Aluminum gallium nitride laser

Abstract

Description

axy of Gallium Nitride on Sapphire Substrate" by Amano, et al, THIN SOLID FILMS, Vol. 163, pages 415-420, 1988. Whereas the former reference utilized molecular beam epitaxy, the latter reference utilized metalorganic vapor phase epitaxy to achieve a gallium nitride film with a smooth surface, free from cracks, on a sapphire substrate.

Another apparatus and method for growing a single crystalline GaN film was reported in "P-Type Conduction in Mg-Doped GaN treated with Low Energy Electron Beam Irradiation (LEEBI)", by Amano, et al., in the Japanese Journal of Applied Physics, Vol. 28, No. 12 (December, 1989), pp. L2112-L2114. Amano, et al, utilized a horizontal type metalorganic vapor phase epitaxy reactor at atmospheric pressure with a trimethylgallium source. The particular residence times of each step in the growth process were not disclosed, however.

The use of Gallium Nitride materials in a light emitting application within the ultraviolet region is reported by Amano, et al, "Stimulated Emissions Near Ultraviolet at Room Temperature from a Gallium Nitride Film Grown on Sapphire by Metalorganic Vapor Phase Epitaxy using an Aluminum Nitride Buffer Layer", Japanese Journal of Applied Physics, Vol. 29, No. 2, pages L205-L206, February 1990. In this Amano, et al reference, the metalorganic vapor phase epitaxy system operated at atmospheric pressure and resulted in a gallium nitride film that is approximately 31/2 micrometers thick residing on an aluminum nitride interface with a depth of approximately 50 nanometers, the latter residing on a sapphire substrate of approximately 250 micrometers in thickness. This resulted in a gallium nitride film having a carrier concentration of about 2.times.10.sup..intg. per cubic centimeter at room temperature and an electron mobility of approximately 350 square centimeters per volt second at room temperature.

In the Amano paper emissions from CaN were reported. However, no information was given regarding the use of GaN/mirrors, etc., to create an actual laser, rather than a mere light emitter.

Finally, Kahn et al. reported on the photoluminescent characteristics of quantum wells composed of an AlGaN-GaN-AlGaN structure, in Applied Physics Letters, Vol. 56, pp. 1257-1259, Mar. 26, 1990. These quantum wells were grown on basal plane sapphire by low pressure metalorganic vapor deposition. The photoluminescence spectrum showed a peak emitted light intensity near the region having a wavelength of approximately 3400 angstroms.

Ideally, the ability to deposit gallium nitride materials in a controllable and precise manner would permit the development of a family of solid state optical devices, such as filters and ultraviolet lasers. Despite the efforts of previous researchers, ultraviolet lasers continue to be physically large and difficult to operate, requiring the use of high purity gasses which must be vented from the laser apparatus and the building housing the laser apparatus.

3. SUMMARY OF THE INVENTION

The present invention resides in an apparatus and method for creating high quality single crystal gallium nitride layers over basal plane sapphire substrates and a family of optical devices fabricated therefrom. A low pressure metalorganic chemical vapor deposition technique is used which results in materials having carrier densities as low as 10.sup.17 per cubic centimeter at room temperature with corresponding electron mobilities of approximately 300 square centimeters per volt second. The photoluminescence line widths are as narrow as three nanometers. Narrow bandwidth filters are created by depositing quarter wavelength laminates, or stacks, of Al.sub.y Ga.sub.l-y N/Al.sub.x Ga.sub.l-x N, where x and y have values between zero and one. The improved gallium nitride material permits the construction of improved optical devices, including mirrors, quantum wells, and lasers. In particular, the present invention includes a solid state ultraviolet laser, thereby providing an efficient, compact, rugged and lightweight alternative to prior art ultraviolet laser devices.

4. BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic diagram depicting the essential elements of a laser;

FIG. 2 is a schematic diagram of the surface emitting visible/ultraviolet laser utilizing electronic pumping;

FIG. 3 is a schematic view of an edge emitting visible/ultraviolet laser utilizing an electronic pump;

FIG. 4 is a surface emitting visible/ultraviolet light laser with electron beam or optical pumping; and

FIG. 5 is an edge emitting visible/ultraviolet light laser with electronic beam or optical pumping;

FIG. 6 is a reflectance profile for Sample one as described in Example 4;

FIG. 7 is a reflectance profile for Sample two as described in Example 4;

FIG. 8 is a graph depicting the photoluminescence spectrum for bulk GaN and bulk Al.sub.0.14 Ga.sub.0.86 N at a temperature of 30.degree. K.;

FIG. 9 is a graph depicting the photoluminescence spectrum of a GaN quantum well constructed according to the principles of the present invention.

5. DESCRIPTION OF THE PREFERRED EMBODIMENT

Basal plane sapphire substrates having the dimensions of approximately 1.25 centimeters by 1.25 centimeters were used as the deposition surface. The sapphire substrates were degreased, then etched in hot H.sub.3 PO.sub.4 :H.sub.2 SO.sub.4 and loaded onto a silicon carbide coated graphite susceptor in the reactor chamber. The susceptor was preheated by radio frequency induction heating to 1,050.degree. C. in a hydrogen atmosphere at an ambient pressure of 76 torr.

The column 3 source material was triethylgallium, while the column 5 source material was high purity ammonia. The triethylgallium flux was approximately 3.6 micromoles per minute.

In the case of the first three examples, a thin buffer layer of aluminum nitride (approximately 500 angstroms) was deposited prior to the growth of the gallium nitride layer.

EXAMPLE 1

At a growth temperature of 775.degree. C., the resulting gallium nitride film had a carrier concentration of approximately 1.times.10.sup.19 per cubic centimeter at 300.degree. Kelvin. The electron mobility was approximately 70 square centimeters per volt second at a range of temperatures varying from 300.degree. Kelvin to 77.degree. Kelvin. The photoluminescence was 20 nanometers at 300.degree. Kelvin with an absolute edge of 15 nanometers. There were no photoluminescent excitonic features at 300.degree. Kelvin.

EXAMPLE 2

At a growth temperature of 875.degree. C., the carrier concentration was approximately 7.times.10.sup.17 per cubic centimeter at 300.degree. Kelvin. The electron mobility was approximately 110 square centimeters per volt second at 300.degree. Kelvin, 120 square centimeters per volt second at 180.degree. Kelvin, and 65 square centimeters per volt second at 77.degree. Kelvin. The photoluminescence at 300.degree. Kelvin was 10 nanometers, with an absolute edge of 10 nanometers. There were no photoluminescent exitonic features at 300.degree. Kelvin.

EXAMPLE 3

At a growth temperature of 1,050.degree. C., the carrier concentration was approximately 1.times.10.sup.17 per cubic centimeter at 300.degree. Kelvin. The electron mobility at 300.degree. Kelvin was 350 square centimeters per volt second, at 180.degree. Kelvin the electron mobility was approximately 435 square centimeters per volt second and at 77.degree. Kelvin the electron mobility was approximately 254 square centimeters per volt second. The photoluminescence at 300.degree. Kelvin was approximately 3 nanometers with an absolute edge of approximately 5 nanometers. There were photoluminescent exitonic features at 300.degree. Kelvin.

EXAMPLE 4

Two filters were deposited using a low pressure metalorganic chemical vapor deposition technique. Basal plane sapphire (0001) substrates were prepared for growth using the following procedure:

1. Degreased in propanol for 5 minutes; 2. Nitrogen dry; 3. 10 minute etch in tricky solution at 150.degree. C.; 4. 10 minute acetone flush; 5. 10 minute methanol flush; 6. 15 minute etch in 1:1 sulfuric:phosphoric acid solution at 150.degree. C.; 7. 5 minute D1 water rinse; 8. Rinse and flush with 150.degree. C. propanol; 1- y 1- y 9. Nitrogen blowoff and chamber load.

