Patent Application
20210164076
The present disclosure relates to an aluminum alloy, in particular an aluminum alloy from the 7000 group corresponding to the classification of the Aluminum Association (AA). The present disclosure further relates to an overaged aluminum alloy product produced from such an alloy.
In the aeronautics and space travel industry, high-strength aluminum alloys are necessary for producing mainly load-bearing fuselage, wing and landing gear parts, which exhibit high strength both under static and under dynamic stress. The required strength properties can be achieved by using alloys of the 7000 group corresponding to the classification of aluminum alloys made by the Aluminum Association (AA).
Highly stressed parts in aeronautics and space travel are made, for example, of the alloys AA7075, AA7175, AA7475 and particularly preferably of the alloys AA7049 and AA7050 which are used in the American region and of the alloys AA7010, AA7049A and AA7050A which are used in the European region.
In WO 02/052053 A1, a high-strength aluminum alloy of the aforementioned type is disclosed, which, in comparison to earlier alloys of the same type, has an elevated zinc content, coupled with a reduced copper and magnesium content. The total content of copper and magnesium together of this previously disclosed alloy amounts to less than 3.5 wt %. The copper content itself is indicated to be 1.2-2.2 wt %, preferably 1.6-2.2 wt %. In addition to the elements zinc, magnesium and copper, this previously disclosed alloy necessarily contains one or more elements from the group consisting of zirconium, scandium and hafnium with maximum proportions of 0.4 wt % zirconium, 0.4 wt % scandium and 0.3 wt % hafnium.
In EP 1 683 882 A1, an alloy with low quench sensitivity is disclosed, from which highly stressed parts, for example for use in the aeronautics and space travel technology, and thus components with high static and dynamic strength properties and simultaneously good fracture toughness and good stress corrosion cracking behavior, are produced, wherein these components can also have a thickness of more than 200 mm. This previously disclosed alloy consists of: 7 to 10.5 wt % Zn, 1.0 to 2.5 wt % Mg, 0.1 to 1.15 wt % Cu, 0.06 to 0.25 wt % Zr, 0.02 to 0.15 wt % Ti as obligatory alloy elements, wherein the sum of the alloy elements Zn+Mg+Cu is at least 9 wt %, and the rest being Al in addition to unavoidable impurities. In the production method described in this prior art, the semi-finished product produced from this aluminum alloy is overaged in a single step or in multiple steps in order to optimize the desired material properties. The fracture toughness determined for the semi-finished products produced from this alloy in a neutral environment according to ASTM E399 is improved in comparison to the previously disclosed prior art.
The relevant properties include, among others, fracture toughness as well as stress corrosion cracking resistance in surroundings influenced by the environment (according to ASTM E1823: environment assisted cracking; abbreviated EAC). For this purpose, stress corrosion cracking (SCC) is usually carried out in a salt water environment with the usual test set-up for determining the stress corrosion cracking resistance (SCC resistance). In the test set-up, for example, a pre-notched sample (for example, ASTM G168-00) is exposed to a force which attacks the test specimen in order to enlarge the notch or crack opening in the case of sufficient force such that crack formation occurs. With increasing crack length, the associated stress intensity factor (K factor) decreases until the crack formation finally ceases. If a test specimen is more SCC resistant, then less crack growth is observed or a higher load (in the form of the stress intensity factor K) is necessary for crack propagation, that is to say the higher the stress intensity factor is to which a notched test specimen can be exposed without observable crack propagation.
The SCC resistance of aluminum alloys can be very different in one and the same alloy depending on the environmental conditions in which the SCC test is performed. The state of the overaging of the semi-finished product or test specimen also has an influence on the SCC resistance. In an alloy according to AA7010, with increasing overaging of the test specimen starting from the T6 state via the state T76 to the state T74, the SCC resistance increases significantly, in particular also in a salt water environment. Other 7xxx alloys in the conventional SCC test (i.e., in salt water) generally exhibit the same behavior. With changed environmental conditions (for example, high humidity at elevated temperature), it has been shown that in particular 7xxx alloys with higher zinc content generally also have a tendency to undergo “environment assisted cracking” in the overaged state (i.e., T7x). Here, the crack propagation due to hydrogen embrittlement occurs preferentially along the grain boundaries (see, for example, EASA Safety Information Bulletin No. 2018-04). For AA7010, under such EAC environmental conditions, in the T6 state, KIEAC values between 6 and 7 MPa√m can be achieved; however, in the overaged state T74, the KIEAC values increase up to 25 MPa√m with clearly reduced strength in comparison to the T6 state due to the overaging. According to the above explanation, the K factor KIEAC here is a measure of the EAC resistance, since no crack propagation occurs for stresses KI<KIEAC.
