of gases/dross immediately arises when the exothermic reaction takes place, and melt flows up in the cavity (33). As gases released from the melt leads to a certain pressure increase, it is important that such gas can freely escape through the second opening (45). The removal of gases and dross has been optimized in the device and method according to the invention, where the melt enters the lower part of the cavity (33). Gases and dross will therefore escape easily upwards inside the cavity (33) and through the second opening (45). The result is a welding joint with less volumetric failures than prior art.
As part of the process the sleeve (30) should be arranged in the welding position. This should be done before igniting the exothermic mixture, such that the melt flows properly through the channels and a high-quality weld can be achieved.
Pre-heating can be used to further improve the quality of the weld. In an embodiment the method comprises pre-heating the first and second pipe members (10, 12) before igniting said exothermic mixture.
In an embodiment the pipe members (10, 12) are heated to about 700 degree Celsius.
This can be achieved by various means. In its simplest form the pipe members (10, 12) may be pre-heated directly before arranging them in the sleeve (30) by heat from e.g. a gas burner, electric heater or chemical heater.
It can also be achieved by heating the pipe members (10, 12) after they have been arranged in the sleeve by e.g. blowing a gas flame from a gas burner into the sleeve (30), or using an electric or chemical heat element to pre-heat the form.
In an embodiment, the method comprises the step of arranging the crucible (50) above the cavity (33) when the sleeve (30) is in the welding position.
In this part of the process, it is important to control that the temperature does not drop too fast, such that the dross phase and gases is allowed to float completely to allow upwards through the second opening (45). These substances can be removed before the viscosity of the melt is too high, and the melt solidifies. Voids in the weld joint, generated due to impurities such as oxides/dross and/or gases, should be avoided as far as possible.
In an embodiment the method comprises the step of cooling the melt (36) to establish a solid weld joint.
Temperature control could in an embodiment be carried out by adding hot fluid, e.g. hot gases in circulation through cooling cavity (66), and then controlling the temperature drop in the melt joint via the temperature in the mantle gas. As a coolant for circulation in the cooling cavity (66), water or other liquid/gas could be utilized, if the temperature at the inlet is adapted to the temperature in the joining area.
Before the cooling mantle (60) has mounted to the pipes (10, 12), alternatively before the melting process has been initialized, the pipe ends are in an embodiment pre-heated up to the temperature at which the melt flows from the crucible (50), and then the temperature is brought to drop in a controlled manner.
In an embodiment, the method comprises the steps of extracting the oxidation products through a drain channel (44). An external drain pump connected to the drain channel (44) may be used to improve extraction.
In an embodiment, the method comprises the step of creating the melt comprised of iron and alumina by creating an exothermic reaction from a transformation of the exothermic mixture comprising iron oxide and aluminum.
In an embodiment, the exothermic mixture comprises iron powder or iron particles. However, other metals or mixture of metals may also be used in other embodiments to weld alloys, such as e.g. Chromium, Nickel and Molybdenum.
When the welding joint has cooled down, the cooling mantle (60) and sleeve (30) are removed, upon which the joint can be treated by grinding, polishing or other suitable processing in order to form an even and smooth joint. Alternatively, the sleeve (30) could form part of the pipe joint and be left welded in place.
In the exemplary embodiments, various features and details are shown in combination. The fact that several features are described with respect to a particular example should not be construed as implying that those features by necessity have to be included together in all embodiments of the invention. Conversely, features that are described with reference to different embodiments should not be construed as mutually exclusive. As those with skill in the art will readily understand, embodiments that incorporate any subset of features described herein and that are not expressly interdependent have been contemplated by the inventor and are part of the intended disclosure. However, explicit description of all such embodiments would not contribute to the understanding of the principles of the invention, and consequently some permutations of features have been omitted for the sake of simplicity or brevity.