Prior to deposition of the filter stack, a thin layer of AlN was used as a buffer layer onto which 0.5 .mu.m of GaN was deposited. Following the completion of buffer layer growth, individual layers of AlGaN and GaN were deposited in sequence. All growths were terminated with the higher refractive index material on top and thus these structures were terminated with GaN. Following the growth of the last layer, the substrate was cooled to 500.degree. C. under an ammonia flux to prevent column III material sublimation. The sample was then allowed to cool to room temperature under a hydrogen ambient. The thicknesses of the GaN and AlGaN layers were 46.5 nm and 45.2 nm respectively resulting in a center wavelength of 450 nm. Previous growth calibrations for AlGaN and GaN were conducted and were 1.25 and 1.32 A/sec respectively. Hence, the growth times for the AlGaN and GaN layers were 372 and 342 seconds respectively. The growth of the second sample, centered at 400 nm, proceeded identically, only the growth times of the two layers were reduced. Both filter stacks were comprised of 18. periods. The spectrophotometer used to characterize these filters was an IBM model 6420 UV/Vis spectrophotometer. The wavelength range is 200 nm to 900 nm. FIGS. 6 and 7 show the reflectivity results for the two filter designs. Shown is a plot of reflectance vs. wavelength for samples one and two. Sample one has a reflectivity maximum at 405 nm while Sample two's peak is centered at 368 nm. The peak reflectance of Sample one and Sample two is 66% and 78% respectively.

EXAMPLE 5

Quantum wells were also created using the AlGaN-GaN-AlGaN materials. The growth of the GaN and AlGaN layers by LPMOCVD on basal plane sapphire substrates proceeded as follows. The sapphire substrates were degreased, then etched in hot H.sub.3 PO.sub.4 :H.sub.2 SO.sub.4 and loaded onto a silicon carbide coated graphite susceptor in the reactor chamber. The susceptor was preheated by rf induction heating to 1050.degree. C. in a hydrogen ambient at 76 Torr. The column three source materials were triethylaluminum (bubbler temperature 18.degree. C.) and triethylgallium (bubbler temperature 10.degree. C.). The column five source material was high-purity NH.sub.3, which was injected into the growth chamber through a separate line at 1000 sccm. To initiate growth an AlN buffer layer was deposited at 1000.degree. C. (70 sccm of triethylaluminum). The desired epitaxial layers of GaN or AlGaN were then deposited at 850.degree. C. The aluminum mole fraction x was then controlled by adjusting the flow rate of triethylaluminum (50 sccm for x=0.2; 60 sccm for x=0.25). The growth rates were in the range of 0.1-0.5 .mu.m./h. Growth of the quantum well structures consisted of depositing a 0.2 .mu.m layer of AlGaN followed by the GaN well (100-300 .ANG.) and finally a 0.2 .mu.m AlGaN layer.

The photoluminescence experiments were performed using a Spectra Physics 2035-3.0 argon ion laser (pump wavelength =2750-3050 .ANG., up to 400 mW) to excite the samples which were cooled in a closed cycle helium refrigerator to 30K. The recombination radiation was collected with UV compatible optics, dispersed in an ISA HR-640 spectrometer with a 2400 grooves/mm grating, and detected with an uncooled RCA 83010E photomultiplier.

The photoluminescence spectra at 30K from 0.2 .mu.m bulk GaN and Al.sub.0.14 Ga.sub.0.86 N are shown in FIG. 8. The peak emission from the GaN occurs at 3600 .ANG. or 3.444 eV and the peak emission from Al.sub.0.14 Ga.sub.0.86 N occurs at 3350 .ANG. or 3.70 eV. The choice of 30 K was related to the lowest reproducible temperature with the cooling apparatus. Photoluminescence was observed from all the samples (bulk and quantum wells) up to room temperature. Note that the peaks from GaN and AlGaN are distinct and no secondary long-wavelength defect peaks are observed from either sample.

When a thin GaN layer (100-300 .ANG.) is sandwiched (epitaxially) between two wider band-gap Al.sub.0.14 Ga.sub.0.86 N layers the emission from the GaN single quantum well (SQW) is shifted to higher energy (characteristic of type 1 heterojunctions) as shown in FIG. 9. The data in FIG. 9 were obtained from a GaN quantum well whose estimated thickness was 300 .ANG. (growth time, 180 s) with Al.sub.0.14 Ga.sub.0.86 N in the confining layers.