The alloy (AA7037) disclosed in EP 1 683 882 A1, which is improved in terms of its strength properties compared to the alloy AA7010, surprisingly does not exhibit the expected EAC resistance with increasing overaging, as is observed in a test specimen made of the alloy AA7010. Even in the overaged T7452 state, with the alloy according to AA 7037, in a humid environment at elevated temperature (50° C., 85% relative humidity), an EAC resistance of only approximately KIEAC=6 to 7 MPa√m can be achieved.
Proceeding from this background, an aspect of the present disclosure is to propose an aluminum alloy from which an aluminum alloy product with strength values comparable to those of an alloy product made of the alloy AA7037 can be produced, but which also exhibits an improved EAC resistance under environmental influences which promote crack initiation and crack propagation.
This is achieved by an aluminum alloy with the following composition:
0.04-0.1 wt % Si,
0.8-1.8 wt % Cu,
1.5-2.3 wt % Mg,
0.15-0.6 wt % Ag,
7.05-9.2 wt % Zn,
0.08-0.14 wt % Zr,
0.02-0.08 wt % Ti
max. 0.35 wt % Mn,
max. 0.1 wt % Fe,
max. 0.06 wt % Cr,
optionally 0.0015-0.008 wt % Be,
the rest being aluminum in addition to unavoidable impurities.
In the alloys described in the context of these embodiments, unavoidable impurities can be present with max. 0.05 wt % per element and in total with max. 0.15 wt %.
Concerning semi-finished products produced from such an alloy, it has been surprisingly observed that, in spite of a relatively high Zn content, the EAC resistance is considerably improved in comparison to the values that can be achieved with samples made of the alloy AA7037 even under corrosion cracking-promoting environmental influences. Nevertheless, the mechanical strength values are sufficiently high. The yield point Rp0.2 amounts to more than 440 MPa and can reach values of 460 MPa and higher in a forged part having a thickness of 150 mm. The fracture toughness is above 20 MPa√m and can reach values of 25 MPa√m and higher.
When performing an EAC test (ASTM E1823; ASTM G168) in an environment with a humidity of 85% and a temperature of 50° C., the SCC resistance surprisingly shows that no crack propagation is observed with an applied stress of KI=20 MPa√m for a test duration of 30 days. Therefore, even under these environmental conditions, the EAC resistance of an alloy product produced from the alloy according to the present disclosure, in the case of overaging to the state T7xxx, is clearly improved in comparison to that of previously disclosed alloys, such as, for example, AA7037, or with respect to AA7010 in parts having a greater thickness (thickness≥100 mm, in particular also ≥150 mm). Here, it is found that this alloy or semi-finished products and products produced therefrom has/have a particularly low quench sensitivity. This means that, even as a result of a greater thickness (cross-sectional area), parts produced from the alloy undergo no losses or at least no significant losses in terms of their strength in the central sections due to their slow cooling. The consequence is that these parts exhibit high strengths, even in the case of large cross sections. It is precisely in high-strength aluminum alloy products, as used in aeronautics and space travel, that the EAC resistance in such an environment (85% relative humidity at 50° C.) is of particular interest. This result is surprising since the EAC resistance of an alloy product produced from an AA7037 alloy in the same overaged state does not suggest it. Finally, for the alloy product of the alloy AA7037, which is in the same overaged state, an EAC resistance of only approximately 6 to 7 MPa√m was determined with the same overaging.
Thus, while stress intensity factors KIEAC of approximately 6 to 7 MPa√m are achieved with alloy products produced from the aluminum alloy AA7037 in the EAC tests, in aluminum alloy products made of the alloy according to the present disclosure, these values are clearly higher than 20 MPa√m in the same overaging state. The achieved KIEAC values in aluminum alloy products made of the alloy according to the present disclosure are approximately 70% and higher with respect to the fracture toughness KIc at room temperature. In many cases, the KIEAC values might even correspond to the KIC value (and thus cannot be experimentally determined for technical reasons), since no crack propagation could be observed over the test duration used (more than 30 days). The particular EAC resistance was not expected in light of the high Zn content. According to the prevailing teaching, higher Zn contents negatively affect the EAC resistance.
