The present invention relates to a coating process, specifically to an aluminum alloy imitated electroplating process.
Aluminum alloy electroplated hubs having high brightness and metallic luster are loved by a vast number of car consumers. However, the electroplating process is complex, and the electroplating production process greatly influences the environment. With increasing improvement on environmental protection requirement, a wheel surface treatment process having electroplating silver effect and environment friendliness needs to be developed.
This patent provides an aluminum wheel surface treatment process having no harm to the environment, high brightness and metallic luster.
An aluminum alloy hub surface treatment process achieves the metal electroplating effect by spraying a layer of 2-5 μm electroplating silver colored paint onto a polished metallic aluminum alloy matrix.
The process of the present invention comprises the procedures of providing an aluminum alloy hub blank, sanding, polishing, pre-treating, spraying electroplating silver, flash-drying, spraying celluloid paint, and curing.
The metallic matrix is sanded by adopting 400#, 800# and 1000# sand paper in sequence to control the positive roughness RA at 0.20-0.23 μm.
A manual polishing machine is matched with polishing paste for polishing to control the roughness RA at 0.16-0.17 μm.
The electroplating silver is sprayed by using air guns, wherein the operation parameters comprise: 14-15″ (Din-4), paint throughput 80-150 CC, atomization pressure 2.0-3.5 bar, sector pressure 2.0-3.5 bar, and gun distance 180-250 mm; and the curing condition of the colored paint comprises: keeping the temperature of the workpiece at 150° C. for 10-15 minutes. The electroplating silver product is acrylic series paint.
The celluloid paint is sprayed by using air guns, wherein the operation parameters comprise: operation viscosity 20-21″ (Din-4 cup), paint throughput 80-150 CC, atomization pressure 2.5-3.5 bar, sector pressure 2.5-3.5 bar, and gun distance 180-250 mm. The curing condition of the celluloid paint comprises: keeping the temperature of the workpiece at 150° C. for 10-15 minutes. The celluloid paint is acrylic series high-brightness celluloid paint.
Compared with the traditional electroplating process, this process has the advantages that the electroplating procedure having environmental pollute and high cost is replaced with spraying a layer of colored paint, so that the influence on the environment is reduced, the cost is reduced and the production efficiency is improved.
An aluminum alloy hub surface treatment process comprises the procedures of providing an aluminum alloy hub blank, sanding, polishing, pre-treating, spraying electroplating silver, flash-drying, spraying celluloid paint, and curing.
The metallic matrix is sanded by adopting 400#, 800# and 1000# sand paper in sequence to guarantee the positive roughness RA at 0.20 μm.
A manual polishing machine is matched with polishing paste for polishing to guarantee the roughness RA at 0.16 μm.
The operation parameters for spraying electroplating silver comprise: 15″ (Din-4), paint throughput 100 CC, atomization pressure 3.0 bar, sector pressure 2.5 bar, and gun distance 200 mm; and the flash-drying time is 15 min.
The operation parameters for spraying celluloid paint comprise: operation viscosity 20″ (Din-4 cup), paint throughput 150 CC, atomization pressure 2.8 bar, sector pressure 3.0 bar, and gun distance 200 mm.
The curing condition comprises: keeping the temperature of the workpiece at 150° C. for 13 min.
An aluminum alloy hub surface treatment process comprises the procedures of providing an aluminum alloy hub blank, sanding, polishing, pre-treating, spraying electroplating silver, flash-drying, spraying celluloid paint, and curing.
The metallic matrix is sanded by adopting 400#, 800# and 1000# sand paper in sequence to guarantee the positive roughness RA at 0.21 μm.
A manual polishing machine is matched with polishing paste for polishing to guarantee the roughness RA at 0.17 μm.
The operation parameters for spraying electroplating silver comprise: 15″ (Din-4), paint throughput 90 CC, atomization pressure 2.8 bar, sector pressure 2.5 bar, and gun distance 200 mm; and the flash-drying time is 15 min.
The operation parameters for spraying celluloid paint comprise: operation viscosity 20″ (Din-4 cup), paint throughput 150 CC, atomization pressure 2.5 bar, sector pressure 2.8 bar, and gun distance 200 mm.
The curing condition includes: keeping the temperature of the workpiece at 150° C. for 13 min.
An aluminum alloy hub surface treatment process comprises the procedures of providing an aluminum alloy hub blank, sanding, polishing, pre-treating, spraying electroplating silver, flash-drying, spraying celluloid paint, and curing.
The metallic matrix is sanded by adopting 400#, 800# and 1000# sand paper in sequence to guarantee the positive roughness RA at 0.21 μm.
A manual polishing machine is matched with polishing paste for polishing to guarantee the roughness RA at 0.16 μm.
The operation parameters for spraying electroplating silver comprise: 15″ (Din-4), paint throughput 120 CC, atomization pressure 3.0 bar, sector pressure 3.0 bar, and gun distance 200 mm; and the flash-drying time is 15 min.
The operation parameters for spraying celluloid paint comprise: operation viscosity 20″ (Din-4 cup), paint throughput 160 CC, atomization pressure 3.0 bar, sector pressure 3.2 bar, and gun distance 200 mm.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017 1 0482437 | Jun 2017 | CN | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20060019089 | Leininger | Jan 2006 | A1 |