Laser Fabrication

The improved quality of the Al.sub.x Ga.sub.l-x N material system permits the fabrication of surface emitting and edge emitting lasers having improved characteristics, as well as an ability to deposit thin, reproducible and abrupt layers.

Referring to FIG. 1, the essential elements of a visible/ultraviolet light laser constructed with the improved aluminum gallium nitride material can be understood. The laser mirrors 1 and 2 reflect light at the wavelength of laser emission. Sandwiched between the mirrors 1 and 2 is the laser active material 3 which is excited by an energy source 4 which may either electronic, optical or an electron beam. Regardless of the particular laser configuration, the active material can be either a single layer, a heterojunction, a quantum well or a super lattice.

Referring to FIG. 2, a surface emitting visible/ultraviolet laser with electronic pumping for excitation is shown. The surface emitting laser 5 is based on gallium nitride/aluminum gallium nitride PN junctions. The laser is deposited on a substrate 6 having a thickness of approximately 250 micrometers. The substrate may be a variety of materials, such as sapphire, silicon, gallium arsenide, silicon carbide or zinc oxide. A buffer layer 7 is deposited on the substrate 6, the buffer being approximately 50 nanometers in thickness and typically formed of aluminum nitride. The buffer layer 7 facilitates deposition of subsequent layers which may have difficulty bonding directly to substrate 6.

Deposited onto buffer 7 is a series of alternating layers of Al.sub.x Ga.sub.l-x N and Al.sub.y Ga.sub.l-y N material. Typically x has a value of approximately 0.2, and y has a value of approximately 0.3. The outer layers 9 and 10 of the mirror 8 are fabricated from the Al.sub.x GA.sub.l-x N material, whereas the alternating layers 11 and 12 are formed from the Al.sub.y Ga.sub.l-y N material. Layers 13 and 14 are therefore made of the Al.sub.x Ga.sub.l-x N material and layers 15 and 16 alternate to the Al.sub.y Ga.sub.l-y N material. This alternation of layers continues such that the center layer 17 must necessarily be of the Al.sub.x Ga.sub.l-x N material. The thickness of the N type mirror 8 corresponds to a quarter wavelength of the desired light emission frequency.

Deposited onto the N type mirror 8 is an N type spacer 18, having a thickness of approximately 5 micrometers and being constructed of an Al.sub.x Ga.sub.l-x N material, where z is approximately 0.4.

The active region 19 of laser 5 abuts N type spacer 18, and is composed of either an Al.sub.x Ga.sub.l-x N material or a quantum well constructed of Al.sub.x Gal-xN/GaN/Al.sub.x Ga.sub.l-x N. The thickness of the active region 19 is approximately 300 angstroms.

The next layer to be deposited onto the active region 19 is a P-type spacer 20, composed of an Al.sub.z Ga.sub.l-z N material, and having a thickness of approximately 250 angstroms. The combined thickness of layers 18, 19 and 20 should correspond to a half wavelength of the desired light emission frequency. The next layer 21 is a P-type mirror which is substantially identical to N type mirror 8, and insofar as the outer layers 22 and 23 are composed of an Al.sub.x Ga.sub.l-x N material, with alternating layers, such as layers 24 and 25, composed of an Al.sub.y Ga.sub.l-y N material. The center layer 26 is necessarily composed of Al.sub.x Ga.sub.l-x N material. P-type mirror 21 is a quarter wave stack having a thickness corresponding to a quarter wavelength of the desired light emission frequency. Excitation, or population inversion, of the laser is accomplished by current source 27 which is connected to buffer layer 7 through N-type ohmic contact 28, the circuit being completed through P-type ohmic contact 29 which is affixed to layer 22 of P-type mirror 21. Light 30 is emitted from surface 31 of layer 22 of P-type mirror 21.

Referring to FIG. 3, an edge emitting laser 31 is disclosed. The laser resides on substrate 32 which is approximately 250 micrometers thick and may be constructed of sapphire, silicon, gallium arsenite, silicon carbide or zinc oxide. An aluminum nitride buffer layer 33 approximately 50 nanometers thick is deposited onto substrate 32. An N-type layer 34, having a thickness of approximately 4 micrometers, is deposited onto buffer layer 33 and is composed of an Al.sub.x Ga.sub.l-x N material, where x is equal to approximately 0.14. The N-type layer 34 has a first edge 35 and a second edge 36.