An aluminum alloy product produced from the aluminum alloy according to the present disclosure is overaged preferably in the state T74, T7451, T7452 or T7454. In this state, the aluminum alloy product still exhibits sufficient mechanical strength values as well as the desired SCC resistance both in the conventional immersion test in salt water solution and also in an environment favoring hydrogen-induced EAC, for example, in an environment with a humidity of 85% and a temperature of 50° C. If the overaging that does not reach the state T74 or T74xx, higher mechanical strength values can in fact be achieved, but in that case the SCC/EAC resistance generally does not appear to the desired extent. Overaging beyond T74/T74xx, on the other hand, leads to a further decrease of the mechanical strength values with generally improved SCC/EAC properties.
According to an embodiment of this aluminum alloy, the alloy contains 0.35 to 0.6 wt % Ag, in particular 0.40 to 0.50 wt % Ag. Interestingly, it has been shown that the above-described properties appear in an alloy having this Ag content, particularly with regard to the EAC resistance. In this embodiment of the alloy, the preferred Zn/Mg ratio is greater than 3.4 and up to and including 4.95. A Zn—Mg ratio between 3.5 and 4.25 is preferable. The preferred copper content of this alloy embodiment is between 0.8 and 1.35 wt % Cu, in particular between 0.9 and 1.2 wt % Cu, in connection with an Mn content between 0.18 and 0.3 wt %, in particular 0.2 to 0.25 wt %, and a Zn content between 7.1 and 8.9 wt %. If the Cu content in such an aluminum alloy is within the range of greater than 1.35 and up to 1.8 wt %, the alloy product has comparable alloy product properties if the Mn content is less than 0.1 wt %, in particular less than 0.05 wt %.
These special properties—high strength values and a particular EAC resistance—are exhibited in an alloy which has a lower Ag content compared to the above-described Ag content, namely when said content is less than 0.35 wt % Ag but more than 0.15 wt %. The Cu and Zn contents correspond to the Ag-richer alloy, wherein the Zn/Mg ratio is between 3.9 and 4.3. The present description of these example embodiments illustrates that the desired effects extend over the entire range of the claimed alloy.
The special properties of the alloy product produced from this alloy are to be associated with the very narrow spectrum of the elements participating in the alloy. Indeed, it is only with this composition that the desired EAC resistance can appear in the state T74/T74xx due to overaging of the alloy product produced from the alloy.
Be can optionally participate in the alloy. The introduction of Be into the melt is used for reducing the susceptibility to oxidation of same. Be can be included in the amount between 0.0015 and 0.008, in particular in the range of 0.0015 to 0.0035, for the mentioned purposes in the design of the alloy.
The below descriptions are provided using example embodiments. Reference is made to the appended figures which show the following results for test performances with test specimens according to ASTM G168 under the environmental conditions of 50° C. and 85% relative humidity:
From the comparison alloys and the test alloy, test specimens were produced as follows:
The alloy compositions of the comparison alloys and of the test alloys in wt % are as follows:
The samples in the state T7452 were subjected to an EAC test according to ASTM E1681 using DCB samples according to ASTM G168 in the present case at a relative humidity of 85% and a temperature of 50° C. The stresses of the samples provided with incipient cracking at the start of the test were between 20 and 30 MPa√m, respectively, depending on the determined fracture toughness. The investigations with regard to the EAC behavior on the DCB samples occurred in an S-L orientation. Thus, the KIEAC values relate to this orientation. The S-L orientation is the direction in which a sample is most susceptible to an EAC-induced failure. The sample is stressed in the ST direction of the forged piece (in the direction of the shortest extension). Thus, an incipient crack formation in L direction (direction of the greatest extension) is to be expected. The EAC tests were therefore carried out on S-L oriented samples.
Using the sample made of the alloy AA7010,
Although the alloy AA7037, which is already improved in terms of strength with respect to the alloy AA7010, in the state T7452, exhibits sufficient mechanical strength values with a yield point Rp0.2 of 450 MPa and more and a fracture toughness KIC of approximately 30 MPa√m, it does not have a sufficient EAC resistance to meet the requirements, see
In contrast, as can be seen from the diagram of
The KIEAC values, from four samples of the alloy E5 according to the present disclosure, can be obtained from the diagram of
The above-discussed strength values of the test specimens made of the comparison alloys as well as of the test specimens of alloys E1-E6 according to the present disclosure are summarized in the following table:
The description of the alloys according to the present disclosure and of the overaged alloy products produced therefrom clearly shows that the EAC resistance of these alloy products is unexpectedly satisfactory.