Deposited onto top layer 37 of N-type layer 34 is the laser active region, which is of an N-type material such as Al.sub.y Ga.sub.l-y N or Al.sub.y Ga.sub.l-y N/GaN/Al.sub.y Ga.sub.l-y N quantum wells. The active region 38 is approximately 300 angstroms in thickness.

Deposited onto top layer 39 of active region 38 is a P-type layer 40 composed of Al.sub.x Ga.sub.l-x N material, having a P-type layer 40 composed of Al.sub.x Ga.sub.l-x N material, having a thickness of approximately 4 micrometers.

The active region 38 has a first edge 41 and a second edge 42, whereas P-type layer 40 has a first edge 43 and a second edge 44.

A first laser mirror 45, approximately 2 micrometers thick, abuts edges 35, 41 and 43, while a second laser mirror 46 is deposited onto edges 36, 42 and 44 of the N-type layer/active region/P-type layer stack. The laser mirrors

45, 46 are constructed of multiple layers of Al.sub.y Ga.sub.l-y N/Al.sub.x Ga.sub.l-x N or dielectric multilayers, dielectric/metal multilayers to which dielectric reflective coatings have been added. The laser is excited by means of current source 47 which is electrically connected through N-type ohmic contact 48 which resides on buffer layer 33, the circuit being completed through P-type ohmic contact 49 which resides on top surface 50 of P-type layer 40. Laser emission 51 occurs through mirrors 45, 46.

Another embodiment of the present invention is shown in FIG. 4, which depicts a surface emitting visible/ultraviolet light laser 52 which is excited with electron beam or optical pumping. The laser 52 is formed on a substrate 53, having a thickness of approximately 250 micrometers which is formed of either sapphire, silicon, gallium arsenide, silicon carbide or zinc oxide. Deposited on inner surface 54 of substrate 53 is a buffer material 55, having a thickness of approximately 50 nanometers. The buffer layer 55 is typically formed of aluminum nitride.

Deposited onto outer surface 56 of buffer layer 55 is an N-type mirror 57. The N-type mirrors formed in a manner substantially identical to that as described for the embodiment of FIG. 2, namely having alternating layers, for example, layers 58, 59, 60, 61, with layers 58 and 60 being formed of an Al.sub.x Ga.sub.l-x N material, and layers 59 and 61 being formed of an Al.sub.y Ga.sub.l-y N material, and layers 59 and 61 being formed of an Al.sub.y Ga.sub.l-y N where x can have any value between 0 and 1, and similarly can have any value between 0 and 1. Outer layer 62 would necessarily be fabricated of an Al.sub.x Ga.sub.l-x N material.

Deposited onto layer 62 is an N-type spacer 63 which is formed of an Al.sub.z Ga.sub.l-z N material, where z may have any value between 0 and 1. Deposited onto outer surface 64 of spacer 63 is the laser active region 65, having a thickness of approximately 100 micrometers and being formed of either an Al.sub.x Ga.sub.l-x N material or an Al.sub.x Ga.sub.l-x N/GaN/Al.sub.x Ga.sub.l-x N quantum well.

Deposited onto surface 66 of active region 65 is P-type spacer 67 which is formed of an Al.sub.z Ga.sub.l-z N material. The thickness of layers 63, 65 and 67 should equal one half wavelength of the desired light emission frequency.

Finally, the P-type mirror 68 is deposited onto surface 69 of P-type spacer 67. The P-type mirror 68 is formed in a substantially identical manner to the P-type mirror 21 as described with reference to the embodiment of FIG. 2. In other words, a series of alternating layers, for example, 70, 71, 72 and 73 are deposited sequentially with layers 70 and 72 being formed of an Al.sub.x Ga.sub.l-x N material while layers 71 and 73 are formed of an Al.sub.y Ga.sub.l-y N type material Outer layer 74 is necessarily composed of an Al.sub.x Ga.sub.l-x N material.

The laser 52 is excited by electron beam or optical pumping source 75 causing the emission of light 76 through outer surface 77 of substrate 53.

Referring to FIG. 5, an alternate embodiment of the present invention is shown in the form of an edge emitting visible/ultraviolet laser with electron beam or optical pumping for excitation of the laser active region. The edge emitting laser 78 is fabricated on a substrate 79, preferably having thickness between 200 and 300 micrometers and being formed of either sapphire, silicon, gallium arsenide, silicon carbide or zinc oxide. Deposited on upper surface 80 of substrate 79 is buffer layer 81, which is typically composed of aluminum nitride and preferably has a thickness between 25 and 75 nanometers. Deposited on surface 82 of buffer layer 81 is an N-type layer composed of Al.sub.x Ga.sub.l-x N, where x can assume any value between 0 and 1. N-type layer 83, preferably has a thickness between 3 and 5 micrometers, and has a first edge surface 84 and a second edge surface 85.

Deposited on surface 86 of N-type layer 83 is the laser active region 87, which is typically approximately 5 micrometers in thickness, and has a first edge 88 and a second edge 89. The laser active region 87 is typically conducted of N-type Al.sub.y Ga.sub.l-y N or Al.sub.y Ga.sub.l-y N/GaN/Al.sub.y Ga.sub.l-y N quantum wells.

Deposited on surface 90 of laser active region 87 is a P-type layer 91, approximately 5 micrometers thick, and being composed substantially of Al.sub.x Ga.sub.l-x N. The P-type layer 91 has a first edge 92 and a second edge 93.

A first cavity mirror 94 abuts edges 92, 88 and 84 of the laser laminate, being formed by polishing the cavity and applying dielectric reflective coatings. The materials used are typically Al.sub.y Ga.sub.l-y N/Al.sub.x Ga.sub.l-x N and multilayers were dielectric multilayers, or either dielectric multilayers or dielectric/metal multilayers. A substantially identical cavity mirror 95 abuts edges 93, 89 and 85 of the laser laminent.

The laser is excited by electron beam or optical pumping source 96 which causes a laser emission 97 to emerge from mirrors 94, 95.

Those skilled in the art will appreciate that the foregoing Examples and descriptions of various preferred embodiments of the present invention are merely illustrative of the invention as a whole, and that variations in implementation of the present invention are still within the spirit and scope of the invention as defined by the following claims.

Claims

1. An edge emitting laser, comprising:

(a) a substrate;

(b) a buffer layer, said buffer layer being deposited upon and abutting a surface of said substrate;

(c) an N-type layer, said N-type layer being deposited onto said buffer layer, said N-type layer having an end surface, said N-type layer being composed substantially of Al.sub.x Ga.sub.l-x N, where x has a value between 0 and 1;

(d) a laser active region, said laser active region being deposited onto said N-type layer, said laser active region having an end portion;

(e) a P-type layer, said P-type layer being deposited onto said laser active region, said P-type layer having an end region; and

(f) a first and second mirror, said mirrors abutting aid end regions of said N-type layer, said laser active region and said P-type layer, such that when said laser active region is excited by a current source light is emitted from said first mirror.

2. The laser of claim 1, wherein said substrate has a thickness of between approximately 200 and 300 micrometers, and is composed substantially of a material from said group of sapphire, silicon, gallium arsenide, silicon carbide, and zinc oxide.

3. The laser of claim 2, wherein said buffer layer is composed substantially of aluminum nitride, said aluminum nitride having a thickness of between approximately 25 and 75 nanometers.

4. The laser of claim 3, wherein said N-type layer has a thickness of between approximately 3 micrometer sand 5 micrometers.

5. The laser of claim 4, wherein said P-type layers are composed substantially of Al.sub.x Ga.sub.l-x N material, said P-type layer having a thickness of between approximately 2 micrometers and 5 micrometers, with x having a value of between 0 and 1.

6. The laser of claim 5, wherein said laser active region is formed as a quantum well composed of an Al.sub.y Ga.sub.l-y N/GaN/Al.sub.y Ga.sub.l-y N material, where y has a value of between 0 and 1.